Patent Application
20130284589
The present disclosure relates generally to radio frequency (RF) sputtering physical vapor deposition (PVD).
Radio frequency sputtering PVD is a method for depositing a thin film on a substrate. The substrate is placed in a vacuum chamber facing a target that is connected to an RF power supply. When the RF power is initiated, a plasma is formed. Positive gas ions are pulled to the target surface, strike the target, and remove target atoms by momentum transfer. The removed target atoms then deposit on the substrate to form a thin film layer. During physical vapor deposition, it can be important to control the properties of the deposited thin film.
In general, in one aspect, a method of physical vapor deposition includes applying a radio frequency signal to a cathode in a physical vapor deposition apparatus, wherein the cathode includes a sputtering target electrically connecting a chuck in the physical vapor deposition apparatus to ground through an impedance matching network, wherein the chuck supports a substrate, and wherein the impedance matching network consists of an inductor in series with a capacitor, and depositing material from the sputtering target onto the substrate.
Implementations can include one or more of the following features. A capacitance of the capacitor may be selected or adjusted such that a positive self bias direct current voltage is generated on the substrate. The positive self bias direct current voltage may be between 10 and 100V, e.g., between 60 and 75V. Selecting or adjusting the capacitance of the capacitor may include selecting or adjusting the capacitance to have a magnitude of between 10 pF and 1200 pF. An inductance of the inductor may have a magnitude of between 300 and 600 micro Henry. The radio frequency signal may have a radio frequency power having a magnitude of between 1000 W and 5000 W. The target may be a dielectric material, e.g., lead zirconate titanate (“PZT”). Depositing material from the sputtering target onto the substrate may include creating a thin film having a thickness of between 2000 Å and 10 μm. The thin film may have a thickness of between 2 μm and 4 μm. Depositing material from the sputtering target onto the substrate comprises creating a thin film having a (100) crystalline structure.
In general, in another aspect, a physical vapor deposition apparatus includes a vacuum chamber having side walls, a cathode inside the vacuum chamber, wherein the cathode is configured to include a sputtering target, a radio frequency power supply configured to apply a radio frequency signal to the cathode, an anode inside and electrically connected to the side walls of the vacuum chamber, a chuck inside the vacuum chamber, wherein the chuck is configured to support a substrate, and an impedance matching network electrically connecting the chuck to ground, wherein the impedance matching network consists of an inductor in series with a capacitor.
Implementations can include one or more of the following features. The inductor may be connected between the capacitor and the chuck. The capacitor may be connected between the inductor and ground. The capacitor may have a capacitance between 10 pF and 1200 pF. The inductor may have an inductance between 300 and 600 micro Henry. The target may be a dielectric material, e.g., lead zirconate titanate (“PZT”). The cathode may include comprises a magnetron assembly. The impedance matching network may have a resonant frequency about 1 to 2 MHz lower than a frequency of the of the radio frequency signal applied to the cathode. The impedance matching network may have a resonant frequency about 1 to 2 MHz higher than a frequency of the of the radio frequency signal applied to the cathode.
A simplified LC circuit can be more stable and easier to tune to provide the desired bias. Since the simplified LC circuit includes fewer components, and there are fewer sources of variation, and consistency in tuning can be improved. In addition, the simplified LC circuit has a single path for current; it should not experience circular currents.
Creating a positive self bias DC voltage by connecting an impedance network to the chuck can result in the formation of thin films having advantageous piezoelectric and dielectric properties, such as PZT thin films having a dielectric constant in the range of 1000 to 1700, a high d31 coefficient, and a high break-down voltage. Likewise, creating a negative self bias using an impedance matching network can be advantageous for re-sputtering, or etching, of deposited thin films, particularly PZT thin films.
The details of one or more embodiments are set forth in the accompanying drawings and the description below. Other features, aspects, and advantages will become apparent from the description, the drawings, and the claims.
Like reference numbers and designations in the various drawings indicate like elements.
When RF physical vapor deposition, or sputtering, is used to create a thin film on a substrate, it can be difficult to control the properties of the deposited film. By altering the DC self bias of the substrate, for example by connecting the chuck to ground through an impedance matching network to the chuck, the properties of the film can be better controlled.
Referring to
A cathode assembly 106 can be housed inside and near the top surface 154 of vacuum chamber 102. Cathode assembly 106 can include a target 126 that can be bonded to a metallic backing plate (not shown). The target 126 can be generally circular, with an outer edge 160. The target can be made of, for example, a dielectric material such as lead zirconate titanate (“PZT”). Cathode 106 can act as an electrode for RF current when RF power is applied by RF power supply 104. Cathode assembly 106 can be electrically isolated from the vacuum chamber 102 by an insulator ring 150.
A substrate support or chuck 110 to support one or more substrates can be housed inside vacuum chamber 102 near, but spaced above, the bottom surface 156 of the vacuum chamber 102. The chuck 110 can include a substrate holding mechanism 122, such as a substrate clamping plate, configured to hold substrate 116 such that substrate 116 can be coated with a thin film during the PVD process. Substrate 116 can be, for example, a microelectromechanical system (MEMS) wafer. A temperature control (not shown) can be located on the chuck 110 to, for example, maintain the temperature of substrate 116 at a prescribed temperature between 25° C. and 800° C., such as 650° C. to 700° C.
In one embodiment, shown in
The impedance matching network 107 can include a variable tune capacitor 111 and an inductor 113. The variable tune capacitor 111 and an inductor 113 can be connected in series. The variable tune capacitor 111 can be electrically connected to ground. The inductor 113 can be electrically connected between the input terminal 109 and the variable tune capacitor 111. The inductor can have an inductance of about 300 to 600 micro Henry. The impedance matching network 107 can be tuned to a frequency of about 5 to 100 MHz.
In some implementations, the impedance matching network 107 consists of only the variable tune capacitor 111 and the inductor 113. Having additional electrical elements can introduce additional sources of variation in the electrical performance of the apparatus 100, and therefore a simplified LC circuit with only the variable tune capacitor 111 and the inductor 113 can be more stable and easier to tune to provide the desired bias. In addition, the simplified LC circuit has a single path for current from the input terminal 109 to ground, so it should not experience circular currents.
An anode 108 can also be housed inside vacuum chamber 102. The anode 108 can provide a counterpart electrode to the cathode 106 so as to provide an RF current return path. In some embodiments, the anode 108 and the chuck 110 can be the same component. In other embodiments, however, as described herein, the anode 108 may be electrically isolated from the chuck 110 so that the chuck 110 can be floating or held at a different potential than the anode 108. The anode can be grounded, i.e., electrically connected in this context (the anode need not be actually connected to ground), to the vacuum chamber sidewalls 152.
Referring to FIGS. 1 and 2A-2B, the anode 108 can have an annular body 302 and can be extended by an annular flange 304 projecting inwardly from the annular body 302. The annular flange 304 can define an intended discharge space 128 (see
Shown in
The annular flange 304 can project inwardly from the lower portion 308 such that at least some of the flange extends below target 126. As shown in
An annular opening 310 (see
The vacuum chamber 102 can also include an RF shield 124 to protect the sidewalls of vacuum chamber 102 from being coated with thin film material. The shield 124 can be made, for example, of non-magnetic stainless steel or aluminum and can be grounded to the sidewalls 152 of the vacuum chamber 102.
In some implementation shown in
The annular opening 406, in
In some embodiments, shown in FIGS. 3 and 4A-4B the shield can be extended such that a set of concentric annular projections 404 projects from the annular flange 146, for example towards the cathode 106. The annular projections 404 can extend parallel to annular body 402. As shown in FIGS. 3 and 4A-4B, the height of the annular projections 404 can increase along a radius from the center of the vacuum chamber 102 to the sidewalls 152. The annular body 402 can have a height that is taller than the height of the annular projections 404.
The physical vapor deposition apparatus 100 can further include an electrically conductive body 130, for example a strap, that directly connects the anode 108 and the shield 124. The electrically conductive body 130 can be flexible and can be configured to permit gas flow between the anode 108 and shield 124. For example, the electrically conductive body 130 can be a mesh or a wire strap. The electrically conductive body 130 can be made, for example, of copper or aluminum.
There can be a number of connections between the anode 108 and shield 124. For example, the electrically conductive body 130 can be connected to the anode 108 and the shield 124 at at least four points. The electrically conductive body 130 can be connected between a lower surface of the anode 108 and a top portion of the shield 124. The electrically conductive body 130 can also be connected between a top portion of the anode 108 and an outer surface of the shield 124.
The physical vapor deposition apparatus 100 can further include a secondary chamber shield 134. The chamber shield can be made of, for example, non-magnetic stainless steel or aluminum. An upper portion of the chamber shield can be positioned between the anode 108 and the sidewalls of the vacuum chamber 102. A lower portion of the chamber shield 134 can be positioned between the sidewalls of the vacuum chamber 102 and shield 124. The chamber shield 134 can be concentric with and surround shield 124 and/or anode 108. The height of the chamber shield 134 can be equal to or greater than the height of shield 124. The chamber shield 134 can include a vertical annular body 142 and an annular flange 144 (shown in
The physical vapor deposition apparatus 100 can further include a process gas inlet 112, process gas control devices (not shown), a vacuum outlet 114, pressure measurement and control devices (not shown), and vacuum pumps (not shown). The chamber shield 134 can be configured such that process gases may still be pumped into and out of the vacuum chamber 102. For example, the chamber shield 134 may be short enough so as not to cover a process gas inlet 112 or the vacuum outlet 114. Alternatively, the chamber shield 134 may have holes (not shown) in locations corresponding to the locations of the process gas inlet 112 and vacuum outlet 114. Furthermore, the chamber shield 134 can be separately removable and can be cleaned easily and reused over time.
The chamber shield 134 can be electrically bonded to shield 124 with an electrically conductive body 136. The electrically conductive body 136 can be of similar material and shape as electrically conductive body 130. Thus, the electrically conductive body 136 can be configured to permit gas flow between shield 124 and chamber shield 134. Likewise, the electrically conductive body 136 can be composed of mesh, can be one or more straps, and can comprise copper or aluminum. Moreover, the electrically conductive body 136 can be connected between a bottom surface of shield 124 and an inner surface of chamber shield 134.
During the sputtering or PVD process, gases, such as argon and oxygen, are supplied through the process gas inlet 112 at a flow rate of 10-200 sccm/0.2 to 4 sccm, such as 10 to 60 sccm/0.5 to 2 sccm. A vacuum pump (not shown) maintains a base vacuum, for example, of 10−7 Ton or below, and a plasma operation pressure, for example, of 0.5 mTorr to 20 mTorr, particularly 4 mTorr, through vacuum outlet 114. When the RF power from RF power supply 104 is applied on the order of 500 W to 5,000 W, for example 2000W to 4,000 W, or 3000 W, to the cathode assembly 106, the target 126 is negatively biased and the anode 108 is positively biased, causing plasma to form in the intended discharge space 128 between the cathode 106 and the anode 108. The magnetron assembly 118 creates a magnetic field of, for example, 50 Gauss to 400 Gauss, such as 200 Gauss to 300 Gauss, at and near the front surface of the cathode 106. The magnetic field confines the electrons to a helical motion parallel to the front surface of target 126.
The negative selfbias DC voltage on target 126, in conjunction with the electrons confined near the surface of target 126 by the magnetic field, facilitates bombardment of the target 126 by energetic positive ions of the plasma. Momentum transfer causes neutral target material, such as PZT molecules, to dislocate from the target 126 and deposit on substrate 116, creating a thin film on substrate 116. The resulting thin film can have a thickness of 2000 Å to 10 μm, for example 2-4 μm.
In the embodiment shown in
As an example, a graph of a positive self bias of a substrate vs. gas flow is shown in
The charge of the DC self bias can be controlled by the amount of RF power applied to the substrate 116 in addition to the impedance of the impedance matching network 107. In general, to get a positive DC self-bias with the impedance matching network, the resonant frequency should be set slightly smaller than the critical resonant frequency. For example, the resonant frequency can be set 1-2 MHz smaller than the critical resonant frequency. The frequency of the RF power to the cathode can be the same as the critical resonant frequency, e.g., 13.56 MHz. With the resonant frequency of the impedance matching network set slightly smaller than critical resonant frequency, a positive DC self-bias, e.g. of 10V-100V, such as 60V, can develop on the substrate 116. On the other hand, the impedance matching network 107 should not be set to have a resonant frequency that is the same as or too close to that of the target RF frequency, because this may resulting in an unstable condition where the bias DC voltage oscillates between positive and negative.
A positive voltage results in attracting and accelerating electrons from the plasma to the surface of substrate 116. Those electrons with sufficient energies will cause modification of the sputtered material properties without causing any substantial re-sputtering due to their low momentum. Moreover, a positive voltage can prevent plasma ions from bombarding the surface of substrate 116 and thus avoid etching of the surface. A negative voltage can cause plasma ions to be attracted and accelerated towards the substrate, which can result in re-sputtering of the surface. Re-sputtering can be useful, for example, for etching the substrate surface. For a given implementation, such as chamber configuration, gas composition and flow rate, pressure, magnetic field, and voltage, experimentation may be required to obtain the RF power and impedance values of the elements in the impedance matching network 107 necessary to generate a positive or negative self bias voltage.
A flow chart for a process of forming a thin film using the apparatus of
Use of either an impedance matching network in a physical vapor deposition apparatus can be particularly advantageous for the creation of piezoelectric thin films, such as PZT thin films. In particular, use of an impedance matching network 107 to create an indirect bias on the substrate or deposited film is advantageous because an external DC bias cannot be directly applied to a dielectric material such as PZT. Furthermore, the impedance matching network 107 can modify the electric field strength in the dark space between substrate 116 and the intended discharge space 128, thereby changing the re-sputtering effects of the deposition process. In contrast, while directly biasing a substrate can shift the overall system voltages into an offset value to both the target and/or the substrate, it cannot modify the dark space between substrate 116 and the intended discharge space 128.
If PZT films are sputtered using a physical vapor deposition apparatus having a substrate with a positive DC self bias as described herein, the electrons that are attracted to the surface of the substrate can cause electron heating, which can increase the mobility of the thin films atoms. Further, the electrons on the surface can help reject plasma ions from the surface to avoid re-sputtering of the surface. As a result, a film having a preferable structure, for example, a thin film having a (100) crystalline structure, can be formed. Such films sputtered on a substrate having a positive DC self bias, for example a PZT film having a Perovskite PZT (100)/(200) crystal orientation, can have advantageous dielectric and piezoelectric properties, such as a dielectric constant in the range of 1000 to 1700, a high d31 coefficient (e.g., about 250 pm/V or greater), and a high break-down strength (e.g., 1 MV/cm or greater). For example, PZT thin films having a (100) crystal orientation can be used as MEMS devices, such as actuators for ink dispensing devices.
A number of embodiments have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of what is described. For example, it should be understood that terms of positioning and orientation (e.g., top, vertical) have been used to describe the relative positioning and orientation of components within the physical vapor deposition apparatus, but the physical vapor deposition apparatus itself can be held in a vertical or horizontal orientation or some other orientation. As another example, the steps of the exemplary flow chart of