Selective metal encapsulation schemes

Abstract

A method and system of processing a semiconductor substrate includes, in one or more embodiments, depositing a protective layer on the substrate surface comprising a conductive element disposed in a dielectric material; processing the protective layer to expose the conductive element; electrolessly depositing a metallic passivating layer onto the conductive element; and removing at least a portion of the protective layer from the substrate after electroless deposition. In another aspect, a method and system of processing a semiconductor includes depositing a metallic passivating layer onto a substrate surface comprising a conductive element, masking the passivating layer to protect the underlying conductive element of the substrate surface, removing the unmasked passivating layer, and removing the mask from the passivating layer.

Description

FIELD OF THE INVENTION

[0002] The present invention relates generally to semiconductor manufacturing, and more particularly to systems and methods for the deposition of barrier film layers on a conductive feature of the device.

BACKGROUND OF THE INVENTION

[0003] A common goal in the integrated circuit (IC) industry is to place more conductive circuitry into a smaller substrate surface area. Recent improvements in circuitry of ultra-large scale integration (ULSI) on semiconductor substrates indicate that future generations of semiconductor devices will require sub-quarter micron (or less) multilevel metallization. The multilevel interconnects that lie at the heart of this technology require planarization of interconnect features formed in high aspect ratio apertures, including contacts, vias, lines and other features. One example of the use of such multilevel metallization is in “dual damascene” processing, in which two channels of conductive materials are positioned in vertically separated planes perpendicular to each other and interconnected by a vertical “via” at their closest point.

[0004] Currently, copper and its alloys have become the metals of choice for ULSI technology because copper has a lower resistivity than aluminum, (1.7 μΩ-cm compared to 3.1 i-cm for aluminum), a higher current carrying capacity, and significantly higher electromigration resistance. These characteristics are important for supporting the higher current densities experienced at high levels of integration and increased device speed. Further, copper has a good thermal conductivity and is available in a highly pure state.

[0005] However, copper readily forms copper oxide when exposed to atmospheric conditions or environments outside of processing equipment. Metal oxides can result in an increase the resistance of metal layers, become a source of particle problems, and reduce the reliability of the overall circuit.

[0006] One known solution is to deposit a passivating layer or an encapsulation layer such as a dielectric material on the metal layer to prevent metal oxide formation. However, the high dielectric constant of the dielectric material increases the interlayer capacitance in multilayer environments. Furthermore, the electromigration of copper in dielectric materials is unacceptably high.

[0007] Cobalt and cobalt alloys, which are conductive (low dielectric constant) and are good barriers to electromigration of copper, have been used for passivating copper. Cobalt may be deposited by electroless deposition techniques on copper. However, copper does not satisfactorily catalyze or initiate deposition of materials from electroless solutions. It is possible to activate the copper surface to cobalt deposition by first depositing a catalytic material, such as palladium, on the copper surface. Cobalt is then selectively deposited by electroless plating onto the catalytic material. However, deposition of the catalytic material may require multiple steps or the use catalytic colloidal compounds. Catalytic colloidal compounds, and colloidal palladium materials in particular, adhere to dielectric materials and result in the undesired, excessive, and non-selective deposition of the catalyst material on the substrate surface. Alternatively, palladium can be deposited selectively on copper surfaces by a displacement mechanism in which palladium replaces a thin layer of the exposed copper on the wafer surface. However, common semiconductor fabrication methods invariably leave copper atom contaminants on the wafer surface, so that palladium is deposited on undesired locations, e.g., dielectric surfaces, as well as desired locations, e.g., conductive metal feature. In the subsequent step of cobalt deposition, cobalt is electrolessly deposited wherever palladium is present, leading to the non-selective deposition of cobalt.

[0008] Non-selective deposition of passivation material may lead to surface contamination, unwanted diffusion of conductive materials into dielectric materials, and even device failure from short circuits and other device irregularities.

[0009] There is a need for methods and systems for deposition of passivation materials that eliminate or minimize their non-selective deposition.

SUMMARY OF THE INVENTION

[0010] In one aspect of the methods and systems of the present invention, a sacrificial protective layer is used to prevent stray electroless deposition of a conductive passivating layer on a substrate surface. In one or more embodiments, the protective layer is deposited onto a substrate surface having at least one conductive element, and the protective layer is processed to expose the conductive element of the substrate surface. A conductive passivating layer is then deposited, e.g., electrolessly, on the exposed conductive element(s) of the substrate. The sacrificial protective layer prevents nucleation of the passivating layer on the substrate surface during deposition of the passivating layer. Any undesired deposition of passivation material on areas other than the conductive element(s), e.g., on the protective layer, is eliminated with the removal of the protective layer.

[0011] In one or more embodiments, the protective layer is an organic material, such as photoresist, amorphous carbon, a dielectric material, or an etch stop material. In one or more embodiments, the method includes providing one or more intermediate layers disposed between the substrate surface and the protective layer.

[0012] One or more embodiments of the present invention contemplate the deposition of an intermediate layer onto the substrate surface prior to deposition of the protective layer.

[0013] In another aspect of the invention, a method of processing a semiconductor substrate to encapsulate a conductive element is provided. The method includes the steps of depositing a metallic passivating layer onto a substrate surface comprising a conductive element, masking the passivating layer to protect the underlying conductive element of the substrate surface, etching the unmasked passivating layer to expose the underlying intermediate layers or substrate surface, and removing the mask from the passivating layer after etching.

[0014] The methods and systems of the present invention provide a semiconductor device having a conductive element selectively encapsulated by a metallic passivating layer. The passivating layer interface with the conductive element is of low capacitance. The passivating layer also provides an effective barrier to electromigration of copper into adjacent dielectric regions. Significantly, the surface of the substrate is substantially free of stray electrolessly deposited passivation material, which reduces the incidence of surface contamination, device failure from short circuit, and other device irregularities.

BRIEF DESCRIPTION OF THE DRAWING

[0015] Various objects, features, and advantages of the present invention can be more fully appreciated with reference to the following detailed description of the invention when considered in connection with the following drawings, in which like reference numerals identify like elements. The following drawings are for the purpose of illustration only and are not intended to be limiting of the invention, the scope of which is set forth in the claims that follow.

[0016] FIG. 1 is a flow chart illustrating steps undertaken in selective metal encapsulation schemes according to one or more embodiments of the present invention;

[0017] FIGS. 2-4 are schematic illustrations of exemplary deposition processes for the selective deposition of a conductive passivating layer according to one or more exemplary embodiments of the present invention;

[0018] FIG. 5 is a flow chart illustrating the steps undertaken in selective metal encapsulation schemes according to one or more embodiments of the present invention; and

[0019] FIG. 6 is a schematic illustration of an exemplary integration scheme for deposition of a selective metal encapsulation layer according to one or more embodiments of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0020] The words and phrases used herein should be given their ordinary and customary meaning in the art by one skilled in the art unless otherwise further defined.

[0021] “Substrate surface” as used herein refers to a layer of material that serves as a basis for subsequent processing operations. For example, a substrate surface may contain one or more “conductive elements,” such as aluminum, copper, tungsten, or combinations thereof, and may form part of an interconnect feature such as a plug, via, contact, line, wire, and may also form part of a metal gate electrode. A substrate surface may also contain one or more nonconductive materials, such as silicon, doped silicon, germanium, gallium arsenide, glass, and sapphire. The substrate surface may also contain one or more low k materials such as carbon-doped oxides, porous low k materials such as organic low k and inorganic low k materials and hybrids thereof, or air-gap structures.

[0022] The term “about” is used herein to mean approximately, in the region of, roughly or around. When the term “about” is used in conjunction with a numerical range, it modifies that range by extending the boundaries above and below the numerical values set forth. In general, the term “about” is used herein to modify a numerical value above and below the stated value with a variance of 10%.

[0023] FIG. 1 is a flow chart illustrating an exemplary processing sequence 100 undertaken in depositing a conductive passivating layer according to one or more embodiments of the present invention.

[0024] In step 110 in FIG. 1, a substrate surface is prepared for deposition of the passivating layer. The surface can be treated to remove surface contaminants using materials removal and/or cleaning techniques known in the art. Exemplary materials removal techniques include chemical mechanical polishing (CMP) and etching. Wet etching techniques using HF solution and dry etch techniques using HF vapor are suitable for removing dielectric materials, such as silicon oxide, from the substrate surface. Other etching techniques include downstream or remote plasma etching using a hydrogen and water plasma, or a hydrogen plasma and in situ etch processes using hydrogen, hydrogen and nitrogen, or ammonia to remove metal oxides from the substrate surface. CMP is suitable for removal of various materials, including metals and dielectric materials. Other exemplary surface treatments include ultrasonication and cleaning with an acidic solution to remove metal oxides and other contaminants from the substrate surface. The exposed conductive feature(s) can also be rinsed with distilled water to remove residual contaminants from the surface treatment process.

[0025] In step 120 of FIG. 1, a sacrificial protective layer is deposited on the substrate surface. The protective layer can be any material that is compatible with the semiconductor fabrication process and that is unaffected by the subsequent deposition of a passivating layer. Exemplary materials for the protective layer include dielectrics, such as SiN, SiC, SiOC/SiC, and SiCN, photoresist, and organics such as amorphous carbon. The protective layer is deposited using known techniques such as chemical vapor deposition (CVD), plasma-enhanced chemical vapor deposition (PECVD), spin-on deposition and physical deposition processes, e.g., sputtering. The thickness of the protective layer can vary depending upon the materials used and the methods of material deposition and removal. Exemplary layer thicknesses are in the range of about 100 Å to about 5000 Å. With advances in deposition technology, such as atomic layer deposition, further reductions in film thickness are anticipated.

[0026] In step 130 of FIG. 1, the protective layer is processed to remove materials above the underlying conductive element(s) so as to expose the conductive element in the underlying substrate surface. Conventional masking and materials removal techniques known in the art can be used. Etching is a common technique used for the selective removal of material. Before etching begins, a wafer is coated with photoresist and exposed to a circuit pattern (or other pattern corresponding to the conductive element) during photolithography. Etching removes material only from areas dictated by the photoresist pattern. The photoresist can be a positive photoresist, in which case the exposed areas of a positive resist film are removed by the process of development. Alternatively, the photoresist can be a negative photoresist, in which case the mask pattern is a negative of the underlying conductive layer structure and the unexposed areas of the resist film are removed by the process of development.

[0027] The exposed protective layer is then etched to selectively remove the protective layer and expose the underlying conductive element. The etching technique is selective to the material of the protective layer and can be a dry etch such as HF vapor or reactive ion etch (RIE) with CHF3/O2 or plasma etch as described above. Plasma etching is performed by applying an electrical field to a gas containing a chemically reactive element, thereby generating reactive ions that can remove (etch) materials very rapidly. It also gives the chemicals an electric charge, which directs them toward the wafer vertically. This allows vertical etching profiles, which is desired in selective exposure of the features of the underlying substrate surface.

[0028] In the next step 140, it is contemplated by one or more embodiments of the present invention that an initiation layer can be deposited on the substrate surface to initiate the electroless deposition process. The initiation layer can be a noble metal and is typically very thin, e.g., only a few monolayers thick. The initiation layer generally forms selectively on the exposed conductive element by displacement of the noble metal for the conductive metal, or can be deposited as colloidal palladium. Although the displacement process is selective for the conductive metal, there typically is some stray deposition occurring on the nonconductive surfaces, e.g., the protective layer. The substrate is then rinsed to remove the displacement solution.

[0029] A conductive passivating layer then is selectively electrolessly deposited on the initiation layer in step 150 of FIG. 1. The conductive material used as the passivating layer is generally a metal that does not form a solid solution with copper or other conductive metals, such as ruthenium, tantalum, tungsten, cobalt, palladium, nickel, tin, titanium, molybdenum, platinum, iron, and niobium and their alloys. In one or more embodiments, the passivating conductive metal is cobalt or a cobalt alloy. In one or more other embodiments, the passivating layer is deposited directly onto the conductive element (step 150), without the need to first deposit an initiation layer (step 140). Electroless deposition processes for certain cobalt alloys, using boron-containing reducing agents, permit electroless deposition of metal without the need for an initiation layer.

[0030] At least a portion of the protective layer is removed in step 160 of FIG. 1 to remove any undesired passivation material at nucleation sites outside of the conductive element area. In one or more embodiments, a portion of the thickness of the protective layer is removed to ensure the removal of stray electroless deposition on the protective coating. In other exemplary embodiments, the entire protective layer is removed to expose the underlying layer, which may be the substrate surface or an intermediate layer.

[0031] The protective layer is removed or lifted using materials removal techniques known in the art. Exemplary, non-limiting materials removal techniques include chemical mechanical polishing (CMP), etching and ashing, e.g., plasma ashing. Reactive ion etching using CHF3/O2, wet etch techniques using HF solution, or dry etch techniques using HF vapor, are suitable for removing dielectric materials. Other etching techniques include downstream or remote plasma etching using a hydrogen and water plasma or a hydrogen plasma and in situ etch processes using hydrogen, hydrogen and nitrogen or ammonia. Wet etching and ashing can be used for the removal of carbon-containing layers, such as amorphous carbon and photoresist. The appropriate technique depends upon the composition of the material being removed. The exposed conductive feature also can be rinsed with distilled water to remove residuals from the materials removal process.

[0032] The process provides a conductive element having a conductive passivating layer selectively deposited thereon. Elsewhere, the substrate surface is free of unwanted conductive material. In exemplary embodiments, other than the deposited passivating layer, the substrate is returned to its original state prior to deposition of the passivating layer and is ready for further processing.

[0033] The electroless deposition process is described in greater detail below. Additional information regarding electroless deposition technology, generally, is found in co-pending U.S. application Ser. No. 10/117,712, entitled “Electroless Deposition Methods” and co-pending U.S. application Ser. No. 10/284,855, entitled “Post Rinse To Improve Selective Deposition Of Electroless Cobalt On Copper For ULSI Application,” both of which are commonly owned and are incorporated by reference herein.

[0034] Electroless deposition is generally defined herein as deposition of a conductive material generally provided as charged ions in a bath over an active surface to deposit the conductive material by chemical reduction in the absence of an external electric current. Electroless deposition typically involves exposing a substrate to a solution by immersing the substrate in a bath or by spraying the solution over the substrate.

[0035] In one or more embodiments, an initiation layer may be formed on the exposed conductive elements by deposition of a noble metal in step 140. Embodiments of the present invention also contemplate the use of noble metals, such as gold, silver, iridium, rhenium, rhodium, rhenium, ruthenium, palladium, platinum, osmium, and combinations thereof. In one or more embodiments, the noble metal is selected from the group of palladium, platinum, or combinations thereof. The noble metal is deposited from an activation solution containing at least a noble metal salt and an inorganic acid. Examples of noble metal salts include palladium chloride (PdCl2), palladium sulfate (PdSO4), palladium ammonium chloride, and combinations thereof. Examples of inorganic acids include hydrochloric acid (HCl), sulfuric acid (H2SO4), hydrofluoric acid (HF) and combinations thereof. Alternatively, inorganic acids, such as carboxylic acids including acetic acid (CH3COOH), may be used in the activation solution for the initiation layer.

[0036] In one or more embodiments of the present invention, displacement of the exposed conductive element, e.g., copper, by a noble metal, e.g., palladium, is carried out as follows. In a displacement plating process, wafers with an exposed copper surface are immersed in a bath containing dissolved ions of a metal more noble than copper. With simple immersion, the copper dissolves, i.e., is oxidized, and a film of the more noble metal deposits, i.e., is reduced, to thereby displace atoms of copper with the noble metal. Displacement is selective to copper and the coating thickness is self-limiting. Depending on the porosity of the copper, the noble metal may be up to a few monolayers thick.

[0037] The noble metal salt may be in the deposition solution at a concentration between about 20 parts per million (ppm) and about 20 g/liter. The concentration of the metal salt may also be described as a volume percent with 1 vol % corresponding to about 40 ppm. The inorganic acid is used to provide an acidic deposition composition, for example, at a pH of about 7 or less. A pH level between about 1 and about 3 has been observed to be effective in displacement deposition of the noble metals from the activation solution. An acidic solution has also been observed to be effective in removing or reducing oxides, such as metal oxides including copper oxides, from the metal or dielectric surface of the substrate during the activation deposition process.

[0038] The activation solution for the initiation layer is generally applied to the substrate surface for between about 1 second and about 300 seconds at a composition temperature between about 15° C. and about 80° C. The activation solution is generally provided at a flow rate between about 50 ml/min and about 2000 ml/min. In one aspect a total application of about 120 ml and about 200 ml of activation solution was provided to deposit the activation layer. The activation solution generally provides for the deposition of a noble metal to a thickness of about 50 Å or less, such as about 10 Å or less. The initiation layer may be continuous or discontinuous.

[0039] An example of an activation solution composition for depositing the initiation material includes about 3 vol % (120 ppm) of palladium chloride and sufficient hydrochloric acid to provide a pH of about 1.5 for the composition, which is applied to the substrate surface for about 30 seconds at a flow rate of about 750 ml/min at a composition temperature of about 25° C.

[0040] In other embodiments, the initiation layer is formed by exposing the exposed conductive materials to a borane-containing composition in step 140. The borane-containing composition forms a metal boride layer selectively on the exposed conductive metals, which provides catalytic sites for subsequent electroless deposition processes.

[0041] The borane-containing composition includes a borane reducing agent. Suitable borane-containing reducing agents include alkali metal borohydrides, alkyl amine boranes, and combinations thereof. Examples of suitable borane-containing reducing agents include sodium borohydride, dimethylamine borane (DMAB), trimethylamine borane, and combinations thereof. The borane-containing reducing agent comprises between about 0.25 grams per liter (g/L) and about 6 g/L of the boron-containing composition. The borane-containing composition may additionally include pH-adjusting agents to provide a pH of between about 8 and about 13. Suitable pH adjusting agents include potassium hydroxide (KOH), sodium hydroxide (NaOH), ammonium hydroxide, ammonium hydroxide derivatives, such as tetramethyl ammonium hydroxide, and combinations thereof.

[0042] The conductive element is generally exposed to the borane-containing composition between about 30 seconds and about 180 seconds at a composition temperature between about 15° C. and about 80° C. The borane-containing composition may be delivered to the substrate at a flow rate between about 50 ml/min and about 2000 ml/min. In one aspect a total application of about 120 ml and about 200 ml of the borane-containing composition was provided to form the initiation layer of a metal boride compound.

[0043] An example of a borane-containing composition for forming the layer includes about 4 g/L of dimethylamine borane (DMAB) and sufficient sodium hydroxide to provide a pH of about 9 for the composition, which is generally applied to the substrate surface for about 30 seconds at a flow rate of about 750 ml/min at a composition temperature of about 25° C.

[0044] A rinsing agent, typically deionized water, is then applied to the substrate surface to remove any solution used in forming the initiation layer.

[0045] A metallic passivating layer is deposited by an electroless process on the initiation layer in step 150. In one or more embodiments of the present invention, the metal passivating layer comprises cobalt or a cobalt alloy. Cobalt alloys include cobalt-tungsten alloy, cobalt-phosphorus alloy, cobalt-tin alloys, cobalt-boron alloys, including ternary alloys, such as cobalt-tungsten-phosphorus and cobalt-tungsten-boron. One or more embodiments of the present invention also contemplate the use of other materials, including nickel, tin, titanium, tantalum, tungsten, molybdenum, platinum, iron, niobium, palladium, platinum, and combinations thereof, and other alloys including nickel cobalt alloys, doped cobalt and doped nickel alloys, or nickel iron alloys, to form the metal layer as described herein.

[0046] In one or more embodiments of the present invention, the metallic passivation material is deposited from an electroless solution containing at least a metal salt and a reducing agent. The electroless solution may further include additives to improve deposition of the metal. Additives may include surfactants, complexing agents, pH adjusting agents, or combinations thereof.

[0047] Suitable metal salts include chlorides, sulfates, sulfamates, or combinations thereof. An example of a metal salt is cobalt chloride. The metal salt may be in the electroless solution at a concentration between about 0.5 g/L and about 30 g/L.

[0048] Cobalt alloys, such as cobalt-tungsten may be deposited by adding tungstic acid or tungstate salts including sodium tungstate, and ammonium tungstate, and combinations thereof for tungsten deposition. Phosphorus for the cobalt-tungsten-phosphorus deposition may be formed by phosphorus-containing reducing agents, such as hypophosphite. Cobalt alloys, such as cobalt-tin may be deposited by adding stannate salts including stannic sulfate, stannic chloride, and combinations thereof. The additional metals salts, for example, for tungsten and tin, may be in the electroless solution at a concentration between about 0.5 g/L and about 30 g/L.

[0049] Suitable reducing agents include sodium hypophosphite, hydrazine, formaldehyde, and combinations thereof. The reducing agents have a concentration between about 1 g/L and about 30 g/L of the electroless solution. For example, hypophosphite may be added to the electroless solution at a concentration between about 15 g/L and about 30 g/L.

[0050] The reducing agents may also include borane-containing reducing agents, such as sodium borohydride, dimethylamine borane (DMAB), trimethylamine borane, and combinations thereof. The borane-containing reducing agent comprises between about 0.25 grams per liter (g/L) and about 6 g/L of the boron-containing composition. The presence of borane-containing reducing agents allow for the formation of cobalt-boron alloys such as cobalt-tungsten-boron and cobalt-tin-boron among others.

[0051] The metal electroless solutions described herein are generally applied to the substrate surface for between about 30 seconds and about 180 seconds at a composition temperature between about 60° C. and about 90° C. The electroless solution is generally provided at a flow rate between about 50 ml/min and about 2000 ml/min. In one embodiment of the present invention, a total application of between about 120 ml and about 200 ml of electroless solution was provided to deposit the electroless layer. The electroless solution generally provides for the deposition of a metal layer to a thickness of about 500 Å or less, such as between about 300 Å and about 400 Å.

[0052] An example of a cobalt electroless composition for forming a cobalt layer includes about 20 g/L of cobalt sulfate, about 50 g/L of sodium citrate, about 20 g/L of sodium hypophosphite, with sufficient potassium hydroxide to provide a pH of between about 9 and about 11 for the composition, which is applied to the substrate surface for about 120 seconds at a flow rate of about 750 ml/min at a composition temperature of about 80° C. A cobalt-tungsten layer is deposited by the addition of about 10 g/L of sodium tungstate.

[0053] An example of a cobalt electroless composition for forming a cobalt layer with a borane-containing reducing agent includes about 20 g/L of cobalt sulfate, about 50 g/L of sodium citrate, about 4 g/L of dimetylamineborane, with sufficient potassium hydroxide to provide a pH of between about 10 and about 12 for the composition, which is applied to the substrate surface for about 120 seconds at a flow rate of about 750 ml/min at a composition temperature of about 80° C. A cobalt-tungsten-boron layer is deposited by the addition of about 10 g/L of sodium tungstate.

[0054] Borane-containing reducing agents in the metal electroless deposition process allow electroless deposition on exposed conductive material without the need for an initiation layer. When an initiation layer is first deposited on the substrate surface prior to the metal electroless deposition, the process is typically performed in two processing chambers. When the metal electroless deposition process occurs without the initiation layer, such as with the use of borane-containing reducing agents in the metal electroless deposition, the electroless process can be performed in one chamber.

[0055] Additionally, the method of depositing the material from an electroless solution, whether the initiation layer or metal layer, may include applying a bias to a conductive portion of the substrate structure if available (i.e. a seed layer), such as a DC bias, during the electroless deposition process.

[0056] The initiation layer and/or metal passivating layer may be annealed (i.e., heated) at a temperature between about 100° C. to about 400° C. The anneal may be performed in a vacuum or in a gas atmosphere, such as a gas atmosphere of one or more noble gases (such as Argon, Helium), nitrogen, hydrogen, and mixtures thereof.

[0057] Suitable apparatus for performing electroless deposition processes include an Electra Cu™ ECP processing platform or Link™ processing platform that are commercially available from Applied Materials, Inc., located in Santa Clara, Calif. The Electra Cu™ ECP platform, for example, includes an integrated processing chamber capable of depositing a conductive material by an electroless process, such as an electroless deposition processing (EDP) cell, which is commercially available from Applied Materials, Inc., located in Santa Clara, Calif. The Electra Cu™ ECP platform generally includes one or more electroless deposition processing (EDP) cells as well as one or more pre-deposition or post-deposition cell, such as spin-rinse-dry (SRD) cells, etch chambers, or annealing chambers.

[0058] Suitable apparatus for deposition of dielectric films are the Producer™ CVD and PECVD systems, available from Applied Materials, Inc., located in Santa Clara, Calif. The Producer™ systems use a multichamber architecture in a design that transfers wafers in pairs to process modules; each module has two identical chambers that use common vacuum and gas delivery subsystems. In addition to handling the full range of conventional dielectric CVD and PECVD applications, the Producer™ system deposits DARC™, damascene nitride and low k films such as TEOS FSG, Black Diamond™ and BLOk™ (Barrier Low k).

[0059] Etching processes, including dry etch and plasma etch, can be carried out on an eMax™ etching system available from Applied Materials, Inc., located in Santa Clara, Calif. The system includes a low pressure/high gas flow regime, controllable magnetic field, and high rf power capability. The eMax™ system integrates etch, photoresist strip and barrier removal steps on a single system. Etch rates of over 6000 angstroms/min. is possible. Wet etch or wet cleaning processes can be accomplished on an Oasis Clean™ system, also available from Applied Materials, Inc., CA. The apparatus uses both ultrasonic cleaning and wet chemical cleaning processes to clean substrate surfaces.

[0060] A suitable integrated controller and polishing apparatus is the Mirra™ with iAPC or Mirra Mesa™ with iAPC, also available from Applied Materials, Inc., CA.

[0061] FIGS. 2A-2E illustrate an exemplary process for selective metal encapsulation of a conductive element according to one or more embodiments of the present invention. Device 200 is shown in FIG. 2A having a substrate 210 containing conductive element 220 therein. The features of device 200 represent only a portion of the device and the actual device may include additional layers and/or additional device features. Furthermore, the conductive element is represented in cross-section as a trench, however, is it within the scope of the invention for the conductive element to comprise a variety of shapes or forms and to perform a variety of functions. By way of example only, the conductive element can be an interconnect feature such as a plug, via, trench, contact, line, wire, and may also form part of a metal gate electrode. It can also be a metal film covering a substantial portion of the substrate surface. The conductive element is made up of a conductive material, e.g., a metal having high conductivity, for example, copper.

[0062] The metallic conductive element is formed in the substrate using, for example, selective electroless metallization, in which the conductive metal is catalytically deposited from a metal ion solution without the application of an electrical current. Because the conductive metals, and copper in particular, tend to diffuse into adjacent dielectric materials such as SiO2, it is common practice to line the via opening 220 with a diffusion barrier layer (not shown) such as titanium nitride, titanium tungsten, tantalum, tantalum nitride and tungsten nitride. In addition, the diffusion barrier layer is activated, for example by the deposition of a seed layer of palladium or displacement reaction with copper, to promote the autocatalytic deposition of copper. Other methods of metallic deposition include physical vapor deposition methods such as sputter deposition from the appropriate target. CMP techniques are used to polish away unwanted conductive metal and to prepare the substrate for deposition of the passivating layer.

[0063] The surface can be further treated to clean the substrate surface of contaminants using techniques known in the art. Wet etching techniques using HF solution and dry etch techniques using HF vapor are suitable for removing dielectric materials, such as silicon oxide, from the substrate surface. Other etching techniques include downstream or remote plasma etching using a hydrogen and water plasma or a hydrogen plasma and in situ etch processes using hydrogen, hydrogen and nitrogen, or ammonia to remove metal oxides from the substrate surface. CMP is suitable for removal of various materials, including metals and dielectric materials. Other exemplary surface treatments include cleaning with an acidic solution to remove metal oxides and other contaminants from the substrate surface. The exposed conductive feature can also be rinsed with distilled water to remove residual contaminants from the surface treatment process.

[0064] After substrate surface preparation, a sacrificial protective layer 230 is deposited on the substrate surface, as is illustrated in FIG. 2B. The protective layer can be deposited by any method that is compatible with the device fabrication process and can be made up of any material that can be incorporated into the device fabrication process without detriment to the subsequent processing steps.

[0065] In exemplary embodiments, the protective layer is a photoresist, which can be applied to the substrate as a spin-on layer at a thickness of about 1000 Å to about 5000 Å. Subsequently, the photoresist is exposed and developed to define one or more openings 240 that provides access to the underlying conductive element(s) 220, as is shown in FIG. 2C. A thin layer 250 of passivation material is deposited on conductive element 220 by electroless deposition as described above and as shown in FIG. 2D. The passivating layer can be less than about 400 Å and can have a thickness in the range of about 30 Å to about 300 Å in at least some embodiments. The passivating layer may be deposited in two steps by first depositing an initiation layer, followed by depositing a conductive passivating layer. Alternatively, the passivating layer may be deposited in a single step directly onto the conductive element. Regardless of the method of passivating layer deposition, random nucleation sites 255 of the passivating metal also form on the protective layer 230. In a subsequent step shown in FIG. 2E, the photoresist 230 is lifted off of the substrate surface so that unwanted nucleation sites 255 are removed and the passivating layer 250 remains only on the conductive element 220. The photoresist is removed by conventional processes, such as wet etch or ashing, that is selected to remove the photoresist without negative effect on the underlying intermediate layer(s) or substrate surface. The substrate can be cleaned using wet solvent that does not dissolve the passivating layer. The device is then further processed consistent with its intended function.

[0066] The above procedure is attractive because it does not require the use of a high k dielectric material adjacent to the conductive element. Low k materials, e.g., polyarylethers, fluorinated polyarylethers, polyimides and fluorinated polyimides, benzocyclobutenes, carbon-doped oxides, organic and inorganic porous low k materials and hybrids thereof, and the like, can be directly applied to the substrate surface after completion of the processing steps set forth in FIGS. 2A-2E to provide improved electrical isolation between adjacent conductive regions of an integrated circuit that is advantageous in many semiconductor devices.

[0067] In another exemplary embodiment, the protective layer 230 is a dielectric barrier layer such as an etch stop layer. Exemplary etch stop materials include SiN or SiOC available from Applied Materials, Inc., located in Santa Clara, Calif., under the tradename Blok™. The etch stop layer (or other dielectric) is deposited as a thin layer, e.g., about 50 Å, over the substrate surface by, for example, PECVD or spin-on polymer deposition. Alternatively, a thick layer of dielectric material is deposited and is etched or polished back to a very thin protective layer, for example about 50 Å. The thinness of the protective layer is chosen to reduce the amount of high k material deposited on the metallic conductive element and thereby reduce interlayer capacitance. The conductive element is exposed by removing, i.e., etching, the dielectric layer in those areas not protected by a photomask (not shown) to define one or more openings 240 that exposes the underlying conductive element 220, as is shown in FIG. 2C. A passivating layer 250 is deposited as described above. The dielectric barrier (protecting layer) or at least a portion of the protecting layer is then removed along with surface contaminates 255. In one or more other exemplary embodiments, only a portion of the dielectric layer is removed (sufficient to remove stray electrolessly deposited sites 255), and additional dielectric material is deposited on the remaining dielectric layer to a final thickness. The final thickness is desirably low to minimize the effects of the high k material, and can be in the range of about 600 Å. The device is then further processed consistent with its intended function.

[0068] In another embodiment of the present invention, the protective layer 230 is an amorphous carbon layer. In one or more embodiments, the amorphous carbon layer is deposited onto the substrate surface, for example, by CVD or spin-on polymer deposition to a thickness of about 100 Å to about 5000 Å. The conductive element is exposed by masking the amorphous carbon film and developing the photoresist to expose the underlying amorphous carbon film. The carbon film is then removed, e.g., by etching, in those areas not protected by the photomask (not shown) to define one or more openings 240 that exposes the underlying conductive element(s) 220, as is shown in FIG. 2C. A passivating layer 250 is deposited as described above. The amorphous carbon layer is then removed along with surface contaminates 255 to eliminate stray electrolessly deposited passivation material (and other contaminants). Amorphous carbon can be removed by ashing, plasma ashing and wet or dry chemical etching. As with the use of a photoresist, the process results in the complete removal of the amorphous carbon film, so that no high k dielectric material remains adjacent to the conductive elements. The device is then further processed consistent with its intended function.

[0069] In another exemplary embodiment of the present invention, intermediate layers may be deposited between the substrate surface and the protective layer. FIGS. 3A-3F illustrate an exemplary process for such an integration scheme using a conductive passivating layer. Device 300 is shown in FIG. 3A having a substrate 310 containing a conductive element 320 therein. As noted above, the features of device 300 represent only a portion of the device and the actual device may include additionally layers and/or additional device features.

[0070] A sacrificial protective layer 330 is deposited on the substrate surface, as is illustrated in FIG. 3B. Prior to deposition of the protective layer, one or more intermediate layer(s) 335 is deposited on the substrate surface. The protective and intermediate layers can be any of the materials and layers described above, and can be deposited according to any of the method described herein or any other conventional technique. In an exemplary embodiment, the protective layer is a photoresist and the intermediate layer is a dielectric material such as an etch stop.

[0071] As is shown in FIG. 3B, dielectric material 335 is deposited over the substrate surface 310, e.g., by PECVD or spin-on polymer deposition, to a thickness of about 50 to about 1000 Å. A photoresist layer 330 then is applied to the intermediate layer as a spin-on layer at a thickness of about 1000 Å to about 5000 Å. Subsequently, the photoresist is exposed and developed to define one or more openings 340 that exposes the underlying intermediate layer 335 above the conductive element 320, as is shown in FIG. 3C. The conductive element is exposed by removing, i.e., etching, the dielectric layer in those areas not protected by a protective layer 330 to define one or more openings 345 that exposes the underlying conductive element 320, as is shown in FIG. 3D. In one or more embodiments of the present invention, the etch is selective for the intermediate layer 335, so that protective layer 330 is not affected by the etch process. In one or more embodiments, the photomask is removed only after etching of both the protective and intermediate layers.

[0072] A thin layer 350 of passivation material is deposited on conductive element 320 by electroless deposition as described above and as shown in FIG. 3E. The passivating layer can be less than about 400 Å, and has a thickness in the range of about 30 Å to about 300 Å in exemplary embodiments. The passivating layer 350 can be of the same or different thickness as the dielectric layer 335. The passivating layer may be deposited in two steps by depositing an initiation layer, followed by depositing the conductive passivating layer. Alternatively, the passivating layer may be deposited in a single step directly onto the conductive element. Regardless of the method of passivating layer deposition, random nucleation sites 355 of the passivating metal also form on the protective layer. In a subsequent step shown in FIG. 3F, the protective layer 330 (e.g., photoresist), including unwanted nucleation sites 355, is lifted off of the substrate surface, leaving the passivating layer 350 only on the conductive element 320. The photoresist is removed by conventional processes, such as wet etch or ashing, that is selected to remove the photoresist without negative effect on the underlying dielectric materials of the intermediate layer(s) or substrate surface. Upon removal of the photoresist layer, dielectric layer 335 covers the remaining surface of the substrate 310. In those embodiments where the dielectric layer 335 and the passivating layer 350 are of the same thickness, a smooth planar substrate surface containing the passivating layer embedded in a dielectric is obtained, as illustrated in FIG. 3F. The substrate can be cleaned using wet solvent that does not dissolve the passivating layer. The device is then further processed consistent with its intended function.

[0073] FIGS. 4A-4D illustrate still another embodiment of the present invention. FIG. 4A shows a device 400 including a first lower layer 430 of a first dielectric material and a second upper layer 440 of a second dielectric material deposited on a substrate 410. The device also includes a conductive element 420 embedded in the second dielectric/first dielectric/substrate composite. The layers are deposited and processed using conventional methods. The first and second materials of dielectric layers 430, 440 are selected to have different etching chemistries so that one layer is inert to etching under conditions that etch the other layer. Exemplary first and second dielectric materials include organic dielectrics such as organic low k materials and inorganic dielectrics such as carbon-doped oxides, SiOC, fluorine-doped silicon glass (FSG), and silicon oxide-based low k materials such as Black Diamond™ available from Applied Materials, Inc., located in Santa Clara, Calif. In an exemplary embodiment, the upper dielectric layer 440 is an organic low k material and the lower dielectric layer 430 is a carbon-doped oxide. In one or more embodiments, the upper and lower dielectric materials are the same, and an intermediate surface is treated to alter the etching characteristics of the layer. Exemplary treatments that alter etching properties of the layer include inert gas plasma treatments. The surface treated substrate acts as an etch stop. The surface treatment can be applied in a separate step or as an integral part of the deposition process for dielectric layers.

[0074] Referring to FIG. 4B, the device is processed by CMP to remove a portion of the upper dielectric layer 440 and conductive element 420 from the substrate surface. In an exemplary embodiment, the dielectric layer 440 has a thickness of about 100 Å to about 400 Å after CMP processing. The surface is then cleaned as described above, for example, with an acid bath to remove residual traces of metal on the substrate surface. Subsequently, a passivating layer is deposited on the substrate surface using electroless deposition as described herein. The resultant layer forms a continuous passivating layer 450 on the conductive element and random discontinuous islands 455 of passivation material on the dielectric layer 440, as is shown in FIG. 4C. The device is then exposed to an etchant that selectively removes the remaining traces of dielectric layer 440. The final device includes a clean dielectric layer 430 in which a conductive metal layer 450 is embedded. In one or more embodiments, the metallic passivating layer (and a portion of the conductive element) may extend above the plane of the substrate surface. The device is then further processed consistent with its intended function.

[0075] One or more embodiments of the present invention also contemplate methods of encapsulating a conductive element using a conductive passivating layer without the need for first depositing a sacrificial protective layer. According to one or more embodiments of the present invention, a conductive element is encapsulated without stray electoless deposition of passivating metal elsewhere on the substrate surface by depositing a layer of the passivation material over the entire substrate surface or a portion thereof containing the conductive element(s), masking the passivation layer to protect the underlying conductive element(s) and removing the unmasked passivation material from the substrate surface to reveal the underlying substrate or other underlying intermediate layers. One or more embodiments of the present invention contemplate the deposition of an intermediate layer onto the substrate surface prior to deposition of the metallic passivating layer. The mask is subsequently removed to obtain the selectively encapsulated metal device, in which the surrounding substrate surface areas are substantially free of contaminants arising from the deposition of the passivating layer.

[0076] FIG. 5 is a flow chart illustrating an exemplary processing sequence 500 undertaken in encapsulating a conductive element with conductive passivating layer according to one or more embodiments of the present invention.

[0077] In step 510 in FIG. 5, a substrate surface is prepared as previously described by treating the substrate surface so as to expose the conductive element. The substrate surface can be treated using materials removal and cleaning techniques known in the art. Exemplary materials removal techniques include chemical mechanical polishing (CMP) and etching. Wet etching techniques using HF solution and dry etch techniques using HF vapor are suitable for removing dielectric materials, such as silicon oxide, from the substrate surface. Other etching techniques include downstream or remote plasma etching using a hydrogen and water plasma or a hydrogen plasma and in situ etch processes using hydrogen, hydrogen and nitrogen or ammonia to remove metal oxides from the substrate surface. CMP is suitable for removal of various materials, including metals. Other exemplary surface treatments include ultrasonication and cleaning with an acidic solution to remove metal oxides and other contaminants from the substrate surface. The exposed conductive feature can also be rinsed with distilled water to remove residual contaminants from the surface treatment process.

[0078] A conductive passivating layer then is deposited on the substrate surface in step 530 of FIG. 5. The conductive passivation material is generally a metal that does not form a solid solution with copper or other conductive metals, such as ruthenium, tantalum, tungsten, cobalt, palladium, nickel, tin, titanium, molybdenum, platinum, iron, and niobium and their alloys. In one or more embodiments, the passivating conductive metal is cobalt or a cobalt alloy. One or more embodiments contemplate the deposition of the conductive passivation layer as a continuous film across the substrate surface. The continuous film is deposited, for example, physical deposition techniques such as sputter deposition using a suitable target.

[0079] In step 540 of FIG. 5, the passivating layer is masked in a pattern of the underlying conducting elements. The passivating layer can be masked with photoresist, which is developed to remove selected areas of the photoresist film so that the underlying conductive elements are protected and the surrounding dielectric regions are exposed. The photoresist can be a positive photoresist, in which case the exposed areas of a positive resist film are removed by the process of development. Alternatively, the photoresist can be a negative photoresist, in which case the mask pattern is a negative of the underlying conductive layer structure and the unexposed areas of the resist film are removed by the process of development.

[0080] In step 550 of FIG. 5, the exposed passivating layer is then etched to selectively remove the unmasked passivating layer and to expose the underlying substrate surface. Exemplary etching processes for removal of cobalt includes etching at elevated temperatures, e.g., of greater than 120° C., using Cl2 gas, and including CO, CF4 or N2 gas for passivation. The etching process is selective for the metallic passivation material and leaves the substrate surface free of passivation material (and other contaminants) without deleterious effect to the substrate, i.e., the dielectric regions or conductive elements of the substrate.

[0081] The protective mask is then removed or lifted to expose the encapsulating passivating layer, as is shown in step 560. Materials removal techniques known in the art can be used. Wet etching and ashing can be used for the removal of the photoresist. The device also can be rinsed with distilled water to remove residuals from the materials removal process.

[0082] FIGS. 6A-6D illustrate an exemplary process for selective metal encapsulation of a conductive element according to one or more embodiments of the present invention. Device 600 is shown in FIG. 6A having a substrate 610 containing conductive element 620 therein. As above, the features of device 600 illustrate only a portion of the device and the actual device may include additional layers and/or additional device features. The metallic conductive element can be prepared as previously described or according to known methods in the art.

[0083] A thin layer 630 of passivation material is deposited as a continuous layer on substrate surface 610 as shown in FIG. 6B, thereby encapsulating at least the conductive element 620. The passivating layer can cover the entire substrate surface, or a selected region thereof; however, the deposited passivating layer should cover at least the conductive element(s). The passivating layer can be less than about 400 Å and has a thickness in the range of about 30 Å to about 300 Å in some embodiments. The passivating layer can be deposited using physical vapor deposition techniques such as sputtering. In sputtering, a target of a composition commensurate with the desired composition of the passivating layer is bombarded with a sputtering gas, typically an inert gas, to remove atoms from the target, which are then deposited on the substrate surface. A suitable apparatus for sputter deposition is the Endura™ processing system, available from Applied Materials, Inc., located in Santa Clara, Calif.

[0084] A photoresist 640 is deposited and developed as shown in FIG. 6C to mask the underlying conductive element 620 of the substrate surface. The photoresist can be applied to the substrate as a spin-on layer and developed using conventional techniques. The surface is then etched as shown by arrows 650 to remove exposed passivation material 655 and to uncover the underlying regions of the substrate surface 610. Exemplary etch process suitable for metals etching include the use of decoupled plasma source (DPS) technology. Suitable apparatus for metal etching of cobalt (or other passivating metals) includes the Centura System using Metal Etch DPS processing platform, available from Applied Materials located in Santa Clara, Calif.

[0085] In a subsequent step shown in FIG. 6D, the photoresist 640 is lifted off to reveal passivating layer 660 and to provide a passivating layer-encapsulated conductive element 665 in which the surrounding substrate surface is substantially free of surface contaminations.

[0086] Although various embodiments that incorporate the teachings of the present invention have been shown and described in detail herein, those skilled in the art can readily devise many other varied embodiments that incorporate these teachings, including embodiments with numerical values and ranges differing from those set forth herein. It is appreciated that the figures and discussion herein illustrate only a portion of an exemplary semiconductor device. Thus, the present invention is not limited to only those structures described herein.

Claims

1. A method of processing a semiconductor substrate, comprising the steps of: depositing a protective layer on a substrate surface comprising a conductive element; selectively removing a portion of the protective layer to expose the conductive element of the substrate surface; depositing a metallic passivating layer onto the exposed conductive element; and removing at least a portion of the protective layer from the substrate after deposition of the metallic passivating.

2. The method of claim 1, wherein the substrate surface comprises a dielectric material in which the conductive element is disposed.

3. The method of claim 1, wherein the substrate surface comprises a low k dielectric material.

4. The method of claim 1, wherein a portion of the thickness of the protective layer is removed.

5. The method of claim 1, wherein the entire thickness of the protective layer is removed.

6. The method of claim 1, wherein the substrate surface is treated to expose the conductive element prior to deposition of the protective layer.

7. The method of claim 1, wherein the step of depositing a protective layer is accomplished using a technique selected from the group consisting of chemical vapor deposition (CVD), plasma enhance chemical vapor deposition (PECVD), spin on deposition and physical vapor deposition.

8. The method of claim 1, wherein the protective layer comprises an organic material.

9. The method of claim 8, wherein the organic material of the layer is selected from the group consisting of photoresist and amorphous carbon.

10. The method of claim 9, wherein the steps of depositing and processing the photoresist protective layer comprise the steps of: depositing a photoresist over the substrate surface; and exposing and developing the photoresist under conditions that do not degrade the substrate surface to expose a selected region of an underlying layer.

11. The method of claim 10, wherein the exposed and developed photoresist is removed after deposition of the metallic passivating layer by ashing or wet chemical etch.

12. The method of claim 9, wherein the steps of depositing and processing the amorphous carbon protective layer comprise the steps of: depositing an amorphous carbon layer over the substrate surface; and etching the amorphous carbon layer under conditions that do not degrade the substrate surface.

13. The method of claim 12, wherein the amorphous carbon layer is removed after deposition of the metallic passivating layer by ashing or reactive ion etch.

14. The method of claim 1, wherein the protective layer comprises a dielectric material.

15. The method of claim 14, wherein steps of depositing and processing the dielectric protective layer comprise the steps of: depositing a dielectric layer over the substrate surface; and selectively etching the dielectric layer under conditions that do not degrade the substrate surface.

16. The method of claim 15, wherein the dielectric protective layer is removed after deposition of the passivating layer by etching using a technique selected from the group consisting of wet etch, dry etch, reactive ion etch and plasma etch.

17. The method of claim 1, where steps for depositing and processing the protective layer comprise the steps of: depositing an intermediate layer on the substrate surface; depositing a protective layer on the intermediate layer; selectively removing the protective layer to expose the intermediate layer; and selectively removing the intermediate layer under conditions that do not degrade the conductive element.

18. The method of claim 17, wherein the intermediate layer comprises an etch stop and the protective layer comprises a photoresist.

19. The method of claim 17, wherein the intermediate layer comprises a dielectric material.

20. The method of claim 1, wherein the conductive material comprises copper.

21. The method of claim 1, wherein the passivating layer is selected from the group consisting of ruthenium, tantalum, tungsten, cobalt, palladium, nickel, tin, titanium, molybdenum, platinum, iron, and niobium, and alloys thereof.

22. The method of claim 1, wherein the step of depositing a metallic passivating layer comprises electroless deposition.

23. The method of claim 22, wherein the step of electrolessly depositing a metallic passivating layer comprises the steps of: depositing an initiation layer on the first conductive material by exposing the substrate to an activation solution; cleaning the substrate after deposition of the initiation layer; and depositing a metallic passivating layer on the initiation layer by exposing the initiation layer to an electroless solution.

24. A method of processing a semiconductor substrate, comprising: steps for depositing a protective layer on the substrate surface comprising a conductive element disposed in a dielectric material; steps for processing the protective layer to expose the conductive element; steps for depositing a metallic passivating layer onto the conductive element; and steps for removing at least a portion of the protective layer from the substrate after electroless deposition.

25. The method of claim 24, wherein the step of depositing a metallic passivating layer comprises the steps of: steps for depositing an initiation layer on the first conductive material by exposing the substrate to an activation solution; steps for cleaning the substrate after deposition of the initiation layer; and steps for depositing a metallic passivating layer on the initiation layer by exposing the initiation layer to an electroless solution.

26. The method of claim 24, where steps for depositing and processing the protective layer comprise the steps of: steps for depositing an intermediate layer on the substrate surface; steps for depositing a protective layer on the intermediate layer; steps for exposing and developing the protective layer to expose the intermediate layer; and steps for etching the intermediate layer under conditions that do not degrade the conductive element.

27. The method of claim 24, wherein steps for depositing and processing an amorphous carbon protective layer comprise the steps of: steps for depositing an amorphous carbon layer over the substrate surface; and steps for etching the amorphous carbon layer under conditions that do not degrade the conductive element.

28. The method of claim 24, wherein the steps for depositing and processing a photoresist protective layer comprise the steps of: steps for depositing a photoresist over the substrate surface; and steps for exposing and developing the photoresist under conditions that do not degrade the conductive element.

29. The method of claim 24, wherein the steps of depositing and processing a dielectric protective layer comprise the steps of: steps for depositing a dielectric protective layer over the substrate surface; and steps for etching the dielectric protective layer under conditions that do not degrade the conductive element.

30. A system for processing a semiconductor substrate, comprising: means for depositing a protective layer on the substrate surface comprising a conductive element disposed in a dielectric material; means for processing the protective layer to expose the conductive element; means for electrolessly depositing a metallic passivating layer onto the conductive element; and means for removing at least a portion of the protective layer from the substrate after electroless deposition.

31. The system of claim 30, wherein the steps for depositing and processing a photoresist protective layer comprises the steps of: means for depositing a photoresist over the substrate surface; and means for exposing and developing the photoresist under conditions that do not degrade the conductive element.

32. The system of claim 30, wherein the step of electrolessly depositing a metallic passivating layer comprises the steps of: means for depositing an initiation layer on the first conductive material by exposing the substrate to an activation solution; means for cleaning the substrate after deposition of the initiation layer; and steps for depositing a metallic passivating layer on the initiation layer by exposing the initiation layer to an electroless solution.

33. The system of claim 30, where steps for depositing and processing the protective layer comprises the steps of: means for depositing an intermediate layer on the substrate surface; means for depositing a protective layer on the intermediate layer; means for exposing and developing the protective layer to expose the intermediate layer; and means for etching the intermediate layer under conditions that do not degrade the conductive element.

34. The system of claim 30, wherein steps for depositing and processing an amorphous carbon protective layer comprises the steps of: means for depositing an amorphous carbon layer over the substrate surface; and means for etching the amorphous carbon layer under conditions that do not degrade the conductive element.

35. The system of claim 30, wherein depositing and processing a dielectric protective layer comprises: means for depositing a dielectric layer over the substrate surface; and means for etching the dielectric layer under conditions that do not degrade the conductive element.

36. A method of processing a semiconductor substrate, comprising the steps of: depositing a metallic passivating layer onto a substrate surface comprising a conductive element; masking the passivating layer to protect the underlying conductive element of the substrate surface; removing the unmasked passivating layer; and removing the mask from the passivating layer.

37. The method of claim 36, wherein the mask is removed by ashing or reactive ion etch.

38. The method of claim 36, wherein the unmasked passivating layer is removed to expose the underlying substrate surface.

39. The method of claim 36, wherein the unmasked passivating layer is removed by etching.

40. The method of claim 36, wherein the conductive material comprises copper.

41. The method of claim 36, wherein the passivating layer is selected from the group consisting of ruthenium, tantalum, tungsten, cobalt, palladium, nickel, tin, titanium, molybdenum, platinum, iron, and niobium, and alloys thereof.

42. The method of claim 36, wherein the passivating layer is deposited as a continuous film.