This application is a national stage application, filed under 35 U.S.C. §371, of International Application No. PCT/CN2011/071345, filed Feb. 26, 2011, which claims the priority of Chinese Patent Application No. 201010264536.6, filed Aug. 26, 2010, all of which are hereby incorporated by reference in their entirety.
The present invention generally relates to a semiconductor device structure and a method for manufacturing the same, and specifically, to a semiconductor device structure with an interconnect structure of better performance and a method for manufacturing the same.
With the rapid development of the semiconductor technology, integrated circuits with better performance and more powerful functions require greater element density, thus the sizes of CMOS (Complementary Metal Oxide Semiconductor) devices and of components such as metal wirings have to be further scaled, so as to enable the devices to run increasingly faster. However, the scaling in the sizes of metal wirings also results in increase of resistance of the metal wirings, which may consequently cause such a problem that the signal transmission speed of the metal wirings lags behind the operation speed of the devices.
As the industry comes into the nanometer era, the sizes of the devices are further scaled, the local interconnect structures, including incorporated vias and metal wirings, are replaced by the metal Cu or other materials which have smaller resistance rate but better anti-electro-migration capability. Nonetheless, metal ions in these metal materials would easily diffuse into the semiconductor structure, and thus cause shorts in the device structure or other problems of poor performance.
Accordingly, in order to solve the above mentioned problems existing in the interconnect structures, there is a need for a novel semiconductor device structure and a method for manufacturing the same structure.
The present invention provides A method for manufacturing a semiconductor structure, comprising: providing a semiconductor substrate on which a device structure is formed; forming an interlayer dielectric layer on the device structure, and patterning the interlayer dielectric layer to form a trench which comprises an incorporated via trench and a conductive wiring trench, wherein the conductive wiring trench is positioned on the via trench; and forming a conductive layer within the trench to fill up the trench, wherein the conductive layer is electrically connected with the device structure; wherein the conductive layer comprises a conductive material and a nanotube/wire layer surrounded by the conductive material.
The present invention further provides a semiconductor structure manufactured in accordance with the aforesaid method; the structure comprises: a semiconductor substrate on which a device structure is formed thereon; an interlayer dielectric layer formed on the device structure, wherein a trench is formed in the interlayer dielectric layer, the trench comprises an incorporated via trench and a conductive wiring trench, and the conductive wiring trench is positioned on the via trench; and a conductive layer filled in the trench, wherein the conductive layer is electrically connected with the device structure; wherein the conductive layer comprises a conductive material and a nanotube/wire layer surrounded by the conductive material.
In the embodiments of the present invention, the metal wiring and the interconnect structure with incorporated vias, which are formed according to the method for manufacturing a semiconductor structure, are formed with a conductive material and a nanotube/wire layer surrounded by the conductive material; since the nanotube/wire has unique physical structure and physical and chemical properties, it enables the conductive layer to have better thermal conductivity, conductivity and high anti-electromigration capability, thereby improving the signal transmission speed at the conductive layer, which thus enables its signal transmission speed to match with the increasingly enhanced speed of the devices. Besides, since the carbon nanotube/wire is a structure formed by single-layer carbon atoms or metal atoms, thus it is favorable for preventing the metal or other ions within the conductive material from diffusing into other places in the semiconductor structure, and is able to provide an interconnect structure of high quality, and also is able to reduce short circuits taking place in the semiconductor structure.
The present invention generally relates to a method for manufacturing a semiconductor structure. The following disclosure provides a plurality of different embodiments or examples to achieve different structures of the present invention. To simplify the disclosure of the present invention, description of components and arrangements of specific examples is given. Of course, they are only illustrative and not limiting the present invention. Moreover, in the present invention, reference number(s) and/or letter(s) may be repeated in different embodiments. Such repetition is for the purposes of simplification and clearness, and does not denote the relationship between the respective embodiments and/or arrangements being discussed. In addition, the present invention provides various examples for specific processes and materials. However, it is obvious for a person of ordinary skill in the art that other processes and/or materials may alternatively be utilized. Furthermore, the following structure in which a first object is “on” a second object may include an embodiment in which the first object and the second object are formed to be in direct contact with each other, and may also include an embodiment in which another object is formed between the first object and the second object such that the first and second objects might not be in direct contact with each other.
The device structure may comprise a transistor, a diode or other semiconductor assembly, and other electronics device(s) or interconnect structure(s), etc. With reference to
In step S02, an interlayer dielectric layer 310 is formed on the device structure 300, and then the interlayer dielectric layer 310 is patterned to form a trench 320 which comprises an incorporated via trench 320-1 and a conductive wiring trench 320-2, as shown in
It can be seen from
Optionally, after formation of the trench 320, an insulating layer (not shown in the figures) may be formed on its sidewalls. The insulating layer may comprise nitride, oxide, or any other appropriate material, so as to prevent metal ions in a conductive layer to be formed subsequently from diffusing into the semiconductor structure.
Preferably, after formation of the trench 320 or the insulating layer, a barrier layer 330 may be formed at the bottom and the sidewalls of the trench 320, as shown in
In step S03, a conductive layer is formed within the trench 320 to fill up the trench 320, wherein the conductive layer comprises a conductive material 340 and a nanotube/wire layer 350 surrounded by the conductive material 340.
Specifically, a conductive material, for example a metal material such as a copper (Cu) seed layer 340, may be deposited on the barrier layer 330 by a process such as CVD (Chemical Vapor Deposition). The metal material may further comprise Al, W or other materials as appropriate. Then, a carbon nanotube/wire layer 350 is formed on the copper (Cu) seed layer 340. With the direction of the bottom surface of the trench 320 in a horizontal direction as the reference direction, in an embodiment, the carbon nanotube/wire layer 350 may be a nanotube/wire in the horizontal direction, as shown in
The conductive material may be formed by PVD, CVD, Atomic Layer Deposition (ALD), PLD (Pulsed Laser Deposition), Metal Organic Chemical Vapor Deposition (MOCVD), Plasma Enhanced ALD (PEALD), sputtering, Molecular Beam Epitaxy (MBE), etc. The carbon nanotube/wire may be formed by methods such as CVD, Arc discharge, or laser ablation or any other processes as appropriate. The metal nanotube/wire may be formed by means of, for example, hard/soft template process, optical/electrochemical reduction process, seed mediated growth method or any other methods as appropriate. The forming of a carbon nanotube/wire may refer to the prior art and thus is omitted here.
Next, a metal material 340 such as Cu, Al or W is formed on the nanotube/wire mesh. In an embodiment, Cu is partially filled into the trench, for example, by plating, as shown in
Then, another carbon nanotube/wire layer 350 is formed on the metal material. Similar to the aforesaid carbon nanotube/wire layer, the carbon nanotube/wire layer 350 may be a nanotube/wire in the vertical direction, a nanotube/wire in the horizontal direction, or a nanotube/wire mesh, on which the metal material 340 such as Cu is filled. The carbon nanotube/wire layer and the filling metal material 340 may be formed repeatedly as appropriate to fill up the trench 320, as shown in
Then, the metal material is planarized by means of such as Chemical-mechanical polishing (CMP) so that the conductive layer may be substantially flushed with the interlayer dielectric layer, as shown in
Then, the subsequent process steps may be performed as needed. For example, another interconnect structure, another interlayer dielectric layer or other components may be formed thereon.
Besides forming one metal layer, the method for manufacturing a semiconductor device structure of the embodiment for the present invention may be performed both for manufacturing of the first metal layer and for manufacturing of other metal layers in Back end of line (BEOL). The foregoing embodiments are not for limiting the present invention.
According to the aforesaid method, the present invention further provides a semiconductor device structure formed by means of the aforesaid method, as shown in
The device structure may comprise a transistor, a diode or other semiconductor components, and other electronic devices or interconnect structures, etc. With reference to
The semiconductor device structure of the embodiment of the present invention may be applied to the first metal layer and the subsequent metal layers. The embodiment shown in
The semiconductor device structure having an incorporated interconnect structure with a nanotube/wire layer and the method for manufacturing the same is described in detail. A conductive layer i.e. an interconnect structure, which comprises a metal material and a nanotube/wire layer surrounded by the metal material is formed, so that the conductive layer has better thermo-conductivity, conductivity and high anti-electromigration capability due to the particular electrical-physical structure and physicochemical properties of the nanotube/wire, thus the signal transmission speed of the conductive layer is improved, and the signal transmission speed may be matched with the increasingly enhanced device speed. Additionally, because the carbon nanotube/wire is a structure formed by single-layer C atoms or metal atoms, it is quite favorable for preventing the metal ions or other ions in the conductive material from diffusing into other places in the semiconductor structure, and is able to provide an interconnect structure of high quality, and reduce shorts in the semiconductor structure.
Although the embodiments and their advantages have been described in detail, it is readily apparent to those having ordinary skill in the art that various alterations, substitutions and modifications may be made to the embodiments without departing from the spirit of the present invention and the scope as defined by the appended claims. For other examples, it may be easily recognized by a person of ordinary skill in the art that the order of the process steps may be changed without departing from the scope of the present invention.
In addition, the scope to which the present invention is applied is not limited to the process, mechanism, manufacture, material composition, means, methods and steps described in the specific embodiments in the specification. A person of ordinary skill in the art would readily appreciate from the disclosure of the present invention that the process, mechanism, manufacture, material composition, means, methods and steps currently existing or to be developed in future, which perform substantially the same functions or achieve substantially the same as that in the corresponding embodiments described in the present invention, may be applied according to the present invention. Therefore, it is intended that the scope of the appended claims of the present invention includes these process, mechanism, manufacture, material composition, means, methods or steps.
Number | Date | Country | Kind |
---|---|---|---|
2010 1 0264536 | Aug 2010 | CN | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/CN2011/071345 | 2/26/2011 | WO | 00 | 5/13/2011 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2012/024918 | 3/1/2012 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
7402909 | Suh et al. | Jul 2008 | B2 |
7468320 | Hu et al. | Dec 2008 | B2 |
7744947 | Lee et al. | Jun 2010 | B2 |
7781260 | Sane et al. | Aug 2010 | B2 |
20060281306 | Gstrein et al. | Dec 2006 | A1 |
20080157375 | Lee | Jul 2008 | A1 |
20090065932 | Sane et al. | Mar 2009 | A1 |
20090072400 | Zhu et al. | Mar 2009 | A1 |
20090108378 | Zhu et al. | Apr 2009 | A1 |
20100130005 | Lee et al. | May 2010 | A1 |
20100283093 | Pei et al. | Nov 2010 | A1 |
Entry |
---|
International Searching Authority, International Search Report for International Application No. PCT/CN2011/071345, The State Intellectual Property Office of the P.R.C., mailed May 26, 2011, 7 pages, China. |
Number | Date | Country | |
---|---|---|---|
20120193798 A1 | Aug 2012 | US |