SEMICONDUCTOR DEVICE INCLUDING GRAPHENE AND METHOD OF MANUFACTURING THE SEMICONDUCTOR DEVICE

BACKGROUND
1. Field

The present disclosure relates to a semiconductor device, and more particularly, to a semiconductor device including graphene and a method of manufacturing the semiconductor device.

2. Description of Related Art

In semiconductor device fields, a new material may be used to limit and/or prevent a resistance increase caused by a reduced width of metal wiring and/or provide a thin and new barrier material. Recently, studies on graphene are being actively conducted.

Graphene is a crystalline material having a hexagonal honeycomb structure as carbon atoms are 2-dimensionally connected, and is very thin, having a thickness of a single atom. The graphene may be synthesized via chemical vapor deposition (CVD) or obtained by detaching graphite layer by layer.

SUMMARY

Provided is a semiconductor device including graphene.

According to an aspect of the present disclosure, a semiconductor device includes: a substrate including an insulator and a semiconductor; and a graphene layer configured to directly grow only on a surface of the semiconductor, wherein the semiconductor includes at least one of a group IV material and a group Il-V compound.

The graphene layer may have a hexagonal honeycomb structure extending in parallel to the surface of the semiconductor on which the graphene layer is grown.

The group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z, wherein 0≤x, y, and z≤1. The group III-V compound may include a group III material including one or more of indium (In), gallium (Ga), and aluminum (Al), and a group V material including one or more of nitrogen (N), phosphorous (P), arsenic (As), and antimony (Sb).

The insulator may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The substrate may include a semiconductor substrate including the semiconductor and an insulating layer including the insulator and provided on the semiconductor substrate.

The substrate may include an insulator substrate including the insulator and a semiconductor layer including the semiconductor and provided on the insulator substrate.

A surface of the semiconductor and a surface of the insulator may be located on planes of a same height or of different heights.

According to another aspect of the present disclosure, a semiconductor device includes: a substrate including an insulator and a semiconductor; a first graphene layer configured to directly grow only on a surface of the semiconductor; and a second graphene layer configured to directly grow only on a surface of the insulator, wherein a thickness of the first graphene layer is greater than a thickness of the second graphene layer.

The first graphene layer may have a hexagonal honeycomb structure extending in parallel to the surface of the semiconductor on which the first graphene layer is grown, and the second graphene layer may have a hexagonal honeycomb structure extending in parallel to the surface of the insulator on which the second graphene layer is grown.

The semiconductor may include at least one of a group IV material and a group III-V compound.

A surface of the semiconductor and a surface of the insulator may be located on planes of a same height or of different heights.

BRIEF DESCRIPTION OF THE DRAWINGS

These and/or other aspects will become apparent and more readily appreciated from the following description of some example embodiments, taken in conjunction with the accompanying drawings in which:

FIG. 1 is a cross-sectional view of a semiconductor device according to some example embodiments;

FIG. 2 is a photograph of a graphene layer grown, via a plasma-enhanced chemical vapor deposition (PECVD) process, on a surface of a germanium (Ge) semiconductor layer on which a silicon oxide (SiO₂) insulating layer is patterned;

FIG. 3 is a cross-sectional view of a semiconductor device according to some example embodiments;

FIG. 4 is a cross-sectional view of a semiconductor device according to some example embodiments;

FIG. 5 is a cross-sectional view of a semiconductor device according to some example embodiments;

FIG. 6 is a cross-sectional view of a semiconductor device according to some example embodiments;

FIG. 8 is a cross-sectional view of a semiconductor device according to some example embodiments;

FIG. 9 is a cross-sectional view of a semiconductor device according to some example embodiments; and

FIG. 10 is a cross-sectional view of a semiconductor device according to some example embodiments.

DETAILED DESCRIPTION

Reference will now be made in detail to some example embodiments that are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout and sizes and thicknesses of components may be exaggerated for clarity. In this regard, the present embodiments may be embodied different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the embodiments are merely described below, by referring to the figures, to explain aspects. When a certain material layer is on a substrate or another layer, the certain material layer may be directly contact the substrate or the other layer or a third layer may exist between the certain material layer and the substrate or the other layer. Also, since a material forming each layer is an example, and thus another material may be used. Expressions such as “at least one of,” when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.

FIG. 1 is a cross-sectional view of a semiconductor device 100 according to some example embodiments.

Referring to FIG. 1, the semiconductor device 100 includes a substrate 110 and a graphene layer 130 grown on a surface of the substrate 110. Here, the substrate 110 includes two types of materials, e.g., a semiconductor and an insulator. The graphene layer 130 is grown on a surface of the semiconductor of the substrate 110.

The substrate 110 may include a semiconductor substrate 111 and an insulating layer 112 provided on a surface (for example, on a top surface) of the semiconductor substrate 111. The insulating layer 112 may be patterned in a certain shape on the surface of the semiconductor substrate 111. Here, the surface of the semiconductor substrate 111 and a surface of the insulating layer 112 may be provided on planes having different heights.

The semiconductor substrate 111 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z(0<x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of indium (In), gallium (Ga), and aluminum (Al), and a group V material including one or more of nitrogen (N), phosphorous (P), arsenide (As), and antimony (Sb). However, a material of the semiconductor substrate 111 is not limited thereto, and the semiconductor substrate 111 may include any one of various semiconductor materials.

Meanwhile, the semiconductor substrate 111 may further include a doping material. The doping material may include at least one of boron (B), As, P, Sb, carbon (C), Si, or magnesium (Mg). However, the doping material is not limited thereto. Here, concentration of the doping material may be, for example, from about 10¹⁵to 10²²cm⁻³.

The insulating layer 112 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0<x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The graphene layer 130 is formed on an exposed surface of the semiconductor substrate 111. Here, the graphene layer 130 may include one graphene layer or a plurality of stacked graphene layers. Graphene is a crystalline material having a hexagonal honeycomb structure in which carbon atoms are two-dimensionally connected. Graphene is in the limelight as a material applicable to various devices due to various characteristics, such as a very thin thickness of an atom size level, excellent electric conductivity, a strong mechanical characteristic, and chemical stability.

The graphene layer 130 may be grown on the surface of the semiconductor substrate 111 via a plasma-enhanced chemical vapor deposition (PECVD) process described later. According to some example embodiments, the graphene layer 130 is not formed on the surface of the insulating layer 112, but is formed only on the exposed surface of the semiconductor substrate 111. As such, the semiconductor device 100, in which the graphene layer 130 is formed only on the surface of the semiconductor substrate 111, may be realized by adjusting a growth time during the PECVD process.

A method of manufacturing the semiconductor device 100 will now be described.

First, the substrate 110 including the semiconductor and the insulator are prepared in a reaction chamber (not shown). Here, the substrate 110 may include the semiconductor substrate 111 and the insulating layer 112 patterned on the surface of the semiconductor substrate 111.

Then, the graphene layer 130 is grown on the exposed surface of the semiconductor substrate 111 through a CVD process, for example, through a PECVD process. Here, inductively coupled plasma-chemical vapor deposition (ICP-CVD) may be performed as the PECVD process, but an example of the PECVD process is not limited thereto.

A source gas supplied into the reaction chamber during the PECVD process for growing the graphene layer 130 on the surface of the semiconductor substrate 111 may be hydrocarbon, such as methane (CH₄), acetylene (C₂H₂), or ethylene (C₂H₄). Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C., but is not limited thereto.

Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr, but are not limited thereto.

When the PECVD process is performed under such process conditions, graphene starts to grow on the exposed surface of the semiconductor substrate 111 in the reaction chamber. Here, the graphene layer 130 may be selectively grown only on the exposed surface of the semiconductor substrate 111 by suitably adjusting the growth time. Carbide may be formed on an interface between the semiconductor substrate 111 and the graphene layer 130. However, inventive concepts are not limited thereto, and carbide may not be formed on the interface between the semiconductor substrate 111 and the graphene layer 130. As will be described below, when an SiO₂insulating layer is patterned on a surface of a Ge semiconductor substrate, a graphene layer may be grown only on a surface of the Ge semiconductor substrate by adjusting a growth time to about 120 minutes or less.

FIG. 2 is a photograph of a graphene layer grown, via a PECVD process, on a surface of a Ge semiconductor layer on which a SiO₂insulating layer is patterned. During the PECVD process, a CH₄source gas, process pressure of 20 mTorr, a process temperature of 580° C., and plasma power of 150 W were used as process conditions. Also, a growth time was 60 minutes. Referring to FIG. 2, the graphene layer is selectively grown only on an exposed surface of the Ge semiconductor layer.

As such, according to some example embodiments, the semiconductor device 100 may be manufactured by growing the graphene layer 130 directly on the surface of the semiconductor substrate 111 by using the PECVD process. Generally, a method of transferring a graphene layer grown via CVD process to a semiconductor substrate by using polymethyl methacrylate (PMMA) is used so as to manufacture a semiconductor device including a graphene layer. However, it is difficult to accurately form a graphene layer on a desired region as a line width of a semiconductor device is recently gradually reduced, and PMMA residue may be generated or an oxide may be formed according to a wet process.

According to some example embodiments, the graphene layer 130 is directly grown on the surface of the semiconductor substrate 111 by using the PECVD process. Also, the graphene layer 130 may be selectively grown only on a desired region according to a structure of the substrate 110 while directly growing the graphene layer 130.

FIG. 3 is a cross-sectional view of a semiconductor device 200 according to some example embodiments.

Referring to FIG. 3, the semiconductor device 200 includes a substrate 210 including an insulator and a semiconductor, and a graphene layer 230 grown on a surface of the semiconductor of the substrate 210. The substrate 210 may include an insulator substrate 211 and a semiconductor layer 212 patterned on a surface of the insulator substrate 211 in a certain form. Here, a surface of the insulator substrate 211 and a surface of the semiconductor layer 212 may be provided on planes having different heights.

The insulator substrate 211 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y 1≤), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The semiconductor layer 212 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)GeSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb.

The semiconductor layer 212 may further include a doping material. The doping material may include at least one material from among B, As, P, Sb, C, Si, and Mg, but is not limited thereto. Here, concentration of the doping material may be from about 10¹⁵to about 10²²cm³.

The graphene layer 230 is formed on the surface of the semiconductor layer 212. Here, the graphene layer 230 may include one graphene (e.g., an atomic layer of graphene) or a plurality of stacked graphenes. The graphene layer 230 may be grown on the surface of the semiconductor layer 212 via a PECVD process. According to some example embodiments, the graphene layer 230 is not formed on the surface of the insulator substrate 211 but is formed only on the surface of the semiconductor layer 212. As such, the semiconductor device 200, in which the graphene layer 230 is formed only on the surface of the semiconductor layer 212, may be realized by adjusting a growth time during the PECVD process.

A method of manufacturing the semiconductor device 200 will now be described.

First, the substrate 210 including the semiconductor and the insulator are prepared in a reaction chamber (not shown). Here, the substrate 210 may include the insulator substrate 211 and the semiconductor layer 212 patterned on the surface of the insulator substrate 211.

Then, the graphene layer 230 is grown on the surface of the semiconductor layer 212 through a PECVD process. A source gas supplied into the reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄. Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr. However, process conditions are not limited thereto.

When the PECVD process is performed under such process conditions, graphene starts to grow on the surface of the semiconductor layer 212 in the reaction chamber, and the graphene layer 230 having a certain thickness may be formed. Here, the graphene layer 230 may be selectively grown only on the surface of the semiconductor layer 212 by suitably adjusting the growth time.

As such, the semiconductor device 200 may be manufactured by growing the graphene layer 230 directly only on the surface of the semiconductor layer 212 patterned on the insulator substrate 211 by using the PECVD process. Also, the graphene layer 230 may be selectively grown only on a desired region according to a structure of the substrate 210 when the graphene layer 230 is directly grown.

FIG. 4 is a cross-sectional view of a semiconductor device 300 according to some example embodiments.

Referring to FIG. 4, the semiconductor device 300 includes a substrate 310 including an insulator and a semiconductor, and a graphene layer 330 grown on a surface of the semiconductor of the substrate 310. The substrate 310 may include a semiconductor substrate 311 and an insulating layer 312 patterned on a surface of the semiconductor substrate 311. Here, the semiconductor substrate 311 may include surfaces having different heights, and the insulating layer 312 is provided on a low surface from among the surfaces of the semiconductor substrate 311. Accordingly, an exposed surface of the semiconductor substrate 311 and a surface of the insulating layer 312 may be on the same plane.

The semiconductor substrate 311 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb. The semiconductor substrate 311 may further include a doping material including at least one material from among B, As, P, Sb, C, Si, and Mg.

The insulating layer 312 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The graphene layer 230 is formed on the exposed surface of the semiconductor substrate 311. The graphene layer 330 may include one graphene or a plurality of stacked graphenes. Here, the graphene layer 330 is not formed on the surface of the insulating layer 312 but is formed only on the exposed surface of the semiconductor substrate 311.

In order to manufacture the semiconductor device 300, the substrate 310 including the semiconductor and the insulator are prepared. The substrate 310 may include the semiconductor substrate 311 and the insulating layer 312 provided on the surface of the semiconductor substrate 311. Here, the exposed surface of the semiconductor substrate 311 and the surface of the insulating layer 312 may be on the same plane.

Then, the graphene layer 330 is grown only the exposed surface of the semiconductor substrate 311 through a PECVD process. A source gas supplied into a reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄. Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr. However, process conditions are not limited thereto.

When the PECVD process is performed under such process conditions, graphene starts to grow on the surface of the semiconductor substrate 311, and the graphene layer 330 having a certain thickness may be formed. Here, the graphene layer 330 may be selectively grown only on the surface of the semiconductor substrate 311 by suitably adjusting the growth time.

FIG. 5 is a cross-sectional view of a semiconductor device 400 according to some example embodiments.

Referring to FIG. 5, the semiconductor device 400 includes a substrate 410 including an insulator and a semiconductor, and a graphene layer 430 grown on a surface of the semiconductor of the substrate 410. The substrate 410 may include an insulator substrate 411 and a semiconductor layer 412 patterned on a surface of the insulator substrate 411. Here, the insulator substrate 411 may include surfaces having different heights, and the semiconductor layer 412 is provided on a low surface from among the surfaces of the insulator substrate 411. Accordingly, an exposed surface of the insulator substrate 411 and a surface of the semiconductor layer 412 may be on the same plane.

The insulator substrate 411 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The semiconductor layer 412 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)GeSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb. Meanwhile, the semiconductor layer 412 may further include a doping material including at least one material from among B, As, P, Sb, C, Si, and Mg.

The graphene layer 430 is formed on the surface of the semiconductor layer 412. Here, the graphene layer 430 may include one graphene or a plurality of stacked graphenes. The graphene layer 430 is not formed on the surface of the insulator substrate 411 but is formed only on the surface of the semiconductor layer 412.

In order to manufacture the semiconductor device 400, first, the substrate 410 including the semiconductor and the insulator are prepared. The substrate 410 may include the insulator substrate 411 and the semiconductor layer 412 provided on the surface of the insulator substrate 411. Here, the exposed surface of the insulator substrate 411 and the surface of the semiconductor layer 412 may be on the same plane.

Then, the graphene layer 430 is grown only the exposed surface of the semiconductor layer 412 through a PECVD process. A source gas supplied into a reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄. Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr. However, process conditions are not limited thereto.

When the PECVD process is performed under such process conditions, graphene starts to grow on the surface of the semiconductor layer 412, and the graphene layer 430 having a certain thickness may be formed. Here, the graphene layer 430 may be selectively grown only on the surface of the semiconductor layer 412 by suitably adjusting the growth time.

FIG. 6 is a cross-sectional view of a semiconductor device 500 according to some example embodiments.

Referring to FIG. 6, the semiconductor device 500 includes a substrate 510 including a semiconductor and an insulator, a first graphene layer 531 grown on a surface of the semiconductor of the substrate 510, and a second graphene layer 532 grown on a surface of the insulator of the substrate 510. The substrate 510 may include a semiconductor substrate 511 and an insulating layer 512 provided on a surface of the semiconductor substrate 511. The insulating layer 512 may be patterned on the surface of the semiconductor substrate 511 in a certain form. Here, the surface of the semiconductor substrate 511 and a surface of the insulating layer 512 may be provided on planes having different heights.

The semiconductor substrate 511 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb.

The semiconductor substrate 511 may further include a doping material. The doping material may include at least one material from among B, As, P, Sb, C, Si, and Mg, but is not limited thereto. Here, concentration of the doping material may be from about 10¹⁵to about 10²²cm⁻³.

The insulating layer 512 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The first graphene layer 531 is formed on an exposed surface of the semiconductor substrate 511, and the second graphene layer 532 is formed on the surface of the insulating layer 612. Here, the first and second graphene layers 531 and 532 may each include one graphene or a plurality of stacked graphenes.

The first and second graphene layers 531 and 532 may have different thicknesses. For example, a thickness t1 of the first graphene layer 531 may be greater than a thickness t2 of the second graphene layer 532. The first and second graphene layers 531 and 532 may be respectively grown on the surface of the semiconductor substrate 511 and the surface of the insulating layer 512 via a PECVD process to have different thicknesses. The semiconductor device 500, in which the first and second graphene layers 531 and 532 having different thicknesses are formed respectively on the surface of the semiconductor substrate 511 and on the surface of the insulating layer 512, may be realized by adjusting a growth time during the PECVD process.

A method of manufacturing the semiconductor device 500 will now be described.

First, the substrate 510 including the semiconductor and the insulator are prepared in a reaction chamber (not shown). Here, the substrate 510 may include the semiconductor substrate 511 and the insulating layer 512 patterned on the surface of the semiconductor substrate 511.

Then, the first and second graphene layers 531 and 532 are grown respectively on the exposed surface of the semiconductor substrate 511 and on the surface of the insulating layer 512 through a PECVD process. A source gas supplied into a reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄.

Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr. However, process conditions are not limited thereto.

When the PECVD process is performed under such process conditions, graphene first starts to grow on the exposed surface of the semiconductor substrate 511, and the first graphene layer 531 having a certain thickness is formed. Here, carbide may be formed on an interface between the semiconductor substrate 511 and the graphene being grown. However, inventive concepts are not limited thereto, and carbide may not be formed.

Next, graphene also starts to grow on the surface of the insulating layer 512 after a certain incubation time, and the second graphene layer 532 having a certain thickness is formed. Here, the incubation time denotes a time for nuclei for growing the graphene on the surface of the insulating layer 512 to be generated. After the incubation time, the first and second graphene layers 531 and 532 may be respectively grown on the surfaces of the semiconductor substrate 511 and the insulating layer 512, and at this time, the first and second graphene layers 531 and 532 may have different thicknesses. For example, the first graphene layer 531 grown on the surface of the semiconductor substrate 511 may have the thickness t1 greater than the thickness t2 of the second graphene layer 532 grown on the surface of the insulating layer 512.

As such, the first and second graphene layers 531 and 532 having different thicknesses may be grown respectively on the exposed surface of the semiconductor substrate 511 and on the surface of the insulating layer 512 by adjusting a growth time during the PECVD process.

FIG. 7 is a photograph of graphene layers having different thicknesses according to growth times, grown on a surface of a Ge semiconductor layer and on a surface of an SiO₂insulating layer during a PECVD process. During the PECVD process, a CH₄source gas, process pressure of 20 mTorr, a process temperature of 580° C., and plasma power of 150 W are used as process conditions.

Referring to FIG. 7, a thickness of a first graphene layer formed on the surface of the Ge semiconductor layer gradually increases as a growth time increases to 60 minutes, 120 minutes, 180 minutes, and 240 minutes, after graphene starts to grow on the surface of the Ge semiconductor layer at an initial point of time in the PECVD process.

Meanwhile, graphene does not grow on the surface of the SiO₂insulating layer up to the growth time of about 120 minutes, and after the growth time of 120 minutes, nuclei for graphene growth are generated. In this case, an incubation time may be about 120 minutes. After the incubation time, a thickness of a second graphene layer formed on the surface of the SiO₂insulating layer gradually increases as the growth time increases to 180 minutes and 240 minutes. Here, at the same growth time, the thickness of the first graphene layer formed on the surface of the Ge semiconductor layer is greater than the thickness of the second graphene layer formed on the surface of the SiO₂insulating layer.

As such, the first and second graphene layers having different thicknesses may be grown respectively on the surfaces of the Ge semiconductor layer and the SiO₂insulating layer, or the first graphene layer may be grown only on the surface of the Ge semiconductor layer by suitably adjusting the growth time during the PECVD process. For example, the first and second graphene layers having different thicknesses may be grown respectively on the surfaces of the Ge semiconductor layer and the SiO₂insulating layer by adjusting the growth time to be greater than a certain time (e.g., the incubation time) during the PECVD process. Meanwhile, when the growth time is adjusted to be within the certain time (e.g., the incubation time), the first graphene layer may be grown only on the surface of the Ge semiconductor layer.

As such, according to the current embodiment, a semiconductor device may be manufactured by growing the first and second graphene layers 531 and 532 having different thicknesses directly respectively on the surfaces of the semiconductor substrate 511 and the insulating layer 512 by using the PECVD process.

FIG. 8 is a cross-sectional view of a semiconductor device 600 according to some example embodiments.

Referring to FIG. 8, the semiconductor device 600 includes a substrate 610 including an insulator and a semiconductor, a first graphene layer 631 grown on a surface of the semiconductor of the substrate 610, and a second graphene layer 632 grown on a surface of the insulator of the substrate 610. The substrate 610 may include an insulator substrate 611 and a semiconductor layer 612 patterned on a surface of the insulator substrate 611 in a certain form. Here, the surface of the insulator substrate 611 and a surface of the semiconductor layer 612 may be provided on planes having different heights.

The insulator substrate 611 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3). The semiconductor layer 612 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb. Meanwhile, the semiconductor layer 612 may further include a doping material including at least one material from among B, As, P, Sb, C, Si, and Mg. Here, concentration of the doping material may be from about 10¹⁵to about 10²²cm⁻³.

The first graphene layer 631 is formed on a surface of the semiconductor layer 612, and the second graphene layer 632 is formed on an exposed surface of the insulator substrate 611. Here, the first and second graphene layers 631 and 632 may each include one graphene or a plurality of stacked graphenes.

The first and second graphene layers 631 and 632 may have different thicknesses. For example, the thickness t1 of the first graphene layer 631 may be greater than the thickness t2 of the second graphene layer 632. The first and second graphene layers 631 and 632 may be respectively grown on the surface of the semiconductor layer 612 and the surface of the insulator substrate 611 in different thicknesses by adjusting a growth time during a PECVD process.

In order to manufacture the semiconductor device 600, the substrate 610 including the semiconductor and the insulator are prepared in a reaction chamber (not shown). Here, the substrate 610 may include the insulator substrate 611 and the semiconductor layer 612 patterned on the surface of the insulator substrate 611.

Then, the first and second graphene layers 631 and 632 are grown respectively on the surface of the semiconductor layer 612 and on the exposed surface of the insulator substrate 611 through a PECVD process. A source gas supplied into the reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄. Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C., but is not limited thereto. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr, but are not limited thereto.

When the PECVD process is performed under such process conditions, graphene first starts to grow on the exposed surface of the semiconductor layer 612, and the first graphene layer 631 having a certain thickness is formed. Then, graphene also starts to grow on the exposed surface of the insulator substrate 611 after a certain incubation time, and the second graphene layer 632 having a certain thickness is formed. Accordingly, after the incubation time, the first and second graphene layers 631 and 632 may be respectively grown on the surfaces of the semiconductor layer 612 and the insulator substrate 611. Here, the first graphene layer 631 grown on the surface of the semiconductor layer 612 may have the thickness t1 greater than the thickness t2 of the second graphene layer 632 grown on the surface of the insulator substrate 611.

FIG. 9 is a cross-sectional view of a semiconductor device 700 according to some example embodiments.

Referring to FIG. 9, the semiconductor device 700 includes a substrate 710 including an insulator and a semiconductor, a first graphene layer 731 grown on a surface of the semiconductor of the substrate 710, and a second graphene layer 732 grown on a surface of the insulator of the substrate 710. The substrate 710 may include a semiconductor substrate 711 and an insulating layer 712 patterned on a surface of the semiconductor substrate 711 in a certain form. Here, an exposed surface of the semiconductor substrate 711 and a surface of the insulating layer 712 may be provided on the same plane.

The semiconductor substrate 711 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb. Meanwhile, the semiconductor substrate 711 may further include a doping material including at least one material from among B, As, P, Sb, C, Si, and Mg.

The insulating layer 712 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The first and second graphene layers 731 and 732 having different thicknesses may be respectively formed on the exposed surface of the semiconductor substrate 711 and the surface of the insulating layer 712. Here, the thickness t1 of the first graphene layer 731 may be greater than the thickness t2 of the second graphene layer 732. Each of the first and second graphene layers 731 and 732 may include one graphene or a plurality of stacked graphenes.

The first and second graphene layers 731 and 732 may be grown respectively on the surfaces of the semiconductor substrate 711 and the insulating layer 712 via a PECVD process to have different thicknesses. For example, first, the substrate 710 including the semiconductor substrate 711 and the insulating layer 712 provided on the surface of the semiconductor substrate 711 is prepared. Here, the exposed surface of the semiconductor substrate 711 and the surface of the insulating layer 712 may be on the same plane.

Then, the first and second graphene layers 731 and 732 are grown respectively on the exposed surface of the semiconductor substrate 711 and the surface of the insulating layer 712 through the PECVD process. A source gas supplied into the reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄. Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C., but is not limited thereto. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr, but are not limited thereto.

When the PECVD process is performed under such process conditions, graphene first starts to grow on the exposed surface of the semiconductor substrate 711, and the first graphene layer 731 having a certain thickness is formed. Then, graphene also starts to grow on the surface of the insulating layer 712 after a certain incubation time, and the second graphene layer 732 having a certain thickness is formed. Accordingly, the first and second graphene layers 731 and 732 having different thicknesses may be respectively grown on the surfaces of the semiconductor substrate 711 and the insulating layer 712. Here, the first graphene layer 731 grown on the surface of the semiconductor substrate 711 may have the thickness t1 greater than the thickness t2 of the second graphene layer 732 grown on the surface of the insulating layer 712.

FIG. 10 is a cross-sectional view of a semiconductor device 800 according to some example embodiments.

Referring to FIG. 10, the semiconductor device 800 includes a substrate 810 including an insulator and a semiconductor, a first graphene layer 831 grown on a surface of the semiconductor of the substrate 810, and a second graphene layer 832 grown on a surface of the insulator of the substrate 810. The substrate 810 may include an insulator substrate 811 and a semiconductor layer 812 patterned on a surface of the insulator substrate 811 in a certain form. Here, the insulator substrate 811 may include surfaces having different heights, and the semiconductor layer 812 may be provided on a low surface from the surfaces of the insulator substrate 811. Accordingly, an exposed surface of the insulator substrate 811 and a surface of the semiconductor layer 812 may be provided on the same plane.

The insulator substrate 811 may include at least one material selected from the group consisting of SiO_x(0<x≤3), SiN_x(0<x≤3), SiO_xN_y(0≤x, and y≤1), SiO_xC_y(0≤x, and y≤1), GeO_xN_y(0≤x, and y≤1), GeO_xC_y(0≤x, and y≤1), AlO_x(0<x≤3), HfO_x(0<x≤3), and ZrO_x(0<x≤3).

The semiconductor layer 812 may include at least one of a group IV material and a group III-V compound. Here, the group IV material may include Si_(1-x-y-z)Ge_xSn_yC_z(0≤x, y, and z≤1). Also, the group III-V compound may include a group Ill material including one or more of In, Ga, and Al, and a group V material including one or more of N, P, As, and Sb. Meanwhile, the semiconductor layer 812 may further include a doping material including at least one material from among B, As, P, Sb, C, Si, and Mg.

The first graphene layer 831 is formed on the surface of the semiconductor layer 812 and the second graphene layer 932 is formed on the exposed surface of the insulator substrate 811. Here, each of the first and second graphene layers 831 and 832 may include one graphene or a plurality of stacked graphenes. The first and second graphene layers 831 and 832 formed respectively on the surfaces of the semiconductor layer 812 and the insulator substrate 811 may have different thicknesses. For example, the thickness t1 of the first graphene layer 831 may be greater than the thickness t2 of the second graphene layer 832.

The first and second graphene layers 831 and 832 are respectively grown on the surfaces of the semiconductor layer 812 and the insulator substrate 811 in different thicknesses by adjusting a growth time during the PECVD process.

For example, the substrate 810 including the insulator substrate 811 and the semiconductor layer 812 patterned on the surface of the insulator substrate 811 is prepared in a reaction chamber (not shown). Then, the first and second graphene layers 831 and 832 are grown respectively on the surface of the semiconductor layer 812 and the exposed surface of the insulator substrate 811 through the PECVD process. A source gas supplied into the reaction chamber during the PECVD process may be hydrocarbon, such as CH₄, C₂H₂, or C₂H₄. Also, a process temperature in the reaction chamber may be from about 300° C. to about 700° C., but is not limited thereto. Plasma power used during the PECVD process may be from about 50 W to about 300 W, and process pressure in the reaction chamber may be from about 10 mTorr to about 50 mTorr, but are not limited thereto.

When the PECVD process is performed under such process conditions, graphene first starts to grow on the surface of the semiconductor layer 812, and the first graphene layer 831 having a certain thickness is formed. Then, graphene also starts to grow on the exposed surface of the insulator substrate 811 after a certain incubation time, and the second graphene layer 832 having a certain thickness is formed. Accordingly, the first and second graphene layers 831 and 832 having different thicknesses may be respectively grown on the surfaces of the semiconductor layer 812 and the insulator substrate 811. Here, the first graphene layer 831 grown on the surface of the semiconductor layer 812 may have the thickness t1 greater than the thickness t2 of the second graphene layer 832 grown on the surface of the insulator substrate 811.

According to one or more embodiments, a semiconductor device may include a graphene layer selectively formed on a surface of a substrate including two types of materials, e.g., a semiconductor and an insulator. Here, the graphene layer may be formed only on a surface of the semiconductor or formed on surfaces of the semiconductor and the insulator in different thicknesses. The semiconductor device may be manufactured by growing the graphene layer directly only on the surface of the semiconductor or the graphene layers having different thicknesses directly on the surfaces of the semiconductor and the insulator via a PECVD process. Accordingly, the graphene layer may be selectively grown according to a structure of the substrate including two types of materials, and thus the graphene layer may be formed only on a desired region of the substrate.

It should be understood that embodiments described herein should be considered in a descriptive sense only and not for purposes of limitation. Descriptions of features or aspects within each embodiment should typically be considered as available for other similar features or aspects in other embodiments.

While one or more embodiments have been described with reference to the figures, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope as defined by the following claims.

	Number	Date	Country
Parent	15807096	Nov 2017	US
Child	17087968		US

SEMICONDUCTOR DEVICE INCLUDING GRAPHENE AND METHOD OF MANUFACTURING THE SEMICONDUCTOR DEVICE

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

International Classifications

Abstract

Description

Claims

Priority Claims (1)

CROSS-REFERENCE TO RELATED APPLICATION

Continuation in Parts (1)