Patent Application
20180350824
Embodiments of the disclosure relate to the field of semiconductor device design and fabrication. More specifically, embodiments of the disclosure relate to methods of forming a ferroelectric (FE) memory cell including a FE material on an electrode material, and to related semiconductor device structures.
Lead zirconate titanate (PZT) has been investigated as a FE material for use in non-volatile data storage, such as FE Random Access Memory (FERAM). However, PZT is not compatible with conventional semiconductor processing techniques and is not scaleable because the PZT loses its FE properties at lower thicknesses and, therefore, has integration issues.
Hafnium silicate (HfSiOx) is a high-k dielectric material and has been investigated as a replacement ferroelectric material for PZT. Hafnium silicate is polymorphic and may form in monoclinic, tetragonal, cubic, or orthorhombic crystal structures, with each of the crystal structures having multiple possible crystallographic orientations, such as the (111) or (200) crystallographic orientations. Hafnium silicate is conventionally formed with the (111) crystallographic orientation being the dominant formed crystallographic orientation.
Titanium nitride is a polymorphic material and may form many crystal structures, with each crystal structure having multiple possible crystallographic orientations, such as the (001), (002), (100), (110), (111), or (200) crystallographic orientations. Titanium nitride is conventionally formed in the cubic phase and has multiple crystallographic orientations, with the (200) crystallographic orientation often being the dominant formed crystallographic orientation.
It would be desirable to have improved methods of forming hafnium silicate or other FE materials, such that a desired crystallographic orientation of the ferroelectric material can be achieved.
Methods of forming a ferroelectric memory cell are disclosed, as are related semiconductor device structures including a ferroelectric material and an electrode material. The ferroelectric material may be crystallized in a desired crystallographic orientation. The desired crystallographic orientation of the ferroelectric material may be achieved by forming the electrode material at a desired crystallographic orientation, forming a hafnium-based material over the electrode material, and crystallizing the hafnium-based material to produce a ferroelectric material. Thus, the electrode material may function as a template to induce formation of the desired crystallographic orientation of the ferroelectric material.
The following description provides specific details, such as material types, material thicknesses, and processing conditions in order to provide a thorough description of embodiments of the disclosure. However, a person of ordinary skill in the art will understand that the embodiments of the disclosure may be practiced without employing these specific details. Indeed, the embodiments of the disclosure may be practiced in conjunction with conventional fabrication techniques employed in the industry. In addition, the description provided herein does not form a complete process flow for forming a semiconductor device structure, and each of the semiconductor device structures described below do not form a complete semiconductor device. Only those process acts and structures necessary to understand the embodiments of the disclosure are described in detail below. Additional acts to form a complete semiconductor device may be performed by conventional fabrication techniques. Also note, any drawings accompanying the present application are for illustrative purposes only, and are thus not drawn to scale. Additionally, elements common between figures may retain the same numerical designation.
As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.
As used herein, relational terms, such as “first,” “second,” “top,” “bottom,” “upper,” “lower,” “over,” “under,” etc., are used for clarity and convenience in understanding the disclosure and accompanying drawings and do not connote or depend on any specific preference, orientation, or order, except where the context clearly indicates otherwise.
As used herein, the term “substrate” means and includes a foundation material or construction upon which components, such as those within a semiconductor device structure are formed. The substrate may be a semiconductor substrate, a base semiconductor material on a supporting structure, a metal electrode, or a semiconductor substrate having one or more materials, structures, or regions formed thereon. The substrate may be a conventional silicon substrate or other bulk substrate including a semiconductive material. As used herein, the term “bulk substrate” means and includes not only silicon wafers, but also silicon-on-insulator (“SOT”) substrates, such as silicon-on-sapphire (“SOS”) substrates or silicon-on-glass (“SOG”) substrates, epitaxial layers of silicon on a base semiconductor foundation, or other semiconductor or optoelectronic materials, such as silicon-germanium (Si1-xGex, where x is, for example, a mole fraction between 0.2 and 0.8), germanium (Ge), gallium arsenide (GaAs), gallium nitride (GaN), or indium phosphide (InP), among others. Furthermore, when reference is made to a “substrate” in the following description, previous process stages may have been utilized to form materials, regions, or junctions in or on the base semiconductor structure or foundation.
As used herein, the term “ferroelectric” means and includes a material having a spontaneous electric polarization (electric dipole) that can be reversed in the presence of an electric field.
As used herein, the term “dominant” in reference to a crystallographic orientation of a material means and includes a material exhibiting a specified crystallographic orientation at a relatively greater amount than any other crystallographic orientation. By way of non-limiting example, a “dominant (111) crystallographic orientation” means the material exhibits the (111) crystallographic orientation at a greater amount than any other crystallographic orientation.
As used herein, the term “hafnium silicate” means and includes a material including hafnium, silicon, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfSiOx,” which does not indicate the stoichiometry of the hafnium, silicon, and oxygen atoms.
As used herein, the term “hafnium aluminate” means and includes a material including hafnium, aluminum, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfAlOx,” which does not indicate the stoichiometry of the hafnium, aluminum, and oxygen atoms.
As used herein, the term “hafnium zirconate” means and includes a material including hafnium, zirconium, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfZrOx,” which does not indicate the stoichiometry of the hafnium, zirconium, and oxygen atoms.
As used herein, the term “strontium-doped hafnium oxide” means and includes a material including hafnium, strontium, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfSrOx,” which does not indicate the stoichiometry of the hafnium, strontium, and oxygen atoms.
As used herein, the term “magnesium-doped hafnium oxide” means and includes a material including hafnium, magnesium, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfMgOx,” which does not indicate the stoichiometry of the hafnium, magnesium, and oxygen atoms.
As used herein, the term “gadolinium-doped hafnium oxide” means and includes a material including hafnium, gadolinium, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfGdOx,” which does not indicate the stoichiometry of the hafnium, gadolinium, and oxygen atoms.
As used herein, the term “yttrium-doped hafnium oxide” means and includes a material including hafnium, yttrium, and oxygen atoms. For convenience, the composition of the material may be abbreviated by “HfYOx,” which does not indicate the stoichiometry of the hafnium, yttrium, and oxygen atoms.
The semiconductor device structure 100 may be configured as a memory cell of a FERAM. The memory cells may, for example, be arrayed in a 1 transistor/1 capacitor (1T/1C) configuration. However, other configurations of the memory cells may also be used. Additional acts to form a complete FERAM including the semiconductor device structure 100 of
The FE material 106 may be a metal oxide material, such as a hafnium-based material, that includes a dopant. The hafnium-based material is crystallized to form the FE material 106. For simplicity and convenience, the term “hafnium-based material” is used herein to refer to the material before the material is crystallized and the term “FE material” is used to refer to the material after the material is crystallized. The FE material 106 may be hafnium oxide into which the dopant is incorporated. The dopant may be an element such as silicon, aluminum, zirconium, magnesium, strontium, gadolinium, yttrium, other rare earth elements, or combinations thereof. Examples of ferroelectric materials include, but are not limited to, hafnium silicate (HfSiOx), hafnium aluminate (HfAlOx), hafnium zirconate (HfZrOx), strontium-doped hafnium oxide (HfSrOx), magnesium-doped hafnium oxide (HfMgOx), gadolinium-doped hafnium oxide (HfGdOx), yttrium-doped hafnium oxide (HfYOx), or combinations. While hafnium oxide does not exhibit ferroelectric properties, hafnium oxide in crystalline form and including one of the above-mentioned dopants may be ferroelectric. Hafnium oxide in crystalline form and including one of the above-mentioned dopants at the correct composition is ferroelectric. The FE material 106 may include from 0.1 mol % to about 70 mol % of the dopant. If the FE material 106 is HfSiOx, the FE material 106 may be hafnium oxide including from about 4 mol % to about 6 mol % silicon, such as from about 4.4 mol % to about 5.6 mol % silicon. In one embodiment, the HfSiOx material includes 4.7 mol % silicon. If the FE material 106 is HfAlOx, the FE material 106 may be hafnium oxide including from about 5 mol % to about 7 mol % aluminum. If the FE material 106 is HfYOx, the FE material 106 may be hafnium oxide including from about 2.5 mol % to about 5.5 mol % yttrium. If the FE material 106 is HfZrOx, the FE material 106 may be hafnium oxide including from about 40 mol % to about 70 mol % zirconium. The FE material 106 of the semiconductor device structure 100 may be in a crystalline state and have a desired crystallographic orientation.
The another electrode 108 may be formed of titanium nitride (TiN) in a crystalline state. The material of the another electrode 108 is not limited to a specific crystallographic orientation and, thus, may be formed from crystalline TiN in a (001), (002), (100), (110), (111), or (200) crystallographic orientation, or combinations thereof. The another electrode 108 may be formed of titanium nitride having the same or a different dominant crystallographic orientation as the electrode 104. While examples herein describe that the another electrode 108 is formed of TiN, other conventional materials may be used.
The metal silicide material 110 may be tungsten silicide (WSix) or other metal silicide. The metal silicide material 110 may be positioned over the another electrode 108 and the FE material 106. The metal silicide material 110 may prevent deterioration, such as oxidation, of the another electrode 108 during fabrication of the semiconductor device structure 100.
In one embodiment, the electrode 104 is formed of TiN in the dominant (111) crystallographic orientation, the FE material 106 is hafnium silicate in the dominant (200) crystallographic orientation, the another electrode material 106 is formed from TiN, and the metal silicide material 110 is tungsten silicide.
Accordingly, the present disclosure describes a FE memory cell that comprises an electrode comprising titanium nitride in a dominant (111) crystallographic orientation over a substrate. A ferroelectric material is over the electrode and another electrode material is over the ferroelectric material.
To form the semiconductor device structure 100, the electrode 104 exhibiting the desired dominant crystallographic orientation may be formed on the substrate 102 by appropriately selecting the electrode material and the formation conditions. For instance, the electrode 104 may be formed by depositing (111) crystallographic orientation titanium nitride over the substrate 102. In one embodiment, the (111) crystallographic orientation titanium nitride of the electrode 104 is formed by depositing titanium nitride by ALD, using an organometallic ALD precursor. The organometallic ALD precursor may include, but is not limited to, tetrakis-dimethylamino titanium (TDMAT). However, other organometallic ALD precursors may be used. ALD techniques for forming TiN are known in the art and, therefore, are not described in detail herein. Since the organometallic ALD precursor is free of chlorine, the resulting TiN has a low chlorine content, which reduces shielding and results in uniform electric fields in the electrode 104. The electrode 104 may be formed as a continuous material, such as at a thickness ranging from about 20 Å to about 200 Å, from about 50 Å to about 130 Å, or from about 40 Å to about 70 Å. In one embodiment, the electrode 104 thickness is about 60 Å.
While an ALD method of forming the electrode 104 from TiN using a specific ALD precursor is described herein, other methods of forming the electrode 104 may be used, as long as the resulting electrode 104 has the desired dominant crystallographic orientation, i.e., TiN in the dominant (111) crystallographic orientation. For instance, the electrode 104 with the desired dominant crystallographic orientation may alternatively be formed by depositing titanium nitride using TiAlN or by depositing titanium nitride using a titanium tetrachloride (TiCl4) precursor and ammonia (NH3). Process conditions for these other techniques may be selected such that the TiN of the electrode 104 is formed in the dominant (111) crystallographic orientation.
The hafnium-based material of the FE material 106 may be formed over the electrode 104. The hafnium-based material may include the hafnium oxide material with the dopant, as previously described. The hafnium-based material may be formed by conventional techniques, such as sputtering, ALD, CVD, PECVD, or MOCVD, which are not described in detail herein. Since the metal oxide material is not ferroelectric as formed, the molar concentration of the dopant in the metal oxide material may be tailored to provide the metal oxide material with ferroelectric properties. The molar concentration of the dopant in the metal oxide material may be controlled by appropriately selecting the relative ratios of metal precursor, oxygen precursor, and dopant precursor used and by varying the number of cycles conducted. The hafnium-based material, in its initial, as-formed state, may be an amorphous material.
The electrode material of the another electrode 108 may be formed over the hafnium-based material of the FE material 106. The electrode material of the another electrode 108 may be formed by conventional techniques, which are not described in detail herein. In one embodiment where the electrode material of the another electrode 108 is TiN, the TiN may be formed by a conventional Sequential Flow Deposition (SFD) process using TiCl4 and NH3. If both the electrode 104 and the another electrode 108 are formed from TiN, the TiN of the another electrode 108 may have the same, or a different, crystallographic orientation as the electrode 104. The electrode 104, the hafnium-based material of the FE material 106, and another electrode 108 may form a metal-insulator-metal (MIM) stack 112. During the formation of the another electrode 108, the hafnium-based material of the FE material 106 may remain in its amorphous state.
After forming the hafnium-based material of the FE material 106 and the another electrode 108, the MIM stack 112 may be subjected to an anneal process to crystallize the hafnium-based material into its desired crystallographic orientation. The annealing conditions may be determined based on the composition of the hafnium-based material and the thickness of the electrodes 104, 108. The crystallization temperature of the hafnium-based material may be a function of the amount of dopant present in the hafnium-based material. At relatively higher dopant concentrations, the crystallization temperature of the hafnium-based material may be higher than the crystallization temperature of the hafnium-based material having a lower amount of the dopant. The crystallization temperature of the hafnium-based material may range from about 800° C. to about 1000° C. By appropriately forming the electrode 104 having the desired dominant crystallographic orientation and following the anneal, the hafnium-based material may crystallize into its desired crystallographic orientation. By way of example, if the electrode 104 is formed from (111) crystallographic orientation TiN and the hafnium-based material of the FE material 106 is formed from hafnium silicate having 4.7 mol % silicon, following the anneal, the FE material 106 has an orthorhombic crystal structure with a dominant (200) crystallographic orientation. The (111) crystallographic orientation titanium nitride of the electrode 104 may provide a smooth surface that functions as a template for forming the dominant (200) crystallographic orientation of the hafnium silicate used as the FE material 106. If a material other than hafnium silicate is used as the hafnium-based material of the FE material 106, following the anneal process the FE material 106 may have an orthorhombic crystal structure. However, the resulting dominant crystallographic orientation of the FE material 106 may be a crystallographic orientation other than the (200) crystallographic orientation, depending on the hafnium-based material used.
Additional process acts to form a FERAM including the semiconductor device structure 100 of the present disclosure may be performed by conventional fabrication techniques, which are not described in detail herein.
Accordingly, the present disclosure also includes a method of forming a ferroelectric memory cell. The method comprises forming an electrode material exhibiting a desired dominant crystallographic orientation. A hafnium-based material is formed over the electrode material and the hafnium-based material is crystallized to induce formation of a ferroelectric material having a desired crystallographic orientation.
The present disclosure includes another method of forming a ferroelectric memory cell. The method comprises forming an electrode material comprising titanium nitride in a dominant (111) crystallographic orientation. An amorphous hafnium silicate material is formed over the electrode material. Another electrode material is formed over the amorphous hafnium silicate material and the amorphous hafnium silicate material is crystallized to induce formation of a dominant (200) crystallographic orientation.
During use and operation, the semiconductor device structure 100 of the present disclosure may exhibit improved cell performance. The semiconductor device structure 100 where the FE material 106 has the desired crystallographic orientation on the electrode 104 having the desired dominant crystallographic orientation exhibited intrinsically improved ferroelectric properties, such as improved cycling, improved data retention, lower ferroelectric coercivity (Ec), and lower electrical field saturation.
Without being bound by any theory, it is believed that by forming the electrode 104 having the desired dominant crystallographic orientation, the desired crystallographic orientation of the hafnium-based material of the ferroelectric material 106 may be formed. By forming the ferroelectric material 106 having the desired crystallographic orientation, the dipole mechanism of the ferroelectric material 106 may be oriented perpendicular to the electrodes 104, 108. For instance, the dominant (111) crystallographic orientation of TiN is believed to be smoother than any other crystallographic orientation of TiN. The dominant (111) crystallographic orientation of TiN is believed to function as a smooth template upon which the (200) crystallographic orientation of the hafnium-based material of the ferroelectric material, such as HfSiOx, may be formed. In a FERAM cell having the electrode 104 formed of the dominant (111) crystallographic orientation of TiN and the FE material 106 formed of HfSiOx in the (200) crystallographic orientation, the dipole of the ferroelectric material 106 is oriented perpendicular to the electrodes 104, 108. Thus, the FERAM cell can be easily polarized and operated along its c axis.
The following examples serve to explain embodiments of the present invention in more detail. These examples are not to be construed as being exhaustive or exclusive as to the scope of the present disclosure.
A 150 Å layer of titanium nitride was formed by a conventional Sequential Flow Deposition (SFD) process using TiCl4 and NH3. Another 150 Å layer of titanium nitride was formed by an ALD process using TDMAT as the ALD precursor. The crystal structures and crystallographic orientation of the TiN materials was determined by grazing incidence x-ray diffraction (GIXRD) analysis. The crystal structures of both TiN materials were polycrystalline cubic. However, the both materials had different crystallographic orientations. As shown in
The roughness of the two titanium nitride materials was also different. The roughness of the materials was measured by conventional atomic force microscopy (AFM) techniques. As shown in
Test wafers including TiN materials formed by different techniques were prepared. The control wafer included a polysilicon substrate, a 50 Å TiN material (a bottom electrode) over the substrate, a 100 Å HfSiOx material over the TiN material of the bottom electrode, a 100 Å TiN material (a top electrode) over the HfSiOx material, and a 600 Å WSix over the TiN material of the top electrode. The TiN of the bottom electrode had a dominant (200) crystallographic orientation. The HfSiOx material included 4.7 mol % silicon. The TiN of the bottom and top electrodes was formed by a conventional Sequential Flow Deposition (SFD) process using TiCl4 and NH3. The control wafer is referred to herein and in the drawings as wafer 5.
In the sample wafers, the TiN material of the bottom electrode was formed to 60 Å or 125 Å by an ALD process using TDMAT as the ALD precursor. The sample wafer having the 125 Å TiN material of the bottom electrode is referred to herein and in the drawings as wafer 5 and the 60 Å TiN material of the bottom electrode is referred to herein and in the drawings as wafer 18. The TiN of the bottom electrode had a dominant (111) crystallographic orientation. The sample wafers included a polysilicon substrate, a 100 Å HfSiOx material (including 4.7 mol % silicon) over the TiN material of the bottom electrode, a 100 Å TiN material (a top electrode) over the HfSiOx material, and a 600 Å WSiX over the TiN material of the top electrode. The 100 Å TiN material of the top electrode was formed by a conventional SFD process.
The control and sample wafers including stack 112 of material as described above were subjected to an anneal at 1000° C. Following the anneal, the HfSiOx material over the TiN material formed by the ALD process (wafer 18) exhibited an orthorhombic crystal structure and a dominant (200) crystallographic orientation, as shown in
The performance of the control and sample wafers was also determined. Data retention characteristics were evaluated by a conventional Positive Up Negative Down (PUND) pulse technique at 100 cycles. As shown in
These results show that wafer 18 (having the orthorhombic HfSiOx crystal structure and a dominant (200) crystallographic orientation on the dominant (111) crystallographic orientation TiN) had intrinsically improved ferroelectric properties, such as improved 2 Pr values, improved cycling, improved Ec, and lower electrical field saturation, compared to the control wafer.
While the disclosure is susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, the disclosure is not intended to be limited to the particular forms disclosed. Rather, the disclosure is to cover all modifications, equivalents, and alternatives falling within the scope of the disclosure as defined by the following appended claims and their legal equivalents.
This application is a continuation of U.S. patent application Ser. No. 15/459,136, filed Mar. 15, 2017, pending, which is a continuation of U.S. patent application Ser. No. 14/936,013, filed Nov. 9, 2015, now U.S. Pat. No. 9,698,343, issued Jul. 4, 2017, which is a divisional of U.S. patent application Ser. No. 14/026,883, filed Sep. 13, 2013, now U.S. Pat. No. 9,231,206, issued Jan. 5, 2016, the disclosure of each of which is hereby incorporated herein in its entirety by this reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14026883 | Sep 2013 | US |
| Child | 14936013 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15459136 | Mar 2017 | US |
| Child | 16059672 | US | |
| Parent | 14936013 | Nov 2015 | US |
| Child | 15459136 | US |