This invention is one which can be applied to the smoothing of the substrate of e.g. a semiconductor, another electronic device, or the like, and to the smoothing of a wide variety of device surfaces, and pertains to a method, and an apparatus therefor, for smoothing a solid surface by means of irradiation with a gas cluster ion beam.
So far, a wide variety of vapor phase reaction methods aimed at the surface smoothing, etc., of electronic devices, have been developed and put into practical use. E.g., the method of smoothing a substrate surface shown in Patent Reference 1 irradiates a substrate surface at a low angle with ions of monomer atoms or molecules of Ar (argon) gas and so on, and smoothes it by sputtering.
Moreover, in recent years, solid surface smoothing methods using a gas cluster ion beam have gained attention for enabling little surface damage and very small surface roughness. E.g., in Patent Reference 2, there is disclosed a method of reducing surface roughness by irradiating a gas cluster ion beam on a solid surface. In this method, the gas cluster ions irradiated on the object being processed are broken down by collisions with the object being processed, on which occasion there arise many-body collisions between the constituent atoms or molecules of the cluster and the constituent atoms or molecules of the object being processed, and a movement in a horizontal direction with respect to the object being processed becomes noticeable, as a result of which cutting is performed in a transverse direction with respect to the surface of the object being processed. This is a phenomenon called “lateral sputtering”. By further movement of particles in a lateral direction on the surface of the object being processed, the apices of the surface are planed, the result being that atomic-size, ultra-accurate polishing is obtained. In addition, the energy held by the gas cluster ion beam is different from that of conventional ion etching in that, the energy being lower, no damage is inflicted on the surface of the object being processed, making possible the required ultra-accurate polishing. This means that solid surface smoothing method based on a gas cluster ion beam exhibits the advantage of there being less damage to the processed surface than the ion etching method shown in the aforementioned Patent Reference 1.
For smoothing based on a gas cluster ion beam, it is generally recognized that it is desirable for the direction of irradiation of the cluster ion beam on the surface of the object being processed to be one coming from a nearly perpendicular direction with respect to the surface being processed. This is to make maximum use of the effect of “surface smoothing based on lateral sputtering” described previously. However, in the aforementioned Patent Reference 2, it is described that, in case the surface being processed is a curved surface or the like, the irradiation may be in an oblique direction in response to that situation of the surface, but there is no mention regarding the effect in the case of irradiation be in an oblique direction. Consequently, in this Patent Reference 1, it comes about that the most efficient method for the smoothing of a solid surface is one where the beam is irradiated from a nearly perpendicular direction with respect to that surface.
Moreover, concerning the smoothing of a solid surface using a gas cluster ion beam, there is also an example in Patent Reference 3. There is no description in this Patent Reference 3 either of the relationship between the angle formed between the gas cluster ion beam and the solid surface, and the smoothing of the surface, so if one considers, from the disclosed description, that the “lateral sputtering” effect is used, one may consider that data for perpendicular irradiation are shown, in the same way as the previously indicated Patent Reference 2.
In addition, there is also an account pertaining to the smoothing of a solid surface based on gas cluster ion beam irradiation in Non-Patent Reference 1. Toyoda et al. carried out irradiating Ar cluster ions on surfaces of materials like Cu, SiC, and GaN and show a reduction in surface roughness. Even in this case, the work presented is irradiated by a gas cluster ion beam from a nearly perpendicular direction with respect to the surface.
Moreover, there are descriptions in Non-Patent Reference 2 regarding the changes in the roughness of a solid surface in the case of irradiating a gas cluster ion beam at various irradiation angles with respect to a solid surface. If the case of perpendicular irradiation with respect to the solid surface is taken to be 90° and the case of irradiation in parallel with the surface is taken to be 0°, it is shown that the sputtering rate, which is the speed at which the surface is etched, is the greatest for perpendicular irradiation and the etching rate decreases as the irradiation angle decreases. Regarding the relationship between surface roughness and irradiation angle, tests were performed by changing the irradiation angle to 90°, 75°, 60°, 45°, and 30°, and it was shown that the surface roughness increases as the irradiation angle decreases. No investigation was carried out experimentally for irradiation angles below 30°, but this may be thought to be due to the fact that it was judged to be of no use to carry out something like that, since surface roughness increases as the irradiation angle is decreased.
In addition, the majority of electronic devices such as integrated circuits and optical devices used in optical communications have concavo-convex patterns prepared by microshaping in solid surfaces or thin film material surfaces, but there is no account of using a gas cluster ion beam for the smoothing of the side wall surfaces of concave portions or convex portions in those concavo-convex patterns. This is because it was believed that it is difficult to irradiate a gas cluster ion beam nearly perpendicularly to the side wall surfaces of concave portions or convex portions or that the smoothing of side wall surfaces is not possible with the lateral sputtering mechanism.
As mentioned above, since, in the case of smoothing a solid surface by using a gas cluster ion beam, the surface roughness is the smallest when the irradiation angle of the gas cluster ion beam with respect to the solid surface is chosen to be 90°, and the surface roughness increases as the irradiation angle is decreased, it is not an exaggeration to say that no consideration has been given to cases other than making the irradiation angle nearly perpendicular.
Patent Reference 1: Japanese Patent Application Laid Open No. 1995-58089.
Patent Reference 2: Japanese Patent Application Laid Open No. 1996-120470.
Patent Reference 3: Japanese Patent Application Laid Open No. 1996-293483.
Non-Patent Reference 1: Japanese Journal of Applied Physics, Vol. 41 (2002), pp. 4287-4290.
Non-Patent Reference 2: Materials Science and Engineering, R34 (2001), pp. 231-295.
According to the smoothing method, disclosed in Patent Reference 1, based on sputtering the side wall faces of terraces protruding from the substrate surface by irradiating an Ar (argon) ion beam at an irradiation angle close to parallel with the substrate surface, e.g. at an angle of 5°, the convex portions present on the substrate surface are planed preferentially and are smoothed to a certain extent, but it is necessary to choose the irradiation energy to be at or below 100 eV in order to suppress damage to the substrate surface, in which case the ion current becomes very weak, so there has been the problem that it becomes impossible to obtain a practical sputtering speed.
The method, shown in Patent References 2 and 3 and Non-Patent References 1 and 2, of performing surface smoothing by irradiating a gas cluster ion beam on a solid surface and using “nearly perpendicularly incident lateral sputtering” reduces surface roughness to a certain extent, but it cannot cope with further reductions. Also, with this nearly vertically incident irradiation lateral sputtering by a gas cluster ion beam, there arises sputtering to a certain extent across the whole solid surface in the case of smoothing a surface, and there are cases where that amount of etching can not be disregarded. E.g., in case it is attempted to smooth a thin film material surface having a thin film with a thickness of something like several tens of nanometers with a surface roughness Ra of several nanometers, there are cases where an etching amount of several tens of nanometers is required when the surface roughness is reduced to something like 1 nm. In this case, there was the problem that a gas cluster ion beam could not be adopted for the smoothing of that thin film material.
Moreover, there was the problem that it was not possible to adopt a gas cluster ion beam for the smoothing of side wall surfaces of the concave or convex portions with which a concavo-convex pattern is formed and that was difficult to smooth these side wall surfaces sufficiently.
This invention is one which solves problems like these and has as an object to provide a surface smoothing method, and an apparatus therefor, making possible little surface damage as well as smaller surface roughness than for the case of conventional methods, with respect to a wide variety of devices and materials such as semiconductors.
The method, according to this invention, of smoothing a solid surface by using a gas cluster ion beam includes a process of irradiating the aforementioned gas cluster ion beam by making the angle formed by the aforementioned solid surface and the aforementioned gas cluster ion beam less than 30° for at least a portion of the time period of the aforementioned gas cluster ion beam irradiation process.
The smoothing apparatus according to this invention, which smoothes a solid surface by using a gas cluster ion beam, includes a gas cluster ion beam generating apparatus emitting a gas cluster ion beam and an irradiation angle setting means capable of setting the irradiation angle formed by the aforementioned solid surface with respect to the aforementioned gas cluster ion beam to less than 30°.
As explained above, according to the present invention, it is possible, in the sample surface smoothing process based on gas cluster ion beam irradiation, to make surface roughness smaller and also to make surface damage something which is smaller, than for conventional methods, by providing for the angle of the gas cluster ion beam to be less than 30° with respect to the sample surface for at least part of the time.
The mechanism of the smoothing method according to the present invention can be considered as follows. If a gas cluster ion beam irradiates a solid surface at a small angle exceeding a critical angle, the atoms or molecules forming the gas clusters recoil in a parallel direction to the solid surface without scarcely penetrating the solid surface. These recoil atoms or recoil molecules can be thought of as sputtering the protrusions of the solid surface.
At this point, if a conventional ion beam, distinct from a gas cluster ion beam, is used, in a very small domain of irradiation angles, there can be recognized an effect which at a first glance apparently resembles that of the gas cluster ion beam, but its essence is completely different. In a smoothing method using a conventional ion beam, since there is not the many-body collision effect specific to gas clusters, the phenomenon specific to gas clusters that “the atoms or molecules forming the gas clusters recoil in a parallel direction to the solid surface without scarcely penetrating the solid surface” does not occur. Consequently, the result is that the smoothing method of this invention and the smoothing method using a conventional ion beam are completely different smoothing processes. For this reason, in the surface smoothing method using a conventional ion beam, problems like those of the surface damage becoming bigger, the surface roughness reduction effect being weakened, and the processing speed becoming markedly lower are generated.
Further, the effect based on the aforementioned mechanism of the method of this invention will be called the “Oblique Incidence Surface Sputtering Effect”.
Below, the working modes of this invention will be explained by means of embodiments. First, the basic configuration of a gas cluster ion beam smoothing apparatus implementing the solid surface smoothing method of the present invention will be explained with reference to
Using a mixture of SF6 gas and He gas as the feedstock gas, an SF6 cluster ion beam was generated with a size distribution having a peak for clusters aggregating approximately 500 SF6 molecules, and the SF6 cluster ions were accelerated by 30 kV and irradiated onto sample 19 at various irradiation angles θp with the irradiation dose set to 4×1015 ions/cm2. The surface roughness of a sample film was measured before and after irradiation with an Atomic Force Microscope (AFM). The measured results are shown in
The etching amounts of the Cr film and the Si film for the case of irradiating an SF6 cluster ion beam at an irradiation angle of 25° were measured with an atomic force microscope. The results were respectively 10 nm and 340 nm. As against this, the etching amount of the Si film in the case of irradiation at 90° was 1050 nm. Further, the initial surface roughness (before irradiation) of the Cr film was 3.1 nm. Also, in order to measure the extent of damage in the surface after the smoothing process for the Si film, the profile of S (sulphur) atom penetration in the surface layer in a Si film for an irradiation angle of 25° was evaluated using the Secondary Ion Mass Spectroscopy (SIMS) method. The results were that S atoms only penetrated to a depth of something like 10 nm from the surface.
With the same conditions as in Embodiment 1 apart from setting the irradiation dose to 5×1014 ions/cm2, a Cr film was irradiated with SF6 cluster ions at an irradiation angle of 25°. The surface roughness of the Cr film after irradiation was measured using an atomic force microscope. The surface roughness Ra measured was 0.92 nm. Since the surface roughness of the Cr film for the case of an irradiation angle of 25° in
With the same apparatus as in Embodiment 1, but using Ar instead of SF6 as the feedstock gas, an Ar cluster ion beam was generated with a size distribution having a peak for clusters aggregating approximately 2000 Ar atoms, and the Ar cluster ions were accelerated by 30 kV and irradiated at various irradiation angles θp on a Cr film. The irradiation dose was set to 4×1015 ions/cm2. The surface roughness of the Cr film was measured before and after irradiation with an Atomic Force Microscope (AFM). The measured results are shown in curve (g) of
With the same conditions as in Embodiment 1, an irradiation with SF6 cluster ions was carried out for the Cr film, but on that occasion, a cycle was chosen with a continuous variation of the irradiation angle θp with respect to one sample from 90° to 0° and again with a continuous variation from 0° to 90°, the variation being carried out in cycles of 1 s. In addition, the irradiation dose was set to 5×1014 ions/cm2. The surface roughness of the Cr film after irradiation was measured using an atomic force microscope. The surface roughness Ra measured was 0.43 nm.
With the same conditions as in Embodiment 1, the Cr film was irradiated with an SF6 gas cluster ion beam, and as a first step, irradiation was carried out with an irradiation angle θp of 90°, the irradiation at this time being set to 3×1014 ions/cm2, and as a second step, the Cr film surface was irradiated at an irradiation angle θp of 25° with an irradiation dose at this time of 2×1014 ions/cm2, so as to make the total irradiation dose 5×1014 ions/cm2, the same as that in Embodiment 4. The surface roughness of the Cr film after irradiation was measured using an atomic force microscope. The surface roughness Ra measured was 0.41 nm.
A mask pattern was formed by applying a resist layer on a silicon substrate having a thermal oxide formed on it, drawing a line and space pattern (multiple parallel lines with spaces in between) by using an electron beam lithography apparatus, and developing the pattern. The line width was set to 1 μm and the space width was set to 4 μm. Through the use of a reactive ion etching apparatus, the silicon oxide layer was etched and a hard mask was formed. Subsequently, the silicon substrate was etched to a depth of something like 10 μm using radio-frequency Inductively Coupled Plasma Reactive Ion Etching (ICP-RIE).
As shown in
A mask pattern was formed by applying a resist layer on a silicon substrate having a thermal oxide formed on it, drawing an arrangement of circular patterns by using an electron beam lithography apparatus, and developing the pattern. The circular pattern diameter was set to 5 μm and the pitch of the arrangement of circular patterns was set to 10 μm. Through the use of a reactive ion etching apparatus, the silicon oxide layer was etched and a hard mask was formed. Subsequently, the silicon substrate was etched to a depth of something like 10 μm using radio-frequency Inductively Coupled Plasma Reactive Ion Etching (ICP-RIE). As shown in
Using a mixture of SF6 gas and He gas as the feedstock gas, an SF6 cluster ion beam was generated with a size distribution having a peak for clusters aggregating approximately 500 SF6 molecules, and the SF6 cluster ions were accelerated by 30 kV and irradiated onto the surface of each sample 19 with a silicon film formed thereon. The irradiation with respect to the sample surfaces being carried out in two steps, at one selected irradiation angle θp and by changing the cluster ion beam direction (bearing angle) θr in the plane of projection on the faces of the samples. Specifically, irradiation was carried out with the irradiation angles (θp, θr1) in the first step, and the irradiation angles (θp, θr2) in the second step. Note, however, that bearing angle θr2 is a relative value with θr1 as the reference, e.g. setting θr1=0°. With θp selected from the angles 5°, 10°, 20°, 25°, 30°, and 35° and with θr2 selected from the angles 3°, 5°, 10°, 15°, 20°, 30°, 45°, 70°, and 90°, irradiation was performed for the set of all (θp, θr2) angles, with respectively differing samples 8-1 to 8-54. The irradiation doses were also set to the same value of 2×1015 ions/cm2 for the first step and the second step. The roughness of the sample surfaces before and after irradiation was measured using an atomic force microscope (AFM). The measured results are shown in Table 1 in
As a sample, a Si film was deposited on a silicon substrate, by a sputtering method. Samples with a Pt film, a Ni film, an SiO2 film, and a Cr film formed respectively in the same way on a silicon substrate were irradiated in the first step with an SF6 cluster ion beam at the angles θp=10°, θr1=0°, and θr2=45° and the measured results for the roughness after irradiation were Ra=0.14 nm for the Pt film, Ra=0.1 nm for the Ni film, Ra=0.08 nm for the SiO2 film, and Ra=0.16 nm for the Cr film. Also, regarding the Si film, the profile of S atoms penetrating the surface layer in the Si film for an irradiation angle of θp=25° was evaluated using the secondary ion mass spectroscopy (SIMS) method, in order to measure the extent of damage in the surface after the smoothing process. The result was that S atoms had only penetrated to a depth of something like 10 nm from the surface.
With the same apparatus as in Embodiment 8 and using Ar as the feedstock gas, an Ar cluster ion beam was generated with a size distribution having a peak for clusters aggregating approximately 2000 Ar atoms, the Ar cluster ions were accelerated by 30 kV, and, setting the irradiation angle to θp=10°, the Si film surface was irradiated in two steps with different irradiation bearing angles θr2. The irradiation dose was set to 4×1015 ions/cm2. The surface roughness of the Si film was measured regarding samples 9-1 to 9-9 before and after irradiation with an atomic force microscope (AFM). The measured results are shown in Table 2 in
With the same conditions as in Embodiment 8, an irradiation with SF6 cluster ions was carried out for the Si film, but on that occasion, with the irradiation angle θp set to 10°, the bearing angle θr was varied continuously from 0° to 90° and was again varied continuously from 90° to 0° This roundtrip was repeated continuously at a rate of one cycle per second. Further, the irradiation dose was set to 4×1015 ions/cm2. The surface roughness of the Si film after irradiation was measured using an atomic force microscope. The surface roughness Ra measured was 0.09 nm. Also, the time of the concerned cycle was tested at 0.1 s and 5 s in the same way. The result was that the surface roughness Ra worked out to 0.08 nm and 0.09 nm, respectively.
Further, an experiment was performed in which the θr angle change quantity was set from 0° to 30°, with a cycle of 1 s. The result was that the surface roughness Ra worked out to 0.11 nm.
Line and space pattern lamellae 32 (refer to
With the exception of changing the irradiation angle θp in the first step and the second step, irradiation was carried out with a gas cluster ion beam in the same way as in Embodiment 8, by combining a number of different θp and θr angles. The measured results are shown in Table 3 in
Using a commercially available ion beam etching apparatus, an SF6 ion beam was generated, the SF6 ions were accelerated by 30 kV and irradiated on a Cr film, a Pt film, an SiO2 film, and an Si film similar to those used in Embodiments 1 and 8. The irradiation dose was set to 4×1015 ions/cm2. The surface roughness of the surfaces of various materials before and after irradiation was measured using an atomic force microscope. The result was that the surface roughness Ra of the surfaces of the various materials worked out to 2 nm or more for any irradiation condition. Also, the profile of S atoms penetrating the surface layer in the Si film was evaluated using the secondary ion mass spectroscopy (SIMS) method, in order to measure the extent of damage in the surface after the smoothing process. The result was that S atoms had penetrated as deeply as 40 to 50 nm from the surface.
A solid surface having the concavo-convex pattern shown in
With the exception of setting the irradiation angle of the gas cluster ion beam with respect to substrate surface 31a to 90°, the same conditions were chosen as in Embodiment 6. The roughness of the side wall surfaces of the concave portions or the convex portions was measured with an atomic force microscope. The surface roughness Ra measured was 3.03 nm.
A mask pattern was formed by applying a resist layer on a silicon substrate having a thermal oxide formed on it, drawing a line and space pattern by using an electron beam lithography apparatus, and developing the pattern. Using a reactive ion etching apparatus, the silicon oxide layer was etched and a hard mask was formed. Subsequently, the masked silicon substrate was irradiated with an SF6 gas cluster ion beam under the same conditions as those in Embodiment 1 and etched, but this was done in such a way that the irradiation angle θp with respect to the substrate surface became 90°. The irradiation dose at this time was set to 2×1015 ions/cm2. After this irradiation, concavo-convex surfaces of parallel linear grooves with spaces in between, i.e. a line and space pattern, were formed in the silicon substrate. The roughness of the side walls of those grooves, i.e. the side wall surfaces of the concave portions or the convex portions occurring in the solid surface having concavo-convex portions, was measured with an atomic force microscope. The surface roughness Ra measured was 2.17 nm.
Choosing basically the same conditions as in Embodiment 8 with the exception of irradiating in the first step without changing the irradiation bearing angle θr, GCIB (Gas Cluster Ion Beam) irradiation was carried out for a Si film, a Pt film, an SiO2 film, and a Cr film. The irradiation dose was set to 4×1015 ions/cm2. The measured results are shown in Table 4 in
Using a commercially available ion beam etching apparatus, an SF6 ion beam was generated, the SF6 ions were accelerated by 30 kV and irradiated on an Si film, a Pt film, an SiO2 film, and a Cr film similar to those used in Embodiment 8. The irradiation angle conditions and the irradiation dose were also chosen to be the same as in Embodiment 1. The surface roughness of the surfaces of various materials before and after irradiation was measured using an atomic force microscope. The result was that, in the same way as in Comparative Example 1, the surface roughness Ra of the surfaces of the various materials worked out to 2 nm or more for any irradiation condition. Also, the profile of S atoms penetrating the surface layer in the Si film was evaluated using the secondary ion mass spectroscopy (SIMS) method, in order to measure the extent of damage in the surface after the smoothing process, the result being, in the same way as in Comparative Example 1, that S atoms had penetrated as deeply as 40 to 50 nm from the surface.
The same conditions were chosen as in Embodiment 11, with the exception of forming a line and space pattern and adopting one type for the irradiation bearing angle θr of the gas cluster ion beam. The surface roughness of the side walls of this line and space pattern was measured with an atomic force microscope. The surface roughness Ra measured was 2.98 nm.
By referring to Embodiment 1, Embodiment 3, and Comparative Example 1, the following can be seen. As the irradiation angle θp of a gas cluster ion beam is decreased from 90° (vertical irradiation), the surface roughness increases relatively monotonically down to an irradiation angle θp of 30°. When the irradiation angle θp becomes smaller than 30°, it is seen that the surface roughness is reduced abruptly, and moreover, that it even becomes smaller than the surface roughness in the case of irradiation at 90°. Even if irradiation angle θp is decreased further, the state of small surface roughness continues, but when it reaches a value less than 1°, the surface roughness again increases abruptly.
In the state of 0° irradiation, the solid surface is hardly etched, and in this case, the value of the surface roughness can be considered to be one which reflects the surface roughness of the initial state of the various films. What should be paid attention to here is that in case irradiation is carried out at less than 30°, a fairly low surface roughness is realized compared to the case of nearly perpendicular irradiation. This result is one which indicates that it is possible, compared to conventional solid surface smoothing methods based on nearly perpendicular irradiation, to make surface roughness considerably smaller with the solid surface smoothing method of the present invention.
Also, since similar results are obtained even in the cases of using chemically reactive SF6 gas and chemically inert Ar gas as gas cluster types, it is seen that the solid surface smoothing method according to this invention does not depend on the type of gas cluster. Further, as for the types of smoothed materials, since similar results are obtained for chemically reactive Si and chemically inert Pt with respect to SF6 clusters, it is seen that the solid surface smoothing method according to this invention does not depend on the type of material smoothed.
In the results for a conventional ion beam, which is not a gas cluster, of Comparative Example 1, no marked smoothing of solid surfaces can be seen, so the superiority of this invention using gas cluster ion beams can be confirmed.
In addition, if one attempts to compare the extent of damage occurring in the surfaces after the smoothing process, S atoms penetrate and inflict damage as deep as 40 to 50 nm from the surface with methods based on conventional ion beams, whereas they only inflict damage at 10 nm or less with the present invention, so it is seen that it is possible to implement a solid surface smoothing method with very low damage by using the present invention.
Further, if one attempts to look at the etching amount of the solid surface during the smoothing process, with the perpendicular irradiation according to the conventional methods, there is a very large etching amount for the Si film, 1050 nm, but with 25° incidence conditions according to the present invention, the Si film etching amount works out to 340 nm, one third or less of the conventional amount, so it is seen that it is possible to implement surface smoothing with a remarkably low etching amount. With a Cr film having an initial roughness of 3.1 nm, even with a roughness of something like 0.5 nm after irradiation, the etching amount does not exceed 10 nm. By this effect of a small etching amount, it is seen that this invention is suitable for smoothing, etc., of thin-film materials.
Next, the following can be seen by referring to Embodiments 4 and 5. By irradiating the gas cluster ion beam while varying the angle formed by the solid surface and the gas cluster ion beam, not irradiating at only a single gas cluster ion beam irradiation angle θp, it is seen that it is possible to reduce surface roughness in a short time (with a condition of a small irradiation dose). Also, even by using an irradiation angle θp of 90° in the first step and using an irradiation angle θp of 25° in the second step, as the angles formed by the solid surface and the gas cluster ion beam, it is seen that it is possible to reduce surface roughness in a short time (with a condition of a small irradiation dose). From the graph shown in
It is considered that this method of changing the irradiation angle θp and using a second-step angle is particularly valid for the following samples. In the case that the surface of the sample is relatively smooth, it is considered that it is the most valid to choose an irradiation angle θp of this invention to be less than 30°, but in the case that the roughness of the surface is relatively large, it results that, when looking at the micro level, there are domains present which have various angles in the surface. In the case of domains like these having various angles in the surface, there are cases when it is more efficient to smooth with an e.g. nearly perpendicular irradiation. As is evident when looking at
If one considers the vicinity of 25°, which lies inside the valid range of irradiation angles evident from this
From the explanation above and the graph of
The number of times that the continuous change in this irradiation angle θp is repeated may be 1 or higher within the time of the entire smoothing process, but it is more effective to choose a number of several tens of times to more than several hundreds of times. Consequently, the rate at which the irradiation angle is changed is not one which is limited to 1 cycle per second, as shown in Embodiment 4.
Next, it will be investigated in which proportions the first step and the second step in Embodiment 5 should be performed. In Embodiment 5, the initial surface roughness Ra (average value) is 3.1 nm, and Rmax (peak value) is something like 30 nm. When the surface is smoothed, Ra is changed to 0.41 nm and Rmax to something like 4 nm, but since the surface of the initial condition has concave-convex portions, it exhibits a shape having a variety of angles, if one looks at the microscopic level. It is expected that the surface has an angular distribution of something like 30°. If this angular distribution is large, in case smoothing is carried out by irradiation according to this invention, and the irradiation angle θp is chosen to be e.g. 15°, the result is that there is a domain which is actually irradiated at 45° (15°+30°), so the efficiency is bad in this region, i.e. if one looks at the microscopic level, the result is that there is a domain which is not smoothed. Consequently, since by making the angular distribution of this surface, viewed from a microscopic level, be 15° or less in the first step, it becomes 30° (15°+15°), so it can be considered that the smoothing efficiency rises. In the example of Embodiment 5, by making Ra something like half (1.5 nm), the surface can be considered to fall within the range described above (actually, it can be considered, for the reason mentioned below, that a reduction by as much as half is not necessary). The fact of reducing this Ra to something like half is nearly equivalent to carrying out the irradiation in the first step to something like half the initial roughness.
This example is a typical industrial application example, but since there are actually various cases, irradiation may be carried out in the first step as far as e.g. reducing the surface roughness by 10% of the initial value or more (to 90% or less). This is because, if the smoothing of a face with large angles due to concave-convex portions of the surface viewed on a microscopic level is carried out to reduce the surface roughness as much as the aforementioned 10%, it is expected that it will fall within the aforementioned range (an angular distribution viewed at the microscopic level of something like 15% or less) because the efficiency of smoothing by irradiating a gas cluster ion beam is high (stated the other way round, it takes more time to further reduce something which has small roughness).
Regarding the second step, it is efficient to allot to the second step approximately 10% or more of the whole processing time for the first step and the second step. The reason for that is that, in Embodiment 5 based on the following, the processing time is on the order of 10 to 30 minutes with the current apparatus, but after processing in the first step, the surface roughness Ra of 3.1 nm has become something like 1 nm. Because the roughness of 1 nm is changed to something like 0.4 nm in the second step, a processing time equal to or greater than the time needed for smoothing the difference in absolute Ra values becomes necessary, i.e. 1 nm−0.4 nm=0.6 mm as against 3.1 nm−1 nm=2.1 nm, so the result is that a time equal to or greater than 20% of the whole processing time needs to be allotted to the second step. Generally, as in the aforementioned first step, it is acceptable to allot to the second step approximately 10% or more of the total processing time for the first step and the second step, as mentioned above.
As mentioned above, according to this invention, in case the irradiation angle θp is chosen to have a fixed value of less than 30°, and in case two steps are chosen, various modes like the repetition of a continuous variation can be considered. In the apparatus of this invention, shown in
When a fixed mode is set by manipulating mode setting part 27a in setting part 27 and the targeted irradiation angle θp is input by manipulating angle setting part 27b, “Fixed” is displayed in mode area 26b of display part 26, the set irradiation angle is displayed in set angle area 26c, and a motor 23, driven via control part 28 and drive part 29, is controlled so that the actual angle θc becomes the set angle θp.
When a two-step mode setting is input and θp1, θp2 are input in order as settings for the irradiation angles, “Two-step” is displayed in the mode area, the initial setting angle θp1 is displayed in set angle area 26c and the second-time setting angle θp2 is set in set angle area 26d, respectively, and the drive of motor 23 is controlled so that, on the occasion of the aforementioned first-step processing by control part 28, the current angle θc becomes the angle θp1 of set angle area 26c. On the occasion of the second-step processing, the drive of motor 23 is controlled so that θc becomes the angle θp2 of set angle area 26d.
When the continuous variation mode setting is input and θp1, θp2 are sequentially input as settings for the angles, “Continuous variation” is displayed in the mode area, set angles θp1 and θp2 are displayed in set angle areas 26c and 26d, and motor 23 is controlled so that the irradiation angle θp with respect to the beam is repeatedly moved back and forth by control part 28 between the two set angles θp1 and θp2.
Control part 28 is a part in which the irradiation angle setting program for the aforementioned various displays, the various drives of motor 23, and so forth, is executed by means of a CPU (Central Processing Unit) or a microprocessor. Setting part 27 is an input means for the keyboard, etc. This mode and angle setting device is installed in the control apparatus of a smoothing processing apparatus capable of setting various conditions for this smoothing process. Further, the smoothing apparatus of this invention may also be an apparatus in which the irradiation angle θp is fixed to less than 30°, i.e. an apparatus in which the irradiation angle θp can not be varied.
When the irradiation dose varies, the etched amount of material varies, this etching amount being nearly proportional to the irradiation dose. Also, directly after the start of the irradiation, the surface roughness is decreased, together with the increase in the irradiation dose, but when the surface roughness is decreased to a certain extent, it never occurs that the surface roughness decreases beyond that. This is something close to the region in which, regarding the irradiation doses used in each of the previous embodiments, the surface roughness decreases to a certain extent but does not decrease beyond this. Since the relationship between irradiation dose and surface roughness is the above-mentioned relationship, the irradiation dose may have a small value, there being no minimum value for the dose. It is generally preferable to use the smallest irradiation dose possible to implement the targeted surface roughness. This is because manufacturability is normally higher with a shorter smoothing process time, because it is frequent that the smoothed materials are film materials, and because it is desirable to have a smaller reduction of film thickness (etching amount) accompanying the smoothing.
In each of the embodiments above, the accelerating voltage was assumed to be 30 kV. The higher the accelerating voltage is, the greater the etching amount becomes, but it can be seen that the processing time becomes shorter. However, the relationship between accelerating voltage and surface roughness is currently not understood. Consequently, it is acceptable to determine the accelerating voltage as well, by various conditions like the time and material required for the smoothing process, and it may be chosen to be in the range of something like 10 to 45 kV.
Further, the following can be seen by referring to Embodiment 6, Embodiment 7, and Comparative Examples 2 to 4. The roughness values of the side wall surfaces of the concave portions or the convex portions in a solid surface provided with a concavo-convex pattern differ markedly by etching method and the processing method thereof. In the conventional etching method shown in Comparative Example 2, it is seen that the magnitude of the roughness of the side walls of the concave portions or the convex portions is great. Even if using the gas cluster ion beam shown in Comparative Example 3 and Comparative Example 4, it is seen that surface roughness does not diminish in the case that the irradiation angle of the beam is perpendicular to the surface desired to be smoothed, i.e. if the irradiation angle θp with the surface (the side wall surfaces of concave portions or convex portions) desired to be smoothed is 90°. Compared to that, by making the irradiation angle θp with the surface desired to be smoothed greater than 0° and smaller than 30°, as in Embodiment 6 of the present invention, it becomes possible to markedly reduce the roughness of the side wall surfaces of the concave portions or the convex portions. Also, it is seen that this invention can be applied effectively to side wall surfaces of concave portions or convex portions which are not plane surfaces, like curved surfaces, as described in Embodiment 7.
In this way, it is seen that this invention can be applied not only to smooth solid surfaces but also to the smoothing of side wall surfaces of concave portions or convex portions occurring in surfaces with concavo-convex patterns formed by etching and the like, as well as to planes and curved surfaces having various angles. This is to say that side wall surfaces of concave portions or convex portions do not have to be perpendicular faces with respect to the substrate. Moreover, even regarding the smoothing of side wall surfaces of concave portions or convex portions, it may be appreciated that effective smoothing is possible by continuously varying the angle θp, as in Embodiment 4, or by two-step irradiation with changed angles θp, as in Embodiment 5.
In the foregoing, an investigation was carried out within an irradiation angle range from 0° to 90°, since it is evident that the surface roughness characteristics with respect to the irradiation angle in
The following can be seen by referring to Embodiment 8 and Comparative Example 5. It is seen that, if irradiation is carried out in two steps at two different bearing angles θr in the plane of projection of the beam on the sample face with respect to the irradiation angle θp of the gas cluster ion beam, the surface roughness becomes smaller than for the same irradiation dose at a single angle θr. It is also seen that the surface roughness effect is further increased, if the value of this second-step angle θr is 5° or more.
With reference to Embodiments 8 and 9 and Comparative Example 5, it is seen that the surface roughness reduction effect due to using a second-step bearing angle θr does not depend on the type of sample or on the type of gas cluster. Also, regarding the angle θp, it is seen that there is a marked effect at 30° or less.
In the result due to a conventional ion beam, distinct from a gas cluster ion beam, of Comparative Example 6, noticeable smoothing of the solid surface similar to the case of Comparative Example 1 can not be observed, so the superiority of this invention using the gas cluster ion beam of Embodiment 8 can be confirmed. The reason why noticeable smoothing does not occur for a conventional ion beam and noticeable smoothing does occur for a gas cluster ion beam of the present invention can be considered in the following way. If a gas cluster ion beam is irradiated obliquely, the clusters collide and recoil, but the recoil directions thereof are mostly distributed in directions within the face of the concerned solid surface. This can be thought of as a mechanism similar to the “lateral sputtering” occurring in the case of vertical irradiation of the gas cluster ion beam on the solid surface. In the case of oblique irradiation at e.g. θp=20°, the recoiling atoms or molecules are mostly distributed at angles for which θp is less than 20°. The result is that, in this way, recoiling atoms or molecules collide again with the protrusions of the solid surface and smooth the pointed ends of the protrusions. Moreover, in case a conventional ion beam is irradiated obliquely, and if θp=20°, the recoiling atoms or molecules have angles with a distribution centered on 20°, the same as the irradiation angle. The result is that, in the case of this conventional ion beam, the probability that recoil atoms or molecules smooth the protrusions becomes very small.
Next, it will be attempted to reflect on the distribution of bearing angle θr directions. If a gas cluster ion beam is irradiated obliquely, it recoils with a distribution of the θr angles as well. The distribution range is wider than for the case of a conventional ion beam, but since there is a distribution, a texture parallel to the irradiation angle is formed. The dimensions of this texture restrict the reduction in surface roughness. Moreover, an attempt will be made to consider the case of irradiating beams from at least two types of directions on the plane of projection of the solid surface. It was discovered for the first time with this invention that, if a cluster ion beam is irradiated from the concerned second type of direction, the formation of a texture formed in parallel with the concerned irradiation direction is noticeably suppressed. This is a characteristic that can not be observed with a conventional ion beam.
By mechanisms like these, the superiority of the present invention can be explained.
In addition, if one attempts to compare the extent of damage occurring in the surface after the smoothing process, as against a situation with S atoms penetrating and inflicting damage as deeply as 40 to 50 nm from the surface with a method based on a conventional ion beam, in the same way as in Comparative Example 1, they only inflict damage at 10 nm or less with this invention, so it is seen that it is possible to implement smoothing with very low damage of a solid surface by using this invention.
By referring to Embodiments 8 and 10, even in the case of choosing two steps for the angle θr or in the case of continuously varying the angle, it is seen that there is an effect of reducing the surface roughness in the same way. It is seen that this is something for which it is essentially important to choose a condition in which the angle θr is not single, but does not depend on the number of multiple steps which do not have to be two steps but can e.g. be three steps or four steps. Also, it is seen that the range of angles continuously varied may also be arbitrary.
By referring to Embodiment 11 and Comparative Example 7, it is seen that the effect of reducing surface roughness by a method with the angle θr not being fixed, like changing it in two steps or continuously varying it, can also be applied to the pattern side wall surfaces. From this result, it is seen that it is possible to apply the solid surface smoothing method of the present invention to three-dimensional and complex surfaces, curved surfaces, and the like.
By referring to Embodiment 8 and Embodiment 12, it is seen that the effect of reducing surface roughness by using two-step bearing angles θr is higher when the first-step angle θp and the second-step angle θp are the same. This phenomenon is something which has become experimentally evident for the first time with this invention. This can be thought of in the following way. Regarding the smoothing effect of the solid surface, it is seen that there is not much θp dependence due to the irradiation of the first step in the domain θp<30°, as shown in Comparative Example 5. However, as shown by the atomic force spectroscopy photographs after smoothing by irradiation with a cluster ion beam, for samples 5-3 and 5-2 in
When looking at
As mentioned above, according to this invention, in case the irradiation angle θr is chosen to have a fixed value of less than 30°, and in case two steps are chosen, various modes like the repetition of a continuous variation can be considered. In the smoothing apparatus taking into account the execution of Embodiments 8 to 11, the apparatus is set up to enable a mode setting and irradiation angle (θp, θr) settings. As e.g. shown in
When a fixed mode is set by manipulating mode setting part 27a in setting part 27 and the targeted irradiation angle θp is input by manipulating angle setting part 27b, “Fixed” is displayed in mode area 26b in display part 26, the set irradiation angle is displayed in set angle area 26c, and a motor 23, driven via control part 28 and drive part 29, is controlled so that the actual angle θc becomes the set angle θp.
When a two-step mode setting is input and θp, θr1, θr2 are input in order as settings for the irradiation angles, “Two-step” is displayed in the mode area, the initial setting angle θp is displayed in set angle area 26c and the set angles θr1 and θr2 are set in set angle area 26d, respectively, and the drive of motor 23 is controlled so that the current angle θc, on the occasion of the aforementioned first-step processing by control part 28, becomes the angle θp, and motor 42 is controlled so that the rotation angle θr of rotary disk 41 becomes θr1. In the second-step processing, the angle θp is maintained as is and the drive of motor 42 is controlled so that the angle θr becomes the angle θr2.
When the continuous variation mode setting is input and θp, θr1, θr2 are input in order as settings for the angles, “Continuous variation” is displayed in the mode area, and motor 23 is controlled by control part 28 so that the irradiation angle becomes θp, and motor 42 is further repeatedly moved back and forth so as to change continuously between the two set angles θr1 and θr2.
Control part 28 is a part in which the irradiation angle setting program for the aforementioned various displays, the various drives of motors 23 and 42, and so forth, are executed by means of a CPU (Central Processing Unit) or a microprocessor. Setting part 27 is an input means for the keyboard, etc. This mode and angle setting device is installed in the control apparatus of a smoothing processing apparatus capable of setting various conditions for this smoothing process.
As is evident from the description above, the gas types used for gas cluster ion beams are not limited to SF6 or Ar but can be of any type and, moreover, apparatus conditions and experimental parameters like irradiation conditions and cluster sizes are not particularly restricted, any conditions and parameters being acceptable.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-339566 | Sep 2003 | JP | national |
| 2004-072642 | Mar 2004 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10573942 | Mar 2006 | US |
| Child | 12642633 | US |