Thermally-inhibited non-pregelatinized granular starches and flours and process for their preparation

FIELD OF THE INVENTION
This invention relates to starches and flours that are inhibited and to a process for their preparation. The inhibited starches and flours may be used in place of the chemically crosslinked (i.e., chemically inhibited) starches and flours presently used in foods and in the manufacture of industrial products.
BACKGROUND OF THE INVENTION
Heat Treatment of Starches and Flours
Heat/moisture treatment and annealing of starches and/or flours are taught in the literature and distinguished by the amount of water present. "Annealing" involves slurrying a granular starch with excess water at temperatures below the starch's or flour's gelatinization temperature. "Heat/moisture-treatment" involves a semi-dry treatment at temperatures below the starch's or flour's gelatinization temperature, with no added moisture and with the only moisture present being that normally present in a starch granule (which is typically 10% or more).
In the following discussion, a history of the various heat/moisture and annealing treatments of starch and/or flour is set out.
GB 263,897 (accepted Dec. 24, 1926) discloses an improvement in the heat treatment process of GB 228,829. The process of the U.S. Pat. No. '829 involves dry heating flour or wheat to a point at which substantially all of the gluten is rendered non-retainable in a washing test and then blending the treated flour or wheat with untreated flour or wheat to provide a blend having superior strength. The improvement of the U.S. Pat. No. '897 is continuing the dry heating, without, however, gelatinizing the starch, for a considerable time beyond that necessary to render all of the gluten non-retainable. "Dry-heating" excludes heating in a steam atmosphere or an atmosphere containing considerable quantities of water vapor which would tend to gelatinize the starch. The wheat or flour may contain the usual amount of moisture, preferably not greater than 15%. The heat treatment may exceed 7 hours at 77-93.degree. C. (170-200.degree. F.), e.g., 8 to 14 hours at 82.degree. C. (180.degree. F.) or 6 hours at 100.degree. C. (212.degree. F.).
GB 530,226 (accepted Dec. 6, 1940) discloses a method for drying a starch cake containing about 40-50% water with hot air or another gas at 149.degree. C. (300.degree. F.) or above without gelatinizing the starch. The starch cake is disintegrated by milling it to a finely divided state prior to drying.
GB-595,552 (accepted Dec. 9, 1947) discloses treatment of starch, more particularly a corn starch, which involves drying the starch to a relatively low moisture content of 1-2%, not exceeding 3%, and subsequently dry heating the substantially moisture-free starch at 115-126.degree. C. for 1 to 3 hours. The treatment is intended to render the starch free from thermophilic bacteria. The starch should not be heated longer than necessary to effect the desired sterilization.
U.S. Pat. No. 3,490,917 (issued Jan. 20, 1970 to C.A.F. Doe et al.) discloses a process for preparing a non-chlorinated cake flour suitable for use in cakes and sponges having a high sugar to flour ratio. The starch or a flour in which the gluten is substantially or completely detached from the starch granules is heated to a temperature of from 100-140.degree. C. and then cooled. The conditions are selected so that dextrinization does not occur, e.g., about 15 minutes at 100-115.degree. C. and no hold and rapid cooling at the higher temperatures. The heat treatment should be carried out under conditions which allow the water vapor to escape. The reduction in moisture content due to the heat treatment depends upon the temperature employed. At treatment temperatures of 100-105.degree. C., the moisture content is reduced from 10-12% to 8-9%, by weight, while at medium and high temperatures the moisture content is typically reduced to 7% or less. Preferably, during cooling the moisture is allowed to reach moisture equilibrium with the atmosphere. The gelatinization temperature of the heat treated starch or flour is approximately 0.5-1.degree. C. higher than that of a comparable chlorinated flour or starch. The heating can be carried out in many ways, including heating in a hot air fluidized bed.
U.S. Pat. No. 3,578,497 (issued May 11, 1971 to E. T. Hjermstad) discloses a process for non-chemically improving the paste and gel properties of potato starch and imparting a swelling temperature as much as 20 to 30.degree. F. higher. A concentrated suspension (20-40% dry solids) at a neutral pH (5.5-8.0, preferably 6-7.5) is heated either for a long time at a relatively low temperature or for a short time at successively higher temperatures. The suspension is first heated at a temperature below the incipient swelling temperature of the particular batch of starch being treated (preferably 49.degree. C.-120.degree. F.). Then the temperature is gradually raised until a temperature well above the original swelling temperature is attained. It is essential that swelling be avoided during the different heating periods so that gelatinization does not occur. After this steeping treatment the starch has a higher degree of granular stability. It resists rapid gelatinization and produces a rising or fairly flat viscosity curve on cooling. The pastes are very short textured, non-gumming, non-slimy, cloudy and non-cohesive. They form firm gels on cooling and aging.
U.S. Pat. No. 3,977,897 (issued Aug. 31, 1976 to Wurzburg et al.) discloses a method for preparing non-chemically inhibited amylose-containing starches. Both cereal and root starches can be inhibited, but the inhibition effects are more observable with root starches. Amylose-free starches, such as waxy corn starch, show no or very slight inhibition. The Brabender viscosity of cooked pastes derived from the treated starch was used to determine the inhibition level. Inhibition was indicated by a delayed peak time in the case of the treated corn starch, by the lack of a peak and a higher final viscosity in the case of the treated achira starch, and by the loss of cohesiveness in the case of the treated tapioca starch. The granular starch is suspended in water in the presence of salts which raise the starch's gelatinization temperature so that the suspension may be heated to high temperatures without causing the starch granules to swell and rupture yielding a gelatinized product. The preferred salts are sodium, ammonium, magnesium or potassium sulfate; sodium, potassium or ammonium chloride; and sodium, potassium or ammonium phosphate. About 10-60 parts of salt are used per 100 parts by weight of starch. Preferably, about 110 to 220 parts of water are used per 100 parts by weight of starch. The suspension is heated at 50-100.degree. C., preferably 60-90.degree. C., for about 0.5 to 30 hours. The pH of the suspension is maintained at about 3-9, preferably 4-7. Highly alkaline systems, i.e., pH levels above 9 retard inhibition.
U.S. Pat. No. 4,013,799 (issued Mar. 22, 1977, to Smalligan et al.) discloses heating a tapioca starch above its gelatinization temperature with insufficient moisture (15 to 35% by total weight) to produce gelatinization. The starch is heated to 70-130.degree. C. for 1 to 72 hours. The starch is used as a thickener in wet, pre-cooked baby foods having a pH below about 4.5.
U.S. Pat. No. 4,303,451 (issued Dec. 1, 1981 to Seidel et al.) discloses a method for preparing a pregelatinized waxy maize starch having improved flavor characteristics reminiscent of a tapioca starch. The starch is heat treated at 120-200.degree. C. for 15 to 20 minutes. The pregelatinized starch has gel strength and viscosity characteristics suitable for use in pudding mixes.
U.S. Pat. No. 4,303,452 (issued Dec. 1, 1981 to Ohira et al.) discloses smoking a waxy maize starch to improve gel strength and impart a smoky taste. In order to counteract the smoke's acidity and to obtain a final product with a pH of 4-7, the pH of the starch is raised to pH 9-11 before smoking. The preferred water content of the starch during smoking is 10-20%
The article "Differential Scanning Calorimetry of Heat-Moisture Treated Wheat and Potato Starches" by J. W. Donovan et al. in Cereal Chemistry, Vol. 60, No. 5, pp. 381-387 (1983) discloses that the gelatinization temperature of the starches increased as a result of the heat/moisture treatment or annealing. See also the article "A DSC Study Of The Effect Annealing On Gelatinization Behavior Of Corn Starch" by B. R. Krueger et al. in Journal of Food Science, Vol. 52, No. 3, pp. 715-718 (1987).
U.S. Pat. No. 4,391,836 (issued Jul. 5, 1983 to C.-W. Chiu) discloses instant gelling tapioca and potato starches which are non-granular and which have a reduced viscosity. Unmodified potato and tapioca starches do not normally gel. The starches of the patent are rendered non-granular and cold-water-dispersible by forming an aqueous slurry of the native starch at a pH of about 5-12 and then drum-drying the slurry. The starches are rendered gelling by heat treating the drum-dried starch for about 1.5 to 24 hours at 125-180.degree. C. to reduce the viscosity to within defined Brabender viscosity limitations.
U.S. Pat. No. 4,491,483 (issued Jan. 1, 1985 to W. E. Dudacek et al.) discloses subjecting a semi-moist blend of a granular starch with at least 0.25 wt. % of a fatty acid surfactant and sufficient water (about 10-40 wt. %) to a heat-moisture treatment at from about 50-120.degree. C., followed by drying to about 5-15 wt. %, preferably 10 wt. %, moisture.
The heat-moisture treated starch-surfactant product is characterized by a hot water dispersibility of from about 60-100% and a higher pasting temperature than the granular starch from which it is derived. Preferably, the treatment takes place in a closed container so that the moisture can be maintained at a constant level. The preferred conditions are 3 to 16 hours at 60-90.degree. C. Degradation and dextrinization reactions are undesirable as they destroy the thickening ability of the starch. The use of conditions, such as, e.g., 35% moisture at 90.degree. C. for 16 hours results in reduced paste viscosity. It is believed the presence of the surfactant during the treatment permits formation of a complex within the partially swollen starch matrix with straight chain portions of the starch molecules. The limited moisture environment allows complex formation without gelatinization.
Japanese Patent Publication No. 61-254602, (published Dec. 11, 1987) discloses a wet and dry method for heating waxy corn starch and derivatives thereof to impart emulsification properties. The wet or dry starch is heated at 100-200.degree. C., preferably 130-150.degree. C., for 0.5 to 6 hours. In the dry method, the water content is 10%, preferably 5%, or less. In the wet method, the water content is 5 to 50%, preferably 20-30%. The pH is 3.5-8, preferably 4-5.
The article "Hydrothermal Modification of Starches: The Difference between Annealing and Heat/Moisture-Treatment", by Rolf Stute, Starch/Starke Vol. 44, No. 6, pp. 205-214 (1992) reports almost identical modifications in the properties of potato starch with annealing and heat/moisture treatments even through the alteration of the granular structure is different. The Brabender curves of the heat/moisture-treated and annealed potato starches show the same typical changes, including a higher gelatinization temperature and a lower peak viscosity or no peak. The DSC curves also show a shift to higher gelatinization temperatures for both treatments. A combined treatment involving annealing a heat/moisture-treated potato starch leads to a further increase in gelatinization temperature without detectable changes in gelatinization enthalpy and with retention of the viscosity changes caused by the heat treatment. A combined treatment involving annealing a heat/moisture-treated potato starch does not lower the gelatinization temperature, when compared to the base starch, and increases the gelatinization temperature at higher heat/moisture treatment levels.
Chemical Crosslinking of Starches and Flours
Starches are chemically modified with difunctional reagents, such as phosphorus oxychloride, sodium trimetaphosphate, mixed adipic/acetic anhydride, and epichlorohydrin, to produce chemically crosslinked starches having excellent tolerance to processing variables such as heat, shear, and pH extremes. Such chemically crosslinked (also referred to as "inhibited" starches) provide a desirable smooth texture and possess viscosity stability throughout the processing operation and normal shelf life.
In contrast, unmodified (i.e., non-crosslinked) starches breakdown in viscosity, lose thickening capacity and textural qualities, and behave unpredictably during storage as a result of the stresses encountered during processing. Heat, shear, and/or an extreme pH, especially an acidic pH, tend to fully disrupt the starch granules and disperse the starch.
When native starch granules are dispersed in water and heated, they become hydrated and swell at about 60.degree. C., and reach a peak viscosity through the 65.degree.-95.degree. C. range. This increase in viscosity is a desired property in many food and industrial applications and results from the physical force or friction between the highly swollen granules. Swollen, hydrated starch granules, however, are quite fragile. As the starch slurry is held at temperatures of 92.degree.-95.degree. C., the starch granules begin to fragment and the viscosity breaks down. Shear or conditions of extreme pH also tend to disrupt and fragment the granules, so that the starch polymers dissociate and become solubilized, leading to a rapid breakdown from the initially high viscosity.
It has been known that both the swelling of the starch granules and the breakdown in viscosity can be inhibited by treating the starch with chemical reagents that introduce covalent intermolecular bridges or crosslinks between the starch molecules. The crosslinks reinforce the associative hydrogen bonds holding the granules together, restrict the swelling of the starch granules, and consequently inhibit disruption and fragmentation of the granules. Because of this inhibition, crosslinked starches are also called inhibited starches.
Because chemically crosslinked starches are used in many applications where a stable-viscosity starch paste is needed, it would be an advantage in cost, time, and in the reduction of the use of chemicals, if native or modified starch could be "inhibited" to perform in the same way as chemically crosslinked starch without the use of chemicals.
SUMMARY OF THE INVENTION
Non-pregelatinized starches and flours are thermally inhibited, without the addition of chemical reagents, in a heat treatment process that results in the starch or flour becoming and remaining inhibited. The starches and flours are referred to as "inhibited" or "thermally-inhibited" (abbreviated "T-I"). When these thermally-inhibited starches and flours are dispersed and/or cooked in water, they exhibit the textural and viscosity properties characteristic of a chemically-crosslinked starch. The starch granules are more resistant to viscosity breakdown. This resistance to breakdown results in what is subjectively considered a non-cohesive or "short" textured paste, meaning that the gelatinized starch or flour tends to be salve-like and heavy in viscosity rather than runny or gummy.
The non-pregelatinized thermally-inhibited granular starches and flours exhibit an unchanged or reduced gelatinization temperature. In contrast, most annealed and heat/moisture treated starches show an increased gelatinization temperature. Chemically-crosslinked starches show an unchanged gelatinization temperature. It is believed the overall granular structure of the thermally-inhibited starches and flours has been altered.
The starches and flours that are substantially completely thermally inhibited will resist gelatinization. The starches and flours that are highly inhibited will gelatinize to a limited extent and show a continuing rise in viscosity but will not attain a peak viscosity. The starches and flours that are moderately inhibited will exhibit a lower peak viscosity and a lower percentage breakdown in viscosity compared to the same starch that is not inhibited. The starches and flours that are lightly inhibited will show a slight increase in peak viscosity and a lower percentage breakdown in viscosity compared to the same starch that is not inhibited.
The starches and flours are inhibited by a process which comprises the steps of dehydrating the starch or flour until it is anhydrous or substantially anhydrous and then heat treating the anhydrous or substantially anhydrous starch or flour at a temperature and for a period of time sufficient to inhibit the starch or flour. As used herein, "substantially anhydrous" means containing less than 1% moisture by weight. The dehydration may be a thermal dehydration or a non-thermal dehydration such as alcohol extraction or freeze drying. An optional, but preferred, step is adjusting the pH of the starch or flour to neutral or greater prior to the dehydration step.
Depending on the extent of the heat treatment, various levels of inhibition can be achieved. For example, lightly inhibited, higher viscosity products with little breakdown, as well as highly inhibited, low viscosity products with no breakdown, can be prepared by the thermal inhibition processes described herein.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
All starches and flours are suitable for use herein. The thermally-inhibited starches and flours can be derived from any native source. A "native" starch or flour is one as it is found in nature in unmodified form. Typical sources for the starches and flours are cereals, tubers, roots, legumes and fruits. The native source can be corn, pea, potato, sweet potato, banana, barley, wheat, rice, sago, amaranth, tapioca, sorghum, waxy maize, waxy pea, waxy wheat, waxy tapioca, waxy rice, waxy barley, waxy potato, waxy sorghum, starches having an amylose content of 40% or greater and the like. Preferred starches are waxy starches, potato, tapioca and corn (including waxy maize, waxy tapioca, waxy pea, waxy wheat, waxy rice, waxy potato, waxy sorghum, and waxy barley.
The thermal inhibition process may be carried out prior to or after other starch or flour reactions used to modify starch or flour. The starches may be modified by conversion (i.e., acid-, enzyme-, and/or heat-conversion), oxidation, phosphorylation, etherification (e.g., by reaction with propylene oxide), esterification (e.g., by reaction with acetic anhydride or octenylsuccinic anhydride), and/or chemical crosslinking (e.g., by reaction with phosphorus oxychloride or sodium trimetaphosphate). The flours may be modified by bleaching or enzyme conversion. Procedures for modifying starches are described in the Chapter "Starch and Its Modification" by M. W. Rutenberg, pages 22-26 to 22-47, Handbook of Water Soluble Gums and Resins, R. L. Davidson, Editor (McGraw-Hill, Inc., New York, N.Y. 1980).
Native granular starches have a natural pH of about 5.0-6.5. When such starches are heated to temperatures above about 125.degree. C. in the presence of water, acid hydrolysis (i.e., degradation) of the starch occurs. This degradation impedes or prevents inhibition. Therefore, the dehydration conditions need to be chosen so that degradation is avoided. Suitable conditions are dehydrating at low temperatures and the starch's natural pH or dehydrating at higher temperatures after increasing the pH of the starch to neutral or above. As used herein, "neutral" covers the range of pH values around pH 7 and is meant to include from about pH 6.5-7.5. A pH of at least 7 is preferred. More preferably, the pH is 7.5-10.5. The most preferred pH range is above 8 to below 10. At a pH above 12, gelatinization more easily occurs. Therefore, pH adjustments below 12 are more effective. It should be noted that the textural and viscosity benefits of the thermal inhibition process tend to be enhanced as the pH is increased, although higher pHs tend to increase browning of the starch or flour during the heat treating step.
To adjust the pH, the non-pregelatinized granular starch or flour is typically slurried in water or another aqueous medium, in a ratio of 1.5 to 2.0 parts of water to 1.0 part of starch or flour, and the pH is raised by the addition of any suitable base. Buffers, such as sodium phosphate, may be used to maintain the pH if needed. Alternatively, a solution of a base may be sprayed onto the powdered starch or flour until the starch or flour attains the desired pH, or an alkaline gas such as ammonia can be infused into the starch or flour. After the pH adjustment, the slurry is then either dewatered and dried, or dried directly, typically to a 2-15% moisture content. These drying procedures are to be distinguished from the thermal inhibition process steps in which the starch or flour is dehydrated to anhydrous or substantially anhydrous and then heat treated.
Suitable bases for use in the pH adjustment step include, but are not limited to, sodium hydroxide, sodium carbonate, tetrasodium pyrophosphate, ammonium orthophosphate, disodium orthophosphate, trisodium phosphate, calcium carbonate, calcium hydroxide, potassium carbonate, and potassium hydroxide, and any other bases approved for use under the applicable regulatory laws. The preferred base is sodium carbonate. It may be possible to use bases not approved provided they can be washed from the starch or flour so that the final product conforms to good manufacturing practices for the desired end use.
A thermal dehydration is carried out by heating the starch or flour in a heating device for a time and at a temperature sufficient to reduce the moisture content to less than 1%, preferably 0%. Preferably, the temperatures used are 125.degree. C. or less, more preferably 100-120.degree. C. The dehydrating temperature can be lower than 100.degree. C., but a temperature of at least 100.degree. C. will be more efficient for removing moisture.
Representative processes for carrying out a non-thermal dehydration include freeze drying or extracting the water from the starch or flour using a solvent, preferably a hydrophilic solvent, more preferably a hydrophilic solvent which forms an azeotropic mixture with water (e.g., ethanol).
For a laboratory scale dehydration with a solvent, the starch or flour (about 4-5% moisture) is placed in a Soxhlet thimble which is then placed in a Soxhlet apparatus. A suitable solvent is placed in the apparatus, heated to its reflux temperature, and refluxed for a time sufficient to dehydrate the starch or flour. Since during the refluxing the solvent is condensed onto the starch or flour, the starch or flour is exposed to a lower temperature than the solvent's boiling point. For example, during ethanol extraction the temperature of the starch is only about 40-50.degree. C. even though ethanol's boiling point is about 78.degree. C. When ethanol is used as the solvent, the refluxing is continued for about 17 hours. The extracted starch or flour is removed from the thimble, spread out on a tray, and the excess solvent is allowed to flash off. The time required for ethanol to flash off is about 20-30 minutes. The dehydrated starch or flour is immediately placed in a suitable heating apparatus for the heat treatment. For a commercial scale dehydration any continuous extraction apparatus is suitable.
For dehydration by freeze drying, the starch or flour (4-5% moisture) is placed on a tray and put into a freeze dryer. A suitable bulk tray freeze dryer is available from FTS Systems of Stone Ridge, N.Y. under the trademark Dura-Tap. The freeze dryer is run through a programmed cycle to remove the moisture. The temperature is held constant at about 20.degree. C. and a vacuum is drawn to about 50 milliTorr (mT). The starch or flour is removed from the freeze dryer and immediately placed into a suitable heating apparatus for the heat treatment.
After it is dehydrated, the starch or flour is heat treated for a time and at a temperature sufficient to inhibit the starch or flour. The preferred heating temperatures are greater than about 100.degree. C. For practical purposes, the upper limit of the heat treating temperature is about 200.degree. C. Typical temperatures are 120-180.degree. C., preferably 140-160.degree. C., most preferably 160.degree. C. The temperature selected will depend upon the amount of inhibition desired and the rate at which it is to be achieved.
The time at the final heating temperature will depend upon the level of inhibition desired. When a conventional oven is used, the time ranges from 1 to 20 hours, typically 2 to 5 hours, usually 3.5 to 4.5 hours. When a fluidized bed is used, the times range from 0 minutes to 20 hours, typically 0.5 to 3.0 hours. Longer times are required at lower temperatures to obtain more inhibited starches.
For most applications, the thermal dehydrating and heat treating steps will be continuous and accomplished by the application of heat to the starch or flour beginning from ambient temperature. The moisture will be driven off during the heating and the starch will become anhydrous or substantially anhydrous. Usually, at these initial levels of inhibition, the peak viscosities are higher than the peak viscosities of starches heated for longer times, although there will be greater breakdown in viscosity from the peak viscosity. With continued heat treating, the peak viscosities are lower, but the viscosity breakdowns are less.
The process may be carried out as part of a continuous process involving the extraction of the starch from a plant material.
As will be seen in the following examples, the source of the starch or flour, the initial pH, the dehydrating conditions, the heating time and temperature, and the equipment used are all interrelated variables that affect the amount of inhibition.
The heating steps may be performed at normal pressures, under vacuum or under pressure, and may be accomplished by conventional means known in the art. The preferred method is by the application of dry heat in dry air or in an inert gaseous environment.
The heat treating step can be carried out in the same apparatus in which the thermal dehydration occurs. Most conveniently the process is continuous with the thermal dehydration and heat treating occurring in the same apparatus, as when a fluidized bed is used.
The dehydrating and heat treating apparatus can be any industrial ovens, conventional ovens, microwave ovens, dextrinizers, dryers, mixers and blenders equipped with heating devices and other types of heaters, provided that the apparatus is fitted with a vent to the atmosphere so that moisture does not accumulate and precipitate onto the starch or flour. The preferred apparatus is a fluidized bed. Preferably, the apparatus is equipped with a means for removing water vapor, such as, a vacuum or a blower to sweep air or the fluidizing gas from the head-space of the fluidized bed. Suitable fluidizing gases are air and nitrogen. Dry air is preferred. For safety reasons, it is preferable to use a gas containing less than 12% oxygen.
Superior inhibited starches having high viscosities with low percentage breakdown in viscosity are obtained in shorter times in the fluidized bed than can be achieved using other conventional heating ovens or dryers.
Optional steps can be carried out to improve the color and/or flavor. They include washing the starch or flour with water and/or removing protein and/or lipid from the starch or flour prior to the dehydrating step and/or after the heat treating step. A bleaching agent (e.g., sodium chlorite) or an alkali can be used for the protein and/or lipid removal.
The starches or flours may be inhibited individually or more than one may be inhibited at the same time. They may be inhibited in the presence of other materials or ingredients that would not interfere with the thermal inhibition process or alter the properties of the starch or flour product.
Sample Preparation
Unless indicated otherwise, all the starches and flours used were granular and were provided by National Starch and Chemical Company of Bridgewater, N.J.
The controls were from the same native source as the test samples, were unmodified or modified in the same manner as the test sample, and were at the same pH, unless otherwise indicated. All starches and flours, both test and control samples, were prepared and tested individually.
The pH of the starch samples was raised by slurrying the starch or flour in water at 30-40% solids and adding a sufficient amount of a 5% sodium carbonate solution until the desired pH was reached. All samples were spray dried or flash dried, as conventional in the art (without gelatinization) to about 2-15% moisture, except for the non-thermally dehydrated starches which were generally oven dried (without gelatinization) to about 2-6% moisture.
Measurements of pH, either on samples before or after the thermal inhibition steps, were made on samples consisting of one part starch or flour to four parts water.
Except where a conventional oven or dextrinizer is specified, the test samples were dehydrated and heat treated in a fluidized bed reactor, model number FDR-100, manufactured by Procedyne Corporation of New Brunswick, N.J. The cross-sectional area of the fluidized bed reactor was 0.05 sq meter. The starting bed height was 0.3 to 0.8 meter, but usually 0.77 meter. The fluidizing gas was air, except where otherwise indicated, and the air was used at a velocity of 5-15 meter/min. The sidewalls of the reactor were heated with hot oil, and the fluidizing gas was heated with an electric heater. The samples were loaded to the reactor and then the fluidizing gas was introduced, or the samples were loaded while the fluidizing gas was being introduced. No difference was noted in the samples depending on the order of loading. Unless otherwise specified, the samples were brought from ambient temperature up to no more than 125.degree. C. until the samples became anhydrous and were further heated to the specified heat treating temperature. When the heat treating temperature was 160.degree. C., the time to reach that temperature was less than three hours.
The moisture level of the samples at the final heating temperature was 0%, except where otherwise stated. Portions of the samples were removed and tested for inhibition at the temperatures and times indicated in the tables.
Unless specified otherwise, the samples were tested for inhibition using the following Brabender Procedures.
Brabender Procedure
All samples, except for corn, tapioca and waxy rice flour, were slurried in a sufficient amount of distilled water to give a 5% anhydrous solids starch slurry. Corn, tapioca, and waxy rice flour were slurried at 6.3% anhydrous solids. The pH was adjusted to pH 3.0 with a sodium citrate/citric acid buffer. The slurry was introduced into the sample cup of a Brabender VISCO.backslash.Amylo.backslash.GRAPH fitted with a 350 cm/gram cartridge. The starch slurry was heated rapidly to 92.degree. C. and held for 10 minutes.
The peak viscosity and viscosity ten minutes (10') after peak viscosity were recorded in Brabender Units (BU). The percentage breakdown (.+-.2%) in viscosity was calculated according to the formula: ##EQU1## where "peak" is the peak viscosity in Brabender Units, and "(peak+10')" is the viscosity in Brabender Units at ten minutes after peak viscosity.
If no peak viscosity was reached, that is, the data indicate a rising curve or a flat curve, the viscosity at 92.degree. C. and the viscosity at 30 minutes after attaining 92.degree. C. were recorded.
Using data from Brabender curves, inhibition was determined to be present if, when dispersed at 5-6.3% solids in water at 92-95.degree. C. and pH 3 during the Brabender heating cycle, the Brabender data showed (i) no or almost no viscosity, indicating the starch was so inhibited it did not gelatinize or strongly resisted gelatinization; (ii) a continuous rising viscosity with no peak viscosity, indicating the starch was highly inhibited and gelatinized to a limited extent; (iii) a lower peak viscosity and a lower percentage breakdown in viscosity from peak viscosity compared to a control, indicating a moderate level of inhibition; or (iv) a slight increase in peak viscosity and a lower percentage breakdown compared to a control, indicating a low level of inhibition.
Characterization of Inhibition by Brabender Data
Characterization of a thermally inhibited starch is made more conclusively by reference to a measurement of its viscosity after it is dispersed in water and gelatinized. The instrument used to measure the viscosity is a Brabender VISCO.backslash.Amylo.backslash.GRAPH, (manufactured by C. W. Brabender Instruments, Inc., Hackensack, N.J.). The VISCO.backslash.Amylo.backslash.GRAPH records the torque required to balance the viscosity that develops when a starch slurry is subjected to a programmed heating cycle. For non-inhibited starches, the cycle passes through the initiation of viscosity, usually at about 60.degree.-70.degree. C., the development of a peak viscosity in the range of 65.degree.-95.degree. C., and any breakdown in viscosity when the starch is held at the elevated temperature, usually 92.degree.-95.degree. C. The record consists of a curve tracing the viscosity through the heating cycle in arbitrary units of measurement termed Brabender Units (BU).
Inhibited starches will show a Brabender curve different from the curve of the same starch that has not been inhibited (hereinafter the control starch). At low levels of inhibition, an inhibited starch will attain a peak viscosity somewhat higher than the peak viscosity of the control, and there may be no decrease in percentage breakdown in viscosity compared to the control. As the amount of inhibition increases, the peak viscosity and the breakdown in viscosity decrease. At high levels of inhibition, the rate of gelatinization and swelling of the granules decreases, the peak viscosity disappears, and with prolonged cooking the Brabender trace becomes a rising curve indicating a slow continuing increase in viscosity. At very high levels of inhibition, starch granules no longer gelatinize, and the Brabender curve remains flat.
Characterization of Inhibition by Texture
Starches or flours with a low to moderate degree of inhibition will exhibit certain textural characteristics when dispersed in an aqueous medium and heated to gelatinization. In the following examples, the starches or flours were determined to be inhibited if a heated gelatinized slurry of the starch or flour exhibited a non-cohesive, smooth texture.
Brabender Procedure--Crosslinked Starches
The crosslinked, thermally-inhibited cationic and amphoteric starches (23.0 g) to be tested were combined with 30 ml of an aqueous solution of citric acid monohydrate (prepared by diluting 210.2 g of citric acid monohydrate to 1000 ml in a volumetric flask) and sufficient water was added to make the total charge weight 460.0 g. The slurry is added to the cooking chamber of the Brabender VISCO amylo GRAPH fitted with a 700 cm/gram cartridge and rapidly heated from room temperature to 95.degree. C. The peak viscosity (highest viscosity observed) and the viscosity after 30 minutes at 95.degree. C. were recorded. The percentage breakdown in viscosity (.+-.2%) was calculated according to the formula ##EQU2##
Brookfield Viscometer Procedure
Test samples are measured using a Model RVT Brookfield Viscometer and the appropriate spindle (the spindle is selected based on the anticipated viscosity of the material). The test sample, usually a cooked starch paste, is placed in position and the spindle is lowered into the sample to the appropriate height. The viscometer is turned on and the spindle is rotated at a constant speed (e.g., 10 or 20 RPM) for at least 3 revolutions before a reading is taken. Using the appropriate conversion factors, the viscosity (in centipoises) of the sample is recorded.
Angle of Repose Determination
This test measure the flow properties of the starch or flour. A large sheet of heavy Kraft paper (about 6 ft. square) is secured to a flat, level surface with masking tape. Two rings (3 in. and 4 in. in diameter) are clamped onto a ring stand (6.times.9 in. base and 24 in. rod) in such a way that the base faces in the opposite direction from the rings. The small ring is placed above the larger ring. To keep the funnels stationary, 1 in. pieces of heavy walled vacuum tubing (1/4 in. base by 3/16 in. wall) are cut lengthwise through one wall and fitted equidistantly at 3 locations on each ring. A chemical funnel having a 100 mm top interior diameter (ID) (Kimax 58) is modified by removing the existing stem and annealing a 8 mm I.D. glass tubing 85 mm in length as the stem. The modified funnel is placed in the large ring and the height is adjusted so that the orifice of the funnel is 1.+-.0.1 cm above the paper. A powder funnel having a 60 mm top I.D. and 13 mm stem I.D. (Kimax 29020-04) is placed in the small ring and the ring is lowered as far as possible, i.e., until the clamps meet. The small funnel should be centered above the large funnel with the orifice of the large funnel stem parallel to the paper. Approximately 50 g of the sample to be tested are slowly added to the powder funnel while gently placing the top of an index finger over the orifice of the large funnel so that any sample which overflows the powder funnel does not flow out of the large funnel. The finger is slowly removed from the orifice while taking care not to move the funnel and allow the sample to flow onto the paper. Flow will cease when the top of the pile reaches the orifice of the funnel stem. With a pencil, the circumference of the sample pile is traced as accurately as possible without disturbing the sample. The sample is removed and the radius of the pile is measured. Each sample is run in triplicate. The test is repeated if the funnel stem becomes clogged before the pile meets the funnel orifice or if the pile is disturbed in any way. The funnels are cleaned after each run.
The average radius of the sample pile is calculated and the angle of repose is determined using the following formula: ##EQU3##
Horiba Wet Particle Size Determination
For determination of the Horiba wet particle size determination, the thermally-inhibited starches were analyzed, according to the instruction manual-version 1.81C, of the Horiba, Model #LA-900, Laser Scattering Particle Size Distribution Analyzer (Horiba Instrument Inc., Irvine, Calif. 92174). This determination requires that the sample be added under agitation to a cup which contains distilled or de-ionized water until a desired concentration is achieved. The software package then automatically initiates the analysis.
Some of the granular non-pregelatinized starch samples were tested for pasting temperature and/or gelatinization temperature using the following procedures.
Rapid Visco Analyzer (RVA)
This test is used to determine the onset of gelatinization, i.e., the pasting temperature. The onset of gelatinization is indicated by an increase in the viscosity of the starch slurry as the starch granules begin to swell.
A 5 g starch sample (anhydrous basis) is placed in the analysis cup of a Model RVA-4 Analyzer and slurried in water at 20% solids. The total charge is 25 g. The cup is placed into the analyzer, rotated at 160 rpm, and heated from an initial temperature of 50.degree. C. up to a final temperature of 80.degree. C. at a rate of 3.degree. C./minute. A plot is generated showing time, temperature, and viscosity in centipoises (cP). The pasting temperature is the temperature at which the viscosity reaches 500 cP. Both pasting temperature and pasting time are recorded.
Differential Scanning Calorimetry (DSC)
This test provides a quantitative measurement of the enthalpy (.DELTA.H) of the energy transformation that occurs during the gelatinization of the starch granule. The peak temperature and time required for gelatinization are recorded. A Perkin-Elmer DSC-4 differential scanning calorimeter with data station and large volume high pressure sample cells is used. The cells are prepared by weighing accurately 10 mg of starch (dry basis) and the appropriate amount of distilled water to approximately equal 40 mg of total water weight (moisture of starch and distilled water). The cells are then sealed and allowed to equilibrate overnight at 4.degree. C. before being scanned at from 25-150.degree. C. at the rate of 10.degree. C./minute. An empty cell is used as the blank.
Brookfield Viscometer Procedure
Test samples are measured using a Model RVT Brookfield Viscometer and the appropriate spindle (the spindle is selected based on the anticipated viscosity of the material). The test sample, usually a cooked starch paste, is placed in position and the spindle is lowered into the sample to the appropriate height. The viscometer is turned on and the spindle is rotated at a constant speed (e.g., 10 or 20 rpm) for at least 3 revolutions before a reading is taken. Using the appropriate conversion factors, the viscosity (in centipoises) of the sample is recorded.

EXAMPLES
The following examples will more fully illustrate the embodiments of the invention. In the examples, all parts are given by weight and temperature are in degrees Celsius unless otherwise noted. The thermally-inhibited starches and controls in the following examples were prepared as described above and are defined by textural characteristics or in relation to data taken from Brabender curves using the above described procedures. The thermally-inhibited starches and flours are referred to as "T-I" starches and flours and the conditions used for their preparation (i.e., pH to which the starch is adjusted and heat treatment temperature and time at that temperature are included in parenthesis--(pH; temperature/hold time at that temperature). All pH adjustments are done with sodium carbonate unless specified otherwise. Unless otherwise specified, the thermally-inhibited starches and flours referred to as "granular" starches are non-pregelatinized granular starches and flours.
In the first three examples, the moisture indicated is the moisture of the starch before the dehydration and heat treating steps. As indicated above, as the starches were brought from ambient temperature up to the heating temperature, the starches became anhydrous or substantially anhydrous.
In the tables the abbreviations "sl.", "mod.", "v.", "ris." and "N.D." stand for slight or slightly, moderate or moderately, very, rising, and not determined.
Example 1
This example illustrates the preparation of the starches of this invention from a commercial granular waxy maize base starch by the heat treatment process of this invention.
Processing conditions and their effects on viscosity and texture of waxy maize starch are set forth in the Tables below.
To obtain a heat-stable, non-cohesive thickener, samples of granular starch were slurried in 1.5 parts of water, the pH of the slurry was adjusted with the addition of a 5% Na.sub.2 CO.sub.3 solution and the slurry was agitated for 1 hour, then filtered, dried, and ground. The dry starch samples (150 g) were placed into an aluminum foil pan (4".times.5".times.11/2") and heated in a conventional oven under the conditions described below. Brabender viscosity measurements demonstrated that the most heat-stable starches were obtained by heating at 160.degree. C. and a pH of at least 8.0 for about 3.5 to 6.0 hours.
______________________________________Process Variables Heating - 160.degree. C. Mois- Cold Evaluation ofWaxy ture Time Gelatinized Samples.sup.d,eMaize.sup.a pH (%) (hrs.) Viscosity Texture______________________________________1 6.0 10.9 2 heavy to v. cohesive heavy2 6.0 10.9 4 thin to mod. --3 8.2 10.6 3.5 heavy to v. cohesive, heavy less than unmodified control4 8.2 10.6 4 heavy to v. sl. to heavy mod. cohesive5 8.2 10.6 4.5 heavy non- cohesive6 8.2 10.6 5.5 heavy, non- thinnest cohesive7 8.2 10.6 6 mod. heavy non- cohesiveunmod- -- -- v. heavy cohesiveified.sup.bcross- -- -- v. heavy non-linked.sup.c cohesive______________________________________ .sup.a All samples were commercial samples of granular waxy maize starch obtained from National Starch and Chemical Company, Bridgewater, New Jersey. .sup.b The unmodified control was a commercial granular waxy maize starch obtained from National Starch and Chemical Company, Bridgewater, New Jersey. .sup.c The modified control was a commercial crosslinked (phosphorous oxychloride treated) granular waxy maize starch obtained from National Starch and Chemical Company, Bridgewater, New Jersey. .sup.d Samples were cooked by slurrying 7.0 g of starch (at 12% moisture) in 91 mls water at neutral pHs and heating the starch slurry for 20 minutes in a boiling water bath. .sup.e The cold evaluation was carried out at 25.degree. C.
______________________________________Brabender Evaluation Brabender Viscosity.sup.b Process Variables (BU) Heating ViscosityWaxy Temp. Time Peak at 95.degree. C./Maize.sup.a pH (.degree. C.) (hrs.) Viscosity 20 mins.______________________________________3 8.2 160 3.5 985 8304 8.2 160 4.0 805 6855 8.2 160 4.5 640 6356 8.2 160 5.5 575 570Unmodified -- none none 1640 630control1 6.0 160 2.0 1055 5602 6.0 160 4.0 140 80______________________________________ .sup.a See prior Table for a description of samples. .sup.b In the Brabender procedure, a sample containing 5.4% anhydrous solids of starch dispersed in water was heated rapidly to 50.degree. C., then the heat was increased by 1.5.degree. C. per minute to 95.degree. C. and held for 20 minutes.
Example 2
This example illustrates that a variety of granular starches may be processed by the method of this invention to provide a non-cohesive thickener with properties similar to chemically crosslinked starches.
Processing conditions and their effects on the viscosity and texture of waxy barley, tapioca, V.O. hybrid and waxy rice starches are set forth in the tables below.
______________________________________Process Variables Heating - 160.degree. C. Mois- Cold Evaluation of ture Time Gelatinized Sample.sup.bSample.sup.a pH (%) (hrs.) Viscosity/Texture______________________________________Waxy Barley Starch1 8.7 8.5 1.5 heavy cohesive2 8.7 8.5 2.5 heavy sl. mod. cohesive3 8.7 8.5 3.5 mod. heavy non- to heavy cohesive4 5.2 10.8 1.5 thin --5 5.2 10.8 2.5 thin/ -- thinnestWaxy -- -- 0 heavy cohesiveBarleyControlTapioca Starch6 8.8 10.3 2 heavy to v. cohesive heavy7 8.8 10.3 3 heavy to v. cohesive/ heavy less than Sample 68 8.8 10.3 4 heavy to v. sl. heavy cohesive to sl. lumpy9 8.8 10.3 5 heavy non- cohesive lumpy10 5.5 10.9 3 mod. heavy --Tapioca -- -- 0 v. heavy cohesiveControlWaxy Rice Starch1 9.1 9.0 2 v. heavy cohesive2 9.1 9.0 3 heavy sl. cohesive3 9.1 9.0 4 heavy sl. cohesive4 9.1 9.0 5 mod. heavy non- to heavy cohesiveWaxy -- -- 0 v. heavy cohesiveRiceControl______________________________________ .sup.a Tapioca starch samples were commercial granular starch obtained from National Starch and Chemical Company, Bridgewater, New Jersey. Waxy barley starch samples were commercial granular starch obtained from AlKo, Finland. Waxy rice starch samples were commercial granular starch obtaine from Mitsubishi Corporation, Japan. .sup.b Samples were cooked by slurring 7.5 g of starch at 12% moisture in 100 mls of water and heating the starch slurry for 20 minutes in a boilin water bath.
______________________________________Process Variables Heating - 160.degree. C. Mois- Cold Evaluation of ture Time Gelatinized Sample.sup.bSample.sup.a pH (%) (hrs.) Viscosity/Texture______________________________________V.O. Hybrid Starch1 8.7 10.5 2.0 heavy cohesive v. sl. less than control2 8.7 10.5 3.0 heavy sl. mod. cohesive3 8.7 10.5 4.0 mod. heavy smooth, to heavy very sl. cohesive4 8.7 10.5 5.0 mod. heavy smooth, short, non- cohesive5 8.7 10.5 6.0 moderate smooth, short, non- cohesiveV.O. 5.9 11.4 0 heavy cohesiveHybridControl______________________________________ .sup.a V.O. hybrid starch samples were granular starches obtained from National Starch and Chemical Company, Bridgewater, New Jersey. .sup.b Samples were cooked by slurrying 7.5 g of starch at 12% moisture i 100 mls of water and heating the starch slurry for 20 minutes in a boilin water bath.
The viscosity and texture evaluation results show that a non-cohesive, heat-stable starch thickener may be prepared from waxy barley, V.O. hybrid, tapioca and waxy rice starches by the process of this invention. The amount of inhibition (non-cohesive, thickening character in cooked aqueous dispersion) increased with increasing time of heat treatment.
Example 3
This example illustrates the effects of temperature, the pH, and starch moisture content on the viscosity and texture of the treated starch.
Part A
A waxy maize starch sample (100 g) containing 20.4% moisture was heated in an oven at 100.degree. C. for 16 hours in a sealed glass jar. A second sample was heated for 4 hours and a third sample was heated for 7 hours under the same conditions. The product viscosity and texture were compared to a 12.1% moisture granular waxy maize starch control using the cook evaluation method of Example 1.
Results are shown below.
______________________________________Effect of Process Moisture Process Variables.sup.b Cold Evaluation ofWaxy Heat Time Gelatinized Starch.sup.cMaize.sup.a (hrs.) Viscosity Texture______________________________________1. Test 16 heavy, sl. cohesive (20.4% H.sub.2 O) thinner than control2. Control 0 heavy cohesive (12.1% H.sub.2 O)3. Test 4 heavy cohesive (20.4% H.sub.2 O)4. Control 0 heavy cohesive (12.1% H.sub.2 O)5. Test 7 heavy cohesive (20.4% H.sub.2 O)6. Control 0 heavy cohesive (12.1% H.sub.2 O)______________________________________ .sup.a Samples were obtained from National Starch and Chemical Company, Bridgewater, New Jersey. .sup.b Process was conducted at pH 5.2. .sup.c See Example 2 for cook conditions.
The results demonstrate that moisture added during the process yields a product which is as cohesive and undesirable as a control starch which had not been heated.
Part B
Samples (900 g) of a commercial granular waxy maize starch (obtained from National Starch and Chemical Company, Bridgewater, N.J.) were placed in a 10".times.15".times.0.75" aluminum tray and heated in an oven at 180.degree. C. for 15, 30, 45 and 60 minutes. The pH of the starch was not adjusted and remained at about 5.2 during the heating process. Sample viscosity and texture were evaluated by the method of Example 1.
As shown in the following table, the pH 5.2 samples were characterized by an undesirable, cohesive texture similar to that of a waxy maize starch control which had not been heat treated.
______________________________________Effect of Acidic Process pHProcessVariables.sup.a Cold Evaluation ofHeating Time Gelatinized Starch.sup.bSample (minutes) Viscosity Texture______________________________________1 15 v. heavy cohesive2 30 v. heavy cohesive3 45 v. heavy cohesive4 60 heavy to cohesive v. heavyControl 0 v. heavy cohesive______________________________________ .sup.a The pH was not adjusted from that of the native waxy maize starch (a pH = 5.2) and Samples 1-4 correspond to starch treated by the process of U.S. Pat. No. 4,303,451 (no pH adjustment). .sup.b See Example 2 for cook conditions.
Thus, a combination of selected factors, including the pH, moisture content and the type of native starch, determine whether a desirable, non-cohesive, heat-stable starch thickener is produced by the process of this invention.
Example 4
This example shows carrying out the thermal inhibition in the fluidized bed previously described. The effects of temperature and time at the indicated temperature on the level of inhibition of waxy maize granular starch at pH 9.5 are shown below.
______________________________________ Viscosity (B.U.) Break- Peak + downHeating Temperature and Time Peak 10' (%)______________________________________Control (none) 1135 730 64.3110.degree. C. for 22 hrs. 1185 970 18.1160.degree. C. for 0 hr. 1055 880 16.6160.degree. C. for 2 hrs. 665 660 0.7175.degree. C. for 0 hr. 850 755 11.2180.degree. C. for 0 hr. 715 680 4.9190.degree. C. for 0 hr. 555 550 0.9200.degree. C. for 0 hr. ris. -- --200.degree. C. for 2 hrs. none -- --______________________________________
The data shows that inhibited anhydrous or substantially anhydrous samples can be obtained at heat treating temperatures between 100-200.degree. C., with more inhibition obtained at higher temperatures or at longer times at lower temperatures. The starch samples heated at 200.degree. C. were highly inhibited (rising curves) or completely inhibited (no gelatinization).
Example 5
Samples of tapioca starch, waxy maize starch, and waxy rice flour at pH 9.4 to 9.6 were dehydrated to less than 1% moisture at a temperature below 125.degree. C., equilibrated to 160.degree. C. in a thermal reactor (a horizontal double ribbon jacketed vessel). The heat treating time for the samples ranged from three to six hours.
The samples were evaluated for inhibition according to the previously described Brabender procedure and the results are given in the following table.
______________________________________ Viscosity (BU) BreakdownStarch at (pH 9.4-9.6) Peak Peak + 10' (%)______________________________________Tapioca Control 1300 385 70.4 T-I 340 295 13.2Waxy Maize Control 1135 405 64.3 T-I 580 560 3.5Waxy Rice Control 1140 307 73.1Flour T-I 600 590 1.7______________________________________
The dehydrated and heated starches and flour inhibited a viscosity inhibited from breakdown relative to the controls that were not dehydrated and heated. This inhibition correlated to a short, noncohesive texture in the cooled product.
Example 6
The effects of initial pH and heat treating time on the level of inhibition on samples of waxy maize starch at naturally occurring pH (about 6.0) and at pH 7.5, pH 8.5 and pH 9.5 were evaluated and the data set out in the following table.
______________________________________Waxy Maize Heat Treated at 160.degree. C.Effects of Initial pH and Heating Time Viscosity (BU) PeakInitial Heating Time Viscosity Peak at 10' BreakdownpH (min) (BU) (BU) (%)______________________________________6.0 control 1135 405 64.36.0 0 1058 463 56.4 30 710 460 35.2 60 645 445 31 90 570 440 22.8 120 560 440 21.4 150 485 395 18.67.3 90 645 500 22.5 120 580 450 22.4 150 572 445 22.2 180 522 427 18.18.5 0 980 630 35.7 30 770 655 14.9 60 665 615 6.0 90 625 600 4.0 120 585 580 0.99.5 0 1055 880 16.6 30 825 800 3.0 60 705 700 0.7 90 690 690 0 120 665 660 0.7______________________________________
The data show that starches with varying levels of inhibition, as reflected by the variance in percentage breakdown in viscosity, can be obtained at different heating times and initial pHs, and that a higher degree of inhibition can be obtained at the higher pH values and at longer heating times. Moreover, comparing the shortened heat treating times in this Example, in which the fluidized bed reactor was used, with the heat treating times in hours in Examples 4 and 5, it can be seen that inhibited starches with higher peak viscosities can be obtained at much shorter times using the fluidized bed than are possible with standard thermal reactors or ovens.
Example 7
The effects of temperature and time on the level of inhibition of waxy maize starch at pH 9.5 were evaluated. The results are set forth in the following table.
______________________________________Effects of Heating Temperature and Time Time At Heating Viscosity Break-Heating Temp. (BU) downTemp. (hrs) Peak Peak + 10' (%)______________________________________Control -- 1135 730 64.3110.degree. C. 22 1185 970 18.1160.degree. C. 0 1055 880 16.6160.degree. C. 2 665 660 0.7175.degree. C. 0 850 755 11.2180.degree. C. 0 715 680 4.9190.degree. C. 0 555 550 0.9200.degree. C. 0 ris. -- --200.degree. C. 2 none -- --______________________________________
The data show that inhibited starches can be obtained at heat treating temperatures between 100.degree.-200.degree. C., with more inhibition obtained at higher temperatures or at longer times with lower temperatures. The starch samples heated at 200.degree. C. were highly inhibited (rising curves) or completely inhibited (no gelatinization).
Example 8
Waxy maize starch at initial pH of 9.5 was evaluated for inhibition in the presence of between 1-2% moisture by weight of the sample by injecting saturated air into the chambers of the fluidized bed reactor.
The results are set out in the following tables.
______________________________________ Viscosity (BU)Temp Time Peak + 92.degree. C. + Breakdown(.degree. C.) (min) Peak 10' 92.degree. C. 30' (%)______________________________________Waxy Maize (pH 9.5; 0% Moisture)Control 1140 410 64140 0 1260 500 -- -- 60150 0 1160 540 -- -- 45155 0 1100 720 -- -- 35160 0 1080 840 -- -- 22160 0 930 825 -- -- 11160 15 760 740 -- -- 3160 30 700 690 -- -- 1160 45 695 690 -- -- 1160 60 -- -- 490 690 ris.160 90 605 590 414 590 ris.160 120 -- -- 320 580 ris.160 150 -- -- 200 480 ris.Waxy Maize (pH 9.5; 1-2% Moisture)Control 1140 410 64155 0 1215 465 -- -- 62160 0 1090 530 -- -- 51160 15 985 740 -- -- 25160 30 885 700 -- -- 21160 45 750 530 -- -- 29160 60 700 480 -- -- 31160 90 685 505 -- -- 26160 120 610 450 -- -- 26160 150 580 430 -- -- 26160 180 530 400 -- -- 25______________________________________
The results show that more inhibition can be obtained when the starch is heat treated at anhydrous or substantially anhydrous condition than if heat treated in the presence of moisture (note the lower percentage in viscosity breakdown for the anhydrous samples).
Example 9
Waxy maize samples at an initial moisture content of 10.9% were introduced to a fluidized bed reactor with a nitrogen fluidizing gas containing ammonia in the concentrations specified in the tables. The samples were evaluated for the effect of the ammonia gas on the level of inhibition.
______________________________________Waxy Maize (0.1% NH.sub.3 in N.sub.2) ViscosityTemp Time (BU) Breakdown Final(.degree. C.) (min) Peak Peak + 10' (%) pH______________________________________Control 1040 200 81 --160 0 965 450 53 8.7160 60 625 420 33 8.6160 120 440 325 26 8.9160 180 340 290 15 8.8160 240 300 250 17 8.4______________________________________
Comparing the results to those obtained in Example 6 at pH 9.5, it can be seen that ammonia gas is effective to raise the pH of the starch and prevent hydrolysis, but is not as effective as direct pH adjustment of the starch in preventing hydrolysis and promoting inhibition.
______________________________________ ViscosityTemp Time (BU) Breakdown Final(.degree. C.) (min) Peak Peak + 10' (%) pH______________________________________Waxy Maize (1% NH.sub.3 in N.sub.2)Control 1040 200 81160 0 1100 460 58 8.9160 60 670 470 30 8.8160 120 505 405 20 8.9160 180 410 345 16 8.9160 210 380 320 16 9.8Waxy Maize (10% NH.sub.3 in N.sub.2)Control 1040 200 81160 0 1020 390 62 9.7160 60 730 410 44 9.6160 120 540 360 33 9.6160 180 415 310 25 10.2160 240 330 270 18 10.4______________________________________
Example 10
Waxy maize samples were introduced to a fluidized bed reactor and sprayed with a 25% solution of sodium carbonate, while the fluidizing gas was being introduced, in order to raise the pH. The samples were then brought from ambient temperature to 160.degree. C. in less than three hours, and held at 160.degree. C. for the times specified in the table.
The samples were evaluated for inhibition. The data show that this technique is successful for raising the pH of the samples in order to prevent acid hydrolysis and promote inhibition.
______________________________________Waxy Maize (with Na.sub.2 CO.sub.3) ViscosityTemp Time (BU) Breakdown(.degree. C.) (min) Peak Peak + 10' (%) Final pH______________________________________Control 1040 200 81 --160 0 1000 500 50 9.4160 30 750 530 29 9.2160 60 645 500 22 9.1160 180 465 400 14 9______________________________________
Example 11
The effect of the fluidizing gas on the level of inhibition was evaluated on waxy maize samples at pH 9.5 fluidized with nitrogen gas and with air. The samples were tested for inhibition and the data show that a higher rate of inhibition is attained when air is used as a fluidizing gas compared to nitrogen.
______________________________________Waxy Maize1 (pH 9.5) Nitrogen Air Viscosity (BU) Break- Viscosity (BU) Break- Time Peak + down Peak + downTemp. (min) Peak 10' (%) Peak 10' (%)______________________________________160 0 1055 880 16.6 1055 880 16.6160 30 1150 920 20.0 825 800 3.0160 60 985 870 11.7 705 700 0.7160 90 875 810 7.4 690 690 0160 120 865 815 5.9 665 660 0.7160 180 820 755 7.9 630 620 1.6______________________________________
Example 12
The effects of initial pH and heat treating times at 160.degree. C. on the level of inhibition on samples of corn starch at its naturally occurring pH, and at an initial pH 9.5, were evaluated.
The results set out in the following tables.
______________________________________ Viscosity (BU)Temp Time Peak + 92.degree. C. + Breakdown(160.degree. C.) (min) Peak 10' 92.degree. C. 30' (%)______________________________________Corn (natural pH)Control 640 420 34 0 560 370 -- -- 34 30 510 330 -- -- 35 60 500 400 -- -- 20 90 450 360 -- -- 20120 410 335 -- -- 18Corn (pH 9.5)Control 660 550 17 0 990 900 -- -- 9 30 940 910 -- -- 3 60 -- -- 20 910 ris. 90 -- -- 20 690 ris.120 -- -- 20 510 ris.______________________________________
The data show that very high levels of inhibition can be obtained at basic pH (note increasing viscosity) compared to natural pH, and that more inhibition is obtained with longer heat-treating times.
Example 13
The effect of initial pH on the level of inhibition on samples of potato starch at naturally occurring pH and at initial pH 9.5 was evaluated.
The results set out in the following tables.
______________________________________ Viscosity (BU)Temp Time Peak + 92.degree. C. + Breakdown(160.degree. C.) (min) Peak 10' 92.degree. C. 30' (%)______________________________________Potato (natural pH)Control 785 310 61125 0 560 360 -- -- 36160 0 240 140 -- -- 42160 90 22 15 -- -- 32160 180 20 18 -- -- 10Potato (pH 9.5)Control 690 390 43 0 640 480 -- -- 25 30 940 795 -- -- 15 60 1020 900 -- -- 12 90 995 945 -- -- 5120 -- -- 800 980 ris.150 -- -- 650 870 ris.180 -- -- 350 680 ris.______________________________________
The Brabender data at naturally occurring pH indicate that starch degradation, rather than inhibition, occurred as heat treating progressed. This example illustrates that thermal inhibition can be a function of both pH and the starting starch. In this case, thermal inhibition of potato starch appears to be more dependent on pH compared to other starches (for example, waxy maize). Therefore, the conditions required for dehydration and successful thermal inhibition of potato starch are more strict in order to avoid hydrolysis and degradation.
Dehydration and heat treating in the basic pH range, however, provided inhibited starches that maintained high viscosities, and at heat treating times over 90 minutes, provided highly inhibited starches as indicated by a continuous increasing viscosity.
Example 14
Samples of a high amylose containing starch (Hylon V) at natural pH and pH 9.5 were evaluated for the effect of high amylose content on inhibition.
Due to the high levels of amylose, it was necessary to use a pressurized Visco/amylo/Graph (C. W. Brabender, Hackensack, N.J.) to obtain Brabender curves. Samples were slurried at 10% starch solids, heated to 120.degree. C. and held for 30 minutes.
______________________________________High Amylose Cornnatural pH pH 9.5160.degree. C. Viscosity (BU) Break- Viscosity (BU) Break-Time peak + down peak + down(min) peak 10' (%) peak 10' (%)______________________________________Control 1180 525 55.5 1180 525 55.5 0 700 235 66120 282 25 91 290 225 22______________________________________
The data show that inhibition was obtained only on the high pH sample.
Example 15
This example shows that a granular starch can be dehydrated by ethanol (EtOH) extraction and that a better tasting starch is obtained.
A granular waxy maize starch was slurried in 1.5 parts water based on the weight of the starch and adjusted to pH 7 and 9.5 with 5% sodium carbonate, held for 30 minutes, filtered, and dried on a tray to a moisture content of about 5-6% moisture. The starch having the pH of 5.3 was a native starch which was not pH adjusted.
For the dehydration, the dried pH 5.3, pH 7.0, and pH 9.5 starches were each separated into two samples. One sample was dried on trays in a forced draft oven at 80.degree. C. overnight to thermally dehydrate the starch to <1% (0%) moisture. The other sample was placed in a Soxhlet extractor and allowed to reflux overnight (about 17 hours) with anhydrous ethanol (boiling point 78.32.degree. C.). The ethanol-extracted sample was placed on paper so that the excess alcohol could flash off which took about 30 minutes. The ethanol-extracted starch was a free flowing powder which was dry to the touch.
For the heat treatment, the oven-dehydrated starches and ethanol-extracted starches were placed on trays in a forced draft oven and heated for 3, 5, and 7 hours at 160.degree. C.
The thermally-inhibited (T-I) starches and the controls were evaluated using the Brabender Procedure previously described was used. The results are shown below:
______________________________________BRABENDER RESULTS Heat Viscosity (BU)Dehydra- Treat- Break-tion ment Peak + downMethod (160.degree. C.) Peak 10' (%)______________________________________Waxy Maize (pH 5.3)Control -- -- 1245 330 74Dehydrated oven -- 1290 350 73Dehydrated ethanol -- 1205 245 80T-I oven 5 hrs. 95 45 53T-I ethanol 5 hrs. 255 185 28T-I oven 7 hrs. 60 35 42T-I ethanol 7 hrs. 165 105 36Waxy Maize (pH 7.0)Dehydrated oven -- 1240 380 69T-I oven 7 hrs. 298 240 20T-I ethanol 7 hrs. 400 310 23Waxy Maize (pH 9.5)Dehydrated oven -- 1250 400 68Dehydrated ethanol -- 1070 350 67T-I ethanol 3 hrs. 665 635 5T-I oven 3 hrs. 680 655 4T-I oven 5 hrs. 245 460 ris.T-I ethanol 5 hrs. 160 375 ris.T-I oven 7 hrs. 110 295 ris.T-I ethanol 7 hrs. 110 299 ris.______________________________________
The results show that the starches can be dehydrated by ethanol extraction. The results also show that dehydration without the subsequent heat treatment did not inhibit the starch. The viscosity breakdown was not significantly different from that of the native waxy maize starch. Both of the thermally-inhibited pH 7 starches were higher in viscosity than the pH 5.3 (as is) thermally-inhibited starches. The starches which were thermally-inhibited at pH 9.5 were moderately highly inhibited or highly inhibited (rising curve).
Example 16
Granular tapioca, corn, and waxy rice starches and waxy rice flour were adjusted to pH 9.5, dehydrated in an oven and by extraction with ethanol, and heat treated at 160.degree. C. for the indicated time. They were evaluated for Brabender viscosity using the procedure previously described.
The Brabender results are shown below.
______________________________________ Heat Viscosity (BU) Dehydra- Treat- Break- tion ment Peak + downStarch Method Time Peak 10' (%)______________________________________Tapioca (pH 9.5 and 160.degree. C.)Dehydrated oven -- 745 330 58Dehydrated ethanol -- 720 330 54T-I oven 5 hrs. 270 260 3T-I ethanol 5 hrs. 260 258 1T-I oven 7 hrs. 110 155 ris.T-I ethanol 7 hrs. 100 145 ris.Corn (pH 9.5 and 160.degree. C.)Dehydrated oven -- 330 280 15Dehydrated ethanol -- 290 250 14T-I oven 5 hrs. 10 80 ris.T-I ethanol 5 hrs. 10 170 ris.T-I oven 7 hrs. 10 65 ris.T-I ethanol 7 hrs. 10 45 ris.Waxy Rice (pH 9.5 and 160.degree. C.)Dehydrated oven -- 1200 590 50.8Dehydrated ethanol -- 1155 450 61.0T-I oven 5 hrs. 518 640 ris.T-I oven 7 hrs. 265 458 ris.T-I ethanol 7 hrs. 395 520 ris.Waxy Rice Flour (pH 9.5 and 160.degree. C.)Dehydrated oven -- 895 700 22Dehydrated ethanol -- 870 410 53T-I oven 5 hrs. 38 73 ris.T-I ethanol 5 hrs. 140 260 ris.T-I oven 7 hrs. 10 16 ris.T-I ethanol 7 hrs. 40 100 ris.______________________________________
The results show that pH 9.5-adjusted, ethanol-extracted, heat-treated tapioca and corn starches had viscosity profiles generally similar to those of the same thermally-inhibited starches which were oven-dehydrated. The 7 hours heat-treated samples were more inhibited than the 5 hour heat-treated samples.
Example 17
This example compares ethanol extracted granular waxy maize starches and oven-dehydrated granular waxy maize starches heat treated in an oven for 5 and 7 hours at 160.degree. C. at the same pH, i.e., pH 8.03.
The Brabender results are shown below.
______________________________________ Viscosity (BU)Dehydration/ Break-Heat treatment Peak Peak + 10' down (%)______________________________________Oven/None 1160 360 69EtOH/None 1120 370 67Oven/5 hrs. 510 455 11EtOH/5 hrs. 490 445 9Oven/7 hrs. 430 395 8EtOH/7 hrs. 360 330 8______________________________________
The thermally-inhibited starches were slurried at 6.6% solids (anhydrous basis), Ph adjusted to 6.0-6.5, and then cooked out in a boiling water bath for 20 minutes. The resulting cooks were allowed to cool and then evaluated for viscosity, texture, and color.
______________________________________Dehydration Time atMethod 160.degree. C. Viscosity Texture Color______________________________________Oven None heavy to cohesive sl. off- v. heavy whiteEthanol None heavy to cohesive sl. off- v. heavy whiteOven 5 hours mod. heavy non- sl. tan, to heavy cohesive, darker* smoothEthanol 5 hours mod. heavy non- sl. tan to heavy cohesive, smoothOven 7 hours mod. heavy non- mod. tan, to heavy cohesive, darker* smoothEthanol 7 hours mod. heavy non- mod. tan to heavy cohesive, smooth______________________________________ *Slightly darker than ethanoldehydrated samples.
These Brabender results show that highly inhibited starches can be obtained by both thermal and non-thermal dehydration. The cook evaluation results show that there is a benefit for the ethanol-dehydrated, thermally-inhibited starches in terms of reduced color. As will be shown hereafter, there is also a flavor improvement with ethanol dehydration.
Example 18
This example shows that alcohol dehydration provides better tasting thermally-inhibited starches.
The test performed was a "Triangle Taste Test" which employs three coded samples, two identical and one different, presented simultaneously. None of the samples are identified as the standard. Control and experimental treatments were systematically varied so that each was presented in odd and identical sample positions an equal number of times. The judge determined which of the three samples differed from the other two. A forced choice was required. Statistical analysis was used to determine whether a significant difference between treatments existed. The probability of choosing the different or odd sample by chance alone was one-third. Once the odd sample was chosen the judges were asked why the samples were different and which they preferred.
The starches tested were waxy maize starches adjusted to pH 9.5 and heat treated for 7 hours at 140.degree. C. but one sample was dehydrated by ethanol extraction and the other sample was thermally dehydrated prior to the thermal inhibition step.
The thermally-inhibited starches were washed by slurring the granular starch with 1.5 parts water, mixing for 10 minutes on a stir plate, vacuum filtering the slurry, and washing the starch cake twice with 50 mis of distilled water. Then sufficient water was added to bring the slurry solids to 3%, the pH was adjusted to 6.0-6.5 and the slurry was cooked 20 minutes in a boiling water bath, cooled to slightly above room temperature, and evaluated.
The judges were given 20 ml samples for tasting. They observed a significant difference between the oven-dehydrated and ethanol-dehydrated starches. Nine out of the twelve judges chose the one different sample. All nine of the judges who could determine the different sample preferred the sample that was ethanol-extracted. Attributes that were used to describe the ethanol-extracted sample included clean, not bitter, and smooth compared to the oven-dehydrated sample.
Example 19
This example shows that an alcohol extraction after a granular starch is thermally-inhibited provides a better tasting starch.
A thermally-inhibited, granular waxy maize (adjusted to pH 9.5 and heat treated for 180 minutes in a fluidized bed at 160.degree. C.) was placed in a Soxhlet extraction apparatus and allowed to reflux overnight (about 17 hrs) using ethanol as the solvent (bp .about.78.degree. C.). The extracted starch was then laid on paper to allow excess ethanol to flash off. The resulting dry starch was washed by slurring the starch with 1.5 parts water, mixing for 10 minutes on a stir plate, vacuum filtering the slurry, and washing the starch cake twice with 50 ml of distilled water. Then sufficient water was added to bring the slurry solids to 3%, the pH was adjusted to 6.0-6.5, and the slurry was cooked in a boiling water bath for 20 minutes. The cook was cooled to slightly above room temperature and evaluated. The thermally-inhibited, non-ethanol-extracted base was used as the control.
The taste test performed was a "Paired-Preference Test". Two samples are presented, simultaneously or sequentially. The judge is requested to express a preference based on a specific attribute, here which sample is cleaner. Results are obtained in terms of relative frequencies of choice of the two samples as accumulated for all participants. Six of the eight trained judges identified the ethanol-extracted sample as having a blander, cleaner flavor with less aftertaste.
Example 20
The effects of the presence of protein, and heat treating times and temperatures on inhibition on samples of waxy maize containing 3.95% endogenous protein, adjusted to pH 8.5 and 9.5, and on samples containing 1.52% endogenous protein, adjusted to pH 7.5 and 9.5, were evaluated and the results set out in the following tables. The data show that the presence of protein leads to higher levels of inhibition than are attained in samples without protein. The results also show that the protein level, the pH and the time and the temperature for heat treating all have an independent and a cumulative effect on the level of inhibition, so that inhibition increases as the protein, pH, time, and temperature increase.
______________________________________ Viscosity (BU)Temp Time Peak + 92.degree. C. + Breakdown(.degree. C.) (min) Peak 10' 92.degree. C. 30' (%)______________________________________Waxy Maize (3.95% endogenous protein/pH 9.5)Control 940 400 57125 0 -- -- 660 680 ris.125 30 -- -- 710 750 ris.140 0 -- -- 540 600 ris.160 0 -- -- 350 375 ris.160 30 -- -- 260 295 ris.160 60 -- -- 220 275 ris.160 90 -- -- 180 255 ris.160 100 -- -- 130 200 ris.160 120 -- -- 150 210 ris.160 150 -- -- 150 190 ris.160 180 -- -- 130 180 ris.Waxy Maize (1.52% endogenous protein/pH 9.5)Control 1030 300 71125 0 1090 540 -- -- 50125 15 1080 650 -- -- 40140 0 1010 840 -- -- 17160 30 -- -- 480 575 ris.160 60 -- -- 340 610 ris.160 90 -- -- 255 540 ris.160 120 -- -- 120 340 ris.160 150 -- -- 120 330 ris.Waxy Maize (3.95% endogenous protein/pH 8.5)Control 740 235 68125 0 1005 550 -- -- 45125 15 935 700 -- -- 25140 0 705 610 -- -- 13160 0 -- -- 470 480 ris.160 30 -- -- 380 455 ris.160 60 -- -- 290 430 ris.160 90 -- -- 235 410 ris.160 120 -- -- 210 380 ris.Waxy Maize (1.52% endogenous protein/pH 7.6)Control 1100 240 78125 0 1230 480 -- -- --140 0 950 730 -- -- 23140 0 660 570 -- -- 14160 30 535 505 -- -- 6160 60 -- -- 480 415 ris.160 90 -- -- 490 430 ris.160 120 -- -- 465 435 ris.160 150 -- -- 435 420 ris.______________________________________
Example 21
This example describes the effect of the removal of various proteins, lipids, and other off flavor components on the flavor (i.e., taste and aroma) of a thermally-inhibited waxy maize.
Prior to the thermal inhibition process (i.e., solvent extraction or freeze drying and heat treatment), the protein is extracted from a waxy maize starch as follows. The starch is slurried at W=1.5 (50 lbs starch to 75 lbs of water) and the pH is adjusted to 3-3.5 with sulfuric acid. Sodium chlorite is added to give 2% on the weight of the starch. The starch is steeped overnight at room temperature. The pH is raised to about 9.5 using a 3% sodium hydroxide solution and washed well prior to drying. The protein level of the starch is reduced to about 0.1%. The protein level of an untreated waxy maize control (pH 9.5) is about 0.3%.
This treatment should improve the flavor of the thermally-inhibited granular starches prepared using the non-thermal dehydration methods since the same treatment of a thermally-inhibited granular starch prepared using thermal dehydration improved the flavor as reported below. Removal of various proteins, lipids, and other off flavor components is expected to improve the flavor of all starch bases and flours.
Using a one-sided, directional difference taste testing procedure, as described in "Sensory Evaluation Techniques" by M. Meilgaard et al., pp. 47-111 (CRC Press Inc., Boca Raton, Fla. 1987), the protein-reduced thermally-inhibited waxy maize (adjusted to pH 9.5; dehydrated and heat treated for 90 min at 160.degree. C. in a fluidized bed) was compared to the thermally-inhibited waxy maize (pH 9.5; 160.degree. C./90 min) which had not been protein-reduced prior to heat treatment.
For the taste test, 3% starch cooks (samples heated at 100.degree. C. for 15 min) were prepared and panelists were asked to select which sample was "cleaner" in flavor. All tests were done in a sensory evaluation room under red lights in order to negate any color differences that may have been present between samples. The results are shown below:
______________________________________ Number of Number of Positive Significance LevelTrial # Panelists Responses.sup.1 (.alpha. risk).sup.2______________________________________1 15 12 5%2 14 11 5%______________________________________ .sup.1 The number indicates those respondents who selected the proteinreduced product as being cleaner in flavor. .sup.2 The .alpha. values were determined from a statistical table. An .alpha. risk of 5% indicates (with 95% confidence) that the samples are statistically different, i.e., that the proteinreduced product is cleaner than the control.
Example 22
A granular waxy maize starch was pH adjusted to pH 9.5 as previously described. The starch was then placed in a freeze dryer and dried for 3 days until it was anhydrous (0% moisture). The freeze-dried (FD) starch was heat treated for 6 and 8 hours at 160.degree. C. in a forced draft oven.
Brabender evaluations were run. The results are shown below:
______________________________________Waxy Maize (pH 9.5)Viscosity (BU) BreakdownTime at 160.degree. C. Peak Peak + 10' (%)______________________________________Control -- 1260 320 75F.D. -- 1240 320 74T-I 6 hrs. 340 465 ris.T-I 8 hrs. 285 325 ris.______________________________________
The results show that the starch can be dehydrated by freeze drying and that the subsequent heat treatment is necessary to inhibit the starch. The starches are highly inhibited as shown by their rising viscosity.
Example 23
This example shows that thermal inhibition reduced the gelatinization temperature of the granular waxy maize starches.
The gelatinization temperature of an untreated waxy maize, a thermally-inhibited (T-I) waxy maize (pH adjusted and not pH adjusted), and chemically-crosslinked (X-linked) waxy maize starches (0.02%, 0.04%, and 0.06% phosphorus oxychloride) were determined by Differential Scanning Calorimetry. The starches were thermally dehydrated and heat treated in an oven for the indicated time and temperature.
The peak gelatinization temperature and enthalpy (.DELTA.H) are shown below.
______________________________________ Peak GelatinizationWaxy Maize Temperature (.degree. C.) Enthalpy (cal/g)______________________________________Unmodified 74 4.3T-I 68 2.9(pH 9.5; 160.degree. C.for 8.5 hrs.)T-I Waxy Maize 59 2.8(pH 6; 160.degree. C.for 8 hrs.)X-linked 73 4.4(0.02% POCl.sub.3)X-linked 72 4.2(0.04% POCl.sub.3)X-linked 74 4.2(0.06% POCl.sub.3)______________________________________
The results show that there was a significant reduction in peak gelatinization temperature of the thermally inhibited (T-I) starches. The heat treatment reduced the enthalpy (.DELTA.H) from 4.3 cal/g for the unmodified starch to 2.8-2.9 cal/g for the thermally-inhibited starch. The chemically crosslinked (X-linked) starches are essentially identical to the unmodified waxy starch in peak temperature (72-74.degree. C. vs. 74.degree. C.) and enthalpy (4.2-4.4 vs 4.3 cal/g). The reduced gelatinization temperature suggests that the overall granular structure has been altered by the dehydration and heat treatment.
Example 24
This example shows that the thermal inhibition may begin as early as 110.degree. C. (230.degree. F.), that it is substantially noticeable at 160.degree. (320.degree. F.), and that the gelatinization is unchanged or reduced. Granular waxy maize starches were pH adjusted to 7.0 and 9.5 and dehydrated and heat treated using air having a Dew point below 9.4.degree. C. (15.degree. F.) in the fluidized bed previously described at the indicated temperature and time. The Brabender and DSC results are shown below.
______________________________________Waxy Maize (pH 7.0)Dehydration/ Brabender Viscosity (BU)Heat Treatment BreakdownConditions Peak Peak + 10' (%)______________________________________Control* 1010 220 78.293.degree. C. for 0 min. 1010 220 78.2116.degree. C. for 0 min. 1030 250 75.7127.degree. C. for 0 min. 1050 260 75.2149.degree. C. for 0 min. 1130 350 69.0160.degree. C. for 0 min. 1010 590 41.6160.degree. C. for 10 min. 980 630 35.7160.degree. C. for 20 min. 910 610 33.0160.degree. C. for 80 min. 750 510 32.0160.degree. C. for 90 min. 735 510 30.6______________________________________ *Not pHadjusted.
Dehydration/ PeakHeat Treatment GelatinizationConditions Temperature** Enthalpy** (cal/g)______________________________________Control* 73.07 4.4393.degree. C. for 0 min. 71.79 4.01116.degree. C. for 0 min. 70.70 4.18127.degree. C. for 60 min. 70.66 4.07149.degree. C. for 90 min. 70.07 3.92160.degree. C. for 0 min. 69.50 4.08160.degree. C. for 10 min. 71.20 4.17160.degree. C. for 20 min. 68.87 4.32160.degree. C. for 80 min. 67.84 4.35160.degree. C. for 90 min. 67.29 4.38______________________________________ *Not pHadjusted. **Average of 2 readings.
Waxy Maize (pH 9.5)Dehydration/ Brabender Viscosity (BU)Heat Treatment BreakdownConditions Peak Peak + 10' (%)______________________________________Control (pH 9.5) 1240 300 75.893.degree. C. for 0 min. 1200 300 75.0104.degree. C. for 0 min. 1205 320 73.4110.degree. C. for 0 min. 1260 400 68.3121.degree. C. for 0 min. 1230 430 65.0127.degree. C. for 0 min. 1255 420 66.5138.degree. C. for 0 min. 1245 465 62.7149.degree. C. for 0 min. 1300 490 62.3160.degree. C. for 0 min. 1120 910 18.8160.degree. C. for 60 min. 750 730 2.7160.degree. C. for 90 min. 690 680 1.4______________________________________Dehydration/ PeakHeat Treatment GelatinizationConditions Temperature* Enthalpy* (cal/g)______________________________________Control (pH 9.5) 74.82 4.05127.degree. C. for 0 min. 74.84 4.17160.degree. C. for 0 min. 73.04 4.50160.degree. C. for 60 min. 71.84 4.60160.degree. C. for 90 min. 70.86 4.26______________________________________ *Average of 2 readings.
The DSC results show that at the onset of inhibition there was a slight reduction in the peak gelatinization temperature and that as the inhibition temperature and time increased there was a reduction in peak gelatinization temperature.
Example 25
This example shows the correlation between the RVA pasting temperature and time and DSC peak gelatinization temperature and time and the reduction in Brabender viscosity breakdown for various granular starch bases and for granular waxy maize starches dehydrated by various methods including heating, ethanol extraction, and freeze drying. The base starches were unmodified. The starches were all adjusted to pH 9.5 before dehydration. The ethanol-extracted and freeze-dried controls were pH adjusted and dehydrated but not heat treated. The dehydrated starches were all heat treated in an oven at 160.degree. C. for the indicated time except for the starches chemically crosslinked with sodium trimetaphosphate (STMP) which were heat treated at 160.degree. C. for the indicated time in the fluidized bed previously described.
The results are shown below.
______________________________________Starch DSC Viscosity (B.U.)Pasting Peak BreakTemp. Time Temp. Time Peak + down(.degree. C.) (min) (.degree. C.) (min) Peak 10' (%)______________________________________Tapioca 68.20 3.7 70.61 6.6 1595 440 72.41ControlDehydrated Thermally/Heat Treated at 160.degree. C.T-I 66.65 3.4 68.31 6.3 1230 560 54.47(2 hrs.)T-I 64.20 2.9 65.41 6.0 355 335 5.63(6 hrs.)Potato 61.05 2.3 62.67 5.8 1825 1010 44.66ControlDehydrated Thermally/Heat Treated at 160.degree. C.T-I 60.25 2.1 61.41 5.6 995 810 18.59(3 hrs.)T-I 60.20 2.1 61.13 5.6 ris. ris. ris.(6 hrs.)Waxy 70.95 4.3 73.86 6.9 1215 350 71.79MaizeControlDehydrated Thermally/Heat Treated at 160.degree. C.T-I 68.15 3.7 70.71 6.6 760 720 5.26(8 hrs.)Waxy 70.95 4.3 74.23 6.9 1250 400 68.00MaizeControlEthanol Dehydrated/Heat Treated at 160.degree. C.T-I 65.00 3.1 71.81 6.7 ris. ris. ris.(2 hrs.)T-I 63.85 2.8 68.12 6.3 ris. ris. ris.(7 hrs.)Waxy 71.30 4.4 74.16 6.9 1240 320 74.19MaizeControlDehydrated by Freeze Drying/Heat Treated at 160.degree. C.T-I 69.50 4.0 66.09 6.1 ris. ris. ris.(6 hrs.)T-I 66.75 3.5 64.64 6.0 ris. ris. ris.(8 hrs.)Cross- 71.70 N.D. 74.33 6.9 ris. ris. ris.linkedWaxyMaizeControlThermally Dehydrated Crosslinked Waxy Maize*T-I 69.10 N.D. 71.66 6.7 ris. ris. ris.(30 min.)T-I 66.00 N.D. 67.14 6.2 ris. ris. ris.(150min.)______________________________________ *Fluidized bed.
The results show that heat treatment of thermally and non-thermally dehydrated granular starches reduced the pasting and peak gelatinization temperatures while at the same time inhibiting the viscosity breakdown. Because the gelatinization temperature has been lowered by the heat treatment of the dehydrated starch, less time is required to reach the pasting and gelatinization temperatures. The more highly inhibited starches showed a lower pasting temperature and less breakdown in viscosity.
Example 26
This example describes a visual evaluation of the dry powder flow properties of granular waxy maize starches adjusted to pH 9.5 and thermally dehydrated and heat treated in the fluidized bed previously described.
The starches evaluated are shown below:
______________________________________No. Heat Treatment Conditions______________________________________1 160.degree. C. for 30 min.2 160.degree. C. for 60 min.3 160.degree. C. for 180 min.______________________________________
Powder No. 1 distributed fairly evenly and the flow pattern was uniform. It was somewhat fluid and had some dynamic quality. Only a slight amount of air was entrapped in the body of the powder. Powder No. 2 distributed evenly and the flow pattern was uniform. The powder was fluid and had a dynamic quality. There was no air entrapment in the body of the powder. Powder No. 3 distributed evenly and the flow pattern was uniform. The powder was fluid, water-like, and had a dynamic quality. No air was entrapped in the body of the powder. The control starch powder clumped and had an irregular flow. It had a cake-like static quality. Air was entrapped in the body of the powder.
Example 27
This example measures the flow properties of thermally-inhibited waxy maize starches by determining the angle of repose which is an indication of performance with regard to mobility/flow. The starches were adjusted to pH 9.5 and thermally inhibited by dehydration and heat treatment in the fluidized bed previously described.
The results are shown below:
______________________________________ Angle ofHeat Treatment Conditions Repose*______________________________________160.degree. C. for 30 min. 24.17160.degree. C. for 60 min. 26.75160.degree. C. for 180 min. 23.60______________________________________ *Average of 5 readings.
The thermally-inhibited starches had good flow properties. The control did not flow. A chemically crosslinked and derivatized waxy corn starch also did not flow. The funnels were completely blocked upon addition of the sample. This starch would not even flow through powder funnels with larger internal diameter orifices without constant tapping. Similar results, i.e., no flow, were observed with native corn starch.
Example 28
The following example shows the wet particle size of waxy maize starches adjusted to pH 9.5 and dehydrated and heat treated in the fluidized bed previously described.
______________________________________ Wet Particle Size*Starch Heat Treatment Conditions (microns)______________________________________Control 15.198T-I 160.degree. C. for 0 min. 17.029T-I 160.degree. C. for 90 min. 19.251T-I 169.degree. C. for 180 min. 18.880______________________________________
The result shows that the thermally-inhibited starches swell more than the uninhibited control. As the starch became more highly inhibited, the swelling was somewhat reduced but the starch was still more swollen than the control. This increased swelling indicates that the thermally-inhibited starches would be useful as tablet disintegrants.
Example 29
This example shows that the thermally-inhibited starches and flours are substantially sterilized by the dehydration heat treatment in the fluidized bed. This property is useful in all pharmaceutical applications.
The testing was done according to the methods described in The United States Pharmacopeia (USP 23), The National Formulary (NF 18) dated Jan. 1, 1995, which is the procedure described at pages 17-19 of Chapter 3 "Aerobic Plate Count" by J. T. Peeler and L. J. Maturin, F.D.A. Bacteriological Analytical Manual, 7th Edition A.D.A.C. International, Arlington, Va. (1992). The starches were tested for the presence of Coliform, Salmonella, yeast and molds, Staphylococcus aureus, Escherichia coli, and Pseudomonas aeruginosa. The total plate count at 32.degree. C. was determined and any organisms were identified.
PART A--Thermally-Inhibited Waxy Rice Flour
The flour was adjusted to pH 9.5, heat treated under the conditions shown below, and stored for about 3 months in non-sterilized, covered glass containers.
The results are shown below.
______________________________________Heat Treatment Plate Count (CFU)*______________________________________None 7500160.degree. C. for 0 min. <10160.degree. C. for 60 min. <10160.degree. C. for 120 min. <10______________________________________ *Colony forming units.
PART B--Thermally-Inhibited Waxy Maize Starch
The starch was adjusted to pH 9.5, and thermally-inhibited under the conditions shown below, and stored for about 2 months in non-sterilized, covered glass containers. The thermally-inhibited starches and the control starch were microbiologically tested for their total plate count and the presence of organisms using the above procedure.
The results are shown below.
______________________________________ Plate Count Colony Forming Units (CFU)*______________________________________None 2000160.degree. C. for 60 min. <10160.degree. C. for 60 min. sample <10160.degree. C. for 120 min. <10sample)______________________________________ *Colony forming units.
Coliform, Salmonella, yeast and molds, Staphylococcus aureus, Escherichia Coli, and Pseudomonas aeruginosa were not present. A reading of <10 CFU means there is essentially nothing measurable. The above results are particularly surprising, especially since the thermally-inhibited flours and starches were not handled using aseptic techniques. If stored and maintained under sterile conditions, these starches should be useful in products where microbiological considerations are of concern.
Example 30
Waxy maize samples, crosslinked with phosphorus oxychloride POCl.sub.3 at 0.02% by weight, were heat treated, at the naturally occurring pH and at pH 9.5, and were evaluated for inhibition.
The results set out in the following tables.
______________________________________ Viscosity (BU)Temp Time Peak + 92.degree. C. + Breakdown(160.degree. C.) (min) Peak 10' 92.degree. C. 30' (%)______________________________________Waxy Maize (POCl.sub.3 Natural pH)Control 830 820 1 0 750 742 730 720 1 30 635 522 630 580 2 60 550 525 550 465 5 90 425 415 420 360 2120 335 315 330 280 6150 280 260 280 210 7180 205 200 200 180 2Waxy Maize (pH 9.5)Control 830 820 1 0 750 720 -- -- 4 30 -- -- 630 669 ris. 60 -- -- 400 635 ris. 90 -- -- 330 520 ris.120 -- -- 180 530 ris.150 -- -- 110 470 ris.180 -- -- 100 470 ris.______________________________________
The data show decreasing viscosity and almost no breakdown in viscosity with longer heat treating times, indicating that crosslinked starches can be made even more inhibited by this process. The data also show that increasing the pH further increases inhibition.
Example 31
This example shows the thermal inhibition of converted starches.
Samples of waxy maize and tapioca starch were slurried in 1.5 parts water. The slurries were placed in a 52.degree. C. water bath, with agitation, and allowed to equilibrate for one hour. Concentrated hydrochloric acid (HCl) was added at 0.8% on the weight of the samples. The samples were allowed to convert at 52.degree. C. The pH was then adjusted to 5.5 with sodium carbonate, then to pH 8.5 with sodium hydroxide. The samples were recovered by filtering and air drying (approximately 11% moisture). The starches in 50 g amounts were placed in an aluminum tray, covered and placed into a forced draft oven at 140.degree. C. for 5.5 hours. The starches were evaluated for inhibition.
The results set out in the following table.
______________________________________Waxy Maize TapiocaViscosity (BU) Viscosity (BU) Peak + Break- Peak + Break-Peak 10' down (%) Peak 10' down (%)______________________________________unmodified 1380 250 81.9 810 225 72.2acid 640 110 82.3 432 115 73.4convertedT-I acid 805 728 9.6 495 350 29.3converted______________________________________
The results show that converted starches can be thermally inhibited by this process.
Example 32
This example describes the preparation of a thermally-inhibited enzyme-converted starch.
A total of 1.5 kg of a thermally-inhibited waxy maize starch (pH 9.5; heated at 160.degree. C. for 100 minutes in the fluidized bed previously described) is slurried in 4.5 liters of water. The pH of the slurry is then adjusted to 4.5 using dilute hydrochloric acid. the temperature of the mixture is then raised to 55.degree. C. and 75 g. of glucoamylase is added. The mixture is stirred until the desired degree of reducing sugar is produced, for example, 23 DE (Dextrose Equivalent), the pH of the mixture is adjusted to 9.5 using dilute sodium hydroxide and held for 30 minutes to inactivate the enzyme. It is then readjusted to pH 6.0-7.0 with dilute hydrochloric acid, recovered by filtration, washing and drying. Alternatively, the reaction mixture can be recovered directly by spray drying without the purification step.
Example 33
Waxy maize samples reacted with 7% and 3% by weight propylene oxide (PO) and thermally inhibited, at the naturally occurring pH and at pH 9.5, were evaluated for inhibition.
The results set out in the following tables.
______________________________________ Viscosity (BU)Temp. Time Peak + 92.degree. C. + Breakdown(.degree. C.) (min) Peak 10' 92.degree. C. 30' (%)______________________________________Waxy Maize (7% PO and natural pH at 160.degree. C.)Control -- 1420 395 -- -- 72160 0 1030 380 -- -- 63160 30 800 530 -- -- 34160 60 685 430 -- -- 37160 90 635 340 -- -- 46160 120 620 340 -- -- 45160 150 565 300 -- -- 47160 180 540 280 -- -- 48Waxy Maize (7% PO and pH 9.5 at 160.degree. C.)Control -- 1420 395 -- -- 72160 0 1360 960 -- -- 29160 30 1010 950 -- -- 6160 60 1030 930 -- -- 10160 90 910 890 -- -- 2160 120 843 830 -- -- 2160 180 800 792 -- -- 1Waxy Maize (3% PO and natural pH at 160.degree. C.)Control -- 1155 280 -- -- 76160 0 900 360 -- -- 60160 30 570 370 -- -- 35160 60 480 350 -- -- 27Waxy Maize (3% PO and natural pH at 160.degree. C.)Control -- 1155 280 -- -- 76160 90 440 300 -- -- 32160 120 375 235 -- -- 37160 150 310 185 -- -- 40160 180 300 180 -- -- 40Waxy Maize (3% PO and pH 9.5 at 160.degree. C.)Control -- 1155 280 -- -- 76160 0 1220 960 -- -- 21160 30 1020 950 -- -- 7160 60 880 865 -- -- 2160 90 -- -- 750 790 ris.160 120 -- -- 620 780 ris.160 150 -- -- 510 750 ris.160 180 -- -- 400 700 ris.______________________________________
The data show that derivatized starches, in this case etherified starches, can be thermally inhibited by this process and that higher inhibition can be achieved at higher pH.
Example 34
A converted hydroxypropylated waxy maize starch (25 WF starch reacted with 2% propylene oxide) was adjusted to pH 9.5 and thermally inhibited using the fluidized bed previously described. Samples were taken at 110.degree. C., 125.degree. C., and 140.degree. C., all for 0 minutes.
The thermally-inhibited starch samples were cooked in tap water at 88-93.degree. C. (190-200.degree. F.) bath temperature for 30-60 minutes to yield solutions having a Brookfield viscosity of approximately 3000 cps. The viscosity stability at room temperature was evaluated. The control was a hydroxy-propylated waxy maize starch which was not thermally-inhibited.
The results are tabulated below.
______________________________________Solution Stability Control 110.degree. C. 125.degree. C. 140.degree. C.______________________________________Water Fluidity 25.0 25.5 20.6 21.8Solids (%) 18 18 18 18Initial 3160 2550 2820 2800Viscosity (cps)Viscosity after 3280 -- -- 264024 hours (cps)Viscosity after 3020 2475 2730 28107 days (cps)Viscosity after 3000 1980 2140 29408 days (cps)Viscosity after 2850 1990 2230 28709 days (cps)Appearance clear clear clear yellow______________________________________
Example 35
Waxy maize samples were reacted with 1% by weight acetic anhydride (Ac.sub.2 O) and thermally-inhibited at the naturally occurring pH and at pH 8.5. The control was the non-thermally-inhibited waxy maize starch acetate.
______________________________________Waxy Maize (1% Ac.sub.2 O and pH 8.5 at 160.degree. C.)______________________________________Control -- 1480 490 -- -- 67 0 1170 560 -- -- 52 30 970 725 -- -- 25 60 875 600 -- -- 31 120 690 490 -- -- 29 180 585 545 -- -- 7______________________________________
The data show that derivatized starches, in this case esterified starches, can be inhibited to varying degrees and that higher inhibition can be obtained at higher pH.
Example 36
This example shows the preparation of a thermally-inhibited cationic starch.
A granular waxy corn starch (1000 g) was slurried in 1500 cc water, 175 g of 4% sodium hydroxide were added, and the slurry was heated to 40.degree. C. One hundred (100) g of a 50% aqueous solution of 3-chloro-2-hydroxypropyl trimethyl ammonium chloride was added while maintaining the pH at 11.5 by adding 4% sodium hydroxide. The mixture was allowed to react overnight at 40.degree. C. The slurry was adjusted to pH 6.5 with hydrochloric acid, filtered, washed and air dried to about 8-15% moisture. The degree of substition was of 0.04.
A portion of the above cationic starch derivative was chemically crosslinked with 0.01 wt. % of epichlorohydrin at 40.degree. C. for 16 hours, neutralized to pH 6.0, filtered, water washed (2 parts water per part of starch), and air dried to about 8-15% moisture.
A portion of the above chemically-crosslinked, cationic starch was thermally inhibited by adjusting the pH to 9.5 with a 5% solution of sodium carbonate, spray-drying without gelatinization to between 3-15% moisture, and thermally dehydrating and heat treating the cationic, chemically-crosslinked granular starch in the fluidized bed previously described.
The starch samples were slurried at 4-6% solids and cooked in a mini-jet cooker (scaled down jet cooker to simulate a commercial jet cooker) at a temperature of 105-122.degree. C. and an applied back pressure of 5-20 psi using controlled live steam. The mini-jet cooker had a cooking chamber capacity or volume of 5.0 ml. The starch was passed through the cooking chamber at a flow rate of about 130 ml/min with a retention time of about 2.3 seconds.
The samples of starches were tested for Brookfield viscosity at 3% solids at 20 rpm with a No. 5 spindle.
______________________________________Brookfield Viscosity (cps)______________________________________Control 300T-I Chemically Crosslinked 3650T-I (120.degree. C. for 0 min.) 440T-I (125.degree. C. for 15 min.) 790T-I (130.degree. C. for 0 min.) 990T-I (160.degree. C. for 0 min.) 1900T-I (160.degree. C. for 30 min.) <60T-I (160.degree. C. for 120 min.) <60______________________________________
The results show that the thermally-inhibited starches are much lower in viscosity (<60 to 1900 cps) than the thermally-inhibited chemically crosslinked starch (3650 cps.). This is a significant advantage in some end uses.
A Brabender analysis run on the starch which thermally inhibited at 160.degree. C. for 120 minutes. It showed a percentage breakdown of 2%.
Example 37
This example shows the preparation of potato starches modified with an amino-multicarboxylic acid (CEPA) reagent, i.e., 2-chloroethylaminodipropionic acid (hereinafter referred to as CEPA-starches) and their subsequent thermal-inhibition.
Deionized water (150 ml) was added to a liter beaker and heated to 45.degree. C. with an external constant temperature bath. A total of 30 g sodium sulfate (30% on starch) was dissolved in the water followed by the addition of 100 g of the potato starch. A solution of 3% aqueous sodium hydroxide (25 ml) was added slowly with good agitation to minimize starch swelling. A 25% aqueous solution of the CEPA reagent (32 ml) to give an 8% starch treatment (dry basis was added simultaneously with a 3% aqueous sodium hydroxide solution (170 ml). The addition rates used kept the level of caustic high so that pH was about 11.0 to 11.5 during the reaction. The reaction was run at 42-45.degree. C. for 16 hours and then neutralized by adding 3 N hydrochloric acid to adjust pH to about 9.5, followed by stirring for 30 minutes. Overhead stirring was used throughout this reaction. The starch was then filtered and washed twice with 150 ml of water and allowed to air dry. Analysis of the starch for bound nitrogen showed 0.25% N (dry basis).
The pH 9.5 CEPA-starch was heat treated at 100.degree. C., 110.degree. C., 120.degree. C., 130.degree. C., and 140.degree. C. for 0 minutes using the fluidized bed previously described.
Example 38
This example describes the preparation of a barbecue sauce containing a thermally inhibited waxy maize starch at its naturally occurring pH (pH 6), heat treated at 160.degree. C. for 150 minutes (T-I starch). The ingredients in percent by weight are as follows:
______________________________________T-I starch 2.5%sugar 3.0salt 0.3paprika 0.2chili powder 0.2cinnamon 0.2ground cloves 0.2tomato puree 47.4minced onion 5.3Worcestershire sauce 6.6water 26.2vinegar 7.9TOTAL 100.0______________________________________
The sauce is heated to 85.degree. C., held for 15 minutes, and cooled overnight at room temperature. The sauce will have a smooth, non-cohesive texture.
Now that the preferred embodiments of the invention have been described in detail, various modifications and improvements thereon will become readily apparent to the practitioner. Accordingly, the spirit and scope of the present invention are to be limited only by the appended claims, and not by foregoing specification.

Number	Name	Date
2274789	Horesi	Mar 1942
2317752	Fuller	Apr 1943
2373016	Daly et al.	Apr 1945
2427328	Schopmeyer et al.	Sep 1947
2590912	Yarber	Apr 1952
2661349	Caldwell et al.	Feb 1949
2791512	Hatch et al.	May 1957
2897086	Sowell et al.	Jul 1959
2951776	Scallet et al.	Sep 1960
3155527	Mentzer	Nov 1964
3331697	Salamon	Jul 1967
3399081	Bernetti et al.	Aug 1968
3408214	Mentzer	Oct 1968
3463668	Evans et al.	Aug 1969
3477903	Semegran et al.	Nov 1969
3490917	Doe et al.	Jan 1970
3515591	Feldman et al.	Jun 1970
3563798	Germino et al.	Feb 1971
3578497	Hjermstad	May 1971
3607394	Germino et al.	Sep 1971
3607396	Germino et al.	Sep 1971
3640756	Beersma et al.	Feb 1972
3690938	Swift	Sep 1972
3725387	McClendon et al.	Apr 1973
3810783	Bomball	May 1974
3844807	Bramel	Oct 1974
3949104	Cheng et al.	Apr 1976
3950593	Bomball	Apr 1976
3967975	Idaszak	Jul 1976
3977897	Wurzburg et al.	Aug 1976
4013799	Smalligan et al.	Mar 1977
4131574	Isherwood et al.	Dec 1978
4256509	Tuschhoff et al.	Mar 1981
4266348	Ledding	May 1981
4280851	Pitchon et al.	Jul 1981
4303451	Seidel et al.	Dec 1981
4303452	Ohira et al.	Dec 1981
4329181	Chiu et al.	May 1982
4366275	Silano et al.	Dec 1982
4391836	Chiu	Jul 1983
4428972	Wurzburg et al.	Jan 1984
4465702	Eastman et al.	Aug 1984
4491483	Dudacek et al.	Jan 1985
4575395	Rudin	Mar 1986
4600472	Pitchon et al.	Jul 1986
4610760	Kirkpatrick et al.	Sep 1986
4847371	Schara et al.	Jul 1989
5037929	Rajagopalan et al.	Aug 1991
5085228	Mooney et al.	Feb 1992
5087649	Wegner et al.	Feb 1992
5149799	Rubens	Sep 1992
5155140	Marten et al.	Oct 1992
5181959	Nagai et al.	Jan 1993
5329004	Eden et al.	Jul 1994
5368690	Solarek et al.	Nov 1994
5725676	Chiu et al.	Mar 1998

Number	Date	Country
1 150 934	Feb 1983	CAX
0 108 833	Nov 1982	EPX

	Number	Date
Parent	473688	Jun 1995
Parent	374279	Jan 1995
Parent	296211	Aug 1994
Parent	099753	Jul 1993

Thermally-inhibited non-pregelatinized granular starches and flours and process for their preparation

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Parent Case Info

US Referenced Citations (56)

Foreign Referenced Citations (2)

Continuation in Parts (4)