Patent Application
20120211266
The priority of Japan Patent Application Nos. 2011-035338 and 2011-136176 upon which this patent application is based is hereby incorporated by reference.
1. Field of the Invention
The present invention relates to a wiring board having a through hole and a manufacturing method thereof.
2. Description of the Related Art
A wiring board consists of a fiber reinforced resin plate made of reinforcement fiber such as glass fiber and matrix resin. When a terminal, which is pressed and connected, is pressed in a through hole penetrating through the wiring board, a portion near the through hole of the wiring board whitens.
In this manner, the wiring board in which the whitening is generated is judged as inferior products. As a result, the productivity of the wiring board is reduced. Further, when a test of high temperatures and humidity is performed in the wiring board including the whitening, insulation properties result in low result and it becomes a problem.
In Patent Document 1, a technique relaxing physical stress when pressing a terminal in a through hole by changing a shape of the terminal is disclosed.
More specifically, as shown in
However, although using this technique, generation of the whitening in a portion around the through hole of the wiring board has not been able to prevent completely.
Accordingly, an object of the present invention is to provide a wiring board improving the above problem, that is, the wiring board having a through hole which can prevent generation of whitening.
The applicants of the present invention have conducted a search for a cause of the whitening in detail.
When a terminal 9 is pressed into a through hole 7, resin material 3b of a fiber reinforced resin plate 3 which consists of a glass cloth 3 made of glass fiber being a reinforcement fiber in the wiring board A and the resin material 3b impregnated with a fiber layer of the glass cloth 3 and hardened is destroyed by a stress of the terminal 9, and microcrack is generated, or glass fibers of a glass cloth 3a are delaminated (see
More specifically, in order to attain the above object, according to a first aspect of the present invention, the wiring board of the present invention consists of the fiber reinforced resin plate, and has a through hole and a whitening prevention portion made only with matrix resin forming the fiber reinforced resin plate. The whitening prevention portion is integrally formed in the fiber reinforce resin plate, and arranged around the through hole.
Furthermore, according to a second aspect of the present invention, a hollow shape land is arranged on a surface of the wiring board around the through hole, and an outer diameter of the land is larger than a diameter of the whitening prevention portion.
Furthermore, according to a third aspect of the present invention, a hollow shaped land is arranged on a surface of the wiring board around the through hole, and connected to a wiring of the wiring board via a wide portion larger than a width of the wiring.
According to a fourth aspect of the present invention, a manufacturing method of a wiring board made of a fiber reinforced resin plate and having a through hole, the manufacturing method comprising the steps of:
According to the wiring board of the present invention, the wiring board having the through hole can be provided without a generation of the whitening around through hole.
Furthermore, in addition to the above effect, damage and disconnection can be prevented in advance when the wiring board is used in high temperatures and subjected to high temperatures.
The above and other objects and features of this invention will become more apparent from the following description taken in conjunction with the accompanying drawings.
A wiring board according to an embodiment of the present invention will be explained with reference to drawings.
The wiring board A is made of a fiber reinforced resin plate and has the through hole 7. The fiber reinforced resin plate is formed by laminating a prepreg which impregnates a glass cloth 3a with insulating resin composition such as matrix resin and is constructed and then by hardening the matrix resin. In this embodiment, a metal core 2 is laminated between two prepregs. A whitening prevention portion 4 made of the matrix resin constituting the fiber reinforced resin plate is arranged around the through hole 7.
The above wiring board A can be provided as follows.
The wiring board is made of the prepreg formed by impregnating the glass cloth with the matrix resin of thermoset resin. A portion forming the through hole or a surrounding portion thereof is removed from the prepreg of the wiring board (reinforced fiber removing step).
Next, the prepreg having a hole is laminated as needed, and then is hardened by press forming under the proper conditions (for example, heating temperature, press, and time) to the matrix resin, and formed. In this pressing forming step, the matrix resin has flow property, and the matrix resin reaches the portion in which the prepreg is partly removed. As a result, the portion, namely through hole forming portion, made only with matrix resin is integrally formed in the fiber reinforced resin plate.
After the wiring board is formed in this manner, the through hole is arranged in the through hole forming portion. Thereafter, the through hole is formed according to a general manufacturing method of the wiring board. The whitening prevention portion 4 made only with the matrix resin is arranged around the through hole. Thus, the wiring board having the whitening prevention portion 4 can be produced.
In such the wiring board, the through hole 7 is away from the glass cloth 3a so as to arrange the whitening prevention portion 4 around the through hole 7. Therefore, as shown in
In the above example, single-layered the metal core 2 is arranged in the wiring board A. However, it is not limited thereto. For example, the wiring board may have a plurality of the metal cores, and may not have the metal core.
When the wiring board is used in a high-temperature environment, for example, the wiring board is used near a dashboard or inside of a door, stress may be added between land in itself and/or wirings of the wiring board connected to a land from difference of rate of thermal expansion between the whitening prevention portion and the fiber reinforced resin plate. As a result, damage and disconnection may be generated.
More specifically, as shown in
As shown in
Furthermore, a portion enclosed with an oval shown in
The whitening prevention portion 4 is arranged close to the edge of the land 7a. Because of the arrangement, when the wiring board is subjected to heat, the whitening prevention portion 4 which does not include the glass cloth 3a is easily expanded as shown with a double-headed arrow in
In order to prevent the breakage and the disconnection in the connection connecting the land 7a with the wiring 10, an outer diameter of the land 7a is formed larger than an outer diameter of the whitening prevention portion 4 as shown in
In addition, a wide portion larger than a width of the wiring 10 may be arranged in the connection connecting the wiring 10 with the land 7a besides arranging the land 7a larger than the whitening prevention portion 4.
A specific example is shown in
The hollow disk-shaped land 7a was explained as an example in the above embodiment. However, the prevent invention is not limited to the disk-shaped land 7a. For example, various shapes such as an ellipse or box shape may be applied to the present invention.
It is intended that the above-described embodiment is only a representative embodiment, and it should be understood that the present invention is not limited thereto. Various changes and modifications can be made without departing the scope of the present invention.