The present invention relates to the cleaning of etchant residues formed in the etching of substrates.
When an energized gas is used to process a substrate in a chamber, for example to etch the substrate, etchant residues are often deposited on internal surfaces of the chamber. The deposited etchant residues may adversely affect the substrate processing operations conducted in the chamber. For example, the etchant residues can corrode the surfaces of the chamber and its internal components, requiring frequent replacement of the components, and thereby increasing chamber downtime. The accumulated etchant residues can also flake off from the chamber surfaces and contaminate substrates being etched in the chamber. Thus, the etchant residues needs to be periodically cleaned off the chamber surfaces.
In conventional cleaning processes, a cleaning gas energized by RF or microwave energy is provided in the chamber to clean the etchant residues. The cleaning gas composition and other process parameters are tailored to clean the particular etchant residue composition that is generated during the etching process. For example, a conventional cleaning process to clean a chamber having silicon containing etchant residues that are generated by the etching of silicon containing substrate material in the chamber, may use a cleaning gas composition tailored to clean the silicon containing etchant residues.
However, conventional cleaning processes are generally not very efficient at cleaning etchant residues composed of multiple layers having different chemical compositions, such as those generated in foundry etching processes. In foundry etching, the same chamber is often used to etch a number of different types of substrate materials, thereby often generating layers of etchant residues having a variety of different types of compositions which deposit upon one another on the surfaces in the chamber. Conventional cleaning processes do not efficiently clean these multi-layer etchant residues because they are tailored to clean the single composition etching residues formed in a simpler etching process. Thus, when conventional cleaning process are used to clean foundry etch chambers, the chamber is often cleaned non-uniformly because the cleaning gas is more effective at cleaning certain compositions of etchant residues. The conventional cleaning process can also result in overcleaning and resultant erosion of the foundry etch chamber.
Thus, it is desirable to have a cleaning process capable of cleaning a chamber after the etching of a number of different types of substrates in the chamber. It is further desirable to have a cleaning process capable of cleaning multi-layer etchant residues without excessive erosion of the underlying chamber surfaces.
A substrate processing apparatus comprising a chamber comprising a substrate transport to transport a substrate onto a substrate support in the chamber, a gas supply to provide a gas in the chamber, a gas energizer to energize the gas, and a gas exhaust to exhaust the gas, a controller to operate the substrate support, gas supply, gas energizer, and gas exhaust, to set etching process conditions in the chamber to etch a plurality of substrates, thereby depositing etchant residues on surfaces in the chamber, and cleaning process conditions in the chamber to clean the etchant residues, the process conditions comprising a volumetric flow ratio of O2 to CF4 of from about 1:1 to about 1:40.
A method of processing substrates in a chamber, the method comprising etching a plurality of substrates in the chamber, thereby depositing etchant residues on surfaces in the chamber, and cleaning the etchant residues by introducing a cleaning gas comprising O2 and CF4 into the chamber, the volumetric flow ratio of O2 to CF4 being from about 1:1 to about 1:40, energizing the cleaning gas, and exhausting the cleaning gas from the chamber.
A substrate processing apparatus comprising a chamber comprising a substrate transport to transport a substrate onto a substrate support in the chamber, a gas supply to provide a gas in the chamber, a gas energizer to energize the gas, and a gas exhaust to exhaust the gas, a controller to operate the substrate support, gas supply, gas energizer, and gas exhaust, to set etching process conditions in the chamber to etch a plurality of substrates, thereby depositing etchant residues on surfaces in the chamber, sacrificial substrate processing conditions to process one or more sacrificial substrates in the chamber, thereby depositing a sacrificial coating on surfaces in the chamber, and cleaning process conditions in the chamber to clean the etchant residues and sacrificial coating, the process conditions comprising a volumetric flow ratio of O2 to CF4.
A method of processing substrates in a chamber, the method comprising etching a plurality of substrates in the chamber, thereby depositing etchant residues on surfaces in the chamber, processing one or more sacrificial substrates in the chamber, thereby depositing a sacrificial coating on surfaces in the chamber, and cleaning the etchant residues and sacrificial coating by introducing a cleaning gas comprising O2 and CF4 into the chamber, energizing the cleaning gas, and exhausting the cleaning gas from the chamber.
These and other features, aspects, and advantages of the present invention will become better understood with regard to the following description, appended claims, and accompanying drawings which illustrate examples of the invention, where:
An etching chamber 106 comprises, for example, a decoupled plasma source (DPS) chamber, schematically illustrated in
Generally, the etching chamber 106 comprises walls 107 typically fabricated from metal or ceramic materials. Metals commonly used to fabricate the chamber 106 include aluminum, anodized aluminum, “HAYNES 242,” “Al-6061,” “SS 304,” “SS 316,” and INCONEL, of which anodized aluminum is preferred. The wall 107 may comprise sidewalls 114, a bottom wall 116, and a ceiling 118. The ceiling 118 may comprise a substantially arcuate shape, or in other versions, the ceiling 118 may comprise a domed, substantially flat, or multi-radius shaped portion. The chamber 106 typically comprises a volume of at least about 5,000 cm3, and more preferably from about 10,000 to about 50,000 cm3. In operation, gas is introduced into the chamber 106 through a gas supply 130. The gas supply 130 may include a gas source 138 and a gas distributor 137, the gas distributor 137 comprising conduits 136 having flow control valves 134 to control the flow of gas into the chamber 106 and gas outlets 142. In one version, the gas outlets 142 may be arranged about a periphery of the substrate 104, as shown in
The gas is energized to process the substrate 104 by a gas energizer 154 that couples energy to the gas in the process zone 108 of the chamber 106 (as shown) or in a remote zone upstream from the chamber 106 (not shown). In one version, the gas energizer 154 comprises an antenna 156 comprising one or more inductor coils 158 which may have a circular symmetry about the center of the chamber 106. Typically, the antenna 156 comprises solenoids having from about 1 to about 20 turns. A suitable arrangement of solenoids is selected to provide a strong inductive flux linkage and coupling to the process gas. When the antenna 156 is positioned near the ceiling 118 of the chamber 106, the adjacent portion of the ceiling may be made from a dielectric material, such as silicon dioxide, which is transparent to RF or electromagnetic energy. An antenna power supply 155 provides, for example, RF power to the antenna 156 at a frequency of typically about 50 KHz to about 60 MHz, and more typically about 13.56 MHz; and at a power level of from about 100 to about 5000 Watts.
In one version, the gas energizer 154 may also or alternatively comprise process electrodes (not shown) that may be used to energize or further energize the process gas. Typically, the process electrodes include one electrode (not shown) in a wall, such as a sidewall 114 or ceiling 118 of the chamber 106 that may be capacitively coupled to another electrode, such as an electrode in the support 110 below the substrate 104. Generally, the electrodes may be electrically biased relative to one another by an electrode voltage supply (not shown) that includes an AC voltage supply for providing an RF bias voltage. The RF bias voltage may comprise frequencies of about 50 kHz to about 60 MHz, and is preferably about 13.56 MHz, and the power level of the RF bias current is typically from about 50 to about 3000 watts. The gas energizer 154 may also comprise a microwave source (not shown) to energize the gas in the chamber 106 or in a remote chamber (also not shown).
In operation, a substrate transport 111, such as for example a robotic arm and associated robotics, transports the substrate 104 onto the substrate support 110 in the chamber 106. The support 110 may comprise an electrostatic chuck 170 which comprises a dielectric body 174 which at least partially covers an electrode 178 and which may include a substrate receiving surface 180. The electrode 178 may also serve as one of the process electrodes discussed above. The electrode 178 may be capable of generating an electrostatic charge for electrostatically holding the substrate 104 to the support 110 or electrostatic chuck 170. A power supply 182 provides the chucking voltage to the electrode 178.
The chamber 106 may also comprise a detector 200 for monitoring a process, such as a cleaning process, in the chamber 106 and sending a signal to a chamber controller 300. The detector 200 should be positioned to detect a radiation emission from, for example, an energized gas in the chamber 106. Also, the detector 200 should have the sensitivity required to accurately detect the changes in the attribute of the radiation emission. For example, the detector 200 should have the sensitivity required to determine when an endpoint value of the intensity of the radiation emission has been obtained. In one version, a suitable detector 200 may comprise a sensor 201, such as for example a spectrometer, charge coupled device, or photodiode mounted to detect radiation passing through a window 202 formed in a wall 107 of the chamber 106 that is permeable to radiation of the desired wavelengths. The detector 200 may also comprise a monochrometer or optical filter, which may be used to select the desired wavelength of radiation to be monitored.
A number of different processes may be performed in the chamber 106. The different processes may be performed to etch different materials on different substrates 104, using process parameters and etchant gas compositions which are selected according to the type of material to be etched. For example, multiple etching processes may be performed to etch silicon containing materials, such as for example polycide, polysilicon, tungsten silicide, titanium silicide; carbon containing materials such as for example low k dielectric materials; metal containing materials; or resist materials such as for example photoresist which may be patterned to a desirable pattern configuration which is to be etched in the underlying layers; on different batches of substrates 104. The substrates 104 can be silicon wafers, compound semiconductors, or dielectric materials such as silicon oxide or aluminum oxide. The multiple etching processes performed may comprise, for example, polysilicon, polisilicide, or photoresist etching processes. The multiple etching processes may generate a variety of different types of etchant residues which deposit as layers on the internal surfaces 115 in the chamber 106 to form a multi-layer etchant residue on the chamber surfaces 115. The different etching processes are often performed to etch the different etchant residues.
The multiple etching processes may include a number of processes, for example, a first etching process to etch a first material on one or more first substrates 104, and a second etching process to etch a second material on one or more second substrates 104. The first etching process may be used to first substrates 104 comprising a first material such as tungsten silicide. In the first etching process, the substrate 104 is etched by placing a first substrate 104 on a substrate support 110, introducing a first etchant gas into the etching chamber 106, and energizing the etchant gas by, for example, applying power to an antenna about the chamber 106 and/or an electrode 178 in the chamber 106. To etch tungsten silicide, the first etchant gas typically comprises one or more of Cl2, O2, and N2; and the gas is energized by applying an RF power level of about 1200 Watts to the antenna 156 about the chamber 106 and a bias power level of about 120 Watts to the electrode 178 in the chamber 106. After a batch of the first substrates 104 are etched, a second etching process may be used to etch a second material, such as for example, silicon, on a batch of second substrates 104. In the second etching process, the second substrates 104 are placed in the chamber 106, a second etchant gas is introduced into the etching chamber 106, and the gas is energized by applying power to the antenna 156 and electrode 178 in the chamber 106. To etch silicon oxide, the second etchant gas may include one or more of CF4, HBr, Cl2, and O2; and may be energized by applying an RF power level of about 750 Watts to the antenna 156 and a bias power level of about 70 Watts to the electrode 178.
The multiple etching processes conducted in the etching chamber 106 generate a variety of different types of etchant residues which deposit as successive layers on the internal surfaces 115 in the chamber 106. For example, in the first etching process, silicon-containing etchant residues such as SiOx, may be generated by the reaction of the tungsten silicide material on the substrates 104 with the energized etchant gas; and in the second etching process, carbon-containing etchant residues, such as polymeric CFx containing residues, may be formed by the decomposition of the carbon-containing CF4 etchant gas. The compositionally different residues deposit as successive layers on one another to form a multi-layer process residue on the chamber surfaces.
The different types of etchant residues formed in the different etching processes, may also form a complex distribution pattern of etchant residue dispersed about the chamber 106 depending upon the types of etching processes performed in the chamber. For example, certain etching processes result in the increased deposition of etchant residues in a process zone 108 of the chamber 106, in which a number of substrates 104 are etched, whereas other etching processes may generate increased residue deposition about an exhaust region of the chamber 106, such as a pumping channel 146 of the gas exhaust 144. Thus, the etching of multiple different substrates 104 in the chamber 106 may result in the non-uniform deposition of different types of etchant residues across the internal surfaces 115 in the chamber 106.
A cleaning process is performed to remove the multi-layer etchant residues generated in the multiple etching processes. The cleaning process may generally comprise introducing a cleaning gas into the chamber 106 and energizing the cleaning gas, either within the chamber 106 or in a remote energizing chamber 106, and selecting process parameters, such as cleaning gas composition, pressure and power levels, to uniformly clean a distribution of etchant residues in the chamber. The cleaning process is capable of cleaning the different types of etchant residues compositions which may be generated in the multiple etching processes at good cleaning rates and without excessive corrosion of the internal surfaces 115 in the chamber 106. The cleaning process may also be capable of cleaning the etchant residues deposited in different regions in the chamber 106, such as the process zone 108 or the gas exhaust 144, without undercleaning or overcleaning the regions. The cleaning process may also be performed to reduce contamination of subsequent substrates 104 processed in the chamber 106 and also to inhibit the corrosion of surfaces 115 in the chamber 106 by etchant residues.
In the cleaning process, a cleaning gas comprising O2 and CF4 are provided to clean the chamber. The oxygen containing gas is capable of cleaning carbon containing etchant residue, such as for example CFx, which may be generated by etching a substrate with a carbon containing gas such as CF4, by reacting with the residues to form volatile fluorine and COx species which may be exhausted from the chamber 106. The fluorine containing CF4 gas is capable of cleaning silicon containing etchant residue, such as for example SiOx by forming volatile residues comprising SiFx which are also exhausted from the chamber 106. The flow rate of the oxygen containing gas and the flow rate of the fluorine containing gas is regulated to provide a volumetric flow ratio of O2 to CF4 that is capable of providing uniform cleaning of the different types of etchant residues generated in multiple etching processes. The volumetric flow ratio of the oxygen containing gas to the fluorine containing gas is also selected such that different types of etchant residues are cleaned at good cleaning rates.
The cleaning ability of a cleaning gas comprising O2 and CF4 is demonstrated in
The gas pressure during the cleaning process may also be selected to further enhance cleaning of the different compositions of etchant residues formed in the multiple etching processes. Good cleaning rates were obtained for gas pressures in the range of from about 5 to about 40 mTorr, and even about 10 mTorr. The cleaning rates for etchant residues comprising SiOx within this range of pressures are shown in FIG. 4. In this Figure, the cleaning rate of two different distributions of SiOx containing etchant residues are shown for increasing gas pressure. In the first distribution, the etchant residues were deposited mostly on the surfaces in the process zone 108 which surrounds the energized etchant gas formed in the etching process, such as the surfaces of the ceiling 118 and sidewalls 114 in the chamber 106. In the second distribution, the etchant residues were formed about the exhaust region 145 of the chamber 106 which is further away from the process zone 108 and the energized etchant gas, such as on the surfaces of the pumping channel 146 and bottom wall 116. The cleaning rates of both the first and second distributions are about the same indicating that the residues are uniformly cleaned off from all the regions of the chamber 106. In particular, at a gas pressure of about 10 mTorr, substantially identical cleaning rates were provided for the first and second distributions and without overcleaning or undercleaning.
The chamber pressure during the cleaning process may also be selected to reduce the corrosion of the chamber surfaces 115 by the energized cleaning gas.
The cleaning gas is energized in the chamber 106 at levels that allow effective cleaning of the multiple layer etchant residues generated in the different etching processes. For example, the electrodes 178 may be operated by applying a relatively low bias power level of less than about 40 Watts, or even about 1 Watt, to provide good cleaning of the etchant residues.
The cleaning process may also be monitored to determine an endpoint of the cleaning process. The cleaning endpoint may be, for example, the time at which the chamber 106 has been substantially cleaned of etchant residue, or the time at which the chamber 106 has been sufficiently cleaned that subsequent substrates 104 may be processed in the chamber 106 without contamination. By determining the endpoint of the cleaning process, the chamber may be cleaned without undercleaning or overcleaning the chamber 106. For example, the cleaning process may be monitored by detecting an intensity of a wavelength of a radiation emission from the energized cleaning gas in the chamber 106. The intensity of the selected wavelength is related to the presence of detectable etchant residues in the chamber 106. For example, the intensity of the selected wavelength may be related to the presence of two or more types of etchant residues in the chamber 106, such as the presence of silicon or carbon containing etchant residue, such as for example SiOx and CFx, in the chamber 106. Etchant residues containing SiOx are detectable by observing the intensity of a 4405 Å wavelength of the radiation emissions from the chamber, whereas etchant residues containing CFx are detectable by observing the intensities of wavelengths in the range of 4000 to 6000 Å; thus, a suitable detection wavelength may be at 4405 Å. The cleaning process may be monitored by detecting the intensity of this wavelength to determine when both the SiOx and CFx containing residues have been cleaned.
The intensity of the selected wavelength of the radiation emission from the energized gas may be monitored to determine the endpoint of cleaning of different types of distributions of the etchant residues across different regions of the chamber 106.
To determine the accuracy of the graphically determined cleaning endpoint time, the endpoint time was also measured by monitoring the weight loss registered by a quartz crystal microbalance positioned in the chamber 106.
Because different types of etching processes are performed in the chamber 106 in the foundry etching processes, it is not always known whether etchant residues have actually been formed on the chamber surfaces. Running a cleaning process in a chamber which does not have an etchant residues would result in erosion of the chamber walls (which are typically aluminum) by the cleaning gas to form erosion byproducts, such as AlFx. To ensure that the chamber surfaces are at least partially coated with etchant residues to prevent such erosion, the chamber 106 may be treated by depositing a sacrificial coating on the internal surfaces in the chamber 106, before any production substrate etching or cleaning process is performed. The sacrificial coating reduces erosion of surfaces 115 in the chamber 106 in the event that etchant residues have not formed on the chamber surfaces, by providing a sacrificial coating that may be removed by the cleaning gas. In this process, a sacrificial substrate 104 is processed in the chamber 106, for example by etching the substrate, to deposit a sacrificial coating on the internal surfaces 115 in the chamber 106. The sacrificial coating ensures that some material is present on the chamber surfaces when the cleaning gas is used to clean the chamber 106. The treatment substrate 104 may comprise materials such as silicon containing materials, for example, a bare silicon wafer. The silicon wafer may be processed by an etchant gas comprising 70 sccm Cl2, 110 sccm HBr, and 5 to 10 sccm O2 to etch the silicon and deposit sacrificial SiOx residues on the chamber surfaces. The etchant gases may be maintained at a pressure of from about 3 to about 10 mTorr in the chamber 106 while the etchant gas is energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156 and 80 to 150 Watts to the electrode 178.
The multiple etching and cleaning processes may be performed in the chamber 106 illustrated in
The data signals received by and/or evaluated by the controller 300 may be sent to a factory automation host computer 338. The factory automation host computer 338 may comprise a host software program 340 that evaluates data from several systems, platforms or chambers 106, and for batches of substrates 104 or over an extended period of time, to identify statistical process control parameters of (i) the processes conducted on the substrates 104, (ii) a property that may vary in a statistical relationship across a single substrate 104, or (iii) a property that may vary in a statistical relationship across a batch of substrates 104. The host software program 340 may also use the data for ongoing in-situ process evaluations or for the control of other process parameters. A suitable host software program comprises a WORKSTREAM™ software program available from aforementioned Applied Materials. The factory automation host computer 338 may be further adapted to provide instruction signals to (i) remove particular substrates 104 from the processing sequence, for example, if a substrate property is inadequate or does not fall within a statistically determined range of values, or if a process parameter deviates from an acceptable range; (ii) end processing in a particular chamber 106, or (iii) adjust process conditions upon a determination of an unsuitable property of the substrate 104 or process parameter. The factory automation host computer 338 may also provide the instruction signal at the beginning or end of processing of the substrate 104 in response to evaluation of the data by the host software program 340.
In one version the controller 300 comprises a computer-readable program 320 may be stored in the memory 308, for example on the non-removable storage media 312 or on the removable storage media 310. The computer readable program 320 generally comprises process control software comprising program code to operate the chamber 106 and its components, process monitoring software to monitor the processes being performed in the chamber 106, safety systems software, and other control software, as for example, illustrated in FIG. 9. The computer-readable program 320 may be written in any conventional computer-readable programming language, such as for example, assembly language, C++, Pascal, or Fortran. Suitable program code is entered into a single file, or multiple files, using a conventional text editor and stored or embodied in computer-usable medium of the memory 308. If the entered code text is in a high level language, the code is compiled, and the resultant compiler code is then linked with an object code of precompiled library routines. To execute the linked, compiled object code, the user invokes the object code, causing the CPU 306 to read and execute the code to perform the tasks identified in the program.
An illustrative block diagram of a hierarchical control structure of a specific embodiment of a computer readable program 320 according to the present invention is also shown in FIG. 9. Using a light pen interface, a user enters a process set and chamber number into the computer readable program 320 in response to menus or screens displayed on the CRT terminal. The computer readable program includes process selector program code 321 to control the substrate position, gas flow, gas pressure, temperature, RF power levels, and other parameters of a particular process, as well as code to monitor the chamber process. The process sets are predetermined groups of process parameters necessary to carry out specified processes. The process parameters are process conditions, including without limitations, gas composition, gas flow rates, temperature, pressure, gas energizer settings such as RF or microwave power levels, magnetic field generation, heat transfer gas pressure, and wall temperature.
The process sequencer instruction set 322 comprises program code to accept a chamber type and set of process parameters from the process selector 321 and to control its operation. The sequencer program 322 initiates execution of the process set by passing the particular process parameters to a chamber manager instruction set 324 that controls multiple processing tasks in the process chamber 106. Typically, the process chamber instruction set 324 includes a substrate positioning instruction set 326, a gas flow control instruction set 328, a gas pressure control instruction set 330, a temperature control instruction set 332, a gas energizer control instruction set 334, and a process monitoring instruction set 336. Typically, the substrate positioning instruction set 326 comprises program code for controlling chamber components that are used to load the substrate 104 onto the support 110 and optionally, to lift the substrate 104 to a desired height in the chamber 106. The gas flow control instruction set 328 comprises program code for controlling the flow rates of different constituents of the process gas. The gas flow control instruction set 328 regulates the opening size of the gas flow control valves 134 to obtain the desired gas flow rate into the chamber 106. The gas pressure control instruction set 330 comprises program code for controlling the pressure in the chamber 106 by regulating open/close position of the throttle valve 150. The temperature control instruction set 332 comprises program code to control temperatures in the chamber 106, such as for example the temperature of a wall 107 in the chamber 106 or the temperature of the substrate 104. The gas energizer control instruction set 334 comprises program code for setting, for example, the RF power level applied to the antenna 156 by the antenna power supply 155.
The process monitoring instruction set 336 may comprise code for monitoring a process in the chamber 106 and determining a process endpoint. For example, the process monitoring instruction set 336 may comprise program code to monitor a cleaning process in the chamber 106 and determining a cleaning endpoint. In one version, the process monitoring instruction set 334 may monitor a cleaning process by receiving a signal from the detector 200 which is related to the intensity of a wavelength of the radiation emitted by the energized cleaning gas in the chamber 106. The signal may be processed to determine the intensity of the signal as a function of time. When the signal intensity reaches a pre-determined value, such as for example a constant value, for a pre-determined length of time, the process monitoring instruction set 334 may give a signal to halt the cleaning process.
In one version, the chamber manager instruction set 324 may set process conditions in the chamber 106 to etch a plurality of batches of substrates 104. For example, the substrate positioning instruction set 326 may position a first substrate 104 to be etched in the chamber 106 and the gas flow instruction set 328 may regulate the flow of etchant gases into the chamber 106 while the gas energizer sets the RF power levels for energizing the etchant. gas. The etching process may also be performed on multiple substrates 104 having different materials with etching process conditions selected by the chamber manager instruction set to etching the different substrates. In one version, the chamber manager instruction set 324 comprises program code to set etching process conditions to etch one or more first substrates 104 comprising a first material, such as for example polysilicon, and thereafter, the chamber manager instruction set 324 comprises program code to etch one or more second substrates 104 comprising a second material, such as for example, silicon oxide.
The chamber manager instruction set 324 may also set process conditions in the chamber to clean the chamber 106 after etching the different substrates 104. For example, the gas flow instruction set 328 may regulate the flow of cleaning gases into the chamber 106, for example by setting a volumetric flow ratio of gases in the cleaning gas, while the gas energizer control instruction set 334 sets the RF power levels for energizing the cleaning gas. The process conditions may be set to clean a number of different types of etchant residue, such as for example silicon containing etchant residues and carbon containing etchant residue, in different distributions in the chamber 106. For example, the gas flow instruction set 328 may include program code to set a volumetric flow ratio of an oxygen containing gas to a fluorocarbon gas of from about 1:1 to about 1:40 to provide good cleaning rates of different types of etchant residues in the chamber 106.
The data signals received by and/or evaluated by the controller 300 may also be sent to a factory automation host computer 338. The factory automation host computer 338 may comprise a host software program 340 that evaluates data from several systems, platforms or chambers 106, and for batches of substrates 104 or over an extended period of time, to identify statistical process control parameters of (i) the processes conducted on the substrates 104, (ii) a property that may vary in a statistical relationship across a single substrate 104, or (iii) a property that may vary in a statistical relationship across a batch of substrates 104. The host software program 340 may also use the data for ongoing in-situ process evaluations or for the control of other process parameters. A suitable host software program comprises a WORKSTREAM™ software program available from aforementioned Applied Materials. The factory automation host computer 338 may be further adapted to provide instruction signals to (i) remove particular substrates 104 from the processing sequence, for example, if a substrate property is inadequate or does not fall within a statistically determined range of values, or if a process parameter deviates from an acceptable range; (ii) end processing in a particular chamber 106, or (iii) adjust process conditions upon a determination of an unsuitable property of the substrate 104 or process parameter. The factory automation host computer 338 may also provide the instruction signal at the beginning or end of processing of the substrate 104 in response to evaluation of the data by the host software program 340.
The following examples demonstrate chamber cleaning and substrate etching processes according to the present invention. In these examples, batches of substrates were etched in a DPS chamber 106 commercially available from Applied Materials having a process volume of about 35 liters, and which is generally described above.
In this example, a first etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising a polysilicon layer formed over a silicon oxide layer. The multiple stage etching process was performed to etch the polysilicon layer. The first etching process comprised a main etch stage in which a first etchant gas comprising 70 sccm Cl2, 110 sccm HBr, and 5 to 10 sccm O2, was introduced into the chamber 106; the gas pressure was maintained at 3 to 10 mTorr; and the gas energized by applying an RF power level of 600 to 1000 Watts to the antenna 156 and 40 to 120 Watts to the electrode 178. Thereafter, an overetch stage was performed using an etchant gas comprising 100 sccm HBr and 2 to 5 sccm O2; the pressure of the gases in the chamber 106 was maintained at within 30 to 80 mTorr; and the gas was energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156, and 80 to 150 Watts to the electrode 178.
Following the first etching process, a second etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising a polysilicon layer formed over a silicon oxide layer. The multiple stage etching process was performed to etch the polysilicon layer. The second etching process comprised a main etch stage in which a second etchant gas comprising 25 sccm CF4, 110 sccm HBr, 40 sccm Cl2, and 2 sccm O2, was introduced into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 750 Watts to the antenna 156 and 70 Watts to the electrode 178. Thereafter, an overetch stage was performed using an etchant gas comprising 100 sccm HBr and 2 to 5 sccm O2; the pressure of the gases in the chamber 106 was maintained at within 30 to 80 mTorr; and the gas was energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156, and 80 to 150 Watts to the electrode 178.
Upon completion of the first and second etching process, a cleaning process was performed to clean the chamber 106 of the different types of residues generated in the processes. In the cleaning process, a cleaning gas comprising O2 and CF4 was introduced into the chamber 106. The O2 gas was introduced at a volumetric flow rate equivalent to 20 sccm and the CF4 gas was introduced at a volumetric flow rate equivalent to 100 sccm for a chamber 106 having a process volume of 35 liters, or in other words, in a volumetric flow ratio of O2 to CF4 of 1:5. The gas pressure in the chamber 106 was maintained at 10 mTorr. The cleaning gas was energized by applying an RF power level of 600 Watts to the antenna 156 and a bias power level of 1 Watt to the electrode 178. The intensity of the radiation emission of the energized cleaning gas was monitored at 4405 Å to determine the cleaning process endpoint. The cleaning process provided substantially uniform cleaning of the multiple types of etchant residues, such as carbon and silicon containing etchant residue, generated by the first and second etching process. Thus, this example demonstrates that an energized cleaning gas comprising O2 and CF4 in a volumetric flow ratio of 1:5 may be used to clean the multiple types of etch residue generated in different etching processes.
In this example, a first etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising silicon. The process was performed to etch shallow trenches on the silicon substrates 104. The first etching process comprised introducing a first etchant gas comprising 100 sccm Cl2, 5 sccm O2 and 7 sccm N2 into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 1200 Watts to the antenna 156 and 120 Watts to the electrode 178.
Following the first etching process, a second etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising polysilicon. The multiple stage etching process was performed to etch the polysilicon material, which formed a layer over a silicon oxide layer. The second etching process comprised a main etch stage in which a second etchant gas comprising 25 sccm CF4, 110 sccm HBr, 40 sccm Cl2, and 2 sccm O2, was introduced into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 750 Watts to the antenna 156, and 70 Watts to the electrode 178. Thereafter, an overetch stage was performed using an etchant gas comprising 100 sccm HBr and 2 to 5 sccm O2; the pressure of the gases in the chamber 106 was maintained at within 30 to 80 mTorr; and the gas was energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156, and 80 to 150 Watts to the electrode 178.
Upon completion of the first and second etching process, a cleaning process was performed to clean the chamber 106 of the different types of residues generated in the processes. In the cleaning process, a cleaning gas comprising O2 and CF4 was introduced into the chamber 106. The O2 gas was introduced at a volumetric flow rate equivalent to 20 sccm and the CF4 gas was introduced at a volumetric flow rate equivalent to 100 sccm for a chamber 106 having a process volume of 35 liters, or in other words, in a volumetric flow ratio of O2 to CF4 of 1:5. The gas pressure in the chamber 106 was maintained at 10 mTorr. The cleaning gas was energized by applying an RF power level of 600 Watts to the antenna 156 and a bias power level of 1 Watt to the electrode 178. The intensity of the radiation emission of the energized cleaning gas was monitored at 4405 Å to determine the cleaning process endpoint. The cleaning process provided substantially uniform cleaning of the multiple types of etchant residues, such as carbon and silicon containing etchant residue, generated by the first and second etching process. Thus, this example demonstrates that an energized cleaning gas comprising O2 and CF4 in a volumetric flow ratio of 1:5 may be used to clean the multiple types of etch residue generated in different etching processes.
In this example, a first etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising a first material comprising tungsten silicide. The multiple stage etch process was performed to etch the tungsten silicide material. The first etching process comprised a main etching stage in which a first etchant gas comprising 100 sccm Cl2, 5 sccm O2 and 7 sccm N2 was introduced into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 1200 Watts to the antenna 156 and 120 Watts to the electrode 178. Thereafter, an overetch stage was performed using an etchant gas comprising 100 sccm HBr and 2 to 5 sccm O2; the pressure of the gases in the chamber 106 was maintained at within 30 to 80 mTorr; and the gas was energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156 and 80 to 150 Watts to the electrode 178.
Following the first etching process, a second etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising a second material comprising silicon. The second etching process was performed to etch shallow trenches in the silicon material. The second etching process comprised introducing a second etchant gas comprising 100 sccm Cl2, 5 sccm O2 and 7 sccm N2 into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 1200 Watts to the antenna 156 and 120 Watts to the electrode 178.
Upon completion of the first and second etching process, a cleaning process was performed to clean the chamber 106 of the different types of residues generated in the processes. In the cleaning process, a cleaning gas comprising O2 and CF4 was introduced into the chamber 106. The O2 gas was introduced at a volumetric flow rate equivalent to 20 sccm and the CF4 gas was introduced at a volumetric flow rate equivalent to 100 sccm for a chamber 106 having a process volume of 35 liters, or in other words, in a volumetric flow ratio of O2 to CF4 of 1:5. The gas pressure in the chamber 106 was maintained at 10 mTorr. The cleaning gas was energized by applying an RF power level of 600 Watts to the antenna 156 and a bias power level of 1 Watt to the electrode 178. The intensity of the radiation emission of the energized cleaning gas was monitored at 4405 Å to determine the cleaning process endpoint. The cleaning process provided substantially uniform cleaning of the multiple types of etchant residues generated by the first and second etching process. Thus, this example demonstrates that an energized cleaning gas comprising O2 and CF4 in a volumetric flow ratio of 1:5 may be used to clean the multiple types of etch residue generated in different etching processes.
In this example, a first etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising a first material comprising tungsten silicide. The multiple stage etch process was performed to etch the tungsten silicide material. The first etching process comprised a main etching stage in which a first etchant gas comprising 100 sccm Cl2, 5 sccm O2 and 7 sccm N2 was introduced into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 1200 Watts to the antenna 156 and 120 Watts to the electrode 178. Thereafter, an overetch stage was performed using an etchant gas comprising 100 sccm HBr and 2 to 5 sccm O2; the pressure of the gases in the chamber 106 was maintained at within 30 to 80 mTorr; and the gas was energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156 and 80 to 150 Watts to the electrode 178.
Following the first etching process, a second etching process was performed in the chamber 106 on a batch of twenty five substrates 104 comprising second material comprising polysilicon. The multiple stage etching process was performed to etch the polysilicon material, which formed a layer over a layer of silicon oxide. The second etching process comprised a main etch stage in which a second etchant gas comprising 25 sccm CF4, 110 sccm HBr, 40 sccm Cl2, and 2 sccm O2 was introduced into the chamber 106; the gas pressure was maintained at 4 mTorr; and the gas energized by applying an RF power level of 750 Watts to the antenna 156 and 70 Watts to the electrode 178. Thereafter, an overetch stage was performed using an etchant gas comprising 100 sccm HBr and 2 to 5 sccm O2; the pressure of the gases in the chamber 106 was maintained at within 30 to 80 mTorr; and the gas was energized by applying an RF power level of 1000 to 1500 Watts to the antenna 156 and 80 to 150 Watts to the electrode 178.
Upon completion of the first and second etching process, a cleaning process was performed to clean the chamber 106 of the different types of residues generated in the processes. In the cleaning process, a cleaning gas comprising O2 and CF4 was introduced into the chamber 106. The O2 gas was introduced at a volumetric flow rate equivalent to 20 sccm and the CF4 gas was introduced at a volumetric flow rate equivalent to 100 sccm for a chamber 106 having a process volume of 35 liters, or in other words, in a volumetric flow ratio of O2 to CF4 of 1:5. The gas pressure in the chamber 106 was maintained at 10 mTorr. The cleaning gas was energized by applying an RF power level of 600 Watts to the antenna 156 and a bias power level of 1 Watt to the electrode 178. The intensity of the radiation emission of the energized cleaning gas was monitored at 4405 Å to determine the cleaning process endpoint. The cleaning process provided substantially uniform cleaning of the multiple types of etchant residues, such as carbon and silicon containing residues generated by the first and second etching process. Thus, this example demonstrates that an energized cleaning gas comprising O2 and CF4 in a volumetric flow ratio of 1:5 may be used to clean the multiple types of etch residue generated in different etching processes.
Although exemplary embodiments of the present invention are shown and described, those of ordinary skill in the art may devise other embodiments which incorporate the present invention, and which are also within the scope of the present invention. For example, other substrate etching processes may be performed without deviating from the scope of the present invention. Also, cleaning gas compositions other than those specifically mentioned may be used, as would be apparent to those of ordinary skill in the art. Furthermore, the terms below, above, bottom, top, up, down, first and second and other relative or positional terms are shown with respect to the exemplary embodiments in the figures and are interchangeable. Therefore, the appended claims should not be limited to the descriptions of the preferred versions, materials, or spatial arrangements described herein to illustrate the invention.
Number | Name | Date | Kind |
---|---|---|---|
4282267 | Kuyel | Aug 1981 | A |
4433228 | Nishimatsu et al. | Feb 1984 | A |
4465532 | Fukano | Aug 1984 | A |
4490209 | Hartman | Dec 1984 | A |
4502914 | Trumpp et al. | Mar 1985 | A |
4529474 | Fujiyama et al. | Jul 1985 | A |
4705595 | Okudaira et al. | Nov 1987 | A |
4738748 | Kisa | Apr 1988 | A |
4786352 | Benzing | Nov 1988 | A |
4818326 | Liu et al. | Apr 1989 | A |
4820377 | Davis et al. | Apr 1989 | A |
RE32928 | Jacob | May 1989 | E |
4831963 | Saito et al. | May 1989 | A |
4863561 | Freeman et al. | Sep 1989 | A |
4867841 | Loewenstein et al. | Sep 1989 | A |
4876212 | Koury | Oct 1989 | A |
4975144 | Yamazaki et al. | Dec 1990 | A |
4992136 | Tachi et al. | Feb 1991 | A |
5002632 | Loewenstein et al. | Mar 1991 | A |
5013398 | Long et al. | May 1991 | A |
5035768 | Mu et al. | Jul 1991 | A |
5084126 | McKee | Jan 1992 | A |
5094712 | Becker et al. | Mar 1992 | A |
5110408 | Fujii et al. | May 1992 | A |
5110411 | Long et al. | May 1992 | A |
5118387 | Kadomura | Jun 1992 | A |
5158644 | Cheung et al. | Oct 1992 | A |
5160407 | Latchford et al. | Nov 1992 | A |
5164330 | Davis et al. | Nov 1992 | A |
5176792 | Fullowan et al. | Jan 1993 | A |
5188980 | Lai | Feb 1993 | A |
5192702 | Tseng | Mar 1993 | A |
5256245 | Keller et al. | Oct 1993 | A |
5281302 | Gabric et al. | Jan 1994 | A |
5282899 | Balmashov et al. | Feb 1994 | A |
5312519 | Sakai et al. | May 1994 | A |
5318668 | Tamaki et al. | Jun 1994 | A |
5338398 | Szwejkowski et al. | Aug 1994 | A |
5354417 | Cheung et al. | Oct 1994 | A |
5356478 | Chen et al. | Oct 1994 | A |
5378311 | Nagayama et al. | Jan 1995 | A |
5382316 | Hills et al. | Jan 1995 | A |
5401356 | Enami et al. | Mar 1995 | A |
5413954 | Aydil et al. | May 1995 | A |
5417826 | Blalock | May 1995 | A |
5443686 | Jones et al. | Aug 1995 | A |
5449411 | Fukuda et al. | Sep 1995 | A |
5514622 | Bornstein et al. | May 1996 | A |
5521119 | Chen et al. | May 1996 | A |
5620615 | Keller | Apr 1997 | A |
5644153 | Keller | Jul 1997 | A |
5647953 | Williams et al. | Jul 1997 | A |
5700741 | Liao | Dec 1997 | A |
5753533 | Saito | May 1998 | A |
5756400 | Ye et al. | May 1998 | A |
5767021 | Imai et al. | Jun 1998 | A |
5788778 | Shang et al. | Aug 1998 | A |
5788799 | Steger et al. | Aug 1998 | A |
5817578 | Ogawa | Oct 1998 | A |
5843239 | Shrotiya | Dec 1998 | A |
5846373 | Pirkle et al. | Dec 1998 | A |
5866483 | Shiau et al. | Feb 1999 | A |
5869401 | Brunemeier et al. | Feb 1999 | A |
5874363 | Hoh et al. | Feb 1999 | A |
5879575 | Tepman et al. | Mar 1999 | A |
5882424 | Taylor et al. | Mar 1999 | A |
5897740 | Tamura | Apr 1999 | A |
6068729 | Shrotriya | May 2000 | A |
6070552 | Mizuno et al. | Jun 2000 | A |
6071375 | Chen et al. | Jun 2000 | A |
6079426 | Subrahmanyam et al. | Jun 2000 | A |
6090718 | Soga et al. | Jul 2000 | A |
6108929 | Kato et al. | Aug 2000 | A |
6124927 | Zhong et al. | Sep 2000 | A |
6132577 | Smith et al. | Oct 2000 | A |
6281116 | Yanagida | Aug 2001 | B1 |
6283130 | Tamura | Sep 2001 | B1 |
Number | Date | Country |
---|---|---|
4132559 | Apr 1993 | DE |
0272143 | Jun 1988 | EP |
0314990 | May 1989 | EP |
0463373 | Jan 1992 | EP |
0516043 | Dec 1992 | EP |
0555546 | Aug 1993 | EP |
697467 | Feb 1996 | EP |
0697467 | Feb 1996 | EP |
0709877 | May 1996 | EP |
0746015 | Jan 1998 | EP |
4056770 | Feb 1982 | JP |
59142839 | Aug 1984 | JP |
60059739 | Apr 1985 | JP |
63005532 | Jan 1988 | JP |
6303578 | Feb 1988 | JP |
63089684 | Apr 1988 | JP |
1064326 | Mar 1989 | JP |
6025859 | Feb 1994 | JP |
6177092 | Jun 1994 | JP |
7029879 | Jan 1995 | JP |
6240728 | Feb 1997 | JP |
9036085 | Feb 1997 | JP |
9129596 | May 1997 | JP |
9249975 | Sep 1997 | JP |
1054274 | Feb 1998 | JP |
1023387 | Sep 1998 | JP |
11345802 | Dec 1999 | JP |
9615545 | May 1996 | WO |
9906610 | Feb 1999 | WO |
9920812 | Apr 1999 | WO |
0108209 | Feb 2001 | WO |
0188966 | Nov 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20020117472 A1 | Aug 2002 | US |