Conductive implant structure in a dielectric

Abstract
The present invention is directed toward the formation of implanted thermally and electrically conductive structures in a dielectric. An electrically conductive structure, such as an interconnect, is formed through ion implantation into several levels within a dielectric layer to penetrate into an electrically conductive region beneath the dielectric layer, such as a semiconductor substrate. Ion implantation continues in discreet, overlapping implantations of the ions from the electrical conductive region up to the top of the dielectric layer so as to form a continuous interconnect. Structural qualities achieved by the method of the present invention include a low interconnect-conductive region resistivity and a low thermal-cycle stress between the interconnect and the dielectric layer in which the interconnect has been implanted. Implantation elements are selected in connection with dielectric materials so that heat treatment will cause continuous metallic structures to form within the interconnect implantation area. In an alternative embodiment, implantation dosages and depths are selected to form a thermally conductive structure that is entirely insulated within the dielectric layer and that function as a conduit to heat-sink structures.
Description




BACKGROUND OF THE INVENTION




1. The Field of the Invention




The present invention comprises a conductor forming process in which ion implantation forms an electrically conductive interconnect within a dielectric layer. The inventive conduct forming process also uses implantation to form a thermally conductive structure that is insulated by and contained within the dielectric layer.




2. The Relevant Technology




In the microelectronics industry, a substrate refers to one or more semiconductor layers or structures which includes active or operable portions of semiconductor devices. A substrate assembly refers to a substrate with one or more layers or structures formed thereon. For example, a substrate assembly in the present disclosure can refer to a substrate with interconnects that connect to active areas within the substrate. The interconnects can be within an insulative layer upon the substrate assembly. A semiconductor device can refer to a substrate assembly upon which at least one microelectronic device has been or is being fabricated. The semiconductor device can also refer to a semiconductor substrate assembly having formed thereon elements such as transistors. Interconnection layers are formed on the semiconductor substrate assembly for electrically connecting such elements.




The semiconductor industry has, since the development of the integrated circuit, used a process that required the etching of a hole or via in a dielectric layer and the subsequent filling of the hole with a conductive material to make a connection between one conductive layer and another. The connection was formed of such materials as polysilicon, high melting-point metals, high melting-point metal silicides, aluminum, and aluminum alloys. The ever-increasing pressure to miniaturize and to increase semiconductor device speed has required that both interconnect size and interconnect resistance be reduced. Therefore, semiconductor integrated circuit devices require interconnect structures of smaller lateral dimensions, and require materials that have smaller resistivities. A reliability problem in conventional etched via structures is over etching the via and undercutting a structure with which contact is to be made.




Because hole filling following an etch is problematic, interconnect hole filling seldom achieves a complete connection between the interconnect interface and the electrically conductive region beneath the interconnect. Attempts have been made to create interconnects by forming an interconnect first, followed by forming a dielectric layer, for example, by filling the regions between interconnects with a gelatinous material and curing the material into a solid dielectric. Thus, hole filling is avoided, however, there remains a discrete interface between the interconnect and the electrically conductive region that the interconnect contacts.




Additionally, as semiconductor device dimensions continue to shrink in size the problem of heat management continues to increase in complexity. As heat management requirements continue to increase, methods of removing heat from the semiconductor device without increasing the vertical or lateral geometries of the devices are constantly being sought.




What is needed is a method of forming an interconnect without the prior art via etching and via hole-filling process. What is also needed is a method of forming an interconnect wherein the interconnect minimizes interface discontinuities between the electrically-conductive region beneath the interconnect and the interconnect itself. What is also needed is a method of forming an interconnect that resists thermal cycle stresses at the interface with the dielectric material and with the electrically conductive region beneath the interconnect. What is also needed is a method of forming heat management structures within semiconductor devices without increasing the vertical or lateral geometries of the devices.




SUMMARY OF THE INVENTION




The present invention is directed toward the formation of an interconnect that is not within an etched via. Interconnect formation is accomplished through ion implantation into several levels within a dielectric layer. Ion implantation penetrates into an electrically conductive region beneath the dielectric layer and continues in discreet, overlapping implantations up to the top of the dielectric layer, thus forming a continuous interconnect.




Structural qualities achieved by the method of the present invention include a low resistivity between the interconnect and the conductive region. There is also a low thermal-cycle stress between the interconnect and the dielectric layer in which the interconnect has been implanted, and between the interconnect and the electrically conductive region beneath the interconnect.




Implantation elements may be selected in connection with dielectric materials so that heat treatment will cause continuous metallic structures to form within the interconnect implantation area by dissociation of metallic elements from the dielectric material and the combination of these dissociated elements with the implanted metal ions.




The present invention is also directed toward the implantation of ion dosages and depths that are selected so as to form heat-management structures that are entirely insulated within the dielectric layer. Heat-management structures of the present invention have coefficients of thermal conductivity that are greater than the coefficients of thermal conductivity of the preferred dielectric materials. Implantation can also simultaneously form semiconductor active areas with interconnect formation by the implantation methods of the present invention.




These and other features of the present invention will become more fully apparent from the following description and appended claims, or may be learned by the practice of the invention as set forth hereinafter.











BRIEF DESCRIPTION OF THE DRAWINGS




In order that the manner in which the above-recited and other advantages of the invention are obtained, a more particular description of the invention briefly described above will be rendered by reference to specific embodiments thereof which are illustrated in the appended drawings. Understanding that these drawings depict only typical embodiments of the invention and are not therefore to be considered to be limiting of its scope, the invention will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:





FIG. 1

is a cross-sectional elevation view illustrating a region of a semiconductor device into which conductive structures of the present invention are to be implanted.





FIGS. 2

,


3


, and


4


are cross-sectional elevation views illustrating progressive process steps of forming the implanted conductive structures of the present invention.





FIG. 5

is a cross-sectional elevation view taken along the


5





5


section line in

FIG. 4

, and illustrates the result of ion-implantation wherein ions have been implanted within a dielectric layer with a portion of the implanted ions overlapping into an underlying substrate.





FIG. 6

is a cross-sectional elevation view taken along the


6





6


section line in

FIG. 4

, and illustrates ions having been implanted within the dielectric layer to contact an active area in the underlying substrate.





FIG. 7

is a cross-sectional elevation view taken along the


5





5


section line in

FIG. 4

, and illustrates ions having been implanted wholly within the dielectric layer.





FIG. 8

is a cross-sectional elevation view illustrating embodiments of the conductive structures of the present invention which are seen

FIGS. 5-7

.





FIG. 9

shows top, cross-sectional, and bottom views of metallization lines upon a dielectric layer having therein implanted thermal conductors for thermally conducting heat away from the metallization lines according to the present invention.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS




The present invention is directed toward methods of forming an implanted interconnect and a structure for conducting thermal energy away from semiconductor devices. Disclosed is a method that does not require etching of a dielectric layer in the region that normally is removed in order to form a via, which is then filled with a conductive material to form the interconnect. Rather, the present method uses a succession of ion implants to produce an electrically or thermally conductive structure in sections of a dielectric layer where desired. The present invention is applicable to integrated semiconductor circuits, as well as in other applications where a connection is needed between two structures which will be separated by a dielectric layer.





FIG. 1

illustrates a first embodiment of the present invention in which a semiconductor device


10


comprising a substrate


12


has a dielectric layer


14


disposed upon an upper surface


16


. Preferred materials for dielectric material


14


include commercial polyimides.




Examples of polyimides include pyromellitic dianhydride (PMDA) and oxydianiline (ODA, also named 4,4′-diaminodiphenyl ether). Other preferred polymers for use pursuant to the present invention are the polymers of benzophenonetetracarboxylic dianhydride (BTDA) and ODA and/or 1,3-phenylenediamine and the polymer of 3,3′-biphenylenetetracarboxylic acid (BPDA) and 1,4-phenylenediamine (PDA). Polyimide films based on PMDA-ODA are available from Allied Corporation under the tradename Apical® and from Du Pont under the tradename Kapton®. Films based on BPDA-PDA are available from Ube Corporation as Upilexg® and from Hitachi Chemical Company as PIQ-L 100. Other tradename polyimides useful pursuant to the present invention include Durimid® from Rogers Corporation and the Du Pont Pyralin® series, including PI-2525 and PI-2566. In combination, preferred dielectric polymers include BPDA-PDA, BPDA-ODA, BTDA-ODA, BTDA-PDA, PMDA-PDA, and PMDA-ODA.




Other perferred dielectrics include, borophosphosilicate glass (BPSG), borosilicate glass (BSG), phosphosilicate glass (PSG), silica, thoria. ceria, zirconia, and organometallic compounds.




First, second, and third mask layers


18


,


20


,


22


are disposed upon dielectric layer


14


. An electrically conductive region


24


may be imbedded in upper surface


16


of substrate


12


, or electrically conductive region


24


may be formed by the methods of the present invention. Region


24


can be a conductive line such as metallization formed of polysilicon, or it can be an active region substantially composed of doped silicon.





FIGS. 2

,


3


, and


4


progressively illustrate an example of the method of the present invention of etching through first, second, and third mask layers


18


,


20


,


22


, and the ion implanting of electrically conductive material therethrough to form interconnects. In

FIG. 2

an etch has been conducted in which etch holes


26


are formed in third mask layer


22


. In

FIG. 3

an etch continues to form etch holes


26


in second mask layer


20


. In

FIG. 4

an etch has formed an etch hole in first mask


18


layer.




Ion implantation is illustrated in

FIG. 4

with downwardly vertical arrows. Ions implant within etch holes


26


into dielectric layer


14


. Etch holes


26


may be, but need not be, above an electrically conductive region


24


within substrate


12


. The step of ion implantation may serve as both a doping step in forming an electrically conductive region in substrate


12


, and as an interconnect-forming implantation step of the present invention. In this simultaneous doping and interconnect-forming method alternative, an extra process step is avoided for active region doping. The advantage of the method is that it forms an electrically conductive region


24


, a doped active area in this example, that is inherently aligned with the implanted interconnect.





FIG. 5

illustrates the result of ion-implantation within the section-line


5





5


in FIG.


4


. In

FIG. 5

an implanted interconnect


30


is illustrated wherein ions have been implanted within dielectric layer


14


. A portion of implanted interconnect


30


overlaps into substrate


12


. The overlap portion is implanted to overlap depth


32


that minimizes the electrical resistance interface and the thermal stress interface between interconnect


30


and electrically conductive region


24


if it is present. Preferably, implanted interconnect


30


will have a length in a range from about 1,000 Å to about 30,000Å.




Formation of an active area simultaneously with formation of an interconnect makes the active area and the interconnect self-aligned. If substrate


12


is not doped, doping of substrate


12


can occur simultaneously with forming an interconnect in the region within and below etch hole


26


. For example if substrate


12


is monocrystalline silicon, n-doping or p-doping can be performed by implanting selected ions. The ions that are implanted within substrate


12


will make that portion of substrate


12


into electrically conductive region


24


. For example, aluminum ions produce n-doping in a monocrystalline silicon substrate, and subsequent aluminum ion implantation, or another selected metal ion, will form implanted interconnect


30


.




Although substrate


12


is usually made of monocrystalline silicon, other substrates can be provided and doped simultaneously with formation of implanted interconnect


30


. By way of example, semiconductors are fabricated from compounds made by a combination of elements from periodic table groups IA-VIIA, IIA-VIA, and IIIA-VA, as well as IA-IIIA-VI


2


A, and IIA-IVA-V


2


.




Implanted overlap depth


32


expands laterally upon heat treatment of device


10


to form, for example, an active area in a transistor source-drain structure.




Dielectric layer


14


can be selected to be an organometallic dielectric or equivalent that releases metal elements in favor of bonding with oxygens or nitrogens and equivalents. Treatment is carried out in an oxygen or nitrogen atmosphere following implantation. Implantation of metal ions to form implanted interconnect


30


or an implanted thermal conductor will, either spontaneously or with heat treatment, cause the metals in the organometallic dielectric to combine with the implanted metal ions to form a substantially coherent and continuous metal interconnect.




Combination of the metals in the organometallic and the implanted species accomplishes more metallization in the implanted interconnect


30


or in an implanted thermal conductor than simple implantation alone achieves. Combination also renders the organometallic dielectric that remains more resistant to electrical conductivity than regions not implanted with metal ions.




An alternative to an organometallic dielectric that releases its metal element in favor of oxides or nitrides, is an organometallic that releases its metal element by catalysis caused by the presence of the implanted metal species. By this optional method, the regions of dielectric not implanted by the metal ions, do not become conductive at the temperatures at which the catalytic reaction occurs.





FIG. 6

illustrates electrically conductive region


24


that is imbedded within substrate


12


. Ion implantation into dielectric layer


14


is illustrated as implanted interconnect


30


, extending to implanted overlap depth


32


. Overlap depth


32


can be optimized so as to minimize the electrical resistance interface and the thermal stress interface between interconnect


30


and electrically conductive region


24


. Implanted overlap depth


32


and implanted interconnect


30


form a substantially continuous electrically conductive interface between substrate


12


and implanted interconnect


30


. The advantage of a substantially continuous electrical interface between an interconnect and an electrically conductive region is that both resistivity and thermal stresses are ameliorated for field use of the semiconductor device.





FIG. 7

illustrates ion-implantation resulting in an implanted thermal conductor


36


that is formed entirely within dielectric layer


14


. As such, there is no overlap into substrate


12


, and no portion of the implanted contacts upper surface


34


of dielectric layer


14


. Where no electrically conductive region


24


lies beneath etch hole


26


, ion implantation may form a lateral interconnect to an implanted thermal conductor


30


. Dielectric layer


14


continues to serve as an electrical insulator and implanted thermal conductor


36


serves as a thermal conductor where the coefficient of thermal conductivity of conductor


36


is greater than the coefficient of thermal conductivity of dielectric layer


14


. Implanted thermal conductor


36


serves as a collector for Joule heat and a conduit for channeling heat therein, and acts as a heat sink.





FIG. 8

is an illustration of semiconductor device


10


with three (3) features of the present invention illustrated therein. Two implanted interconnects


30


are illustrated wherein implantation has occurred in a first instance above electrically conductive region


24


, and in a second instance above substrate


12


with no electrically conductive region thereunder. Implanted thermal conductor


36


is also illustrated in

FIG. 8

wherein no electrical connection is made to substrate


12


. Metallization lines


38


have been formed upon upper surface


34


of dielectric layer


14


. Implanted interconnects


30


form interconnects from to metallization lines


38


to electrically conductive region


24


and to substrate


12


. Implanted thermal conductor


36


lies beneath metallization lines


38


and serves as an excess Joule heat collector for metallization lines


38


.




Preferred ions to form the implanted interconnect are chosen to be compatible with the structure in which it is used. In an integrated circuit, implantation of copper or gold in areas where these elements might migrate into the substrate could cause field failure and affect carrier lifetime. In other applications, copper or gold would be acceptable materials to use. In a semiconductor application, elements such as Al, Ni, Cr, Mo, Ta, W, Ti, Zr, Hf, or V and equivalents might be chosen. In some applications in which a preferred dielectric layer material is used, Ni would be a preferred element because of its resistance to oxidation and its relatively good electrical conductivity. In some applications in which a preferred dielectric layer material is used, Al would be a preferred element because it can be implanted into a dielectric that will not substantially oxidize it and because of aluminum's relatively good electrical conductivity.




Materials that will form the implanted interconnect or thermally conductive implants are selected so that when the total implant dose is integrated over any segment, the total amount of implant meets or exceeds the desired concentration. In an example of a 10,000 Å film the first implant dose is selected so that at least 4 percent of the implant dose penetrates the entire 10,000 Å film, and that at least 10 percent of the implant dose is deposited in the 500 Å slice between 9,500 Å and 10,000 Å. The percentage of the implant dose is then calculated for each succeeding slice of 500 Å in which any appreciable amount of the implant dose is absorbed. The dose of the implant is then calculated to produce a concentration that exceeds the desired minimum in the first slice. The percentage is then multiplied by the dose amount and divided by the nominal Si concentration of about 5×10


22


atoms/cm


3


to obtain the percent of the implanted species in each slice. The second and succeeding implants are determined in a like manner until an implanted interconnect or an implanted thermal conductor is formed as desired.





FIG. 9

illustrates top, cross-sectional, and bottom views of metallization lines


38


and implanted thermal conductor


36


. Implanted thermal conductor


36


is designed to conduct heat away from metallization lines


38


or away from another functional element within a semiconductor device that generates Joule heat during field operation. Implanted thermal conductor


36


is electrically isolated from metallization lines


38


by dielectric layer


14


. Implanted thermal conductor


36


is situated proximal to metallization lines


38


such that heat generated in metallization lines


38


is conducted through dielectric layer


14


into implanted thermal conductor


36


. Implanted thermal conductor


36


may serve, for example, as a channel that leads to a heat sink structure.




The implanted electrically conductive structure formed in the inventive process will have a width in a range from about 0.3 Å to about 0.49 Å, and the dielectric layer will have a thickness from about 2,000 Å to about 12,000 Å. More preferably, where the dielectric layer has a thickness range of from about 8,000 Å to about 12,000 Å, the implanted electrically conductive structure will have a width range of from about 0.39 Å to about 0.49 Å. Where the dielectric layer has a thickness range of from about 4,000 Å to about 6,000 Å, the implanted electrically conductive structure will have a width range of from about 0.33 Å to about 0.43 Å. Where the dielectric layer has a thickness range of from about 2,000 Å to about 3,000 Å, the implanted electrically conductive structure will have a width range of from about 0.30 Å to about 0.40 Å.




The following process is an example used to produce a no via-etch interconnect in a layer polyamide having a thickness of 10,000 Å, which is seen in the Figures as dielectric layer


14


. An appropriate mask is first put in place. This can be either a simple mask, a multiple-layer mask, or a stand-off mask covered by a thin metal or inorganic layer. The mask is then covered with an imaging resist layer. In any case, the mask must be thick enough to stop essentially all of the incoming implant species. The mask is then imaged to produce openings through which a series of implantations of the implant species are then performed.




If an electrical contact is desired, the energy of the implantation is chosen so that penetration of the implant species is substantially continuous through dielectric layer


14


to substrate


12


. The energy of the implantation and the range of the depth of penetration of each implanted level can be calculated using, for example, a Monte Carlo simulation of the scatter and subsequent distribution of each of the required implant levels.




Calculations are given below in Table 1 for the formation of an implanted conductor in a dielectric layer having a thickness of about 10,000 Å and being substantially composed of BPDA-ODA or PMDA-ODA. The implanted conductor is formed, as shown in the Figures, by applying first mask


18


as a 5,000 Å thick positive photo resist. Second mask


20


is applied as a 5,000 Å thick Si


3


N


4


layer. Third mask


22


is applied as a 2,000 Å top imaging photo resist. Masks


18


,


20


,


22


are exposed and patterned to form a mask that will facilitate ion implantation to form implanted interconnects


30


. Implantation of Ni is then carried out. The remaining portions of masks


18


,


20


, and


22


serve to mask out unwanted ion implantation Table 1 illustrates eight (8) implantation steps of this example embodiment.

















TABLE 1











Implant #




Implant Energy




Implant dose






























1




825 KEV




1.35




10


18









2




410 KEV




8.98




10


17









3




175 KEV




3.2




10


17









4




 70 KEV




1.3




10


17









5




 20 KEV




7.0




10


16









6




 5 KEV




1.6




10


16









7




900 V




1.3




10


16









8




 80 V




4.0




10


16

















Illustration of the method of the present example continues by removing all masks and the metallizing the structure with appropriate electrically conductive materials such as is illustrated in

FIG. 8

as metallization lines


38


. Following connection of implanted interconnects


30


to metallization lines


38


, additional layers may then be built upon the present structure, such as by depositing a second dielectric layer (not shown) and continuing to build up the device.




Implant dose and energy are a function of the qualities of both the dielectric layer and the implanted species. Variation of the type of material of the dielectric layer and the implanted species to achieve a desired structure are contemplated. Table 2 illustrates the result of a Ni implant in the inventive example.















TABLE 2











Distance from Upper Surface








of Dielectric Layer (Å)




Ni. Percent













 0-20




42







20-50




73







 50-100




37







100-150




42







150-200




46







200-300




72







300-400




45







400-600




33







600-800




51







 800-1000




47







1000-1250




33







1250-1500




44







1500-1750




53







1750-2000




56







2000-2500




43







2500-3000




33







3000-3500




38







3500-4000




86







4000-4500




95







4500-5000




66







5000-5500




36







5500-6000




41







6000-6500




31







6500-7000




40







7000-7500




48







7500-8000




67







8000-8500




86







8500-9000




68







9000-9500




49







 9500-10000




66















As can be seen in Table 2, the minimum Ni concentration in any segment of 500 Å or less is at least 31 percent. A preferred random distribution of metal atoms is a range from about 35 percent to about 40 percent metal provides enough electrically conductive material to give sufficient contact, whereas more than about four percent and less than about 10 percent is preferably in a segregated mixture. Depending upon the nature of the implant, some segregation will occur.




It may be desirable to anneal an implanted conducive structure to distribute the implanted species. Anneal conditions are chosen so that diffusion takes place in the implanted columns but no significant atom diffusion occurs between adjacent implanted areas. As implant damage occurs in areas of implantation, local diffusion rates in these areas will be enhanced.




In cases where an implanted conductive structure segregates during anneal into grain or sub-grain boundaries of the dielectric layer, a reduced amount of implant is required to give adequate electrical interconnect qualities. When the dielectric layer is a polymer, as in the above-given example, the heat treatment is preferably in a range from about 300 to about 500 degrees centigrade, and more preferably about 400 degrees centigrade. In the case of the above-given example, curing of the polyamide dielectric layer provides required heat for annealing of the implanted conductive structure.




Heat treatment following implantation can be beneficial. For instance, an implanted conductive structure with in a dielectric layer that overlaps into a semiconductor substrate will expand laterally upon heat treatment to form, for example, an active area associated with a transistor source-drain structure.




Dielectric layer


14


, seen in the Figures, can be selected to be an organometallic dielectric or equivalent that releases metal elements in favor of bonding with oxygens or nitrogens and equivalents. Treatment is carried out in an oxygen or nitrogen atmosphere following implantation. Implantation of metal ions to form implanted interconnect


30


or an implanted thermal conductor


36


will, either spontaneously or with heat treatment, cause the metals in the organometallic dielectric to combine with the implanted metal ions to form a substantially coherent and continuous metal interconnect.




Combination of the metals in the organometallic and the implanted species accomplishes more metallization in implanted interconnect


30


or in an implanted thermal conductor


36


than simple implantation alone achieves. The combination also renders the organometallic dielectric more resistant to electrical conductivity than regions not implanted with metal ions.




The capabilities of a beam current implanter device being for used ion implantation will determine an optimized implant time. The thickness of the dielectric layer will also determine implant time. If the dielectric layer in the above-given example were 5,000 angstroms, the first implant would not be required and the total implant time would be 51 percent less than that required for a 10,000 angstrom dielectric layer. For a 2,500 angstrom dielectric layer, the first two implants would not be required and implant time would be reduced to 20 percent of implant time required for a 10,000 angstrom dielectric layer.




In the case of a 10,000 angstrom dielectric layer that is situated over an electrically conductive region, the minimum size contact which could be made is dependent upon the scatter of the ion implant species, and the size of the minimum photo-definable image. For example, if the minimum definable image were 0.25 microns with a tolerance of ±0.05 micron, the radial range of the most energetic implant would be added to the photolithographic tolerance to determine the appropriate minimum contact size. In the case of an implant of about 825 KeV, the minimum size would be approximately 0.14 microns, giving a total minimum contact size of approximately 0.44 microns. For a 4,500 angstrom film where maximum implant energy would be about 410 KeV, the radial range is approximately 0.075 microns, and results in a minimum effective contact size of about 0.38 micron. For a 2,500 angstrom film where maximum implant energy is about 175 KeV, the radial range is about 0.35 microns and results in a minimum contact size of about 0.34 microns.




The present invention may be embodied in other specific forms without departing from its spirit or essential characteristics. The described embodiments are to be considered in all respects only as illustrated and not restrictive. The scope of the invention is, therefore, indicated by the appended claims and their combination in whole or in part rather than by the foregoing description. All changes that come within the meaning and range of equivalency of the claims are to be embraced within their scope.



Claims
  • 1. An interconnect structure comprising:a substrate assembly having at least one electrically conductive active area; a dielectric layer, composed of a dielectric material, disposed upon said substrate assembly, said dielectric layer having a top surface thereon; and an interconnect, composed of electrically conductive ions and the dielectric material so as to render said interconnect to be electrically conductive, said interconnect forming an electrical connection between said electrically conductive active area and the top surface of said dielectric layer.
  • 2. An interconnect structure according to claim 1, wherein said interconnect extends between said electrically conductive active area and the top surface of said dielectric layer and has a length in a range from about 1,000 Å to about 30,000 Å.
  • 3. An interconnect structure according to claim 1, wherein said interconnect comprises at least one electrically conductive element, and wherein said electrically conductive element has an ion concentration at any portion in said interconnect in a range from about 25 percent to about 50 percent.
  • 4. An interconnect structure according to claim 1, wherein said dielectric layer has a thickness range of from about 8,000 Å to about 12,000 Å, and wherein said interconnect has a width range from about 0.39 Å to about 0.49Å.
  • 5. An interconnect structure according to claim 1, wherein said dielectric layer has a thickness range of from about 4,000 Å to about 6,000 Å, and said interconnect has a width range from about 0.33 Å to about 0.43 Å.
  • 6. An interconnect structure according to claim 1, wherein said dielectric layer has a thickness range from about 2,000 Å to about 3,000 Å, and said interconnect has a width in a range from about 0.30 Å to about 0.40 Å.
  • 7. An interconnect structure according to claim 1, wherein said interconnect has therein at least one metal ion selected from the group consisting of Al, Ni, Cr, Mo, Ta, W, Ti, Zr, Hf, and V.
  • 8. An interconnect structure according to claim 1, wherein said interconnect has a concentration of said electrically conductive ions situated in a series of overlapping depths.
  • 9. An interconnect structure according to claim 8, wherein each of said series of overlapping depths has a concentration of the electrically conductive ions greater than about 30 percent of a region into which each of said series is situated.
  • 10. An interconnect structure according to claim 1, wherein the dielectric material is selected from a group consisting of:BPSG, PSG, silica, thoria, ceria, and zirconia; organic, fluoro organic, and organometallic compounds; PMDA-ODA, BPDA-ODA, BPDA-PDA, PMDA-ODA, BTDA-PDA, and BTDA-ODA.
  • 11. An interconnect structure comprising:a substrate assembly having at least one electrically conductive active area; a layer including: a dielectric material selected from a group consisting of: BPSG, PSG, silica, thoria, ceria, and zirconia; organic, fluoro organic, and organometallic compounds; PMDA-ODA, BPDA-ODA, BPDA-PDA PMDA-ODA, BTDA-PDA, and BTDA-ODA, said dielectric layer being disposed upon said substrate assembly and having a top surface thereon; and an interconnect: having an electrical connection between said electrically conductive active area and the top surface of said dielectric layer; including a combination of said dielectric material and at least one electrically conductive element having an ion concentration in a range from about 25 percent to about 50 percent, said at least one electrically conductive element being selected from the group consisting of Al, Ni, Cr, Mo, Ta, W, Ti, Zr, Hf, and V, said at least one electrically conductive element being situated in overlapping segments each of which has a concentration of said at least one electrically conductive element that is greater than about 30 percent of a volume into which each of said segment is situated, whereby said ion concentration of said at least one electrically conductive element within said dielectric material renders said interconnect to be electrically conductive.
  • 12. A heat-transferring dielectric composite comprising:a dielectric layer, composed of a dielectric material, disposed upon a substrate assembly, wherein said dielectric layer comprises at least one electrically conductive region that: has a higher coefficient of thermal conductivity than the dielectric layer; is electrically isolated within said dielectric layer; is composed of a mixture of both electrically conductive ions and said dielectric material; is electrically conductive.
  • 13. A heat-transferring dielectric composite according to claim 12, wherein said dielectric layer has a thickness range from about 2,000 Å to about 12,000 Å.
  • 14. A heat-transferring dielectric composite according to claim 12, wherein said electrically conductive ions are selected from the group consisting of Al, Ni, Cr, Mo, Ta, W, Ti, Zr, Hf, and V.
  • 15. A heat-transferring dielectric composite according to claim 12, wherein:said dielectric material is selected from a group consisting of: BPSG, PSG, silica, thoria, ceria, and zirconia; organic, fluoro organic, and organometallic compounds; PMDA-ODA, BPDA-ODA, BPDA-PDA, PMDA-ODA, BTDA-PDA, and BTDA-ODA.
  • 16. A heat-transferring dielectric composite according to claim 12, wherein said at least one electrically conductive region has said electrically conductive ions situated in a series of overlapping depths.
  • 17. A heat-transferring dielectric composite according to claim 16, wherein each of said series of overlapping depths comprises a concentration of the metal ions greater than about 30 percent of a volume into which each of said series is situated.
  • 18. A heat-transferring dielectric composite comprising:a dielectric layer: composed of a dielectric material selected from a group consisting of: BPSG, PSG, silica, thoria, ceria, and zirconia; organic, fluoro organic, and organometallic compounds; PMDA-ODA, BPDA-ODA, BPDA-PDA, PMDA-ODA, BTDA-PDA, and BTDA-ODA; disposed upon a substrate assembly; and having at least one region that: has a higher coefficient of thermal conductivity than the dielectric layer; is electrically isolated within said dielectric layer; has therein a mixture of at least one metal ion and said dielectric material such that said at least one region is thereby rendered electrically conductive, said at least one metal ion being selected from the group consisting of Al, Ni, Cr, Mo, Ta, W, Ti, Zr, Hf, and V.
  • 19. The heat-transferring dielectric composite according to claim 18, wherein said at least one region has a concentration of said at least one metal ion at a series of overlapping depths.
  • 20. The heat-transferring dielectric composite according to claim 19, wherein the concentration of said at least one metal ion in each of said series of overlapping depths is greater than about 30 percent of a volume into which each of said overlapping depth is situated.
RELATED APPLICATIONS

This is a divisional application of U.S. patent application Ser. No. 08/829,851, filed Apr. 1, 1997, U.S. Pat. No. 6,017,829 titled “Implanted Conductor and Method of Making”, which is incorporated herein by reference.

US Referenced Citations (6)
Number Name Date Kind
4088799 Kurtin May 1978
4906591 Okumura Mar 1990
5232863 Roberts Aug 1993
5317197 Roberts May 1994
5726805 Kaushik et al. Mar 1998
5883000 Pasch Mar 1999
Foreign Referenced Citations (1)
Number Date Country
2-287594 Jun 1992 JP