Claims
- 1. A method of forming a silica-containing ceramic coating on a substrate comprising:
- applying a coating comprising a silicon hydride resin of the structure (SiO.sub.2).sub.x (RSiO.sub.3/2).sub.y (R.sub.2 SiO).sub.z on the substrate, wherein R independently comprises hydrogen or a hydrocarbon of 1 to 20 carbon atoms, y is a mole fraction between about 0.05 and 1, and x and z are mole fractions between about 0 and about 0.95, with the proviso that at least about 20% of the R groups are hydrogen; and
- heating the coated substrate in an atmosphere comprising nitrous oxide at a temperature sufficient to convert the silicon hydride resin coating to a silica-containing ceramic coating.
- 2. The method of claim 1 wherein the silicon hydride resin comprises hydrogen silsesquioxane resin.
- 3. The method of claim 1 wherein the silicon hydride resin comprises (HSiO.sub.3/2).sub.y (H.sub.2 SiO).sub.z.
- 4. The method of claim 2 wherein-the hydrogen silsesquioxane resin is applied to the substrate by a process which comprises coating the substrate with a solution comprising a solvent and the hydrogen silsesquioxane resin and then evaporating the solvent.
- 5. The method of claim 4 wherein the substrate is an electronic device.
- 6. The method of claim 4 wherein said solution is coated onto the substrate by spray coating, dip coating, flow coating or spin coating.
- 7. The method of claim 1 wherein the coated substrate is heated at a temperature in the range of between about 100.degree. C. and about 600.degree. C. for between about 1 and 3 hours.
- 8. The method of claim 2 wherein the hydrogen silsesquioxane resin is fractionated into polymeric species such that at least 75% of the polymeric species have a molecular weight between about 1200 and about 100,000.
- 9. The method of claim 2 wherein the resin contains residual Si--OH and Si--OR' bonds, wherein R' comprises a hydrocarbon of 1-20 carbon atoms.
- 10. The method of claim 1 wherein the silicon hydride resin coating also contains modifying ceramic oxide precursors comprising a compound containing an element selected from the group consisting of titanium, zirconium, aluminum, tantalum, vanadium, niobium, boron and phosphorous wherein the compound contains at least one hydrolyzable substituent selected from the group consisting of alkoxy or acyloxy and the compound is present in an amount such that the silica containing ceramic coating contains 0.1 to 30 percent by weight modifying ceramic oxide.
- 11. The method of claim 1 wherein the silicon hydride resin coating also contains a platinum or rhodium catalyst in an amount of between about 5 and about 500 ppm platinum based on the weight of resin.
- 12. The method of claim 1 wherein the silicon hydride resin coating also contains fillers.
- 13. The method of claim 1 wherein the heating atmosphere also contains an inert gas.
- 14. The method of claim 1 wherein the heating atmosphere also contains an additional reactive gas.
- 15. The method of claim 1 wherein the heating atmosphere also contains water vapor.
- 16. The method of claim 1 wherein the coated substrate is first heated in an inert environment to allow the coating to flow and then in the nitrous oxide.
- 17. The method of claim 1 wherein the coated substrate is only exposed to the nitrous oxide during a portion of the heating.
RELATED APPLICATIONS
This application is a continuation in part of Ser. No. 07/912,436, filed Jul. 13, 1992, now abandoned.
US Referenced Citations (8)
Non-Patent Literature Citations (3)
Entry |
Cotton et al, "Advanced Inorganic Chemistry", Section 12-6 Oxides Of Nitrogen, p. 341, (Feb. 1967). |
The Merck Index, Eleventh Edition, "6575 Nitrous Oxide", p. 1051, (1990). [no month]. |
Desu et al., J Electrochem Soc., vol. 139, No. 9, Sep. 1992. |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
912436 |
Jul 1992 |
|