This application claims priority under 35 U.S.C. §119 to European Patent Application No. 06026658.2 filed in the European Patent Office on 22 Dec. 2006, the entire contents of which are hereby incorporated by reference in their entireties.
An electronic device with a base plate for a heat sink is disclosed.
WO 2004/065050 describes a method to solder a capacitor to a printed circuit board (PCB). In order to achieve a defined thickness of the solder layer between the capacitor and the PCB, the solder paste contains a solder material and a spacer material, which has a melting point higher than the melting point of the solder material. Typically, the spacer material is in form of spheres. During heating of the solder paste, the solder paste is heated to a temperature that is higher than the melting point of the solder material, but lower than the melting point of the spacer material. The spacer material stays as a solid in the paste, so that the capacitor and the PCB are spaced at a predetermined thickness from each other after the heating process. The distance between the capacitor and PCB can be varied by varying the dimensions of the spacer material in the solder paste.
U.S. Pat. No. 5,784,256 refers to a notebook with a printed circuit board (PCB) including a heat generating IC chip. The chip on the PCB is cooled by clamp contacting the PCB between a cover and a cooling plate having four bosses with holes for inserting screws. The cover and cooling plate with the PCB in between are clamped together by inserting screws from the cover to the holes in the cooling plate. Between the chip and the cooling plate, which is made of a metal with high electrical and thermal conductivity, an electrically and thermally conductive layer is arranged.
An electronic device with a base plate for a heat sink is disclosed, which allows metallurgical bonding of the base plate to a power electronic component without the danger of tilting of the base plate against the power electronic component and which base plate is easy to manufacture.
An electronic device is disclosed comprising at least one power electronic component, in particular at least one semiconductor chip, an electrically insulating plate and a base plate with a cooling plate, wherein the base plate comprises spacer elements, which are arranged on the surface of the cooling plate, the spacer elements and the cooling plate being made as one piece and the material in the surface region of the cooling plate and of the spacer elements being the same, in that the at least one power electronic component is bonded by a metallurgical process, in particular by soldering, metal or low-temperature bonding, on the electrically insulating plate, in particular on a ceramic substrate, which electrically insulating plate is bonded by a metallurgical process, in particular by soldering or low-temperature bonding, on the base plate.
The subject matter of the disclosure will be explained in more detail in the following text with reference to the attached drawings, in which:
The reference symbols used in the figures and their meaning are summarized in the list of reference symbols. Generally, alike or alike-functioning parts are given the same reference symbols. The described embodiments are meant as examples and shall not confine the disclosure.
An exemplary electronic device comprises a base plate with a cooling plate and spacer elements, which are arranged on the surface of the cooling plate. The spacer elements and the cooling plates are made as one piece with the material at least in the surface region of the cooling plate and the spacer elements being the same.
The base plate of the exemplary electronic device allows to achieve a predetermined distance to a power electronic component, which is metallurgical bonded to the base plate. A tilting of the power electronic component against the base plate is minimised by the introduction of spacer elements on the cooling plate, which tilting would lead to different thermal extension of the areas of the bonding layer with different bonding layer, e.g. solder layer thicknesses. In that case heat distribution would be worse in the areas of greater solder thickness, because the solder material has typically a worse heat conductivity than the base plate itself or the electronic element. Additionally, there would be a danger of a delamination of the power electronic component from the base plate in case of extended thermal cycling.
With the exemplary electronic device with a base plate, any solder material, suitable for achieving the desired connection between the base plate and the power electronic component in terms of temperature during the soldering and thermal properties of the solder layer can be used.
Furthermore, with such an exemplary electronic device with a base plate heat can be distributed in a uniform way between the heat producing parts of a power electronic component and the base plate, if the spacer elements are arranged in areas of the base plate, which are not directly below the heat producing part of the power electronic component.
In
Typically the cooling plate 2 is made of a metal matrix composite, e.g. a Silicon-Carbide (SiC) preform infiltrated with molten Aluminum. For the manufacturing of such a metal matrix composite the SiC preform is placed in a mold, which has the negative form of the desired final base plate 1 and then the preform is infiltrated with the Aluminum. For an exemplary base plate the mold comprises recesses, by which in the final base plate 1 spacer elements 3 are formed.
The spacer elements 3, as shown in
The spacer elements 3 and the cooling plate 2 are made as one piece and the material in the surface region of the cooling plate 2 and of the spacer elements 3 is the same. For a metal matrix composite that means that the pins 31 can be made of Aluminum in the same step as the infiltration with Aluminum.
In another exemplary embodiment the pins 31 extend the surface of the cooling plate 2 to a height 32 between 50 to 200 μm. The minimum height of the pins 31 is given by the maximum unevenness of the surfaces of the power electronic component and the cooling plate 2, whereas the maximum height of the pins 31 is defined by thermal resistance of the solder joint. The pins 31 may have any appropriate cross section like a quadrangular cross section, in particular a square or a rectangular cross section or a round cross section, in particular a circular or an oval cross section. The cross section can be chosen for reasons of easy manufacturing or for geometrical reasons in the final electronic device.
In
In
Another exemplary embodiment of the base plate 1 is also shown in
In
The at least one semiconductor chip 4 is bonded by a metallurgical process, e.g., by soldering or metal bonding, on an electrically insulating plate 8, which is typically a ceramic substrate. The insulating plate 8 is plate is bonded by a metallurgical process, in particular by soldering, on the side, which lies opposite the side, on which the at least one semiconductor chip 4 is arranged, on the base plate 1. Also low temperature bonding can be used as a metallurgical bonding for one or both bondings. Such low temperature bondings are typically made under high pressure and temperatures typically below 300° C. Metals like silver and indium or tin and gold are used for making the joint. The metals are applied on the surfaces to be jointed together as thin sheets and/or as a powder. Such low-temperature bonding methods are for example described in PCT/CH2006/00610.
These metallurgical bondings are non-detachable connections, i.e. the connections are destroyed if trying to separate the two elements bonded together under normal conditions.
In another exemplary embodiment, shown in
In another exemplary embodiment, not shown in a figure, the exemplary base plate 1 is thermally and electrically conductive connected to the at least one semiconductor chip 4.
It will be appreciated by those skilled in the art that the present invention can be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The presently disclosed embodiments are therefore considered in all respects to be illustrative and not restricted. The scope of the invention is indicated by the appended claims rather than the foregoing description and all changes that come within the meaning and range and equivalence thereof are intended to be embraced therein.