The present application claims priority to Chinese Patent Application No. 200910195981.9, filed on Sep. 18, 2009 by inventors Xian J. Ning and Bei Zhu, commonly assigned and incorporated in its entirety by reference herein for all purposes. The present application is also related to U.S. patent application Ser. No. 11/244,955 filed Oct. 5, 2005, U.S. patent application Ser. No. 12/234,393 filed Sep. 19, 2008, U.S. patent application Ser. No. 11/678,582 filed Feb. 24, 2007, U.S. patent application Ser. No. 11/442,009 filed May 26, 2006, U.S. patent application Ser. No. 11/609,748 filed Dec. 12, 2006, now U.S. Pat. No. 7,557,000. The disclosures of all the above applications are incorporated by reference in their entirety herein for all purposes.
The present invention is directed to integrated circuits and their processing for the manufacture of semiconductor devices. More particularly, embodiments of the invention provide a method and structures for integrating PMOS and NMOS devices using strained silicon structures for advanced CMOS integrated circuit devices. But it would be recognized that the invention has a much broader range of applicability.
Integrated circuits have evolved from a handful of interconnected devices fabricated on a single chip of silicon to millions of devices. Conventional integrated circuits provide performance and complexity far beyond what was originally imagined. In order to achieve improvements in complexity and circuit density (i.e., the number of devices capable of being packed onto a given chip area), the size of the smallest device feature, also known as the device “geometry”, has become smaller with each generation of integrated circuits.
Increasing circuit density has not only improved the complexity and performance of integrated circuits but has also provided lower cost parts to the consumer. An integrated circuit or chip fabrication facility can cost hundreds of millions, or even billions, of U.S. dollars. Each fabrication facility will have a certain throughput of wafers, and each wafer will have a certain number of integrated circuits on it. Therefore, by making the individual devices of an integrated circuit smaller, more devices may be fabricated on each wafer, thus increasing the output of the fabrication facility. Making devices smaller is very challenging, as each process used in integrated fabrication has a limit. That is to say, a given process typically only works down to a certain feature size, and then either the process or the device layout needs to be changed. Additionally, as devices require faster and faster designs, process limitations exist with certain conventional processes and materials.
An example of such a process is the manufacture of MOS devices itself Such device has traditionally became smaller and smaller and produced faster switching speeds. Although there have been significant improvements, such device designs still have many limitations. As merely an example, these designs must become smaller and smaller but still provide clear signals for switching, which become more difficult as the device becomes smaller. Additionally, these designs are often difficult to manufacture and generally require complex manufacturing processes and structures. These and other limitations will be described in further detail throughout the present specification and more particularly below.
From the above, it is seen that an improved technique for processing semiconductor devices is desired.
According to the present invention, techniques for processing integrated circuits for the manufacture of semiconductor devices are provided. More particularly, the invention provides a method and structures for integrating PMOS and NMOS devices using strained silicon structures for advanced CMOS integrated circuit devices. But it would be recognized that the invention has a much broader range of applicability.
As further background information, integrated circuit processes generally involves gate patterning, which is normally using a poly crystalline silicon as a gate conductor. In the process, a polysilicon film is deposited on the substrate, which is a single crystal silicon that has undergone various processes such as implantations, gate oxide formation, among others. The polysilicon is then covered with one or more dielectric materials such as silicon oxide and/or silicon oxynitride. The dielectric film is then photo lithographically patterned and etched to form the gate conductor pattern. The patterned dielectric materials is then used as “hard mask” to transfer the pattern into polysilicon using a plasma etch process. The hard mask is stripped by wet chemicals after polysilicon patterning.
As critical dimension getting smaller, silicon germanium (e.g., SiGe) and silicon carbide (e.g., SiCx) as source and drains in a CMOS transistor provided for integrated circuits have been used by selective growth of epitaxal films in etched regions of the silicon substrate. Prior to the epitaxial film growth, a silicon etch is applied to for a recess in the silicon surface to form a site for silicon germanium to be deposited. The hard mask for polysilicon gate layer patterning mentioned above is used as a self-aligned mask for a recess etch of the silicon substrate. The hard mask is removed after epi growth in order to form silicide on top of patterned polysilicon gate structures. The dielectric hard mask removal process also undesirably erodes the polysilcon gate spacer (and possibly structure) that was formed after poly gate pattern as well as the shallow trench isolation (STI). Also, a polysilicon-gate, which is also doped by ion-implantation, is subjected to further degradation and other undesirable influences. This patent specification discloses an integration scheme that have SiGe and SiCx epi for PMOS and NMOS, respectively. The poly hard mask and spacer materials are designed to have reduced and/or minimum process steps as compared to conventional techniques. Further details of our method and structure can be found throughout the present specification and more particularly below.
In a specific embodiment, the present invention provides a method for forming a semiconductor integrated circuit device, e.g., CMOS. The method includes providing a semiconductor substrate (e.g., silicon wafer, silicon on insulator, epitaxial silicon) including a first well region and a second well region. In a specific embodiment, the method includes forming a dielectric layer (e.g., gate oxide, gate oxynitride, gate nitride) overlying the semiconductor substrate including the first well region and the second well region. In a specific embodiment, the method includes forming a polysilicon gate layer (e.g., doped polysilicon, in-situ polysilicon) overlying the dielectric layer. The polysilicon gate layer is overlying a first channel region in the first well region and a second channel region in the second well region in the semiconductor substrate. In a specific embodiment, the method includes forming a hard mask (e.g., silicon dioxide) overlying the polysilicon gate layer.
In a specific embodiment, the method patterns the polysilicon gate layer, including the hard mask layer, to form a first gate structure including first edges in the first well region and a second gate structure including second edges in the second well region. In a specific embodiment, the method forms a liner layer overlying the first gate structure and the second gate structure and overlying first source/drain regions in the first well region and second source/drain regions in the second well region. In a specific embodiment, the method includes forming a spacer dielectric layer overlying the liner layer. In a preferred embodiment, the spacer dielectric layer includes a first portion overlying the first gate structure and a second portion overlying the second gate structure.
Next, the method separately forms strained regions in the first and second well regions. In a specific embodiment, the method includes protecting the second gate structure, including second source/drain regions, and the second portion of the spacer dielectric layer provided in the second well region using a second photoresist mask material. The method includes patterning the first portion of the spacer dielectric layer to form first sidewall spacer structures on the first gate structure, including the first edges while the second photomasking material protects the second portion of the spacer dielectric layer and the second gate structure, including the second source/drain regions in the second well region. The method includes etching a first source region and a first drain region adjacent to the first gate structure using a first portion of the hard mask layer and the first sidewall spacers as a protective layer. The method includes depositing a silicon germanium fill material into the first source region and the first drain region to fill the etched first source region and the etched first drain region while causing the first channel region between the first source region and the first drain region to be strained in compressive mode from at least the silicon germanium material formed in the first source region and the first drain region. The second photoresist masking material is removed.
In a specific embodiment, the method protects the first gate structure, including first source/drain regions, and the first portion of the spacer dielectric layer provided in the first well region using a first photoresist mask material. The method includes patterning the second portion of the spacer dielectric layer to form second sidewall spacer structures on the second gate structure, including the second edges while the first photomasking material protects the first gate structure, including the first source/drain regions in the first well region. In a specific embodiment, the method includes etching a second source region and a second drain region adjacent to the second gate structure using a second portion of the hard mask layer and the second sidewall spacers as a protective layer. The method then deposits a silicon carbide fill material into the second source region and the second drain region to fill the etched second source region and the etched second drain region while causing the second channel region between the second source region and the second drain region to be strained in tensile mode from at least the silicon carbide material formed in the second source region and the second drain region. The first photoresist masking material is removed.
Depending upon the embodiment, one or more of these features may exist.
1. In a specific embodiment, the present method and structure can include a silicon dioxide and polysilicon hard mask for the present CMOS strained epi scheme.
2. In a preferred embodiment, transistors including PMOS and NMOS spacers are formed separately using two photo mask steps.
3. In a specific embodiment, the present method and structure can include an oxide nitride and/or nitride only as spacers for the present strained epi CMOS scheme.
4. In a specific embodiment, the present method and structure include an oxide hard mask for an NMOS silicon recess etch and epitaxial growth in the recessed region while the hard mask is used as a protecting layer. (Alternatively, if the process sequence is exchanged, the hard mask can also be for a PMOS recess etch and SiGe epitaxial growth in the recessed region).
5. In a specific embodiment, the method and structure include an oxide or like material in replacement of, for example, a polysilicon hard mask provided for an epitaxial recess etch and growth. In a preferred embodiment, removal of the oxide hard mask using a strip process does not attack spacers made of silicon nitride material.
Depending upon the embodiment, one or more of these features can exist. Of course, there can be other variations, modifications, and alternatives.
Many benefits are achieved by way of the present invention over conventional techniques. For example, the present technique provides an easy to use process that relies upon conventional technology. In some embodiments, the method provides higher device yields in dies per wafer. Additionally, the method provides a process that is compatible with conventional process technology without substantial modifications to conventional equipment and processes. Preferably, the invention provides for an improved process integration for design rules of 90 nanometers and less and/or 65 nanometers and less. Additionally, the invention provides for increased mobility of holes using a strained silicon structure for CMOS devices. In a preferred embodiment, the present invention provides an improved integration scheme for CMOS devices according to an embodiment of the present invention. Depending upon the embodiment, one or more of these benefits may be achieved. These and other benefits will be described in more throughout the present specification and more particularly below.
Various additional features and advantages of the present invention can be more fully appreciated with reference to the detailed description and accompanying drawings that follow.
According to the present invention, techniques for processing integrated circuits for the manufacture of semiconductor devices are provided. More particularly, the invention provides a method and structures for integrating PMOS and NMOS devices using strained silicon structures for advanced CMOS integrated circuit devices. But it would be recognized that the invention has a much broader range of applicability.
1. Provide a silicon substrate (100);
2. Form gate layer (103);
3. Form dielectric hard mask (205);
4. Pattern dielectric mask;
5. Pattern gate layer to form polysilicon gates;
6. Deposit spacer layer and etch back to form spacer structures 207;
7. Etch source/drain recessed regions 209 in silicon;
8. Form epitaxial silicon/germanium 301 in recessed regions;
9. Remove hard mask; and
10. Perform other steps as desired.
As noted above, the MOS device is often made using the above process steps. As the device becomes more complex and line rules become smaller, it is more difficult to manufacture the strained silicon MOS devices for CMOS technologies. These and other limitations may be overcome by the present method and structures, which will be described in more detail below.
A method for fabricating an integrated circuit device according to an embodiment of the present invention may be outlined as follows:
1. Provide a semiconductor substrate (e.g., silicon, silicon on insulator, epitaxial silicon);
2. Form a first well region (e.g., N-type well) and a second well region, e.g., P-type well in the semiconductor substrate;
3. Form a dielectric layer (e.g., silicon dioxide, silicon nitride, silicon oxynitride) overlying the semiconductor substrate including the first well region and the second well region;
4. Form a polysilicon gate layer (e.g., doped polysilicon, insitu-doped polysilicon, amorphous silicon, which is crystallized) overlying the dielectric layer;
5. Form a hard mask (e.g., dielectric layer) overlying the polysilicon gate layer;
6. Pattern the polysilicon gate layer, including the hard mask layer, to form a first gate structure including first edges in the first well region and a second gate structure including second edges in the second well region;
7. Form a liner layer (e.g., TEOS) overlying the first gate structure and the second gate structure and overlying first source/drain regions in the first well region and second source/drain regions in the second well region;
8. Form a spacer dielectric layer overlying the liner layer;
9. Protect the second gate structure, including second source/drain regions, and a second portion of the spacer dielectric layer provided in the second well region using a second photoresist mask material;
10. Pattern the first portion of the spacer dielectric layer to form first sidewall spacer structures on the first gate structure, including the first edges while the second photomasking material protects the second portion of the spacer dielectric layer and the second gate structure, including the second source/drain regions in the second well region.
11. Etch a first source region and a first drain region adjacent to the first gate structure using a first portion of the hard mask layer and the first sidewall spacers as a protective layer;
12. Deposit a silicon germanium fill material into the first source region and the first drain region to fill the etched first source region and the etched first drain region while causing the first channel region between the first source region and the first drain region to be strained in compressive mode from at least the silicon germanium material formed in the first source region and the first drain region;
13. Remove the second photoresist masking material;
14. Form a blanket layer of silicon oxide overlying the first gate structure including the first source/drain regions in the first well region and the second gate structure including the second source/drain regions in the second well region;
15. Protect the first gate structure, including first source/drain regions, and a first portion of the spacer dielectric layer provided in the first well region using a first photoresist mask material;
16. Pattern the second portion of the spacer dielectric layer to form second sidewall spacer structures on the second gate structure, including the second edges while the first photomasking (used alternately for photoresist mask) material protects the first gate structure, including the first source/drain regions in the first well region;
17. Etch a second source region and a second drain region adjacent to the second gate structure using a second portion of the hard mask layer and the second sidewall spacers as a protective layer;
18. Deposit a silicon carbide fill material into the second source region and the second drain region to fill the etched second source region and the etched second drain region while causing the second channel region between the second source region and the second drain region to be strained in tensile mode from at least the silicon carbide material formed in the second source region and the second drain region;
19. Remove the first photoresist masking material;
20. Perform other steps, as desired.
The above sequence of steps provides a method according to an embodiment of the present invention. As shown, the method uses a combination of steps including a way of forming an integrated circuit device such as an MOS device for a CMOS integrated circuit. As shown, the method includes using a silicon rich oxide or silicon rich nitride or silicon oxide layer to facilitate the manufacture of both NMOS and PMOS devices in the CMOS integrated circuit device according to a specific embodiment. Other alternatives can also be provided where steps are added, one or more steps are removed, or one or more steps are provided in a different sequence without departing from the scope of the claims herein. Further details of the present method can be found throughout the present specification and more particularly below.
In a specific embodiment, the method includes forming a dielectric layer 509 (e.g., silicon dioxide, silicon nitride, silicon oxynitride) overlying the semiconductor substrate including the first well region and the second well region. The method forms a polysilicon gate layer 511 overlying the dielectric layer. In a preferred embodiment, the polysilicon gate layer is overlying a first channel region in the first well region and a second channel region in the second well region in the semiconductor substrate. The polysilicon can be made using a suitable technique including doped polysilicon, in-situ-doped polysilicon, and/or amorphous silicon, which is crystallized. Of course, there can be other variations, modifications, and alternatives.
In a specific embodiment, the method forms a hard mask 513 overlying the polysilicon gate layer, as also shown in
In a preferred embodiment, the method forms a liner layer 515 overlying the first gate structure and the second gate structure and overlying first source/drain regions in the first well region and second source/drain regions in the second well region, as shown in
In a specific embodiment, the method forms a spacer dielectric layer 517 overlying the liner layer, also shown in
Referring again to
Referring to
In a preferred embodiment, the silicon germanium fill material is single crystalline and deposited using an epitaxial reactor. The ratio of silicon/germanium is 10% to 20% according to a specific embodiment. In a specific embodiment, the germanium is characterized by a concentration ranging from about 5 to about 45%, but can be others. The etched source region and the etched drain region are each coupled to the gate structure. As shown, the device has a strained channel region between the filled source region and the filled drain region from at least the silicon germanium material formed in the etched source region and the etched drain region. The device also has lightly doped drain regions or implant regions, which are formed before growing the silicon/germanium material in the recessed regions. Of course, there can be other variations, modifications, and alternatives.
In a specific embodiment, the method forms a blanket layer of silicon oxide overlying the first gate structure including the first source/drain regions in the first well region and the second gate structure including the second source/drain regions in the second well region, as illustrated in
In a specific embodiment, the method protects the PMOS gate structure, including first source/drain regions, and the first portion of the spacer dielectric layer provided in the first well region using a first photoresist mask material, as shown in
In a specific embodiment, the method includes etching a second source region and a second drain region adjacent to the second gate structure using a second portion of the hard mask layer and the second sidewall spacers as a protective layer. Etching occurs in the second source/drain regions, which are substantially silicon based, while other portions of dielectric material act as masking materials according to a specific embodiment. Etching occurs using a plasma etch process to form the recessed regions. Next, the method strips the masking layer overlying the second well region and exposes the second transistor structures in the second well region.
In a specific embodiment, the method then deposits a silicon carbide fill material into the second source region and the second drain region to fill the etched second source region and the etched second drain region, as illustrated by
In a specific embodiment, the method includes a photolithography and etching process that forms one or more regions that do not include silicide formation blocked by a dielectric layer, while removing the bulk part of the film at other regions. The etching process is preferably anisotropic reactive ion etching (RIE) that remove more material on a horizontal surface than on vertical surface regions. As a result, the exposed spacer is covered by a thin oxide layer. Of course, there can be other variations, modifications, and alternatives.
In a specific embodiment, the photoresist is then stripped by ashing, for example. In a preferred embodiment, the substrate is then dipped in a phosphoric acid solution, which selectively removes the silicon rich nitride or silicon oxide or silicon rich oxide and also strips the polysilicon hard mask. In a preferred embodiment, the substrate is further cleaned by a diluted hydrofluoric acid, commonly termed HF, to remove any remaining oxide on the surface regions after removal of the hard mask layer. The method deposits metals including titanium, cobalt, nickel, platinum, and tungsten, for example, using a silicidation process. Other metals can also be used. As has been illustrated, the present method includes a combination of a spacer protection layer that prevents nitride spacer erosion during the gate polysilicon hardmask removal with salicide block into a single process according to a specific embodiment. Hence, the present method can reduce certain steps such as oxide deposition, etch back wet clean, and others associated with both of these processes. Of course, there can be other variations, modifications, and alternatives.
In a specific embodiment, further details of the present method and structures can be found throughout the present specification and more particularly below. In a specific embodiment, the hard mask used for poly gate patterning can be a silicon oxide or oxide rich SiON formed by PECVD, or other suitable techniques. In a specific embodiment, the spacer used can be a silicon oxide liner with thickness of 10 Angstroms (Å) to 200 Ansgtroms followed by a SiN with thickness of 50 Å to 900 Å, as well as other dimensions.
In a specific embodiment, a SiNx film with high tensile stress is then deposited on the structures by plasma enhanced chemical vapor deposition (PECVD), for example, or other suitable technique. The silicon nitride film thickness ranges from about 200 Angstroms to 1200 Angstroms and is provided overlying the NMOS devices to cause additional strain in a tensile mode in the NMOS channel region. Of course, there can be other variations, modifications, and alternatives.
In a specific embodiment, the method also includes forming an interlayer dielectric material overlying the entirety of the PMOS and NMOS device structures. In a preferred embodiment, the interlayer dielectric, such as boro-phosphate-silicate-glass (BPSG), boro-silicate glass (BSG), phosphosilicate glass (PSG) or high density plasma (HDP) film is then deposited followed by PECVD oxide layer. Depending upon the specific embodiment, the interlayer dielectric can be a single material, a combination of layers, and the like. The method also includes contact pattern and formation performed to complete the PMOS and NMOS integration on strained silicon. Of course, there can be other variations, modifications, and alternatives.
Although the above has been described in terms of an MOS device, there can be other variations, modifications, and alternatives. It is also understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
2009 1 0195981 | Sep 2009 | CN | national |
Number | Name | Date | Kind |
---|---|---|---|
5168072 | Moslehi | Dec 1992 | A |
6043545 | Tseng et al. | Mar 2000 | A |
6121100 | Andideh et al. | Sep 2000 | A |
6179973 | Lai et al. | Jan 2001 | B1 |
6251242 | Fu et al. | Jun 2001 | B1 |
6274894 | Wieczorek et al. | Aug 2001 | B1 |
6277249 | Gopalraja et al. | Aug 2001 | B1 |
6291321 | Fitzgerald | Sep 2001 | B1 |
6352629 | Wang | Mar 2002 | B1 |
6372569 | Lee et al. | Apr 2002 | B1 |
6406599 | Subramani et al. | Jun 2002 | B1 |
6406973 | Lee | Jun 2002 | B1 |
6483151 | Wakabayashi et al. | Nov 2002 | B2 |
6503773 | Fitzgerald | Jan 2003 | B2 |
6514836 | Belford | Feb 2003 | B2 |
6563152 | Roberds et al. | May 2003 | B2 |
6566276 | Maloney et al. | May 2003 | B2 |
6617623 | Rhodes | Sep 2003 | B2 |
6713357 | Wang et al. | Mar 2004 | B1 |
6730196 | Wang et al. | May 2004 | B2 |
6881635 | Chidambarrao et al. | Apr 2005 | B1 |
6891192 | Chen et al. | May 2005 | B2 |
7052946 | Chen et al. | May 2006 | B2 |
7078722 | Anderson et al. | Jul 2006 | B2 |
7195985 | Murthy et al. | Mar 2007 | B2 |
7381623 | Chen et al. | Jun 2008 | B1 |
7425488 | Wu et al. | Sep 2008 | B2 |
7446026 | Zhang et al. | Nov 2008 | B2 |
7547595 | Ning | Jun 2009 | B2 |
7557000 | Chen et al. | Jul 2009 | B2 |
7709336 | Ning et al. | May 2010 | B2 |
7820500 | Ning | Oct 2010 | B2 |
20020190284 | Murthy et al. | Dec 2002 | A1 |
20030080361 | Murthy et al. | May 2003 | A1 |
20030139001 | Snyder et al. | Jul 2003 | A1 |
20040063300 | Chi | Apr 2004 | A1 |
20050035409 | Ko et al. | Feb 2005 | A1 |
20050142768 | Lindert et al. | Jun 2005 | A1 |
20050158931 | Chen et al. | Jul 2005 | A1 |
20050179066 | Murthy et al. | Aug 2005 | A1 |
20060086987 | Chen et al. | Apr 2006 | A1 |
20060105511 | Yang et al. | May 2006 | A1 |
20060115949 | Zhang et al. | Jun 2006 | A1 |
20060138398 | Shimamune et al. | Jun 2006 | A1 |
20070072353 | Wu et al. | Mar 2007 | A1 |
20070072376 | Chen et al. | Mar 2007 | A1 |
20070128786 | Cheng et al. | Jun 2007 | A1 |
20070138570 | Chong et al. | Jun 2007 | A1 |
20070184668 | Ning et al. | Aug 2007 | A1 |
20070196992 | Xiang et al. | Aug 2007 | A1 |
20080124874 | Park et al. | May 2008 | A1 |
20080191244 | Kim et al. | Aug 2008 | A1 |
20080251851 | Pan et al. | Oct 2008 | A1 |
20080283926 | Sridhar | Nov 2008 | A1 |
20090023258 | Liang et al. | Jan 2009 | A1 |
20090065805 | Wu et al. | Mar 2009 | A1 |
20090085125 | Kim et al. | Apr 2009 | A1 |
20090289379 | Han et al. | Nov 2009 | A1 |
20100124818 | Lee et al. | May 2010 | A1 |
20100224937 | Sridhar | Sep 2010 | A1 |
Number | Date | Country |
---|---|---|
1499578 | May 2004 | CN |
2006186240 | Jul 2007 | JP |
WO 0154175 | Jul 2001 | WO |
WO 2005038890 | Apr 2005 | WO |
Number | Date | Country | |
---|---|---|---|
20110070701 A1 | Mar 2011 | US |