Patent Application
20120090536
The present invention relates to a method for producing a silicon epitaxial wafer.
A production method is known which grows a vapor phase epitaxial layer on the surface of a silicon single crystal wafer processed through mirror polishing and then subjects the surface of the epitaxial layer to mirror polishing process (Patent Document 1). According to this production method, crown defects having occurred during the epitaxial growth are allowed to be removed and the flatness of the surface may be achieved.
Patent Documents
Patent Document 1: Examined Patent Publication No. H8-17163 (1996)
Problem to be Solved by the Invention
However, the above prior art production method may not solve the problems, such as degradation in flatness caused by damages on the back surface of the wafer and ununiformity in thickness of the epitaxial layer.
Problems to be solved by the present invention include providing a method for producing a silicon epitaxial wafer, in which the degradation in flatness caused by damages on the back surface of a wafer and ununiformity in thickness of an epitaxial layer are allowed to be suppressed.
Means for Solving the Problems
The present invention solves the above problems through providing a first double side polishing step at which both main surfaces of a silicon single crystal substrate are subjected to rough polishing simultaneously before a growth step at which an epitaxial layer is grown on the silicon single crystal substrate, while providing a second double side polishing step at which the both main surfaces of the silicon single crystal substrate are subjected to finish polishing simultaneously after the growth step.
Effects of the Invention
According to the present invention, the rough polishing in the first double side polishing step ensures the flatness of a wafer, and the final polishing in the second double side polishing step allows damages on the wafer back surface to be removed, thereby also allowing the thickness of the epitaxial layer to be even.
a), 5(b), and 5(c) are schematic cross-sectional views illustrating polishing statuses by the polishing apparatus in
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
Describing at first one example of a pre-process for slicing step A, through Czochralski pulling up method, a p-type silicon single crystal ingot is produced which has the main axis orientation of <100> and the diameter of 305 mm, and this ingot is peripherally ground into the diameter of 300 mm and then subjected to notch forming thereafter being cut into a plurality of blocks with resistivity of 5 to 10 mΩcm.
Note that, as the main axis orientation of the silicon single crystal, any main axis orientations other than <100>, such as <110>, may be applicable. Also note that, as the wafer diameter, any diameters other than 300 mm, such as 200 mm and 450 mm, may be applicable.
In the slicing step A, each of the above blocks is sliced using a wire saw to provide wafer-like substrates with a certain thickness.
Sliced wafer substrates are subjected to double side grinding in lapping step B thereby to ensure a certain degree of flatness. In the lapping step B, the wafer substrates are interposed between upper and lower grinding surface plates of a double side grinding machine, and both surfaces, i.e. the front surface and the back surface of each wafer substrate are ground while supplying slurry containing abrasive grains.
Wafer substrates having been flattened to a certain degree through the lapping step B are subjected to single side grinding step C, and the front surfaces thereof are further flattened. In the single side grinding step C, the front surfaces of wafer substrates are ground using a grinding stone containing diamond etc.
After ensuring the flatness of the single side grinding step C, wafer substrates are put into chamfering step D and the shapes of outer faces thereof are adjusted using grinding stone.
In the producing method according to the present embodiment, first double side polishing step E is provided which performs rough polishing simultaneously, before epitaxial growth step G, both surfaces of the wafer substrate having been completed the chamfering step D. In this first double side polishing step E, each wafer substrate is interposed between upper and lower polishing surface plates of a double side polishing apparatus, to which hard polishing pads are attached, and both surfaces of the wafer substrate are simultaneously polished under the condition of no abrasive grains or using free abrasive grains. The polishing amount in this first double side polishing step E is 5 to 30 μm, for example. This first double side polishing step E further improves the flatness of wafer substrates. This first double side polishing step E preferably involves polishing under the condition of no abrasive grains thereby allowing damages to be suppressed during the subsequent epitaxial growth. Such a damage control is significant for the integrity of epitaxial layer, and damages, if remain, contribute to stacking faults.
For the epitaxial growth step G, before supplying reactive gases into an epitaxial reactor furnace in which wafer substrates are set, halogenated gas is supplied into the reactor furnace to remove oxidized films having formed on the surface of the wafer substrates (etching step F). Note that, alternatively to the method of etching by supplying halogenated gas into the epitaxial reactor furnace, a wet etching step may be provided in which etching liquid for the oxidized films is dropped onto the wafer substrates.
In the epitaxial growth step G, the wafer substrates are set on susceptors in the epitaxial reactor furnace and the reactive gases are supplied thereby to form epitaxial layers on the surface of the wafer substrates.
Wafer substrates having formed thereon with epitaxial layers are sent to second double side polishing step H to be subjected to final polishing. The second double side polishing step H according to the present embodiment is comprised of double side simultaneous polishing step H1 and subsequent single side mirror polishing step H2.
In the double side simultaneous polishing step H1, it is preferred to use a double side polishing apparatus and a polishing method as shown in
The polishing apparatus shown in
The lower polishing surface plate 1 is rotatively driven by a motor 11. The upper polishing surface plate 2 is suspended from a cylinder 5 via a joint 6 to be rotatively driven in the opposite direction by another motor (not shown) different from the motor 11. In addition, a polishing liquid supply system is provided, which includes a tank 7 for supplying polishing liquid between the lower polishing surface plate 1 and itself . The sun gear 3 and the internally-toothed gear 4 are also independently driven by still another motor 12 different from the motors for driving the polishing surface plates.
Facing surfaces of the lower polishing surface plate 1 and the upper polishing surface plate 2 are, as shown in
As shown in
When performing the polishing of wafer substrates 10, in the status where the upper polishing surface plate 2 is lifted up, a plurality of carriers 8 are set on the lower polishing surface plate 1 and the wafer substrates 10 are set into holes 9 of each carrier 8. The upper polishing surface plate 2 is then caused to move down to apply a predetermined pressing force to each wafer substrate 10. In this status, while supplying polishing liquid between the lower polishing surface plate 1 and the upper polishing surface plate 2, the lower polishing surface plate 1, the upper polishing surface plate 2, the sun gear 3, and the internally-toothed gear 4 are caused to rotate in predetermined directions with predetermined speeds.
This allows a sun-and-planet motion to run where the plurality of carriers 8 revolve around the sun gear 3 while each rotating between the lower polishing surface plate 1 and the upper polishing surface plate 2. The wafer substrates 10 held by each carrier 8 are contacted and rubbed with the abrasive clothes 15 and 25 in the polishing liquid, and both the upper and the lower surfaces are simultaneously polished. Polishing conditions are set such that both surfaces of each wafer substrate 10 are evenly polished and the plurality of wafer substrates 10 is evenly polished.
During the polishing, the torque of the motor 11 for driving the lower polishing surface plate 1 or the torque of the motor for driving the upper polishing surface plate 2 is monitored. Thereafter, when the monitored torque decreases from a stable value by a predefined fraction, such as 10% thereof, the upper polishing surface plate 2 is lifted up to complete the polishing. This allows the finally obtained thickness of the wafer substrates 10 to be accurately and stably controlled as being slightly thinner than or equal to the carrier thickness before polishing.
The carriers 8 possibly deteriorate due to the friction with the abrasive clothes 15 and 25 attached to the polishing surface plates 1 and 2, and therefore, the material for each carrier 8 is preferred to be a material which has a small friction coefficient with respect to the abrasive clothes 15 and 25 thereby to be of high anti-abrasion property, and of which the chemical resistance property is high in alkali polishing liquid of pH 8 to 12. As carrier materials fulfilling such requirements, stainless-steels, or FRPs obtained by combining resins, such as epoxy resin, phenol resin, polyimide resin, etc, with reinforcement fibers, such as glass fiber, carbon fiber, aramid fiber, etc, may be mentioned. In addition, the carriers 8 may have a certain degree of strength because they are used to hold the wafer substrates 10.
The three holes 9 of each carrier 8 according to the present embodiment are arranged such that centers C9 thereof are positioned on a circle P as being concentric with the carrier 8 and also arranged along the circle P with equal intervals so as to be in a rotative point-symmetric fashion with respect to the center CP of the circle P (the center of the carrier 8).
Moreover, the size of the hole 9 is determined such that the area ratio of the circle P passing through the centers C9 of the holes 9 to each hole 9 substantially equal to the wafer substrate 10 is 1.33 or more and less than 2.0, and more preferred is 1.33 or more and 1.5 or less. That is, the radius R of the circle P and the radius r of the holes 9 are set to satisfy the expression below.
1.33≦(R/r)2≦1.5
Note that the lower limit of the defined range of this area ratio (square of the radius ratio) may be 1.3333 . . . or more, and may also be 1.334 or more.
If, in the carrier 8, the area ratio of the circle P passing through the centers C9 of the holes 9 to each hole 9 is less than the above range, then only two holes 9 are allowed to be provided in one carrier 8, and the processing of the wafer substrates 10 treated in the same carrier 8 may not thus be even, so that no advantageous effect for preventing edge-roll-off of the wafer substrates 10 is obtained, thereby not being preferred. Moreover, if the upper limit of that area ratio is set as being 2 or more when the holes 9 at three locations are provided in one carrier 8, then the distances among the wafer substrates 10 come to be too long, so that no advantageous effect for preventing edge-roll-off of the wafer substrates 10 is obtained, thereby not being preferred. Furthermore, if the upper limit of the area ratio is set as being 2 or more when the holes 9 at four locations or more are provided in one carrier 8, then the stress concentration may not be sufficiently distributed, so that no advantageous effect for preventing edge-roll-off of the wafer substrates 10 is obtained, thereby not being preferred. In addition, although the edge-roll-off may be prevented if the upper limit of the area ratio is set as being more than 1.5 and less than 2, it is more preferred to set the ratio as being 1.5 or less in order to obtain flatness sufficient to be product wafers.
Note that the dimensions of the wafers 10 and the holes 9 are to be substantially the same, for example, the diameter of the holes 9 is 201 mm for the wafer substrates 10 of 9200 mm, and the diameter of the holes 9 is 302 mm for the wafer substrates 10 of 9300 mm.
According to the present embodiment, the wafer substrates 10 are subjected to double side polishing using the carriers 8 formed therein with the holes 9 as described above to prevent edge-roll-off from occurring in the wafers 10 thereby to allow for producing polished wafers with high degree of flatness.
In the conventional polishing technique which involves a polishing step using carriers 8 thinner than wafer substrates 10, pressures from the abrasive clothes 15 and 25 are concentrated at outer edges A of the wafer substrates 10, one of which is denoted by symbol A in
In contrast, according to the polishing method of the present embodiment, by closely arranging the holes 9 in the planar arrangement within each carrier 8 to concentrate the locations of the wafer substrates 10 toward the center of each carrier 8, as shown in
This is considered as being due to that the distances among the wafer substrates 10 are made smaller in the status of eliminating the influence from the deformation of carriers 8 caused by the wafer substrates 10 during polishing, etc. Consequently, the concentration of polishing pressures from the abrasive clothes 15 and 25 on the surfaces of the polishing surface plates 1 and 2 to the wafer substrates 10 is suppressed from occurring in the vicinity of the position where adjacent wafer substrates 10 come to be most close to each other.
During operation of the polishing, at the position between a wafer substrate 10 and another wafer substrate 10, due to the difference in thickness between the wafer substrates 10 and the carrier 8, a status is provided where the abrasive clothes 15 and 25 on the surfaces of the polishing surface plates having flexibility are deformed to outstand toward the carrier 8 from the height (the position in the thickness direction) at the planar position of each wafer substrate 10. For this reason, the pressures from the abrasive clothes 15 and 25 may be concentrated at edge portions of the wafer substrates 10 thereby to increase the polishing amount at the edge portions of the wafer substrates 10.
According to the polishing method of the present embodiment, however, as shown in
This enables to easily and appropriately perform the polishing to a predetermined amount and to easily perceive the ending point of polishing, and to avoid the polishing pressure degradation to the wafer substrates 10 due to the decreasing of the pressure from the polishing surface plates to the carriers 8 even if during the latter half of the polishing step thereby to prevent the operation time efficiency/polishing efficiency from deteriorating, and also prevents the carriers 8 from being polished thereby to obtain long life-time thereof , and additionally avoids the flatness deterioration and the like by preventing the occurrence of edge-roll-off thereby enabling to produce the wafer substrates 10 having high flatness.
Moreover, during the polishing operation, in the vicinity of the border, as the outer edge portion of each wafer substrate 10, between the wafer substrate 10 and the carrier 8, due to the difference in thickness between the wafer substrate 10 being polished and the carrier 8, the abrasive clothes 15 and 25 on the surfaces of the polishing surface plates having flexibility are deformed to outstand toward the carrier 8 from the height (the position in the thickness direction) at the planar position of the wafer substrate 10. Consequently, the pressures from the abrasive clothes 15 and 25 may be concentrated in the vicinity of the edge portion of the wafer substrate 10 along the entire length of the outer edge portion of the wafer substrate 10, thereby to possibly cause the occurrence of the edge-roll-off of the wafer substrate 10.
According to the polishing method of the present embodiment, however, through decreasing the distances among the wafer substrates 10 to be subjected to the double side polishing and causing the wafer substrates 10 to be close to one another, it is enabled to approach the status where the wafer substrates 10 placed in three holes 9 within one carrier 8 are polished as if they are of one wafer substrate 10. This allows to limit the length where the stress concentration occurs relative to the entire outer edge length of one wafer substrate 10, that is, to reduce the area where the polishing condition within the outer edge portion of the wafer substrate 10 becomes to be significant because the pressures from the abrasive clothes 15 and 25 on the surfaces of the polishing surface plates 1 and 2 having flexibility are concentrated at the outer edge portion of the wafer substrate 10 due to the difference in thickness between the wafer substrate 10 and the carrier 8. Consequently, the polishing pressure concentration is allowed to be alleviated for the entire length of the edge portion of one wafer substrate 10 at the time of completing the polishing, and the occurrence of the edge-roll-off along the outer edge portion of each wafer substrate 10 is also allowed to be reduced, while polishing to the extent of allowing the damages and the depositions on the back surface to be removed.
Although the depicted example employs the configuration involving three carriers 8, other number thereof may also be applicable, and other than this, any configuration of a part of the polishing apparatus may also be applicable so long as the arrangement of the holes 9 or the wafer substrates 10 within each carrier 8 complies with the above structure.
Referring again to
In the subsequent single side mirror polishing step H2, the front surface of the wafer substrate is subjected to a mirror polishing. The polishing amount in the mirror polishing is, for example, 0.01 to 0.2 μm.
As described above, according to the method for producing a silicon epitaxial wafer in the present embodiment, the flatness of each wafer substrate is ensured, as shown in
At the same time, the double side simultaneous polishing step H1 after the epitaxial growth may remove, as shown in
Furthermore, the double side simultaneous polishing step H1 after the epitaxial growth allows the polishing amount of the wafer surfaces to be small as much as possible to the extent of removing an oxidized layer on the front surface, thereby maintaining the thickness of the epitaxial layer on the front surface to be even.
It is to be noted that the embodiments as explained above are described to facilitate understanding of the present invention and are not described to limit the present invention. Therefore, it is intended that the elements disclosed in the above embodiments include all design changes and equivalents to fall within the technical scope of the present invention.
Hereinafter, the above invention will be described with reference to further specified examples and comparative examples.
Through Czochralski pulling up method, a p-type silicon single crystal ingot was produced as having the main axis orientation of <100> and the diameter of 305 mm, and this ingot was peripherally ground into the diameter of 300 mm and then subjected to notch forming thereafter being cut into blocks with resistivity of 5 to 10 mΩcm. Each of these blocks was sliced using a wire saw to provide wafer substrates with a certain thickness.
The wafer substrates were interposed between upper and lower grinding surface plates of a double side grinding machine, and both surfaces, i.e. the front surface and the back surface of each wafer substrate were ground while supplying slurry containing abrasive grains (the lapping step B shown in
The wafer substrates ground in the above manner were interposed between upper and lower polishing surface plates of a double side polishing apparatus, to which hard polishing pads were attached, and both surfaces of the wafer substrates were simultaneously polished to 12 μm under the condition of no abrasive grains (the first double side polishing step (rough polishing) E in
Then, before supplying reactive gases into an epitaxial reactor furnace in which wafer substrates completed with the first double side polishing step E were set, halogenated gas was supplied into the reactor furnace to remove oxidized films formed on the surfaces of the wafer substrates (etching step F in
Thereafter, the wafer substrates formed thereon with epitaxial layers were set into the holes 9 of the carriers 8 of the double side polishing apparatus as shown in
Finally, the front surfaces of wafer substrates were mirror polished (the single side mirror polishing step H2 in
Among the above steps, the flatness (using partial sites for SFQR) was measured each after the first double side polishing step E, after the epitaxial growth step G, after the double side simultaneous polishing step H1, and after the single side mirror polishing step H2, and results thereof are shown in
Partial sites for the flatness SFQR are intended to mean imperfect sites (sites of not being rectangular) due to that the wafer is circular, when one wafer surface is sectioned into sites of 25 mm×25 mm square shapes or 26 mm×8 mm rectangular shapes, for example. In this example, about fifty partial sites arose when sectioning the area of a 300 mm wafer except for the edge portion of 3 mm into 26 mm×8 mm rectangular sites.
When haze levels at the surfaces of epitaxial layers of the wafer substrates completed with the single side mirror polishing step H2 were tested at DWO mode (Dark Field Wide Oblique mode) using Unpatterned Wafer Surface Inspection System: trade name (model: Surf scan SP2) available from KLA-Tencor Corporation, they were 0.09 ppm (corresponding to 33 nm as SP2 detectable minimum particle diameter) . In contrast, haze levels after the epitaxial growth step G were 0.3 ppm (corresponding to 39 nm as SP2 detectable minimum particle diameter), and good haze levels were thus confirmed.
For comparison to the above Example 1, wafer substrates were prepared through steps in which the front surfaces of wafer substrates were mirror polished after the first double side polishing step (rough polishing) E in
The flatness (using partial sites for SFQR) was measured each after the mirror polishing prior to the epitaxial growth step, after the epitaxial growth step G, and after the mirror polishing subsequent to the epitaxial growth step, and results thereof are shown in
From the results of
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-113157 | May 2009 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2010/057795 | 5/7/2010 | WO | 00 | 1/5/2012 |