Patent Grant
7967969
The present invention pertains to methods and apparatus for electroplating metal onto a work piece. More specifically, the invention pertains to methods and apparatus for controlling the electrical resistance and current flow characteristics in an electrolyte environment encountered by the work piece during electroplating.
The transition from aluminum to copper required a change in process “architecture” (to damascene and dual-damascene) as well as a whole new set of process technologies. One process step used in producing copper damascene circuits is the formation of a “seed-” or “strike-” layer, which is then used as a base layer onto which copper is electroplated (“electrofill”). The seed layer carriers the electrical plating current from the edge region of the wafer (where electrical contact is make) to all trench and via structures located across the wafer surface. The seed film is typically a thin conductive copper layer. It is separated from the insulating silicon dioxide or other dielectric by a barrier layer. The seed layer deposition process should yield a layer which has good overall adhesion, excellent step coverage (more particularly, conformal/continuous amounts of metal deposited onto the side-walls of an embedded structure), and minimal closure or “necking” of the top of the embedded feature.
Market trends of increasingly smaller features and alternative seeding processes drive the need for a capability to plate with a high degree of uniformity on increasingly thin seeded wafers. In the future, it is anticipated that the seed film may simply be composed of a plate-able barrier film, such as ruthenium, or a bilayer of a very thin barrier and copper (deposited, for example, by an atomic layer deposition (ALD) or similar process). These films present the engineer with an extreme terminal effect situation. For example, when driving a 3 amp total current uniformly into a 30 ohm per square ruthenium seed layer (a likely value for a 30-50 Å film) the resultant center to edge voltage drop in the metal will be over 2 volts. To effectively plate a large surface area, the plating tooling makes electrical contact to the conductive seed only in the edge region of the wafer substrate. There is not direct contact made to the central region of the substrate. Hence, for highly resistive seed layers, the potential at the edge of the layer is significantly greater than at the central region of the layer.
where n is the total number of parallel paths that the circuit is divided into, i (sometime used as a subscript) refers to the ith parallel current path (from the edge terminal), t refers to the total circuit, I is current, Rf is the resistance in the metal film between each element (constructed, for simplicity, to be the same between each adjacent element), Rct is the local charge transfer resistance, Zw is the local diffusion (or Warberg) impedance and Rel is the electrolyte resistance. With this, Ii is the current to through the ith surface element pathway, and It is the total current to the wafer. The charge transfer resistance at each interfacial location is represented by a set of resistors Rct in parallel with the double layer capacitance Cdl, but for the steady state case does not effect the current distribution. The diffusion resistances, represented by the Warberg impedance (symbol Zw) and the electrolyte resistance (Rel) are shown in a set of parallel circuit paths, all in series with the particular surface element circuit, give one of several parallel paths for the current to traverse to the anode. In practice, Rct and Zw are quite non-linear (depending on current, time, concentrations, etc.), but this fact does not diminish the utility of this model in comparing how the current art and this disclosure differ in accomplishing uniform current distribution. To achieve a substantially uniform current distribution, the fractional current should be the same, irrespective of the element position (i). When all terms other than the film resistance term, Rf, are relatively small, the current to the ith element is
Equation 2 has a strong i (location) dependence and results when no significant current distribution compensating effects are active. In the other extreme, when Rct, Zw, Rel or the sum of these terms are greater than Rf, the fractional current approaches a uniform distribution; the limit of equation 1 as these parameters become large is F=1/n, independent of location i.
Classical means of improving plating non-uniformity draw upon (1) increase Rct through the use of copper complexing agents or charge transfer inhibitors (e.g., plating suppressors and levelers, with the goal of creating a large normal-to-the-surface voltage drop, making Rf small with respect to Rct) or (2) very high ionic electrolyte resistances (yielding a similar effect through Rel), (3) creating a significant diffusion resistance (Zw), variations of plating current recipe to minimize voltage drop, or control of mass transfer rate to limit current density in areas of high interfacial voltage drop (U.S. Pat. Nos. 6,110,344; 6,074,544; 6,162,344).
These approaches have significant limitations related to the physical properties of the materials and the processes. Typical surface polarization derived by organic additives cannot create polarization in excess of about 0.5V (which is a relatively small value in comparison to seed layer voltage drop that must be compensated). Also, because the conductivity of a plating bath is tied to its ionic concentration and pH, decreasing the conductivity directly and negatively impacts the rate of plating and morphology of the plated material.
Beyond these classical approaches, a few newer approaches have been pursued to address the terminal effect problem. One class alters the effective ionic path resistance Rel for different current path elements (i.e., it provides a non-uniform Rel in the radial direction) in order to balance the resistance in the film with that external to the film as discussed in U.S. Pat. Nos. 6,126,798; 6,569,299; and 6,179,983 Some current shielding and concentric multiple anode source approaches fall into this solution class. See U.S. Pat. No. 6,773,571 issued to Mayer et al. on Aug. 10, 2004 and U.S. Pat. No. 6,402,923 issued to Mayer et al. on Jun. 11, 2002, both of which are incorporated herein by reference for all purposes. Another class utilizes a time averaging exposure effect (for example, with a rotating wafer and a current shield element) to, over time, plate the same thickness at all locations. In other words, the plating current is modified according to the time-averaged exposure that a rotating wafer “sees” the anode with a mask of a certain shape and size covering the work piece during a portion of the rotational period. See U.S. Pat. No. 6,027,631 issued to Broadbent et al. on Feb. 22, 2000 and U.S. application Ser. No. 10/916,374, naming Steven T. Mayer as inventor, filed Aug. 10, 2004, titled “UNIFORM ELECTROPLATING OF THIN METAL SEEDED WAFERS USING ROTATIONALLY ASYMMETRIC VARIABLE ANODE CORRECTION,” which are incorporated herein by reference for all purposes.
While the approaches discussed above have proven useful, they have potential limitations such as (1) the inability to continuously (throughout the process) change the resistance compensation as appropriate when the thickness of the plated layer grows and thereby reduces the electronic resistance, (2) a high cost of implementation, and/or (3) mechanical limitations (e.g., excess number of moving parts in a corrosive bath, material compatibility limitations, or reliability). Furthermore, the above approaches are not all easily adaptable/integrateable to particularly desirable apparatus configurations such as microcell configurations, a newly developed and desirable class of plating cells. See U.S. Patent Publication No. 2004/0065540 (Mayer et al.), titled “Liquid Treatment Using Thin Liquid Layer,” and published Apr. 8, 2004, which is incorporated herein by reference for all purposes. See also U.S. patent application Ser. No. 10/739,822, naming Steven T. Mayer, et al. as inventors, filed Dec. 17, 2003, titled, “METHOD FOR PLANAR ELECTROPLATING,” which is also incorporated herein by reference for all purposes.
What is needed therefore is an improved technique for uniform electroplating onto thin-metal seeded wafers, particularly wafers with large diameters (e.g. 300 mm).
The present invention pertains to methods and apparatus for electroplating a substantially uniform layer of a metal onto a work piece having a seed layer thereon. This invention mitigates or eliminates the terminal problem by placing an ionically resistive element (e.g., a microporous ceramic or fretted glass membrane) in close proximity to the work piece, thereby swamping the system's resistance. The resistive element thus approximates a constant current source. By keeping the work piece close to the resistive element surface, the ionic resistance from the top of the element to the surface is much less than the ionic path resistance to the work piece edge, substantially compensating for the sheet resistance in the thin metal film and directing a significant amount of current over the center of the work piece. The deposition profiles thus obtained are smoother than those obtained by other approaches (monotonic), and as the film thickens, the system naturally (without changing power settings or moving elements) leads to a progressively more uniform current distribution. This approach provides an improved deposition profile without significantly increasing overall system resistance. The combination of a resistive element with either a shielding member, located under the membrane, or a set of dynamically operable anodes with focusing elements leading up to the bottom of the membrane, and/or a rotationally asymmetric anode approach, allows additional control over the center to edge deposition profiles and dynamic control.
One aspect of the invention provides methods of electroplating a substantially uniform layer of metal onto a thin conductive seed layer of a work piece surface having edge regions around a center region. The method may be characterized by the following operations: (a) making electrical connection to the seed layer at one or more locations on the edge regions, but not at the center region; (b) positioning the work piece in a plating cell having an ionically resistive porous membrane substantially co-extensive with the seed layer; and (c) delivering current through the plating cell via the electrical connections to the seed layer. The resistive membrane is oriented to have one surface facing the work piece surface and an opposite surface facing an anode in the plating cell, such that the surface to be plated is located within about 5 millimeters or less of the porous membrane. In this arrangement, the membrane introduces a circuit resistance in an ionic current path of the plating cell, which compensates for a potential drop in the seed layer between edge regions and the center regions to thereby promote uniform plating across the seed layer on the work piece surface.
Preferably, the membrane has a porosity of between about 0.5% and 25%, more preferably about 5% or less. As indicated the membrane may be placed in close proximity to the work piece, preferably within about 1 to 5 millimeters. The distance may scale with the size of the work piece to be plated. For example, when the surface of the work piece is substantially flat and circular (e.g., a semiconductor wafer), and the surface may separated from the membrane by a distance of not greater than about 5% (more preferably about 2%) of the diameter of the work piece's circular region.
Preferably, the thickness of the porous membrane is between about 5 and 25 millimeters. Of course, this thickness depends upon the porosity, location and material of construction for the membrane. In certain embodiments, the thickness should be chosen so that the membrane does not increase the overall ionic resistance in the plating cell beyond that needed to obtain the desired level of uniformity. In one example, the presence of the porous membrane increases the ionic resistance between the anode and the work piece by no more than about 5 ohms when the work piece is a 200 or 300 millimeter semiconductor wafer.
As indicated, the invention may be coupled with other approaches to controlling the plating deposition profile. For example, the current may be delivered through two separate anode segments, controlled independently of one another. In one embodiment, these are arranged concentrically with respect to one another. In another embodiment, at least one anode segment is azimuthally asymmetric with respect to the work piece surface. In yet another approach, the plating cell comprises an iris positioned to restrict ionic current proximate the edge regions of the work piece surface.
Another aspect of the invention pertains to apparatus for electroplating a substantially uniform layer of metal onto a conductive seed layer of a work piece surface having edge regions around a center region. The apparatus may be characterized by the following features: (a) a plating chamber; (b) a work piece holder for holding the work piece in the plating chamber at a position in alignment with an anode; (c) electrical contacts arranged to make electrical connection to the seed layer at one or more locations on the edge regions; and (d) an ionically resistive porous membrane positioned to have one surface facing the work piece surface, and located within about 5 millimeters of said work piece surface, and an opposite surface facing the anode during plating in the plating chamber.
These and other features and advantages of the present invention will be described in more detail below with reference to the associated drawings.
This invention relates to electroplating methods and apparatus for use in integrated circuit (IC) fabrication and other applications. More specifically it relates to the use a resistive ion current source hardware set and process. Generally, the technology employs a low porosity membrane or other barrier to ionic conductivity located between the anode and the work piece, with the membrane positioned in close proximity to the plating surface, typically separated by about 1 to 5 mm. This use of a resistive membrane compensates for the preferential edge plating associated with electrical resistance and voltage drop across the wafer by adding a large circuit resistance to the ionic current path. The approach is designed to gives adequate uniformity at the beginning of the process (when the wafer film resistance is highest). As the metallic film is plated, the sheet resistance of the film decreases and the plating rate uniformity improves.
The apparatus and processes of this invention enable a simple, low cost, reliable method for the production of uniform electroplated film deposits on thin metal seeded work piece. More specifically, this invention enables superior uniformity control of work pieces having (1) very thin “seed” layers with sheet resistances of about 1 ohm/sq or greater, (2) large diameters (e.g., 300 mm semiconductor wafers), (3) high feature densities (e.g., at least about 5000 features per cm), and (4) small feature sizes (e.g., average size of at most about 95 nm).
While the apparatus of this invention employs plating cells in which electrical contact is made in the edge region of the wafer substrate, it is not limited to any general class of plating apparatus. One suitable example is the SABRE™ clamshell electroplating apparatus available from Novellus Systems, Inc. of San Jose, Calif. and described in U.S. Pat. Nos. 6,156,167, 6,159,354, 6,193,859, and 6,139,712, and in U.S. patent application Ser. No. 10/010,954, filed Nov. 30, 2001, titled “Improved Clamshell Apparatus with Dynamic Uniformity Control,” each of which is herein incorporated by reference in its entirety. The invention is also applicable to plating hardware in which the anode or virtual anode (e.g., top of the membrane) and the wafer lay in close proximity to one another, such as in a “microcell” or “microgap” configuration. See e.g., U.S. Patent Publication No. 2004/0065540 (Mayer et al.), which was previously incorporated by reference.
In some embodiments, the invention combines the resistive membrane with another mechanism for compensating the terminal effect. For example, the inventive apparatus may employ set of concentric anodes or a dynamic movable iris to direct additional current to the center of the work piece. Other compensating mechanisms that may be employed together with the resistive membrane include dynamic shielding and rotationally asymmetric anodes. Use of these mechanisms allows one to “turn down” the compensation as the plated layer grows thicker and thereby reduces the terminal effect.
Various terms of art are used in this description of this invention. These terms should be construed broadly. Some relevant considerations follow.
For example, the invention is described in terms of electroplating on wafers, particularly semiconductor wafers undergoing damascene processing. However, the work piece is not limited to such wafers. The work piece may be of various shapes, sizes, and materials. In addition to semiconductor wafers, other work pieces that may take advantage of this invention include printed circuit boards, flat panel displays, and the like. In this document, the term “wafer” will be used interchangeably with “wafer substrate”, and “substrate.” One skilled in the art would understand that these terms could refer to a semiconductor (e.g. silicon) wafer during any of many stages of integrated circuit fabrication thereon.
Wafer Holder—A wafer holder generally describes a component that immobilizes a wafer and has positioning components for moving the wafer, e.g., rotation, immersion, and that has circuitry for applying an electrical potential to the wafer via a conductive layer thereon. An exemplary wafer holder is the Clamshell apparatus available from Novellus Systems, Inc. of San Jose, Calif. A detailed description of the clamshell wafer holder is provided in U.S. Pat. Nos. 6,156,167, 6,159,354, 6,193,859, and 6,139,712, each of which is incorporated herein by reference for all purposes. In a microcell reactor, a mechanical or vacuum chuck may be employed to hold the wafer. This is described in the above-referenced U.S. Patent Publication No. 2004/0065540.
Seed Layer—A seed layer generally refers to a thin conductive layer on a work piece through which current is passed to effect, for example, electroplating. Frequently, seed layers of the invention will be copper layers on wafers, however, the invention is not so limited. Layers of other materials such as ruthenium and some conductive barrier materials may be employed as well. The seed layer thickness is generally a function of the technology node being implemented. In many situations, the seed layer will have a thickness of between about 30 and 1000 Angstroms.
Plating Cell
The apparatus of this invention is not limited in use to a particular electroplating tool design or plating chemistry, though certain designs for the tool and chemistry are described herein. The porous membrane and plating chamber should be made of materials that are substantially resistance to corrosion or attack from the particular plating solution being used. But otherwise, many different designs may be employed.
Wafer holder 223 is capable of positioning wafer 221 in close proximity to the topmost portion of the focusing elements. Preferably the distance between the top surface of resistive member 227 and the wafer is about 10 millimeters or less during plating, more preferably about 1 to 5 millimeters. Preferably the walls of at least the anode chamber are between about 0.1 and 5 millimeters thick, more preferably between about 0.25 and 1 millimeters thick. Similar thickness ranges are appropriate for all the focusing element walls in the reactor.
Plating cells of the invention can include a variety other features not shown in
The anodes used with this invention can be of either an inert or consumable type. The reactions of the consumable type (also referred to as active anodes) for plating copper are simple and balanced (no overall depletion or generation of new species). Copper ions in solution are reduced at the cathode and removed from the electrolyte, simultaneously as copper is oxidized at the anode and copper ions added to the electrolyte. The inert type (also referred to as “dimensionally stable” and non-reactive) provides unbalanced reactions and copper ions (or ions of any other metal being plated) must be added to plating solution. Various electrolyte formulations may be employed in either reactor. In addition to a salt of the metal to be plated (e.g., copper sulfate), many electrolytes contain an acid such as sulfuric acid. Other additives conventionally used in electroplating may also be employed.
The design and placement of the resistive element in the plating cell should be chosen to balance at least two considerations: improved plating uniformity across the face of the work piece and minimal increase in overall resistance within the plating cell. The primary goal is to introduce ionic current resistance between the work piece and the anode in a manner that promotes more uniform current distribution across the work piece surface. This goal may be achieved by carefully choosing various membrane characteristics including the membrane porosity, materials of construction, membrane thickness, and placement with respect to the work piece.
Overall, the resistive element will be ionically conductive, but not nearly as conductive as the electrolyte itself. In some embodiments, the resistive element is constructed from a material that is an ionic insulator. In such embodiments, limited ionic conduction is provided by introducing pores into the element. In alternative embodiments, the resistive element is constructed from a porous or non-porous material that is itself a weak ionic conductor (e.g., “Naphion” from DuPont Corporation of Wilmington, Del.). In all cases, the element will allow passage of some ionic current, but does so only when introducing significant ionic resistance. Generally, the element is engineered to have an appropriate ionic resistivity (via porosity and thickness), and positioned to drive the effect (e.g., less than 5 mm separation from the work piece, depending on the solution resistivity and practical limitations). Examples of ionically resistive materials for use in the resistive elements include electrolyte filled microporous ceramic, sintered silica (fretted glass), inorganic or organic gels and aerogels and sintered plastics (e.g., “Porex” porous plastics available from Porex Corporation of Fairburn, Ga. Example of ionically conductive materials with substantially higher resistance than the plating solution resistance include “Naphion” and other similar proton exchange membranes. As indicated, the material should be compatible with the chosen electrolyte and should resist corrosion or other degradation over many hours of electroplating. In many embodiments, the material is a solid. But it may be present in other phases as well; e.g., as a gel.
If a porous resistive element is employed, the porosity should be set to a low enough value that the ionic resistance of the element is significant. The optimal porosity will depend on the type of material employed (i.e., ionic conductor or insulator), the number and extent of the tortuous paths of pores, as well as the thickness of the element. If a relatively thin element is employed, then the porosity should be kept low. The same is true when an ionic conductor is employed. That is, when the material used to construct the element is an ionic conductor, then the porosity should remain relatively low (in comparison to the case where the resistive element is constructed from an ionic insulator). Note that for ionic insulators, porosity may be determined by the fractional superficial conductance of the region occupied by the membrane with respect to the specific conductance of the electrolyte within the membrane. In a specific embodiment employing ionic insulators of about 5 to 30 millimeters in thickness, the porosity is about 2% to 10% (e.g., about 5%).
The thickness of the resistive element also affects its total ionic resistance. Thicker elements provide greater resistance for a given material and porosity. However, if the membrane is too thick it may become incompatible with the design of the plating cell. In some embodiments, the thickness of the element is preferably between about 5 millimeters and 30 millimeters. Obviously, the optimal thickness is dependent on other characteristics of the element (e.g., porosity and intrinsic conductivity) as well as the design of the plating cell.
Another important design parameter is the distance between the upper edge of the membrane and the work piece plating surface. For embodiments employing semiconductor wafers, the separation distance is preferably about 5 millimeters or less, more preferably about 1-5 millimeters. In another characterization, the separation distance is preferably less than about 5% of the wafer diameter, more preferably less than about 2% of the wafers diameter (e.g., less than about 6 mm below the wafer for a 300 mm wafer).
While the ionically resistive element, when properly placed, can lead to significant improvements in current distribution, various physical and process constraints may limit its application. For example, it may be desirable to use higher currents once some film has been plated, and if the membrane is too thick/resistive, the power or voltage required and/or the heat generated could be prohibitive. When this is the case, a thinner and/or less resistive membrane may be employed in conjunction with an additional compensation mechanism. Examples of these additional mechanisms include shielding elements and anodes designed to deliver additional current to the center region of the work piece.
One anode design that can be used for this purpose employs multiple anode segments, each of which can be separately controlled. The anode segments can be arranged so that greater current levels are provided from segments located proximate the center of the work piece. Concentrically arranged anode segments provide this capability. See U.S. Pat. No. 6,773,571 issued Aug. 10, 2004, which was previously incorporated by reference. In another embodiment, an azimuthally asymmetric anode is employed. The work piece rotates with respect to the anode to produce a time averaged current source that provides higher currents to the center of the work piece than to the edge regions. Examples of this apparatus are depicted in U.S. patent application Ser. No. 10/916,374 filed Aug. 10, 2004 by Mayer et al. and titled “Uniform Electroplating Of Thin Metal Seeded Wafers Using Rotationally Asymmetric Variable Anode Correction” which is incorporated herein by reference for all purposes.
Shielding mechanisms provide mechanisms for selectively modulating the electric field between the anode and the work piece to control or adjust the electrodeposition rate across the plating face of the work piece surface. Shield elements are made from non-conductive materials that are resistant to the plating electrolyte. Examples include polyolefins, fluoropolymers, etc. One approach employs an insulating iris that blocks passage of all ionic current in a region of the plating cell immediately beneath the periphery of the work piece surface. Such mechanisms are described in U.S. Pat. No. 6,402,923, previously incorporated by reference. Other approaches to shielding employ asymmetric elements that rotate with respect to the work piece to provide a time average current distribution that focuses additional current toward the center of the work piece as described in U.S. Pat. No. 6,027,631, previously incorporated by reference.
In the concentric anode embodiment, the anodes are preferably in close proximity to the membrane (preferably within a distance of about 5% or less of the wafer diameter, more preferably about 2% or less), or are accompanied by electrically and ionically insulating focusing cylinders that mate with the lower surface of the membrane. When an inner anode is then energized, current is preferentially directed to the center and cannot leak to the edge through a low resistance path. Current reaching the edge regions must either first transverse through the membrane and the through the electrolyte gap between the membrane and the wafer to the edge, or alone an angular lengthy path through the membrane. In one specific example, the plating cell provides a total system current of 6.9 A and has an inner anode 6.3 cm in radius, which initially supplies all the cell current from 100 mm below the wafer. The center cylinder in this case is 60 mm high, and is directing all its current up to the wafer 40 mm from the top of the cylinder.
Current can be distributed between a plurality of anodes so that metal is deposited uniformly onto wafer 221. Initially, compensating for the terminal effect when the seed layer is thin, the current is distributed disproportionately so that inner area A of the wafer receives a larger fraction of the current in the electrolyte resulting from the potential applied to an anode (or anodes) proximate to the inner region. As the plated layer thickens and the terminal effect lessens, the plating current can be redistributed between the anodes.
In this example, anodes 425 and 427 are positioned in the bottom of vessel 213 such that there is sufficient space for focusing cylinders 429 and 431. Focusing elements such as these cylinders are effective in aiding methods of shaping current density in the electrolyte. The focusing elements provide “virtual” current sources or “virtual anodes” at the cylinder openings, which are mathematically and physically similar to having an actual anode located at the cylinder openings. Preferably focusing cylinders of the invention are made, at least in part, of insulative materials. Preferred insulative materials include at least one of plastic, nanoporous ceramic, and glass.
Inner focusing cylinder 429 is used to focus current in electrolyte 215 arising from closure of the cell circuit between the cathode (seed layer 219) and inner anode 425 (region A′ in the electrolyte). Region A′ is a cylindrical space spanning the distance between the work surface of inner anode 425 and seed layer 219. The inner diameter of the topmost portion of inner focusing cylinder 429 defines the area of a circular opening that is the virtual anode corresponding to anode 425. The area of a cross section of region A′ in the electrolyte approximately corresponds to the area of inner region A on the wafer surface (see
Wafer holder 223 is capable of positioning wafer 221 in close proximity to the topmost portion of the inner focusing cylinder. Preferably the distance between the topmost portion of the inner focusing cylinder and the wafer is preferably between about four and ten times the thickness of the inner focusing cylinder walls during plating. Within that separation distance, resistive membrane 227 resides.
Outer focusing cylinder 431 is used (in conjunction with cylinder 429) to focus current in electrolyte 215 arising from closure of the cell circuit between the cathode (seed layer 219) and outer anode 427 (region B′ in the electrolyte). Region B′ is a cylindrical space spanning the distance between the work surface of outer anode 427 and seed layer 219 (minus the space encompassed by region A′ and inner focusing cylinder 429). The inner diameter of the topmost portion of outer focusing cylinder 431 and the outer diameter of inner focusing cylinder 429 define the area of an annular opening that is the virtual anode for anode 427. Preferably the outer focusing cylinder has an inner diameter at its topmost portion (aperture) that approximates the diameter of the wafer being plated. Thus the area of a cross section of region B′ in the electrolyte approximately corresponds to the area of outer region B on the wafer surface (see
In this example, the inner focusing cylinder and outer focusing cylinder are of different height, that is, their topmost portions (which define the virtual anodes as described above) are different distances away from the seed layer during plating. Also they have walls of different thickness. This is only one example. The height of the inner and outer focusing cylinders and their respective wall thicknesses can be the same or different.
In the example described in relation to
Initially, to provide a large fraction ionic current to the central region of the work piece (proximate the rotational axis), only asymmetric anode 503 is energized and provides current. The regions of assembly 501 occupied by segments 505, 507, and 509 do not provide any significant current during this initial phase of the plating process when the terminal effect is most severe. At any given instant in time, a relatively large section of the work piece periphery is not located over top of anode 503 (or otherwise aligned with any portion of anode 503). Of course, as the work piece rotates, any given point on its periphery comes over the region of anode 503 and then passes beyond it. Because a relatively large segment of the work piece periphery is out of “contact” with anode 503 at any instant in time, while much more of the central regions remains in contact, the driving force for plating from anode 503 is non-uniformly distributed over the radius of the work piece. This compensates for the terminal effect. As the plated layer grows, and the terminal effect decreases, the other anode segments can be turned on gradually.
The asymmetric anode is shaped to yield a particular time-of-exposure correction to the current distribution. As shown in the example of
As shown in
In this example, anodes 525 and 527 are positioned in the bottom of vessel 213 such that there is sufficient space for vertical focusing element wall(s) 529 and an anode chamber wall 231. Anode chamber wall 529 defines a partially closed region for at least some of the focusing elements of anode segments in the anode assembly. A focusing element for the primary asymmetric anode 525 is used to focus current in electrolyte 215. Region A′ is an asymmetric space spanning the distance between the work surface of anode 525 and seed layer 219. Region B′ is a similar asymmetric space associated with secondary anode 527.
Preferably the work surface areas of the virtual anodes of the invention are aligned to the work surface of the seed layer on which metal is deposited to thereby provide a relatively direct current path between the anode and the work piece. In practice this means that the rotational axes or center points of the anode and work piece should be substantially aligned and the planes defined by these electrodes should be substantially parallel. Further, the outer perimeters and areas of these electrodes (possibly as traced during a single rotation) are preferably substantially similar. As indicated, the ionically resistive layer is located between the work piece and any actual or virtual anodes.
As mentioned, another compensation mechanism for the terminal effect employs a shield (or iris). It has been found that an iris acts in a generally similar fashion to the concentric anode design, but with a little less center current, a larger current excursion up to the iris edge, and then no current at all flowing over most of the iris shielded area right up the wafer edge. In a specific embodiment, a 3 inch diameter iris (3 mm thick) is located at 8 mm in front of the wafer. The presence of the iris prevents current from entering the membrane through that interface. But by creating a small gap between the resistive membrane and the iris shield, some current slips into this resistive gap and redistributes favorably (as indicated in an example discussed below).
Method
In certain applications (most notably IC fabrication), the work piece is substantially flat and circular, and it is located in the plating cell such that its surface is separated from the membrane by a distance of not greater than about 5% of the diameter of the work piece's circular region (more preferably not greater than about 2%). Preferably the method and apparatus are designed such that the presence of the porous membrane increases the ionic resistance between the anode and the work piece by no more than about 10 ohms when the work piece is a 200 or 300 millimeter semiconductor wafer.
As indicated above, the operation of delivering current through the plating cell may involve delivering current through two separate anode segments, controlled independently of one another. The anode segments may be concentrically or non-concentrically arranged with respect to one another. Further the segments may be rotationally/azimuthally symmetric or asymmetric. Further the current distribution may be shaped by one or more shielding elements in addition to the porous membrane.
Case 1 in
In the next case, labeled as case 2, a 5 mm thick membrane (5% porosity) is placed 3 millimeters below and parallel to the wafer. Note that porosity is represented in these simulations as the fractional superficial conductance of the membrane region with respect to the specific conductance of the electrolyte within the membrane. In this case, the system resistance is increased to only about 1.23 ohm and the amount of center current (8%). Furthermore, the shape of the response curve for this case is generally monotonic, with more current in the radial regions from 60 mm and beyond. In this example, the anode potential was set to 8.5 V with respect to the cathode which yielded an average current of 6.875 A.
Increasing the thickness of the membrane to 25 mm (case 3 in
Note that, as one increases the distance between the membrane and the plated interface from 3 to 30 mm, the uniformity progressively worse, but the system resistance decreases only marginally, to 2.0 ohms. This situation is represented in case 4 in
As explained above, it may be desirable to employ multiple concentric anodes in conjunction with the resistive membrane. Case 5 in
Another method and means of accomplishing a similar effect is to use a dynamically variable field-shaping element placed below the membrane.
In a case 6, the cell had a 3 inch diameter iris opening placed between the resistive membrane and the anode, and touching the lower face of the membrane. The presence of the iris prevented current from entering the membrane through that interface.
In the simulations of cases 6 and 7, the iris was 3 mm thick and stationary, with the 3 inch diameter extending from the outer edge of the wafer (radial position 150 mm) inwardly to a radial position 3 inches toward center of the 150 mm edge. The membrane had 5% porosity and 25 mm thickness. Its top face was located 3 mm from the wafer plating surface. In both cases, the anode potential was set to 51 V, which yielded an average current of 6.875 A.
Although various details have been omitted for clarity's sake, various design alternatives may be implemented. Therefore, the present examples are to be considered as illustrative and not restrictive, and the invention is not to be limited to the details given herein, but may be modified within the scope of the appended claims.
This application is a division of U.S. patent application Ser. No. 11/040,359 (now U.S. Pat. No. 7,622,024, issued Nov. 24, 2009), naming Steven T. Mayer and Jonathan D. Reid as inventors, filed Jan. 20, 2005, and titled, “HIGH RESISTANCE IONIC CURRENT SOURCE,” which claims priority under 35 USC 119(e) from U.S. Provisional Application No. 60/580,433, naming Steven T. Mayer and Jonathan D. Reid as inventors, filed Jun. 16, 2004, and titled, “HIGH RESISTANCE IONIC CURRENT SOURCE,” which are herein incorporated by reference in their entirety. This application is related to U.S. patent application Ser. No. 10/318,497 (now U.S. Pat. No. 6,890,416, issued May 10, 2005), filed Dec. 11, 2002, naming Steven T. Mayer et al. as inventors, and titled, “COPPER ELECTROPLATING METHOD AND APPARATUS,” to U.S. patent application Ser. No. 09/706,272 (now U.S. Pat. No. 6,527,920, issued Mar. 4, 2003), naming Steven T Mayer et al. as inventors and titled “COPPER ELECTROPLATING METHOD AND APPARATUS,” to U.S. Provisional Application No. 60/203,432, naming Steven T Mayer et al. as inventors, filed May 10, 2000, and titled “METHODS, MATERIALS AND APPARATUS FOR IMPROVED COPPER ELECTROPLATING.” This application is also related to U.S. application Ser. No. 10/916,374 (now U.S. Pat. No. 6,919,010, issued Jul. 19, 2005), naming Steven T. Mayer as inventor, filed Aug. 10, 2004, titled “UNIFORM ELECTROPLATING OF THIN METAL SEEDED WAFERS USING ROTATIONALLY ASYMMETRIC VARIABLE ANODE CORRECTION.” Each of these patent documents is incorporated herein by reference for all purposes.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3652442 | Powers et al. | Mar 1972 | A |
| 3706651 | Leland | Dec 1972 | A |
| 3862891 | Smith | Jan 1975 | A |
| 4033833 | Bestel et al. | Jul 1977 | A |
| 4082638 | Jumer | Apr 1978 | A |
| 4240886 | Hodges et al. | Dec 1980 | A |
| 4272335 | Combs | Jun 1981 | A |
| 4304641 | Grandia et al. | Dec 1981 | A |
| 4389297 | Korach | Jun 1983 | A |
| 4409339 | Matsuda et al. | Oct 1983 | A |
| 4469564 | Okinaka et al. | Sep 1984 | A |
| 4545877 | Hillis | Oct 1985 | A |
| 4604177 | Sivilotti | Aug 1986 | A |
| 4604178 | Fiegener et al. | Aug 1986 | A |
| 4605482 | Shirgami et al. | Aug 1986 | A |
| 4696729 | Santini | Sep 1987 | A |
| 4828654 | Reed | May 1989 | A |
| 4906346 | Hadersbeck et al. | Mar 1990 | A |
| 4931149 | Stierman et al. | Jun 1990 | A |
| 4933061 | Kulkarni et al. | Jun 1990 | A |
| 4988417 | DeYoung | Jan 1991 | A |
| 5035784 | Anderson et al. | Jul 1991 | A |
| 5039381 | Mullarkey | Aug 1991 | A |
| 5096550 | Mayer et al. | Mar 1992 | A |
| 5146136 | Ogura et al. | Sep 1992 | A |
| 5156730 | Bhatt et al. | Oct 1992 | A |
| 5162079 | Brown | Nov 1992 | A |
| 5217586 | Datta et al. | Jun 1993 | A |
| 5316642 | Young, Jr. et al. | May 1994 | A |
| 5332487 | Young et al. | Jul 1994 | A |
| 5368711 | Poris | Nov 1994 | A |
| 5391285 | Lytle et al. | Feb 1995 | A |
| 5421987 | Tzanavaras et al. | Jun 1995 | A |
| 5443707 | Mori | Aug 1995 | A |
| 5472592 | Lowery | Dec 1995 | A |
| 5476578 | Forand | Dec 1995 | A |
| 5498325 | Nishimura et al. | Mar 1996 | A |
| 5516412 | Andricacos et al. | May 1996 | A |
| 5567300 | Datta et al. | Oct 1996 | A |
| 5723028 | Poris | Mar 1998 | A |
| 5935402 | Fanti | Aug 1999 | A |
| 6027631 | Broadbent | Feb 2000 | A |
| 6126798 | Reid et al. | Oct 2000 | A |
| 6132587 | Jorne et al. | Oct 2000 | A |
| 6179983 | Reid et al. | Jan 2001 | B1 |
| 6193860 | Weling | Feb 2001 | B1 |
| 6251255 | Copping et al. | Jun 2001 | B1 |
| 6368475 | Hanson et al. | Apr 2002 | B1 |
| 6391166 | Wang | May 2002 | B1 |
| 6391188 | Goosey | May 2002 | B1 |
| 6395152 | Wang | May 2002 | B1 |
| 6402923 | Mayer et al. | Jun 2002 | B1 |
| 6497801 | Woodruff et al. | Dec 2002 | B1 |
| 6527920 | Mayer et al. | Mar 2003 | B1 |
| 6755954 | Mayer et al. | Jun 2004 | B2 |
| 6773571 | Mayer et al. | Aug 2004 | B1 |
| 6821407 | Reid et al. | Nov 2004 | B1 |
| 6964792 | Mayer et al. | Nov 2005 | B1 |
| 7070686 | Contolini et al. | Jul 2006 | B2 |
| 7169705 | Ide et al. | Jan 2007 | B2 |
| 7622024 | Mayer et al. | Nov 2009 | B1 |
| 20020017456 | Graham et al. | Feb 2002 | A1 |
| 20020020627 | Kunisawa et al. | Feb 2002 | A1 |
| 20030029527 | Yajima et al. | Feb 2003 | A1 |
| 20030102210 | Woodruff et al. | Jun 2003 | A1 |
| 20070238265 | Kurashina et al. | Oct 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| 0037325 | Mar 1981 | EP |
| 59-162298 | Sep 1984 | JP |
| 09-53197 | Feb 1997 | JP |
| 20021316887 | Nov 2001 | JP |
| 2003-268591 | Sep 2003 | JP |
| 10-0707121 | Apr 2007 | KR |
| WO9941434 | Aug 1999 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20100032304 A1 | Feb 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60580433 | Jun 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11040359 | Jan 2005 | US |
| Child | 12578310 | US |