Patent Application
20140106502
1. Field of the Invention
The present invention relates to an object, a method, a manufacturing method, a process, a machine, manufacture, or a composition of matter. In particular, one embodiment of the present invention relates to a semiconductor device, a display device, a light-emitting device, a driving method thereof, or a manufacturing method thereof.
In this specification, a semiconductor device generally means a device which can function by utilizing semiconductor characteristics. Electro-optical devices, display devices, memory devices, semiconductor circuits, and electronic devices are in some cases included in semiconductor devices and in other cases include semiconductor devices.
2. Description of the Related Art
Attention has been focused on a technique for forming a transistor using a semiconductor layer (also referred to as a thin film transistor (TFT)). The transistor is applied to a wide range of electronic devices such as an integrated circuit (IC) or an image display device (display device). A silicon-based semiconductor layer is widely known as a semiconductor layer applicable to such a transistor. As another material, an oxide semiconductor layer is attracting attention.
For example, a transistor including an amorphous oxide semiconductor layer containing indium (In), gallium (Ga), and zinc (Zn) in a channel formation region is disclosed (see Patent Document 1).
In a transistor including an oxide semiconductor layer serving as a channel formation region, an oxygen vacancy (also referred to as an oxygen defect) is generated by release of oxygen from the oxide semiconductor layer, and a carrier is generated owing to the oxygen vacancy. It is known that, to solve the above problem, oxygen released from a silicon oxide film containing excess oxygen is supplied to the oxide semiconductor layer to fill the oxygen vacancy in the oxide semiconductor layer, whereby a highly reliable semiconductor device with small change in electrical characteristics can be provided (see Patent Document 2).
In order to achieve high-speed operation, low power consumption, or high integration of a transistor including an oxide semiconductor layer, it is becoming more necessary to miniaturize the transistor. For example, high-speed operation of the transistor can be achieved by shortening the channel length.
However, short channel length of a transistor causes a decrease in threshold voltage, an increase in leakage current, or the like. This is because an electric field of a drain reaches the vicinity of a source when the channel length is short.
In view of the above problem, an object is to provide stable electrical characteristics and high reliability for a miniaturized semiconductor device or the like including an oxide semiconductor layer. Another object is to provide a miniaturized semiconductor device or the like. Another object is to provide a semiconductor device or the like with stable electrical characteristics. Another object is to provide a highly reliable semiconductor device or the like. Further, another object is to provide a method for manufacturing the above semiconductor device or the like. Note that the descriptions of these objects do not disturb the existence of other objects. In one embodiment of the present invention, there is no need to achieve all the objects. Other objects will be apparent from and can be derived from the description of the specification, the drawings, the claims, and the like.
A semiconductor device of one embodiment of the present invention includes a base insulating layer; an oxide stack which is over the base insulating layer and includes an oxide layer and an oxide semiconductor layer having an electron affinity higher than that of the oxide layer by 0.1 eV or more; a source electrode layer and a drain electrode layer in contact with the oxide stack; a gate insulating layer over the oxide stack, the source electrode layer, and the drain electrode layer; a gate electrode layer over the gate insulating layer; and an interlayer insulating layer over the gate electrode layer. The oxide semiconductor layer has a low defect density.
For example, the oxide semiconductor layer in the semiconductor device has a spin density of 1.5×1018 spins/cm3 or less, preferably 1×1017 spins/cm3 or less corresponding to a signal at a g-factor of 1.93 in electron spin resonance (ESR) spectroscopy. Note that the spin density corresponding to a signal at a g-factor of 1.93 in electron spin resonance spectroscopy represents the number of oxygen vacancies in the oxide semiconductor layer. The g-factor corresponding to oxygen vacancies varies depending on, for example, the composition of the oxide semiconductor layer; thus, the g-factor may deviate within a range of about ±5% and is preferably about 1.90 to 1.95.
Further, it is preferable that the gate insulating layer have a spin density of 2×1018 spins/cm3 or more, preferably 2×1019 spins/cm3 or more corresponding to a signal at a g-factor of 2.001 in electron spin resonance spectroscopy. Note that the spin density corresponding to a signal at a g-factor of 2.001 in electron spin resonance spectroscopy represents the number of dangling bonds in the gate insulating layer. The g-factor varies depending on the composition or the kind of the insulating layer; thus, the g-factor may deviate within a range of about ±5% and is preferably about 2.00 to 2.01.
Thus, one embodiment of the present invention is a semiconductor device including a base insulating layer; an oxide stack including an oxide layer over the base insulating layer and an oxide semiconductor layer having an electron affinity higher than that of the oxide layer by 0.1 eV or more; a source electrode layer and a drain electrode layer in contact with the oxide stack; a gate insulating layer over the oxide stack, the source electrode layer, and the drain electrode layer; a gate electrode layer over the gate insulating layer; and an interlayer insulating layer over the gate electrode layer. The oxide semiconductor layer has a spin density of 1.5×1018 spins/cm3 or less corresponding to a signal at a g-factor of greater than or equal to 1.90 and less than or equal to 1.95 in electron spin resonance spectroscopy. The gate insulating layer has a spin density of 2×1018 spins/cm3 or more corresponding to a signal at a g-factor of greater than or equal to 2.00 and less than or equal to 2.01 in electron spin resonance spectroscopy.
In a region including at least the oxide stack and the gate insulating layer in the above semiconductor device, a spin density of 1.5×1012 spins/cm2 or less corresponding to a signal at a g-factor of greater than or equal to 1.90 and less than or equal to 1.95 and a spin density of 2×1012 spins/cm2 or more corresponding to a signal at a g-factor of greater than or equal to 2.00 and less than or equal to 2.01 are obtained by electron spin resonance spectroscopy.
Thus, one embodiment of the present invention is a semiconductor device including an oxide stack including an oxide layer and an oxide semiconductor layer that is over the oxide layer and has an electron affinity higher than that of the oxide layer by 0.1 eV or more; a gate insulating layer in contact with the oxide stack; and a gate electrode layer overlapping with the oxide stack with the gate insulating layer therebetween. A spin density corresponding to a signal at a g-factor of greater than or equal to 1.90 and less than or equal to 1.95 is 1.5×1012 spins/cm2 or less and a spin density corresponding to a signal at a g-factor of greater than or equal to 2.00 and less than or equal to 2.01 is 2×1012 spins/cm2 or more in electron spin resonance spectroscopy.
The oxide layer and the oxide semiconductor layer contain at least indium. The proportion of indium in the oxide semiconductor layer is preferably higher than that in the oxide layer. The oxide layer and the oxide semiconductor layer preferably contain at least indium and zinc. Further, the oxide layer and the oxide semiconductor layer preferably contain one or more elements selected from Ga, Fe, Mn, and Co.
The oxide semiconductor layer preferably includes a crystal whose c-axis is aligned in a direction substantially perpendicular to an upper surface of the oxide semiconductor layer.
The concentration of silicon contained in the oxide semiconductor layer is preferably lower than 2×1018 atoms/cm3, further preferably lower than 2×1017 atoms/cm3.
Another embodiment of the present invention is a method for manufacturing a semiconductor device including the steps of forming a base insulating layer; forming an oxide stack including an oxide semiconductor layer over the base insulating layer; forming a source electrode layer and a drain electrode layer over the oxide stack; forming a gate insulating layer over the oxide stack, the source electrode layer, and the drain electrode layer; forming a gate electrode layer over the gate insulating layer; forming an interlayer insulating layer over the gate electrode layer; and performing heat treatment at a temperature higher than or equal to 300° C. and lower than 450° C. after forming the interlayer insulating layer. The gate insulating layer is formed by a plasma CVD method with the pressure inside a treatment chamber set to higher than or equal to 100 Pa and lower than or equal to 300 Pa.
Further, heat treatment may be performed after formation of the oxide stack. In addition, oxygen may be implanted to the base insulating layer by an ion implantation method.
According to one embodiment of the present invention, a miniaturized transistor including an oxide semiconductor can be formed. Further, the reliability of the transistor can be improved.
FIGS. 37A1, 37A2, 37B1, 37B2, 37C1, and 37C2 each show the Vg-Id characteristics of a transistor before and after a gate BT stress test.
FIGS. 38A1, 38A2, 38B1, 38B2, 38C1, and 38C2 each show the Vg-Id characteristics of a transistor before and after a gate BT stress test.
FIGS. 39A1, 39A2, 39B1, 39B2, 39C1, and 39C2 each show the Vg-Id characteristics of a transistor before and after a gate BT stress test.
Hereinafter, embodiments and examples of the present invention will be described in detail with reference to the accompanying drawings. However, the present invention is not limited to the description below, and it is easily understood by those skilled in the art that modes and details thereof can be modified in various ways. Therefore, the present invention is not construed as being limited to description of the embodiments and the examples.
In embodiments hereinafter described, the same parts are denoted with the same reference numerals throughout the drawings in some cases. Note that the thickness, width, relative positional relation, and the like of components, i.e., a layer, a region, and the like, which are illustrated in the drawings are exaggerated for clarification of descriptions of the embodiments in some cases.
Note that the term such as “over” in this specification and the like does not necessarily mean that a component is placed “directly on” another component. For example, the expression “a gate electrode layer over an insulating layer” does not exclude the case where there is an additional component between the insulating layer and the gate electrode layer. The same applies to the term “below”.
In this specification and the like, the term “electrode layer” or “wiring layer” does not limit the function of components. For example, an “electrode layer” can be used as part of a “wiring layer”, and the “wiring layer” can be used as part of the “electrode layer”. In addition, the term “electrode layer” or “wiring layer” can also mean a combination of a plurality of “electrode layers” or “wiring layers”, for example.
Functions of a “source” and a “drain” are sometimes replaced with each other when a transistor of opposite polarity is used or when the direction of current flow is changed in circuit operation, for example. Therefore, the terms “source” and “drain” can be replaced with each other in this specification.
Note that in this specification and the like, the term “electrically connected” includes the case where components are connected through an object having any electric function. There is no particular limitation on an object having any electric function as long as electric signals can be transmitted and received between components that are connected through the object.
Examples of an “object having any electric function” are an electrode and a wiring.
In this specification, a term “parallel” indicates that the angle formed between two straight lines is greater than or equal to −10° and less than or equal to 10°, and accordingly also includes the case where the angle is greater than or equal to −5° and less than or equal to 5°. In addition, a term “perpendicular” indicates that the angle formed between two straight lines is greater than or equal to 80° and less than or equal to 100°, and accordingly includes the case where the angle is greater than or equal to 85° and less than or equal to 95°.
In this specification, trigonal and rhombohedral crystal systems are included in a hexagonal crystal system.
A transistor 420, which is a semiconductor device of one embodiment of the present invention, is described with reference to
The transistor 420 includes a base insulating layer 402 over a substrate 400; an oxide stack 404 including an oxide layer 404a over the base insulating layer 402, an oxide semiconductor layer 404b over the oxide layer 404a, and an oxide layer 404c over the oxide semiconductor layer 404b; a source electrode layer 406a and a drain electrode layer 406b over the oxide stack 404; a gate insulating layer 408 over the oxide stack 404, the source electrode layer 406a, and the drain electrode layer 406b; a gate electrode layer 410 over the gate insulating layer 408; an interlayer insulating layer 412 and an interlayer insulating layer 414 over the gate electrode layer 410; and a source wiring layer 416a and a drain wiring layer 416b connected to the source electrode layer 406a and the drain electrode layer 406b through openings formed in the gate insulating layer 408, the interlayer insulating layer 412, and the interlayer insulating layer 414. Note that a transistor operates as long as it includes at least a semiconductor layer serving as a channel formation region, a gate insulating layer, and a gate electrode layer overlapping with the semiconductor layer with the gate insulating layer provided therebetween. Accordingly, the transistor 420 includes at least the oxide stack 404, the gate insulating layer 408, and the gate electrode layer 410; one or more of the base insulating layer 402, the source electrode layer 406a, the drain electrode layer 406b, the interlayer insulating layer 412, the source wiring layer 416a, and the drain wiring layer 416b may be omitted.
The oxide stack 404 includes the oxide layer 404a, the oxide semiconductor layer 404b over the oxide layer 404a, and the oxide layer 404c over the oxide semiconductor layer 404b. Here, the oxide stack 404 includes three layers; however, the oxide stack may include two layers or four or more layers as long as the oxide stack is a stack of multiple oxide layers including an oxide semiconductor layer. For example, the oxide stack may be a stack of two layers: an oxide semiconductor layer and an oxide layer which is formed between the oxide semiconductor layer and a gate insulating layer; or an oxide layer formed over a base insulating layer and an oxide semiconductor layer formed over the oxide layer.
Materials are appropriately selected for the oxide stack 404 so that a channel is formed in the oxide semiconductor layer 404b by an electric field of the gate electrode layer 410. With such a structure, the channel can be formed apart from the base insulating layer 402 and the gate insulating layer 408. Thus, entry of an impurity to the channel from the base insulating layer 402 and the gate insulating layer 408 can be prevented. For example, in the case where an insulating layer containing silicon (hereinafter also referred to as a silicon insulating layer), such as a silicon oxide film, a silicon oxynitride film, a silicon nitride oxide film, or a silicon nitride film, is used as each of the base insulating layer 402 and the gate insulating layer 408, silicon contained in the base insulating layer 402 and the gate insulating layer 408 can be prevented from entering the oxide semiconductor layer 404b.
Here, silicon oxynitride means the one that contains more oxygen than nitrogen. For example, silicon oxynitride contains at least oxygen, nitrogen, and silicon at concentrations ranging from greater than or equal to 50 atomic % and less than or equal to 70 atomic %, greater than or equal to 0.5 atomic % and less than or equal to 15 atomic %, and greater than or equal to 25 atomic % and less than or equal to 35 atomic %, respectively. Note that the above ranges are obtained in the case where measurement is performed using Rutherford backscattering spectrometry or hydrogen forward scattering (HFS). In addition, the total of the percentages of the constituent elements does not exceed 100 atomic %.
To form a channel in the oxide semiconductor layer 404b, the oxide stack is preferably structured such that the depth of the bottom of the conduction band from the vacuum level (electron affinity) in the oxide semiconductor layer 404b is greatest in the oxide stack. Accordingly, in the transistor 420, materials are appropriately selected so that the electron affinity of the oxide semiconductor layer 404b is greater than those of the oxide layer 404a and the oxide layer 404c. A difference in electron affinity between the oxide semiconductor layer 404b and the oxide layer 404a and a difference in electron affinity between the oxide semiconductor layer 404b and the oxide layer 404c are each preferably greater than or equal to 0.1 eV, further preferably greater than or equal to 0.15 eV. With such a structure, the bottom of the conduction band in the oxide semiconductor layer 404b has lower energy level than those of the conduction band in the oxide layer 404a and the oxide layer 404c; thus, a current path of the transistor 420 is formed in the oxide semiconductor layer 404b.
The band structure of the oxide stack 404 is described with reference to
As shown in
Note that
According to
Note that when the energy gap between the oxide layer 404a or the oxide layer 404c, and the oxide semiconductor layer 404b is small, an electron in the oxide semiconductor layer 404b might reach the trap level by passing over the energy gap. When an electron is trapped in the trap level, a negative fixed charge is generated; thus, the threshold voltage of the transistor is shifted in the positive direction.
Thus, the energy gap between the oxide layer 404a and the oxide semiconductor layer 404b and the energy gap between the oxide layer 404c and the oxide semiconductor layer 404b are each preferably greater than or equal to 0.1 eV, more preferably greater than or equal to 0.15 eV because the amount of change of the threshold voltage of the transistor is reduced and the transistor has stable electrical characteristics.
The oxide layer 404a and the oxide layer 404c each may be either an insulating film or a film having semiconductor characteristics as long as it has a smaller electron affinity than the oxide semiconductor layer 404b. Note that oxide layers which do not contain an impurity such as silicon or hydrogen as a main component are used as the oxide layer 404a and the oxide layer 404c so that a trap level is not formed at the interface between the oxide semiconductor layer 404b and each of the oxide layer 404a and the oxide layer 404c, which are formed in contact with the oxide semiconductor layer 404b. In particular, when the oxide semiconductor layer 404b contains the same main component as the oxide layer 404a and the oxide layer 404c, interface scattering between the oxide semiconductor layer 404b and each of the oxide layer 404a and the oxide layer 404c can be prevented, leading to a reduction in the number of trap levels.
For example, in the case where the oxide semiconductor layer 404b is formed using an In—Ga—Zn oxide target containing In, Ga, and Zn at an atomic ratio of 1:1:1, the oxide layer 404a and the oxide layer 404c are preferably formed using an In—Ga—Zn oxide target containing In, Ga, and Zn at an atomic ratio of 1:3:2.
It is effective to make the oxide semiconductor layer 404b be a highly purified intrinsic oxide semiconductor so that a transistor including the oxide stack 404 has stable electrical characteristics. Specifically, the carrier density of the oxide semiconductor layer 404b is set to be lower than 1×1017/cm3, lower than 1×1015/cm3, or lower than 1×1013/cm3. In the oxide semiconductor layer 404b, hydrogen, nitrogen, carbon, silicon, and a metal element other than a main component become an impurity. In order to reduce the concentration of impurities in the oxide semiconductor layer 404b, it is preferable to also reduce the concentration of impurities in the oxide layers 404a and 404c which are close to the oxide semiconductor layer 404b to a value almost equal to that in the oxide semiconductor layer 404b.
Particularly when elements such as silicon (Si), germanium (Ge), carbon (C), hafnium (Hf), and titanium (Ti) are contained in the oxide semiconductor layer 404b at a high concentration, an impurity state due to the elements is formed in the oxide semiconductor layer 404b. In some cases, the impurity state becomes a trap, which degrades electrical characteristics of the transistor. In order to prevent degradation of the electrical characteristics of the transistor, the concentration of the elements in the oxide semiconductor layer 404b is set to be lower than 1×1019 atoms/cm3, preferably lower than 2×1018 atoms/cm3, further preferably lower than 2×1017 atoms/cm3. Moreover, the concentrations of the elements at the interface between the oxide layer 404a and the oxide semiconductor layer 404b and the interface between the oxide semiconductor layer 404b and the oxide layer 404c are each set to be lower than 1×1019 atoms/cm3, preferably lower than 5×1018 atoms/cm3, more preferably lower than 1×1018 atoms/cm3.
Further, hydrogen and nitrogen in the oxide semiconductor layer 404b form donor levels, which increase carrier density. In order to make the oxide semiconductor layer 404b intrinsic or substantially intrinsic, the concentration of hydrogen in the oxide semiconductor layer 404b, which is measured by secondary ion mass spectrometry (SIMS), is set to be lower than or equal to 2×1020 atoms/cm3, preferably lower than or equal to 5×1019 atoms/cm3, more preferably lower than or equal to 1×1019 atoms/cm3, still more preferably lower than or equal to 5×1018 atoms/cm3. The concentration of nitrogen in the oxide semiconductor layer 404b, which is measured by SIMS, is set to be lower than 5×1019 atoms/cm3, preferably lower than or equal to 5×1018 atoms/cm3, more preferably lower than or equal to 1×1018 atoms/cm3, still more preferably lower than or equal to 5×1017 atoms/cm3.
Note that when silicon and carbon are contained in the oxide semiconductor layer 404b at a high concentration, the crystallinity of the oxide semiconductor layer 404b is lowered in some cases. In order not to lower the crystallinity of the oxide semiconductor layer 404b, the concentration of silicon in the oxide semiconductor layer 404b is set to be lower than 1×1019 atoms/cm3, preferably lower than 5×1018 atoms/cm3, more preferably lower than 1×1018 atoms/cm3. Moreover, in order not to lower the crystallinity of the oxide semiconductor layer 404b, the concentration of carbon in the oxide semiconductor layer 404b is set to be lower than 1×1019 atoms/cm3, preferably lower than 5×1018 atoms/cm3, more preferably lower than 1×1018 atoms/cm3. Description of the crystallinity of the oxide semiconductor layer 404b will be given later.
When the oxide semiconductor layer 404b contains hydrogen, hydrogen serves as a donor and changes the characteristics of the transistor. Thus, it is preferable that the concentration of hydrogen contained in the oxide semiconductor layer be lower than 5×1018 atoms/cm3, preferably lower than or equal to 1×1018 atoms/cm3, further preferably lower than or equal to 5×1017 atoms/cm3, still further preferably lower than or equal to 1×1016 atoms/cm3.
Oxygen vacancies in the oxide semiconductor layer 404b form donors and serve as carriers; thus, when oxygen vacancies are formed in the oxide semiconductor layer, the characteristics of the transistor are changed and the reliability thereof is lowered. Accordingly, the number of oxygen vacancies in the oxide semiconductor layer is preferably reduced. For example, it is preferable that the oxide semiconductor layer have a spin density of 1.5×1018 spins/cm3 or less, further preferably 1×1017 spins/cm3 or less corresponding to a signal at a g-factor of 1.93 (greater than or equal to 1.90 and less than or equal to 1.95) in electron spin resonance spectroscopy in which a magnetic field is applied in parallel to the film surface. In addition, it is preferable that the oxide semiconductor layer have a spin density per unit area of 1.5×1012 spins/cm2 or less, further preferably 1×1011 spins/cm2 or less corresponding to the signal at a g-factor of 1.93. Note that the spin density corresponding to a signal at a g-factor of 1.93 in electron spin resonance spectroscopy represents the number of oxygen vacancies in the oxide semiconductor layer. The g-factor corresponding to oxygen vacancies varies depending on, for example, the composition of the oxide semiconductor layer; thus, the g-factor may deviate within a range of about ±5% and may be about 1.90 to 1.95 here. By reducing the number of oxygen vacancies in the oxide semiconductor layer as much as possible, generation of carriers can be reduced. As a result, the transistor can be prevented from having normally-on characteristics, so that the electrical characteristics and reliability of the semiconductor device can be improved.
It is preferable that the gate insulating layer 408 have a spin density of 2×1018 spins/cm3 or more, preferably 2×1019 spins/cm3 or more corresponding to a signal at a g-factor of 2.001 (greater than or equal to 2.00 and less than or equal to 2.01) in electron spin resonance spectroscopy. In addition, it is preferable that the gate insulating layer 408 have a spin density per unit area of 2×1012 spins/cm2 or more, further preferably 2×1013 spins/cm2 or more corresponding to the signal at a g-factor of 2.001. The spin density corresponding to a signal at a g-factor of 2.001 represents the number of dangling bonds in the gate insulating layer 408. The g-factor varies depending on the composition or the kind of the insulating layer; thus, the g-factor may deviate within a range of about ±5% and may be about 2.00 to 2.01 here. The gate insulating layer 408 including a large number of dangling bonds releases a large amount of oxygen by being subjected to heat treatment or the like. Therefore, when the gate insulating layer 408 including a large number of dangling bonds is provided over the oxide semiconductor layer 404b, oxygen released from the gate insulating layer 408 fills the oxygen vacancies in the oxide semiconductor layer 404b; thus, the transistor can have stable electrical characteristics.
When a gate insulating layer including a large number of dangling bonds is used, the electrical characteristics of a transistor become unstable by the effect of the dangling bonds in some cases. However, in the semiconductor device of one embodiment of the present invention, since the oxide layer 404c is provided between the oxide semiconductor layer 404b and the gate insulating layer 408, the transistor can have stable electrical characteristics even with the gate insulating layer 408 including a large number of dangling bonds.
Further, the gate insulating layer 408 over the oxide semiconductor layer 404b is made dense; thus, constituent elements in the oxide semiconductor layer can be prevented from being partly released outside. The density can be evaluated by measuring the wet etching rate of the gate insulating layer, for example. The denser the film is, the lower the wet etching rate is; that is, a denser film is less likely to be etched.
The semiconductor device of one embodiment of the present invention is a semiconductor device in which the defect density in an oxide semiconductor layer is reduced and which has excellent electrical stability. For example, the amount of change in the threshold voltage of the semiconductor device in a gate bias-temperature (BT) stress test is small.
Note that the gate BT stress test is one kind of accelerated test and can evaluate, in a short time, a change in characteristics (i.e., a change with time) of a transistor, which is caused by long-term use. The amount of change in characteristics of the transistor due to the gate BT stress test is an important indicator when examining the reliability of the transistor.
A specific method of the gate BT stress test is described. First, electrical characteristics of a transistor are measured. Next, the temperature of a substrate over which the transistor is formed (substrate temperature) is set at fixed temperature, a pair of electrodes serving as a source and a drain of the transistor are set at a same potential, and a potential different from that of the pair of electrodes serving as a source and a drain is applied to a gate electrode for a certain period. The substrate temperature may be determined as appropriate in accordance with the test purpose. Then, the substrate temperature is set at a temperature similar to that at which the electrical characteristics have been measured, and the electrical characteristics of the transistor are measured again. As a result, a difference in threshold voltage and a difference in shift value between before and after the gate BT stress test can be obtained as the amount of change in the electrical characteristics.
Note that in this specification, the test in the case where the potential applied to the gate electrode is higher than the potentials of the source and the drain is referred to as a positive gate BT stress test, and the test in the case where the potential applied to the gate electrode is lower than the potentials of the source and the drain is referred to as a negative gate BT stress test.
In this specification, in a curve where the horizontal axis represents the gate voltage (Vg; voltage between a source and a gate) and the vertical axis represents the logarithm of drain current (Id), the shift value is defined as a gate voltage at a point of intersection of an extrapolated tangent line of Id having the highest inclination with a straight line of Id=1×10−12 [A]. Note that in this specification, the shift value was calculated with a drain voltage (voltage between a source and a drain) of 10 V.
The number of oxygen vacancies in the oxide semiconductor layer is sufficiently reduced in the semiconductor device of one embodiment of the present invention; thus, even a miniaturized transistor with a short channel length can have excellent electrical stability as the semiconductor device.
Next, a method of manufacturing the transistor 420 is described.
First, the base insulating layer 402 is formed over the substrate 400. There is no particular limitation on a substrate that can be used, as long as it has heat resistance high enough to withstand heat treatment performed later. For example, a glass substrate of barium borosilicate glass, aluminoborosilicate glass, or the like, a ceramic substrate, a quartz substrate, or a sapphire substrate can be used.
A single crystal semiconductor substrate or a polycrystalline semiconductor substrate of silicon, silicon carbide, or the like or a compound semiconductor substrate of silicon germanium or the like may be used as the substrate 400. Alternatively, an SOI substrate, a semiconductor substrate over which a semiconductor element is provided, or the like can be used.
The base insulating layer 402 can be formed by a sputtering method, a molecular beam epitaxy (MBE) method, a chemical vapor deposition (CVD) method, a pulsed laser deposition (PLD) method, an atomic layer deposition (ALD) method, or the like, as appropriate.
An inorganic insulating layer can be used as the base insulating layer 402. It is preferable to use, for example, a silicon oxide film, a silicon oxynitride film, an aluminum oxide film, an aluminum oxynitride film, a hafnium oxide film, a gallium oxide film, a silicon nitride film, an aluminum nitride film, a silicon nitride oxide film, or an aluminum nitride oxide film. Further, the base insulating layer 402 can be formed with a single-layer structure or a stacked-layer structure including two or more layers with the use of these compounds.
As the base insulating layer 402, a silicon oxide film or a silicon oxynitride film may be formed under the following conditions: a vacuum-evacuated treatment chamber in a plasma CVD apparatus is held at a temperature higher than or equal to 180° C. and lower than or equal to 450° C., preferably higher than or equal to 180° C. and lower than or equal to 350° C.; a source gas is introduced into the treatment chamber; the pressure in the treatment chamber is higher than or equal to 100 Pa and lower than or equal to 250 Pa, preferably higher than or equal to 100 Pa and lower than or equal to 200 Pa; and the high-frequency power supplied to an electrode provided in the treatment chamber is greater than or equal to 1.48 W/cm2 and less than or equal to 2.46 W/cm2, preferably greater than or equal to 1.48 W/cm2 and less than or equal to 1.97 W/cm2.
As the source gas, a deposition gas containing silicon and an oxidation gas are preferably used. Typical examples of the deposition gas containing silicon include silane, disilane, trisilane, and silane fluoride. Examples of the oxidation gas include oxygen, ozone, dinitrogen monoxide, nitrogen dioxide, and dry air.
As deposition conditions, the power density is set high as described above in the treatment chamber under the above pressure, whereby the decomposition efficiency of the source gas in plasma is increased, oxygen radicals are increased, and oxidation of the deposition gas containing silicon is promoted; thus, the amount of oxygen contained in the base insulating layer 402 exceeds that in the stoichiometric composition. However, in the case where the substrate temperature is within the above temperature range, the bond between silicon and oxygen is weak. As a result, an oxide insulating layer which contains oxygen in excess of the stoichiometric composition and from which part of oxygen is released by heating can be formed.
In the source gas of the base insulating layer 402, the ratio of the deposition gas containing silicon to the oxidation gas is increased, and the high-frequency power is set to have the above power density. Thus, the deposition rate can be increased, and the amount of oxygen contained in the base insulating layer 402 can be increased.
After formation of the base insulating layer 402, oxygen may be implanted to the base insulating layer 402.
Here, oxygen atoms are implanted to silicon oxynitride films by an ion implantation method, and the results of detecting a gas (O2; m/z (m: mass, z: charge)=32) by thermal desorption spectroscopy are shown.
First, a method for fabricating samples is described. Thermal oxidation was performed on a silicon substrate in an HCl atmosphere to form a thermal oxide film with a thickness of 100 nm on a surface of the substrate. The thermal oxidation was performed at 950° C. for four hours in a thermal oxidation atmosphere containing HCl at 3 vol % with respect to oxygen.
Next, a 300-nm-thick silicon oxynitride film was formed over the thermal oxide film. For the formation of the silicon oxynitride film, silane with a flow rate of 2.3 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 50 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the silicon substrate at the formation of the silicon oxynitride film was 400° C. After the formation, heat treatment was performed at 450° C. for one hour.
Next, oxygen atoms were implanted by an ion implantation method to samples obtained in the above manner. Oxygen was implanted under the following conditions: the acceleration voltage was set to 60 kV; and the dosage was set to 2×1016 ions/cm2, 1×1016 ions/cm2, and 5×1015 ions/cm2 for Sample 1, Sample 2, and Sample 3, respectively.
In Sample 1 for which the oxygen dosage was set to 2×1016 ions/cm2, oxygen begins to be released at around 100° C., and there are peaks at around 300° C. and around 450° C. In Sample 2 for which the oxygen dosage was set to 1×1016 ions/cm2, oxygen begins to be released at around 200° C., and there are peaks at around 300° C. and around 400° C. The amount of released oxygen at the peak at around 300° C. is less than or equal to one-half that in Sample 1 for which the oxygen dosage was set to 2×1016 ions/cm2. In Sample 3 for which the oxygen dosage was set to 5×1015 ions/cm2, oxygen begins to be released at around 200° C., and there are peaks at around 300° C. and around 400° C. The amount of released oxygen at the peak at around 300° C. is less than or equal to one-half that in Sample 2 for which the oxygen dosage was set to 1×1016 ions/cm2 (i.e., less than or equal to one-quarter that in Sample 1). According to
Note that the base insulating layer 402 is not necessarily provided as long as insulation between the substrate 400 and the oxide semiconductor layer 404b to be formed later can be ensured. That is, when the substrate 400 has a sufficient insulating property, a structure without the base insulating layer 402 may be employed in some cases.
Next, the oxide stack 404 including the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c is formed over the base insulating layer 402 (see
As a stabilizer, gallium (Ga), tin (Sn), aluminum (Al), zirconium (Zr), and the like can be given. As another stabilizer, lanthanoid such as lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), or lutetium (Lu) can be given.
For the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c, for example, any of the following can be used: indium oxide, tin oxide, zinc oxide, an In—Zn oxide, a Sn—Zn oxide, an Al—Zn oxide, a Zn—Mg oxide, a Sn—Mg oxide, an In—Mg oxide, an In—Ga oxide, an In—Ga—Zn oxide, an In—Al—Zn oxide, an In—Sn—Zn oxide, a Sn—Ga—Zn oxide, an Al—Ga—Zn oxide, a Sn—Al—Zn oxide, an In—La—Zn oxide, an In—Ce—Zn oxide, an In—Pr—Zn oxide, an In—Nd—Zn oxide, an In—Sm—Zn oxide, an In—Eu—Zn oxide, an In—Gd—Zn oxide, an In—Tb—Zn oxide, an In—Dy—Zn oxide, an In—Ho—Zn oxide, an In—Er—Zn oxide, an In—Tm—Zn oxide, an In—Yb—Zn oxide, an In—Lu—Zn oxide, an In—Sn—Ga—Zn oxide, an In—Al—Ga—Zn oxide, an In—Sn—Al—Zn oxide, an In—Sn—Hf—Zn oxide, or an In—Hf—Al—Zn oxide.
Note that here, for example, an “In—Ga—Zn oxide” means an oxide containing In, Ga, and Zn as its main components and there is no particular limitation on the ratio of In, Ga, and Zn. The In—Ga—Zn oxide may contain a metal element other than In, Ga, and Zn.
Alternatively, a material represented by InMO3(ZnO)m (m>0 is satisfied, and m is not an integer) may be used. Note that M represents one or more metal elements selected from Ga, Fe, Mn, and Co. Alternatively, a material represented by In2SnO5(ZnO)n (n>0, n is an integer) may be used.
Note that materials are appropriately selected so that the electron affinity of the oxide semiconductor layer 404b is greater than those of the oxide layer 404a and the oxide layer 404c by 0.1 eV or more, preferably 0.15 eV or more. Accordingly, the bottom of the conduction band in the oxide semiconductor layer 404b is deeper from the vacuum level than those of the conduction band in the oxide layer 404a and the oxide layer 404c; thus, a channel is formed in the oxide semiconductor layer 404b by an electric field of the gate electrode layer 410.
An oxide used for each of the oxide layer 404a and the oxide layer 404c contains aluminum, gallium, germanium, yttrium, tin, lanthanum, or cerium such that the proportion of the element in each of the oxide layer 404a and the oxide layer 404c is higher than that in the oxide semiconductor layer 404b. Specifically, the content of any of the above elements in the oxide used for each of the oxide layer 404a and the oxide layer 404c is more than 1.5 times, preferably more than 2 times, further preferably more than 3 times as high as that in the oxide used for the oxide semiconductor layer 404b. The element strongly bonds to oxygen and high energy is needed for forming an oxygen vacancy; thus, an oxygen vacancy is less likely to occur. For this reason, an oxygen vacancy is less likely to occur in the oxide layer 404a and the oxide layer 404c in each of which the proportion of the element is higher than that in the oxide semiconductor layer 404b. This means that the oxide layer 404a and the oxide layer 404c have stable characteristics. Thus, the proportion of the element in each of the oxide layer 404a and the oxide layer 404c is set high, so that a stable interface can be formed between the oxide stack 404 and each of the base insulating layer 402 and the gate insulating layer 408, which results in highly reliability of the semiconductor device.
Note that when the oxide layer 404a is an In-M-Zn oxide, the atomic ratio of In to M is preferably as follows: the percentage of In is lower than 50 atomic % and the percentage of M is higher than or equal to 50 atomic %; further preferably, the percentage of In is lower than 25 atomic % and the percentage of M is higher than or equal to 75 atomic %. When the oxide semiconductor layer 404b is an In-M-Zn oxide, the atomic ratio of In to M is preferably as follows: the percentage of In is higher than or equal to 25 atomic % and the percentage of M is lower than 75 atomic %; further preferably, the percentage of In is higher than or equal to 34 atomic % and the percentage of M is lower than 66 atomic %. When the oxide layer 404c is an In-M-Zn oxide, the atomic ratio of In to M is preferably as follows: the percentage of In is lower than 50 atomic % and the percentage of M is higher than or equal to 50 atomic %; further preferably, the percentage of In is lower than 25 atomic % and the percentage of M is higher than or equal to 75 atomic %.
Note that when the oxide layer 404a and the oxide layer 404c each contain a material represented by InGaXZnYOZ, it is preferable that X do not exceed 10. An increase in the proportion of gallium in the oxide layer increases the amount of powder substances (also referred to as dust) generated in deposition by RF sputtering, which leads to deterioration in characteristics of a semiconductor device in some cases.
Note that the oxide semiconductor layer and the oxide layers can be formed by, instead of an RF sputtering method in which a high-frequency power source is used as a sputtering power source, a DC sputtering method in which a direct-current power source is used, an AC sputtering method in which an alternating-current power source, or the like. In particular, by a DC sputtering method, dust generated in the deposition can be reduced and the film thickness can be uniform.
The indium content in the oxide semiconductor layer 404b is preferably higher than those in the oxide layer 404a and the oxide layer 404c. In an oxide semiconductor, the s orbital of heavy metal mainly contributes to carrier transfer, and when the proportion of In in the oxide semiconductor is increased, overlap of the s orbitals is likely to be increased. Therefore, an oxide having a composition in which the proportion of In is higher than that of Ga has higher mobility than an oxide having a composition in which the proportion of In is equal to or lower than that of Ga. Thus, with use of an oxide having a high indium content for the oxide semiconductor layer 404b, high mobility can be achieved.
To form the oxide stack 404 in which a continuous junction as shown in
To form a continuous junction, it is necessary to stack the layers in succession without exposure to the air using a multi-chamber deposition apparatus (sputtering apparatus) with load lock chambers. Each chamber in the sputtering apparatus is preferably evacuated to high vacuum (about 1×10−4 Pa to 5×10−7 Pa) with an entrapment vacuum evacuation pump such as a cryopump so that water or the like, which is an impurity for an oxide semiconductor, is removed as much as possible. Alternatively, a turbo molecular pump and a cold trap are preferably used in combination to prevent backflow of gas into the chamber through an evacuation system.
To obtain a highly purified intrinsic oxide semiconductor, it is necessary not only to evacuate the chamber to high vacuum but also to highly purify a sputtering gas. A highly purified gas having a dew point of −40° C. or lower, preferably −80° C. or lower, still preferably −100° C. or lower is used as an oxygen gas or an argon gas which is used as a sputtering gas; thus, entry of moisture or the like to the oxide semiconductor layer can be prevented as much as possible.
Note that the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c may have different crystallinities. In other words, a single crystal oxide layer, a polycrystalline oxide layer, an amorphous oxide layer, and the like may be combined as appropriate.
A structure of an oxide semiconductor layer is described below.
An oxide semiconductor layer is classified roughly into a single-crystal oxide semiconductor layer and a non-single-crystal oxide semiconductor layer. The non-single-crystal oxide semiconductor layer includes any of an amorphous oxide semiconductor layer, a microcrystalline oxide semiconductor layer, a polycrystalline oxide semiconductor layer, a c-axis aligned crystalline oxide semiconductor (CAAC-OS) layer, and the like.
The amorphous oxide semiconductor layer has disordered atomic arrangement and no crystalline component. A typical example thereof is an oxide semiconductor layer in which no crystal part exists even in a microscopic region, and the whole of the layer is amorphous.
The microcrystalline oxide semiconductor layer includes a microcrystal (also referred to as nanocrystal) with a size greater than or equal to 1 nm and less than 10 nm, for example. Thus, the microcrystalline oxide semiconductor layer has a higher degree of atomic order than the amorphous oxide semiconductor layer. Hence, the density of defect states of the microcrystalline oxide semiconductor layer is lower than that of the amorphous oxide semiconductor layer.
The CAAC-OS layer is one of oxide semiconductor layers including a plurality of crystal parts, and most of the crystal parts each fit inside a cube whose one side is less than 100 nm. Thus, there is a case where a crystal part included in the CAAC-OS layer fits inside a cube whose one side is less than 10 nm, less than 5 nm, or less than 3 nm. The density of defect states of the CAAC-OS layer is lower than that of the microcrystalline oxide semiconductor layer. The CAAC-OS layer is described in detail below.
In a transmission electron microscope (TEM) image of the CAAC-OS layer, a boundary between crystal parts, that is, a grain boundary is not clearly observed. Thus, in the CAAC-OS layer, a reduction in electron mobility due to the grain boundary is less likely to occur.
According to the TEM image of the CAAC-OS layer observed in a direction substantially parallel to a sample surface (cross-sectional TEM image), metal atoms are arranged in a layered manner in the crystal parts. Each metal atom layer has a morphology reflected by a surface over which the CAAC-OS layer is formed (hereinafter, a surface over which the CAAC-OS layer is formed is referred to as a formation surface) or a top surface of the CAAC-OS layer, and is arranged in parallel to the formation surface or the top surface of the CAAC-OS layer.
On the other hand, according to the TEM image of the CAAC-OS layer observed in a direction substantially perpendicular to the sample surface (plan TEM image), metal atoms are arranged in a triangular or hexagonal configuration in the crystal parts. However, there is no regularity of arrangement of metal atoms between different crystal parts.
From the results of the cross-sectional TEM image and the plan TEM image, alignment is found in the crystal parts in the CAAC-OS layer.
A CAAC-OS layer is subjected to structural analysis with an X-ray diffraction (XRD) apparatus. For example, when the CAAC-OS layer including an InGaZnO4 crystal is analyzed by an out-of-plane method, a peak appears frequently when the diffraction angle (2θ) is around 31°. This peak is derived from the (009) plane of the InGaZnO4 crystal, which indicates that crystals in the CAAC-OS layer have c-axis alignment, and that the c-axes are aligned in a direction substantially perpendicular to the formation surface or the top surface of the CAAC-OS layer.
On the other hand, when the CAAC-OS layer is analyzed by an in-plane method in which an X-ray enters a sample in a direction substantially perpendicular to the c-axis, a peak appears frequently when 2θ is around 56°. This peak is derived from the (110) plane of the InGaZnO4 crystal. Here, analysis (φ scan) is performed under conditions where the sample is rotated around a normal vector of a sample surface as an axis (φ axis) with 2θ fixed at around 56°. In the case where the sample is a single-crystal oxide semiconductor film of InGaZnO4, six peaks appear. The six peaks are derived from crystal planes equivalent to the (110) plane. On the other hand, in the case of a CAAC-OS layer, a peak is not clearly observed even when φ scan is performed with 2θ fixed at around 56°.
According to the above results, in the CAAC-OS layer having c-axis alignment, while the directions of a-axes and b-axes are different between crystal parts, the c-axes are aligned in a direction parallel to a normal vector of a formation surface or a normal vector of a top surface. Thus, each metal atom layer arranged in a layered manner observed in the cross-sectional TEM image corresponds to a plane parallel to the a-b plane of the crystal.
Note that the crystal part is formed concurrently with deposition of the CAAC-OS layer or is formed through crystallization treatment such as heat treatment. As described above, the c-axis of the crystal is aligned in a direction parallel to a normal vector of a formation surface or a normal vector of a top surface. Thus, for example, in the case where a shape of the CAAC-OS layer is changed by etching or the like, the c-axis might not be necessarily parallel to a normal vector of a formation surface or a normal vector of a top surface of the CAAC-OS layer.
Further, the degree of crystallinity in the CAAC-OS layer is not necessarily uniform. For example, in the case where crystal growth leading to the CAAC-OS layer occurs from the vicinity of the top surface of the layer, the degree of the crystallinity in the vicinity of the top surface is higher than that in the vicinity of the formation surface in some cases. Further, when an impurity is added to the CAAC-OS layer, the crystallinity in a region to which the impurity is added is changed, and the degree of crystallinity in the CAAC-OS layer varies depending on regions.
Note that when the CAAC-OS layer with an InGaZnO4 crystal is analyzed by an out-of-plane method, a peak of 2θ may also be observed at around 36°, in addition to the peak of 2θ at around 31°. The peak of 2θ at around 36° indicates that a crystal having no c-axis alignment is included in part of the CAAC-OS layer. It is preferable that in the CAAC-OS layer, a peak of 2θ appear at around 31° and a peak of 2θ do not appear at around 36°.
In a transistor using the CAAC-OS layer, change in electrical characteristics due to irradiation with visible light or ultraviolet light is small. Thus, the transistor has high reliability.
Note that an oxide semiconductor layer may be a stacked film including two or more layers of an amorphous oxide semiconductor layer, a microcrystalline oxide semiconductor layer, and a CAAC-OS layer, for example.
A CAAC-OS layer is formed by, for example, a sputtering method using a polycrystalline oxide target. By collision of ions with the target, a crystal region included in the target may be separated from the target along an a-b plane; in other words, a sputtered particle having a plane parallel to an a-b plane (flat-plate-like sputtered particle or pellet-like sputtered particle) may flake off from the target. In that case, the flat-plate-like sputtered particle reaches a substrate while maintaining its crystal state, whereby the CAAC-OS layer can be formed. To improve the crystallinity of the CAAC-OS layer, the average grain size of crystal grains included in the polycrystalline oxide target is set to 3 μm or less, preferably 2 μm or less, further preferably 1 μm or less.
The flat-plate-like sputtered particle has, for example, an equivalent circle diameter of a plane parallel to the a-b plane of greater than or equal to 3 nm and less than or equal to 10 nm, and a thickness (length in the direction perpendicular to the a-b plane) of greater than or equal to 0.7 nm and less than 1 nm. Note that in the flat-plate-like sputtered particle, the plane parallel to the a-b plane may be a regular triangle or a regular hexagon. Here, the term “equivalent circle diameter of a plane” refers to the diameter of a perfect circle having the same area as the plane.
The following conditions are preferably employed in order to form a CAAC-OS layer over an amorphous surface, a surface of an amorphous insulating layer, or a surface of an insulating layer.
By increasing the substrate heating temperature during the deposition, migration of sputtered particles occurs after the sputtered particles reach the substrate. Specifically, the substrate heating temperature during the deposition is higher than or equal to 100° C. and lower than or equal to 740° C., preferably higher than or equal to 200° C. and lower than or equal to 500° C. By increasing the substrate heating temperature during the deposition, when the flat-plate-like sputtered particles reach the substrate, migration occurs on the substrate, so that a flat plane of each flat-plate-like sputtered particle is attached to the substrate. At this time, the sputtered particles are positively charged, thereby being attached to the substrate while repelling each other; thus, the sputtered particles are not stacked unevenly, so that a CAAC-OS layer with a uniform thickness can be deposited.
By reducing the amount of impurities entering the CAAC-OS layer during the deposition, the crystal state can be prevented from being broken by the impurities. For example, the concentration of impurities (e.g., hydrogen, water, carbon dioxide, or nitrogen) which exist in a deposition chamber may be reduced. Furthermore, the concentration of impurities in a deposition gas may be reduced. Specifically, a deposition gas whose dew point is −80° C. or lower, preferably −100° C. or lower is used.
Furthermore, it is preferable that the proportion of oxygen in the deposition gas be increased and the power be optimized in order to reduce plasma damage at the deposition. The proportion of oxygen in the deposition gas is higher than or equal to 30 vol %, preferably 100 vol %.
After the CAAC-OS layer is deposited, heat treatment may be performed. The temperature of the heat treatment is higher than or equal to 100° C. and lower than or equal to 740° C., preferably higher than or equal to 200° C. and lower than or equal to 500° C. The heat treatment time is longer than or equal to 1 minute and shorter than or equal to 24 hours, preferably longer than or equal to 6 minutes and shorter than or equal to 4 hours. The heat treatment may be performed in an inert atmosphere or an oxidation atmosphere. It is preferable to perform heat treatment in an inert atmosphere and then perform heat treatment in an oxidation atmosphere. The heat treatment in an inert atmosphere can reduce the concentration of impurities in the CAAC-OS layer in a short time. At the same time, the heat treatment in an inert atmosphere may generate oxygen vacancies in the CAAC-OS layer. In such a case, the heat treatment in an oxidation atmosphere can reduce the oxygen vacancies. The heat treatment can further increase the crystallinity of the CAAC-OS layer. Note that the heat treatment may be performed under a reduced pressure, such as 1000 Pa or lower, 100 Pa or lower, 10 Pa or lower, or 1 Pa or lower. The heat treatment under the reduced pressure can reduce the concentration of impurities in the CAAC-OS layer in a shorter time.
By using the above method, a CAAC-OS layer can be formed over an amorphous surface, a surface of an amorphous insulating layer, or a surface of an insulating layer.
Alternatively, the CAAC-OS layer may be formed by the following method.
First, a first oxide semiconductor layer is formed to a thickness of greater than or equal to 1 nm and less than 10 nm. The first oxide semiconductor layer is formed by a sputtering method. Specifically, the substrate temperature is set to higher than or equal to 100° C. and lower than or equal to 500° C., preferably higher than or equal to 150° C. and lower than or equal to 450° C., and the proportion of oxygen in a deposition gas is set to higher than or equal to 30 vol %, preferably 100 vol %.
Next, heat treatment is performed so that the first oxide semiconductor layer becomes a first CAAC-OS layer with high crystallinity. The temperature of the heat treatment is higher than or equal to 350° C. and lower than or equal to 740° C., preferably higher than or equal to 450° C. and lower than or equal to 650° C. The heat treatment time is longer than or equal to 1 minute and shorter than or equal to 24 hours, preferably longer than or equal to 6 minutes and shorter than or equal to 4 hours. The heat treatment may be performed in an inert atmosphere or an oxidation atmosphere. It is preferable to perform heat treatment in an inert atmosphere and then perform heat treatment in an oxidation atmosphere. The heat treatment in an inert atmosphere can reduce the concentration of impurities in the first oxide semiconductor layer in a short time. At the same time, the heat treatment in an inert atmosphere may generate oxygen vacancies in the first oxide semiconductor layer. In such a case, the heat treatment in an oxidation atmosphere can reduce the oxygen vacancies. Note that the heat treatment may be performed under a reduced pressure, such as 1000 Pa or lower, 100 Pa or lower, 10 Pa or lower, or 1 Pa or lower. The heat treatment under the reduced pressure can reduce the concentration of impurities in the first oxide semiconductor layer in a shorter time.
The first oxide semiconductor layer with a thickness of greater than or equal to 1 nm and less than 10 nm can be easily crystallized by heat treatment as compared to the case where the first oxide semiconductor layer has a thickness of greater than or equal to 10 nm.
Next, a second oxide semiconductor layer having the same composition as the first oxide semiconductor layer is formed to a thickness of greater than or equal to 10 nm and less than or equal to 50 nm. The second oxide semiconductor layer is formed by a sputtering method. Specifically, the substrate temperature is set to higher than or equal to 100° C. and lower than or equal to 500° C., preferably higher than or equal to 150° C. and lower than or equal to 450° C., and the proportion of oxygen in a deposition gas is set to higher than or equal to 30 vol %, preferably 100 vol %.
Next, heat treatment is performed so that solid phase growth of the second oxide semiconductor layer from the first CAAC-OS layer occurs, whereby the second oxide semiconductor layer is turned into a second CAAC-OS layer having high crystallinity. The temperature of the heat treatment is higher than or equal to 350° C. and lower than or equal to 740° C., preferably higher than or equal to 450° C. and lower than or equal to 650° C. The heat treatment time is longer than or equal to 1 minute and shorter than or equal to 24 hours, preferably longer than or equal to 6 minutes and shorter than or equal to 4 hours. The heat treatment may be performed in an inert atmosphere or an oxidation atmosphere. It is preferable to perform heat treatment in an inert atmosphere and then perform heat treatment in an oxidation atmosphere. The heat treatment in an inert atmosphere can reduce the concentration of impurities in the second oxide semiconductor layer in a short time. At the same time, the heat treatment in an inert atmosphere may generate oxygen vacancies in the second oxide semiconductor layer. In such a case, the heat treatment in an oxidation atmosphere can reduce the oxygen vacancies. Note that the heat treatment may be performed under a reduced pressure, such as 1000 Pa or lower, 100 Pa or lower, 10 Pa or lower, or 1 Pa or lower. The heat treatment under the reduced pressure can reduce the concentration of impurities in the second oxide semiconductor layer in a shorter time.
In the above-described manner, a CAAC-OS layer having a total thickness of 10 nm or more can be formed.
A stack of an oxide semiconductor layer and oxide layers which are formed by the above method is partly etched, whereby the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c can be formed. Note that the oxide semiconductor layer and the oxide layers to be the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c are preferably formed in succession without exposure to the air.
Heat treatment is preferably performed after formation of the oxide stack 404. Heat treatment here may be performed at a temperature higher than or equal to 250° C. and lower than or equal to 650° C., preferably higher than or equal to 300° C. and lower than or equal to 500° C. The heat treatment is performed in an inert gas atmosphere, an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more, or under reduced pressure. Alternatively, the heat treatment may be performed in such a manner that heat treatment is performed in an inert gas atmosphere, and then another heat treatment is performed in an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more in order to compensate desorbed oxygen. By the heat treatment, the crystallinity of the oxide semiconductor layer 404b can be improved and impurities such as hydrogen and water can be removed from the oxide stack 404.
Moreover, by the heat treatment, excess oxygen contained in the base insulating layer 402 can be supplied to the oxide semiconductor layer 404b. Supply of oxygen to the oxide semiconductor layer 404b enables hydrogen in the oxide semiconductor layer 404b to be removed.
Next, a conductive layer which is to be the source electrode layer 406a and the drain electrode layer 406b is formed and partly etched, whereby the source electrode layer 406a and the drain electrode layer 406b are formed (see
The source electrode layer 406a and the drain electrode layer 406b may be formed using a single layer or a stack of a conductive layer containing one or more of aluminum, titanium, chromium, cobalt, nickel, copper, tantalum, and tungsten. Note that the source electrode layer 406a and the drain electrode layer 406b may have the same composition or different compositions.
Next, the gate insulating layer 408 is formed over the source electrode layer 406a and the drain electrode layer 406b (see
It is preferable to select appropriate conditions so that the oxide stack 404 is not damaged and the defect density in the oxide stack 404 is not increased in forming the gate insulating layer 408. As an example of a way to reduce damage to the oxide stack 404, the gate insulating layer 408 is preferably formed using a plasma CVD apparatus at a high deposition pressure. Specifically, the deposition pressure is preferably set to higher than or equal to 100 Pa and lower than or equal to 300 Pa, further preferably higher than or equal to 100 Pa and lower than or equal to 200 Pa. Increasing the deposition pressure in a reaction chamber enables high-density plasma to be generated, leading to a reduction in plasma damage to the deposition surface.
Further, by increasing the pressure in deposition of the gate insulating layer 408, a semiconductor device with high field-effect mobility and excellent electrical characteristics can be provided.
Next, a conductive layer which is to be the gate electrode layer 410 is formed over the gate insulating layer 408 and etched, whereby the gate electrode layer 410 is formed (see
Next, the interlayer insulating layer 412 and the interlayer insulating layer 414 are formed over the gate insulating layer 408 and the gate electrode layer 410 (see
Heat treatment is preferably performed after formation of the interlayer insulating layer 414. Heat treatment makes it possible to fill oxygen vacancies which are formed in the formed oxide semiconductor layer 404b owing to etching, plasma treatment, and the like in the process for forming the source electrode layer 406a, the drain electrode layer 406b, the gate electrode layer 410, and the like.
When heat treatment is performed here, oxygen can be supplied to the oxide semiconductor layer 404b from the base insulating layer 402 or the gate insulating layer 408, or both, so that oxygen vacancies in the oxide semiconductor layer 404b are reduced and the reliability of the transistor can be improved.
Here, the results of analyzing the amount of released oxygen after silicon oxynitride films are subjected to heat treatment are shown.
First, a method for fabricating samples is described. Thermal oxidation was performed on a silicon substrate in an HCl atmosphere to form a thermal oxide film with a thickness of 100 nm on a surface of the substrate. The thermal oxidation was performed at 950° C. for one hour in a thermal oxidation atmosphere containing HCl at 3 vol % with respect to oxygen.
Next, a 300-nm-thick silicon oxynitride film was formed over the thermal oxide film. For the formation of the silicon oxynitride film, silane with a flow rate of 2.3 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 50 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the silicon substrate at the formation of the silicon oxynitride film was 400° C. After the formation, heat treatment was performed at 450° C. for one hour.
Next, oxygen was implanted to the silicon oxynitride film by an ion implantation method. The conditions of the oxygen implantation were as follows: an acceleration voltage of 60 kV and a dosage of 2×1016 ions/cm2.
A 100-nm-thick In—Ga—Zn oxide layer was formed over the silicon oxynitride film by a sputtering method. Here, the In—Ga—Zn oxide layer was formed under the following conditions: a sputtering target containing In, Ga, and Zn at an atomic ratio of 1:1:1 was used, Ar with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm were supplied as a sputtering gas to a reaction chamber of a sputtering apparatus, the pressure in the reaction chamber was controlled to 0.4 Pa, and a direct current power of 0.5 kW was supplied. Note that the substrate temperature in the formation of the In—Ga—Zn oxide layer was set at 300° C.
Here, a sample which was not subjected to heat treatment, a sample which was subjected to heat treatment at 450° C. in a nitrogen atmosphere for one hour and then in an oxygen atmosphere for one hour, and a sample which was subjected to heat treatment at 450° C. in a nitrogen atmosphere for one hour and then in an oxygen atmosphere for one hour and then subjected to heat treatment at 400° C. in an oxygen atmosphere for one hour were prepared as Sample A1, Sample A2, and Sample A3, respectively.
After that, Samples A1 to A3 were subjected to etching with an Al mixed-acid etchant (produced by KANTO CHEMICAL CO., INC.), whereby the In—Ga—Zn oxide was removed, and analyzed by TDS; thus, the amount of oxygen released from the silicon oxynitride films, that is, oxygen contained in the samples were measured.
The amount of released oxygen was 1.17×1016 atoms/cm2 in Sample A1 not subjected to heat treatment, 6.23×1015 atoms/cm2 in Sample A2 subjected to heat treatment once, and 5.26×1015 atoms/cm2 in Sample A3 subjected to heat treatment twice.
As shown in
Accordingly, by performing heat treatment again after formation of an interlayer insulating layer, oxygen can be supplied to the oxide semiconductor layer again from the silicon oxynitride film (here, the base insulating layer 402) formed under the oxide semiconductor layer. Oxygen supplied here fills oxygen vacancies which are formed in the oxide semiconductor layer in forming the gate insulating layer, the gate electrode layer, and the like, thus stabilizing the characteristics of the oxide semiconductor layer.
Here, the results of analyzing the spin density in an oxide semiconductor layer in the case where a silicon oxynitride film is formed over the formed oxide semiconductor layer and heat treatment is performed are shown.
A method for fabricating samples is described. First, a 300-nm-thick silicon oxynitride film was formed over a quartz substrate. For the formation of the silicon oxynitride film, silane with a flow rate of 2.3 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 50 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the quartz substrate at the formation of the silicon oxynitride film was 400° C. After the formation, heat treatment was performed at 450° C. for one hour.
Next, oxygen was implanted to the silicon oxynitride film by an ion implantation method. The conditions of the oxygen implantation were as follows: an acceleration voltage of 60 kV and a dosage of 2×1016 ions/cm2.
Then, a 50-nm-thick In—Ga—Zn oxide layer was formed over the silicon oxynitride film by a sputtering method. Here, the In—Ga—Zn oxide layer was formed under the following conditions: a sputtering target containing In, Ga, and Zn at an atomic ratio of 1:1:1 was used, Ar with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm were supplied as a sputtering gas to a reaction chamber of a sputtering apparatus, the pressure in the reaction chamber was controlled to 0.4 Pa, and a direct current power of 0.5 kW was supplied. Note that the substrate temperature in the formation of the In—Ga—Zn oxide layer was set at 300° C.
Here, heat treatment was performed at 450° C. in a nitrogen atmosphere for one hour and then in an oxygen atmosphere for one hour.
Next, a 20-nm-thick silicon oxynitride film was formed over the In—Ga—Zn oxide layer. The silicon oxynitride film was formed under the following conditions: the quartz substrate was placed in a treatment chamber of a plasma CVD apparatus, silane with a flow rate of 1 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to the treatment chamber, and a power of 150 W was supplied with the use of a 60 MHz high-frequency power source. Further, the temperature of the quartz substrate at the formation of the silicon oxynitride film was 350° C. The deposition pressure was 40 Pa, which might not suitable for a gate insulating layer used in a semiconductor device of one embodiment of the present invention.
Here, a sample which was not subjected to heat treatment was prepared as Sample B1. Then, a sample which was subjected to heat treatment at 350° C. in an oxygen atmosphere for one hour was prepared as Sample B2, and a sample which was subjected to heat treatment at 400° C. in an oxygen atmosphere for one hour was prepared as Sample B3.
The samples were subjected to ESR measurement. The ESR measurement was performed under the following conditions: the measurement temperature was room temperature (25° C.), the high-frequency power (power of microwaves) of 9.5 GHz was 20 mW, and the direction of a magnetic field was parallel to a surface of each sample. Note that the lower limit of detection of the spin density corresponding to a signal at a g-factor of 1.93 due to oxygen vacancies in the In—Ga—Zn oxide layer was 1×1017 spins/cm3.
However, the spin density was decreased by heat treatment performed after the formation of the silicon oxynitride film, and became less than the lower limit of detection (1×1017 spins/cm3) for both Sample B2 and Sample B3. Thus, oxygen vacancies generated in the oxide semiconductor layer after formation of the silicon oxynitride film can be filled by heat treatment performed with the oxide semiconductor layer being in contact with the silicon oxynitride film.
In particular, when a film having a property of blocking oxygen is used as the interlayer insulating layer 412 and heat treatment is performed, oxygen released from the base insulating layer 402 or the gate insulating layer 408, or both is prevented from being released to above the oxide semiconductor layer 404b, so that more oxygen can be supplied to the oxide semiconductor layer 404b.
The heat treatment is preferably performed at a temperature higher than or equal to 300° C. and lower than 450° C., further preferably higher than or equal to 350° C. and lower than or equal to 400° C. Note that when a metal with a high oxygen affinity is used for the source electrode layer 406a and the drain electrode layer 406b which are formed in contact with the oxide stack 404 and heat treatment is performed, the metal might extract oxygen from the oxide stack 404. Thus, the temperature range may be appropriately set so that heat treatment is performed at such a temperature that the amount of oxygen supplied from the base insulating layer 402 and the gate insulating layer 408 is larger than the amount of oxygen extracted to enter the source electrode layer 406a and the drain electrode layer 406b.
The above heat treatment can reduce the number of oxygen vacancies in the oxide semiconductor layer 404b, thus stabilizing the characteristics of the oxide semiconductor layer 404b. In particular, when the channel length of the transistor is shortened, the effect of oxygen vacancies in the oxide semiconductor layer on the characteristics of the transistor becomes greater. Thus, the above heat treatment is performed to reduce the number of oxygen vacancies in the oxide semiconductor layer 404b, so that a highly reliable semiconductor device which can maintain normally-off characteristics can be provided even when the channel length is shortened.
Next, openings are formed in the interlayer insulating layer 414, the interlayer insulating layer 412, and the gate insulating layer 408, a conductive layer is formed in the openings, and the conductive layer is etched; thus, the source wiring layer 416a and the drain wiring layer 416b are formed (see
The structure of a semiconductor device of one embodiment of the present invention is not limited to the above structure. For example, the oxide stack 404 may be composed of two layers, the oxide semiconductor layer 404b and the oxide layer 404c, as in a transistor 430 illustrated in
In addition, a source region 405a and a drain region 405b may be formed in the oxide stack 404 as in
Alternatively, as in a transistor 440 illustrated in
Further alternatively, as in a transistor 450 illustrated in
The distance between the first source electrode layer 418a and the first drain electrode layer 418b corresponds to the channel length of the transistor 450. In order that the channel length of the transistor 450 is less than 50 nm, preferably less than 30 nm, a developed mask which is obtained by exposing a resist with use of an electron beam is preferably used as an etching mask, for example. At this time, in an electron beam writing apparatus capable of electron beam irradiation, it is preferable that irradiation be performed with the minimum beam size set to 2 nm or less.
The thickness of a mask that can be formed by an electron beam is small. For this reason, the first source electrode layer 418a and the first drain electrode layer 418b are preferably formed to have a small thickness in consideration of the coverage of the resist functioning as the mask. However, a reduction in the thickness of the first source electrode layer 418a and the first drain electrode layer 418b makes the resistance high. Accordingly, to reduce the resistance, it is preferable to form the second source electrode layer 419a and the second drain electrode layer 419b which can have a large thickness.
Note that the thick second source electrode layer 419a and second drain electrode layer 419b are formed over the thin first source electrode layer 418a and first drain electrode layer 418b in
As an example of a semiconductor device, a circuit diagram of a NOR circuit, which is a logic circuit, in which any of the above transistors can be used is illustrated in
In the NOR circuit illustrated in
In the NOR circuit illustrated in
In the NAND circuit illustrated in
In the NAND circuit illustrated in
By using a transistor including an oxide semiconductor for the channel formation region and having extremely small off-state current, power consumption of the semiconductor device can be sufficiently reduced.
The use of any of the transistors 420, 430, 440, and 450 makes it possible to provide a NOR circuit and a NAND circuit which are miniaturized, have high reliability, and show stable characteristics.
An example of a semiconductor device (memory device) which includes any of the above transistors, which can hold stored data even when not powered, and which has an unlimited number of write cycles is described with reference to
In a transistor 260 illustrated in
Although all the transistors are n-channel transistors here, p-channel transistors can be used as the transistors used for the semiconductor device.
In
The semiconductor device illustrate in
Writing and holding of data will be described. First, the potential of the fourth wiring is set to a potential at which the transistor 262 is turned on, so that the transistor 262 is turned on. Accordingly, the potential of the third wiring is supplied to the gate electrode layer of the transistor 260 and to the capacitor 264. That is, predetermined charge is supplied to the gate electrode layer of the transistor 260 (writing). Here, charge for supplying either of two different potential levels (hereinafter referred to as low-level charge and high-level charge) is given. After that, the potential of the fourth wiring is set to a potential at which the transistor 262 is turned off, so that the transistor 262 is turned off. Thus, the charge given to the gate electrode layer of the transistor 260 is held (holding).
Since the off-state current of the transistor 262 is extremely low, the charge of the gate electrode layer of the transistor 260 is held for a long time.
Next, reading of data will be described. By supplying an appropriate potential (reading potential) to the fifth wiring while supplying a predetermined potential (constant potential) to the first wiring, the potential of the second wiring varies depending on the amount of charge held at the gate electrode layer of the transistor 260. This is because in general, when the transistor 260 is an n-channel transistor, an apparent threshold voltage Vth
Note that in the case where memory cells are arrayed to be used, only data of desired memory cells needs to be read. In the case where such reading is not performed, a potential at which the transistor 260 is turned off regardless of the state of the gate electrode layer, that is, a potential lower than Vth
In the semiconductor device illustrated in
Here, the transistor 262 including an oxide semiconductor has extremely low off-state current. For that reason, a potential of the first terminal of the capacitor 254 (or a charge accumulated in the capacitor 254) can be held for an extremely long time by turning off the transistor 262.
Next, writing and holding of data in the semiconductor device (a memory cell 250) illustrated in
First, the potential of the word line WL is set to a potential at which the transistor 262 is turned on, so that the transistor 262 is turned on. Accordingly, the potential of the bit line BL is supplied to the first terminal of the capacitor 254 (writing). After that, the potential of the word line WL is set to a potential at which the transistor 262 is turned off, so that the transistor 262 is turned off. Thus, the potential of the first terminal of the capacitor 254 is held (holding).
Because the off-state current of the transistor 262 is extremely small, the potential of the first terminal of the capacitor 254 (or a charge accumulated in the capacitor) can be held for an extremely long period.
Next, reading of data will be described. When the transistor 262 is turned on, the bit line BL which is in a floating state and the capacitor 254 are electrically connected to each other, and the charge is redistributed between the bit line BL and the capacitor 254. As a result, the potential of the bit line BL is changed. The amount of change in potential of the bit line BL varies depending on the potential of the first terminal of the capacitor 254 (or the charge accumulated in the capacitor 254).
For example, the potential of the bit line BL after charge redistribution is represented by (CB×VB0+C×V)/(CB+C), where V is the potential of the first terminal of the capacitor 254, C is the capacitance of the capacitor 254, CB is the capacitance of the bit line BL (hereinafter also referred to as bit line capacitance), and VB0 is the potential of the bit line BL before the charge redistribution. Therefore, it can be found that assuming that the memory cell 250 is in either of two states in which the potentials of the first terminal of the capacitor 254 are V1 and V0 (V1>V0), the potential of the bit line BL in the case of holding the potential V1 (=(CB×VB0+C×V1)/(CB+C)) is higher than the potential of the bit line BL in the case of holding the potential V0 (=(CB×VB0+C×V0)/(CB+C)).
Then, by comparing the potential of the bit line BL with a predetermined potential, data can be read.
As described above, the semiconductor device illustrated in
Next, the semiconductor device illustrated in
The semiconductor device illustrated in
In the structure illustrated in
It is preferable that a semiconductor material of a transistor provided in the peripheral circuit 253 be different from that of the transistor 262. For example, silicon, germanium, silicon germanium, silicon carbide, gallium arsenide, or the like can be used, and a single crystal semiconductor is preferably used. Alternatively, an organic semiconductor material or the like may be used. A transistor including such a semiconductor material can operate at sufficiently high speed. Therefore, a variety of circuits (e.g., a logic circuit or a driver circuit) which need to operate at high speed can be favorably realized by the transistor.
Note that
When a transistor including an oxide semiconductor in a channel formation region is used as the transistor 262, stored data can be held for a long time. In other words, power consumption can be sufficiently reduced because a semiconductor device in which refresh operation is unnecessary or the frequency of refresh operation is extremely low can be provided.
Further, a transistor which includes an oxide stack and in which an oxide semiconductor layer to be a channel formation region is apart from the surface of the oxide stack is used as the transistor. Thus, a highly reliable semiconductor device that shows stable electrical characteristics can be provided.
The transistor 300 and the transistor 320 are each a transistor obtained by forming an element isolation insulating layer 302 in a silicon substrate and forming a region to be a channel formation region in a region surrounded by the element isolation insulating layer 302. A gate insulating layer 308 and a gate electrode layer 310 are formed to overlap with the channel formation region. A source region 306a and a drain region 306b are formed in contact with the channel formation region, and a source electrode layer 316a and a drain electrode layer 316b are formed in contact with the source region 306a and the drain region 306b.
Although the above structure is shown as an example of the structure of each of the transistors 300 and 320, a known structure of a transistor can be applied to the transistors 300 and 320.
An insulating layer 328, an insulating layer 330, and an insulating layer 332 are formed over the transistors 300 and 320. The insulating layer 332 serves as a protective film which prevents entry of an impurity such as silicon or hydrogen to an oxide semiconductor layer in the transistor 340 from the transistors 300 and 320. The insulating layer 330 prevents entry of oxygen or the like included in the transistor 340 to the transistors 300 and 320.
A conductive layer 322, a conductive layer 324, a conductive layer 326, and the like are formed in openings provided in the insulating layers, and the drain electrode layer 316b of the transistor 320 is electrically connected to a drain electrode of the transistor 340 through the conductive layers.
As illustrated in
Although the variety of films such as the metal film, the semiconductor layer, and the inorganic insulating film which are described in the above embodiment can be formed by a sputtering method or a plasma chemical vapor deposition (CVD) method, such films may be formed by another method, e.g., a thermal CVD method. A metal organic chemical vapor deposition (MOCVD) method or an atomic layer deposition (ALD) method may be employed as an example of a thermal CVD method.
A thermal CVD method has an advantage that no defect due to plasma damage is generated since it does not utilize plasma for forming a film.
Deposition by a thermal CVD method may be performed in such a manner that the pressure in a chamber is set to an atmospheric pressure or a reduced pressure, and a source gas and an oxidizer are supplied to the chamber at a time and react with each other in the vicinity of the substrate or over the substrate.
Deposition by an ALD method may be performed in such a manner that the pressure in a chamber is set to an atmospheric pressure or a reduced pressure, source gases for reaction are sequentially introduced into the chamber, and then the sequence of the gas introduction is repeated. For example, two or more kinds of source gases are sequentially supplied to the chamber by switching respective switching valves (also referred to as high-speed valves). For example, a first source gas is introduced, an inert gas (e.g., argon or nitrogen) or the like is introduced at the same time as or after the introduction of the first gas so that the source gases are not mixed, and then a second source gas is introduced. Note that in the case where the first source gas and the inert gas are introduced at a time, the inert gas serves as a carrier gas, and the inert gas may also be introduced at the same time as the introduction of the second source gas. Alternatively, the first source gas may be exhausted by vacuum evacuation instead of the introduction of the inert gas, and then the second source gas may be introduced. The first source gas is adsorbed on the surface of the substrate to form a first single-atomic layer; then the second source gas is introduced to react with the first single-atomic layer; as a result, a second single-atomic layer is stacked over the first single-atomic layer, so that a thin film is formed. The sequence of the gas introduction is repeated plural times until a desired thickness is obtained, whereby a thin film with excellent step coverage can be formed. The thickness of the thin film can be adjusted by the number of repetitions times of the sequence of the gas introduction; therefore, an ALD method makes it possible to accurately adjust a thickness and thus is suitable for manufacturing a minute FET.
The variety of films such as the metal film, the semiconductor layer, and the inorganic insulating film which are described in the above embodiment can be formed by a thermal CVD method such as a MOCVD method or an ALD method. For example, in the case where an InGaZnOX (X>0) film is formed, trimethylindium, trimethylgallium, and diethylzinc are used. Note that the chemical formula of trimethylindium is (CH3)3In. The chemical formula of trimethylgallium is (CH3)3Ga.
The chemical formula of diethylzinc is (CH3)2Zn. Without limitation to the above combination, triethylgallium (chemical formula: (C2H5)3Ga) can be used instead of trimethylgallium and dimethylzinc (chemical formula: (C2H5)2Zn) can be used instead of diethylzinc.
For example, in the case where a hafnium oxide film is formed, two kinds of gases, i.e., ozone (O3) as an oxidizer and a source gas which is obtained by vaporizing a solvent and liquid containing a hafnium precursor compound (a hafnium alkoxide solution, typically tetrakis(dimethylamide)hafnium (TDMAH)) are used. Note that the chemical formula of tetrakis(dimethylamide)hafnium is Hf[N(CH3)2]4. Examples of another material liquid include tetrakis(ethylmethylamide)hafnium.
For example, in the case where an aluminum oxide film is formed, two kinds of gases, e.g., H2O as an oxidizer and a source gas which is obtained by vaporizing a solvent and liquid containing an aluminum precursor compound (e.g., trimethylaluminum (TMA)) are used. Note that the chemical formula of trimethylaluminum is Al(CH3)3. Examples of another material liquid include tris(dimethylamide)aluminum, triisobutylaluminum, and aluminum tris(2,2,6,6-tetramethyl-3,5-heptanedionato).
For example, in the case where a silicon oxide film is formed, hexadichlorosilane is adsorbed on a surface where a film is to be formed, chlorine contained in the adsorbate is removed, and radicals of an oxidizing gas (e.g., O2 or dinitrogen monoxide) are supplied to react with the adsorbate.
For example, in the case where a tungsten film is formed using a deposition apparatus employing ALD, a WF6 gas and a B2H6 gas are sequentially introduced plural times to form an initial tungsten film, and then a WF6 gas and an H2 gas are introduced at a time, so that a tungsten film is formed. Note that an SiH4 gas may be used instead of a B2H6 gas.
For example, in the case where an oxide semiconductor film, e.g., an InGaZnOX (X>0) film is formed using a deposition apparatus employing ALD, an In(CH3)3 gas and an O3 gas are sequentially introduced plural times to form an InO2 layer, a Ga(CH3)3 gas and an O3 gas are introduced at a time to form a GaO layer, and then a Zn(CH3)2 gas and an O3 gas are introduced at a time to form a ZnO layer. Note that the order of these layers is not limited to this example. A mixed compound layer such as an InGaO2 layer, an InZnO2 layer, a GalnO layer, a ZnInO layer or a GaZnO layer may be formed by mixing of these gases. Note that although an H2O gas which is obtained by bubbling with an inert gas such as Ar may be used instead of an O3 gas, it is preferable to use an O3 gas, which does not contain H. Further, instead of an In(CH3)3 gas, an In(C2H5)3 gas may be used. Instead of a Ga(CH3)3 gas, a Ga(C2H5)3 gas may be used. Instead of an In(CH3)3 gas, an In(C2H5)3 may be used. Furthermore, a Zn(CH3)2 gas may be used.
Examples of application of any of the semiconductor devices described above to electronic devices such as a smartphone or an e-book reader will be described with reference to
First, image data (input image data A) is formed by an application processor (not shown). The input image data A is stored in the memory 952 through the switch 954. The image data (stored image data A) stored in the memory 952 is transmitted to the display 957 through the switch 955 and the display controller 956, and is displayed on the display 957.
In the case where the input image data A is not changed, the stored image data A is read from the memory 952 through the switch 955 by the display controller 956 normally at a frequency of approximately 30 Hz to 60 Hz.
Next, for example, when data displayed on the screen is rewritten by a user (that is, in the case where the input image data A is changed), new image data (input image data B) is formed by the application processor. The input image data B is stored in the memory 953 through the switch 954. Also during this time, the stored image data A is regularly read from the memory 952 through the switch 955. After the completion of storing the new image data (stored image data B) in the memory 953, from the next frame for the display 957, the stored image data B starts to be read, is transmitted to the display 957 through the switch 955 and the display controller 956, and is displayed on the display 957. This reading operation continues until another new image data is stored in the memory 952.
By alternately writing and reading image data to and from the memory 952 and the memory 953 as described above, images are displayed on the display 957. Note that the memory 952 and the memory 953 are not limited to separate memories, and a single memory may be divided and used. By employing any of the semiconductor devices described above for the memory 952 and the memory 953, writing and reading of data can be performed at high speed, data can be held for a long time, and power consumption can be sufficiently reduced. Further, a semiconductor device which is hardly affected by entry of water, moisture, and the like from the outside and has high reliability can be provided.
Here, any of the semiconductor devices described above can be used for the memory circuit 1007 in
Any of the above semiconductor devices can be used for the display portion 9631a and the display portion 9631b, so that the tablet terminal can have high reliability. Further, the above semiconductor devices may be used in combination as appropriate.
Part of the display portion 9631a can be a touch panel region 9632a, and data can be input by touching operation keys 9638 that are displayed. Although a structure in which a half region in the display portion 9631a has only a display function and the other half region also has a touch panel function is shown as an example, the display portion 9631a is not limited to the structure. For example, the display portion 9631a can display a keyboard in the whole region to be a touch panel, and the display portion 9631b can be used as a display screen.
As in the display portion 9631a, part of the display portion 9631b can be a touch panel region 9632b. When a keyboard display switching button 9639 displayed on the touch panel is touched with a finger, a stylus, or the like, a keyboard can be displayed on the display portion 9631b.
Touch input can be performed in the touch panel region 9632a and the touch panel region 9632b at the same time.
The display mode switch 9034 can switch the display between portrait mode, landscape mode, and the like, and between monochrome display and color display, for example. The power saver switch 9036 can control display luminance in accordance with the amount of external light in use of the tablet terminal detected by an optical sensor incorporated in the tablet terminal. In addition to the optical sensor, another detection device including a sensor for detecting inclination, such as a gyroscope or an acceleration sensor, may be incorporated in the tablet terminal.
Although the display portion 9631a and the display portion 9631b have the same display area in
The tablet terminal is closed in
Since the tablet terminal is foldable, the housing 9630 can be closed when the tablet terminal is not used. As a result, the display portion 9631a and the display portion 9631b can be protected; thus, a tablet terminal which has excellent durability and excellent reliability in terms of long-term use can be provided.
In addition, the tablet terminal illustrated in
In this example, silicon oxynitride films which can be used as a gate insulating layer included in a semiconductor device of one embodiment of the present invention were fabricated, and characteristics thereof were evaluated.
First, a method for fabricating samples is described.
A 100-nm-thick silicon oxynitride film was formed over a quartz substrate. The silicon oxynitride film was formed under the following conditions: the substrate was placed in a treatment chamber of a plasma CVD apparatus, silane with a flow rate of 1 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to the treatment chamber, and a power of 150 W was supplied with the use of a 60 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 350° C. Note that the plasma CVD apparatus used in this example is a parallel-plate plasma CVD apparatus in which the electrode area is 615 cm2 and the density of power applied to a wafer is 2.4×10−1 W/cm2.
Here, the silicon oxynitride film was deposited at a pressure of 200 Pa for Sample C1, 100 Pa for Sample C2, and 40 Pa for Comparative Sample C3. Sample C1 and Sample C2 are silicon oxynitride films deposited at pressures greater than or equal to 100 Pa, which are conditions suitable for a gate insulating layer included in a semiconductor device of one embodiment of the present invention. On the other hand, Comparative Sample C3 is a silicon oxynitride film deposited under a condition which is not suitable for a gate insulating layer included in a semiconductor device of one embodiment of the present invention.
Next, the samples were subjected to ESR measurement. In the ESR measurement performed at a predetermined temperature, a value of a magnetic field (H0) where a microwave is absorbed is used for an equation g=hν/βH0; thus, a parameter “g-factor” can be obtained. Note that the frequency of the microwave is denoted by ν, and the Planck constant and the Bohr magneton are denoted by, respectively, h and β, which are both constants.
Here, the ESR measurement was performed under the following conditions. The measurement temperature was room temperature (25° C.), the high-frequency power (power of microwaves) of 9.5 GHz was 20 mW, and the direction of a magnetic field was parallel to a surface of each sample. The spin density corresponding to a signal at a g-factor of 2.001 due to dangling bonds in the silicon oxynitride film was measured. The lower limit of detection was 1×1017 spins/cm3 (1×1011 spins/cm2 per unit area).
Next, the integrated intensity of the signal at a g-factor of around 2.001 in the spectrum shown in each of
Next, the wet etching rate of each sample was measured. Etching was performed at 20° C. using a mixed solution containing 6.7% ammonium hydrogen fluoride (NH4HF2) and 12.7% ammonium fluoride (NH4F) (product name: LAL 500, produced by Stella Chemifa Corporation) as an etchant.
Here, the wet etching rate of Comparative Sample C3 (deposition pressure: 40 Pa) was 108.9 [nm/min], the wet etching rate of Sample C2 (deposition pressure: 100 Pa) was 97.9 [nm/min], and the wet etching rate of Sample C1 (deposition pressure: 200 Pa) was 76.4 [nm/min]. The results show that as the deposition pressure is increased, the etching rate is decreased and a denser film is formed.
Next, the nitrogen concentration in the depth direction in each sample was analyzed by SIMS. The results are shown in
In
The average nitrogen concentration in a region (depth: 20 nm to 60 nm) that is less affected by an interface was 5.7×1020 atoms/cm3 in Sample C1, 3.6×1020 atoms/cm3 in Sample C2, and 1.7×1020 atoms/cm3 in Comparative Sample C3. By comparing the nitrogen concentrations in the samples, it was found that Sample C1 had the highest nitrogen concentration and Comparative Sample C3 had the lowest nitrogen concentration.
In this example, silicon oxynitride films which can be used as a gate insulating layer included in a semiconductor device of one embodiment of the present invention were fabricated, and characteristics thereof were evaluated.
A 100-nm-thick silicon oxynitride film was formed over a silicon substrate. Conditions for forming the silicon oxynitride film were similar to those in Example 1. Here, the silicon oxynitride film was deposited at a pressure of 200 Pa for Sample F1, 100 Pa for Sample F2, and 40 Pa for Comparative Sample F3.
Similarly,
Similarly,
Similarly,
According to
In this example, the silicon oxynitride films described in Example 1 were fabricated and binding states in the films were evaluated.
A 20-nm-thick silicon oxynitride film was formed over a silicon substrate. Conditions for forming the silicon oxynitride film were similar to those in Example 1. Here, the silicon oxynitride film was deposited at a pressure of 200 Pa for Sample G1, 100 Pa for Sample G2, and 40 Pa for Comparative Sample G3.
Next, evaluation of binding states in the samples was carried out by X-ray photoelectron spectroscopy (XPS). The results are shown in
Next, high-resolution XPS spectra of each sample in the vicinity of peaks are shown in
By comparing the high-resolution XPS spectra in
In this example, the silicon oxynitride film described in Example 1 was formed over an oxide semiconductor layer, and the oxide semiconductor layer was evaluated.
First, a method for fabricating samples is described.
A 100-nm-thick In—Ga—Zn oxide layer was formed over a quartz substrate by a sputtering method. Here, the In—Ga—Zn oxide layer was formed under the following conditions: a sputtering target containing In, Ga, and Zn at an atomic ratio of 1:1:1 was used, Ar with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm were supplied as a sputtering gas to a reaction chamber of a sputtering apparatus, the pressure in the reaction chamber was controlled to 0.4 Pa, and a direct current power of 0.5 kW was supplied. Note that the substrate temperature in the formation of the In—Ga—Zn oxide layer was set at 300° C.
Next, a 100-nm-thick silicon oxynitride film was formed over the In—Ga—Zn oxide layer. Conditions for forming the silicon oxynitride film were similar to those in Example 1. Here, the silicon oxynitride film was deposited at a pressure of 200 Pa for Sample D1, 100 Pa for Sample D2, and 40 Pa for Comparative Sample D3.
Sample D1, Sample D2, and Comparative Sample D3 were subjected to ESR measurement. The ESR measurement was performed under the following conditions: the measurement temperature was room temperature (25° C.), the high-frequency power (power of microwaves) of 9.5 GHz was 20 mW, and the direction of a magnetic field was parallel to a surface of each sample. Note that the lower limit of detection of the spin density corresponding to a signal at a g-factor of 1.93 due to oxygen vacancies in the In—Ga—Zn oxide layer was 1×1017 spins/cm3 (1×1011 spins/cm2 per unit area).
As shown in
The above results show that when the pressure in deposition of a gate insulating layer over an In—Ga—Zn oxide is increased, oxygen vacancies in the In—Ga—Zn oxide can be reduced and the In—Ga—Zn oxide can have stable characteristics.
In this example, the silicon oxynitride film described in Example 1 was formed over an oxide semiconductor layer, and the impurity concentrations in the silicon oxynitride film and in the oxide semiconductor layer were measured.
First, a method for fabricating samples is described.
A 300-nm-thick silicon oxide film was formed over a single crystal silicon substrate by a sputtering method. The silicon oxide film was formed under the following conditions: oxygen with a flow rate of 50 sccm was supplied as a sputtering gas to a reaction chamber of a sputtering apparatus, the pressure in the reaction chamber was controlled to 0.4 Pa, and a direct current power of 1.5 kW was supplied. The substrate temperature was set to 100° C.
Then, a 100-nm-thick In—Ga—Zn oxide layer was formed over the silicon oxide film by a sputtering method. Here, the In—Ga—Zn oxide layer was formed under the following conditions: a sputtering target containing In, Ga, and Zn at an atomic ratio of 1:1:1 was used, Ar with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm were supplied as a sputtering gas to a reaction chamber of a sputtering apparatus, the pressure in the reaction chamber was controlled to 0.4 Pa, and a direct current power of 0.5 kW was supplied. Note that the substrate temperature in the formation of the In—Ga—Zn oxide layer was set at 300° C.
Here, heat treatment was performed. The heat treatment was performed at 450° C. in a nitrogen atmosphere for one hour and then in an oxygen atmosphere for one hour.
Next, a 20-nm-thick silicon oxynitride film was formed over the In—Ga—Zn oxide layer by a plasma CVD method. Conditions for forming the silicon oxynitride film were similar to those in Example 1. Here, the silicon oxynitride film was deposited at a pressure of 200 Pa for Sample E1, 100 Pa for Sample E2, and 40 Pa for Comparative Sample E3.
Next, the impurity concentrations in the oxide semiconductor layer were measured in Sample E1, Sample E2, and Comparative Sample E3.
Here, the hydrogen concentration, the carbon concentration, the nitrogen concentration, and the fluorine concentration in the depth direction in each sample were analyzed by SIMS. The results are shown in
In
The hydrogen concentration in the In—Ga—Zn oxide layer in Sample E1 was lower than those in Sample E2 and Comparative Sample E3. There was almost no difference between the samples in the carbon concentration, the nitrogen concentration, and the fluorine concentration in the In—Ga—Zn oxide layer.
Hydrogen is an impurity for an oxide semiconductor and may cause a defect state or the like. Thus, the hydrogen concentration in the oxide semiconductor layer is preferably as low as possible. This means that the silicon oxynitride film in Sample E1 is particularly suitable for a transistor including an oxide semiconductor layer.
In this example, a transistor including a gate insulating layer which can be used in a semiconductor device of one embodiment of the present invention was compared with Comparative Transistor in electrical characteristics.
First, a method for fabricating transistors is described.
A 300-nm-thick silicon oxynitride film as a base insulating layer was formed over a single crystal silicon substrate by a plasma CVD method. For the formation of the silicon oxynitride film, silane with a flow rate of 2.3 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 50 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 450° C. Note that the plasma CVD apparatus used in this example is a parallel-plate plasma CVD apparatus in which the electrode area is 615 cm2 and the power density is 8.1×10−2 W/cm2.
Next, a surface of the silicon oxynitride film was subjected to polishing treatment by a chemical mechanical polishing method, so that the average surface roughness (Ra) of the surface of the silicon oxynitride film was approximately 0.2 nm. Then, oxygen was implanted to the silicon oxynitride film by an ion implantation method. The conditions of the oxygen implantation were as follows: an acceleration voltage of 60 kV and a dosage of 2×1016 ions/cm2.
A 15-nm-thick In—Ga—Zn oxide layer as an oxide semiconductor layer was formed over the base insulating layer. The In—Ga—Zn oxide layer was formed by a sputtering method using an oxide target containing In, Ga, and Zn at an atomic ratio of 1:1:1 under the following conditions: argon with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm as a sputtering gas were supplied, the pressure was 0.4 Pa, the power was 0.5 kW, and the substrate temperature was 300° C.
Next, heat treatment was performed. The heat treatment was performed at 450° C. in a nitrogen atmosphere for one hour and then in an oxygen atmosphere for one hour.
Then, the In—Ga—Zn oxide layer was etched by an inductively coupled plasma (ICP) etching method under the following conditions: BCl3 with a flow rate of 60 sccm and Cl2 with a flow rate of 20 sccm as an etching gas were supplied, the power was 450 W, the bias power was 100 W, and the pressure was 1.9 Pa. By this etching, the In—Ga—Zn oxide layer was processed into an island-shaped oxide semiconductor layer.
Next, a 100-nm-thick tungsten film to be a source electrode layer and a drain electrode layer was formed over the base insulating layer and the oxide semiconductor layer by a sputtering method.
Then, the tungsten film was etched by an ICP etching method. This etching included first etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa; second etching in which oxygen (O2) with a flow rate of 100 sccm was supplied as an etching gas, the power was 2000 W, the bias power was 0 W, and the pressure was 3 Pa; and third etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa. By this etching, the source electrode layer and the drain electrode layer having stepped-shape periphery portions were formed.
Next, a 20-nm-thick silicon oxynitride film to be a gate insulating layer was formed over the source electrode layer and the drain electrode layer. For the formation of the silicon oxynitride film, silane with a flow rate of 1 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 150 W was supplied with the use of a 60 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 350° C. Here, the deposition pressure was set to 200 Pa for Example Transistor and 40 Pa for Comparative Transistor.
A stack of a 30-nm-thick tantalum nitride film and a 135-nm-thick tungsten film to be a gate electrode layer was formed over the gate insulating layer by a sputtering method. Deposition conditions were as follows: for the tantalum nitride film, argon (Ar) with a flow rate of 50 sccm and nitrogen (N2) with a flow rate of 10 sccm were supplied, the pressure was 0.6 Pa, and the power was 1 kW; and for the tungsten film, argon (Ar) with a flow rate of 100 sccm was supplied, the pressure was 2 Pa, and the power was 4 kW.
Next, the stack of the tantalum nitride film and the tungsten film was etched by an ICP etching method. This etching included first etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa; and second etching in which chlorine (Cl2) with a flow rate of 100 sccm was supplied as an etching gas, the power was 2000 W, the bias power was 50 W, and the pressure was 0.67 Pa.
Next, a stack of a 50-nm-thick silicon nitride film and a 300-nm-thick silicon oxynitride film to be an interlayer insulating layer was formed. The silicon nitride film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 20 sccm and nitrogen with a flow rate of 500 sccm as a source gas were supplied to a treatment chamber, and a power of 900 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon nitride film was 350° C. The silicon oxynitride film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 5 sccm and dinitrogen monoxide with a flow rate of 1000 sccm as a source gas were supplied to a treatment chamber, and a power of 35 W was supplied with the use of a 13.56 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 325° C.
In
Example Transistor and Comparative Transistor had almost the same Vg-Id characteristics, whereas Example Transistor had higher field-effect mobility than Comparative Transistor at low gate voltage. In particular, Example Transistor had a field-effect mobility as high as about 5 cm2/Vs at a gate voltage of 1 V.
These results show that a transistor including a gate insulating layer deposited at a high pressure, which can be used in a semiconductor device of one embodiment of the present invention, is capable of high-speed operation even at a low voltage.
In this example, characteristics of transistors, each of which is a semiconductor device of one embodiment of the present invention, were evaluated. First, a method for fabricating the transistors employed in this example is described. In this example, transistors with a structure similar to that of the transistor illustrated in
A 300-nm-thick silicon oxynitride film as the base insulating layer 402 was formed over a single crystal silicon substrate by a plasma CVD method. For the formation of the silicon oxynitride film, silane with a flow rate of 2.3 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 50 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 450° C. Note that the plasma CVD apparatus used in this example is a parallel-plate plasma CVD apparatus in which the electrode area is 615 cm2 and the power density is 8.1×10−2 W/cm2.
Next, a surface of the silicon oxynitride film was subjected to polishing treatment by a chemical mechanical polishing method, so that the average surface roughness (Ra) of the surface of the silicon oxynitride film was approximately 0.2 nm. Then, oxygen was implanted to the silicon oxynitride film by an ion implantation method. The conditions of the oxygen implantation were as follows: an acceleration voltage of 60 kV and a dosage of 2×1016 ions/cm2.
Next, in order to form the oxide stack 404, an oxide layer, an oxide semiconductor layer, and another oxide layer were formed in succession. As an oxide layer to be the oxide layer 404a, a 5-nm-thick In—Ga—Zn oxide layer was formed by a sputtering method using an oxide target containing In, Ga, and Zn at an atomic ratio of 1:3:2. Deposition conditions were as follows: argon with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm as a sputtering gas were supplied, the pressure was 0.4 Pa, the power was 0.5 kW, and the substrate temperature was 200° C.
As an oxide semiconductor layer to be the oxide semiconductor layer 404b, a 15-nm-thick In—Ga—Zn oxide layer was formed by a sputtering method using an oxide target containing In, Ga, and Zn at an atomic ratio of 1:1:1. Deposition conditions were as follows: argon with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm as a sputtering gas were supplied, the pressure was 0.4 Pa, the power was 0.5 kW, and the substrate temperature was 300° C. A 5-nm-thick oxide layer to be the oxide layer 404c was formed over the oxide semiconductor layer under conditions similar to those for the oxide layer to be the oxide layer 404a.
Then, the stack of the In—Ga—Zn oxide layers was etched by an inductively coupled plasma (ICP) etching method under the following conditions: boron trichloride (BCl3) with a flow rate of 60 sccm and chlorine (Cl2) with a flow rate of 20 sccm as an etching gas were supplied, the power was 450 W, the bias power was 100 W, and the pressure was 1.9 Pa. By this etching, the stack was processed into an island shape and the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c were formed.
Next, a 100-nm-thick tungsten film to be the source electrode layer 406a and the drain electrode layer 406b was formed over the base insulating layer 402 and the oxide stack 404 by a sputtering method.
Then, the tungsten film was etched by an ICP etching method. This etching included first etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa; second etching in which oxygen (O2) with a flow rate of 100 sccm was supplied as an etching gas, the power was 2000 W, the bias power was 0 W, and the pressure was 3 Pa; and third etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa. By this etching, the source electrode layer 406a and the drain electrode layer 406b having stepped-shape periphery portions were formed.
Next, a 20-nm-thick silicon oxynitride film to be the gate insulating layer 408 was formed over the source electrode layer 406a and the drain electrode layer 406b. For the formation of the silicon oxynitride film, silane with a flow rate of 1 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 150 W was supplied with the use of a 60 MHz high-frequency power source. Further, the temperature of the substrate was 350° C. and the deposition pressure was 200 Pa at the formation of the silicon oxynitride film.
Then, a stack of a 30-nm-thick tantalum nitride film and a 135-nm-thick tungsten film to be the gate electrode layer 410 was formed over the gate insulating layer 408 by a sputtering method. Deposition conditions were as follows: for the tantalum nitride film, argon (Ar) with a flow rate of 50 sccm and nitrogen (N2) with a flow rate of 10 sccm were supplied, the pressure was 0.6 Pa, and the power was 1 kW; and for the tungsten film, argon (Ar) with a flow rate of 100 sccm was supplied, the pressure was 2 Pa, and the power was 4 kW.
Next, the stack of the tantalum nitride film and the tungsten film was etched by an ICP etching method. This etching included first etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa; and second etching in which chlorine (Cl2) with a flow rate of 100 sccm was supplied as an etching gas, the power was 2000 W, the bias power was 50 W, and the pressure was 0.67 Pa.
Next, a stack of a 50-nm-thick silicon nitride film and a 300-nm-thick silicon oxynitride film to be the interlayer insulating layer 412 was formed. The silicon nitride film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 20 sccm and nitrogen with a flow rate of 500 sccm as a source gas were supplied to a treatment chamber, and a power of 900 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon nitride film was 350° C. The silicon oxynitride film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 5 sccm and dinitrogen monoxide with a flow rate of 1000 sccm as a source gas were supplied to a treatment chamber, and a power of 35 W was supplied with the use of a 13.56 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 325° C.
After formation of the interlayer insulating layer 412, heat treatment was performed in an oxygen atmosphere. Here, the transistor which was subjected to heat treatment at 350° C. for one hour is Sample H1, and the transistor which was subjected to heat treatment at 450° C. for one hour is Sample H2.
Next, a method for fabricating Comparative Sample H3 is described. Comparative Sample H3 has the same structure as Sample H1 and Sample H2 except that the oxide layer 404a and the oxide layer 404c are omitted and that heat treat after formation of the interlayer insulating layer 412 is skipped.
The electrical characteristics of Sample H1, Sample H2, and Comparative Sample H3 fabricated in the above manner were measured.
The dotted line, the solid line, and the dashed-dotted line in each of
Next, Sample H1, Sample H2, and Comparative Sample H3 were subjected to a bias-temperature stress test (BT stress test) and the characteristics thereof were compared.
A measurement method in a positive BT stress test is described. To measure electrical characteristics in the initial state (a state before stress application) of the target transistors, a change in current (drain current (Id)) between the source and the drain, that is, Vg-Id characteristics were measured under the following conditions: the substrate temperature was 40° C., the drain voltage was 0.1 V or 3.3 V, and the gate voltage was swept from −4 V to +4 V.
Next, the substrate temperature was increased to 150° C., and then, the drain voltage of each transistor was set to 0 V. After that, a gate voltage of 3.3 V was applied so that the intensity of the electric field applied to the gate insulating layer was 1.65 MV/cm. The gate voltage was kept being applied for 3600 seconds.
Note that a gate voltage of −3.3 V was applied in a negative BT stress test.
It was found from the above results that a transistor of one embodiment of the present invention is a highly reliable transistor which has a high threshold voltage (normally-off electrical characteristics), low off-state current, and a small amount of change in a gate BT stress test.
In this example, characteristics of transistors, each of which is a semiconductor device of one embodiment of the present invention, were evaluated. First, a method for fabricating the transistors employed in this example is described. In this example, transistors with a structure similar to that of the transistor illustrated in
A 300-nm-thick silicon oxynitride film as the base insulating layer 402 was formed over a single crystal silicon substrate by a plasma CVD method. For the formation of the silicon oxynitride film, silane with a flow rate of 2.3 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 50 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 450° C. Note that the plasma CVD apparatus used in this example is a parallel-plate plasma CVD apparatus in which the electrode area is 615 cm2 and the power density is 8.1×10−2 W/cm2.
Next, a surface of the silicon oxynitride film was subjected to polishing treatment by a chemical mechanical polishing method, so that the average surface roughness (Ra) of the surface of the silicon oxynitride film was approximately 0.2 nm. Then, oxygen was implanted to the silicon oxynitride film by an ion implantation method. The conditions of the oxygen implantation were as follows: an acceleration voltage of 60 kV and a dosage of 2×1016 ions/cm2.
Next, in order to form the oxide stack 404, an oxide layer, an oxide semiconductor layer, and another oxide layer were formed in succession. As an oxide layer to be the oxide layer 404a, an In—Ga—Zn oxide layer was formed by a sputtering method using an oxide target containing In, Ga, and Zn at an atomic ratio of 1:3:2. The thickness of the In—Ga—Zn oxide layer was varied (5 nm and 20 nm). Deposition conditions were as follows: argon with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm as a sputtering gas were supplied, the pressure was 0.4 Pa, the power was 0.5 kW, and the substrate temperature was 200° C.
As an oxide semiconductor layer to be the oxide semiconductor layer 404b, a 15-nm-thick In—Ga—Zn oxide layer was formed by a sputtering method using an oxide target containing In, Ga, and Zn at an atomic ratio of 1:1:1. Deposition conditions were as follows: argon with a flow rate of 30 sccm and oxygen with a flow rate of 15 sccm as a sputtering gas were supplied, the pressure was 0.4 Pa, the power was 0.5 kW, and the substrate temperature was 300° C. A 5-nm-thick oxide layer to be the oxide layer 404c was formed over the oxide semiconductor layer under conditions similar to those for the oxide layer to be the oxide layer 404a.
Then, the stack of the In—Ga—Zn oxide layers was etched by an inductively coupled plasma (ICP) etching method under the following conditions: boron trichloride (BCl3) with a flow rate of 60 sccm and chlorine (Cl2) with a flow rate of 20 sccm as an etching gas were supplied, the power was 450 W, the bias power was 100 W, and the pressure was 1.9 Pa. By this etching, the stack was processed into an island shape and the oxide layer 404a, the oxide semiconductor layer 404b, and the oxide layer 404c were formed.
Next, a 100-nm-thick tungsten film to be the source electrode layer 406a and the drain electrode layer 406b was formed over the base insulating layer 402 and the oxide stack 404 by a sputtering method.
Then, the tungsten film was etched by an ICP etching method. This etching included first etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa; second etching in which oxygen (O2) with a flow rate of 100 sccm was supplied as an etching gas, the power was 2000 W, the bias power was 0 W, and the pressure was 3 Pa; and third etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa. By this etching, the source electrode layer 406a and the drain electrode layer 406b having stepped-shape periphery portions were formed.
Next, a 20-nm-thick silicon oxynitride film to be the gate insulating layer 408 was formed over the source electrode layer 406a and the drain electrode layer 406b. For the formation of the silicon oxynitride film, silane with a flow rate of 1 sccm and dinitrogen monoxide with a flow rate of 800 sccm as a source gas were supplied to a treatment chamber, and a power of 150 W was supplied with the use of a 60 MHz high-frequency power source. Further, the temperature of the substrate was 350° C. and the deposition pressure was varied (200 Pa, 100 Pa, and 40 Pa) at the formation of the silicon oxynitride film.
Then, a stack of a 30-nm-thick tantalum nitride film and a 135-nm-thick tungsten film to be the gate electrode layer 410 was formed over the gate insulating layer 408 by a sputtering method. Deposition conditions were as follows: for the tantalum nitride film, argon (Ar) with a flow rate of 50 sccm and nitrogen (N2) with a flow rate of 10 sccm were supplied, the pressure was 0.6 Pa, and the power was 1 kW; and for the tungsten film, argon (Ar) with a flow rate of 100 sccm was supplied, the pressure was 2 Pa, and the power was 4 kW.
Next, the stack of the tantalum nitride film and the tungsten film was etched by an ICP etching method. This etching included first etching in which chlorine (Cl2) with a flow rate of 45 sccm, carbon tetrafluoride (CF4) with a flow rate of 55 sccm, and oxygen (O2) with a flow rate of 55 sccm were supplied as an etching gas, the power was 3000 W, the bias power was 110 W, and the pressure was 0.67 Pa; and second etching in which chlorine (Cl2) with a flow rate of 100 sccm was supplied as an etching gas, the power was 2000 W, the bias power was 50 W, and the pressure was 0.67 Pa.
Next, a stack of a 50-nm-thick silicon nitride film and a 300-nm-thick silicon oxynitride film to be the interlayer insulating layer 412 was formed. The silicon nitride film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 20 sccm and nitrogen with a flow rate of 500 sccm as a source gas were supplied to a treatment chamber, and a power of 900 W was supplied with the use of a 27.12 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon nitride film was 350° C. The silicon oxynitride film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 5 sccm and dinitrogen monoxide with a flow rate of 1000 sccm as a source gas were supplied to a treatment chamber, and a power of 35 W was supplied with the use of a 13.56 MHz high-frequency power source. Further, the temperature of the substrate at the formation of the silicon oxynitride film was 325° C.
After formation of the interlayer insulating layer 412, heat treatment was performed at 450° C. in a nitrogen atmosphere for one hour and then heat treatment was performed at 450° C. in an oxygen atmosphere for one hour.
For comparison, samples in which the oxide layer 404a and the oxide layer 404c are omitted were prepared by the above method for fabricating samples.
Table 1 briefly shows fabrication conditions of the samples in this example.
Samples I1 to I9 fabricated in the above manner were subjected to a positive BT stress test and a negative BT stress test, and the Vg-Id characteristics thereof before and after the tests were compared. In measuring the Vg-Id characteristics, the drain voltage was set to 0.1 V or 3.3 V and the gate voltage was swept from −4 V to +4 V. FIGS. 37A1, 37A2, 37B1, 37B2, 37C1, and 37C2, FIGS. 38A1, 38A2, 38B1, 38B2, 38C1, and 38C2, and FIGS. 39A1, 39A2, 39B1, 39B2, 39C1, and 39C2 show the Vg-Id characteristics before and after the tests.
FIG. 37A1 shows the Vg-Id characteristics of Sample I1 before and after the positive BT stress test. FIG. 37A2 shows the Vg-Id characteristics of Sample I1 before and after the negative BT stress test. FIG. 37B1 shows the Vg-Id characteristics of Sample I2 before and after the positive BT stress test. FIG. 37B2 shows the Vg-Id characteristics of Sample I2 before and after the negative BT stress test. FIG. 37C1 shows the Vg-Id characteristics of Sample I3 before and after the positive BT stress test. FIG. 37C2 shows the Vg-Id characteristics of Sample I3 before and after the negative BT stress test. FIG. 38A1 shows the Vg-Id characteristics of Sample I4 before and after the positive BT stress test. FIG. 38A2 shows the Vg-Id characteristics of Sample I4 before and after the negative BT stress test. FIG. 38B1 shows the Vg-Id characteristics of Sample I5 before and after the positive BT stress test. FIG. 38B2 shows the Vg-Id characteristics of Sample I5 before and after the negative BT stress test. FIG. 38C1 shows the Vg-Id characteristics of Sample I6 before and after the positive BT stress test. FIG. 38C2 shows the Vg-Id characteristics of Sample I6 before and after the negative BT stress test. FIG. 39A1 shows the Vg-Id characteristics of Sample I7 before and after the positive BT stress test. FIG. 39A2 shows the Vg-Id characteristics of Sample I7 before and after the negative BT stress test. FIG. 39B1 shows the Vg-Id characteristics of Sample I8 before and after the positive BT stress test. FIG. 39B2 shows the Vg-Id characteristics of Sample I8 before and after the negative BT stress test. FIG. 39C1 shows the Vg-Id characteristics of Sample I9 before and after the positive BT stress test. FIG. 39C2 shows the Vg-Id characteristics of Sample I9 before and after the negative BT stress test. In each graph, the solid line represents the Vg-Id characteristics before the test and the dotted line represents the Vg-Id characteristics after the test.
FIGS. 37A1, 37A2, 37B1, 37B2, 37C1, and 37C2, FIGS. 38A1, 38A2, 38B1, 38B2, 38C1, and 38C2, FIGS. 39A1, 39A2, 39B1, 39B2, 39C1, and 39C2, and
According to this example, a transistor in which the amounts of change in threshold voltage and shift value are particularly small and which can be applied to a semiconductor device of one embodiment of the present invention has extremely high reliability.
This application is based on Japanese Patent Application serial no. 2012-230363 filed with Japan Patent Office on Oct. 17, 2012, Japanese Patent Application serial no. 2012-252327 filed with Japan Patent Office on Nov. 16, 2012, and Japanese Patent Application serial no. 2013-052623 filed with Japan Patent Office on Mar. 15, 2013, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-230363 | Oct 2012 | JP | national |
| 2012-252327 | Nov 2012 | JP | national |
| 2013-052623 | Mar 2013 | JP | national |