Semiconductor device including semiconductor memory element and method for producing same

Information

  • Patent Grant
  • 7592235
  • Patent Number
    7,592,235
  • Date Filed
    Thursday, April 21, 2005
    19 years ago
  • Date Issued
    Tuesday, September 22, 2009
    14 years ago
Abstract
A wafer, in which a plurality of rectangular regions are defined on the face of the wafer by streets arranged in a lattice pattern, and a semiconductor memory element is disposed in each of the rectangular regions, is divided along the streets to separate the rectangular regions individually, thereby forming a plurality of semiconductor devices. Before the wafer is divided along the streets, a strained layer having a thickness of 0.20 μm or less, especially 0.05 to 0.20 μm, is formed in the back of the wafer. The strained layer is formed by grinding the back of the semiconductor wafer by a grinding member formed by bonding diamond abrasive grains having a grain size of 4 μm or less by a bonding material.
Description
FIELD OF THE INVENTION

This invention relates to a semiconductor device including a semiconductor memory element, such as DRAM (dynamic random access memory) or a flash memory, and a method for producing the semiconductor device.


DESCRIPTION OF THE PRIOR ART

In the production of a semiconductor device, as is well known among people skilled in the art, a plurality of rectangular regions are defined by streets arranged in a lattice pattern on the face of a semiconductor wafer, and a semiconductor element is disposed in each of the plural rectangular regions. Then, the back of the wafer is ground to decrease the thickness of the water. Then, the wafer is cut along the streets to separate the plural rectangular regions individually, thereby forming semiconductor devices. In a mode called dicing before grinding, the wafer is not completely cut along the streets, but grooves of a required depth are formed in the wafer along the streets, and then the back of the wafer is ground to bring the thickness of the wafer into agreement with the depth of the grooves, whereby the rectangular regions are separated individually to produce semiconductor devices.


In recent times, semiconductor devices have become compact and lightweight. Thus, it is often demanded that the thickness of the semiconductor device be rendered 100 μm or less and, further, 50 μm or less. When the back of the semiconductor wafer is ground, a strained layer is generated in the back of the semiconductor device owing to the grinding. Such a strained layer decreases the transverse rupture resistance of the semiconductor device. If the semiconductor device is brought to such a small thickness, the above strained layer, if left unchanged, would result in insufficient transverse rupture resistance of the semiconductor device. Hence, if the thickness of the semiconductor device is to be rendered that thin, it is usual practice to apply polishing or etching to the ground back of the semiconductor wafer, thereby removing the strained layer, before separating the semiconductor wafer into individual rectangular regions. By so doing, excessively low transverse rupture resistance of the semiconductor device is avoided.


Studies by the inventors have shown that in the case of a semiconductor device including a memory element, such as DRAM or a flash memory, if the strained layer is removed by polishing or etching after the back of the semiconductor wafer is ground, the function of the memory element is deteriorated. The reason is not entirely clear, but the inventors presume that upon removal of the strained layer, a gettering sink effect ascribed to the strained layer is eliminated, with the result that impurities, such as heavy metals, are returned to the neighborhood of the face of the semiconductor wafer.


SUMMARY OF THE INVENTION

It is a first object of the present invention, therefore, to improve a semiconductor device including a memory element, thereby imparting sufficient transverse rupture resistance without inducing the deterioration of a memory function even if the thickness of the semiconductor device is sufficiently small.


It is a second object of the present invention to provide a method for producing a semiconductor device including a memory element, the semiconductor device having sufficient transverse rupture resistance without inducing the deterioration of a memory function even if the thickness of the semiconductor device is sufficiently small.


The inventors diligently conducted studies and experiments, and have found that if a strained layer considerably thinner than a conventional strained layer is intentionally rendered present in the back of a semiconductor device, sufficient transverse rupture resistance can be imparted without deterioration of the function of a memory element.


That is, according to a first aspect of the present invention, there is provided, as a semiconductor device including a semiconductor memory element which attains the above-mentioned first object, a semiconductor device including a semiconductor memory element, wherein a strained layer having a thickness of 0.20 μm or less has been formed on the back of the semiconductor device.


The thickness of the strained layer is preferably 0.05 μm or more. The strained layer preferably has been generated by grinding the back of the semiconductor device by a grinding member formed by bonding diamond abrasive grains having a grain size of 4 μm or less by a bonding material.


According to a second aspect of the present invention, there is provided, as a method for producing a semiconductor device which attains the above-mentioned second object, a method for producing a semiconductor device, comprising dividing a wafer, in which a plurality of rectangular regions are defined on the face of the wafer by streets arranged in a lattice pattern, and a semiconductor memory element is disposed in each of the rectangular regions, along the streets to separate the rectangular regions individually, thereby forming a plurality of semiconductor devices, the method further comprising forming a strained layer having a thickness of 0.20 μm or less on the back of the wafer before dividing the wafer along the streets.


The thickness of the strained layer is preferably 0.05 μm or more. It is preferred to form the strained layer by grinding the back of the semiconductor wafer by a grinding member formed by bonding diamond abrasive grains having a grain size of 4 μm or less by a bonding material.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a perspective view showing a typical example of a wafer to which a preferred embodiment of a manufacturing method according to the present invention is applied.



FIG. 2 is a schematic view showing a state in which the back of the wafer is ground in the preferred embodiment of the manufacturing method of the present invention.



FIG. 3 is a partial sectional view showing a preferred embodiment of a semiconductor device according to the present invention.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS


FIG. 1 shows a wafer to which a preferred embodiment of a manufacturing method according to the present invention is applied. A wafer, entirely indicated at a numeral 2, is formed of silicon, and is circular except an orientation flat 4. On the face 6 of the wafer 2, a plurality of rectangular regions 10 are defined by streets 8 arranged in a lattice pattern. A semiconductor element including a memory element, such as DRAM or flash memory, is formed in each of the rectangular regions 10. Since such a wafer 2 per se is well known among people skilled in the art, its detailed explanation is omitted herein.


In the present invention, it is important to grind the back 12 of the wafer 2, thereby forming a strained layer of a required thickness on the back of the wafer 2. FIG. 2, which shows the manner of grinding the back 12 of the wafer 2, is referred to for the purpose of explanation. Before grinding the back 12 of the wafer 2, a suitable protective sheet 14 is pasted to the face 6 of the wafer 2. The wafer 2, which has the suitable protective sheet 14 pasted to the face 6 thereof, is rendered facedown, and placed on a chuck means 16. The chuck means 16, which is rotated about its central axis extending substantially vertically, has a substantially horizontal upper surface, and many suction holes (not shown) are formed in this upper surface. The wafer 2 is placed on the upper surface of the chuck means 16, and the suction holes are brought into communication with a vacuum source (not shown), whereby the wafer 2 is attracted onto the upper surface of the chuck means 16. A grinding means 18 is caused to act on the back 12 of the wafer 2. The grinding means 18 includes a support disk 22 fixed to a rotating shaft 20 extending substantially vertically. To a peripheral edge portion of the lower surface of the support disk 22, a plurality of arcuate grinding members 24 are fixed with spacing in the circumferential direction. Instead of the plural arcuate grinding members 24, a single grinding member extending continuously in a toroidal form can be fixed to the support disk 22. In grinding the back 12 of the wafer 2, the chuck means 16 is rotated, and the grinding means 18 is rotated at the same time. The grinding member 24 of the grinding means 18 is pressed against the back 12 of the wafer 2, and the grinding means 18 is moved in a horizontal direction with respect to the chuck means 16. When the back 12 of the wafer 2 is ground in this manner to decrease the thickness of the wafer 2 to a required value, microcracks are formed in the back 12 of the wafer 2 owing to the grinding, and such microcracks constitute a strained layer 26 (FIG. 3). In FIG. 3, the wafer 2 stripped of the protective sheet 14 from its face 6 is illustrated in an upright state, and the strained layer 26 constituted of the microcracks formed in the back 12 is indicated by cross-hatching.


In the present invention, it is important to form the strained layer 26 having a thickness t of 0.20 μm or less, preferably 0.05 to 0.20 μm, on the back 12 of the wafer 2. To form the strained layer 26 of such a markedly small thickness, it is recommendable, according to the inventors' experience, to use the grinding member 24 formed by bonding diamond grains having a grain size of 4 μm or less by a suitable bonding material such as a vitrified bond or a resin bond. The thickness t of the strained layer 26 constituted of the microcracks can be measured by observing the back 12 of the wafer 2 under a transmission electron microscope.


In the above-described manner, the back 12 of the wafer 2 is ground to form the strained layer 26 of the required thickness. Then, the wafer 2 is separated along the streets 8, whereby a semiconductor device composed of each of the rectangular regions 10 is completed. To separate the wafer 2 along the streets 8, it suffices to cut the wafer 2 along the streets 8 by a dicer well known per se.


If desired, prior to grinding of the back 12 of the wafer 2, it is possible to cut the wafer 2 along the streets 8 to a predetermined depth from the face 6 of the wafer 2, thereby forming grooves in the face 6 of the wafer 2 along the streets 8, and then grind the back 12 of the wafer 2, thereby decreasing the thickness of the wafer 2 to the depth of the grooves. By this procedure, the rectangular regions 10 can be separated individually.


EXAMPLE

A silicon wafer of a shape as shown in FIG. 1 was rendered ready for use. The diameter of the wafer was 8 inches, and its thickness was 725 μm. On the face of the wafer, 750 rectangular regions were defined. Each of the rectangular regions measured 5×8 mm, and DRAM was formed in each of the rectangular regions. The back of such a wafer 2 was ground in a manner as shown in FIG. 2 to decrease the thickness of the wafer 2 to 150 μm. A grinding member used was formed from diamond grains having a grain size of 4 μm or less bonded by a vitrified bond. Then, the wafer was cut along the streets to produce a semiconductor device comprising the rectangular region separated individually. Observation of the back of the semiconductor device by a transmission electron microscope showed that a strained layer having a thickness of 0.15 to 0.19 μm and constituted of microcracks was formed in the back of the semiconductor device. The transverse rupture resistance of the semiconductor device was measured. The results are shown in Table 1. The transverse rupture resistance of the semiconductor device was measured by a ball transverse rupture method comprising placing the semiconductor device on a cylindrical jig, and pressing a ball against the center of the semiconductor device. Furthermore, a manufacturer of DRAM was asked to test the memory function of the semiconductor device. The results of the test are shown in Table 1.


Comparative Example 1

A semiconductor device was produced in the same manner as in the above Example, except that the grinding member was formed from diamond grains having a grain size of 4 to 6 μm. The back of the semiconductor device was observed by a transmission electron microscope. It was found that a strained layer having a thickness of nearly 0.50 to 1.00 μm and constituted of microcracks was formed in the back of the semiconductor device. The transverse rupture resistance of the semiconductor device was measured. The results are shown in Table 1. Furthermore, a manufacturer of DRAM was asked to test the memory function of the semiconductor device. The results of the test are shown in Table 1.


Comparative Example 2

A semiconductor device was produced in the same manner as in Comparative Example 1, except that after the back of the wafer was ground, the back of the wafer was polished over a thickness of 1.20 μm with the use of a polishing tool sold by DISCO CORP. under the trade name of “DRY POLISH”. When the back of the semiconductor device was observed by a transmission electron microscope, it was found that a strained layer substantially did not exist in the back of the semiconductor device. The transverse rupture resistance of the semiconductor device was measured. The results are shown in Table 1. Furthermore, a DRAM manufacturer was asked to test the memory function of the semiconductor device. The results of the test are shown in Table 1.













TABLE 1







Thickness of
Transverse
Decline in



strained
rupture
memory



layer (μm)
resistance (MPa)
function





















Example
0.15-0.19
910
No



Comparative
0.50-1.00
620
No



Example 1



Comparative
Zero
920
Yes



Example 2









Claims
  • 1. A method for producing a semiconductor device from a wafer in which a plurality of rectangular regions are defined on a face of the wafer by streets arranged in a lattice pattern, and a semiconductor memory element is disposed in each of said rectangular regions comprising: grinding a back surface of the wafer to set a thickness for each produced semiconductor device at 100 μm or less, said grinding forming a strained layer having a thickness of from 0.15 μm to 0.19 μm on the back surface of the wafer, said strained layer being constituted by microcracks; anddividing the wafer to separate said rectangular regions and thereby obtain said semiconductor devices with said memory element on a top side of each device and with said strained layer on a back side of each device.
  • 2. The method for producing a semiconductor device according to claim 1, wherein said grinding is done by a grinding member formed by bonding diamond abrasive grains having a grain size of 4 μm or less by a bonding material.
Priority Claims (1)
Number Date Country Kind
2004-135714 Apr 2004 JP national
US Referenced Citations (16)
Number Name Date Kind
3923567 Lawrence Dec 1975 A
4144099 Edmonds et al. Mar 1979 A
4276114 Takano et al. Jun 1981 A
5162241 Mori et al. Nov 1992 A
5389551 Kamakura et al. Feb 1995 A
5622875 Lawrence Apr 1997 A
6146980 Hsu Nov 2000 A
6171873 Mendelson et al. Jan 2001 B1
6184109 Sasaki et al. Feb 2001 B1
6214704 Xin Apr 2001 B1
6465330 Takahashi et al. Oct 2002 B1
6583032 Ishikawa et al. Jun 2003 B1
6624505 Badehi Sep 2003 B2
20020192964 Francis Dec 2002 A1
20030162368 Connell et al. Aug 2003 A1
20040164425 Urakawa Aug 2004 A1
Related Publications (1)
Number Date Country
20050255674 A1 Nov 2005 US