Patent Application
20080157365
1. Field
Embodiments of the invention relate to microelectronic devices and their manufacture. In particular, embodiments of the invention relate to microelectronic devices that include etch stop layers selectively formed over a metal gate where the etch stop layers include metal compounds, and to methods of manufacturing such microelectronic devices.
2. Background Information
The size of transistors and the spacing between transistors continues to decrease in an effort to increase device integration density in integrated circuits that are spaced more closely together. As the size of the transistors and the spacing between them decrease, the risk of electrical contact shortings increases.
Electrical contacts are typically created to provide electrical connections to the sources, drains, and gates of the transistors. Typically, lithography techniques are used to define the location of the contact holes for the electrical contacts. Then the contact holes are then filled with a conductive material to form electrical contacts to source, drain, and gate regions of the transistor.
Misalignment or misregistration of the contact holes may potentially occur due in part to resolution limitations of the patterning and lithography tools, imperfections of the wafer processing operations, or combinations of these factors. If misalignment or misregistration occurs, in some cases, the contact hole of a source or drain contact may potentially erroneously be created above the gate of the transistor so that the conductive material may electrically couple with the gate. Such electrical coupling may represent contact-to-gate shorting, which may render the transistor inoperable and tend to reduce wafer yields.
One known way to help reduce the risk of such shorting is to reduce the size of the contact holes. However, this may lead to an increase in contact resistance.
Another know way to reduce the risk of such shorting is to increase the spacing between the source, drain, and gate of the transistor so that fewer misalignments are observed for a given registration capability. However, this approach tends to decrease the number of transistors that can be fabricated on a die or make the die bigger.
The invention may best be understood by referring to the following description and accompanying drawings that are used to illustrate embodiments of the invention. In the drawings:
In the following description, numerous specific details are set forth. However, it is understood that embodiments of the invention may be practiced without these specific details. In other instances, well-known circuits, structures and techniques have not been shown in detail in order not to obscure the understanding of this description.
The transistor represents one example of a suitable transistor. The transistor includes a source region 112 of a substrate 110, a drain region 114 of the substrate, and a channel region 116 of the substrate defined between the source and drain regions. The transistor also includes a metal gate 118 over the channel region, and a gate insulator or dielectric 120 disposed between and separating the metal gate from the channel region. The metal gate, source region, and drain region are each terminals of a three-terminal insulated gate field effect transistor (FET). Occasionally the terminals are referred to as junctions or electrodes.
The transistor also includes first 122A and second 122B sidewall spacers, and first 124A and second 124B sidewall etch stops. The first and second sidewall spacers abut the sidewalls of the metal gate above the source and drain regions of the substrate, respectively. The first and second sidewall etch stops abut the respective first and sidewall spacers. The first and second sidewall spacers are separated from the metal gate by the intervening first and second sidewall spacers.
The transistor also includes source tip or extension 126A and drain tip or extension 126B regions of the substrate. The source and drain tip regions are shallower than the source and drain, respectively, and represent portions of the source and drain, respectively, which are closest to the metal gate. The channel region of the substrate is disposed between the tip or extension regions.
The microelectronic device also includes first 106 and second 108 insulating layers formed over an upper surface 128 of the substrate. Three metal or otherwise conductive electrical contact structures are formed through the insulating layers to provide electrical connection to the transistor. In particular, a first conductive electrical contact structure 104A is formed through the first and second insulating layers to provide electrical connection to the source region of the transistor. Likewise, a second conductive electrical contact structure 104B is formed through the first and second insulating layers to provide electrical connection to the drain region of the transistor. A third conductive electrical contact structure 104C is formed through the second insulating layer to provide electrical connection to the metal gate of the transistor.
The microelectronic device includes first 130A and second 130B field isolation regions of the substrate. The first and second field isolation regions may include shallow trench isolation (STI), and help to electrically isolate or at least insulate the transistor. The source and drain regions are disposed between the field isolation regions.
Referring again to
In one or more embodiments of the invention, the etch stop layer may include a metal compound. In one or more embodiments of the invention, the metal compound may be dielectric or insulating. In one or more embodiments of the invention, the etch stop layer may include a compound of a metal and one or more of oxygen, nitrogen, carbon, and boron. Examples of suitable metal compounds include, but are not limited to, oxides of a metal, nitrides of a metal, carbides of a metal, borides of a metal, and combinations thereof. Examples of suitable combinations include oxide-nitrides of a metal, oxide-carbides of a metal, oxide-nitride-carbides of a metal, nitride-carbides of a metal (e.g., carbon nitrides), and nitride-borides of a metal (e.g., boron nitride).
In one or more embodiments of the invention, selectively forming the etch stop layer including the metal compound over the metal gate of the transistor may include forming the metal compound by reactively converting a metal of a top surface of the metal gate. As previously discussed, the reactive conversion may include oxidation (e.g., reacting or combining the metal with oxygen or an oxygen containing compound to form an oxide of the metal), reacting or combining the metal with nitrogen or a nitrogen containing compound to form an nitride of the metal, reacting or combining the metal with carbon or a carbon containing compound to form an carbide of the metal, reacting or combining the metal with boron or a boron containing compound to form an boride of the metal, or a combination thereof.
In one or more embodiments of the invention, a native metal of the top surface of the metal gate may be reactively converted to form the metal compound. This approach will be shown and described further below in conjunction with
As another option, in one or more embodiments of the invention, a metal layer cap may be selectively deposited over the native metal of the top surface of the metal gate, and then the etch stop layer may be formed over the metal gate by reactively converting at least a portion of the deposited metal layer cap to a metal compound. This approach will be shown and described further below in conjunction with
Yet another option is to deposit an etch stop layer directly, rather than reactively converting the top of the metal gate or a metal cap layer. For example, in various embodiments of the invention, an oxide of a metal, a nitride of a metal, a carbide of a metal, a boride of a metal, or a combination thereof may be selectively deposited over the gate, such as, for example, by chemical vapor deposition (CVD) or atomic layer deposition (ALD).
Referring to
Turning to
The microelectronic device includes a substrate 310. The substrate represents a general workpiece object having the transistor formed therein/thereon often as part of an integrated circuit. The substrate may include a semiconductor substrate including a semiconductor material. One suitable semiconductor material is silicon. The use of silicon may allow taking advantage of the large amount of know-how and cost effectiveness of fabricating transistors from silicon, although this is not a requirement of the invention. Suitable substrates including silicon include among others single crystal silicon substrates and silicon on insulator (SOI) substrates. Alternatively, the silicon may potentially be replaced with other well-known elemental or compound semiconductors, such as, for example, germanium (Ge), a combination of elements from Group 4A (e.g., silicon germanium (SiGe) or silicon carbide (SiC)), a combination of elements from Groups 3A and 5A (e.g., gallium arsenide (GaAs), indium phosphide (InP), or gallium nitride (GaN)), or other well-known semiconductors. The substrate may also include other materials, such as, for example, metals, other conductors, dielectrics or insulators, organic materials, and combinations thereof. In addition to the transistor, other passive and/or active devices may potentially be fabricated in and/or on the substrate, including, but not limited to, other transistors, switches, capacitors, resistors, and the like.
The transistor is formed in and/or on the substrate. The transistor includes a source region 312 of the substrate and a drain region 314 of the substrate. The source and drain regions respectively include an optional source tip or extension region 326A and an optional drain tip or extension region 326B. A channel region 316 of the substrate is defined between the source and drain tip or extension regions. A gate dielectric 320 overlies the channel region. The transistor also includes the metal gate 318 over the gate dielectric. The transistor also includes optional first 322A and second 322B sidewall spacers, and optional first 324A and second 324B sidewall etch stops. First 330A and second 330B field isolation regions of the substrate may help to electrically isolate or at least insulate the transistor. In one aspect, the first and second field isolation regions may include shallow trench isolation (STI).
All of these components of the transistor may optionally be conventional, such as, for example, including conventional materials, of conventional sizes and shapes, and formed in conventional ways. Numerous different examples of transistors similar to the one shown are known in the arts and described in the literature. Accordingly, to avoid obscuring the description, a detailed discussion of these components and how they are formed will not be provided. However, a brief discussion of some of the possible variations is warranted.
The source and the drain regions and the tip or extension regions may include doped regions. For n-MOS transistor embodiments, the dopants may include n-type dopants, such as, for example, arsenic (As) ions and/or phosphorous (P) ions. For p-MOS transistor embodiments, the dopants may include p-type dopants, such as, for example, boron (B) ions. By way of example, in one or more embodiments, the concentration of dopant in these regions may range from about 10̂18 cm-3 to 10̂21 cm-3.
The gate dielectric may include an insulating or dielectric material. Examples of suitable materials include, but are not limited to, oxides of silicon, such as, for example, silicon dioxide (SiO2), nitrides of silicon, such as, for example, silicon nitride (Si3N4), oxynitrides of silicon, such as, for example, silicon oxynitride (SiOxNy), and combinations thereof. As another option, the gate dielectric may include a high dielectric constant (high-k) material. A high-k material is a material that has a dielectric constant (k), which is higher than that of silicon dioxide (SiO2). Examples of suitable high-k materials include, but are not limited to, oxides of zirconium, such as, for example, zirconium dioxide (ZrO2), oxides of haffium, such as, for example, hafnium dioxide (HFO2), oxides of lanthanum, such as, for example, lanthanum oxide (La2O4), oxides of tantalum, such as, for example, tantalum oxide (Ta2O5), oxides of titanium, such as, for example, titanium dioxide (TiO2), and combinations thereof. The thickness of the gate dielectric may be scaled depending on the dielectric constant of the material used. In one or more embodiments, the thickness of the gate dielectric is in the range of about 5 Å to 100 Å.
The metal gate includes a metal. Examples of suitable metals according to one or more embodiments include, but are not limited to, copper (Cu), ruthenium (Ru), nickel (Ni), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), titanium (Ti), aluminum (Al), hafnium (Hf), tantalum (Ta), tungsten (W), vanadium (V), molybdenum (Mo), palladium (Pd), gold (Au), silver (Au), platinum (Pt), and combinations thereof. In one or more embodiments, the metal gate may include a noble metal, such as, for example, gold, silver, tantalum, platinum, rhodium, or a combination thereof. The metal gate may also include other materials besides just metals. In one or more embodiments, the metal gate may include a composite metal gate that includes a metal and one or more other sufficiently conductive non-metals. Examples of suitable sufficiently conductive non-metals may include, but are not limited to, conductive semiconductors, such as, for example, polysilicon and polysilicon germanium, various conductive metal compounds, such as, for example, metal nitrides and certain metal oxides, and combinations thereof. In one example embodiment of the invention, the composite metal gate may include a top metal layer overlying one or more other metal or sufficiently conductive non-metal layers. In another example embodiment of the invention, the composite metal gate may be encapsulated on the top and two sides by one or more work function materials, such as, for example, compounds of metals with sufficient conductivities. In one or more embodiments, the thickness of metal gate may range from about 5 nm to 300 nm.
The sidewall spacers, which are optional, may include an oxide material, such as, for example, an oxide of silicon, a nitride material, such as, for example, a nitride of silicon, an oxynitride material, such as, for example, an oxynitride of silicon, a carbide material, such as, for example, a carbide of silicon, or combinations thereof (e.g., an oxy-carbide of silicon and/or a carbide-nitride of silicon). The sidewall etch stops, which are optional, may include a nitride material, such as, for example, a nitride of silicon. Such sidewall etch stops are occasionally known in the art as nitride etch stop layers (NESL). The NESL may help to protect portions of the transistor during a trench contact (TCN) etch.
The microelectronic device also includes a first insulating or dielectric layer 306. The first insulating layer is formed over substantially the entire exposed upper surface 328 of the substrate. The metal gate and its associated sidewall structures are disposed within the first insulating layer. A top surface 336 of the first insulating layer is substantially coplanar with a top surface 334 of the metal gate. The first insulating layer is sometimes referred to as an interlayer dielectric (ILD).
In one or more embodiments of the invention, the first insulating layer may include an oxide of silicon, such as, for example, silicon dioxide (SiO2). As another option, in one or more embodiments, the first insulating layer may include a low dielectric constant (low-k) material having a dielectric constant (k) which is lower than that of silicon dioxide (SiO2). Examples of suitable low-k materials include, but are not limited to, fluorine containing dielectric materials, such as, for example, fluorinated oxide of silicon (e.g., SiOF), fluorine-doped silicate glass (FSG), other fluorine doped glasses, and combinations thereof. Other examples of suitable low-k materials include, but are not limited to, inorganic porous oxide-like low-k dielectric materials, other porous materials, carbon doped oxide of silicon, and other carbon-doped oxides (CDOs). Still other materials that may potentially be used, depending upon the particular implementation (e.g., the temperatures encountered during subsequent processing), include, but are not limited to, WPR-series materials, hybrid organic-inorganic. low-k dielectrics, polyimide, epoxy, benzocyclobutene (BCB)-based photosensitive polymer dielectrics, and combinations thereof. The combinations may include stacks or mixtures.
Insulating layers including these various materials may be formed over the substrate using known techniques. Examples of techniques each useful for one or more of these materials include, but are not limited to, spin-on deposition, plasma CVD, high-density plasma (HDP) CVD, diffusion furnace CVD, other forms of CVD, sputtering, other forms of physical vapor deposition (PVD), ALD, and other deposition approaches known in the arts. In one or more embodiments, first insulating layer may be deposited to a thickness greater than a height of the gate electrode. In one embodiment, first insulating layer may be deposited to a thickness in the approximate range of 50 nm to 500 nm, although the scope of the invention is not limited to any known thickness. The deposited insulating layer may cover the top surface of the metal gate, such as, for example, by at least several nanometers. Then, a top portion of the deposited insulating layer may be removed, such as, for example, by chemical-mechanical polishing (CMP) or other polishing, or by wet etching, dry etching, or other etching, or by a combination of such approaches.
As previously discussed, this is just one illustrative example of a suitable transistor. The scope of the invention is certainly not limited to this particular transistor. Numerous alternate transistor designs known in the art are also suitable. For example, asymmetric transistors with differently sized and/or shaped source and drain regions are suitable. As another example, transistors that omit the sidewall spacers are suitable. As yet another example, transistors that omit the sidewall etch stops are suitable. As a further example, transistors that omit the tips or extension regions are suitable. Other transistors of different sizes, shapes, and configurations or layouts are also suitable.
Referring again to
As previously discussed, in one or more embodiments of the invention, a native metal of the top surface of the metal gate may be reactively converted to form the metal compound. This approach will be shown and described further below in conjunction with
Forming the metal compound by reactively converting the metal of the top surface of the metal gate may include oxidizing, reacting, or combining the metal with oxygen or an oxygen containing compound to form an oxide of the metal, reacting or combining the metal with nitrogen or a nitrogen containing compound to form an nitride of the metal, reacting or combining the metal with carbon or a carbon containing compound to form an carbide of the metal, reacting or combining the metal with boron or a boron containing compound to form an boride of the metal, or a combination thereof.
One example approach for oxidizing the metal, according to one or more embodiments of the invention, may include thermally annealing the metal in the presence of oxygen (O2), water (H2O), or another suitable oxygen containing compound. As one particular example, aluminum may be oxidized by exposing the aluminum to water vapor at about 10 Torr and a temperature of about 400° C.
Another example approach for oxidizing the metal, according to one or more embodiments of the invention, may include treating the metal with a plasma including oxygen, nitrous oxide (N2O), carbon dioxide (CO2) or another suitable oxygen containing compound. In one particular example, titanium, iron, or aluminum may be oxidized by exposure to about 3 Torr of nitrous oxide in a radiofrequency plasma of about 200 W applied power at a temperature of about 300° C. In another example, a metal may be oxidized by treatment with an nitrous oxide (N2O), carbon dioxide (CO2) or oxygen plasma for from 5 to 20 minutes at a temperature of 350 to 450° C. The use of a plasma may tend to be faster than the thermal oxidation described immediately above and may tend to be less detrimental to the diffusion of underlying gates metal.
One example approach for forming the nitride of the metal, according to one or more embodiments of the invention, may include treating the metal with a plasma including ammonia (NH3), nitrogen (N2), or another suitable nitrogen containing compound. In one particular example, a nitride of aluminum or other metals may be formed by exposing the aluminum to about 2.8 Torr of ammonia in a radiofrequency plasma of about 150 W applied power at a temperature of about 350 to 400° C. for about 5 to 15 minutes.
One example approach for forming the carbide of the metal, according to one or more embodiments of the invention, may include treating the metal with a plasma including carbon dioxide (CO2), methane (CH4), ethylene (C2H4), or another suitable carbon containing compound. In one particular example, a carbide of germanium, aluminum or titanium may be formed by exposing the germanium, aluminum, or titanium, to about Torr ethylene in a radiofrequency plasma of about 300 W applied power at a temperature of about 350 C.
A top surface portion of the native metal of the metal gate may be consumed or converted to metal compound by these reactive processes. In one or more embodiments of the invention, the native metal of the gate may be capable of forming a passivating oxide, a passivating nitride, a passivating carbide, or a combination thereof. Many metals are capable of forming such passivating layers. Examples of metals that are capable of forming passivating oxides include, but are not limited to, aluminum (Al), chromium (Cr), molybdenum (Mo), and nickel (Ni), although the scope of the invention is not limited to just these metals. The thickness of the passivating layer may be modified for a given metal by changing the reaction conditions. In such embodiments, the reactive conversion of the metal may be stopped automatically at a given thickness of the etch stop layer due to the passivation or self-limiting nature of the reaction. Alternatively, a metal that doesn't form such a passivating layer may optionally be used and the reactive conversion may be stopped when a desired thickness of the etch stop layer is achieved. The use of a metal that forms a passivating layer may be favored to promote device reliability, stability, and/or across-wafer uniformity in the etch stop layer thickness. In various embodiments of the invention, the thickness of the etch stop layer may range from 5 nm to 100 nm, or from 5 nm to 50 nm, or from 10 nm to 50 nm, or from 10 nm to 30 nm. Although the scope of the invention is not limited to any know thickness.
The top surface of the first insulating layer may be exposed to the treatment used to form the etch stop layer. Oxidation generally will not significantly adversely affect a silicon dioxide (SiO2) or similar oxide-based dielectric material of the first insulating layer. Certain other materials that are suitable for the first insulating layer may potentially be affected or changed slightly by the treatment. Likewise, formation of nitride and carbide-based etch stop layers may potentially affect silicon dioxide and certain other dielectric material of the first insulating layer. Potential efforts that may be used to reduce the affects of the treatment may include localized treatment, short treatment, and selecting a treatment that is relatively compatible with the dielectric material. In certain implementations, any remaining changes to the dielectric material that may potentially result from the treatment may be tolerable. As yet another option, a patterned sacrificial photoresist layer or other layer or screen may optionally be used to help shield the first insulating layer from the treatment, and then later be removed.
Refer now to
Notice that the etch stop layer is directly on the native metal of the metal gate. The etch stop layer has a bottom surface that extends below the top surface of the sidewall spacer a thickness of the etch stop layer. In the illustration, the top surface is substantially aligned with a top surface of a sidewall spacer of the metal gate and/or the top surface of the first insulating layer. This may be the case if there is increase or decrease in volume due to the reactive conversion. Alternatively, if there is an increase in volume, the top surface of the etch stop layer may be slightly above these other surfaces. Similarly, if there is a decrease in volume, the top surface of the etch stop layer may be slightly below these other surfaces. As shown in the illustrated embodiment, the etch stop layer may be disposed between the first and second sidewall spacers. In some cases, a slight amount of lateral encroachment onto the sidewalls spacers may be observed. However, the etch stop layer is not formed to any substantial extent over the top surface of the first insulating layer.
The metal of the metal compound of the etch stop layer may be any metals suitable for the metal gate which are capable of forming metal compounds as disclosed herein under temperature conditions compatible with the transistor. Examples of suitable metals according to one or more embodiments include, but are not limited to, copper (Cu), ruthenium (Ru), nickel (Ni), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), titanium (Ti), aluminum (Al), hafnium (Hf), tantalum (Ta), tungsten (W), vanadium (V), molybdenum (Mo), palladium (Pd), silver (Au), and combinations thereof. In one or more embodiments of the invention, the metal may be capable of forming a passivating layer. In one or more embodiments of the invention, the metal may include aluminum, chromium, molybdenum, nickel, titanium, tungsten, tantalum, or an alloy or other combination thereof.
Referring back to
In one or more embodiments of the invention, the second insulating layer may include an oxide of silicon, such as, for example, silicon dioxide (SiO2). As another option, in one or more embodiments, the second insulating layer may include a low dielectric constant (low-k) material having a dielectric constant (k) which is lower than that of silicon dioxide (SiO2). Examples of suitable low-k materials include, but are not limited to, fluorine containing dielectric materials of the types mentioned before for the first dielectric layer. Other examples of suitable low-k materials include, but are not limited to, inorganic porous oxide-like low-k dielectric materials, other porous materials, carbon doped oxide of silicon, and other carbon-doped oxides (CDOs). Still other materials that may potentially be used, depending upon the particular implementation (e.g., the temperatures encountered during subsequent processing), include, but are not limited to, WPR-series materials, hybrid organic-inorganic low-k dielectrics, polyimide, epoxy, benzocyclobutene (BCB)-based photosensitive polymer dielectrics, and combinations thereof. The combinations may include stacks or mixtures.
The second insulating layer of these various materials may be formed over the substrate using known techniques. Examples of techniques each useful for one or more of these materials include, but are not limited to, spin-on deposition, plasma enhanced-chemical vapor deposition (PE-CVD), high-density plasma (HDP) CVD, diffusion furnace CVD, remote plasma CVD, other forms of CVD, ALD, plasma-enhanced ALD, sputtering, other forms of PVD, and other deposition approaches known in the arts.
In one embodiment, the second insulating layer may be deposited to a thickness in the approximate range of 15 nm to 500 nm, although the scope of the invention is not limited to any known thickness. If desired, a top portion of the deposited second insulating layer may optionally be removed or planarized, such as, for example, by chemical-mechanical polishing (CMP) or other polishing, or by wet etching, dry etching, or other etching, or by a combination of such approaches, although this is not required.
Refer briefly to
Referring back to
In one or more embodiments of the invention, the openings may be formed by depositing and patterning a photoresist layer with gaps or openings corresponding to the openings to be etched. Then, an etchant may be used to remove portions of the second insulating layer to form the openings. Various known hydrocarbon-based or halogen-based etching chemistries are suitable.
Refer now to
In particular, three openings are formed. A first opening 352A is formed through the first and second insulating layers down to the top surface of the substrate over the source region of the transistor. Likewise, a second opening 352C is formed through the first and second insulating layers down to the top surface of the substrate over the drain region. A third opening 352B is formed through the second insulating layer and through, or at least through a substantial portion of, the etch stop layer over the metal gate. The substantial portion will generally include much or most of the thickness of the etch stop layer if the etch stop layer is highly dielectric, alternatively it may be less if the etch stop layer is more conducting.
The scope of the invention is not limited to any known size or shape of the opening. However, in one or more embodiments, the diameter of each of the three openings may be in the range of about 0.2 um to 30 um (often in the range of about 0.2 um to 10 um). In one or more embodiments, the diameter of each of the three openings may be based on the aspect ratio of the openings, and may, for example, be in the range of about 1:10 to 1:100. In one or more embodiments, the openings may have a tapered shape, with the top of the openings being wider than the bottom. However, the scope of the invention is not limited to these particular sizes or shapes.
Referring again to
Refer now to
As previously mentioned, it is not required to convert or consume the native metal of the metal gate to form the etch stop layer. As another option, in one or more embodiments of the invention, a metal layer cap may be selectively deposited over the native metal of the top surface of the metal gate, and then the etch stop layer may be formed over the metal gate by reactively converting at least a portion of the deposited metal layer cap to a metal compound.
Referring first to
In one or more embodiments of the invention, the metal may be different than a native metal of the metal gate on which the metal is deposited directly on. Advantageously, the deposition of a metal cap of a different metal may allow the metal of the etch stop layer and the metal of the metal gate to be selected relatively independently of one another in order to meet each of the metals respective design objectives. For example, the metal of the metal cap may be selected based on its ability to form a metal compound under particular conditions, its ability to form a passivating layer, or for other reasons, without changing the metal of the metal gate. Furthermore, there is no requirement that the metal of the metal gate be either capable of forming a metal compound under the formation conditions or be capable of forming a passivating layer (e.g., some may form thicker oxide layers than desired).
Examples of suitable metals according to one or more embodiments include, but are not limited to, copper (Cu), ruthenium (Ru), nickel (Ni), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), titanium (Ti), aluminum (Al), hafnium (Hf), tantalum (Ta), tungsten (W), vanadium (V), molybdenum (Mo), palladium (Pd), gold (Au), silver (Au), platinum (Pt), and combinations thereof. In one or more embodiments of the invention, the metal may include aluminum (Al), chromium (Cr), molybdenum (Mo), and nickel (Ni), although the scope of the invention is not limited to just these metals. In one or more embodiments of the invention, the metal may be capable of forming a passivating oxide, a passivating nitride, a passivating carbide, or a combination thereof.
Examples of approaches that may be used to selectively deposit the metal over the metal gate include, but are not limited to, electroless deposition, ALD, and CVD. Methods of using these techniques for selective deposition are known in the arts. By way of example, see the article “Selective Metallization by Chemical Vapor Deposition”, by Wayne Gladfelter, in Chem. Mater. 1993, 5, 1372-1388.
In one or more embodiments of the invention, prior to depositing the metal cap layer, the top surface of the metal gate may optionally be pre-treated to improve deposition, although this is not required. By way of example, in one or more embodiments of the invention, the metal of the metal gate may be exposed to hydrogen, such as, for example, in the form of a plasma including hydrogen. The hydrogen may help to reduce or otherwise remove or reduce oxide and/or organic contaminants from the top surface of the metal gate. If the first insulating layer includes silicon dioxide (SiO2), the hydrogen may also help to convert silanol groups (Si—OH) to siloxane (Si—O—Si) bridge bonds. Heating, annealing, or rapid annealing may then be used to desorb the hydrogen. In one aspect, the temperature may be less than about 200° C. This pre-treatment may help to create clean active metal sites with dangling bonds which are receptive to selective deposition, and reduce defects and active sites on the silicon dioxide.
Referring again to
Refer now to
In one or more embodiments of the invention, the etches for the source and drain contacts and the etch for the gate contact may be performed at different times and have different etch chemistries. The etch stop layer may have different and slower etch rate than the first and second insulating layers. The etches for the source and drain contact may be capable of etching the first and second insulating layers but significantly slower at etching the selective etch stop layer over the gate. Accordingly, it may be easy to stop the source and drain etches on the etch stop layer. In addition, the etch stop layer over the gate may be, in one or more embodiments, dielectric or insulating. As a result, if a misaligned source and/or drain etch occurs over the metal gate, the etch may stop at the etch stop layer with a thickness 633 of the insulating or dielectric etch stop layer material disposed between the conductive material in the contact and the metal gate. This insulating material may help to prevent, or at least reduce, contact-to-gate shorts. It is to be appreciated that in practice the misaligned source/drain contact may land partially on the gate but still extend down to contact the source. The illustration represents a simple, conceptual view to better illustrate certain concepts.
In contrast, the etch for the gate contact may be capable of etching the etch stop layer more rapidly than the etch for the source and drain contacts. Since the gate contact etches need to etch through the etch stop layer, but the source and drain contact etches do not, the gate contact etch may be designed to be much better at etching the etch stop layer. Alternatively, the gate etch may stop on the etch stop layer and an additional gate etch may be used to etch through the etch stop layer. As a result, the etch for the gate contact may etch through the etch stop layer and land on or sufficiently near the metal gate that electrical connection may be achieved.
Accordingly, the etch stop layers disclosed herein, which are selectively on the gate, may help to prevent, or at least reduce, the amount of contact-to-gate shortings. Furthermore, this ability to prevent, or at least reduce, shorting at spacings that are smaller then your registration capabilities, may allow more transistors to be packed into a smaller area and help to increase the number of transistors per die and/or reduce die size. The etch stop layers as disclosed herein may also help to reduce rework during lithography to obtain good alignment/registration, which may help to reduce manufacturing costs.
In the following description and claims, the terms “coupled” and “connected,” along with their derivatives, may be used. It should be understood that these terms are not intended as synonyms for each other. Rather, in particular embodiments, “connected” may be used to indicate that two or more elements are in direct physical or electrical contact with each other. “Coupled” may mean that two or more elements are in direct physical or electrical contact. However, “coupled” may also mean that two or more elements are not in direct contact with each other, but yet still co-operate or interact with each other. Similarly, the term “over” may mean, but does not necessarily mean, “on”. There may be one or more intervening materials, layers, or other structures.
In the description above, for the purposes of explanation, numerous specific details have been set forth in order to provide a thorough understanding of the embodiments of the invention. It will be apparent however, to one skilled in the art, that one or more other embodiments may be practiced without some of these specific details. The particular embodiments described are not provided to limit the invention but to illustrate it. The scope of the invention is not to be determined by the specific examples provided above but only by the claims below. In other instances, well-known circuits, structures, devices, and operations have been shown in block diagram form or without detail in order to avoid obscuring the understanding of the description.
It will also be appreciated, by one skilled in the art, that modifications may be made to the embodiments disclosed herein, such as, for example, to the sizes, shapes, configurations, forms, functions, materials, and manner of operation, and assembly and use, of the components of the embodiments. All equivalent relationships to those illustrated in the drawings and described in the specification are encompassed within embodiments of the invention.
For simplicity and clarity of illustration, elements illustrated in the figures have not necessarily been drawn to scale. For example, the dimensions of some of the elements are exaggerated relative to other elements for clarity. Further, where considered appropriate, reference numerals or terminal portions of reference numerals have been repeated among the figures to indicate corresponding or analogous elements, which may optionally have similar characteristics.
Various operations and methods have been described. Some of the methods have been described in a basic form, but operations may optionally be added to and/or removed from the methods. The operations of the methods may also often optionally be performed in different order. Many modifications and adaptations may be made to the methods and are contemplated.
For clarity, in the claims, any element that does not explicitly state “means for” performing a specified function, or “step for” performing a specified function, is not to be interpreted as a “means” or “step” clause as specified in 35 U.S.C. Section 112, Paragraph 6. In particular, any potential use of “step of” in the claims herein is not intended to invoke the provisions of 35 U.S.C. Section 112, Paragraph 6.
It should also be appreciated that reference throughout this specification to “one embodiment”, “an embodiment”, or “one or more embodiments”, for example, means that a particular feature may be included in the practice of the invention. Similarly, it should be appreciated that in the description various features are sometimes grouped together in a single embodiment, Figure, or description thereof for the purpose of streamlining the disclosure and aiding in the understanding of various inventive aspects. This method of disclosure, however, is not to be interpreted as reflecting an intention that the invention requires more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects may lie in less than all features of a single disclosed embodiment. Thus, the claims following the Detailed Description are hereby expressly incorporated into this Detailed Description, with each claim standing on its own as a separate embodiment of the invention.
Accordingly, while the invention has been thoroughly described in terms of several embodiments, those skilled in the art will recognize that the invention is not limited to the particular embodiments described, but may be practiced with modification and alteration within the spirit and scope of the appended claims. The description is thus to be regarded as illustrative instead of limiting.