As consumer devices have gotten smaller and smaller in response to consumer demand, the individual components of these devices have necessarily decreased in size as well. Semiconductor devices, which make up a major component of devices such as mobile phones, computer tablets, and the like, have been pressured to become smaller and smaller, with a corresponding pressure on the individual devices (e.g., transistors, resistors, capacitors, etc.) within the semiconductor devices to also be reduced in size.
One enabling technology that is used in the manufacturing processes of semiconductor devices is the use of photolithographic materials. Such materials are applied to a surface of a layer to be patterned and then exposed to an energy that has itself been patterned. Such an exposure modifies the chemical and physical properties of the exposed regions of the photosensitive material. This modification, along with the lack of modification in regions of the photosensitive material that were not exposed, can be exploited to remove one region without removing the other.
However, as the size of individual devices has decreased, process windows for photolithographic processing has become tighter and tighter. As such, advances in the field of photolithographic processing are necessary to maintain the ability to scale down the devices, and further improvements are needed in order to meet the desired design criteria such that the march towards smaller and smaller components may be maintained.
The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.
It is to be understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the disclosure. Specific embodiments or examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, dimensions of elements are not limited to the disclosed range or values, but may depend upon process conditions and/or desired properties of the device. Moreover, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed interposing the first and second features, such that the first and second features may not be in direct contact. Various features may be arbitrarily drawn in different scales for simplicity and clarity.
Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The device may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly. In addition, the term “made of” may mean either “comprising” or “consisting of.”
Extreme ultraviolet (EUV) lithography to achieve sub-20 nm half-pitch resolution is under development for mass production for next generation sub 5 nm node. EUV lithography requires a high performance photoresist with high sensitivity for cost reduction of the high-power exposure source, and to provide good resolution of the image. Metallic resists have been developed that provide high sensitivity and good resolution. However, pattern collapse and increased line width roughness and line edge roughness may occur. Embodiments of this disclosure provide improved integrity of the photoresist pattern and decreased line width roughness, line edge roughness, and scum reduction. Embodiments of the disclosure allow reduced exposure doses.
A resist layer composition is subsequently coated on a surface of the resist underlayer 20 in operation S130, in some embodiments, to form a resist layer 15, as shown in
After the second (or pre-exposure) baking operation S140 of the photoresist layer 15, the photoresist layer 15 is selectively exposed to actinic radiation 45/97 (see
As shown in
In some embodiments, the selective exposure of the photoresist layer 15 to form exposed regions 50 and unexposed regions 52 is performed using extreme ultraviolet lithography. In an extreme ultraviolet lithography operation a reflective photomask 65 is used to form the patterned exposure light in some embodiments, as shown in
The region of the photoresist layer exposed to radiation 50 undergoes a chemical reaction thereby changing its solubility in a subsequently applied developer relative to the region of the photoresist layer not exposed to radiation 52. In some embodiments, the portion of the photoresist layer exposed to radiation 50 undergoes a crosslinking reaction. In addition to causing the chemical reaction in the photoresist layer 15, a portion of the radiation 45/97 also passes through the photoresist layer 15 and causes a reaction in the resist underlayer 20. The reaction in the resist underlayer 20 results in a small molecule being generated, which subsequently diffuses into the photoresist layer 15.
Next, the photoresist layer 15 and the resist underlayer 20 undergoes a third baking (or post-exposure bake (PEB)) in operation S160. In some embodiments, the photoresist layer 15 is heated at a temperature of about 50° C. to 200° C. for about 20 seconds to about 120 seconds. The post-exposure baking may be used to assist in the generating, dispersing, and reacting of the acid/base/free radical generated from the impingement of the radiation 45/97 upon the photoresist layer 15 during the exposure, and to assist in the diffusion of the small molecule from the exposed portion 20b of the resist underlayer 20 into the photoresist layer 15. Such assistance helps to create or enhance chemical reactions, which generate chemical differences between the exposed region 50 and the unexposed region 52 within the photoresist layer.
The selectively exposed photoresist layer is subsequently developed by applying a developer to the selectively exposed photoresist layer in operation S170. As shown in
In some embodiments, the pattern of openings 55 in the photoresist layer 15 is extended through the underlayer 20 into the substrate 10 to create a pattern of openings 55′ in the substrate 10, thereby transferring the pattern in the photoresist layer 15 into the substrate 10, as shown in
In some embodiments, the substrate 10 includes a single crystalline semiconductor layer on at least it surface portion. The substrate 10 may include a single crystalline semiconductor material such as, but not limited to Si, Ge, SiGe, GaAs, InSb, GaP, GaSb, InAlAs, InGaAs, GaSbP, GaAsSb and InP. In some embodiments, the substrate 10 is a silicon layer of an SOI (silicon-on insulator) substrate. In certain embodiments, the substrate 10 is made of crystalline Si.
The substrate 10 may include in its surface region, one or more buffer layers (not shown). The buffer layers can serve to gradually change the lattice constant from that of the substrate to that of subsequently formed source/drain regions. The buffer layers may be formed from epitaxially grown single crystalline semiconductor materials such as, but not limited to Si, Ge, GeSn, SiGe, GaAs, InSb, GaP, GaSb, InAlAs, InGaAs, GaSbP, GaAsSb, GaN, GaP, and InP. In an embodiment, the silicon germanium (SiGe) buffer layer is epitaxially grown on the silicon substrate 10. The germanium concentration of the SiGe buffer layers may increase from 30 atomic % for the bottom-most buffer layer to 70 atomic % for the top-most buffer layer.
In some embodiments, the substrate 10 includes one or more layers of at least one metal, metal alloy, and metal nitride/sulfide/oxide/silicide having the formula MXa, where M is a metal and X is N, S, Se, 0, Si, and a is from about 0.4 to about 2.5. In some embodiments, the substrate 10 includes titanium, aluminum, cobalt, ruthenium, titanium nitride, tungsten nitride, tantalum nitride, and combinations thereof.
In some embodiments, the substrate 10 includes a dielectric having at least a silicon or metal oxide or nitride of the formula MXb, where M is a metal or Si, X is N or O, and b ranges from about 0.4 to about 2.5. In some embodiments, the substrate 10 includes silicon dioxide, silicon nitride, aluminum oxide, hafnium oxide, lanthanum oxide, and combinations thereof.
In some embodiments, the resist underlayer 20 improves the adhesion of the resist layer 15 to the substrate. In some embodiments, the resist underlayer 20 functions as a bottom anti-reflective coating (BARC). The BARC absorbs actinic radiation that passes through the photoresist layer, thereby preventing the actinic radiation from reflecting off the substrate or a target layer and exposing unintended portions of the photoresist layer. Thus, the BARC improves line width roughness and line edge roughness of the photoresist pattern.
The resist underlayer 20 is made of polymer compositions, wherein the polymer has pendant target groups. In some embodiments, the polymer has one or more pendant target groups and a pendant organic group. In some embodiments, the pendant organic group includes a photosensitive functional group including a chemical reporter molecule, as shown in
In some embodiments, the pendant organic group are aromatic groups, photoacid generators (PAGs), and other sensitizers. In some embodiments, a photosensitive compound is included in the polymer composition, such as a PAG or a photobase generator (PBG). After exposure to actinic radiation, the photosensitive functional group or photosensitive compound releases chemical reporter molecules and the chemical reporter transfers from the photosensitive functional group or photosensitive compound to the target group. The target groups release desired small molecules when receiving the chemical reporter molecules, as shown in
In some embodiments, the chemical reporter molecules include an electron, an anion, a cation, H+, O2, H2O, NH3, HF, HCl, ROH, or RNH2, where R is a C1-C10 group. R includes a functional group selected from the group consisting of one or more of —I, —Br, —Cl, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, an imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, a carboxyl group, an acetic acid group, a cyanide group, an allene group, an alcohol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, and a pyrrole group.
In some embodiments, the small molecules include an electron, an anion, a cation, H+, O2, H2O, NH3, HF, HCl, ROH, or RNH2, where R is a C1-C10 group. R includes a functional group selected from the group consisting of one or more of —I, —Br, —Cl, —F, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, an imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, a carboxyl group, an acetic acid group, a cyanide group, an allene group, an alcohol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, and a pyrrole group. In some embodiments, the chemical reporter molecule and the small molecules are different molecules.
A first reaction mechanism is illustrated in
In a second reaction mechanism according to some embodiments, water is generated as the small molecule from a target group having a carbonyl group, such as an aldehyde or a ketone. The polymer composition includes a photobase generator (PBG). As shown in
In some embodiments, the polymer composition of the resist underlayer 20 includes a polymer having one or more pendant diol target groups D and one or more pendant organic groups B, and the photoacid generator PAG is a separate compound in the polymer composition, as shown in
The diol D can be 1,n-diol, where n>0. The structure of the diol D can be non-cyclic or cyclic, and the cyclic structure can be an aromatic or a non-aromatic ring. In some embodiments, the diol D is a substituted or unsubstituted C2-C30 group. In some embodiments, the C2-C30 group is substituted with one or more of —I, —Br, —Cl, —F, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, an imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, an acetic acid group, a carboxylic acid group, a cyanide group, an allene group, an alcohol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, or a pyrrole group.
The organic group B can be a non-cyclic structure or a cyclic structure, and the cyclic structure can be an aromatic or a non-aromatic ring. In some embodiments, the organic group B is a substituted or unsubstituted C1-C30 group. In some embodiments, the C1-C30 group is substituted with one or more of —I, —Br, —Cl, —F, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, an imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, an acetic acid group, a carboxylic acid group, or a cyanide group.
The crosslinker CL of the resist underlayer 20 may be any suitable crosslinker. The cross linker CL reacts with a functional group on one polymer and a functional group on another polymer to crosslink and bond the two polymer chains together. This bonding and crosslinking increases the molecular weight of the polymer products of the crosslinking reaction and increases the overall density of the underlayer. In some embodiments, the crosslinker is a separate component of the resist underlayer polymer composition. In other embodiments, the crosslinker is attached to the polymer in the resist underlayer polymer composition.
In some embodiments the crosslinker has the following structure:
In other embodiments, the crosslinker has the following structure:
wherein C is carbon, n ranges from 1 to 15; A and B independently include a hydrogen atom, a hydroxyl group, a halide, an aromatic carbon ring, or a straight or cyclic alkyl, alkoxyl/fluoro, alkyl/fluoroalkoxyl chain having a carbon number of between 1 and 12, and each carbon C contains A and B; a first terminal carbon C at a first end of a carbon C chain includes X and a second terminal carbon C at a second end of the carbon chain includes Y, wherein X and Y independently include an amine group, a thiol group, a hydroxyl group, an isopropyl alcohol group, or an isopropyl amine group, except when n=1 then X and Y are bonded to the same carbon C. Specific examples of materials that may be used as the crosslinker include the following:
Alternatively, instead of or in addition to the crosslinker being added to the resist underlayer composition, a coupling reagent is added in some embodiments, in which the coupling reagent is added in addition to the cross linker agent. The coupling reagent assists the crosslinking reaction by reacting with the functional groups on the polymer before the crosslinker, allowing for a reduction in the reaction energy of the crosslinking reaction and an increase in the rate of reaction. The bonded coupling reagent then reacts with the crosslinker agent, thereby coupling the crosslinker to the polymers.
In some embodiments, the coupling reagent has the following structure:
where R is a carbon atom, a nitrogen atom, a sulfur atom, or an oxygen atom; M includes a chlorine atom, a bromine atom, an iodine atom, —NO2; —SO3—; —H—; —CN; —NCO, —OCN; —CO2—; —OH; —OR*, —OC(O)CR*; —SR, —SO2N(R*)2; —SO2R*; SOR; —OC(O)R*; —C(O)OR*; —C(O)R*; —Si(OR*)3; —Si(R*)3; epoxy groups, or the like; and R* is a substituted or unsubstituted C1-C12 alkyl, C1-C12 aryl, C1-C12 aralkyl, or the like. Specific examples of materials used as the coupling reagent in some embodiments include the following:
In some embodiments, the thermal acid generator (TAG) is one or more selected from the group consisting of
where 0≤n≤10, and R is hydrogen or a substituted or unsubstituted C1-C10 alkyl group. In some embodiments, the thermal acid generator is selected from NH4+C4F9SO3− and NH4+CF3SO3−
In some embodiments, the first baking operation S120 activates the TAG and generates an acid. Some of the acid generated by the TAG may diffuse from the underlayer 20 into the photoresist layer 15, and small molecules may be generated as a result of the acid generation by the TAG. However, the effect on the photoresist layer 15 of the TAG is limited, as most of the acid generated by the TAG is used for crosslinking the underlayer polymer. Furthermore, TAG remaining after the crosslinking of the underlayer polymer evaporates during the first baking operation in some embodiments. Small molecule generation by the TAG is insignificant compared to small molecule generation caused by photoacid generator (PAG). Any acid generated by TAG remaining by the time of post-exposure baking operation S160 is negligible compared to the amount of acid generated by the photoacid generator (PAG). Thus, the effect of the TAG on the photoresist baking S140, radiation exposure S150, post exposure baking S160, and development operations S170 is negligible compared to the effect of the PAG in some embodiments.
The PAG or a combination of the PAG and TAG are included in the underlayer at a concentration ranging from about 0.1 wt. % to about 20 wt. % relative to the total weight of the polymer composition. At concentrations below about 0.1 wt. % there may not be a sufficient amount of the PAG or TAG to provide the desired effect. At concentrations of the PAG or TAG greater than about 20 wt. % substantial improvement in the photoresist pattern profile may not be obtained.
In some embodiments, an additive, such as a surfactant, is added to the resist underlayer polymer composition. In some embodiments, the surfactants include nonionic surfactants, polymers having fluorinated aliphatic groups, surfactants that contain at least one fluorine atom and/or at least one silicon atom, polyoxyethylene alkyl ethers, polyoxyethylene alkyl aryl ethers, polyoxyethylene-polyoxypropylene block copolymers, sorbitan fatty acid esters, and polyoxyethylene sorbitan fatty acid esters.
Specific examples of materials used as surfactants in some embodiments include polyoxyethylene lauryl ether, polyoxyethylene stearyl ether, polyoxyethylene cetyl ether, polyoxyethylene oleyl ether, polyoxyethylene octyl phenol ether, polyoxyethylene nonyl phenol ether, sorbitan monolaurate, sorbitan monopalmitate, sorbitan monostearate, sorbitan monooleate, sorbitan trioleate, sorbitan tristearate, polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monopalmitate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan trioleate, polyoxyethylene sorbitan tristearate, polyethylene glycol distearate, polyethylene glycol dilaurate, polyethylene glycol dilaurate, polyethylene glycol, polypropylene glycol, polyoxyethylenestearyl ether, polyoxyethylene cetyl ether, fluorine containing cationic surfactants, fluorine containing nonionic surfactants, fluorine containing anionic surfactants, cationic surfactants and anionic surfactants, polyethylene glycol, polypropylene glycol, polyoxyethylene cetyl ether, combinations thereof, or the like.
In some embodiments, a main chain of the polymer is selected from the group consisting of a polystyrene, a polyhydroxystyrene, a polyacrylate, a polymethylacrylate, a polymethylmethacrylate, a polyacrylic acid, a polyvinyl ester, a polymaleic ester, a poly(methacrylonitrile), and poly(methacrylamide). In some embodiments, the pendant organic groups are photosensitive functional groups that release a chemical reporter molecule in the portions of the resist underlayer exposed to actinic radiation. In some embodiments, the organic group is a substituted or unsubstituted C3-C30 aliphatic or aromatic group having at least one photosensitive functional group. In some embodiments, the photosensitive functional group is one or more of an epoxy group, an azo group, an alkyl halide group, an imine group, an alkene group, an alkyne group, a peroxide group, a ketone group, an aldehyde group, an allene group, an aromatic group or a heterocyclic group. The aromatic groups can be phenyl, napthalenyl, phenanthrenyl, anthracenyl, phenalenyl, and other aromatic groups containing three to ten-membered rings. In some embodiments, the pendant target groups include a substituted, non-cyclic or cyclic structure. The cyclic structure can be an aromatic or a non-aromatic ring. In some embodiments, the target group is a C1-C30 group including a functional group selected from one or more of the group consisting of —I, —Br, —Cl, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, an imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, a carboxyl group, a cyanide group, an allene group, an alcohol group, a diol group, a triol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, and a pyrrole group.
In some embodiments, the various components of the resist underlayer polymer composition are mixed in a solvent to facilitate application of the polymer composition to the substrate. In some embodiments, the solvent is one or more selected from propylene glycol methyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), 1-ethoxy-2-propanol (PGEE), γ-butyrolactone (GBL), cyclohexanone (CHN), ethyl lactate (EL), methanol, ethanol, propanol, n-butanol, acetone, dimethylformamide (DMF), isopropanol (IPA), tetrahydrofuran (THF), methyl isobutyl carbinol (MIBC), n-butyl acetate (nBA), and 2-heptanone (MAK).
In some embodiments, the PAG is bound to the polymer in the resist underlayer polymer composition, as shown in
In some embodiments, the free PAG compounds in the composition illustrated in
The diol group D, organic group B, crosslinker CL, TAG, and additive can be any of the diol groups, organic groups, crosslinkers, TAGs, and additives disclosed herein in reference to the composition illustrated in
In some embodiments, a second mechanism is employed to generate the small molecules. In the second mechanism, a photobase generator (PBG) is used to generate the chemical reporter molecule, and the target group is a carbonyl group, such as an aldehyde group or a ketone group. In some embodiments, the polymer composition includes a polymer having one or more pendant carbonyl target groups E and one of more pendant organic groups B. The PBG is a separate compound in the polymer composition, as shown in
In some embodiments, the target group E has a carbonyl group. In some embodiments, the target group can be an aldehyde group, a ketone group, an ester group, an amide group, or any other suitable group including a carbonyl group. In some embodiments, the pendant target groups include a substituted, non-cyclic or cyclic structure. The cyclic structure can be an aromatic or a non-aromatic ring. In some embodiments, the target group is a C1-C30 group including a functional group selected from one or more of the group consisting of —I, —Br, —Cl, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, an imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, a carboxyl group, a cyanide group, an allene group, an alcohol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, and a pyrrole group.
The organic group B, crosslinker CL, TAG, and additive can be any of the diol groups, organic groups, crosslinkers, TAGs, and additives disclosed herein in reference to the composition illustrated in
Examples of photobase generators and reactions showing the generation of amine chemical reporter molecules upon the exposure of the PBG to actinic radiation are shown in
In some embodiments, the photobase generator is one or more selected from the group consisting of quaternary ammonium dithiocarbamates, a aminoketones, oxime-urethane containing molecules, dibenzophenoneoxime hexamethylene diurethan, ammonium tetraorganylborate salts, and N-(2-nitrobenzyloxycarbonyl)cyclic amines, and combinations thereof. In some embodiments, the thermal base generator is one or more selected from the group consisting of:
In some embodiments, the resist underlayer 20 is formed by preparing an underlayer coating composition of any of the polymer composition components disclosed herein in a solvent. The solvent can be any suitable solvent for dissolving the polymer and the selected components of the compositions. The underlayer coating composition is applied over a substrate 10 or target layer, such as by spin coating. Then the underlayer composition is baked to dry the underlayer, as explained herein in reference to
In some embodiments, the thickness of the resist underlayer 20 ranges from about 2 nm to about 300 nm, and in other embodiments, the resist underlayer thickness ranges from about 20 nm to about 100 nm. In some embodiments, the thickness of the resist underlayer 20 ranges from about 40 nm to about 80 nm. Resist underlayer thicknesses less than the disclosed ranges may be insufficient to provide adequate photoresist adhesion, LWR improvement, and anti-reflective properties. Resist underlayer thicknesses greater than the disclosed ranges may be unnecessarily thick and may not provide further improvement in resist layer adhesion, LWR improvement, and scum reduction.
In some embodiments, the photoresist layer 15 is a photosensitive layer that is patterned by exposure to actinic radiation. Typically, the chemical properties of the photoresist regions struck by incident radiation change in a manner that depends on the type of photoresist used. Photoresist layers 15 are either positive tone resists or negative tone resists. A positive tone resist refers to a photoresist material that when exposed to radiation, such as UV light, becomes soluble in a developer, while the region of the photoresist that is non-exposed (or exposed less) is insoluble in the developer. A negative tone resist, on the other hand, refers to a photoresist material that when exposed to radiation becomes insoluble in the developer, while the region of the photoresist that is non-exposed (or exposed less) is soluble in the developer. The region of a negative resist that becomes insoluble upon exposure to radiation may become insoluble due to a cross-linking reaction caused by the exposure to radiation.
Whether a resist is a positive tone or negative tone may depend on the type of developer used to develop the resist. For example, some positive tone photoresists provide a positive pattern, (i.e. —the exposed regions are removed by the developer), when the developer is an aqueous-based developer, such as a tetramethylammonium hydroxide (TMAH) solution. On the other hand, the same photoresist provides a negative pattern (i.e. —the unexposed regions are removed by the developer) when the developer is an organic solvent. Further, in some negative tone photoresists developed with the TMAH solution, the unexposed regions of the photoresist are removed by the TMAH, and the exposed regions of the photoresist, that undergo cross-linking upon exposure to actinic radiation, remain on the substrate after development.
In some embodiments, the photoresist layer 15 is made of a photoresist composition, including a first compound or a first precursor and a second compound or a second precursor combined in a vapor state. The first precursor or first compound is an organometallic having a formula: MaRbXc, as shown in
In some embodiments, R is alkyl, such as CnH2n+1 where n≥3. In some embodiments, R is fluorinated, e.g., having the formula CnFxH((2n+1)−x). In some embodiments, R has at least one beta-hydrogen or beta-fluorine. In some embodiments, R is selected from the group consisting of i-propyl, n-propyl, t-butyl, i-butyl, n-butyl, sec-butyl, n-pentyl, i-pentyl, t-pentyl, and sec-pentyl, and combinations thereof.
In some embodiments, X is any moiety readily displaced by the second compound or second precursor to generate an M-OH moiety, such as a moiety selected from the group consisting of amines, including dialkylamino and monalkylamino; alkoxy; carboxylates, halogens, and sulfonates. In some embodiments, the sulfonate group is substituted with one or more amine groups. In some embodiments, the halide is one or more selected from the group consisting of F, Cl, Br, and I. In some embodiments, the sulfonate group includes a substituted or unsubstituted C1-C3 group.
In some embodiments, the first organometallic compound or first organometallic precursor includes a metallic core M+ with ligands L attached to the metallic core M+, as shown in
In some embodiments, the organometallic precursor or organometallic compound include a sec-hexyl tris(dimethylamino) tin, t-hexyl tris(dimethylamino) tin, i-hexyl tris(dimethylamino) tin, n-hexyl tris(dimethylamino) tin, sec-pentyl tris(dimethylamino) tin, t-pentyl tris(dimethylamino) tin, i-pentyl tris(dimethylamino) tin, n-pentyl tris(dimethylamino) tin, sec-butyl tris(dimethylamino) tin, t-butyl tris(dimethylamino) tin, i-butyl tris(dimethylamino) tin, n-butyl tris(dimethylamino) tin, sec-butyl tris(dimethylamino) tin, propyl tris(dimethylamino) tin, n-propyl tris(diethylamino) tin, and analogous alkyl(tris)(t-butoxy) tin compounds, including sec-hexyl tris(t-butoxy) tin, t-hexyl tris(t-butoxy) tin, i-hexyl tris(t-butoxy) tin, n-hexyl tris(t-butoxy) tin, sec-pentyl tris(t-butoxy) tin, t-pentyl tris(t-butoxy) tin, i-pentyl tris(t-butoxy) tin, n-pentyl tris(t-butoxy) tin, t-butyl tris(t-butoxy) tin, i-butyl tris(butoxy) tin, n-butyl tris(butoxy) tin, sec-butyl tris(butoxy) tin, i-propyl(tris)dimethylamino tin, or n-propyl tris(butoxy) tin. In some embodiments, the organometallic precursors or organometallic compounds are fluorinated. In some embodiments, the organometallic precursors or compounds have a boiling point less than about 200° C.
In some embodiments, the first compound or first precursor includes one or more unsaturated bonds that can be coordinated with a functional group, such as a hydroxyl group, on the surface of the substrate or an intervening underlayer to improve adhesion of the photoresist layer to the substrate or underlayer.
In some embodiments, the second precursor or second compound is at least one of an amine, a borane, a phosphine, or water. In some embodiments, the amine has a formula NpHnXm, where 0≤n≤3, 0≤m≤3, n+m=3 when p is 1, and n+m=4 when p is 2, and each X is independently a halogen selected from the group consisting of F, Cl, Br, and I. In some embodiments, the borane has a formula BpHnXm, where 0≤n≤3, 0≤m≤3, n+m=3 when p is 1, and n+m=4 when p is 2, and each X is independently a halogen selected from the group consisting of F, Cl, Br, and I. In some embodiments, the phosphine has a formula PpHnXm, where 0≤n≤3, 0≤m≤3, n+m=3, when p is 1, or n+m=4 when p is 2, and each X is independently a halogen selected from the group consisting of F, Cl, Br, and I.
In some embodiments, the operation S130 of depositing a photoresist composition is performed by a vapor phase deposition operation. In some embodiments, the vapor phase deposition operation includes atomic layer deposition (ALD) or chemical vapor deposition (CVD). In some embodiments, the ALD includes plasma-enhanced atomic layer deposition (PE-ALD), and the CVD includes plasma-enhanced chemical vapor deposition (PE-CVD), metal-organic chemical vapor deposition (MO-CVD); atmospheric pressure chemical vapor deposition (AP-CVD), and low pressure chemical vapor deposition (LP-CVD). In other embodiments, the organometallic resist is applied to the substrate 10 or a target layer by a spin coating operation.
In some embodiments, the photoresist layer 15 is formed to a thickness of about 5 nm to about 50 nm, and to a thickness of about 10 nm to about 30 nm in other embodiments. A person of ordinary skill in the art will recognize that additional ranges of thicknesses within the explicit ranges above are contemplated and are within the present disclosure. The thickness can be evaluated using non-contact methods of x-ray reflectivity and/or ellipsometry based on the optical properties of the photoresist layers. In some embodiments, each photoresist layer thickness is relatively uniform to facilitate processing. In some embodiments, the variation in thickness of the deposited photoresist layer varies by no more than ±25% from the average thickness, in other embodiments each photoresist layer thickness varies by no more than ±10% from the average photoresist layer thickness. In some embodiments, such as high uniformity depositions on larger substrates, the evaluation of the photoresist layer uniformity may be evaluated with a 1 centimeter edge exclusion, i.e., the layer uniformity is not evaluated for portions of the coating within 1 centimeter of the edge. A person of ordinary skill in the art will recognize that additional ranges within the explicit ranges above are contemplated and are within the present disclosure.
In some embodiments, the organometallic compound includes tin (Sn), antimony (Sb), bismuth (Bi), indium (In), and/or tellurium (Te) as the metal component, however, the disclosure is not limited to these metals. In other embodiments, additional suitable metals include titanium (Ti), zirconium (Zr), hafnium (Hf), vanadium (V), cobalt (Co), molybdenum (Mo), tungsten (W), aluminum (Al), gallium (Ga), silicon (Si), germanium (Ge), phosphorus (P), arsenic (As), yttrium (Y), lanthanum (La), cerium (Ce), lutetium (Lu), or combinations thereof. The additional metals can be as alternatives to or in addition to the Sn, Sb, Bi, In, and/or Te.
The particular metal used may significantly influence the absorption of radiation. Therefore, the metal component can be selected based on the desired radiation and absorption cross section. Tin, antimony, bismuth, tellurium, and indium provide strong absorption of extreme ultraviolet light at 13.5 nm. Hafnium provides good absorption of electron beam and extreme UV radiation. Metal compositions including titanium, vanadium, molybdenum, or tungsten have strong absorption at longer wavelengths, to provide, for example, sensitivity to 248 nm wavelength ultraviolet light.
When subsequently exposed to extreme ultraviolet radiation, the organometallic compound absorbs the extreme ultraviolet radiation and one or more organic R groups are cleaved from the organometallic compound to form an amino metallic compound in the radiation exposed areas. Then, when the post-exposure bake (PEB) performed, the amino metallic compounds crosslink through the amine groups in some embodiments, as shown in
After PEB, the latent pattern in the photoresist layer is developed to form a patterned photoresist layer. In some embodiments, the photoresist developer 57 includes a solvent, and an acid or a base. In some embodiments, the concentration of the solvent is from about 60 wt. % to about 99 wt. % based on the total weight of the photoresist developer. The acid or base concentration is from about 0.001 wt. % to about 20 wt. % based on the total weight of the photoresist developer. In certain embodiments, the acid or base concentration in the developer is from about 0.01 wt. % to about 15 wt. % based on the total weight of the photoresist developer.
In some embodiments, the developer 57 is applied to the photoresist layer 15 using a spin-on process. In the spin-on process, the developer 57 is applied to the photoresist layer 15 from above the photoresist layer 15 while the photoresist-coated substrate is rotated, as shown in
While the spin-on operation is one suitable method for developing the photoresist layer 15 after exposure, it is intended to be illustrative and is not intended to limit the embodiment. Rather, any suitable development operations, including dip processes, puddle processes, and spray-on methods, may alternatively be used. All such development operations are included within the scope of the embodiments.
During the development process, the developer 57 dissolves the radiation-unexposed regions 52 of the cross-linked negative resist, exposing the surface of the underlayer 20, as shown in
After the developing operation S170, remaining developer is removed from the patterned photoresist covered substrate. The remaining developer is removed using a spin-dry process in some embodiments, although any suitable removal technique may be used. After the photoresist layer 15 is developed, and the remaining developer is removed, additional processing is performed while the patterned photoresist layer 50 is in place. For example, an etching operation, using dry or wet etching, is performed in some embodiments, to transfer the pattern of the photoresist layer 50 through the underlayer 20 to the underlying substrate 10, forming openings 55′ as shown in
In some embodiments, a target layer 60 to be patterned is disposed over the substrate prior to forming the underlayer 20, as shown in
The photoresist layer 15 and resist underlayer 20 are subsequently selectively exposed to actinic radiation 45/97 to form exposed regions 50 and 20b and unexposed regions 52 and 20a, in the photoresist layer and underlayer, respectively, as shown in
As shown in
Then as shown in
In some embodiments, an intermediate layer is provided between the substrate 10 or target layer 60 and the resist underlayer 20 (or BARC layer). The intermediate layer may have a composition that provides anti-reflective properties for the photolithography operation and/or hard mask properties. In some embodiments, the intermediate layer includes a silicon-containing layer (e.g., a silicon hard mask material). The intermediate layer may include a silicon-containing inorganic polymer. In other embodiments, the intermediate layer includes a siloxane polymer. In other embodiments, the intermediate layer includes silicon oxide (e.g., spin-on glass (SOG)), silicon nitride, silicon oxynitride, polycrystalline silicon, a metal-containing organic polymer material that contains metal such as titanium, titanium nitride, aluminum, and/or tantalum; and/or other suitable materials. The intermediate layer may be bonded to adjacent layers, such as by covalent bonding, hydrogen bonding, or hydrophilic-to-hydrophilic forces.
In some embodiments, the photoresist layer 15 includes a chromophore, counter ions, and a quencher.
In some embodiments, the photoresist patterning operation includes a second exposure to actinic radiation after the developing operation to harden the resist after development or improve photoresist pattern contrast. In some embodiments, the second exposure is performed at a different wavelength than the first exposure. In some embodiments, the second exposure is at a wavelength less than 250 nm, and is performed by at least one of a KrF laser, an ArF laser, EUV, or electron beam.
Other embodiments include other operations before, during, or after the operations described above. In some embodiments, the disclosed methods include forming semiconductor devices, including fin field effect transistor (FinFET) structures. In some embodiments, a plurality of active fins are formed on the semiconductor substrate. Such embodiments, further include etching the substrate through the openings of a patterned hard mask to form trenches in the substrate; filling the trenches with a dielectric material; performing a chemical mechanical polishing (CMP) process to form shallow trench isolation (STI) features; and epitaxy growing or recessing the STI features to form fin-like active regions. In some embodiments, one or more gate electrodes are formed on the substrate. Some embodiments include forming gate spacers, doped source/drain regions, contacts for gate/source/drain features, etc. In other embodiments, a target pattern is formed as metal lines in a multilayer interconnection structure. For example, the metal lines may be formed in an inter-layer dielectric (ILD) layer of the substrate, which has been etched to form a plurality of trenches. The trenches may be filled with a conductive material, such as a metal; and the conductive material may be polished using a process such as chemical mechanical planarization (CMP) to expose the patterned ILD layer, thereby forming the metal lines in the ILD layer. The above are non-limiting examples of devices/structures that can be made and/or improved using the method described herein.
In some embodiments, active components such diodes, field-effect transistors (FETs), metal-oxide semiconductor field effect transistors (MOSFET), complementary metal-oxide semiconductor (CMOS) transistors, bipolar transistors, high voltage transistors, high frequency transistors, FinFETs, other three-dimensional (3D) FETs, other memory cells, and combinations thereof are formed, according to embodiments of the disclosure.
Resist underlayers of the present disclosure undergo a dehydration reaction upon exposure to actinic radiation and post-exposure baking. As a result, the molecular weight of the polymer in the underlayer composition decreases. The solubility of the polymer in alcohol decreases in alcohol-based solvent decreases after exposure and post-exposure baking. The water content of underlayer composition increases in some embodiments, as indicated by dry CoCl2 paper and dry CuSO4 paper analyses. In addition, in embodiments where the target group includes a diol, NMR, IR, and Raman analyses show an intensity decrease of the polymer OH groups and an intensity increase of polymer C═O groups after exposure and post-exposure baking.
Comparing a resist underlayer composition of the present disclosure with target groups having diol groups to a polyhydroxystyrene (PHS) underlayer composition not according to the present disclosure, after exposure to actinic radiation and post-exposure baking, the polyhydroxystyrene-based underlayer has no change polymer mass; pH value; NMR, IR, and Raman spectra of OH and C═O groups; time-of-flight secondary ion mass spectrometry (TOF-SIMS); water contact angle; thickness; and thermogravimetric analysis (TGA) (exposure to actinic radiation only). On the other hand, resist underlayer compositions according to the present disclosure show polymer mass loss (e.g. —water loss); more acidic or basic pH; NMR, IR, and Raman polymer OH group intensity decrease and polymer C═O intensity increase; oxygen % decrease in TOF-SIMS; increase in water contact angle; thickness shrinkage; and TGA weight loss (exposure to actinic radiation only).
In a comparison of a metal photoresist overlying the resist underlayer before and after exposure to actinic radiation and post-exposure baking, photoresists formed over an underlayer formed of a polymer compositions according to an embodiment of the present disclosure having target groups containing a diol group and an underlayer formed of a polyhydroxystyrene not according to an embodiment of the disclosure, the photoresist formed over an underlayer according to the present disclosure have a number of improved properties. For example, photoresists formed over underlayers according to the present disclosure have increased density; increased moisture content; increased metal-oxygen bond ratio; decreased TOF-SIMS carbon ratio; NMR, IR, and Raman metal-OH group and metal-O bond intensity increase. Furthermore, after patterning the photoresist films by development, the photoresist patterns formed over underlayers according to an embodiment of the disclosure have an increased photoresist contrast curve, require a much lower photoresist exposure dose, stronger photoresist mechanical line strength, larger peeling window, and increased throughput compared to patterned photoresist formed over polyhydroxystyrene underlayers not formed according to embodiments of the present disclosure.
Embodiments of the present disclosure allow reduced exposure dose required for the photoresist layer while improving line width roughness, increased peeling window, and reducing scum. For example, a 30 nm thick resist underlayer containing a polymer with diol target groups allows about an 11% reduction in photoresist exposure dose than an underlayer made of a polyhydroxystyrene polymer without the disclosed target groups and chemical reporter molecules. Meanwhile when the photoresist layer is exposed at the 11% reduced exposure dose, the use of the underlayers according to the present disclosure also provide about a 3% improvement in line width roughness, about a 9% improvement in the peeling window, and about a 4% reduction in scum. Thicker resist underlayers provide a greater amount of small molecules to the photoresist layer, however, thinner resist underlayers, such as a 5 nm thick underlayer made of a polymer composition according to the present disclosure having a diol-containing target group provide about a 9% improvement in peeling window compared to a 30 nm thick resist underlayer made from a polyhydroxystyrene not according to embodiments of the disclosure. In addition, the 5 nm thick underlayer also provides about a 1% improvement in line width roughness and scum reduction.
The novel underlayer compositions and semiconductor device manufacturing methods according to the present disclosure provide higher semiconductor device feature resolution and density at higher wafer exposure throughput with reduced defects in a higher efficiency process than conventional exposure techniques. Embodiments of the disclosure provide improved adhesion of the photoresist pattern to the substrate thereby preventing pattern collapse while preventing pattern scum. Embodiments of this disclosure provide improved integrity of the photoresist pattern, decreased line width roughness, decreased line edge roughness, and scum reduction. Embodiments of the disclosure allow reduced exposure doses and provide increased semiconductor device yield.
An embodiment of the disclosure is a method of manufacturing a semiconductor device including forming a photoresist underlayer over a semiconductor substrate. The photoresist underlayer includes a polymer, including a main polymer chain having pendant target groups, and pendant organic groups or pendant photoacid generator groups. The main polymer chain is selected from the group consisting of a polystyrene, a polyhydroxystyrene, a polyacrylate, a polymethylacrylate, a polymethylmethacrylate, a polyacrylic acid, a polyvinyl ester, a polymaleic ester, a poly(methacrylonitrile), and a poly(methacrylamide). The pendant target groups are one or more selected from the group consisting of a substituted or unsubstituted: C2-C30 diol group, C1-C30 aldehyde group, and C3-C30 ketone group. The pendant organic groups are C3-C30 aliphatic or aromatic groups having at least one photosensitive functional group, and the pendant photoacid generator groups are C3-C50 substituted aliphatic or aromatic groups. A photoresist layer is formed over the photoresist underlayer. The photoresist layer is selectively exposed to actinic radiation. The selectively exposed photoresist layer is developed to form a photoresist pattern. In an embodiment, the main polymer chain includes the pendant organic group having at least one photosensitive group, and the photosensitive group is selected from the group consisting of an epoxy group, an azo group, an alkyl halide group, an imine group, an alkene group, an alkyne group, a peroxide group, and combinations thereof. In an embodiment, the main polymer chain includes the pendant photoacid generator group, and the photoacid generator group is selected from the group consisting of onium salts, sulfonium salts, triphenylsulfonium triflate, triphenylsulfonium nonaflate, dimethylsulfonium triflate, iodonium salts, diphenyliodonium nonaflate, norbornene dicarboximidyl nonaflate, halogenated triazines, diazonium salts, aromatic diazonium salts, phosphonium salts, imide sulfonates, oxime sulfonates, diazodisulfones, disulfones, o-nitrobenzylsulfonates, sulfonated esters, halogenated sulfonyloxy dicarboximides, α-cyanooxyamine-sulfonates, ketodiazosulfones, sulfonyldiazoesters, 1,2-di(arylsulfonyl)hydrazines, nitrobenzyl esters, and s-triazines. In an embodiment, the photoresist underlayer further comprises a photobase generator. In an embodiment, the photoresist underlayer further comprises a photoacid generator compound. In an embodiment, the photoresist underlayer further comprises a thermal acid generator. In an embodiment, the pendant target groups are substituted with one or more selected from the group consisting of —F, —Cl, —Br, —I, —NH2, —OH, —SH, —N3, a sulfonyl group, an alkene group, an alkyne group, an imine group, an ether group, an ester group, a peroxide group, an amide group, a sulfone group, a carboxyl group, a carbonyl group, an allene group, an amine group, a phosphine group, a triol group, an aniline group, a pyridine group, a pyrrole group, a cyanide group, a phosphite group, and combinations thereof. In an embodiment, the method includes heating the photoresist underlayer at a temperature ranging from 150° C. to 250° C. before forming the photoresist layer. In an embodiment, the method includes heating the selectively exposed photoresist layer and photoresist underlayer at a temperature ranging from 50° C. to 160° C. before the developing the selectively exposed photoresist layer.
Another embodiment of the disclosure is a method of manufacturing a semiconductor device includes forming a photoresist underlayer over a semiconductor substrate. The photoresist underlayer includes a polymer having pendant target groups. A photoresist layer is formed over the underlayer. The photoresist layer and photoresist underlayer are selectively exposed to actinic radiation. A chemical reporter molecule is generated in the photoresist underlayer in portions of the photoresist underlayer exposed to the actinic radiation. The chemical reporter molecule is one or more selected from the group consisting of an electron, O2, water, H+, OH−, a cation, an anion, and a C1-C10 group substituted with a functional group. The functional group is one or more selected from the group consisting of —F, —Cl, —Br, —I, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, a imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, an alkylcarboxyl group, a cyanide group, a allene group, an alkyl alcohol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, and a pyrrole group. A small molecule is generated by an interaction between the chemical reporter molecule and the target group in the portions of the photoresist underlayer exposed to actinic radiation. The small molecule is one or more selected from the group consisting of an electron, O2, water, H+, OH−, a cation, an anion, and a C1-C10 group substituted with a functional group, wherein the functional group is one or more selected from the group consisting of —F, —Cl, —Br, —I, —NH2, —COOH, —OH, —SH, —N3, —S(═O)—, an alkene group, an alkyne group, a imine group, an ether group, an ester group, an aldehyde group, a ketone group, an amide group, a sulfone group, an alkylcarboxyl group, a cyanide group, an allene group, an alkyl alcohol group, an amine group, a phosphine group, a phosphite group, an aniline group, a pyridine group, and a pyrrole group. The small molecule is diffused from the photoresist underlayer to portions of the photoresist layer exposed to actinic radiation. The selectively exposed photoresist layer is developed to form a patterned photoresist layer. In an embodiment, the method includes heating the photoresist underlayer at a temperature ranging from 150° C. to 250° C. before forming the photoresist layer. In an embodiment, the diffusing the small molecule includes heating the selectively exposed photoresist layer and photoresist underlayer at a temperature ranging from 50° C. to 200° C. before the developing the selectively exposed photoresist layer. In an embodiment, the photoresist layer includes an organometallic material. In an embodiment, the actinic radiation is extreme ultraviolet radiation. In an embodiment, the small molecule and the chemical reporter molecule are different.
Another embodiment of the disclosure is a composition, including a polymer, including a main polymer chain having pendant target groups, and pendant organic groups or pendant photoacid generator groups. The main polymer chain is selected from the group consisting of a polystyrene, a polyhydroxystyrene, a polyacrylate, a polymethylacrylate, a polymethylmethacrylate, a polyacrylic acid, a polyvinyl ester, a polymaleic ester, a poly(methacrylonitrile), and poly(methacrylamide). The pendant target groups are one or more selected from the group consisting of a substituted or unsubstituted: C2-C30 diol group, C1-C30 aldehyde group, and a C3-C30 ketone group, wherein the pendant organic groups are C3-C30 aliphatic or aromatic groups having at least one photosensitive functional group, and wherein the pendant photoacid generator groups are C3-C50 substituted aliphatic or aromatic groups. In an embodiment, the polymer includes the pendant organic groups having at least one photosensitive group, and the photosensitive group is selected from the group consisting of an epoxy group, an azo group, an alkyl halide group, an imine group, an alkene group, an alkyne group, a peroxide group, and combinations thereof. In an embodiment, the polymer includes the pendant photoacid generator groups, and the photoacid generator groups are selected from the group consisting of onium salts, sulfonium salts, triphenylsulfonium triflate, triphenylsulfonium nonaflate, dimethylsulfonium triflate, iodonium salts, diphenyliodonium nonaflate, norbornene dicarboximidyl nonaflate, halogenated triazines, diazonium salts, aromatic diazonium salts, phosphonium salts, imide sulfonates, oxime sulfonates, diazodisulfones, disulfones, o-nitrobenzylsulfonates, sulfonated esters, halogenated sulfonyloxy dicarboximides, α-cyanooxyamine-sulfonates, ketodiazosulfones, sulfonyldiazoesters, 1,2-di(arylsulfonyl)hydrazines, nitrobenzyl esters, and s-triazines. In an embodiment, the composition includes a photobase generator. In an embodiment, the composition includes a photoacid generator compound. In an embodiment, the composition includes a thermal acid generator. In an embodiment, the composition includes a solvent. In an embodiment, the composition includes a surfactant. In an embodiment, the pendant target groups are substituted with one or more selected from the group consisting of —F, —Cl, —Br, —I, —NH2, —OH, —SH, —N3, a sulfonyl group, an alkene group, an alkyne group, an imine group, an ether group, an ester group, a peroxide group, an amide group, a sulfone group, a carboxyl group, a carbonyl group, an allene group, an amine group, a phosphine group, a triol group, an aniline group, a pyridine group, a pyrrole group, a cyanide group, a phosphite group, and combinations thereof. In an embodiment, the polymer includes the pendant organic groups, and the pendant organic groups include an aromatic group selected from the group consisting of a substituted or unsubstituted: phenyl group, naphthalenyl group, phenanthrenyl group, anthracenyl group, and phenalenyl group, and combinations thereof. In an embodiment, the composition includes a crosslinker. In an embodiment, the crosslinker is bound to the polymer.
Another embodiment of the disclosure is a method of manufacturing a semiconductor device, including forming a first layer over a semiconductor substrate. The first layer includes a polymer, including a main polymer chain having pendant target groups, and pendant organic groups or pendant photoacid generator groups. The pendant target groups are one or more selected from the group consisting of a substituted or unsubstituted: C2-C30 diol group, C1-C30 aldehyde group, and C3-C30 ketone group. A resist layer is formed over the first layer. Water is generated in first portions of first layer. The water in the first portions of the first layer is diffused into corresponding first portions of the resist layer. Second portions of the resist layer are removed, wherein the second portions of the resist layer are different from the first portions of the resist layer. First portions of the resist layer remain after the removing the second portions of the resist layer. In an embodiment, the method includes heating the first layer at a temperature ranging from 150° C. to 250° C. before forming the resist layer. In an embodiment, generating water in first portions of first layer includes exposing the first portions of the first layer to extreme ultraviolet radiation. In an embodiment, the diffusing the water includes heating the first layer and the resist layer at a temperature ranging from 50° C. to 200° C. before the removing the second portions of the resist layer. In an embodiment, the method includes heating the resist layer and the first layer at temperature ranging from 40° C. to 150° C. before the generating water in first portions of the first layer. In an embodiment, the resist layer includes an organometallic material. In an embodiment, the method includes removing second portions of the first layer, wherein the second portions of the first layer correspond to the second portions of the resist layer. In an embodiment, the method includes removing portions of the semiconductor substrate corresponding to the second portions of the first layer and the second portions of the resist layer. In an embodiment, a target layer is located between the semiconductor substrate and the first layer, and further comprising removing portions of the target layer corresponding to the second portions of the first layer and the second portions of the resist layer.
The foregoing outlines features of several embodiments or examples so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments or examples introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure.
This application claims priority to U.S. Provisional Patent Application No. 63/028,648, filed May 22, 2020, the entire disclosure of which is incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
6319654 | Kim et al. | Nov 2001 | B1 |
8796666 | Huang et al. | Aug 2014 | B1 |
9093530 | Huang et al. | Jul 2015 | B2 |
9213234 | Chang | Dec 2015 | B2 |
9223220 | Chang | Dec 2015 | B2 |
9256133 | Chang | Feb 2016 | B2 |
9310684 | Meyers et al. | Apr 2016 | B2 |
9536759 | Yang et al. | Jan 2017 | B2 |
9548303 | Lee et al. | Jan 2017 | B2 |
9857684 | Lin et al. | Jan 2018 | B2 |
9859206 | Yu et al. | Jan 2018 | B2 |
9875892 | Chang et al. | Jan 2018 | B2 |
9891522 | Cheng et al. | Feb 2018 | B2 |
20040063030 | Barr et al. | Apr 2004 | A1 |
20080220381 | Hatakeyama | Sep 2008 | A1 |
20090176177 | Han et al. | Jul 2009 | A1 |
20100233635 | Shimizu | Sep 2010 | A1 |
20120088369 | Weidman et al. | Apr 2012 | A1 |
20130177848 | Kanto | Jul 2013 | A1 |
20150309403 | Rahman | Oct 2015 | A1 |
20170205709 | Hatakeyama | Jul 2017 | A1 |
20190310551 | Minegishi et al. | Oct 2019 | A1 |
Number | Date | Country |
---|---|---|
1228098 | Sep 1999 | CN |
1310731 | Aug 2001 | CN |
1514302 | Jul 2004 | CN |
2014-157252 | Aug 2014 | JP |
2000-0073111 | Dec 2000 | KR |
201641608 | Dec 2016 | TW |
201702744 | Jan 2017 | TW |
201825505 | Jul 2018 | TW |
2019217749 | Nov 2019 | WO |
Number | Date | Country | |
---|---|---|---|
20210364922 A1 | Nov 2021 | US |
Number | Date | Country | |
---|---|---|---|
63028648 | May 2020 | US |