Patent Application
20120018187
The present invention relates to conductor grids for electronic housings, and to a method for manufacturing such conductor grids.
In electronic modules, in particular those for controlling or regulating high currents, such as occur for example in mechatronics, it is known to electrically connect individual components of the module with the aid of cut-out conductor grids. The conductor grids in such modules may assume many functions in addition to the internal electrical contacting, and serve e.g. as supports for individual components instead of a printed circuit board or at the same time as a plug-and-socket connector for external electrical contacting. The entire arrangement consisting of conductor grid and the components connected thereto can be cast in a module housing or be encapsulated with plastics material by injection moulding.
For internal electrical contacting, the individual components, such as discrete components, printed circuit boards, integrated circuits, power ICs, hybrid circuits, etc., can be soldered to the conductor grid. Wire bonding, however, represents one particularly efficient contacting technique, in which the electrical connection is manufactured by means of aluminium wires which are [connected] to the conductor grid or the connection of the corresponding component by pressure welding. The bonding wires in this case have a thickness of typically 50-500 μm.
To manufacture the conductor grids, metal sheets made from copper, iron, or a copper or iron alloy are used as starting material. These materials, although distinguished by good electrical conductivity, are not suitable for wire bonding. In order to be able to weld the bonding wire to the conductor grid by heating or by the action of ultrasound, it is necessary to coat the conductor grid with aluminium, silver or gold.
In particular in the field of mechatronics, therefore, metal strips which are plated in the longitudinal direction with one or more narrow strips of “bonding-capable” metal, e.g. aluminium, are used as starting material for conductor grids. In what is called the clad inlay process, a recess is made in the longitudinal direction in a metal strip made of one of the above alloys, into which recess a thin strip of the bonding-capable metal is pressed. Temperature and pressure produce a metallurgical connection between the two metals. The conductor grid is then cut out from the plated metal strip such that the fingers of the conductor grid extend transversely to the plated metal strip and thus each have a point (“bonding island”) with a surface suitable for the wire bonding.
What is disadvantageous about the conventional method is the high cost of the plated starting material.
It is therefore the aim of the present invention to devise an improved manufacturing method for conductor grids.
This is achieved by the features of the independent claims. Preferred embodiments are the subject of the dependent claims.
In such case, it is the particular approach of the present invention to produce the conductor grid from two metal strips welded in the longitudinal direction, with only one of the two metal strips having a bonding-capable surface. The use of the conventional, expensive plated starting material can in this way be considerably reduced.
According to a first aspect of the present invention, a method for manufacturing a conductor grid is devised which is characterised in that the conductor grid is produced from at least one first metal strip and a second metal strip, which are connected by a weld seam, the second metal strip having, at least at points, a surface suitable for wire bonding.
According to a second aspect of the present invention, a conductor grid for electronic housings is devised which is characterised in that it comprises at least one first metal strip and a second metal strip, which are connected by a weld seam, the second metal strip having, at least at points, a surface suitable for wire bonding.
Preferably the first metal strip consists of copper, iron, a copper alloy or an iron alloy. These are the conventional materials for producing conductor grids, which are distinguished by good electrical conductivity.
According to one embodiment of the present invention, the second metal strip likewise consists of copper, iron, a copper alloy or an iron alloy, and is plated, at least at points, with a metal suitable for wire bonding, preferably aluminium. In this embodiment, the second metal strip advantageously takes up less than half the total width of the welded metal strip.
According to a further embodiment of the present invention, the second metal strip consists of a metal suitable for wire bonding, preferably of aluminium or an aluminium alloy. In this case, the second metal strip advantageously takes up more than half the total width of the welded metal strips, preferably ⅔ of the total width.
Preferably, the conductor grid is produced by cutting out the metal strips which are connected by a weld seam, which permits particularly inexpensive production.
Advantageously, the first and the second metal strip are welded with the aid of a laser beam. In this way, the two metal strips can be joined at a high welding speed, with a narrow and slim weld-seam form and low thermal distortion. According to the invention, the weld seam in this case extends along the joint edge of the first and the second metal strip.
The invention will be described below with reference to the appended illustrations, in which:
According to the invention, instead of the plated metal strip shown in
The two metal strips 110 and 130 are connected together mechanically and electrically along the joint edge by a weld seam 150 extending in the longitudinal direction. The welding of the two metal strips can be effected by laser welding or another suitable welding method.
The total width of the welded metal strips may be several cm, typically 100 mm. The width of the strip of plated metal sheet 110 may vary depending on the size of the bonding islands necessary for the wire bonding, but is preferably as narrow as possible, in particular narrower than the single metal strip 130. The bonding zone is typically 4 to 10 mm wide. Inclusive of an allowance for the welding zone and edge regions, the width of the plated metal strip is therefore about 20 mm. For a total width of 100 mm, the saving on material costs is approximately 50%.
The metal strip 130 of the second embodiment, as in the first embodiment, preferably consists of copper or a standard copper alloy. The second strip 110, on the other hand, consists uniformly of a metal suitable for wire bonding, preferably aluminium or an aluminium alloy, in particular AlMg3.
The construction of the starting material for producing conductor grids shown in
In accordance with the second embodiment, it is therefore possible to dispense completely with the use of plated material, which yields further cost savings. The costs of a metal strip of AlMg3 are for example less than 10% of the costs of an aluminium-plated copper sheet strip.
The metal strip 130 of the third embodiment, as in the first and second embodiments, preferably consists of copper or a standard copper alloy. The second strip 110, as in the second embodiment, consists uniformly of a metal suitable for wire bonding, preferably aluminium or an aluminium alloy, in particular AlMg3. In contrast to the second embodiment, the second strip, however, is made as wide as possible. The width of the copper sheet strip is reduced accordingly. Preferably copper is only used where an additional electroplated coating, for example with hard gold, silver or tin, is necessary. With such a coating, a further function zone, for example as a plug contact or welded connection, can be produced on the conductor grid.
The two metal strips 130 and 140, as in the first and second embodiments, are connected mechanically and electrically by a weld seam 150 extending in the longitudinal direction.
According to the third embodiment of the present invention, the metal strip 130 of copper or a copper alloy is replaced as far as possible by aluminium or an aluminium alloy. Due to the different material costs for copper and aluminium, this yields a further reduction in costs.
According to the invention, the plated metal strip conventionally used as starting material for producing conductor grids is replaced by a composite material in which two different metal strips are arranged next to each other and are connected by a weld seam along the joint edge. From a production-related point of view, laser welding is a possible solution for this method step. The present invention is however not limited to one specific welding technique. Rather, the advantages of this invention can also be achieved with a different suitable welding technique.
In summary, it can be established that conductor grids for electronic housings and a manufacturing method for such conductor grids can be provided with the present invention. According to the invention, the conductor grid is produced from two metal strips welded along the joint edge, with only one of the two metal strips needing to have a surface suitable for the wire bonding. The amount of the conventionally used, plated starting material can in this way be considerably reduced.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2009 016 842.7 | Apr 2009 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2010/054091 | 3/29/2010 | WO | 00 | 10/7/2011 |