The invention relates to the general field of magneto resistance (MR) with particular reference to the micro-structure of the free layer.
Magnetic tunneling junction (MTJ) is a key component of both magnetic recording heads and magnetic random access memory (MRAM). A typical MTJ structure for a recording head or for an MRAM application is schematically illustrated in
Buffer layer 11, antiferromagnetic layer (AFM) 12, an outer pinned layer, Ru, (neither shown) inner pinned layer 13 (the reference layer), tunnel barrier layer 14, free layer 15, and capping layer 16. In this structure, free layer 15 serves as the sensing layer which responds to external fields (specifically those stored in the media) while inner pinned layer 13 remains fixed and serves as reference layer. The electrical resistance through barrier (i.e. insulating) layer 14 varies with the relative orientation of the free layer moment relative to the reference layer moment thereby converting magnetic information stored in the media into electrical signals.
For effective operation as part of a magnetic recoding head, the basic requirements for TMR sensors are as following:
1) Low resistance·area product (RA)
2) High magneto resistance (MR) ratio
3) A soft free layer having low magnetostriction
4) Low interlayer coupling through the barrier layer.
5) Strongly pinned reference layer.
MgO-based MTJs are promising candidates for achieving high recording density and/or high frequency application because their TMR ratio is significantly higher than those of AlOx or TiOx based MTJs. S. Yuasa et al [1] and S. S. Parkin et al. [2] demonstrated that MR ratios around 200% can be achieved at room temperature in epitaxial Fe(001)/MgO(001)/Fe(001) and with polycrystalline FeCo/MgO/(Fe70Co30)80B20 MTJs.
Yuasa et al. [3] have also reported that TMR ratios as high as 410% at room temperature can be achieved in fully epitaxial Fe(001)/Co(001)/MgO(001)/Co structures. Meanwhile, D. D. Djayaprawira et al [4] showed that MTJs of CoFeB/MgO(001)/CoFeB structure made by conventional sputtering can also have a very high MR ratio (230%) with the added advantage of greater feasibility and uniformity. For low RA applications, the MR ratio of CoFeB/Mg/MgO/CoFeB MTJs can reach 138% at RA=2.4 ohm·μm2 was achieved by K. Tsunekawa et al [5] by inserting a DC-sputtered metallic Mg layer in between the bottom CoFeB and the rf-sputtered MgO, an idea initially proposed by T. Linn et al. [6] to prevent oxidation of the bottom electrode (CoFe) in a CoFe/MgO/reactive sputtering/NiFe structure. Also, Ta getter-presputtering prior to the rf-sputtered MgO layer can achieve 55% TMR with an RA of 0.4 ohm·micron2 as recently reported by Y. Nagamine et al. [7]. An alternative way to form a low RA MgO barrier is to deposit two metallic Mg layers with a natural oxidation process in between as we previously proposed for the benefit of better process control and MRR uniformity.
CoFeB material has been used in MgO based MTJs to achieve a magnetically soft free layer having a high MR ratio. High MR ratio and low RA has been demonstrated in MgO MTJs with CoFeB free layer. It was also demonstrated that insertion of a thin CoFe layer between MgO barrier and CoFeB facilitates getting a high MR ratio even at low annealing temperatures (ca. 300° C.). However, there remains a concern that a CoFeB free layer will have a high positive magnetostriction coefficient (lambda).
There are several possible ways to reduce lambda in a CoFeB based free layer. As shown elsewhere, lambda can be reduced by replacing CoFeB with CoB or by adjusting the CoFeB composition. However, magnetic softness deteriorated at the high annealing temperature needed to achieve a high MR ratio. To tackle this issue, a special annealing procedure was developed whereby a relatively high dR/R could be achieved while the free layer was still soft. An alternative approach for reducing lambda is to add a NiFe layer, which has negative lambda and is magnetically soft, on top of the CoFeB in the free layer. However, CoFeB/NiFe-type free layer structure is not usable because direct contact between CoFeB and NiFe causes a drastic drop in MR ratio.
H. Wang et al have proposed to use CoFe/CoFeB/Ta/NiFe as a free layer with high dR/R. In this structure, high dR/R can be achieved because the CoFeB is separated from the NiFe by a Ta insertion layer. The CoFe\CoFeB and NiFe layers are magnetically coupled through orange-peel type coupling, which tend to align magnetic moments to be parallel. However, this coupling is relatively weak and, in the case of real devices, has to compete with magnetostatic coupling from the edge of two layers which tend to align these two layers anti-parallel. As a result, magnetic noise for this kind of structure is relatively high. So although signal amplitude is high, improvement in signal-to-noise ratio is limited.
Magnetoresistive Sensor With Natural-Oxidized Double MgO Barrier”
In U.S. Patent Application 2008/0117553, Carey et al. disclose a free layer comprising CoFe/spacer/NiFe/spacer/CoFe where the spacer is Cu, Au, or Ag and where a third element can be alloyed with the CoFe or NiFe. Additional discussion of this reference appears later in connection with TABLE I.
In U.S. Pat. No. 7,130,166, Gill shows a three-layer free layer where the first and third layers are CoFe/NiFe and the second layer is NiFe, but any of these layers can be NiFe, CoFe, or an CoFe/NiFe stack. The layers are separated by Ru. U.S. Pat. No. 7,141,314 (Zhang et al—Headway) teaches free layer laminates of CoFe and FeCo with spacer layers of Cu. In U.S. Pat. No. 7,149,105, Brown et al. disclose a free layer comprising NiFe and CoFeB separated by a nonmagnetic spacer such as Ru, having a thickness of 2-30 Angstroms.
U.S. Patent Application 2007/0097561 (Miyauchi et al.) shows a free layer comprising alloys of Co, Fe, Ni having a nonmagnetic layer in between while in U.S. Patent Application 2006/0291108, Sbiaa et al. describe a free layer containing a nonmagnetic spacer such as Ru, Rh, Ag, Cu.
It has been an object of at least one embodiment of the present invention to provide a magneto-resistive device having a large output signal as well as a high signal-to-noise ratio.
Another object of at least one embodiment of the present invention has been that said device be any of CIP-GMR, CPP-GMR, MTJ, and TMR devices.
Still another object of at least one embodiment of the present invention has been to provide a process for forming said magneto-resistive device.
A further object of at least one embodiment of the present invention has been for said process be fully compatible with existing processes for forming magneto-resistive devices.
These objects have been achieved by expanding the free layer into a multilayer laminate comprising at least three ferromagnetic layers separated from one another by antiparallel coupling layers, whereby the central ferromagnetic layer has a magnetization direction that is antiparallel to that of the two outer layers.
Additionally, the first of these three ferromagnetic layers, the one closest to the transition layer, must include (or consist entirely of) CoFeB while the third layer is required to have low Hc as well as a low and negative lambda value. One possibility for the central ferromagnetic layer is NiFe but this is not mandatory.
Processes for forming both the expanded free layer as well as the full device are also described.
The present invention discloses a free layer structure comprising at least three magnetic layers whose magnetic moments are antiparallel coupled through Ru layers. This is illustrated in
Mag1 can be made of single layer or combination of: CoxFe1−x(x=0˜100%), (CoxFe1−x)1−yBy (x=0˜100%, y=10˜40%) or their alloys with third or forth elements, such as Ni, Ta, Mn, Ti, W, Zr, Hf, Tb. For example, CoFeB, CoFe\CoFeB or CoFe\CoFeB\CoFe. The thickness for each layer may be 1˜40 Å. Materials or structures that give higher dR/R are preferred.
Mag2 can be a single layer or a combination of: NixFe1−x (x=0˜100) CoxFe1−x(x=0˜100%) and their alloys with third or fourth elements, such as Ni, Ta, Mn, Ti, W, Zr, Hf, Tb or B. For example, CoFe, NiFe or CoFe\NiFe\CoFe. The thickness for each layer may be 1˜30 A. Materials or structures with low or negative lambda that promote strong coupling through spacers are preferred.
Mag3 can be a single layer or combination of: NixFe1−x (x=0˜100) CoxFe1−x(x=0˜100%), their alloys with third or fourth elements, such as Ni, Ta, Mn, Ti, W, Zr, Hf, Tb or B. For example, NiFe, CoFe\NiFe or CoFe\NiFe\CoFe. The thickness for each layer may be 1˜80 Å. Materials or structures with negative lambda and low Hc are preferred.
The TMR barrier can be MgO, MgZnO, ZnO, Al2O3, TiOx, AlTiO, HfOx, ZrOx or any combination of these.
As illustrated in
The characteristics required for the five main layers are summarized in TABLE I below. For comparison purposes we have also included the main features of the structures disclosed in U.S. 2008/011753, mentioned earlier in connection with our prior art search:
In TABLE II below, we show data for a number of different TMR stacks having different free layer structures. Samples A and B, with free layers of CoFe3\CoFeB\Ru and CoFe3\CoFeB\CoFe\Ru respectively, have high MR ratios (up to 67% at RA 1.5) but cannot be used because of their very high positive lambda values (˜1.4E-5).
Inserting Ru\NiFex\Ru\NiFey on top allows us to significantly reduce magnetostriction while still maintaining a high MR ratio and good magnetic softness (see samples C, D, E, and F). The amount of magnetostriction and the magnetic moment can be readily tuned by adjusting the thickness of the two NiFe layers. Sample F has near zero magnetostriction, a Bs slightly higher than the reference (sample B), and an Hc of only 5.6 Oe.
In samples D and F, a thin CoFe layer has been inserted for the purpose of enhancing the coupling strength between CoFeB and NiFe layers. For example, the coupling field for CoFe3\CoFeB20\Ru8\NiFe35 is 800 Oe and which increases to 1700 Oe for CoFe3\CoFeB20\CoFe3\Ru8\NiFe35. Coupling strength could be even further improved by inserting another thin CoFe layer under the NiFe or by replacing NiFe with CoFe,
Sample G is an example of a synthetic free layer with thicker top NiFe layer and a thinner middle NiFe layer, demonstrating that Bs can be adjusted independently of total thickness and lambda.
MgO MTJ with CoFe\CoFeB and CoFe\CoFeB free layers.
The structure of the full TMR stack was Ta\Ru\IrMn\CoFe\Ru\CoFe\MgO\FL\capping. The films were annealed at 280° C. for 5 hours in a magnetic field of 8K Oe.
Note that the free layer of the present invention may also be used in other similar MR structures (such as CIP-GMR, CPP-GMR and TMR), particularly those that need high lambda material to boost dR/R, while still retaining low free layer softness.
This is a Divisional application of US patent application serial number U.S. Ser. No. 12/313,351, filed on Nov. 19, 2008, which is herein incorporated by reference in its entirety, and assigned to a common assignee.
Number | Date | Country | |
---|---|---|---|
Parent | 12313351 | Nov 2008 | US |
Child | 14166373 | US |