This application claims priority from Korean Patent Application No. 2004-37965, filed on May 27, 2004, the disclosure of which is incorporated herein in its entirety by reference.
1. Field of the Invention
The invention relates to a semiconductor memory device and methods of fabricating the same, and more particularly, to a phase-change memory device and methods of fabricating the same.
2. Description of Related Art
The use of phase-changeable materials for electronic memory applications is known in the art and is disclosed, for example, in U.S. Pat. No. 6,147,395 and U.S. Pat. No. 6,337,266. The two states of a memory, in the case of phase-changeable memory, depend on the resistance to current flow in a memory cell. The phase-changeable material typically has an amorphous phase and a crystalline phase, with inherent high and low electrical resistance, respectively. The amorphous phase exists at relatively high temperatures, and the crystalline phase exists at relatively low temperatures. Phase-changeable memory operates on the basic idea that memory cell states, i.e., “on” or “off”, are dependent on temperature. Thus, means for setting the temperature high or low is incorporated in each memory cell.
A general structure for this type of memory includes a phase-changeable material sandwiched between a lower electrode and an upper electrode. The lower electrode typically plays two roles, one being the conduction electrode to the memory cell, and the other being an ohmic heater to control the phase of the phase-changeable material. As just described, the structure comprises interfaces between the top electrode and the phase-changeable material, and between the bottom electrode and the phase-changeable material. During a fabrication of the memory device, and during its operational life in use, these interfaces may become contaminated or oxidized. Such oxidation causes a large variation in the distribution of contact resistances at these interfaces. Since the operation of phase-changeable memory depends on distinguishing between the memory cell being “on” or “off” based on the cell's resistance to current flow, contamination or oxidation jeopardizes the accuracy of memory programming. A need still remains for a novel phase-change memory structure that can prevent such contamination or oxidation and the manufacturing method thereof.
A phase-change memory device has an oxidation barrier layer to protect against memory cell contamination or oxidation and a method of manufacturing the same. In one embodiment, a semiconductor memory device comprises a molding layer overlying a semiconductor substrate. The molding layer has a protrusion portion vertically extending from a top surface thereof. The device further includes a phase-changeable material pattern adjacent the protrusion portion and a lower electrode electrically connected to the phase-changeable material pattern. According to one aspect of the present invention, an oxidation barrier layer may cover an area where a sidewall of the phase-changeable material pattern and a sidewall of the protrusion portion adjoin. More stable operation and a longer operational lifetime of the phase-change memory device are some of the benefits of the present invention.
a is a schematic view of an embodiment that features a phase-change memory cell array (CA) and a peripheral circuit area (PCA) of the present invention.
b is a plan view of a portion of a phase-change memory cell array area and peripheral circuit area according to an embodiment of the present invention.
a is a schematic view of an embodiment that features a phase-change memory cell array CA and a peripheral circuit area PCA of the present invention. The cell array area CA comprises an array of memory cells CL each of which in turn comprises an access transistor TA and a phase-change resistor RP. Each memory cell CL is connected to a bit line BL, a word line WL, and a common source line CSL in a configuration that is known in the art. Other conventional structures will be included in the present invention. For example, the peripheral circuit area PCA includes first and second integrated circuits PCA1, PCA2 to drive the memory cells CL. The state of a memory cell CL is determined by a current sensing of a writing current IW. The current sensing and other functions of memory control are known to one skilled in the art.
b is a plan view of a portion of the phase-change memory cell array area CA and a portion of the peripheral circuit area PCA according to an embodiment of the invention.
Referring to
Referring to
Also, a gate spacer 11 of a conventional spacer material such as oxide or nitride is preferably formed along opposite sides of the cell gate electrode 7c and also along opposite sides of the peripheral gate electrode 7p, using conventional techniques.
Next, using the gate spacer 11, an n-type first source region 13s′ and an n-type first drain region 13d′ are formed in the cell active region 3c. In addition, a p-type second source region 13s″, a p-type second drain region 13d″ are subsequently formed in the peripheral circuit active region 3p, using the methods known in the art. As a result, a pair of access (switching) MOS transistor TA are formed in the cell area CA and a peripheral MOS transistor TP is formed in the peripheral circuit area PCA.
A silicide layer 15b may be formed on at least one of the second source and drain regions 13s″ and 13d″ and the peripheral gate electrode 7p. A silicide layer 15a may be formed on at least one of the first source and drain regions 13s′ and 13d′ and the cell gate electrode 7c. Then, a lower etch stopper 17 is formed over the resulting structure.
Referring to
Subsequently, the first source contact hole 19s′, the first drain contact hole 19d′ are formed in the lower inter-level insulating layer 20 in the cell area CA. Then, a first source contact plug 21s′ and a first drain contact plug 21d′ are respectively formed in the first source contact hole 19s′, the first drain contact hole 19d′, using the methods known in the art. Also, the second source contact hole 19s″, the second drain contact hole 19d″, a second source contact plug 21s″, and a second drain contact plug 21d″ are formed in the peripheral circuit area PCA in the lower inter-level insulating layer 20, using the conventional techniques.
Then, an upper inter-level insulating layer 26 is formed, comprising an upper etch stopper 23 and an upper insulating layer 25. An element 28 denotes an interlayer insulating layer comprised of the layers 17, 19, 23, and 25 described above.
Referring to
Afterwards, a molding layer 29 is formed on the resulting structure. A phase-change resistor contact hole 29a is then formed in the molding layer 29, using photolithography and etching processes. The molding layer 29 is preferably formed of a material having a high thermal conductivity. For example, the molding layer 29 has a thermal conductivity higher than that of silicon oxide. This gives a high rapid quenching efficiency of a phase transition of a phase-changeable material pattern, in addition to an oxygen barrier characteristic to prevent the phase-changeable material pattern from being oxidized. Such materials include silicon nitride and silicon oxynitride, for example.
Turning to
Referring to
Then, a lower electrode 35 is formed in the phase-change resistor contact hole 29a within the contact spacer 34a. The lower electrode 35 is electrically connected to the first drain pad 27′, which is in turn electrically connected to the first drain region 13d′ of the switching transistor TA through first contact plug 21d′. In detail, the lower electrode 35 in the phase-change resistor contact hole 29a may be formed by depositing a conductive film such as a TiN film, or a TiAlN film overlying the molding layer 29 and within the contact hole 29a and by planarizing the conductive film until the molding layer 29 is exposed. As a result, the contact spacer 34a surrounds the sidewall of the lower electrode 35.
Subsequently, a phase-changeable material layer 37, an upper electrode layer 39, a glue layer 41, and a hard mask layer 43 are sequentially formed on the resulting structure including the molding layer 29. The hard mask layer 43 may be formed of SiO2. The glue layer 41 may be a wetting layer such as SiN. One skilled in the art will, however, understand that the above-described structure is only a preferred embodiment and other suitable structures can also be used within the spirit and scope of the present invention. For example, the hard mask layer 43 can be formed using a dielectric material other than SiO2.
The phase-changeable material layer 37 may be formed of a chalcogenide material, including, but not limited to, a GeSbTe alloy, or a Si or N doped GeSbTe alloy, with a thickness of, for example, about 1000 Å.
In
Next, an oxidation barrier layer 48 may cover the resulting structure including the phase-change resistor 44a. The oxidation barrier layer 48 may comprise a single layer of nitride, for example, silicon nitride or silicon oxynitride, deposited using a PE-CVD process, or an atomic layer deposition (ALD) process at less than or equal to about 350° C. Alternatively, the oxidation barrier layer 48 may be formed of double layers, comprising a lower oxidation barrier layer 45 of nitride, such as silicon nitride or silicon oxynitride, deposited using a PE-CVD process or an ALD process at less than or equal to about 350° C.; and an upper oxidation barrier layer 47 of nitride, such as silicon nitride or silicon oxynitride, deposited using PE-CVD process or an LP CVD process at higher than or equal to about 350° C.
The oxidation barrier layer 48 prevents the phase-changeable material pattern 37a from being oxidized or contaminated by oxygen or impurities that may penetrate into an interface between the lower electrode 35 and the phase-changeable material pattern 37a, or another interface between the upper electrode 39a and the phase-changeable material pattern 37a during a process such as an oxide deposition (ILD deposition) to cover the phase-change resistor 44a.
Because the oxidation barrier layer 48 covers the sidewalls of the protrusion portion 77 of the molding layer 29, as well as the sidewalls and/or the upper surface of the phase-change resistor 44a, penetration of oxygen into the phase-change resistor 44a can be efficiently blocked.
Additionally, a plasma nitridation process may be performed on the surface of the phase-change resistor 44a, using an N2 or NH3 gas at less than or equal to about 350° C. before forming the oxidation barrier layer 48.
Next, a passivation layer 62 including a silicon oxide layer 59 and a silicon nitride layer 61 is formed on the resulting structure to complete a phase-change memory device having the oxidation barrier layer 48.
Consequently, the resulting memory device includes a molding layer 29 overlying a semiconductor substrate 1. The molding layer 29 has a protrusion portion 77 vertically extending from a top surface 67 of the molding layer 29. The protrusion portion 77 may have a thickness of at least 100 angstroms, preferably, in a range of about 300 to about 600 angstroms.
The memory device further includes a phase-changeable material pattern 37a adjacent to the protrusion portion 77 and a lower electrode 35 electrically connected to the phase-changeable material pattern 37a. The lower electrode 35 may extend through the protrusion portion 77, preferably along a center portion thereof. The protrusion portion 77 may be located above the first drain pad, i.e., conductive pad 27d′. Further, the phase-changeable material pattern 37a may overlie the protrusion portion 77, although other configurations are also possible as long as the phase-changeable material pattern 37a is adjacent the protrusion portion 77 within the spirit and scope of the present invention. Also, a sidewall of the phase-changeable material pattern 37a may be self-aligned with a sidewall of the protrusion portion 77. The phase-changeable material pattern 37a preferably comprises a chalcogenide material such as a GST (GeSbTe) alloy. According to an aspect of the present invention, the GST alloy may be doped by at least one of silicon and nitrogen.
The device may further include an upper electrode 39a electrically connected to the phase-changeable material pattern 37a.
Also, the device may include an oxidation barrier layer 48 covering at least a portion of a sidewall of the phase-changeable material pattern 37a and at least a portion of a sidewall of the protrusion portion 77. In one aspect, the oxidation barrier layer 48 may cover the phase-changeable material pattern 37a and the upper electrode 39a. More particularly, the oxidation barrier layer 48 preferably covers an area where a sidewall of the phase-changeable material pattern 37a and a sidewall of the protrusion portion 77 adjoin such that penetration of oxygen into the phase-change resistor 44a can be efficiently blocked. Consequently, with the embodiments of the present invention, a more reliable phase-change memory device can be formed in the present invention.
In another aspect of the present invention, the oxidation barrier layer 48 may comprise a first portion overlying a top of the upper electrode 39a and a second portion covering a sidewall of the phase-change layer pattern 37a. Although not illustrated in the drawing, the first portion has a thickness greater than the thickness of the second portion. Preferably, the thickness of the second portion is greater than or equal to about 300 angstroms.
Sample A does not include an oxidation barrier layer, in contrast with the embodiments of the present invention. In
Specifically, sample B comprises a SiON layer, sample C comprises an SiN layer, and sample D comprises a lower and an upper oxidation barrier layer, each of SiN. For sample B, the SiON layer is formed using a PECVD process at 200° C., to a thickness of 200 Å. For sample C, the SiN layer is formed the same way as for sample B. For sample D, both SiN layers are formed as for samples B and C, except the upper layer is processed at 400° C.
Up to about 5,000 programming cycles, a conventional phase-change memory device has a very low reset resistance value of 6,000-100,000 Ω, as compared with a set resistance value. Thus it is difficult to get enough sensing margin to read the memory cell information accurately.
Comparing
Although the invention has been described with reference to the preferred embodiments thereof, it will be understood that the invention is not limited to the details thereof. Various substitutions and modifications have been suggested in the foregoing description, and other will occur to those of ordinary skill in the art. Therefore, all such substitutions and modifications are intended to be embraced within the scope of the invention as defined in the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2004-0037965 | May 2004 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4115872 | Bluhm | Sep 1978 | A |
| 4366614 | Kumurdjian | Jan 1983 | A |
| 4499557 | Holmberg et al. | Feb 1985 | A |
| 4599705 | Holmberg et al. | Jul 1986 | A |
| 5177567 | Klersy et al. | Jan 1993 | A |
| 5952671 | Reinberg et al. | Sep 1999 | A |
| 6031287 | Harshfield | Feb 2000 | A |
| 6147395 | Gilgen | Nov 2000 | A |
| 6189582 | Reinberg et al. | Feb 2001 | B1 |
| 6337266 | Zahorik | Jan 2002 | B1 |
| 6531391 | Zahorik | Mar 2003 | B2 |
| 6635951 | Zahorik | Oct 2003 | B1 |
| 6642102 | Xu | Nov 2003 | B2 |
| 6744088 | Dennison | Jun 2004 | B1 |
| 6806528 | Lee et al. | Oct 2004 | B2 |
| 6858482 | Gilton | Feb 2005 | B2 |
| 7037749 | Horii et al. | May 2006 | B2 |
| 7042001 | Kim et al. | May 2006 | B2 |
| 7105396 | Hwang et al. | Sep 2006 | B2 |
| 20030209746 | Horii | Nov 2003 | A1 |
| 20030219924 | Bez et al. | Nov 2003 | A1 |
| 20030231530 | Bez et al. | Dec 2003 | A1 |
| 20040087074 | Hwang et al. | May 2004 | A1 |
| 20050263829 | Song et al. | Dec 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 1506973 | Jun 2004 | CN |
| 2822264 | Dec 1978 | DE |
| 3046721 | Oct 1981 | DE |
| 10351017 | May 2004 | DE |
| 2003-298013 | Oct 2003 | JP |
| 2003-0081900 | Oct 2003 | KR |
| Number | Date | Country | |
|---|---|---|---|
| 20050263823 A1 | Dec 2005 | US |