1. Technical Field
The present invention relates to a printed circuit board.
2. Description of the Related Art
A semiconductor package board allows the mounting of electronic components on the surface, and in certain cases, such as for a BGA (ball grid array) board, provides electrical connection to other package boards. Here, to provide electrical connection to components or to other package boards, wire bonding pads or solder ball pads, etc., may be used.
As illustrated in
An OSP pad 134, e.g. a solder ball pad, may be electrically connected with a gold plating pad, e.g. a wire bonding pad. However, due to the difference in ionization tendency between copper and gold, in the OSP pad 134 and gold plating pad 132, galvanic corrosion may occur in an acidic compound. This may result in an excessive etching of the OSP pad 134, whereby the thickness or width of the OSP pad 134 may be significantly decreased.
This problem can be exacerbated as the difference in area between the OSP pad 134 and the gold plating pad 132 is increased. Forming the OSP pad 134 in larger sizes to resolve this problem may pose difficulties in increasing the density of the wiring.
One aspect of the invention provides a printed circuit board, in which excessive etching caused by galvanic corrosion between metal pads of different ionization tendencies can be prevented, when applying an OSP (organic solderability preservative) pretreatment.
Another aspect of the invention provides a printed circuit board that includes an insulation layer, a first metal pad formed on the insulation layer, a second metal pad electrically coupled with the first metal pad and having an ionization tendency lower than that of the first metal pad, and a sacrificial electrode electrically coupled with the second metal pad to prevent corrosion in the first metal pad.
Here, the insulation layer can be partitioned into a unit zone, in which multiple unit boards may be formed, and a dummy zone. The sacrificial electrode can be formed in the dummy zone, or on a unit board. Also, the sacrificial electrode may contain the same metal as that of the first metal pad.
The first metal pad contains copper (Cu), while the second metal pad may contain gold (Au). Additional aspects and advantages of the present invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention.
Before describing particular embodiments of the invention, a description will be provided on OSP (organic solderability preservative) treatment as follows. For example, in the case of a solder ball pad, OSP treatment may be applied in order to prevent oxidation in the copper and to improve adhesion to solder balls. OSP treatment is a method of forming a protective film by displacing the copper in a pad or a hole with an organic compound, such as imidazole, benzotriazole, benzimidazole, etc. An example of a well known type of OSP treatment is the water-soluble pre-flux method.
When applying an OSP treatment, a pad containing copper and a pad containing gold may be exposed to an acidic compound, at which galvanic corrosion may occur.
Galvanic corrosion is caused by a difference in electrode potentials, when two dissimilar metals are placed in an electrolyte solution, which causes electrons to move from one metal to the other. Because of this, the corrosion of the metal having the lower ionization tendency is retarded, while the corrosion of the metal having higher ionization tendency is accelerated. This type of corrosion is referred to as galvanic corrosion or dissimilar metal corrosion.
An important factor affecting galvanic corrosion is the proportion of the area of the anode to the area of the cathode. The more risky situation may involve a set of small anode and large cathode. The higher the current density in an anode, the greater is the rate of corrosion. Conversely, a set of large anode and small cathode may be more favorable in preventing galvanic corrosion. For example, consider the cases of a steel nail hammered into a copper plate and a copper nail hammered into a steel plate. The former case is an example of a set of small anode and large cathode, while the latter case is an example of a set of large anode and small cathode. Therefore, compared to the latter case, the galvanic corrosion in the former case will be much more serious, and the steel nail will be subject to a considerable amount of damage.
As described above, a printed circuit board according to a first disclosed embodiment of the invention may include an insulation layer, a first metal pad formed on the insulation layer, a second metal pad electrically coupled with the first metal pad and having an ionization tendency lower than that of the first metal pad, and a sacrificial electrode electrically coupled with the second metal pad to prevent corrosion in the first metal pad, whereby excessive etching, which may occur due to galvanic corrosion caused by metal pads having different ionization tendencies contacting an etching compound, can be avoided.
A printed circuit board according to a certain embodiments of the invention will now be described in more detail, with reference to the accompanying drawings. Those components that are the same or are in correspondence are rendered the same reference numeral regardless of the figure number, and redundant explanations are omitted.
A printed circuit board is an arrangement that includes an insulation layer 102 and a conductive layer formed in a particular pattern over the insulation layer 102. The printed circuit board may refer to a board strip 100, which is an intermediary product in the manufacturing process, or may refer to a unit board 130, which is a partitioned portion of a board strip 100 that is to be ultimately cut as a final product. It is to be appreciated that the board strip 100 and the unit board 130 are both labels signifying the form of the product with respect to the manufacturing process, and that both of these may be referred to as a printed circuit board. Moreover, it is apparent that the portion ultimately cut along the product zone 140 is also referred to as a printed circuit board.
When the printed circuit board is in the form of a board strip 100, the insulation layer 102 may be partitioned into a unit zone 120, in which multiple unit boards 130 may be formed, and a dummy zone 110, which is a zone outside the unit zone 120. The dummy zone 110 may include guide holes for aligning the board strip 100 or mold gates 112, etc.
The first disclosed embodiment of the invention will be described for an example case as applied to a unit board 130, which is a form of printed circuit board.
As illustrated in
The gold plating pads 132 can be electrically coupled with the OSP pads 134 by the circuit pattern. The OSP pads 134 can be formed on a portion of the circuit pattern, and can include, for example, copper (Cu). Gold (Au) is a metal having a lower ionization tendency than that of copper. Thus, because copper and gold, which have different ionization tendencies, may be electrically coupled, galvanic corrosion may occur in the OSP pads 134 when the two types of metallic pads are exposed to an acidic compound during the OSP pretreatment.
Therefore, in order to prevent galvanic corrosion in the OSP pads 134, sacrificial electrodes 300 may be coupled electrically to the gold plating pads 132. The sacrificial electrodes 300 may include, for example, copper. By coupling the sacrificial electrodes 300 made of the same metal as that used in the OSP pads 134 to the gold plating pads 132, the proportion of the area of the anode between the metals of the OSP pads 134 and gold plating pads 132 can be increased. The sacrificial electrodes 300 can be formed together with the circuit pattern during the operation of forming the circuit pattern.
While this particular embodiment employs a method of using sacrificial electrodes 300 having the same metal (e.g. copper) as that of the OSP pads 134 to increase the proportion of the anode area between the metals used and thereby prevent galvanic corrosion in the OSP pads 134, it is also possible to reduce the occurrence of galvanic corrosion by forming the sacrificial electrodes 300 from a metal having a higher ionization tendency than that of the metal forming the OSP pads 134.
As illustrated in
As a result, by forming the sacrificial electrode 300, not in the unit board 130 which is yielded as the final product, but in the dummy zone 110, problems caused by galvanic corrosion can be resolved, while providing a high wiring density.
The mold gate may be formed on one side of the board strip 100, and gold plating may be performed over the mold gate, in order to facilitate the inflow of epoxy molding resin as well as its subsequent separation. However, with recent improvements in epoxy molding resin, the gold plating for the mold gate can be omitted. As such, the surface of the mold gate may include copper, which can be used as the sacrificial electrode 300, instead of forming a separate sacrificial electrode 300.
In this particular embodiment also, the mold gate containing copper may serve as the sacrificial electrode 300, to increase the proportion of the anode area with respect to the gold plating pads 132 and reduce galvanic corrosion that may occur during the OSP pretreatment. Also, by forming the sacrificial electrode 300 in the dummy zone 110, galvanic corrosion may be prevented without having to form the OSP pads 134 in excessively large sizes, so that the wiring densities of the unit boards 130 may be improved.
As set forth above, certain embodiments of the invention can be utilized to prevent excessive etching that may otherwise occur due to galvanic corrosion between metal pads of different ionization tendencies.
While the spirit of the invention has been described in detail with reference to particular embodiments, the embodiments are for illustrative purposes only and do not limit the invention. It is to be appreciated that those skilled in the art can change or modify the embodiments without departing from the scope and spirit of the invention.