The present application relates generally to the fields of chemistry, optoelectronics, silicon-germanium alloys, semiconductor structures, and related methods and devices.
Heteroepitaxial Ge1-xSix layers on Si(100) with high Ge contents are of interest due to many applications in key technologies such as solar cells, MEMS, quantum cascade lasers and Si-based photonics1,2 including high speed modulators and photodetectors.3 However, these materials are much less developed in spite of this high impact potential in IR optical devices. In addition, they serve as virtual substrates for growth of high mobility, strained Si and Ge device channels, and are also considered as a potential pathway to monolithic integration of III-V based devices with Si technologies.4,5 The best current route to these materials is complicated and fraught with difficulties, requiring both high temperature growth of thick (>10 μm) compositionally graded films and a chemical-mechanical planarization step to relieve the misfit strain between the Ge1-xSix epilayer and Si substrate and produce a flat surface, respectively.6
To circumvent these difficulties we have recently developed new chemical vapor deposition (CVD) heteroepitaxy to produce device quality strain-relieved Ge-rich films on Si without the need for graded compositions.7,8 Our strategy involves depositions of single source hydride precursors with direct Si—Ge bonds such as the (H3Ge)xSiH4-x (x=1-4) family of compounds. These are routinely synthesized with semiconductor grade purity via straightforward methodologies utilizing commercially available starting materials.7 Their physical and chemical properties such as high volatility and facile reactivity make them particularly useful as reagents in low temperature film growth by CVD and gas source molecular beam epitaxy (GSMBE). Our initial growth experiments have yielded single crystal films with compositions Si0.50Ge0.50, Si0.33Ge0.67, Si0.25Ge0.75 and Si0.20Ge0.80, precisely matching those of the corresponding precursors SiH3GeH3, (H3Ge)2SiH2, (H3Ge)3SiH and (H3Ge)4Si.8 Our results demonstrate that exact control of the composition, structure and strain at the atomic level can be achieved via incorporation of the entire Si—Ge framework of the precursors into the film. The resulting films are of much higher quality than those previously reported using conventional sources and grow at much lower temperatures that are compatible with CMOS technology.
Within this compositional range the Si0.50Ge0.50 semiconductor system is of particular importance because it possesses the ideal lattice dimensions to integrate fully strained Si channels exhibiting high electron mobilities into metal oxide silicon field effect transistors (MOSFETS). Thus these materials are ideally suited for immediate technological applications in high-speed devices. However, in our experiments we have observed that stoichiometric Si0.50Ge0.50, with the required device quality properties (surface planarity, low defect densities), can only be grown near a maximum temperature of ˜450° C. at a growth rate of only 0.2 nm/min which is too low to be practical for high throughput device fabrication. Negligible film growth was observed at lower temperatures via H3GeSiH3, while films with rough surfaces and high dislocation densities were obtained above ˜500° C. due to the thermal mismatch with the substrate.
The synthesis of new compounds with increased reactivities and improved properties for device fabrication relative to H3GeSiH3 would be of great value in the art.
In this study we synthesize and fully characterize the butane-like (GeH3)2(SiH2)2 (1) compound containing highly reactive —H2Si—SiH2— functionalities (rather than SiH3). The H2Si═SiH2 dimeric unit has been identified as the dominant reactive intermediate in high temperature CVD via decomposition of conventional Si-hydrides. These species lead to highly efficient growth of homoepitaxial Si.9 Precursor (1) is specifically designed to incorporate these necessary —H2Si—SiH2— building blocks and provide a new low temperature route for development of a broad range of Si-containing materials. Here we demonstrate the utility of (1) to produce device quality Si0.50Ge0.50 alloys at unprecedented low temperatures of 350° C. A 10-fold improvement in the growth rate (˜2.0 nm/min) is achieved at 350° C. relative to growth (0.2 nm/minute) at 450° C. via SiH3GeH3 leading to uniformly stressed or strain-relaxed thin films directly on Si with planar surfaces and remarkably reduced dislocation densities. En route to (1) we have produced the isobutane analog (GeH3)2SiH(SiH3) (2) and have also isolated and fully characterized the Ge-rich derivative (GeH3)2(SiH2GeH2) (3). The latter is a moderately volatile liquid, with potential applications in low temperature synthesis of Ge-rich optoelectronic alloys.
In one aspect, the present invention provides compounds comprising a silicon-germanium hydride of formula I:
(SiHn1)x(GeHn2)y,
wherein x is 2, 3 or 4;
wherein y is 1, 2, or 3;
wherein x+y is 3, 4, or 5;
wherein n1 is independently 0, 1, 2, or 3 for each Si atom in the compound, to satisfy valency; and
wherein n2 is independently 0, 1, 2, or 3 for each Ge atom in the compound, to satisfy valency;
with the proviso that n2 is not 0 when y is 1;
with the further proviso that when x is 3 and y is 1, then n2 is 2 or 3; and
with the further proviso that when x is 2 and y is 1, then n2 is 3.
In a second aspect, the present invention provides semiconductor structures, comprising a substrate and an Si—Ge layer formed by introducing near the surface of a substrate a gaseous precursor comprising one or more compounds according to formula I.
In further aspect, the invention provides semiconductor structures, comprising a substrate and an Si—Ge layer comprising a backbone of one or more compounds according to formula I.
In a third aspect, the present invention provides methods for synthesizing one or more silicon-germanium hydrides of formula I, comprising combining a compound selected from the group consisting of a nonafluorobutane-sulfonic substituted disilane and a triflate substituted disilane, with a compound comprising a GeH3 ligand under conditions whereby the silicon-germanium hydride is formed.
In a fourth aspect, the present invention provides methods for depositing a Si—Ge material on a substrate in a reaction chamber, comprising introducing into the chamber a gaseous precursor comprising one or more compounds according to formula I, under conditions whereby a layer comprising a Si—Ge material is formed on the substrate.
In a fifth aspect, the present invention provides methods for depositing an epitaxial Si—Ge layer on a substrate, comprising introducing at or near a surface of the substrate a gaseous precursor comprising one or more compounds of formula I, and dehydrogenating the precursor under conditions whereby epitaxial Si—Ge is formed on the substrate.
In a sixth aspect, the present invention provides a compound comprising (SO3C4F9)2(SiH2)2.
In a seventh aspect, the present invention provides methods for synthesizing (SO3C4F9)2(SiH2)2 comprising combining (p-tolyl)2(SiH2)2 and HSO3C4F9 under conditions whereby the (SO3C4F9)2(SiH2)2 is formed.
All publications, patents and patent applications cited herein are hereby expressly incorporated by reference for all purposes.
As used herein, the singular forms “a”, “an” and “the” include plural referents unless the context clearly dictates otherwise.
In one aspect, the present invention provides compounds comprising or consisting of a silicon-germanium hydride of formula I:
(SiHn1)x(GeHn2)y,
wherein x is 2, 3 or 4;
wherein y is 1, 2, or 3;
wherein x+y is 3, 4, or 5;
wherein n1 is independently 0, 1, 2, or 3 for each Si atom in the compound, to satisfy valency; and
wherein n2 is independently 0, 1, 2, or 3 for each Ge atom in the compound, to satisfy valency;
with the proviso that n2 is not 0 when y is 1;
with the further proviso that when x is 3 and y is 1, then n2 is 2 or 3; and
with the further proviso that when x is 2 and y is 1, then n2 is 3.
As used herein, the phrase “to satisfy valency” means to maintain tetra-valency of each Si and Ge atom in the compounds of the invention.
As demonstrated herein, compounds according to formula I can be used, for example, in controlled depositions to produce stoichiometric SiGe films possessing desired properties for semiconductor applications including perfectly crystalline and epitaxial microstructures, smooth morphologies, and uniformly strain-relaxed states. The compounds of formula I are herein demonstrated to be remarkably stable over extended periods of time, and thus represent viable molecular sources for potential industrial applications.
Thus, in one embodiment of this first aspect, x is 2; in an alternative embodiment x is 3; in a further alternative embodiment x is 4. In embodiments where x is 2, y can be 1, 2, or 3 preferably 2 or 3, most preferably 2. In embodiments where x is 3, y can be 1 or 2, preferably 2. In embodiments where x is 4, y is 1.
In a further embodiment of this first aspect, x is 2 or 3, with the proviso that if y is 1, then n2 is 0, 1, or 2, and with the further proviso that if x is 2 and y is 2, then at least one of the following is true:
In a still further embodiment, y is 2 or 3 and x+y is 4 or 5, with the proviso that if x is 2 and y is 2, then at least one of the following is true:
Compounds according to formula I include any conformational form of the compound, including but not limited n, g, and iso-forms of the compounds, and combinations thereof.
Exemplary silicon-germanium hydrides according to formula I comprise or consist of those compounds listed in Table 1. All Si and Ge atoms in the compounds are tetravalent. Dashed lines represent bonds between Si and Ge atoms in the linear versions. In the isobutene- and isopentane-like isomers, the Si and Ge atoms inside the brackets are directly bound to the Si or Ge to the left of the brackets; the Si or Ge in parenthesis outside of the brackets at the far right in some of the compounds are directly bound to the last Si or Ge inside of the brackets.
For example,
As noted above, these compounds each include the n or g forms, and stereoisomers thereof.
In a preferred embodiment, the silicon germanium hydride is selected from the group consisting of SiH3—SiH2—GeH2—GeH3; SiH3—GeH2—SiH2—GeH3; SiH3—GeH2—GeH2—SiH3; and GeH3—SiH2—SiH2—GeH3), and SiH[(SiH3)(GeH3)2]
This first aspect also provides compositions comprising combinations of the silicon germanium hydrides. In a preferred embodiment of such combinations, x is 3 and y is 1, or x is 2 and y is 2, for each of the two or more compounds. In a most preferred embodiment, the combination comprises compounds selected from the group consisting of SiH3—SiH2—GeH2—GeH3; SiH3—GeH2—SiH2—GeH3; SiH3—GeH2—GeH2—SiH3; and GeH3—SiH2—SiH2—GeH3), and SiH[(SiH3)(GeH3)2].
In a further embodiment, the compounds of the invention are substantially isolated. As used herein, a “substantially isolated” compound of the invention is one compound, or two or more compounds of the invention in combination, that are at least 75% isolated from precursors and other contaminants, and preferably 80%, 85%, 90%, 95%, 98%, or more isolated.
In a second aspect, the present invention provides semiconductor structures, comprising a substrate; and an Si—Ge layer formed by introducing near the surface of a substrate a gaseous precursor comprising or consisting of one or more silicon-germanium hydride compounds of formula I.
As shown herein, the silicon-germanium hydride compounds of formula I are especially useful for fabricating SiGe semiconductor alloys at unprecedented low temperatures that display homogeneous compositional and strain profiles, low threading dislocation densities and atomically planar surfaces. Controlled depositions have produced stoichiometric SiGe films reflecting the Si/Ge content of the precursor, and possessing the desired properties for semiconductor applications including perfectly crystalline and epitaxial microstructures, smooth morphologies, and uniformly strain-relaxed states.
In this aspect, the substrate can be any substrate suitable for semiconductor or flat panel display use, including but not limited to silicon, germanium, silicon on insulator, Ge:Sn alloys, SiO2, sapphire, quartz, Si:Ge alloys, Si:C alloys, stainless steel, polyimide or other polymer films such as those used in the fabrication of flexible displays. In a preferred embodiment, the substrate comprises Si(100).
In a preferred embodiment, the semiconductor substrates of this aspect of the invention have an SiGe layer which comprises an SiGe film having a thickness of less than one micron, more preferably a thickness in a range from 50 nm to 500 nm. In a further preferred embodiment, the semiconductor substrates of this second aspect have an SiGe layer comprising an SiGe film having a density of threading defects of 106/cm2 or less. In a further preferred embodiment, the semiconductor substrates of this aspect of the invention comprise an SiGe film having a substantially atomically planar surface morphology.
In various embodiments, the gaseous precursor comprises or consists of one or more of the compounds listed in Table 1, each in n or g forms, and stereoisomers thereof.
In a preferred embodiment of the semiconductor substrates of the second aspect, the gaseous precursor comprises or consists of a compound selected from the group consisting of SiH3—SiH2—GeH2—GeH3; SiH3—GeH2—SiH2—GeH3; SiH3—GeH2—GeH2—SiH3; GeH3—SiH2—SiH2—GeH3), and SiH[(SiH3)(GeH3)2].
The semiconductor structure may further comprise other features as desired, including but not limited to the inclusion of dopants, such as boron, phosphorous, arsenic, and antimony. These embodiments are especially preferred for semiconductor substrates used as active devices. Inclusion of such dopants into the semiconductor substrates can be carried out by standard methods in the art.
In a further embodiment, the semiconductor structure may further comprise varying quantities if carbon or tin, as desired for a given application. Inclusion of carbon or tin into the semiconductor substrates can be carried out by standard methods in the art. The carbon can be used to reduce the mobility of the dopants in the structure and more specifically boron. Incorporation of Sn can yield materials with novel optical properties such as direct emission and absorption leading to the formation of Si-based lasers and high sensitivity infrared photodetectors.
In further aspect, the invention provides semiconductor structures, comprising a substrate and an Si—Ge layer comprising or consisting of a backbone of one or more compounds according to the formula I. Preferred embodiments are as described above.
In a further aspect, the invention provides a composition, comprising one or more compounds according to formula I in an inert gas. Such inert gases include, but are not limited to H2, He, N2, and argon. Preferred embodiments are as described above.
By using the compounds of formula I as precursors for preparing semiconductor substrates, the semiconductor substrate will comprise an Si—Ge layer comprising or consisting of a backbone of the compounds of the invention. By using the compounds of the invention, as opposed to the separate use of Si and Ge sources for deposition, the resulting Si—Ge layer comprises highly defined and uniform bonding arrangements and strain compensated Si—Ge atomic patterns, as opposed to the random nature of prior Si—Ge films in which the Si and Ge atoms can exist as an intimate mixture of several (or multi) atom Si and Ge clusters leading to inhomogeneous bonding and locally stressed configurations. In mismatched heteroepitaxy applications these materials exhibit copious dislocations (at levels unacceptable for most device applications), strain non-uniformities and high surface roughness. A distinct and important advantage of our compounds, films, and methods over conventional ones is that the incorporation of the entire Si—Ge molecular core promotes the formation of exceptionally uniform bonding arrangements over the entire crystal, leading to relaxed (or uniformly stressed) films with planar surface morphology (no surface ripples). A crucial advantage is the unprecedented low growth temperatures which reduce surface mobility of the Si and Ge atoms and prevent mass segregation thereby resulting in highly uniform compositional and strain profiles at the atomic level.
The intact incorporation of the massive Si/Ge cores into the film also leads to low surface diffusion and high sticking coefficients compared to the conventional low mass compounds. The high reactivity permits promotes high growth rates which increase systematically with the mass of the precursors
Furthermore, the incorporation of the entire Si/Ge framework of the gaseous precursor into the lattice is particularly important in the formations of SiGe nanoscale systems (quantum dots and wires) because it allows precise control of morphology, tunable composition, and structure that cannot be accomplished by vapor deposition of separate silanes and germanes, or by molecular beam epitaxy of solid Si and Ge sources. The precise control of composition and corresponding morphology, both of which ultimately determine the physical properties of these nanoscale materials is a crucial issue. Any compositional variations that exist within and among individual nanostructures will have a significant impact on the optical and electronic properties and on the performance of devices. In the MBE case an average concentration is assigned on the basis of the flux ratio utilized to grow the materials. In the CVD approach the local stoichiometry on the scale of the nanostructure size is even less certain because reactions of various molecular sources cannot be simultaneously controlled at every site throughout the sample. Thus neither technique can guarantee systematic growth of Si—Ge nanoscale structures with controllable composition, strain and size.
Such highly defined patterns can be determined using standard methods in the art, such as neutron diffraction
An example of an Si—Ge layer comprising a backbone of the compounds of the invention can be found in
Thus, the compounds of the invention can be used to form a random alloy with intimate mixing of the elements using the GeSiSiGe precursors of formula I. The resulting Si—Ge backbone structure consists of polymerized units of the starting compound of the invention, wherein polymerization requires dehydrogenation.
As will be understood by those of skill in the art, other macromolecular, polymeric units of the invention, based on one or more other polymerized compounds of the invention can also lead to Si—Ge lattices with a desired concentration of Ge and Si based on the concentration of each in the compound used.
Preferred embodiments of this aspect are as discussed above for the second aspect of the invention.
In a third aspect, the present invention provides methods for synthesizing one or more silicon-germanium hydrides of formula I, (SiHn1)x(GeHn2)y, wherein the method comprises combining one or more perfluoroalkyl-sulfonate-substituted disilane with a compound comprising a GeH3 ligand under conditions whereby the silicon-germanium hydride is formed. In a preferred embodiment, the perfluoroalkyl-sulfonate-substituted disilane is selected from the group consisting of a nonafluorobutane-sulfonic substituted disilane and a triflate substituted disilane
Thus, this aspect provides methods for making the compounds of formula I. The synthetic routes described herein utilize high yield single-step substitution reactions to yield semiconductor grade materials suitable for industrial application and manufacturing processes.
In one embodiment of this third aspect, the compound comprising a GeH3 ligand is selected from the group consisting alkali and alkaline earth germanides. In a preferred embodiment, the alkali or alkaline earth germanides are selected from the group consisting of KGeH3, NaGeH3, and MR3GeH3, wherein M is a group IV element and R is an organic ligand.
In a further embodiment of this third aspect, the method comprises combining the compound comprising a GeH3 ligand with a nonafluorobutane-sulfonic substituted disilane, wherein the nonafluorobutane-sulfonic substituted disilane comprises (SO3C4F9)2(SiH2)2. In other embodiments, entire families of perfluoroalkyl sulfonyl and alkyl sulfonyl substituted silanes (or germanes) can be used. More preferably, the compound comprising a GeH3 ligand is KGeH3, and the silicon germanium hydride is formed according to the equation (SO3C4F9)2(SiH2)2+2KGeH3→(H3Ge)2(SiH2)2+2K SO3C4F9. Even more preferably, the method comprises:
(a) adding (SO3C4F9)2(SiH2)2 to a slurry of KGeH3 in solvent at between −50° C. and −30° C. (more preferably about −40° C.) to form a mixture;
(b) warming the mixture to between −20° C. and 0° C. (more preferably about −10° C.);
(c) stirring the mixture under nitrogen,
(d) heating the mixture to between 25° C. and 45° C. (more preferably about 35° C.); and
(e) distilling the mixture to form the (H3Ge)2(SiH2)2.
In an alternative embodiment of this third aspect, the method comprises combining the compound comprising a GeH3 ligand with a triflate substituted disilane, and wherein the triflate substituted disilane comprises (SO3CF3)2(SiH2)2. More preferably, the compound comprising a GeH3 ligand is KGeH3, and the silicon germanium hydride is formed according to the equation
(SO3CF3)2(SiH2)2+2KGeH3→(H3Ge)2(SiH2)2+2KSO3CF3. Even more preferably, the method comprises
(a) adding (SO3CF3)2(SiH2)2 to a slurry of KGeH3 in solvent at between −40° C. and −10° C. (more preferably about −30° C.) to form a mixture;
(b) optionally warming the mixture to between 10° C. and 35° C. (more preferably about 23° C.);
(c) stirring the mixture under nitrogen; and
(d) distilling the mixture to form the (H3Ge)2(SiH2)2.
In this embodiment, low temperature (T<−10° C.) reactions of (SO3CF3−)2(SiH2)2 with KGeH3 afforded predominately (H3Ge)2(SiH2)2 and impurity levels of (GeH3)2(SiH2GeH2). These species can be separated by distillation. In contrast to the low temperature pathways, the reaction of (SO3CF3)2(SiH2)2 with KGeH3 at T≧22° C. yields predominately combinations of the positional isomers (GeH3)2(SiH2)2 and (GeH3)2SiH(SiH3) in varying proportions (a small amount of (GeH3)2(SiH2GeH2) is also produced but this is readily separated form the bulk via fractional distillation from the (SO3CF3)2(SiH2)2 and (GeH3)2(SiH2GeH2) mixture.
In a fourth aspect, the present invention provides methods for depositing a Si—Ge material on a substrate in a reaction chamber, comprising introducing into the chamber a gaseous precursor comprising or consisting of one or more compounds according to formula I, under conditions whereby a layer comprising a Si—Ge material is formed on the substrate.
In a fifth aspect, the present invention provides methods for depositing an epitaxial Si—Ge layer on a substrate, comprising introducing near a surface of the substrate a gaseous precursor comprising or consisting of one or more compounds according to formula I, and dehydrogenating the precursor under conditions whereby epitaxial Si—Ge is formed on the substrate.
In this aspect, the substrate can be any substrate suitable for semiconductor or flat panel display use, including but not limited to silicon, germanium, silicon on insulator, Ge:Sn alloys, SiO2, sapphire, quartz, Si:Ge alloys, Si:C alloys, stainless steel, polyimide or other polymer films. In a preferred embodiment, the substrate comprises Si(100).
Embodiments of the gaseous precursors are as described above for previous aspects of the invention. For example, the methods may further comprise adding a dopant on the substrate, including but not limited to the inclusion of dopants, such as boron, phosphorous, arsenic, and antimony. These embodiments are especially preferred for semiconductor substrates used as active devices. Inclusion of such dopants into the semiconductor substrates can be carried out by standard methods in the art.
In another embodiment, the methods comprise adding varying quantities if carbon or tin to the semiconductor substrate. Inclusion of carbon or tin into the semiconductor substrates can be carried out by standard methods in the art. The carbon can be used to reduce the mobility of the dopants in the structure and more specifically boron. Incorporation of Sn can yield materials with novel optical properties such as direct emission and absorption leading to the formation of Si-based lasers and high sensitivity infrared photodetectors.
As demonstrated herein, the silicon-germanium hydrides of the invention were used to deposit device quality layers on substrates that display homogeneous compositional and strain profiles, low threading dislocation densities and atomically planar surfaces.
In a preferred embodiment of the fourth and fifth aspects of the invention, the step of introducing the gaseous precursor comprises introducing the gaseous precursor in substantially pure form. In a further preferred embodiment, the step of introducing the gaseous precursor comprises introducing the gaseous precursor as a single gas source.
In another embodiment of the fourth and fifth aspects, the step of introducing the gaseous precursor comprises introducing the gaseous precursor intermixed with an inert carrier gas. In this embodiment, the inert gas can be, for example, He, argon, H2 or N2.
In these aspects, the gaseous precursor can be deposited by any suitable technique, including but not limited to gas source molecular beam epitaxy, chemical vapor deposition, plasma enhanced chemical vapor deposition, laser assisted chemical vapor deposition, and atomic layer deposition.
In a preferred embodiment of the fourth and fifth aspects, the gaseous precursor is introduced at a temperature of between 300° C. and 450° C., more preferably between 350° C. and 450° C. Practical advantages associated with this low temperature/rapid growth process include (i) short deposition times compatible with preprocessed Si wafers, (ii) selective growth for application in high frequency devices, and (iii) negligible mass segregation of dopants, which is particularly critical for thin layers.
In various further embodiments of the fourth and fifth aspects, the gaseous precursor is introduced at a partial pressure between 10−8 Torr and 1000 Torr. In one preferred embodiment, the gaseous precursor is introduced at between 10−8 Torr and 10−5 Torr (corresponding to UHV vertical furnace technology). In another preferred embodiment, the gaseous precursor is introduced at between 10−8 Torr and 100 Torr, corresponding to LPCVD conditions.
In various other preferred embodiments, the Si—Ge material is formed on the substrate as a strain-relaxed layer having a planar surface; the composition of the Si—Ge material is substantially uniform; and/or the entire Si and Ge framework of the gaseous precursor is incorporated into the Si—Ge material or epitaxial Si—Ge.
In a sixth aspect, the present invention provides a compound comprising or consisting of (SO3C4F9)2(SiH2)2, as well as methods for making the compound. As disclosed herein, (SO3C4F9)2(SiH2)2 is useful as an intermediate in the synthesis of the silicon-germanium hydrides of the invention. In one embodiment, methods for synthesizing (SO3C4F9)2(SiH2)2 comprise combining R(SiH2)2 and HSO3C4F9 under conditions whereby the (SO3C4F9)2(SiH2)2 is formed, where R is an aryl substituent. Such aryl substituents include, but are not limited to, p-tolyl and benzyl.
In a preferred embodiment, methods for synthesizing (SO3C4F9)2(SiH2)2 comprise combining (p-tolyl)2(SiH2)2 and HSO3C4F9 under conditions whereby the (SO3C4F9)2(SiH2)2 is formed. Preferably, the (SO3C4F9)2(SiH2)2 is formed according to the equation
(p-tolyl)2(SiH2)2+2HSO3C4F9→(SO3C4F9)2(SiH2)2+2(toluene)
More preferably, the method comprises
(a) combining HSO3C4F9, (p-tolyl)2(SiH2)2, and solvent in a reaction chamber at between −50° C. and 0° C. to form a mixture;
(b) warming the mixture to between 20° C. and 25° C.;
(c) stirring the mixture; and
(d) filtering the solid (SO3C4F9)2(SiH2)2.
The synthesis of butane-like (GeH3)2(SiH2)2 (Referred to above as GeH3-SiH2-SiH2-GeH3)(1), (GeH3)2SiH(SiH3) (referred to above as SiH[(GeH3)2(SiH3)] (2) and (GeH3)2(SiH2GeH2) (also referred to as GeH3-SiH2-GeH2-GeH3) (3) Si—Ge hydrides with applications in low temperature synthesis of Ge-rich Si1-xGex optoelectronic alloys is herein demonstrated. The compositional, vibrational, structural and thermochemical properties of these compounds were studied by FTIR, multinuclear NMR, mass spectrometry, Rutherford backscattering, and density functional theory (DFT) simulations. The analyses indicate that the linear (GeH3)2(SiH2)2 (1) and (GeH3)2(SiH2GeH2) (3) compounds exist as a mixture of the classic normal and gauche conformational isomers which do not seem to interconvert at 22° C. The conformational proportions in the samples were determined using a new fitting procedure, which combines calculated molecular spectra to reproduce those observed by varying the global intensity, frequency scale and admixture coefficients of the individual conformers. The (GeH3)2(SiH2)2 (1) species was then utilized to fabricate Si0.50Ge0.50 semiconductor alloys reflecting exactly the Si/Ge content of the precursor. Device quality layers were grown via gas source MBE directly on Si(100) at unprecedented low temperatures 350-450° C. and display homogeneous compositional and strain profiles, low threading dislocation densities and atomically planar surfaces. Low energy electron microscopy (LEEM) analysis has demonstrated that the precursor is highly reactive on Si(100) surfaces, with H2 desorption kinetics comparable to those of Ge2H6, despite the presence of strong Si—H bonds in the molecular structure.
The synthesis of the main product 1,2-digermyldisilane, (H3Ge)2(SiH2)2 (1) was accomplished via reactions of KGeH3 with the nonafluorobutane-sulfonic and triflate substituted disilanes (C4F9SO3)2(SiH2)2 (4) and (SO3CF3)2(SiH2)2 (5) as illustrated by Eq 1 and 2 respectively. The starting materials (4) and (5) were prepared via reactions of the corresponding sulfonic acids HSO3C4F9 and HSO3CF3 with 1,2-(p-tolyl)2(SiH2)2 (Eq 3 and 4, respectively).
(SO3C4F9)2(SiH2)2+2KGeH3→(H3Ge)2(SiH2)2+2K SO3C4F9 (1)
(SO3CF3)2(SiH2)2+2KGeH3→(H3Ge)2(SiH2)2+2KSO3CF3 (2)
(p-tolyl)2(SiH2)2+2HSO3C4F9→(SO3C4F9)2(SiH2)2+2(toluene) (3)
(p-tolyl)2(SiH2)2+2HSO3CF3→(SO3CF3)2(SiH2)2+2(toluene) (4)
The route described by (Eq 1) consistently produces pure, single-phase (H3Ge)2(SiH2)2 (1) as a colorless, pyrophoric liquid. Here the replacement of—SO3C4F9 by GeH3 occurs exclusively at the 1,2-substitution sites of (SO3C4F9)2(SiH2)2 (4), as expected. However, the route described by (Eq 2) yields a mixture of products (
—SiH2—SiH2—GeH3+GeH3→SiH3—SiH2—GeH3+GeH2→(GeH3)2SiH(SiH3) (6)
SiH3—SiH2—SiH3+SiH2→(SiH3)2SiH(SiH3) (7)
The synthesis of (5) is described by (Eq 4) and has been previously demonstrated elsewhere. Its (p-tolyl)2(SiH2)2 starting materials has been produced via coupling reactions of (p-tolyl)SiH2Cl with powdered lithium.10 In the present work we adopt a more convenient, analogous approach using readily available sodium fragments as the coupling agent. Compound (5) is obtained as a highly reactive liquid, which is difficult to fully handle and purify. Consequently its reactions with KGeH3 are complex and produce mixtures of products as described above. In contrast the newly prepared compound (4) is readily crystallized as a robust molecular solid that is completely isolated from the reaction byproducts and other contaminants, thereby leading to high purity (H3Ge)2(SiH2)2 in subsequent steps according to (Eq 1). The compositional, vibrational and structural properties of the newly synthesized compounds (1), (2), (3) and (4) are presented below.
(H3Ge)2(SiH2)2 (1): The (H3Ge)2(SiH2)2 (1) species is prepared as described by the reactions depicted in (Eq 1,2) and was isolated and purified by fractional distillation (vapor pressure of ˜8-10 Torr at 22° C.). The FTIR, 29Si NMR (proton-coupled) and mass spectra indicate a 1,2-digermyldisilane with a butane-like structure as shown in
(H3Ge)2(SiH2)2(gas)→2SiGe(film)+5H2(gas) (8)
(GeH3)2SiH(SiH3) (2): The isobutane-like structure of (2) was determined by 29Si and 1H NMR studies. The proton NMR resonances are present as a multiplet centered at 3.049 ppm due to —SiH, and two doublets centered at 3.213 and 3.404 ppm corresponding to the (—GeH3)2 and —SiH3 protons, respectively. The integrated peak intensity ratios of the —SiH, (—GeH3)2 and —SiH3 are 1:6:3, respectively, as expected. The peak intensities, the coupling patterns and the position of the peaks in the spectrum, collectively point to the isobutane-like structure in which an Si center is terahedrally bonded to two GeH3 groups one SiH3 group and an single H atom. This structure is further confirmed by 2D 1H COSY and 1H—29Si HMQC NMR measurements. The 2D 1H COSY spectrum showed cross-peaks that correlate to the central SiH, and terminal GeH3 and SiH3 resonances at 3.049, 3.213 and 3.404 ppm, respectively, indicating a H3Si—SiH-(GeH3)2 connectivity, which is consistent with the proposed isobutane structure. A proton-decoupled 1H—29Si HMQC spectrum showed that the H atoms at 3.049 and 3.404 ppm are directly bonded to Si atoms at −121 and −93 ppm, respectively. The 29Si chemical shift (−121 ppm, in C6D6) due to the central Si atom in this molecule is similar to those found for SiH(GeH3)3 (−113 ppm in CDCl3) and Si(GeH3)4 (−128 ppm, in CDCl3). A close correspondence is also found between the 29Si chemical shift (−93 ppm) due to the terminal Si atom and those of the terminal SiH3 groups (−92 ppm) for H3SiGeH3.
Gas-chromatography mass-spectrometry experiments (GCMS) of samples containing (1) (H3Ge)2(SiH2)2 and (GeH3)2SiH(SiH3) (2) indicated the presence of two major fractions that displayed slightly different retention times in the GC column, which is consistent with a mixture of (1) and (2) possessing slightly different boiling points. Furthermore, these fractions displayed essentially identical mass spectra. The highest mass peak is observed in the 210-196 amu range corresponding to the (Si2Ge2Hx+) parent ions of (1) and (2). Samples of the mixture were further characterized using IR spectroscopy. The spectra are essentially a simple admixture of the individual (1) and (2) components. The spectrum of (2) was theoretically determined since the compound could not be completely separated in pure form from (1) via our distillation method due to the similarity in their boiling points. The contributions of the each compound in the experimental IR spectra were then determined using a fitting procedure involving both the observed and the calculated spectra.
(GeH3)2(SiH2GeH2) (3): Compound (3) is a byproduct of the reaction described by Eq 2. Its gas-phase IR spectrum shows the Si—H and Ge—H stretching bands centered at 2145 and 2073 cm−1, respectively. The intensity of the Ge—H peak in the spectrum is significantly stronger than the Si—H due to the greater number of Ge—H bonds relative to Si—H bonds. The 1H NMR spectra showed a set of two sextets at 3.30 and 3.03 ppm ensconcing two triplets at 3.23, 3.13 ppm. The integrated peak intensity ratios of the sextet-triplet-triplet-sextet sequence are 2:3:3:2. The integrated intensities the coupling patterns and the position of the peaks in the NMR spectrum collectively point to a H3Ge—SiH2—GeH2—GeH3 molecular structure in which a central SiH2GeH2 core is bonded with two terminal GeH3 moieties. In particular, the sextets at 3.30 and 3.03 ppm can be associated, respectively, with the SiH2 and GeH2 protons of the central —SiH2GeH2— while the triplets at 3.23, 3.13 ppm correspond to terminal GeH3 protons. The SiH2 and GeH2 NMR frequencies in this case correlate well with those in the previously reported (H3Ge)2SiH2 and GeH3GeH2SiH3 compounds.7 The assignment of the sextet at 3.30 ppm to the SiH2 protons was further corroborated by a 1H—29Si HMQC NMR spectrum, which indicates a direct coupling to a single 29Si resonance found at −98.2 ppm. In addition, a 2D 1H COSY NMR spectrum was used to unequivocally establish the specific ordering of the Ge—Si—Ge—Ge backbone constituents. Cross-peaks correlate an Si—H and three Ge—H resonances at 3.30, 3.23, 3.13 and 3.03 ppm. These correspond, respectively, to SiH2, GeH3 (terminal) connected to GeH2, Ge—H3 (terminal) connected to SiH2, and GeH2. The mass spectra showed an isotopic envelope at 256-238 amu as the highest mass peak corresponding to the parent ion, (SiGe3Hx+) and a fragmentation pattern consistent with the molecular structure.
(C4F9SO3)2(SiH2)2 (4): Compound (4) is isolated at 95% yield as a colorless, pyrophoric solid with a melting point of 68° C. It is readily soluble in ethers, CHCl3, CH2Cl2 and slightly soluble in toluene. The 1H NMR spectrum showed a singlet centered at 5.08 ppm (δ Si—H) due to SiH2 and 29Si satellite peaks. These exhibit a triplet of triplets with a 1-bond Si—H coupling of 272 Hz and a H—H 3-bond coupling of 3.6 Hz. This indicates the presence of a second SiH2 group consistent with the —SiH2SiH2-core. Furthermore, a proton decoupled 1H—29Si HMQC showed that the proton resonance at 5.08 ppm is directly attached to a Si atom at −30.1 ppm. These values are consistent with those observed for the triflate analog (SO3CF3)2(SiH2)2 (5).10 Compound (4) was further characterized by FTIR, mass spectrometry and C, H, F elemental analysis and the data are fully consistent with the proposed structure (see experimental section).
Structural and thermochemical properties: In order to corroborate the identification of the (GeH3)2(SiH2)2, (GeH3)2SiH(SiH3) and (GeH3)2(SiH2GeH2) described above we simulated the structural, energetic and vibrational trends of these compounds. In prior studies7 we demonstrated that B3LYP hybrid density functional theory (DFT) simulations provide an excellent account of the ground state structural, thermochemical and vibrational properties of the (H3Ge)xSiH4-x family of molecular hydrides. In particular use of the 6-311G++(2d,2p) basis set yielded small typical bond length and frequency discrepancies (on the order of 0.4% and 1.4%, respectively). Accordingly, our first attempt at reconciling the observed IR spectra with those calculated was based on the same procedure, and on the assumption that the fundamental structures are n-butane like. Although this approach provided a close match to most of the main spectral features observed, several strong low-frequency features remained unaccounted for in the calculated IR pattern. In view of the prior success of B3LYP approach we concluded that n-butane like molecular structures alone could not account for the spectrum of the synthesized compounds. We therefore expanded our calculations to include the gauche conformational isomers in which a terminal GeH3 group is rotated out of the Ge—Si—Si—Ge (or Ge—Si—Ge—Ge) skeletal plane, as well as the iso-butane like positional isomer i-Si(SiGeGe) (
Initial basis set convergence tests showed that a full resolution of differences in the calculated properties of the conformational/positional isomers requires an even more stringent treatment than that used in the prior studies on (H3Ge)xSiH4-x hydrides, particularly with regards to calculated vibrational properties. Accordingly all of the calculations described in the present work were carried out at the B3LYP/6-311G++(3df,2pd) level as implemented in the Gaussian03 code.11
The results of the structural optimizations, obtained using “tight” convergence criteria, are presented in
The Si—H and Ge—H bond lengths occur exclusively as central SiH2 moieties and terminal GeH3 groups in the n- and g-GeSiSiGe isomers, with values of 1.486 Å and 1.539 Å, respectively. In the corresponding GeSiGeGe isomers the Si—H bonds associated with the SiH2 moiety has essentially the same value, 1.485 Å, while the GeH2 moiety exhibits a slightly longer Ge—H bond (1.542-1.548 Å) than in a GeH3 terminal group, as expected. Due to its unique structure the i-Si(SiGeGe) isomer possesses both terminal SiH3 and GeH3 groups and a single SiH moiety. Here the Ge—H bond lengths associated with the terminal GeH3 groups have the same value (1.539 Å) as in GeH3 groups of other isomers, while the corresponding terminal group Si—H3 bond lengths are slightly contracted (1.483 Å). The longest Si—H bond length is associated with the central SiH moiety and has a value 1.488 Å. Collectively, these bond length trends are consistent with those found previously in the heaviest members of the (H3Ge)NSiH4-N (N=3,4) family of molecules.
The data presented in
Vibrational spectra: In order to facilitate the interpretation of the observed FTIR spectra we calculated the vibrational frequencies and intensities of the conformational isomers n-GeSiSiGe and g-GeSiSiGe, and positional isomer i-Si(SiGeGe) of the primary product, as well as those of the minor species n-GeSiGeGe and g-GeSiGeGe, using the B3LYP DFT functional at the B3LYP/6-311G++(3df,2pd) level. No symmetry was imposed in the calculation of the frequency spectra and all molecules studied exhibited a positive definite spectrum of harmonic frequencies indicating that the ground state structures are dynamically stable.
Ge2Si2H10 molecules:
The low-frequency non-skeletal vibrational structure, also shown in
The low-frequency spectrum of i-Si(SiGeGe), shown in
SiGe3H10 molecules: For the n- and g-(GeH3)2(SiH2GeH2) isomers we corroborate the NMR characterization by directly comparing the observed IR spectrum with that calculated for a 1:3 mixture of n-GeSiGeGe and g-GeSiGeGe conformations (a detailed explanation is given in the following section). The calculated IR spectra for both the n- and g-isomer, convoluted with a Gaussian of width ˜20 cm−1 to simulate experimental broadening, are given in
The high-frequency Si—H stretching bands are similar to those found in the GeSiSiGe analogs, exhibiting calculated splitting of 13-14 cm−1 between the symmetric and anti-symmetric bands and a systematic overall ˜4-5 cm−1 shift to lower frequency in the gauche isomer. Here (N11:G17) and (N10:G16) correspond to asymmetric and symmetric Si—H stretches, respectively. However, a simple comparison for corresponding Ge—H stretching vibrations for these isomers is vitiated by the lower symmetry of GeSiGeGe isomers. For example the asymmetrical Ge—H stretch (N9) in n-GeSiGeGe is split into contributions G12, G14 and G15 in the gauche isomer while the symmetric Ge—H stretch, N8 in the n-GeSiGeGe, is split into bands G11 and G13.
In the low-frequency range of the spectrum we find a strong correspondence between mode assignments of the n- and g-isomers above 700 cm−1. Specifically, the asymmetrical H—Si—H wagging vibrations N3 in n-GeSiGeGe appears as G6 in g-GeSiGeGe, with a frequency near 731 cm−1. As in our earlier discussion we designate such corresponding pairs between isomer conformations as (N3:G6). Intense Ge—H wagging vibrations (N4:G7) associated with terminal GeH3 groups appear near 808 cm−1. Similarly, H—Ge—H “scissor” modes at 866 cm−1 are designated as (N5:G8), while their H—Si—H counterparts (N7:G10) appear at 936 cm−1 (the frequency of the corresponding mode in the GeSiSiGe isomers was 925 cm−1). The features denoted (N6:G9) consist of asymmetrical “scissor”-like vibrations associated with the terminal GeH3 groups.
The most significant differences between the IR spectra of the n- and g-isomers are found below 700 cm−1. The most intense spectral feature in n-GeSiGeGe (N2) is associated with a highly symmetric wagging of the protons bound to the GeH2 moiety parallel to the molecular backbone. In the gauche isomer this mode is split into three features denoted G3, G4 and G5, corresponding to asymmetrical Ge—H wagging of combinations of individual protons in the GeH2 moiety. Finally, the mode N, in the n-isomer, consisting of concerted symmetrical wagging of terminal GeH3 protons at both ends of the molecule, is split into two modes G1 and G2 in the gauche isomer in which symmetrical wagging occurs independently in the two GeH3 terminal groups.
Isomer Admixture Analysis: To estimate the molar concentration of the conformational and positional isomers in the observed spectra, we adopt an approach commonly employed in “multi-phase” fitting of x-ray spectra, in which a normalized admixture of known pure-phase candidate spectra is fitted to an unknown observed spectrum of the combined molecules. Using the same procedures as in our prior studies on Si—Ge hydrides we have calculated the spectra of 10 digermyl-disilyl positional/conformational isomers (to be described elsewhere). These calculated spectra serve as a proxy for the unknown pure isomer candidate spectra normally supplied by experiment. A comparison of our calculated spectra with that of the synthesized compounds suggests the presence of simple admixtures of conformational {n-GeSiSiGe, g-GeSiSiGe} and positional {i-Si(SiGeGe), g-GeSiSiGe} isomers for the Si2Ge2H10 family. To proceed with the analysis all of the required theoretical spectra (n-, g- and iso-isomers, see
where γ is the normalized admixture of n- and g-spectra, β is the global amplitude of the theoretical spectrum and η is the common frequency scale factor applied to the theoretical spectra. An identical procedure is used to treat the {i-Si(SiGeGe), g-GeSiSiGe} combination. In all cases the theoretical spectra were evaluated at arbitrary frequencies using cubic splines, and a robust simplex method was used to minimize the objective function. For the {n-GeSiSiGe, g-GeSiSiGe} pair this yields a scale factor of η=0.984 and an admixture of γ=0.392 (i.e., ˜39% n-GeSiSiGe). This optimized scale factor is very similar to the value 0.989 used in previous studies of the (H3Ge)xSiH4, hydrides7 and Si2H6, Ge2H6 and H3GeSiH3 molecules12 at this level of theory. As shown in
The corresponding results for the GeSiGeGe impurity compound are shown in
We have observed that the proportions derived for the conformational isomers are essentially constant between different samples. To elucidate this observation we calculated the potential energy surface (PES) of the butane-like GeSiSiGe as a function of the Ge—Si—Si—Ge backbone torsion angle. The linear conformation corresponds a torsion angle of 180° while the gauche modification occurs at ˜66° (see
It should be noted that our B3LYP/6-311G++(3df,2pd) tetrasilane values for ΔEn-g and ΔEe are qualitatively different from those calculated by Albinsson et al13 at the MP2/6-31* level for the same molecule. In particular the latter authors predict a symmetric n-g barrier and a near identity of gauche and linear conformation energy (ΔEn-g˜0.588, ΔEg, ˜−0.04 and ΔEe˜1.236 kcal/mol). Unfortunately, because the basis set levels and model chemistries in our two approaches both differ, the origin of this discrepancy is ambiguous. We therefore carried out a series of coupled cluster calculations at the CCSD/LANL2DZ level for the sequence butane, tetrasilane and GeSiSiGe. The results, shown as solid lines in
It should be noted that the 68% value obtained for the positional isomeric spectrum, shown in
The deposition experiments were conducted on a clean Si(100) substrates in ultra-high vacuum system equipped with a low energy electron microscope (LEEM) that allowed in situ real time observation of the growth process. The (H3Ge)2(SiH2)2 gaseous precursor reacted on the Si surface via complete H2 elimination at partial pressures in the range of 10−5-10−8 Torr. Initially, the reaction growth kinetics was investigated using LEEM and the activation energy (Eact) of the compound with respect to H2 desorption from the Si surface was measured. It is known that for conventional silanes and germanes the Eact is much lower on a Ge containing surface (including Si1-xGex) than on pristine Si. Thus, an accurate determination of Eact can only be obtained from measuring the growth rate of the first monolayer, (which grows directly on pure Si) and not that of subsequent layers, which grow on Ge containing surfaces and have higher growth rates. In this regard LEEM is particularly unique because its dynamic imaging differentiates the Si(001)-(2x1) surface from the Si1-xGex epilayer and thus provides unambiguous means for the correct determination of Eact on Si by measuring the growth rate of the first Si1-xGex monolayer vs. temperature.
For comparison the growth rates of Ge2H6 and H3GeSiH3 were also determined using the same method. For these and for H3Ge)2(SiH2)2 the first monolayer took longer to complete on pristine Si than subsequent monolayers.
The synthesis of Si0.5Ge0.5 films was investigated in the 350° C.-500° C. range via dehydrogenation of (H3Ge)2(SiH2)2. The highest temperature that yields planar layers is ˜450° C. The growth rate is ˜4 nm/min and decreases to 2 nm/min at 350° C. No appreciable growth was observed below 300° C. (1×10−5 Torr) due to the reduced reactivity of the compound. Thick films with rough surfaces and defective microstructures were produced at 500° C. with growth rates as high as 15 nm/min. The composition and heteroepitaxial character of the films were investigated by random and channeling Rutherford backscattering (RBS), which in all cases indicate a highly stoichiometric material aligned with the substrate. The ratio of the aligned versus the random peak heights (χmin), which measures the degree of crystallinity, decreases from 15% at the interface to 6% at the surface indicating a dramatic reduction in dislocation density across the thickness of the film. This is confirmed by high resolution XTEM, which revealed commensurate SiGe/Si interfaces and perfectly monocrystalline layer microstructures. A survey of TEM samples showed no defects penetrating through the layers within a field of view of ˜2.5 μm in the micrographs indicating an upper limit in the threading dislocation density of ˜106/cm2 (
Atomic force microscopy (AFM) studies show that films with thickness of 50 and 750 nm display RMS values of 0.5 and 1.5 nm, respectively, for 10×10 μm2 areas, indicating highly planar surfaces for samples grown at T<450° C. as shown
The thermal properties of the films were investigated between 450° C. and 750° C., a range well within device processing temperatures. The XRD lattice constant, the RBS χmin values, and the AFM roughness were measured for the annealed samples and compared with the corresponding values of the as-grown materials. Samples with a thickness as low as 200 nm did not show any increase in surface roughness even after annealing at 750° C. indicating that the surface planarity of our samples is thermally robust. The XRD and RBS aligned spectra were essentially identical before and after annealing. This result also confirms full relaxation in the as-grown layers at T<450° C.
We have demonstrated the synthesis of the butane-like compounds with molecular formulas (GeH3)2(SiH2)2 (1) (GeH3)2SiH(SiH3) (2) and (GeH3)2(SiH2GeH2) (3) and their conformational isomers. Detailed characterization of the products was conducted via a range of spectroscopic and analytical methods including quantum chemical simulations. A new fitting procedure was developed, based on the admixture of normal and gauche calculated spectra, to obtain the proportions of the individual conformers in the product sample at 22° C. Controlled depositions of (1) have produced stoichiometric SiGe films possessing the desired properties for semiconductor applications including perfectly crystalline and epitaxial microstructures, smooth morphologies, and uniformly strain-relaxed states. Unique practical advantages associated with this low temperature (˜350-450° C.) rapid growth include: (i) short deposition times compatible with preprocessed Si wafers, (ii) selective growth for application in high frequency devices, and (iii) negligible mass segregation of dopants, which is particularly critical for thin layers. Finally we have found that these compounds are remarkably stable over extended periods of time, with evidence of decomposition, and thus represent viable molecular sources for potential industrial applications.
All manipulations were carried out under inert conditions using standard Schlenk and drybox techniques. Dry, air-free solvents were distilled from either anhydrous CaCl2 or sodium benzophenone ketyl prior to use. All NMR spectra were collected either on a Varian INOVA 400 spectrometer operating at 400 MHz or a Gemini 300 spectrometer. Samples were dissolved in CDCl3 or C6D6 and all nuclei were referenced either directly or indirectly to the proton signal of TMS or the residual solvent peak as indicated. IR spectra were recorded using a 10 cm gas cell with KBr windows. Elemental analyses were performed by Desert Analytics (Tucson, Ariz.). Gas chromatography mass spectrometry (GCMS) data were obtained using a JEOL JMS-GC Mate II spectrometer. Powdered lithium (Aldrich), lithium tetrahydroaluminate (Aldrich), trichloro(p-tolyl)silane (Gelest), trifluoromethane sulfonic acid (Alfa Aesar), nonafluorobutane-1-sulfonic acid (Aldrich) and electronic grade germane gas (Voltaix, Inc.) were used as received. The starting materials p-tolylsilane, chloro(p-tolyl)silane, 1,2-bis(p-tolyl)disilane and 1,2-bis(trifluoromethylsulfonyloxy)disilane were prepared according to literature procedures and their purity checked by NMR spectroscopy. Potassium germyl was synthesized in monoglyme using sodium-potassium (80% K) alloy. The coupling reactions using powdered lithium were performed in a helium environment rather that in an N2 atmosphere to prevent formation of lithium nitride.
(p-tolyl)2(SiH2)2. A solution of monochloro(p-tolyl)silane (10.0 g, 63.8 mmol) in di-n-butyl ether (120 mL) and toluene (40 mL) is stirred with sodium pieces (1.68 g, 146.2 mmol) for 5 h at 125° C. The mixture is filtered and the filtrate is distilled to remove the solvents and other impurities. The remaining colorless liquid product (4.40 g, ˜60%) was examined by NMR to determine its identity and purity and was subsequently used without purification.
(C4F9SO3)2(SiH2)2: A sample of C4F9SO3H (7.9 g, 26.3 mmol) was added to a 15 mL solution of 1,2-(p-tolyl)disilane (3.18 g, 13.1 mmol) in toluene at −40° C. A colorless precipitate was immediately formed at low temperatures. The reaction flask was warmed to 23° C. and stirred for 1-2 h. The colorless solid was filtered and dried in vacuo. Repeated concentration and cooling of the toluene filtrate at −20° C. yielded additional product. Yield=7.9 g (95%). Mp=68° C. 1H NMR (300 MHz, CDCl3): δ5.078 (s, 1JSiH=272 Hz, Si—H2, 3JHH=3.6 Hz).29Si NMR (79.5 MHz, CDCl3): δ−30.1. Anal. Calcd for C8F18S2O6Si2H4: C, 14.59; H, 0.61; F, 51.95. Found: C, 14.27; H, 0.87; F, 51.74.
(H3Ge)2(SiH2)2, method A: A 20 mL solution of (C4F9SO3)2(SiH2)2 (4.67 g, 9.5 mmol) was added to a slurry of KGeH3 (2.00 g, 20.9 mmol) in diethyl ether (15 mL), at −40° C. The reaction was then warmed to −10° C. and stirred under nitrogen for 12 h after which it was heated at 35° C. for an additional 1 h. The volatiles were fractionally distilled several times through U-traps held at −20, −50 and −196° C. The −50° C. trap retained pure (H3Ge)2(SiH2)2 (260 mg, 26% Yield) while the −196° C. trap contained solvent, and traces GeH4 and SiH4. Vapor pressure: 7.0 Torr (23° C.). IR (gas, cm−1): 2147 (s), 2073 (vs), 910 (w), 879 (w), 799 (s), 740 (vw), 682 (s), 651 (m), 442 (vw). 1H NMR (400 MHz, C6D6, 7.15 ppm): δ 3.106 (t, J=4.1 Hz, 6H, Ge—H3), δ 3.290 (q, J=3.9 Hz, 4H, S1—H2). 29Si NMR (79.5 MHz, C6D6): δ −105.0 (this value is close to that observed for (H3Ge)2SiH2 at −102.45) GCMS: m/z 210-196 (Si2Ge2Hx+), 180-170 (SiGe2H8-x+), 152-143 (Ge2H6-x+), 140-126 (Si2GeH8-x+), 107-98 (H3SiGeH3+), 77-72 (GeH4+), 62-58 (Si2H6-x+), 32-28 (SiH4+).
(H3Ge)2(SiH2)2, method B: A sample of (CF3SO3)2(SiH2)2 (3.39 g, 9.5 mmol) was added to a slurry of 2.40 g (20.9 mmol) of KGeH3 in diethyl ether (30 mL) at −30° C. The mixture was then warmed to 23° C. and stirred under nitrogen for 5 h. The volatiles were fractionally distilled and the (H3Ge)2(SiH2)2 product in its pure form was collected at a −50° C. trap (0.250 g, ˜13% yield).
(SiH2GeH2)(GeH3)2: The compound is obtained as a byproduct in the synthesis of (H3Ge)2(SiH2)2, and was isolated by repeated distillation through U-traps under static vacuum maintained at −20 and −50° C. to collect SiH2GeH2(GeH3)2 and (H3Ge)2(SiH2)2, respectively. Vapor pressure: 1.0 Torr (22° C.). IR (gas, cm−1): 2145 (m), 2073 (vs), 910 (w), 878 (w), 793 (vs), 723 (w), 679 (w), 615 (s), 443 (vw). 1H NMR (400 MHz, C6D6, 7.15 ppm): (53.30 (sept, J=3.9 Hz, 2H, S1—H2), δ 3.23 (t, J=4.6 Hz, 3H, Ge—H3), (3.13 (t, J=3.90 Hz, 3H, Ge—H3), ±3.03 (sept, J=4.0 Hz, 2H, Ge—H2). 29Si NMR (79.5 MHz, C6D6): δ −98.2. GCMS: m/z 256-240 (SiGe3H10-x+), 230-212 (SiGe2H8-X+), 184-169 (SiGe2H8-x+), 154-141 (Ge2H6-x+), 136-128 (Si2GeH8-x+), 108-98 (SiGeH6-x+), 77-70 (GeH4−+), 32-28 (SiH4+).
This application claims priority to U.S. Provisional Patent Applications Ser. No. 60/739,528 filed Nov. 23, 2005 and Ser. No. 60/764,128 filed Feb. 1, 2006, both of which are hereby incorporated by reference in its entirety.
This work was supported by National Science Foundation grant DMR-0221993 thus the U.S. government may have certain rights in the invention.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US06/45091 | 11/21/2006 | WO | 00 | 9/3/2009 |
| Number | Date | Country | |
|---|---|---|---|
| 60739528 | Nov 2005 | US | |
| 60764128 | Feb 2006 | US |