This application claims priority to and benefit of Chinese Patent Application No. 201310753545.5, filed on 31 Dec. 2013, the Chinese Patent Application being incorporated herein by reference in its entirety.
The present invention is related to a substrate (e.g., a semiconductor substrate), a method for manufacturing the substrate, a device that includes the substrate, and a method for manufacturing the device.
An electronic device may include a three-dimensional integrated circuit (3D IC). The 3D IC may include a plurality of chips that are integrated vertically and horizontally into a circuit.
The 3D IC may include through-silicon vias (TSVs) and/or other interconnection structures for enabling connection between chips. Among TSVs, a through-silicon photonic via (TSPV) may be used for facilitating connection between optical devices, such as waveguide devices. The efficiency of a TSPV connection may depend on one or more structures, e.g., one or more reflective trench sidewalls, in one or more related semiconductor substrates.
A trench sidewall slanted at an angle with a substantially unsuitable size may require additional optical arrangements and/or may not enable a satisfactorily efficient TSPV connection.
An embodiment of the present invention may be related to a method for manufacturing a substrate, such as a semiconductor substrate. The method may include preparing a substrate material member. The method may include processing the substrate material member to form a first remaining portion of the substrate material member. The first remaining portion of the substrate material member may have a first cavity (e.g., a first trench). A sidewall the first cavity may be oriented (e.g., slanted) at a first angle with respect to at least one of a horizontal plane, a bottom surface of the first cavity, and a bottom side of the first remaining portion of the substrate material member. The method may further include providing a sacrificial material member in the first cavity. The sacrificial material member may substantially completely fill the first cavity. The method may further include processing the sacrificial material member when processing the first remaining portion of the substrate material member to substantially completely remove the sacrificial material member and to form a second remaining portion of the substrate material member. The second remaining portion of the substrate material member may have a second cavity (e.g., a second trench). A sidewall the second cavity may be oriented (e.g., slanted) at a second angle with respect to at least one of the horizontal plane, a bottom surface of the second cavity, and a bottom side of the second remaining portion of the substrate material member. The second angle may be less than the first angle. A depth of the second cavity may be less than a height of the sacrificial material member.
The first angle may be in a range of 54 degrees to 56 degrees. The second angle may be in a range of 44.5 degrees to 45.5 degrees. The second angle may be 45 degrees. A length of the sidewall of the second cavity may be in a range of 3 microns to 15 microns.
An etching process may be performed to remove the sacrificial material member and to form the second remaining portion of the substrate material member. In the etching process, a ratio of an etch rate of the sacrificial material member to an etch rate of the first remaining portion of the substrate material member may be in a range of 3.3 to 3.5.
An etching process may be performed to remove the sacrificial material member and to form the second remaining portion of the substrate material member. In the etching process, a ratio of an etch rate of the sacrificial material member to an etch rate of the first remaining portion of the substrate material member may be 3.4.
The method may include using the first angle and a height of the sacrificial material member to determine a target depth for the second cavity. The target depth of the second cavity may be set as the height of the sacrificial material member divided by the tangent of the first angle. In an embodiment, the first angle may be in a range of 54 degrees to 56 degrees, and a ratio of the height of the sacrificial material member to the target depth of the second cavity may be in a range of about 1.37 to about 1.49. In an embodiment, the first angle may be about 54.74 degrees (approximating an angle between two crystallographic planes in the substrate material), and the target depth of the second cavity may be set as the height of the sacrificial material member divided by the tangent of 54.74 degrees (which may be about 1.414).
A process for forming the first remaining portion of the substrate material member may include the following steps: providing a mask material layer on the substrate material member; providing a photoresist layer on the mask material layer, wherein the photoresist layer may have a first pattern; etching the mask material layer when the photoresist layer is positioned on the mask material layer to form a mask that may have a second patter, wherein the second pattern may be similar to or identical to the first pattern; and etching the substrate material member when the mask is positioned on the substrate material layer to form the first cavity.
The mask material layer may be formed of one or more of amorphous silicon, silicon oxynitride, silicon oxide, doped silicon oxide, silicon carbide, silicon nitride, titanium, and titanium oxide.
The sacrificial material member may be formed of a wet-developable material.
The sacrificial material member may be formed of a cross-linked resin that may include one or more of the following elements: an organic solvent that may include at least one of a ketone, an ether, and an alkane; an anti-reflection material; an organic acid group resin that may be reactive to a standard tetramethyl ammonium hydroxide developer solution; and an organic group resin that may include at least one of oxygen and fluorine.
A molecular weight of the sacrificial material member may be in a range of 1000 to 50,000. A refractive index of the sacrificial material member may be in a range of 1.0 to 3.0. An extinction coefficient of the sacrificial material member may be in a range of 0.1 to 3.0.
A process for forming the sacrificial material layer may include the following steps: providing a set of sacrificial material that may include a first coating of sacrificial material and covers the first remaining portion of the substrate material member; determining whether the set of sacrificial material satisfy a set of planarization requirements; if the set of planarization requirements is satisfied, planarizing the set of sacrificial material to form the sacrificial material member, such that a top surface of the sacrificial material member and a top surface of the first remaining portion of the substrate material member are in a same plane; and if the set of planarization requirements is not satisfied, providing an additional coating of sacrificial material that covers the first remaining portion of the substrate material member. One or more of these steps may be repeated if the set of planarization requirements is not satisfied.
The method may include performing a heating process (e.g., a baking process) on the first coating of sacrificial material after providing the first coating of sacrificial material on the first remaining portion of the substrate material member. The sacrificial material amount of the first coating of sacrificial material may be in a range of 0.5 milliliter to 5 milliliters. The heating process may be performed at a temperature that is in a range of 60 degrees Celsius to 250 degrees Celsius for a time duration that is in a range of 10 seconds to 120 seconds.
The method may include the following steps: providing a first anti-reflection layer on the bottom surface of the second cavity; providing a semiconductor material member in the second cavity; and providing a second anti-reflection layer on the semiconductor material member.
An embodiment of the present invention may be related to a method for manufacturing a semiconductor device. The method may include the following steps: preparing a first substrate material member; processing the first substrate material member to form a first remaining portion, wherein the first remaining portion may have a first cavity, wherein a sidewall the first cavity may be oriented at a first angle with respect to at least one of a horizontal plane, a bottom surface of the first cavity, and a bottom side of the first remaining portion; providing a first sacrificial material member in the first cavity; processing the first sacrificial material member when processing the first remaining portion to remove the first sacrificial material member and to form a second remaining portion, wherein the second remaining portion may have a second cavity, wherein a sidewall the second cavity may be oriented at a second angle with respect to at least one of the horizontal plane, a bottom surface of the second cavity, and a bottom side of the second remaining portion, and wherein the second angle may be smaller than the first angle; preparing a first device member using the second remaining portion; preparing a second substrate material member; processing the second substrate material member to form a third remaining portion, wherein the third remaining portion may have a third cavity, wherein a sidewall the third cavity may be oriented at a third angle with respect to at least one of the horizontal plane, a bottom surface of the third cavity, and a bottom side of the third remaining portion; providing a second sacrificial material member in the third cavity; processing the second sacrificial material member when processing the third remaining portion to remove the second sacrificial material member and to form a fourth remaining portion, wherein the fourth remaining portion may have a fourth cavity, wherein a sidewall the fourth cavity may be oriented at a fourth angle with respect to at least one of the horizontal plane, a bottom surface of the fourth cavity, and a bottom side of the fourth remaining portion, and wherein the fourth angle may be smaller than the third angle; preparing a second device member using the fourth remaining portion; and positioning at least one of the first device member and the second device member such that the sidewall of the second cavity overlaps the sidewall of the fourth cavity in a direction perpendicular to at least one of the side of the bottom surface of the fourth cavity and the bottom side of the fourth remaining portion.
Each of the second angle and the fourth angle may be 45 degrees or may approximate 45 degrees, e.g., in a range of 44.5 degrees to 45.5 degrees.
The method may include the following steps: providing a cladding layer between the first device member and the second device member, wherein the cladding layer may include a transmission member (e.g., a TSPV member); and positioning the transmission member between the sidewall of the second cavity and the sidewall of the fourth cavity.
An embodiment of the present invention may be related to a semiconductor device. The semiconductor device may include the following elements: a first substrate, which may have a first cavity, wherein a sidewall of the first cavity may be oriented at a first angle with respect to at least one of a side of the first substrate and a bottom surface of the first cavity, and wherein the first angle may be 45 degrees or may be approximately 45 degrees, e.g., in a range of 44.5 degrees to 45.5 degrees; and a second substrate, which may overlap the first substrate and may have a second cavity, wherein a sidewall of the second cavity may be oriented at a second angle with respect to at least one a side of the second substrate and a bottom surface of the second cavity, wherein the second angle may be 45 degrees or may be approximately 45 degrees, e.g., in a range of 44.5 degrees to 45.5 degrees, and wherein the sidewall of the first cavity may overlap (and/or may be aligned with) the sidewall of the second cavity in a direction perpendicular to the side of the second substrate.
According to embodiments of the invention, a substrate (e.g., a semiconductor substrate) may include a reflective surface oriented at 45 degrees or approximately 45 degrees with respect to at least one of a bottom side of the substrate, an intended light incident direction, and an intended light reflection direction. Advantageously, the substrate may enable substantially efficient photonic connection (e.g., through a TSPV) and/or may enable a relatively simple connection structure in a related device (e.g., a semiconductor device that includes the substrate). Semiconductor devices (and related electronic devices) according to embodiments of the invention may have more efficient connections (or coupling) and/or may have simpler structures than well-known semiconductor devices (and related electronic devices).
The above summary is related to one or more of many embodiments of the invention disclosed herein and is not intended to limit the scope of the invention.
Example embodiments of the present invention are described with reference to the accompanying drawings. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present invention. Embodiments of the present invention may be practiced without some or all of these specific details. Well known process steps and/or structures may not have been described in detail in order to not unnecessarily obscure the present invention.
The drawings and description are illustrative and not restrictive. Like reference numerals may designate like (e.g., analogous or identical) elements in the specification. Repetition of description may be avoided.
The relative sizes and thicknesses of elements shown in the drawings are for facilitate description and understanding, without limiting the present invention. In the drawings, the thicknesses of some layers, films, panels, regions, etc., may be exaggerated for clarity.
Illustrations of example embodiments in the figures may represent idealized illustrations. Variations from the shapes illustrated in the illustrations, as a result of, for example, manufacturing techniques and/or tolerances, may be possible. Thus, the example embodiments should not be construed as limited to the shapes or regions illustrated herein but are to include deviations in the shapes. For example, an etched region illustrated as a rectangle may have rounded or curved features. The shapes and regions illustrated in the figures are illustrative and should not limit the scope of the example embodiments.
Although the terms “first”, “second”, etc. may be used herein to describe various elements, these elements, should not be limited by these terms. These terms may be used to distinguish one element from another element. Thus, a first element discussed below may be termed a second element without departing from the teachings of the present invention. The description of an element as a “first” element may not require or imply the presence of a second element or other elements. The terms “first”, “second”, etc. may also be used herein to differentiate different categories or sets of elements. For conciseness, the terms “first”, “second”, etc. may represent “first-category (or first-set)”, “second-category (or second-set)”, etc., respectively.
If a first element (such as a layer, film, region, or substrate) is referred to as being “on”, “neighboring”, “connected to”, or “coupled with” a second element, then the first element can be directly on, directly neighboring, directly connected to, or directly coupled with the second element, or an intervening element may also be present between the first element and the second element. If a first element is referred to as being “directly on”, “directly neighboring”, “directly connected to”, or “directed coupled with” a second element, then no intended intervening element (except environmental elements such as air) may also be present between the first element and the second element.
Spatially relative terms, such as “beneath”, “below”, “lower”, “above”, “upper”, and the like, may be used herein for ease of description to describe one element or feature's spatial relationship to another element(s) or feature(s) as illustrated in the figures. It will be understood that the spatially relative terms may encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. For example, if the device in the figures is turned over, elements described as “below” or “beneath” other elements or features would then be oriented “above” the other elements or features. Thus, the term “below” can encompass both an orientation of above and below. The device may be otherwise oriented (rotated 90 degrees or at other orientations), and the spatially relative descriptors used herein should be interpreted accordingly.
The terminology used herein is for the purpose of describing particular embodiments and is not intended to limit the invention. As used herein, the singular forms, “a”, “an”, and “the” may indicate plural forms as well, unless the context clearly indicates otherwise. The terms “includes” and/or “including”, when used in this specification, may specify the presence of stated features, integers, steps, operations, elements, and/or components, but may not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups.
Unless otherwise defined, terms (including technical and scientific terms) used herein have the same meanings as commonly understood by one of ordinary skill in the art related to this invention. Terms, such as those defined in commonly used dictionaries, should be interpreted as having meanings that are consistent with their meanings in the context of the relevant art and should not be interpreted in an idealized or overly formal sense unless expressly so defined herein.
The term “connect” may mean “electrically connect”. The term “insulate” may mean “electrically insulate”. The term “conductive” may mean “electrically conductive”
Unless explicitly described to the contrary, the word “comprise” and variations such as “comprises”, “comprising”, “include”, or “including” may imply the inclusion of stated elements but not the exclusion of other elements.
Various embodiments, including methods and techniques, are described in this disclosure. Embodiments of the invention may also cover an article of manufacture that includes a non-transitory computer readable medium on which computer-readable instructions for carrying out embodiments of the inventive technique are stored. The computer readable medium may include, for example, semiconductor, magnetic, opto-magnetic, optical, or other forms of computer readable medium for storing computer readable code. Further, the invention may also cover apparatuses for practicing embodiments of the invention. Such apparatus may include circuits, dedicated and/or programmable, to carry out operations pertaining to embodiments of the invention. Examples of such apparatus include a general purpose computer and/or a dedicated computing device when appropriately programmed and may include a combination of a computer/computing device and dedicated/programmable hardware circuits (such as electrical, mechanical, and/or optical circuits) adapted for the various operations pertaining to embodiments of the invention.
The first device member may include a first substrate 104, which may have a first cavity 107. A sidewall 103 of the first cavity 107 may be oriented at a first angle with respect to at least one of a side (e.g., a top side) of the first substrate, a bottom surface of the first cavity 107, a transmission direction of a light transmitted in the first cavity 107, and a transmission direction of a light transmitted between the first device member 110 and the second device member 120. The sidewall 103 may be reflective and/or may have a reflective coating. The first angle may be 45 degrees or may be approximately 45 degrees, e.g., in a range of 44.5 degrees to 45.5 degrees.
The first device member 110 may include the following elements: a first anti-reflection layer 101 positioned on the bottom surface of the first cavity 107; a semiconductor material member positioned inside the first cavity; and a second anti-reflection layer 102 positioned on the semiconductor material member. The anti-reflection layers and the semiconductor material member may facilitate efficient transmission of light in the first cavity 107.
The second device member 120 may include a second substrate 109, which may overlap the first substrate 107 and may have a second cavity 108. A sidewall 105 of the second cavity may be oriented at a second angle with respect to at least one of a side (e.g., a bottom side) of the second substrate, a bottom surface of the second cavity 108, a transmission direction of a light transmitted in the second cavity 108, and a transmission direction of a light transmitted between the first device member 110 and the second device member 120. The sidewall 105 may be reflective and/or may have a reflective coating. The second angle may be 45 degrees or may be approximately 45 degrees, e.g., in a range of 44.5 degrees to 45.5 degrees. The sidewall 103 of the first cavity 107 may overlap (and/or may be aligned with) the sidewall 105 of the second cavity 109 in a direction perpendicular to the side (e.g., the bottom side) of the second substrate.
The second device member 102 may include anti-reflection layers and a semiconductor material member, e.g., analogous to those included in the first device member 101, for facilitating efficient light transmission in the second cavity 108.
Given the substantially 45-degree orientation of each of the sidewall 103 and sidewall 105, efficient coupling (or connection) between the first device member 110 and the second device member 120 may be enabled without requiring very complicated transmission structure and/or may additional components.
A method for manufacturing the device illustrated in
Each of the first angle and the second angle may be 45 degrees or may approximate 45 degrees, e.g., in a range of 44.5 degrees to 45.5 degrees.
A method for forming the first substrate 104 and/or a method for forming the second substrate 109 may include some steps and features that may be analogous to some steps and features discussed below with reference to one or more of
A method for manufacturing the device illustrated in
Referring to
Referring to
The first angle B may be affected by the crystal structure in the substrate material member 201. In an embodiment, the substrate material member 201 may be a silicon member. Being affected by an angle between two crystallographic planes in the crystal structure of the silicon member, the first angle B may be 54.74 degrees or approximately 54.74 degrees. Given the influence of various process variables in forming the first cavity, the value of the first angle B may deviate from the 54.74 value. For example, the deviation may be in a range of −1 degree to 1 degree. The first angle B may be in a range of 54 degrees to 56 degrees.
A process for forming the first remaining portion of the substrate material member 201 may include the following steps: providing a mask material layer on the substrate material member 201; providing a photoresist layer 203 on the mask material layer, wherein the photoresist layer may have a first pattern (which may affect the shape and position of the first cavity); etching (e.g., through dry etching and/or wet etching) the mask material layer when the photoresist layer is positioned on the mask material layer to form a mask 202 that may have a second patter, wherein the second pattern may be similar to or identical to the first pattern (and may affect the shape and position of the first cavity); and etching the substrate material member 201 when the mask 202 is positioned on the substrate material layer to form the first cavity.
The mask material layer may be formed of one or more of amorphous silicon, silicon oxynitride, silicon oxide, doped silicon oxide, silicon carbide, silicon nitride, titanium, and titanium oxide. The thickness of the mask 202 (in a direction perpendicular to bottom surface of the substrate material member 201) may be in a range of 10 nm to 100 nm.
In an embodiment, the mask material layer may be formed of silicon oxide, and a SiConi™ etching process may be performed on the mask material layer to form the mask 202.
A wet-etching process with a TMAH (tetramethyl ammonium hydroxide) solution may be used for etching the substrate material member 201 to form the first cavity. The mass fraction of the TMAH in the TMAH solution may be in a range of 0.1% to 10%. The wet-etching process may be performed at a temperature that is in a range of 25 degrees Celsius to 90 degrees Celsius for a time duration that that is in a range of 10 seconds to 1000 seconds.
After the first cavity has been formed, the mask 202 may be removed. An etching process with substantial etch selectivity may be used for removing the mask 202, for substantially preventing damage to the first cavity and/or the first remaining portion of the substrate material member 201.
Referring to
The sacrificial material member 204 may be formed of a wet-developable material. The sacrificial material member 204 may be formed of a cross-linked resin that may include one or more of the following elements: an organic solvent that may include at least one of a ketone, an ether, and an alkane; an anti-reflection material; an organic acid group resin that may be reactive to a standard tetramethyl ammonium hydroxide developer solution; and an organic group resin that may include at least one of oxygen and fluorine. A molecular weight of the sacrificial material member 204 may be in a range of 1000 to 50,000. A refractive index of the sacrificial material member 204 may be in a range of 1.0 to 3.0. An extinction coefficient of the sacrificial material member 204 may be in a range of 0.1 to 3.0.
A process for forming the sacrificial material layer may include the following steps: providing a set of sacrificial material that may include a first coating of sacrificial material and covers the first remaining portion of the substrate material member 201; determining whether the set of sacrificial material satisfy a set of planarization requirements; if the set of planarization requirements is satisfied, planarizing the set of sacrificial material to form the sacrificial material member 204, such that a top surface of the sacrificial material member 204 and a top surface of the first remaining portion of the substrate material member 201 are in a same plane; and if the set of planarization requirements is not satisfied, providing an additional coating of sacrificial material that covers the first remaining portion of the substrate material member 201. One or more of these steps may be repeated if the set of planarization requirements is not satisfied.
The method may include performing a heating process (e.g., a baking process) on the first coating of sacrificial material (and/or each additional coating of sacrificial material) after providing the first coating of sacrificial material (and/or each additional coating of sacrificial material) on the first remaining portion of the substrate material member 201. The sacrificial material amount of the first coating of sacrificial material may be in a range of 0.5 milliliter to 5 milliliters. The heating process may be performed at a temperature that is in a range of 60 degrees Celsius to 250 degrees Celsius for a time duration that is in a range of 10 seconds to 120 seconds.
In an embodiment, in forming the sacrificial material member 204, an excess portion of the sacrificial material may be removed through wet-development.
Referring to
The second angle A may be 45 degrees or approximately 45 degrees. Because of variables in the processing, the second angle A may be in a range of 44.5 degrees to 45.5 degrees. A length of the sidewall of the second cavity may be in a range of 3 microns to 15 microns.
An etching process (e.g., a blank dry etching process without using a mask) may be performed to remove the sacrificial material member 204 and to form the second remaining portion of the substrate material member 201. In the etching process, a ratio of an etch rate of the sacrificial material member 204 to an etch rate of the first remaining portion of the substrate material member 201 may be 3.4 or approximately 3.4, e.g., in a range of 3.3 to 3.5.
The method may include determining the ratio (or etch selectivity) for the etching process based on (the value of) the first angle B. As can be appreciated from
In an embodiment, the first angle B may be 54.74 degrees. Therefore, Tangent(54.74 degrees)=H/(H−h), such that the etch selectivity (H/h) for the etching process may be equal to Tangent(54.74 degrees)/[Tangent(54.74 degrees)−1], which is approximately 3.4.
The method may include selecting the material for the sacrificial material element 204 and/or the etchant based on the etch selectivity value (e.g., approximately 3.4).
The method may include using the first angle B and the height H of the sacrificial material member 204 to determine the target depth (H−h) for the second cavity 201. The target depth (H−h) of the second cavity may be set as the height H of the sacrificial material member 204 divided by the tangent of the first angle B. In an embodiment, the first angle B may be in a range of 54 degrees to 56 degrees, and a ratio of the height H of the sacrificial material member to the target depth (H−h) of the second cavity may be in a range of about 1.37 to about 1.49. In an embodiment, the first angle B may be about 54.74 degrees (approximating an angle between two crystallographic planes in the substrate material), and the target depth (H−h) of the second cavity may be set as the height H of the sacrificial material member 204 divided by the tangent of 54.74 degrees (which may be about 1.414).
The method may include fine-tuning the etching process to make the second angle A substantially equal to 45 degrees.
The etching process may be a dry etching process, such as a blank dry etching process involving no masks. The etching process may be performed using nitrogen (N2) as an etching atmosphere. One or more other suitable gasses, such as one or more of carbon tetrafluoride (CF4), carbon dioxide (CO2), and oxygen (O2), of suitable amount(s) may be included in the etching atmosphere. For the etching process, the pressure may be in a range of 50 mTorr to 200 mTorr, such as a pressure in a range of 100 mTorr to 150 mTorr; the power may be in a range of 200 W to 600 W; the time duration may be in a range of 5 seconds to 80 seconds, such as a time duration in a range of 10 seconds to 60 seconds. The gas flow for the etching process may be sufficiently large. In an embodiment, a nitrogen (N2) gas flow for the etching process may be in a range of 30 sccm to 300 sccm. In an embodiment, a nitrogen (N2) gas flow for the etching process may be in a range of 50 sccm to 100 sccm.
The method may include the following steps: providing a first anti-reflection layer (analogous to the anti-reflection layer 101 illustrated in
A substrate manufactured according to an embodiment of the invention may include the second remaining portion of the substrate material member. The substrate may include the first anti-reflection layer, the second anti-reflection layer, and the semiconductor material member. The substrate may be used in a device such as the device discussed with reference to at least one of
According to embodiments of the invention, a substrate (e.g., a semiconductor substrate) may include a reflective surface oriented at 45 degrees or approximately 45 degrees with respect to at least one of a bottom side of the substrate, an intended light incident direction, and an intended light reflection direction. Advantageously, the substrate may enable efficient connection (e.g., through a TSPV) and/or may enable a relatively simple connection structure in a related device (e.g., a semiconductor device that includes the substrate). Semiconductor devices (and related electronic devices) according to embodiments of the invention may have satisfactorily efficient connections (or coupling) and/or may have satisfactorily simple structures.
While this invention has been described in terms of several embodiments, there are alterations, permutations, and equivalents, which fall within the scope of this invention. It should also be noted that there are many alternative ways of implementing the methods and apparatuses of the present invention. Furthermore, embodiments of the present invention may find utility in other applications. The abstract section is provided herein for convenience and, due to word count limitation, is accordingly written for reading convenience and should not be employed to limit the scope of the claims. It is therefore intended that the following appended claims be interpreted as including all such alterations, permutations, and equivalents as fall within the true spirit and scope of the present invention.
Number | Date | Country | Kind |
---|---|---|---|
201310753545.5 | Dec 2013 | CN | national |