Wafer-level fan-out package with enhanced performance

Abstract

The present disclosure relates to a wafer-level fan-out package that includes a first thinned die, a second die, a multilayer redistribution structure underneath the first thinned die and the second die, a first mold compound over the second die, a second mold compound over the multilayer redistribution structure, and around the first thinned die and the second die, and a third mold compound. The second mold compound extends beyond the first thinned die to define an opening within the second mold compound and over the first thinned die, such that a top surface of the first thinned die is at a bottom of the opening. A top surface of the first mold compound and a top surface of the second mold compound are coplanar. The third mold compound fills the opening and is in contact with the top surface of the first thinned die.

Description

FIELD OF THE DISCLOSURE

The present disclosure relates to a wafer-level fan-out (WLFO) package and a process for making the same, and more particularly to a WLFO package with enhanced thermal, electrical, and rigidity performance, and a packaging process to enhance thermal, electrical, and rigidity performance of a WLFO package.

BACKGROUND

The wide utilization of cellular and wireless devices drives the rapid development of radio frequency (RF) technologies. The substrates on which RF devices are fabricated play an important role in achieving high level performance in the RF technologies. Fabrications of the RF devices on conventional silicon substrates may benefit from low cost of silicon materials, a large scale capacity of wafer production, well-established semiconductor design tools, and well-established semiconductor manufacturing techniques.

Despite the benefits of using conventional silicon substrates for RF device fabrication, it is well known in the industry that the conventional silicon substrates may have two undesirable properties for the RF devices: harmonic distortion and low resistivity values. Harmonic distortion is a critical impediment for achieving high level linearity in the RF devices built over silicon substrates. In addition, the low resistivity encountered in the silicon substrates may degrade quality factors (Q) at high frequencies of microelectromechanical systems (MEMS) or other passive components.

Further, high speed and high performance transistors are more densely integrated in RF devices, even as they are required to carry more power. Consequently, the amount of heat generated by the RF devices will increase significantly due to the large amount of power passing through the transistors, the large number of transistors integrated in the RF devices, and the high operation speed of the transistors. Accordingly, it is desirable to package the RF devices in a configuration for better heat dissipation.

Wafer-level fan-out (WLFO) packaging technology and embedded wafer-level ball grid array (EWLB) technology currently attract substantial attention in portable RF applications. WLFO and EWLB technologies are designed to provide high density input/output ports (I/O) as well as low profile package height without increasing the size of the component semiconductor chips. The I/O pad size on the chip remains small keeping die size to a minimum. This capability allows for densely packaging the RF devices within a single wafer.

To accommodate the increased heat generation of the RF devices, to reduce deleterious harmonic distortion and quality factor losses of the silicon substrate, and to utilize advantages of WLFO/EWLB packaging technologies, it is therefore an object of the present disclosure to provide a packaging process for a wafer-level fan-out (WLFO) package with enhanced thermal and electrical performance.

SUMMARY

The present disclosure relates to a wafer-level fan-out (WLFO) package with enhanced thermal, electrical, and rigidity performance, and a packaging process to enhance thermal, electrical, and rigidity performance of the WLFO package. The disclosed WLFO package includes a first thinned die, a second die, a multilayer redistribution structure, a first mold compound, a second mold compound, and a third mold compound. The first thinned die includes a first device layer, a first dielectric layer over the first device layer, and a number of first die bumps underneath the first device layer. The second die includes a second device layer, a silicon substrate over the second device layer, and a number of second die bumps underneath the second device layer. The first thinned die and the second die reside over the multilayer redistribution structure. The multilayer redistribution structure includes a number of package contacts on a bottom surface of the multilayer redistribution structure and redistribution interconnections that connect the package contacts to certain ones of the first die bumps and certain ones of the second die bumps. The first mold compound resides over the silicon substrate of the second die. The second mold compound resides over the multilayer redistribution structure, resides around and underneath the first thinned die, and resides around and underneath the second die. Herein, the second mold compound extends beyond a top surface of the first thinned die to define an opening within the second mold compound and over the first thinned die. The top surface of the first thinned die is at a bottom of the opening. A top surface of the first mold compound and a top surface of the second mold compound are coplanar. The third mold compound fills the opening and is in contact with the top surface of the first thinned die.

In one embodiment of the WLFO package, the redistribution interconnections electrically connect the first thinned die and the second die. Herein, the first thinned die provides a microelectromechanical systems (MEMS) component and the second die provides a complementary metal-oxide-semiconductor (CMOS) controller that controls the MEMS component.

In one embodiment of the WLFO package, the first thinned die is formed from a silicon-on-insulator (SOI) structure, wherein the first device layer of the first thinned die is formed from a silicon layer of the SOI structure, and the first dielectric layer of the first thinned die is a buried oxide layer of the SOI structure.

In one embodiment of the WLFO package, the third mold compound has an electrical resistivity greater that 1E6 Ohm-cm.

In one embodiment of the WLFO package, the third mold compound has a thermal conductivity greater than 2 W/m·K.

In one embodiment of the WLFO package, the third mold compound has a thermal conductivity greater than 10 W/m·K.

In one embodiment of the WLFO package, the first mold compound, the second mold compound, and the third mold compound are formed from different materials.

In one embodiment of the WLFO package, the first mold compound and the second mold compound are formed from a same material.

In one embodiment of the WLFO package, the top surface of the first thinned die at the bottom of the opening is a top surface of the first dielectric layer.

In one embodiment of the WLFO package, the multilayer redistribution structure is glass-free, connections between the redistribution interconnections and the first die bumps are solder-free, and connections between the redistribution interconnections and the second die bumps are solder-free.

In one embodiment of the WLFO package, a portion of the third mold compound resides over the first mold compound and the second mold compound.

In one embodiment of the WLFO package, the top surface of the first mold compound, the top surface of the second mold compound, and a top surface of the third mold compound are coplanar.

According to another embodiment, the WLFO package further includes a fourth mold compound, which resides over the top surface of the first mold compound, the top surface of the second mold compound, and the top surface of the third mold compound.

In one embodiment of the WLFO package, the first mold compound, the second mold compound, and the fourth mold compound are formed from a same material.

In one embodiment of the WLFO package, a periphery of the first mold compound and a periphery of the silicon substrate of the second die are coincident.

According to an exemplary process, a mold package that includes a first die, a second die, a first mold compound, and a second mold compound is firstly provided. Herein, the first die includes a first device layer, a first dielectric layer over the first device layer, a first silicon substrate over the first dielectric layer, and a number of first die bumps underneath the first device layer. The second die includes a second device layer, a second silicon substrate over the second device layer, and a number of second die bumps underneath the second device layer. The first mold compound resides over the silicon substrate of the second die. The second mold compound resides around and underneath the first die and the second die, such that the second mold compound covers sidewalls and a bottom surface of the first die, covers sidewalls and a bottom surface of the second die, covers sidewalls of the first mold compound, and encapsulates the first die bumps and the second die bumps, wherein a top surface of the first mold compound, a top surface of the second mold compound, and a backside of the first silicon substrate are coplanar. Next, the first silicon substrate is substantially removed to provide a first thinned die and form an opening, which is within the first mold compound and over the first thinned die. The first thinned die has a top surface exposed at a bottom of the opening. A third mold compound is then applied to substantially fill the opening and directly contact the top surface of the first thinned die. After the third mold compound is applied, the second mold compound is thinned to expose each first die bump and each second die bump. Lastly, a multilayer redistribution structure is formed underneath the second mold compound. The multilayer redistribution structure includes a number of package contacts on a bottom surface of the multilayer redistribution structure and redistribution interconnections that connect the package contacts to certain ones of the first die bumps and certain ones of the second die bumps.

In one embodiment of the exemplary process, the third mold compound is applied by a compression molding process.

In one embodiment of the exemplary process, a molding pressure used for applying the third mold compound is lower than 1000 psi.

In one embodiment of the exemplary process, providing the mold package starts with placing the first die and a mold die on a mold tape. Herein, the mold die includes the second die and the first mold compound over the second die. The first silicon substrate of the first die and the first mold compound of the mold die are in contact with the mold tape, and the first die bumps and the second die bump are placed upward. The second mold compound is then applied over the mold tape to encapsulate the first die and the mold die. Next, the mold tape is removed to provide a precursor package, such that a portion of the first mold compound and a portion of the first silicon substrate are exposed. After flipping the precursor package, the first die bumps and the second die bumps are downward and encapsulated by the second mold compound. No portion of the second mold compound extends above the first silicon substrate of the first die and the first mold compound. A top surface of the precursor package is planarized to provide the mold package, such that the top surface of the first mold compound, the top surface of the second mold compound, and the backside of the first silicon substrate are coplanar.

In one embodiment of the exemplary process, before placing the first die and the combination of the second die and the first mold compound on the mold tape, a thickness of the first die and a thickness of the combination of the second die and the first mold compound are the same.

Those skilled in the art will appreciate the scope of the present disclosure and realize additional aspects thereof after reading the following detailed description of the preferred embodiments in association with the accompanying drawing figures.

BRIEF DESCRIPTION OF THE DRAWING FIGURES

The accompanying drawing figures incorporated in and forming a part of this specification illustrate several aspects of the disclosure, and together with the description serve to explain the principles of the disclosure.

FIG. 1 shows an exemplary wafer-level fan-out (WLFO) package according to one embodiment of the present disclosure.

FIGS. 2-10 provide exemplary steps that illustrate a process to fabricate a mold package according to one embodiment of the present disclosure.

FIGS. 11-16 illustrate the steps to provide the WLFO package shown in FIG. 1 from the mold package shown in FIG. 10

It will be understood that for clarity of illustration, FIGS. 1-16 may not be drawn to scale.

DETAILED DESCRIPTION

The embodiments set forth below represent the necessary information to enable those skilled in the art to practice the embodiments and illustrate the best mode of practicing the embodiments. Upon reading the following description in light of the accompanying drawing figures, those skilled in the art will understand the concepts of the disclosure and will recognize applications of these concepts not particularly addressed herein. It should be understood that these concepts and applications fall within the scope of the disclosure and the accompanying claims.

It will be understood that, although the terms first, second, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another. For example, a first element could be termed a second element, and, similarly, a second element could be termed a first element, without departing from the scope of the present disclosure. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.

It will be understood that when an element such as a layer, region, or substrate is referred to as being “on” or extending “onto” another element, it can be directly on or extend directly onto the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or extending “directly onto” another element, there are no intervening elements present. Likewise, it will be understood that when an element such as a layer, region, or substrate is referred to as being “over” or extending “over” another element, it can be directly over or extend directly over the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly over” or extending “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.

Relative terms such as “below” or “above” or “upper” or “lower” or “horizontal” or “vertical” may be used herein to describe a relationship of one element, layer, or region to another element, layer, or region as illustrated in the Figures. It will be understood that these terms and those discussed above are intended to encompass different orientations of the device in addition to the orientation depicted in the Figures.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes,” and/or “including” when used herein specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.

Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms used herein should be interpreted as having a meaning that is consistent with their meaning in the context of this specification and the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

The present disclosure relates to a wafer-level fan-out (WLFO) package with enhanced thermal, electrical, and rigidity performance, and a packaging process for making the same. FIG. 1 shows an exemplary WLFO package 10 according to one embodiment of the present disclosure. For the purpose of this illustration, the exemplary WLFO package 10 includes a first thinned die 12T, a second die 14, a multilayer redistribution structure 16, a first mold compound 18, a second mold compound 20, and a third mold compound 22. In different applications, the WLFO package 10 may include fewer or more dies. For instance, in some applications, the WLFO package 10 may include the first thinned die 12, while the second die 14 is omitted. In some applications, the WLFO package 10 may include multiple first thinned dies 12 without the second die 14. In some applications, the WLFO package 10 may include the multiple first thinned dies 12T and one second die 14. In some applications, the WLFO package 10 may include the multiple first thinned dies 12T and multiple second dies 14. In some applications, besides the first thinned die 12T and the second die 14, the WLFO package 10 may include some integrated passive device dies (not shown).

In detail, the first thinned die 12T includes a first device layer 24, a first dielectric layer 26 over the first device layer 24, and a number of first die bumps 28 underneath the first device layer 24. In one embodiment, the first thinned die 12T may be formed from a silicon-on-insulator (SOI) structure, which refers to a structure including a silicon substrate, a silicon layer, and a buried oxide layer sandwiched between the silicon substrate and the silicon layer. The first device layer 24 of the first thinned die 12T may be formed by integrating electronic components (not shown) in or on the silicon layer of the SOI structure. The first dielectric layer 26 of the first thinned die 12T may be the buried oxide layer of the SOI structure. In addition, the silicon substrate of the SOI structure is removed substantially to complete the first thinned die 12T (more details in the following discussion). Herein, the first device layer 24 may have a thickness between 0.1 μm and 50 μm, the first dielectric layer 26 may have a thickness between 10 nm and 2000 nm, and each first die bump 28 may have a thickness between 5 μm and 200 μm. A total thickness of the first thinned die 12T may be between 5 μm and 260 μm.

In another embodiment, the first thinned die 12T may provide a microelectromechanical systems (MEMS) component (not shown) which is typically a switch and within the first device layer 24. Herein, the first device layer 24 may have a thickness between 0.5 μm and 100 μm, and may be formed from a combination of dielectric and metal layers (such as silicon oxide, silicon nitride, aluminum, titanium, copper, or the like). The first dielectric layer 26 may have a thickness between 10 nm and 10000 nm, and may be formed from silicon oxide, silicon nitride, aluminum oxide, or aluminum nitride. Each first die bump 28 may have a thickness between 5 μm and 200 μm, and a total thickness of the first thinned die 12T may be between 5 μm and 310 μm.

Notice that the first thinned die 12T has essentially no silicon substrate over the first dielectric layer 26. Herein, essentially no silicon substrate over the first dielectric layer 26 refers to at most 2 μm silicon substrate over the dielectric layer. In desired cases, the first thinned die 12T does not include any silicon substrate over the first dielectric layer 26, such that a top surface of first thinned die 12T is a top surface of the first dielectric layer 26. For other cases, the top surface of the first thinned die 12T may be a top surface of the thin silicon substrate.

The second die 14 includes a second device layer 30, a second silicon substrate 32 over the second device layer 30, and a number of second die bumps 34 underneath the second device layer 30. If the first thinned die 12T provides a MEMS component, the second die 14 may provide a complementary metal-oxide-semiconductor (CMOS) controller (not shown) that is within the second device layer 30 and controls the MEMS component within the first thinned die 12T. Herein, the second die 14 may have a thickness between 25 μm and 250 μm or between 10 μm and 750 μm, and the second silicon substrate 32 may have a thickness between 25 μm and 250 μm or between 10 μm and 750 μm, respectively. The second device layer 30 may have a thickness between 0.1 μm and 50 μm, and may be formed from a combination of dielectric and metal layers (such as silicon oxide, silicon nitride, aluminum, titanium, copper, or the like). In addition, if the first thinned die 12T does not provide a MEMS component and is formed from a SOI structure, the second die 14 may be omitted.

Herein, the first thinned die 12T and the second die 14 reside over the multilayer redistribution structure 16, which includes a number of redistribution interconnections 36, a dielectric pattern 38, and a number of package contacts 40. For the purpose of this illustration, the redistribution interconnections 36 include three first redistribution interconnections 36(1) and one second redistribution interconnection 36(2). In different applications, the redistribution interconnections 36 may include fewer or more first redistribution interconnections 36(1)/second redistribution interconnections 36(2). Each first redistribution interconnection 36(1) is configured to connect one package contact 40 to a corresponding one of the first and second die bumps 28 and 34. The second redistribution interconnection 36(2) is configured to connect one first die bump 28 to a corresponding second die bump 34, such that the first thinned die 12T is electrically connected to the second die 14. The connections between the redistribution interconnections 36 and the first/second die bumps 28 and 34 are solder-free.

The dielectric pattern 38 is formed around and underneath each redistribution interconnection 36. Herein, a bottom portion of each first redistribution interconnection 36(1) is exposed through the dielectric pattern 38, while the second redistribution interconnection 36(2) is fully encapsulated by the dielectric pattern 38. In different applications, there may be extra redistribution interconnections (not shown) electrically coupled to the first redistribution interconnections 36(1) through the dielectric pattern 38, and extra dielectric patterns (not shown) formed underneath the dielectric pattern 38, such that a bottom portion of each extra redistribution interconnection is exposed.

In this embodiment, each package contact 40 is formed at a bottom of the multilayer redistribution structure 16 and electrically coupled to a corresponding first redistribution interconnection 36(1) through the dielectric pattern 38. Consequently, the first redistribution interconnections 36(1) connect the package contacts 40 to certain ones of the first and second die bumps 28 and 34. In addition, the package contacts 40 are separate from each other and extend underneath the dielectric pattern 38.

The multilayer redistribution structure 16 may be free of glass fiber or glass-free. Herein, the glass fiber refers to individual glass strands twisted to become a larger grouping. These glass strands may then be woven into a fabric. The dielectric pattern 38 may be formed of benzocyclobutene (BCB), polyimide, or other dielectric materials. The redistribution interconnections 36 may be formed of copper or other suitable metals. The package contacts 40 may be formed of at least one of copper, gold, nickel, and palladium. The multilayer redistribution structure 16 may have a thickness between 2 μm and 300 μm.

The first mold compound 18 resides over the second silicon substrate 32 of the second die 14. A periphery of the first mold compound 18 and a periphery of the second silicon substrate 32 are coincident. The first mold compound 18 may be an organic epoxy resin system or the like, which can be used as an etchant barrier to protect the second die 14 against etching chemistries (more details in the following discussion), such as potassium hydroxide (KOH), sodium hydroxide (NaOH), and acetylcholine (ACH).

The second mold compound 20 resides over the multilayer redistribution structure 16, resides around and underneath the first thinned die 12T, and resides around and underneath the second die 14. Herein, the second mold compound 20 covers a bottom surface of the first device layer 24 and a bottom surface of the second device layer 30, and encapsulates the first die bumps 28 and the second die bumps 24. In addition, the second mold compound 20 covers side walls of the first thinned die 12T and extends vertically beyond a top surface of the first thinned die 12T to define an opening 42 within the second mold compound 20 and over the first thinned die 12T. The top surface of the first thinned die 12T is at a bottom of the opening 42. If the first thinned die 12T does not include any silicon substrate over the first dielectric layer 26, the top surface of the first dielectric layer 26 is at the bottom of the opening 42. If the first thinned die 12T includes a thin silicon substrate (<2 μm thickness) over the first dielectric layer 26, the thin silicon substrate is at the bottom of the opening 42 (not shown). Further, the second mold compound covers side walls of the second die 14 and side walls of the first mold compound 18, such that a top surface of the first mold compound 18 and a top surface of the second mold compound 20 are coplanar. The second mold compound 20 may be formed of a same material as the first mold compound 18, such as an organic epoxy resin system or the like. The second mold compound 20 may be used as an etchant barrier to protect the first thinned die 12T and the second die 14 against etching chemistries (more details in the following discussion).

The third mold compound 22 substantially fills the opening 42, and is in contact with the top surface of the first thinned die 12T. Herein, substantially filling an opening refers to filling at least 75% of the entire opening. If there is no silicon substrate left in the opening 42, the third mold compound 22 will directly reside over the first dielectric layer 26. In some cases, a portion of the third mold compound 22 may further reside over the first and second mold compounds 18 and 20. The third mold compound 22 is separated from the second die 14 by the first mold compound 18. A top surface of the second die 14 is only in contact with the first mold compound 18.

The third mold compound 22 has a thermal conductivity greater than 2 W/m·K or greater than 10 W/m·K, and has an electrical resistivity greater than 1E6 Ohm-cm. In general, the higher the thermal conductivity of the third mold compound 22, the better the thermal performance of the first thinned die 12T. Further, the high electrical resistivity of the third mold compound 22 may improve the quality factor (Q) at high frequencies of the MEMS component provided in the first thinned die 12T, or may reduce signal loss in the first thinned die 12T if formed from an SOI structure.

The third mold compound 22 may be formed of thermoplastics or thermoset materials, such as PPS (poly phenyl sulfide), overmold epoxies doped with boron nitride or alumina thermal additives, or the like. The first, second, and third mold compounds 18, 20, and 22 may be formed of a same material or different materials. For instance, the first mold compound 18 and the second mold compound 20 may be formed from a same material, while the third mold compound 22 is formed from a different material. Unlike the third mold compound 22, the first and second mold compounds 18 and 20 do not have thermal conductivity requirements.

FIGS. 2-16 provide exemplary steps to fabricate the WLFO package 10 shown in FIG. 1. Although the exemplary steps are illustrated in a series, the exemplary steps are not necessarily order dependent. Some steps may be done in a different order than that presented. Further, processes within the scope of this disclosure may include fewer or more steps than those illustrated in FIGS. 2-16.

FIGS. 2-10 provide exemplary steps to fabricate a mold package, which is used to manufacture the WLFO package 10. Initially, a first die 12, and a wafer 44 with a number of second intact dies 14D are provided, as illustrated in FIG. 2. The first die 12 includes the first device layer 24, the first dielectric layer 26 over the first device layer 24, the first die bumps 28 underneath the first device layer 24, and a first silicon substrate 46 over the first dielectric layer 26. In one embodiment, the first die 12 may be formed from a SOI structure. The first device layer 24 of the first die 12 may be formed by integrating electronic components (not shown) in or on the silicon layer of the SOI structure. The first dielectric layer 26 of the first die 12 may be the buried oxide layer of the SOI structure. The first silicon substrate 46 of the first die 12 may be the silicon substrate of the SOI structure. Herein, the first die 12 (including the first die bumps 28) may have a total thickness T1 between 25 μm and 250 μm or between 10 μm and 750 μm, and the first silicon substrate 46 may have a thickness between 25 μm and 250 μm or between 10 μm and 750 μm, respectively.

In another embodiment, the first die 12 may provide a MEMS component (not shown), which is typically a switch and within the first device layer. Herein, the first die 12 (including the first die bumps 28) may have the thickness T1 between 25 μm and 300 μm or between 10 μm and 800 μm, and the first silicon substrate 46 may have a thickness between 25 μm and 300 μm or between 10 μm and 800 μm, respectively.

For the purpose of this illustration, the wafer 44 includes three second intact dies 14D. In different applications the wafer 44 may include fewer or more second intact dies 14D. Each second intact die 14D includes the second device layer 30, the second silicon substrate 32 over the second device layer 30, and the second die bumps 34 underneath the second device layer 30. The second device layer 30 from each second intact die 14D is formed from a common device layer 30C, while the second silicon substrate 32 from each second intact die 14D is formed from a common substrate 32C. Herein, the wafer 44 as well as each second intact die 14D (including the second die bumps 28) may have a thickness T2 between 10 μm and 750 μm, and the second silicon substrate 32 may have a thickness between 10 μm and 750 μm.

Herein, if the thickness T2 of the wafer 44 is thicker than the thickness T1 of the first die 12, a first thinning process is applied to the common substrate 32C to provide a thinned wafer 44T with a number of second dies 14, as shown in FIG. 3. The common substrate 32C is thinned down, until a thickness T3 of the thinned wafer 44T as well as each second die 14 (including the second die bumps 34) is thinner than the thickness T1 of the first die 12. Typically, each second die 14 still includes the second silicon substrate 32 and the thickness T3 may be between 10 μm and 750 μm. The remaining second silicon substrate 32 of each second die 14 may have a thickness between 10 μm and 750 μm. In a desired case, a difference between the thickness T1 of the first die 12 and the thickness T3 of the second die 14 may be between 2 μm and 100 μm. The first thinning process may be provided by a mechanical grinding process. If the thickness T2 of the wafer 44 is thinner than the thickness T1 of the first die 12, the first thinning step of the common substrate 32C may be omitted.

Next, the first mold compound 18 is applied over the remaining common substrate 32C to provide a mold wafer 48, as illustrated in FIG. 4. The first mold compound 18 may be an organic epoxy resin system or the like, and may be applied by various procedures, such as sheet molding, overmolding, compression molding, transfer molding, dam fill encapsulation, or screen print encapsulation. In a typical compression molding, a molding pressure used for applying the first mold compound 18 may be between 100 psi and 1000 psi. A curing process (not shown) is then used to harden the first mold compound 18. The curing temperature is between 100° C. and 320° C. depending on which material is used as the first mold compound 18.

After the first mold compound 18 is formed, a thickness T4 of the mold wafer 48 may be thicker than the thickness T1 of the first die 12. A second thinning process may be followed to thin down the first mold compound 18 to provide a precursor wafer 50, as illustrated in FIG. 5. A thickness T5 of the precursor wafer 50 must be essentially the same as the thickness T1 of the first die 12. The second thinning step may be provided by a mechanical grinding process. In some cases, if the thickness T4 of the mold wafer 48 is essentially the same as the thickness T1 of the first die 12, the second thinning step may be omitted, and the precursor wafer 50 is the mold wafer 48.

The precursor wafer 50 is then singulated into a number of mold dies 52 as shown in FIG. 6. Herein, each mold die 52 includes the second die 14 and the first mold compound 18 over the second die 14, and has the thickness T5, which is essentially the same as the thickness T1 of the first die 12. In each mold die 52, the periphery of the first mold compound 18 and the periphery of the second silicon substrate 32 of the second die 14 are coincident.

Next, one mold die 52 (including one second die 14) and one first die 12 are placed on a mold tape 54, as illustrated in FIG. 7. Herein, the first silicon substrate 46 of the first die 12 and the first mold compound 18 of the mold die 52 are in contact with the mold tape 54, and may extend into the mold tape 54 with a depth D1 about 3 μm. The first die bumps 28 and the second die bumps 34 are placed upward. Since the first die 12 and the mold die 52 have the same thickness, an end of each first die bump 28 and an end of each second die bump 34 are essentially at a same plane.

In different applications, there may be fewer or more dies placed on the mold tape 54. If the first die 12 does not provide a MEMS component and is formed from a SOI structure, the mold die 52 including the second die 14 may be omitted. Consequently, the fabrication steps shown in FIGS. 3-6 may be omitted. If the first die 12 provides a MEMS component, the second die 14 within the mold die 52 may provide a CMOS controller (not shown) that controls the MEMS component within the first die 12.

The second mold compound 20 is then applied over the mold tape 54 to encapsulate the first die 12 and the mold die 52, as illustrated in FIG. 8. The second mold compound 20 may be an organic epoxy resin system or the like, and may be applied by various procedures, such as sheet molding, overmolding, compression molding, transfer molding, dam fill encapsulation, or screen print encapsulation. In a typical compression molding, a molding pressure used for applying the second mold compound 20 may be between 100 psi and 1000 psi. Since the first die 12 and the mold die 52 are relatively thick, there may be no vertical deformations occurring to the first die 12 and the mold die 52 during this molding step.

A curing process (not shown) is then used to harden the second mold compound 20. The curing temperature is between 100° C. and 320° C. depending on which material is used as the second mold compound 20. A grinding process (not shown) is followed to provide a planarized top surface of the second mold compound 20. The mold tape 54 is removed to provide a precursor package 56, which is then flipped upside down, as illustrated in FIG. 9. Herein, the second mold compound 20 resides around and underneath the first die 12 and the mold die 52, and has no portion extending above the first silicon substrate 46 of the first die 12 and the first mold compound 18 of the mold die 52. The first silicon substrate 46 of the first die 12 and the first mold compound 18 of the mold die 52 are exposed through the second mold compound 20 at a top of the precursor package 56. After the flipping, the second mold compound 20 has a planarized bottom surface, and encapsulates the downward first die bumps 28 and the downward second die bumps 34.

Since the first silicon substrate 46 of the first die 12 and the first mold compound 18 of the mold die 52 may extend into the mold tape 54, after removing the mold tape 54, a top surface of the precursor package 56 may not be flat. The backside of the first silicon substrate 46 and a top surface of the first mold compound 18 may not be flush with a top surface of the second mold compound 20. FIG. 10 shows that the top surface of the precursor package 56 is planarized to provide a mold package 58. The planarizing step may be provided by a mechanical grinding process. A top surface of the mold package 58 is essentially flat, where the top surface of the first mold compound 18, the top surface of the second mold compound 20, and the backside of the first silicon substrate 46 are coplanar, and exposed to the external environment.

FIGS. 11-16 illustrate the steps to provide the WLFO package 10 shown in FIG. 1 from the mold package 58 shown in FIG. 10. Although the exemplary steps are illustrated in a series, the exemplary steps are not necessarily order dependent. Some steps may be done in a different order than that presented. Further, processes within the scope of this disclosure may include fewer or more steps than those illustrated in FIGS. 11-16.

Firstly, the first silicon substrate 46 is removed substantially to provide an etched package 60, as illustrated in FIG. 11. The removal of the first silicon substrate 46 from the first die 12 provides the first thinned die 12T and forms the opening 42 within the second mold compound 20 and over the first thinned die 12T. Herein, removing substantially a silicon substrate refers to removing at least 95% of the entire silicon substrate and leaving at most 2 μm of the silicon substrate. In desired cases, the first silicon substrate 46 is removed completely, such that the first dielectric layer 26 of the first thinned die 12T is exposed at the bottom of the opening 42.

Removal of the first silicon substrate 46 may be provided by an etching process with a wet/dry etchant chemistry, which may be TMAH, KOH, ACH, NaOH, or the like. The first dielectric layer 26 may function as an etching stop to protect the first device layer 24 of the first thinned die 12T. The second mold compound 20 protects the sidewalls and the bottom surface of the first thinned die 12T from the etchant chemistry. In addition, a combination of the first mold compound 18 and the second mold compound 20 encapsulates and protects the second die 14 from the wet/dry etchant chemistry.

Next, the third mold compound 22 is applied to substantially fill the opening 42, as illustrated in FIG. 12A. Herein, substantially filling an opening refers to filling at least 75% of the entire opening. The third mold compound 22 directly resides over the top surface of the first thinned die 12T. If there is no first silicon substrate 46 left in the opening 42, the third mold compound 22 will directly reside over the first dielectric layer 26. In some cases, a portion of the third mold compound 22 may further reside over the first mold compound 18 and the second mold compound 20. The third mold compound 22 is separated from the second die 14 by the first mold compound 18. A top surface of the second die 12 is in contact with the first mold compound 18.

The third mold compound 22 may have a thermal conductivity greater than 2 W/m·K or greater than 10 W/m·K, and has an electrical resistivity greater than 1E6 Ohm-cm. The third mold compound 22 may be formed of thermoplastics or thermoset materials, such as PPS, overmold epoxies doped with boron nitride or alumina thermal additives, or the like. The first, second, and third mold compounds 18, 20, and 22 may be formed of a same material or different materials. For instance, the first and second mold compounds 18 and 20 may be formed from a same material, while the third mold compound 22 is formed from a different material. Unlike the third mold compound 22, the first and second mold compounds 18 and 20 do not have thermal conductivity requirements.

The third mold compound 22 may be applied by various procedures, such as sheet molding, overmolding, compression molding, transfer molding, dam fill encapsulation, and screen print encapsulation. During the molding process of the third mold compound 22, liquefaction and molding pressure may not be uniform across the entire etched package 60. Because the combination of the first thinned die 12T and a portion of the second mold compound 20 directly underneath the first thinned die 12T are thinner than other portions of the etched package 60, they may suffer more deformations than the other portions of the etched package 60. In a typical compression molding, if the third mold compound 22 is formed of high thermal conductivity materials (>=2 W/m·K), a molding pressure and a temperature used for applying the third mold compound 22 may be between 250 psi and 1000 psi, and between 100° C. and 350° C., respectively. A curing process (not shown) is then used to harden the third mold compound 22. The curing temperature is between 100° C. and 320° C. depending on which material is used as the third mold compound 22. A grinding process (not shown) is followed to provide a planarized top surface of the third mold compound 22.

Notice that the combination of the first thinned die 12T and the second mold compound portion 20 underneath the first thinned die 12T may have a thickness at least 8 μm. There is no air gap under the first thinned die 12T, and the bottom surface of the second mold compound 20 is planarized. As such, there may be no vertical deformations occurring to the first thinned die 12T during the molding step of the third mold compound 22. However, if there is no second mold compound 20 formed underneath the first thinned die 12T, especially not filling gaps between the first die bumps 28 vertically below the first thinned die 12T, vertical deformations of the first thinned die 12T may occur during the molding step of the third mold compound 22. Without support in the gaps vertically below the first thinned die 12T, the first thinned die 12T may not endure high vertical molding pressure.

In some applications, the third mold compound 22 does not cover the top surface of the first mold compound 18 or the top surface of the second mold compound 20. Instead, the top surface of the third mold compound 22, the top surface of the first mold compound 18, and the top surface of the second mold compound 20 are coplanar, as illustrated in FIG. 12B. Further, if a portion of the third mold compound 22 resides over the first mold compound 18 and the second mold compound 20, a grinding process may be applied to thin down the third mold compound 22 until the top surfaces of the first, second, and third mold compounds 18, 20, and 22 are coplanar.

In addition, if the top surfaces of the first, second, and third mold compounds 18, 20, and 22 are coplanar, there might be a fourth mold compound 62 applied over the first, second, and third mold compounds 18, 20, and 22, as illustrated in FIG. 12C. Herein, the fourth mold compound 62 may be formed of a same or different material as the first, second, and/or third mold compounds 18, 20, and 22. For instance, the first, second, and fourth mold compounds 18, 20, and 62 are formed from a same material, while the third mold compound 22 is formed from a different material. Like the first and second mold compounds 18 and 20, the fourth mold compound 62 does not have thermal conductivity requirements. The fourth mold compound 62 may be applied by various procedures, such as sheet molding, overmolding, compression molding, transfer molding, dam fill encapsulation, and screen print encapsulation. A curing process (not shown) is then used to harden the fourth mold compound 62. The curing temperature is between 100° C. and 320° C. depending on which material is used as the fourth mold compound 62. A grinding process (not shown) is followed to provide a planarized top surface of the fourth mold compound 62.

After the third mold compound 22 is applied, the second mold compound 20 is thinned to expose each first die bump 28 and each second die bump 34, as illustrated in FIG. 13. Herein, since the end of each first die bump 28 and the end of each second die bump 34 are at the same plane, each first die bump 28 and each second die bump 34 may be exposed simultaneously. In addition, since the first die bumps 28 protrude from the bottom surface the first thinned die 12T and the second die bumps 34 protrude from the bottom surface of the second die 12, the bottom surface of the first thinned die 12T and the bottom surface of the second die 14 are still fully covered by the second mold compound 20. The thinning procedure may be done with a mechanical grinding process.

With reference to FIGS. 14 through 16, the multilayer redistribution structure 16 is formed according to one embodiment of the present disclosure. Although the redistribution steps are illustrated in a series, the redistribution steps are not necessarily order dependent. Some steps may be done in a different order than that presented. Further, redistribution steps within the scope of this disclosure may include fewer or more steps than those illustrated in FIGS. 14-16.

A number of the redistribution interconnections 36 are firstly formed underneath the second mold compound 20, as illustrated in FIG. 14. For the purpose of this illustration, the redistribution interconnections 36 include three first redistribution interconnections 36(1) and one second redistribution interconnection 36(2). In different applications, the redistribution interconnections 36 may include fewer or more first redistribution interconnections 36(1)/second redistribution interconnections 36(2). Each first redistribution interconnection 36(1) is electrically coupled to the corresponding one of the exposed first and second die bumps 28 and 34. The second redistribution interconnection 36(2) is configured to connect one first die bump 28 to the corresponding second die bump 34, such that the first thinned die 12T is connected to the second die 14. The connections between the redistribution interconnections 36 and the first/second die bumps 28/34 are solder-free.

Next, the dielectric pattern 38 is formed underneath the second mold compound 20 to partially encapsulate each first redistribution interconnection 36(1) as illustrated in FIG. 15. As such, a portion of each first redistribution interconnection 36(1) is exposed through the dielectric pattern 38. Further, the dielectric pattern 38 fully encapsulates the second redistribution interconnection 36(2). Herein, no portion of the second redistribution interconnection 36(2) is exposed through the dielectric pattern 38. In different applications, there may be extra redistribution interconnections (not shown) electrically coupled to the redistribution interconnection 36 through the dielectric pattern 38, and extra dielectric patterns (not shown) formed underneath the dielectric pattern 38, such that a bottom portion of each extra redistribution interconnection is exposed.

Lastly, a number of the package contacts 40 are formed to complete the multilayer redistribution structure 16 and provide the WLFO package 10, as illustrated in FIG. 16. Each package contact 50 is formed at the bottom of the multilayer redistribution structure 16 and electrically coupled to an exposed portion of the corresponding first redistribution interconnection 36(1) through the dielectric pattern 38. Consequently, the first redistribution interconnects 36(1) connect the package contacts 40 to certain ones of the first and second die bumps 28 and 34. In addition, the package contacts 40 are separate from each other and extend underneath the dielectric pattern 38.

The multilayer redistribution structure 16 may be free of glass fiber or glass-free. Herein, the glass fiber refers to individual glass strands twisted to become a larger grouping. These glass strands may then be woven into a fabric. The dielectric pattern 38 may be formed of benzocyclobutene (BCB), polyimide, or other dielectric materials. The redistribution interconnections 36 may be formed of copper or other suitable metals. The package contacts 40 may be formed of at least one of copper, gold, nickel, and palladium. The multilayer redistribution structure 16 may have a thickness between 2 μm and 300 μm.

Those skilled in the art will recognize improvements and modifications to the preferred embodiments of the present disclosure. All such improvements and modifications are considered within the scope of the concepts disclosed herein and the claims that follow.

Claims

1. An apparatus comprising: a first thinned die comprising a first device layer, a first dielectric layer over the first device layer, and a plurality of first die bumps underneath the first device layer;a second die comprising a second device layer, a silicon substrate over the second device layer, and a plurality of second die bumps underneath the second device layer;a multilayer redistribution structure formed underneath the first thinned die and the second die;a first mold compound residing over the silicon substrate of the second die;a second mold compound residing over the multilayer redistribution structure, around and underneath the first thinned die, and around and underneath the second die; wherein: the second mold compound extends beyond a top surface of the first thinned die to define an opening within the second mold compound and over the first thinned die, such that the top surface of the first thinned die is at a bottom of the opening; anda top surface of the first mold compound and a top surface of the second mold compound are coplanar; anda third mold compound filling the opening and in contact with the top surface of the first thinned die, wherein the first mold compound, the second mold compound, and the third mold compound are formed from different materials.

2. The apparatus of claim 1 wherein the multilayer redistribution structure comprises a plurality of package contacts on a bottom surface of the multilayer redistribution structure and redistribution interconnections that connect the plurality of package contacts to certain ones of the plurality of first die bumps and certain ones of the plurality of second die bumps.

3. The apparatus of claim 2 wherein: the redistribution interconnections electrically connect the first thinned die and the second die; andthe first thinned die provides a microelectromechanical system (MEMS) component and the second die provides a complementary metal-oxide-semiconductor (CMOS) controller that controls the MEMS component.

4. The apparatus of claim 2 wherein: the multilayer redistribution structure is glass-free;connections between the redistribution interconnections and the plurality of first die bumps are solder-free; andconnections between the redistribution interconnections and the plurality of second die bumps are solder-free.

5. The apparatus of claim 1 wherein the first thinned die is formed from a silicon-on-insulator (SOI) structure, wherein the first device layer of the first thinned die is formed from a silicon layer of the SOI structure, and the first dielectric layer of the first thinned die is a buried oxide layer of the SOI structure.

6. The apparatus of claim 1 wherein the third mold compound has an electrical resistivity greater that 1E6 Ohm-cm.

7. The apparatus of claim 1 wherein the third mold compound has a thermal conductivity greater than 2 W/m·K.

8. The apparatus of claim 1 wherein the third mold compound has a thermal conductivity greater than 10 W/m·K.

9. The apparatus of claim 1 wherein the top surface of the first thinned die at the bottom of the opening is a top surface of the first dielectric layer.

10. The apparatus of claim 1 wherein a portion of the third mold compound resides over the first mold compound and the second mold compound.

11. The apparatus of claim 1 wherein the top surface of the first mold compound, the top surface of the second mold compound, and a top surface of the third mold compound are coplanar.

12. The apparatus of claim 1 wherein a periphery of the first mold compound and a periphery of the silicon substrate of the second die are coincident.

13. An apparatus comprising: a first thinned die comprising a first device layer, a first dielectric layer over the first device layer, and a plurality of first die bumps underneath the first device layer;a second die comprising a second device layer, a silicon substrate over the second device layer, and a plurality of second die bumps underneath the second device layer;a multilayer redistribution structure formed underneath the first thinned die and the second die;a first mold compound residing over the silicon substrate of the second die;a second mold compound residing over the multilayer redistribution structure, around and underneath the first thinned die, and around and underneath the second die; wherein: the second mold compound extends beyond a top surface of the first thinned die to define an opening within the second mold compound and over the first thinned die, such that the top surface of the first thinned die is at a bottom of the opening; anda top surface of the first mold compound and a top surface of the second mold compound are coplanar;a third mold compound filling the opening and in contact with the top surface of the first thinned die, wherein the top surface of the first mold compound, the top surface of the second mold compound, and a top surface of the third mold compound are coplanar; anda fourth mold compound, which resides over the top surface of the first mold compound, the top surface of the second mold compound, and the top surface of the third mold compound.

14. The apparatus of claim 13 wherein the first mold compound, the second mold compound, and the fourth mold compound are formed from a same material.

15. A method comprising: providing a precursor package that includes a first die, a second die, a first mold compound, and a second mold compound, wherein: the first die comprises a first device layer, a first dielectric layer over the first device layer, a first silicon substrate over the first dielectric layer, and a plurality of first die bumps underneath the first device layer;the second die comprises a second device layer, a second silicon substrate over the second device layer, and a plurality of second die bumps underneath the second device layer;the first mold compound resides over the second silicon substrate of the second die; andthe second mold compound resides around and underneath the first die and the second die; such that the second mold compound partially covers sidewalls of the first die, covers a bottom surface of the first die, covers sidewalls and a bottom surface of the second die, partially covers sidewalls of the first mold compound, and encapsulates the first die bumps and the second die bumps, wherein the first mold compound and the first silicon substrate extend vertically beyond a top surface of the second mold compound;planarizing a top surface of the precursor package to provide a mold package, such that a top surface of the first mold compound, the top surface of the second mold compound, and a backside of the first silicon substrate are coplanar;removing substantially the first silicon substrate to provide a first thinned die and form an opening within the second mold compound and over the first thinned die, wherein the first thinned die has a top surface exposed at a bottom of the opening; andapplying a third mold compound to substantially fill the opening and directly contact the top surface of the first thinned die.

16. The method of claim 15 further comprising: thinning the second mold compound to expose each of the plurality of first die bumps and each of the plurality of second die bumps; andforming a multilayer redistribution structure underneath the second mold compound, wherein the multilayer redistribution structure comprises a plurality of package contacts on a bottom surface of the multilayer redistribution structure and redistribution interconnections that connect the plurality of package contacts to certain ones of the plurality of first die bumps and certain ones of the plurality of second die bumps.

17. The method of claim 15 wherein the third mold compound is applied by a compression molding process.

18. The method of claim 15 wherein a molding pressure used for applying the third mold compound is lower than 1000 psi.

19. The method of claim 15 wherein providing the precursor package comprises: placing the first die and a mold die on a mold tape, wherein: the mold die includes the second die and the first mold compound over the second die; andthe first silicon substrate of the first die and the first mold compound of the mold die are in contact with the mold tape, and the plurality of first die bumps and the plurality of second die bumps are placed upward;applying the second mold compound over the mold tape to encapsulate the first die and the mold die;removing the mold tape to provide the precursor package, such that a portion of the first mold compound and a portion of the first silicon substrate are exposed, and protrude from the second mold compound; andflipping the precursor package, such that the plurality of first die bumps and the plurality of second die bumps are downward and encapsulated by the second mold compound, wherein no portion of the second mold compound extends above the first silicon substrate of the first die and the first mold compound.

20. The method of claim 19 wherein before placing the first die and the combination of the second die and the first mold compound on the mold tape, a thickness of the first die and a thickness of the combination of the second die and the first mold compound are the same.