The present invention relates to an electrically rewritable non-volatile memory element. More specifically, the present invention relates to an electrically rewritable non-volatile memory element having a recording layer that includes phase change material.
Personal computers and servers and the like use a hierarchy of memory devices. There is lower-tier memory, which is inexpensive and provides high storage capacity, while memory higher up the hierarchy provides high-speed operation. The bottom tier generally consists of magnetic storage such as hard disks and magnetic tape. In addition to being non-volatile, magnetic storage is an inexpensive way of storing much larger quantities of information than solid-state devices such as semiconductor memory. However, semiconductor memory is much faster and can access stored data randomly, in contrast to the sequential access operation of magnetic storage devices. For these reasons, magnetic storage is generally used to store programs and archival information and the like, and, when required, this information is transferred to main system memory devices higher up in the hierarchy.
Main memory generally uses dynamic random access memory (DRAM) devices, which operate at much higher speeds than magnetic storage and, on a per-bit basis, are cheaper than faster semiconductor memory devices such as static random access memory (SRAM) devices.
Occupying the very top tier of the memory hierarchy is the internal cache memory of the system microprocessor unit (MPU). The internal cache is extremely high-speed memory connected to the MPU core via internal bus lines. The cache memory has a very small capacity. In some cases, secondary and even tertiary cache memory devices are used between the internal cache and main memory.
DRAM is used for main memory because it offers a good balance between speed and bit cost. Moreover, there are now some semiconductor memory devices that have a large capacity. In recent years, memory chips have been developed with capacities that exceed one gigabits. DRAM is volatile memory that loses stored data if its power supply is turned off. That makes DRAM unsuitable for the storage of programs and archival information. Also, even when the power supply is turned on, the device has to periodically perform refresh operations in order to retain stored data, so there are limits as to how much device electrical power consumption can be reduced, while yet a further problem is the complexity of the controls run under the controller.
Semiconductor flash memory is high capacity and non-volatile, but requires high current for writing and erasing data operations, and these operation times are long. These drawbacks make flash memory an unsuitable candidate for replacing DRAM in main memory applications. There are other non-volatile memory devices, such as magnetoresistive random access memory (MRAM) and ferroelectric random access memory (FRAM), but they cannot easily achieve the kind of storage capacities that are possible with DRAM.
Another type of semiconductor memory that is being looked to as a possible substitute for DRAM is phase change random access memory (PRAM), which uses phase change material to store data. In a PRAM device, the storage of data is based on the phase state of phase change material contained in the recording layer. Specifically, there is a big difference between the electrical resistivity of the material in the crystalline state and the electrical resistivity in the amorphous state, and that difference can be utilized to store data.
This phase change is effected by the phase change material being heated when a write current is applied. Data is read by applying a read current to the material and measuring the resistance. The read current is set at a level that is low enough not to cause a phase change. Thus, the phase does not change unless the material is heated to a high temperature, so data is retained even when the power supply is switched off.
In order to effectively heat a phase change material by a write current, it is preferable to reduce a contact area between a lower electrode, which functions as a heater plug, and a recording layer, thereby reducing a heating region. To realize this, there is proposed a method in which an interlayer insulation film is arranged between the lower electrode of which top surface has a ring shape and a recording layer pattern in stripes, and the both are contacted via an aperture provided in the interlayer insulation film. See US 2004/0012009-A1; “Advances in Phase Change Memory Technology,” E. Varesi, A. Modelli, P. Besana, T. Marangon, F. Pellizzer, A. Pirovano, R. Bez, EPCOS (European Symposium Phase Change and Ovonic Science) 2004 Conf. Proceedings; and “Overview of Phase-Change Chalcogenide Nonvolatile Memory Technology,” S. Hudgens, B. Johnson, MRS Bulletin, November 2004.
According to this method, the recording layer contacts only one portion of the ring-shaped lower electrode, and thus, the heating concentrates in one area. As a result, the heating of the phase change material by the write current is performed effectively, so that a phase change (reset) from a crystalline phase to an amorphous phase that particularly requires a large amount of current can be realized with a smaller amount of current.
In the non-volatile semiconductor memory device shown in
The interlayer insulation film 6 is formed with an aperture 6a. In this portion, a region 3, which is one portion of the top surface 2a of the lower electrode 2, is exposed. The aperture 6a is commonly provided to two adjacent lower electrodes 2. The planar position of an edge 6b in a longitudinal direction is positioned in a region surrounded by the ring-shaped lower electrode 2.
A recording layer 8 composed of a phase change material is formed on the interlayer insulation film 6. Thus, the recording layer 8 contacts the top surface 2a of the lower electrode 2 via the aperture 6a, so that the contact area is limited to the area of the region 3 exposed by the aperture 6a. This limitation reduces the contact area. As a result, high heating efficiency can be obtained.
In the non-volatile semiconductor memory device shown in
For example, as shown in
The problem of such poor connection can be solved to some extent by setting the length of the aperture 6a to be long. In this case, however, as shown in
The present invention has been achieved to solve the above problems. It is therefore an object of the present invention to provide a non-volatile semiconductor memory device that includes a recording layer that contains a phase change material, and that can obtain high heating efficiency while sufficiently securing a process margin.
A non-volatile semiconductor memory device according to one aspect of the present invention comprises:
a plurality of lower electrodes arranged in a matrix manner;
a plurality of recording layer patterns provided on the lower electrode, and containing a phase change material; and
an interlayer insulation film having a plurality of apertures for exposing one portion of the lower electrode, the interlayer insulation film being provided between the lower electrode and the recording layer pattern, wherein
the lower electrode and the recording layer pattern are connected in the aperture,
the apertures extend in parallel to one another in a first direction, and
the recording layer patterns extend in parallel to one another in a second direction that intersects with the first direction.
The non-volatile semiconductor memory device according to the present invention includes a plurality of apertures, arranged in an interlayer insulation film and each having a shape that extends in parallel to each other, so that it becomes possible to form the aperture with higher accuracy as compared to a conventional case in which an independent aperture is formed. Therefore, it is possible to obtain high heating efficiency while effectively preventing occurrence of poor connection or the like.
In a preferred embodiment of the present invention, a top surface of the lower electrode includes a strip region that extends in the second direction, and the aperture is formed at a position for exposing at least one portion of the strip region. Accordingly, even when a formation position of the aperture is slightly deviated in the second direction, the contact area between the lower electrode and the recording layer can be made approximately constant, thereby obtaining a stable device property.
When the top surface of the lower electrode has a ring shape, the aperture can be formed at a position for exposing two regions of the top surface of each lower electrode, or at a position for exposing one region of the top surface of each lower electrode. In the former case, the recording layer pattern is preferably formed at a position that contacts only one of the two exposed regions of the lower electrode. On the other hand, in the latter case, the recording layer pattern is preferably formed at a position that contacts only one portion of the exposed regions of the lower electrode. Accordingly, the contact area is further reduced, thereby obtaining higher heating efficiency.
A non-volatile semiconductor memory device according to another aspect of the present invention comprises:
a lower electrode having a ring-shaped top surface;
an interlayer insulation film provided on the lower electrode; and
a recording layer arranged on the interlayer insulation film, and containing a phase change material, wherein
the interlayer insulation film has an aperture for exposing one portion of the top surface of the lower electrode, the aperture extending in a first direction, and
the recording layer extends in a second direction that intersects with the first direction, and contacts a further one portion of the one portion of the top surface of the lower electrode exposed in the aperture.
According to this aspect of the present invention, it is also possible to obtain high heating efficiency while effectively preventing occurrence of poor connection or the like.
A diameter of the top surface of the lower electrode in the second direction is preferably larger than that in the first direction. Accordingly, even when a formation position of the aperture is slightly deviated in the second direction, the contact area between the lower electrode and the recording layer can be made approximately constant, thereby obtaining a stable device property.
As described above, the non-volatile semiconductor memory device according to the present invention can obtain high heating efficiency while preventing occurrence of poor connection or the like. Therefore, it is possible to reduce a larger amount of write current as compared to the conventional case while securing a sufficient process margin. It is also possible to enhance a writing speed.
The above and other objects, features and advantages of this invention will become more apparent by reference to the following detailed description of the invention taken in conjunction with the accompanying drawings, wherein:
Preferred embodiments of the present invention will now be explained in detail with reference to the drawings.
As shown in
The interlayer insulation film 12 has a plurality of apertures 12a that extend in the X direction. The apertures 12 are formed in parallel to one another. The aperture 12a is formed at a position that traverses the strip region 11y of the lower electrode 11. That is, the aperture 12a is formed at a position sandwiched by the two strip regions 11x. This formation leads to exposure of the top surface 11a of each lower electrode 11 in two regions 15a and 15b that form one portion of the strip region 11y.
The recording layer 13 and the upper electrode 14 extend in the Y direction. These members are formed in parallel to each other. The recording layer 13 and the upper electrode 14 are formed on one of the strip regions 11y (right side in
Each constituent element of the non-volatile semiconductor memory device according to this embodiment will be described in more detail.
The lower electrode 11 is used as a heater plug. That is, the lower electrode 11 forms a portion of a heating element at the time of data writing. For this reason, examples of materials used for the lower electrode 11 preferably include a material having relatively high electric resistance such as metal silicide, metal nitride, and nitride composed of metal silicide. Examples are not restrictive, but preferably include high-melting metals such as W, TiN, TaN, WN, and TiAlN, nitride composed thereof, and nitride composed of high-melting metal silicide such as TiSiN and WSiN. Materials such as TiCN are further preferably used.
As shown in
A bottom surface 11b of the lower electrode 11 is connected to a diffusion region 106 (drain) formed in an active region 105 via contact plugs 122 and 121. The contact plug 121 is embedded in an interlayer insulation film 111, and the contact plug 122 is embedded in an interlayer insulation film 112.
As shown in
The interlayer insulation film 12 functions to separate the lower electrode 11 and the recording layer 13. A silicon oxide film, silicon nitride film, and the like can be used as materials for forming the interlayer insulation film 12. Although not particularly limit, materials of which etching rates vary with one another is preferably used as the materials of the interlayer insulation film 12, and those of the interlayer insulation film 113 and the insulation material 114. For example, when the silicone oxide film is used as the material for the interlayer insulation film 113 and the insulation material 114, the silicone nitride film is preferably used as the material for the interlayer insulation film 12.
Although not particularly limited, the film thickness of the interlayer insulation film 12 can be set to approximately 40 nm, for example. The width of the aperture 12a formed in the interlayer insulation film 12 is not particularly limited as long as it is smaller than the length of the lower electrode 11 in the Y direction. As one example, when the length of the lower electrode 11 in the Y direction is 200 nm, the width of the aperture 12a can be set to approximately 80 nm.
A width W of the aperture 12a is preferably as small as possible. This is because the smaller the width W of the aperture 12a is set, the smaller a contact area of the lower electrode 11 and the recording layer 13. As a result, heating efficiency can be enhanced. In this embodiment, since the aperture 12a has a successive shape that extends in the X direction, an aperture can be formed with higher accuracy as compared to a conventional island-like aperture. Accordingly, the width W of the aperture 12a can be made sufficiently thin.
The recording layer 13 is composed of a phase change material. The phase change material constituting the recording layer 13 is not particularly limited insofar as the material assumes two or more phase states and has an electrical resistance that changes according to the phase state. A so-called chalcogenide material is preferably selected. A chalcogenide material is defined as an alloy that contains at least one or more elements selected from the group consisting of germanium (Ge), antimony (Sb), tellurium (Te), indium (In), selenium (Se), and the like. Examples include GaSb, InSb, InSe, Sb2Te3, GeTe, and other binary-based elements; Ge2Sb2Te5, InSbTe, GaSeTe, SnSb2Te4, InSbGe, and other tertiary-based elements; and AgInSbTe, (GeSn)SbTe, GeSb(SeTe), Te81Ge15Sb2S2, and other quaternary-based elements.
A phase change material that includes a chalcogenide material may assume any phase state including an amorphous phase (non-crystalline phase) and a crystalline phase, with a relatively high-resistance state occurring in the amorphous phase, and a relatively low-resistance state occurring in the crystalline phase.
In order to place the phase change material that includes a chalcogenide material in the amorphous state, the material is cooled rapidly after being heated to a temperature equal to or higher than the melting point Tm, as indicated by the curve a in
When a write current is passed to the recording layer 13, a portion immediately above the lower electrode 11 is heated, among the recording layer 13. That is, by passing a write current to the recording layer 13, the phase state of the chalcogenide material in a phase change region P shown in
The upper electrode 14 also serves as a bit line. Examples of materials used for the upper electrode 14 are selected from metallic materials having lower electric resistance. Materials preferably used therefor include aluminum (Al), titanium (Ti), tungsten (W), an alloy thereof, nitride thereof, and silicide, for example. More specifically, examples include W, WN, and TiN. The film thickness of the upper electrode 14 is not particularly limited, but is preferably set to approximately 60 nm. The upper electrode 14 has the same pattern as the recording layer 13. Therefore, the width of the upper electrode 14 agrees with the width of the recording layer 13.
The non-volatile semiconductor storage device shown in
The non-volatile memory element 10 has a configuration in which the recording layer 13 is connected between the lower electrode 11 and the upper electrode 14, as shown in
The non-volatile semiconductor storage device having this type of configuration can perform writing and reading of data by activating any of the word lines W1-Wn through the use of the row decoder 101, and allowing a current to flow to at least one of the bit lines B1-Bm in this state. In other words, in a memory cell in which the corresponding word line is activated, the transistor 103 is ON, and the corresponding bit line is then connected to the ground via the non-volatile memory element 10. Accordingly, by allowing a write current to flow to the bit line selected by a prescribed column decoder 102 in this state, a phase change can be effected in the recording layer 13 included in the non-volatile memory element 10.
Specifically, by allowing a prescribed amount of current to flow, the phase change material constituting the recording layer 13 is placed in the amorphous phase by heating the phase change material to a temperature equal to or higher than the melting point Tm shown in
Also in the case of reading data, any one of the word lines W1-Wn is activated by the row decoder 101, and while in this state, a read current is allowed to flow to at least one of the bit lines B1-Bm. Since the resistance value is high for a memory cell in which the recording layer 13 is in the amorphous phase, and the resistance value is low for a memory cell in which the recording layer 13 is in the crystalline phase, the phase state of the recording layer 13 can be ascertained by detecting these values using a sense amplifier (not shown).
The phase state of the recording layer 13 can be correlated with a stored logical value. For example, defining an amorphous phase state as “0” and a crystalline phase state as “1” makes it possible for a single memory cell to retain 1-bit data. The crystallization ratio can also be controlled in multi-stage or linear fashion by adjusting the time for which the recording layer 13 is maintained at the temperature equal to or higher than the crystallization temperature Tx and less than the melting point Tm when a change occurs from the amorphous phase to the crystalline phase. Performing multi-stage control of the mixture ratio of amorphous states and crystalline states by this type of method makes it possible for 2-bit or higher order data to be stored in a single memory cell. Furthermore, performing linear control of the mixture ratio of amorphous states and crystalline states makes it possible to store analog values.
The method for manufacturing the non-volatile semiconductor memory device according to the present embodiment will next be described.
Firstly, after the contact plug 122 is embedded into the interlayer insulation film 112, the interlayer insulation film 113 is formed on the entire surface, as shown in
Next, as shown in
Next, as shown in
Next, as shown by a plan view in
In this case, when materials of which etching rates vary with those of the interlayer insulation film 113 and the insulation material 114 are selected as the material for the interlayer insulation film 12, it becomes possible to reduce an over-etching amount of the interlayer insulation film 113 and the insulation material 114 in an etching process at the time of forming the aperture 12a.
Since the aperture 12a extends in the X direction and the strip region 11y extends in the Y direction, the formation of the aperture 12a at a position to traverse the strip region 11y hardly causes any area variation of the regions 15a and 15b even when the formation position of the aperture 12a is slightly deviated in the Y direction.
Thereafter, the recording layer 13 and the upper electrode 14 composed of a phase change material are formed on the entire surface, and these members are collectively patterned so as to form a pattern of the recording layer 13 (recording layer pattern) and a pattern of the upper electrode 14 that extend in the Y direction. Thus, the structure shown in
As described above, in the non-volatile semiconductor memory device according to this embodiment, the aperture 12a formed in the interlayer insulation film 12 has a successive shape that extends in the X direction, and the recording layer 13 has a successive shape that extends in the Y direction. Accordingly, occurrence of poor connection or the like caused by misalignment of the aperture 12a or the recording layer 13 can be prevented.
In this embodiment, when the formation position of the recording layer 13 is greatly deviated in the X direction, there is a possibility of occurrence of poor connection or the like. However, the recording layer 13 has a successive shape that extends in the Y direction, so that a patterning with higher accuracy is possible as compared to the case in which an island-like pattern is formed. Thus, it is possible to obtain a larger margin as compared to the conventional case.
A second preferred embodiment of the present invention will be described next.
As shown in
The formation position of the recording layer 13, however, is set on the strip regionally on one side (right side in
With this configuration, in the second embodiment, when the formation position of the aperture 12a in the Y direction or the formation position of the recording layer 13 in the X direction is controlled, it becomes possible to adjust the area of the region 15a. Accordingly, when the formation position of the aperture 12a in the Y direction and the formation position of the recording layer 13 in the X direction are adjusted with high accuracy, it becomes possible to make significantly small the area of the region 15 where the lower electrode 11 and the recording layer 13 contact, thereby obtaining high heating efficiency.
The present invention is in no way limited to the aforementioned embodiments, but rather various modifications are possible within the scope of the invention as recited in the claims, and naturally these modifications are included within the scope of the invention.
For example, in the above embodiment, although the recording layer 13 and the upper electrode 14 in the same row are common, these can be separated for each individual memory cell as shown in
With such a configuration, it becomes possible to select, as materials for the upper electrode 14, a high resistance material similarly to the lower electrode 11, and to select, as materials for the bit line 18, metallic materials having lower electric resistance compared to that of the upper electrode 14 such as aluminum (Al), titanium, (Ti) tungsten (W), an alloy thereof, nitride thereof, and silicide, for example. Thus, radiation to the upper electrode 14 side and current loss caused by a bit line resistance can be reduced.
In each of the embodiments, the lower electrode 11 and the upper electrode 14 have a single-layered structure. These members, however, can have a multi-layered structure consisting of a plurality of conductive films. For example, a conductive film of some sort (bonding layer, for example) can exist between a main body portion of the lower electrode 11 and the recording layer 13. In this case, it can be considered that the conductive film forms one portion of the lower electrode 11. Therefore, also in this case, it can be considered that the lower electrode 11 and the recording layer 13 are contacted.
Accordingly, the non-volatile semiconductor memory device according to the present invention can obtain high heating efficiency while preventing occurrence of poor connection or the like. Therefore, it is possible to reduce a larger amount of write current as compared to the conventional case while securing a sufficient process margin. It is also possible to enhance a writing speed.
Number | Date | Country | Kind |
---|---|---|---|
2005-335069 | Nov 2005 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
20030146469 | Matsuoka et al. | Aug 2003 | A1 |
20040012009 | Casagrande et al. | Jan 2004 | A1 |
Number | Date | Country | |
---|---|---|---|
20070114510 A1 | May 2007 | US |