The semiconductor integrated circuit (IC) industry has experienced rapid growth. Technological advances in IC materials and design have produced generations of ICs where each generation has smaller and more complex circuits than the previous generation. However, these advances have increased the complexity of processing and manufacturing ICs and, for these advances to be realized, similar developments in IC processing and manufacturing are needed.
In the course of IC evolution, functional density (i.e., the number of interconnected devices per chip area) has generally increased while geometry size (i.e., the smallest component (or line) that can be created using a fabrication process) has decreased. This scaling down process generally provides benefits by increasing production efficiency and lowering associated costs. Such scaling-down also produces a relatively high power dissipation value, which may be addressed by using low power dissipation devices such as complementary metal-oxide-semiconductor (CMOS) devices. CMOS devices have typically been formed with a gate oxide and polysilicon gate electrode. There has been a desire to replace the gate oxide and polysilicon gate electrode with a high-k gate dielectric and metal gate electrode to improve device performance as feature sizes continue to decrease. However, problems arise when integrating a high-k/metal gate feature in a CMOS process flow due to various factors such as the gate trench width used in replaced polysilicon gate (RPG), Lg ˜25.5 nm, devices is very narrow (e.g., <10 nm for N-MOS and <2 nm for P-MOS). Such a narrow trench may include a bridging across an upper portion of the trench. In other words, the space for wetting the gate metal fill (e.g., Al-fill) is very narrow. Accordingly, the bridging may cause the metal gate fill metal to have voids after being filled into the trench.
Accordingly, an improved metal gate fill and method of making is desired.
In an embodiment, a method of fabricating a semiconductor device includes providing a semiconductor substrate and forming a gate structure over the substrate. The gate structure includes a first spacer and a second spacer formed apart from the first spacer. The gate structure also includes a dummy gate formed between the first and second spacers. The method also includes removing a portion of the dummy gate from the gate structure thereby forming a partial trench. Additionally, the method includes removing a portion of the first spacer and a portion of the second spacer adjacent the partial trench thereby forming a widened portion of the partial trench. In addition, the method includes removing a remaining portion of the dummy gate from the gate structure thereby forming a full trench. A high k film and a metal gate are then formed in the full trench.
In another embodiment, a method of fabricating a semiconductor device includes providing a semiconductor substrate and forming an insulator over the substrate. The method also includes forming a first spacer over the insulator, forming a second spacer apart from the first spacer over the insulator and forming, a dummy gate between the first and second spacers. The method further includes removing a portion of the first spacer and a portion of the second spacer thereby forming a widened area between a portion of the first and second spacers. In addition, the method includes removing the dummy gate thereby forming a trench and forming a metal gate in the trench.
In yet another embodiment, a method of fabricating a semiconductor device includes providing a substrate having a first region and a second region. The method also includes forming a first gate structure over the first region and a second gate structure over the second region. The first gate structure includes a first spacer, a second spacer, and a first dummy gate. The second gate structure includes a third spacer, a fourth spacer, and a second dummy gate. The method further includes removing a portion of the first dummy gate from the first gate structure thereby forming a first partial trench. Additionally, the method includes removing a portion of the second dummy gate from the second gate structure thereby forming a second partial trench. Furthermore, the method includes removing a portion of the first and second spacers thereby forming a widened portion of the first partial trench and removing a portion of the third and fourth spacers thereby forming a widened portion of the second partial trench. In addition, the method includes removing remaining portions of the first and second dummy gates thereby forming first and second full trenches. Accordingly, the method includes forming a high k film in the first and second full trenches, and forming metal gates in the first and second full trenches.
Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.
It is to be understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. Moreover, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed interposing the first and second features, such that the first and second features may not be in direct contact. Various features may be arbitrarily drawn in different scales for simplicity and clarity. In addition, the present disclosure provides examples of a “gate last” metal gate process, however one skilled in the art may recognize applicability to other processes and/or use of other materials.
Referring to
The method 100 begins with block 102 in which a semiconductor substrate is provided. In
The method 100 continues with block 104 in which a gate structure is formed over the substrate 202, the gate structure includes spacers 227 and a dummy polysilicon (or poly) layer/gate 218. The formation of the gate structures includes forming various material layers, and etching/patterning the various material layers to form a gate structure. The semiconductor device 200 may include a dummy insulator layer 215 formed over the substrate 202. In the alternative, an insulator layer including an interfacial layer, a high k dielectric layer and/or a barrier layer may be formed on the substrate 202 and left in the final device. These various layers are described in more detail below with reference to
The semiconductor device 200 also includes a dummy polysilicon (or poly) layer 218 formed over the insulator layer 215 by a suitable deposition process. For example, silane (SiH4), di-silane (Si2H6), or di-clorsilane (SiC12H4) may be used as a chemical gas in a CVD process to form the poly layer 218. The poly layer 218 may include a thickness ranging from about 400 to about 2000 angstrom (A). Alternatively, an amorphous silicon layer may optionally be formed instead of the polysilicon layer. The semiconductor device 200 may further include a hard mask layer (not shown) formed on the poly layer 218. The hard mask layer may include silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, and/or other suitable dielectric materials, and may be formed using a method such as CVD or PVD. The hard mask layer may include a thickness ranging from about 100 to about 400 angstrom (A). Additionally, an antireflective coating layer or bottom antireflective coating (BARC) layer may be used to enhance a photolithography process for patterning a photoresist layer. For example, a patterned photoresist layer (not shown) may be formed on the hard mask layer including a gate pattern. The gate patterns may be used to pattern the hard mask layer by a dry etch or wet etch process. The patterned hard mask may then be used to form the gate structure by a dry etch, wet etch, or combination dry and wet etch process. Accordingly, the gate structure may include the insulator layer 215, the dummy poly gate 218, and a hard mask (not shown).
After formation of the gate structure (e.g., gate etching or patterning), it is understood that the semiconductor device 200 may undergo additional processing (e.g., CMOS processing) to form various features as described in more detail below with respect to
The method 100 continues with block 106 in which a portion of the dummy gates is removed from the gate structure thereby forming a partial trench in the gate structure. In
The method 100 continues with block 108 in which a portion of the spacers 227 is removed thereby forming a widened portion 235 of the partial trenches. In an embodiment, the portions of the spacers 227 are removed using a dry argon sputtering to form a funnel-shape in the trenches 235. The molecular size of the argon is appropriate for making the funnel-shape. However other elements or other etching/forming methods may produce acceptable results. As shown in
In an embodiment, this process may be performed in a single etcher PVD tool. The argon sputtering may be performed using an argon gas pressure of approximately 3-20 mTorr and at a flow rate of approximately 300-600 sccm. The argon sputtering may have a bias of approximately 200-500 Watts. In an embodiment, the argon sputtering may be performed at a temperature of approximately 0° C.-100° C. The argon sputtering may be performed for approximately 5-30 seconds.
The method 100 continues with block 110 in which a remaining portion of the dummy gate is removed from the gate structure thereby forming a full trench in the gate structure. In
The dummy poly gate 218 and dummy dielectrics 215 may be removed in a single-step etching process or multiple-step etching process. For example, a first wet etch process may be used to remove the dummy poly gate 218. The first wet etch process may include exposure to a hydroxide containing solution (e.g., ammonium hydroxide), deionized water, and/or other suitable etchant solutions. A second wet etch process may be used to remove the dummy dielectric 215. The second wet etch process may include exposure to a buffered HF solution or a buffered oxide etchant (BOE). The second wet etch process may selectively remove the dummy dielectric 215 and may stop at the substrate 202, thereby forming the full trench 236 in the gate structure. It is understood that other etching chemicals may be used for selectively removing the dummy dielectric and dummy poly gate.
The method 100 continues with block 112 in which a high k gate film and a metal gate layer is formed to substantially fill in the trench. In
The method 100 continues with block 114 in which a chemical mechanical polishing (CMP) process is performed. In
Referring to
The method 300 begins with block 302 in which a semiconductor substrate is provided, the substrate having a first region and a second region. In
The method 300 continues with block 304 in which a first gate structure is formed over the first region and a second gate structure is formed over the second region, the first gate structure includes spacers 227 and a dummy polysilicon (or poly) layer/gate 218. The second gate structure includes spacers 227 and a dummy gate 218. The formation of the gate structures includes forming various material layers, and etching/patterning the various material layers to form a gate structure in the nFET 412 device side and a gate structure in the pFET 414 device side as discussed below.
The semiconductor device 400 may include an interfacial layer 415 formed over the substrate 202. The interfacial layer 415 may include a silicon oxide (SiO2) layer (e.g., thermal or chemical oxide formation) having a thickness ranging from about 5 to about 20 angstrom (A). Alternatively, the interfacial layer 415 may optionally include HfSiO or SiON formed by atomic layer deposition (ALD), chemical vapor deposition (CVD), physical vapor deposition (PVD), thermal oxidation, or combinations thereof. In some embodiments, an Hf film may be formed on a thermal oxide by ALD, CVD, or PVD, and then oxidized by thermal O2 to form HfSiO. In other embodiments, an Hf film may be formed by ALD, CVD, or PVD in a reactive O2 ambient.
The semiconductor device 400 may further include a high-k dielectric layer 416 formed on the interfacial layer 415. The high-k dielectric layer 416 may be formed by ALD, CVD, metalorganic CVD (MOCVD), PVD, thermal oxidation, combinations thereof, or other suitable techniques. The high-k dielectric layer 416 may include a thickness ranging from about 5 to about 20 angstrom (A). The high-k dielectric layer 416 may include a binary or ternary high-k film such as HfOx. Alternatively, the high-k dielectric layer 416 may optionally include other high-k dielectrics such as LaO, AlO, ZrO, TiO, Ta2O5, Y2O3, SrTiO3 (STO), BaTiO3 (BTO), BaZrO, HfZrO, HfLaO, HfSiO, LaSiO, AlSiO, HfTaO, HfTiO, (Ba,Sr)TiO3 (BST), Al2O3, Si3N4, oxynitrides, or other suitable materials. A post high-k deposition anneal may be performed in some embodiments.
The semiconductor device 400 may further include a barrier layer 417 formed over the high-k dielectric layer 416. The barrier layer 417 may include a metal film such as TiN or TaN. Alternatively, the barrier layer 417 may optionally include Si3N4. The barrier layer 417 may include a thickness ranging from about 5 to about 20 angstrom (A). The barrier layer 417 may function as a barrier between the high-k dielectric layer 416 and a subsequent dummy poly gate structure. The barrier layer 417 may help reduce or eliminate the risk of Fermi level pinning between the poly and the high-k dielectric 416 during subsequent processing. Also, the barrier layer 417 may function as a etch stop layer and protection layer during removal of the dummy poly gate as discussed later below. The barrier layer 417 may be formed by various deposition techniques such as ALD, PVD, CVD, or other suitable technique. It should be noted that the interfacial layer 415, high-k dielectric 416, and barrier layer 417 may be alternatively formed in a gate last process as was discussed in
The semiconductor device 400 may further include a polysilicon (or poly) layer 218 formed over the barrier layer 417 by a suitable deposition process. For example, silane (SiH4), di-silane (Si2H6), or di-clorsilane (SiC12H4) may be used as a chemical gas in a CVD process to form the poly layer 218. The poly layer 218 may include a thickness ranging from about 400 to about 2000 angstrom (A). Alternatively, an amorphous silicon layer may optionally be formed instead of the polysilicon layer. The semiconductor device 400 may further include a hard mask layer (not shown) formed on the poly layer 218. The hard mask layer may include silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, and/or other suitable dielectric materials, and may be formed using a method such as CVD or PVD. The hard mask layer may include a thickness ranging from about 100 to about 400 angstrom (A). Additionally, an antireflective coating layer or bottom antireflective coating (BARC) layer may be used to enhance a photolithography process for patterning a photoresist layer. For example, a patterned photoresist layer (not shown) may be formed on the hard mask layer including a gate pattern overlying the nFET 412 device side and a gate pattern overlying the pFET 414 device side. The gate patterns may be used to pattern the hard mask layer by a dry etch or wet etch process.
The patterned hard mask may then be used to form the gate structure 420n in the nFET 412 device side and a gate structure 420p in the pFET 414 device side by a dry etch, wet etch, or combination dry and wet etch process. Accordingly, the gate structures 420n, 420p may each include an interfacial layer 415, high-k dielectric layer 416, a barrier layer 417, a dummy poly gate 218, and/or a hard mask.
After formation of the gate structures 420n, 420p (e.g., gate etching or patterning), it is understood that the semiconductor device 400 may undergo additional CMOS processing to form various features of the nFET 412 and pFET 414. Accordingly, the various features are only briefly discussed herein. In
The method 300 continues with block 306 in which a portion of the dummy gates is removed from the gate structures thereby forming partial trenches in the gate structures. In
The method 300 continues with block 308 in which a portion of the spacers 227 is removed thereby forming a widened portion 235 of the partial trenches. In an embodiment, the portions of the spacers 227 are removed using a dry argon sputtering to form a funnel-shape in the trenches 235. The molecular size of the argon is appropriate for making the funnel-shape. However other elements may produce acceptable results. As shown in
In an embodiment, this process may be performed in a single etcher PVD tool. The argon sputtering may be performed using an argon gas pressure of approximately 3-20 mTorr and at a flow rate of approximately 300-600 sccm. The argon sputtering may have a bias of approximately 200-500 Watts. In an embodiment, the argon sputtering may be performed at a temperature of approximately 0° C.-100° C. The argon sputtering may be performed for approximately 5-30 seconds.
The method 300 continues with block 310 in which a remaining portion of the dummy gates is removed from the gate structures thereby forming full trenches in the gate structures. In
The method 300 continues with block 312 in which a high k gate film and a metal layer is formed to substantially filling in the first and second trenches. In
The method 300 continues with block 314 in which a chemical mechanical polishing (CMP) process is performed. In
It is understood that the semiconductor device 400 may undergo further processing to form various features such as contacts/vias, interconnect metal layers, interlayer dielectric, passivation layers, etc. It should be noted that the techniques and processes disclosed with reference to FIGS. 3 and 4A-4G can also be implemented in the embodiments of FIGS. 1 and 2A-2F disclosed above.
The present invention achieves different advantages in various embodiments disclosed herein. It is understood that different embodiments disclosed herein offer several different advantages, and that no particular advantage is necessarily required for all embodiments. For example, the present disclosed method provides a simple and cost-effective method for forming high-k gate dielectric in a gate last process using a dummy dielectric. As another example, the present disclosed methods provide for less voids in gate fill metal due to a larger opening when filling the gate. Moreover, the present disclosed method provides a simple and cost-effective method for forming metal gates with proper work functions for nFET and pFET devices in a gate last process. Further, the methods and devices disclosed herein may easily be integrated with current CMOS process flow and semiconductor processing equipment. For example, the methods disclosed herein implement materials and processes that are friendly and compatible with the CMOS process flow, and that are inexpensive to incorporate with the process flow.
The foregoing has outlined features of several embodiments so that those skilled in the art may better understand the detailed description that follows. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions and alterations herein without departing from the spirit and scope of the present disclosure. For example, the techniques, methodologies, and processes disclosed with reference to