Embodiments of this disclosure relate generally to bonding and debonding of carrier-workpiece pairs. In particular, various embodiments of debonding temporarily bonded carrier-workpiece pairs by means of applying high pressure solvents are described.
In many applications, a workpiece needs to be thinned or processed with the support of a carrier to make the workpiece mechanically stable. The workpiece can be temporarily bonded to the carrier using adhesives. At end of the application, the workpiece needs to be debonded or separated from the carrier, and cleaned of any residue adhesives. For example, in semiconductor wafer thinning process, the workpiece can be a semiconductor wafer or device wafer on which thousands of chips are finally made. Widespread applications of smartphones, tablets, and portable consumer electronics are driving semiconductor packaging towards thinner, smaller, and more integrated directions. Wafer-level packaging (WLP) techniques is rapidly reducing the size of packages for easier integration into mobile electronics. The wafer thinning process used in device miniaturization and packaging has attracted more and more attention. Thin wafers offer the benefits of improved heat dissipation, three-dimensional (3D) stacking, reduced resistance, and substrate flexibility. In through silicon via (TSV) based 3D-IC wafer level packaging, wafers need to be thinned to less than 100 microns (μm). The thinning process needs to be high throughput and low cost to be suitable for volume production.
Wafer thinning is primarily achieved by mechanical grinding (back-grinding), polishing, and chemical etching. Thin wafers, especially ultra-thin wafers (thickness less than 60 microns or even 30 microns) are very unstable, and more susceptible to stress than traditional thick wafers. During processing, thin wafers may be easily broken and warped. Therefore, temporary bonding to a rigid support carrier is required. Thinned device wafers need to be supported for use on the backside in grinding process and subsequent processes such as photolithography, etching, plating, vacuum deposition, reactive ion etching, and so on.
The present disclosure provides a novel method of debonding or separating a temporarily adhesive-bonded carrier-workpiece pair using high-pressure solvent streams or sprays. The method can be used for processing various workpieces of different shapes such as round, rectangle, or square shapes, of different materials such as silicon, gallium arsenide, sapphire, glass, metal, of different thicknesses, in various applications where the workpieces can be optical lenses, semiconductors, liquid crystal displays (LCD), solar panels, and so on. The method is particularly useful for debonding temporarily adhesive-bonded semiconductor wafers in three-dimensional integrated circuit (3D-IC) semiconductor wafer level packaging.
The disclosed debonding method using high-pressure solvent streams or sprays can advantageously enhance process efficiency, simplify procedures, provide high wafer throughput, and reduce or eliminate defects such as device wafer breakage and internal device damage. The method can greatly increase the range of selection of polymeric adhesives for the use of temporary workpiece bonding and debonding. The use of recyclable polymer adhesive such as thermoplastics is of particular benefit as it can greatly lower the overall cost.
In one aspect of the disclosure, a method of debonding a temporarily bonded carrier-workpiece pair comprises holding in place a carrier-workpiece pair temporarily bonded with an adhesive, and applying a stream of a liquid solvent to the adhesive to debond the carrier-workpiece pair. The liquid solvent is capable of dissolving the adhesive. The stream of the liquid solvent is applied at a pressure ranging from 60 to 10000 pounds per square inch (psi), preferably 300 to 3000 psi.
The stream of the liquid solvent can be applied to the adhesive in the form of a needle, a fan, a blade, or any combination thereof.
The stream of the liquid solvent can be applied with a pump system allowing the stream of the liquid solvent to move in three dimensions (X-Y-Z) relative to the adhesive at a linear or nonlinear velocity.
In some embodiments, the liquid solvent can be heated to a temperature below its flashpoint before applying a stream of the liquid solvent to the adhesive.
In some embodiments, the carrier-workpiece pair is temporarily bonded with a layer of a thermoplastic polymer adhesive. The workpiece can be a semiconductor wafer, an optical lens, quartz, a sapphire wafer, display glass, a liquid crystal display, a thin metal plate, a thin membrane, or a film. In some embodiments, the carrier can be perforated, and the stream of the liquid solvent can be applied to the adhesive from the backside of the carrier.
This Summary is provided to introduce selected embodiments in a simplified form and is not intended to identify key features or essential characteristics of the claimed subject matter, nor is it intended to be used as an aid in determining the scope of the claimed subject matter. The selected embodiments are presented merely to provide the reader with a brief summary of certain forms the invention might take and are not intended to limit the scope of the invention. Other aspects and embodiments of the disclosure are described in the section of Detailed Description.
These and various other features and advantages will become better understood upon reading of the following detailed description in conjunction with the accompanying drawings and the appended claims provided below, where:
Various embodiments of methods for debonding temporarily bonded carrier-workpiece pair are described. It is to be understood that the disclosure is not limited to the particular embodiments described. An aspect described in conjunction with a particular embodiment is not necessarily limited to that embodiment and can be practiced in any other embodiments.
Various embodiments are described with reference to the figures. It should be noted that some figures are not necessarily drawn to scale. The figures are only intended to facilitate the description of specific embodiments, and are not intended as an exhaustive description or as a limitation on the scope of the disclosure. Further, in the figures and description, specific details may be set forth in order to provide a thorough understanding of the disclosure. It will be apparent to one of ordinary skill in the art that some of these specific details may not be employed to practice embodiments of the disclosure. In other instances, well known components may not be shown or described in detail in order to avoid unnecessarily obscuring embodiments of the disclosure.
All technical and scientific terms used herein have the meaning as commonly understood by one of ordinary skill in the art unless specifically defined otherwise. As used in the description and appended claims, the singular forms of “a,” “an,” and “the” include plural references unless the context clearly dictates otherwise. The term “or” refers to a nonexclusive “or” unless the context clearly dictates otherwise.
As used herein, the terms “temporarily bonded,” “temporary bonding,” and their grammatical equivalents, refer to embodiments where the bonding between a carrier and a workpiece is temporary and will be removed upon completion of one or more processing steps on the workpiece.
The workpiece 104 can be a semiconductor device wafer, an optical lens, quartz, a sapphire wafer, display glass, an LED crystal, a thin metal plate, a thin membrane, a film, or the like. The workpiece 104 can be made of silicon, polysilicon, silicon oxide, silicon-germanium, silicon nitride, gallium arsenide, gallium nitride, gallium phosphide, alumina titanium carbide, or silicon carbon. The workpiece 104 can also be metals such as copper, aluminum, steel, gold, tungsten, tantalum, low K dielectrics, metal nitrides, metal alloys, silicides, and any combination thereof. Indeed, any suitable workpiece made of any materials in any form can be used in the method of this disclosure.
The carrier 102 can be any suitable carrier that has sufficient mechanical strength. The carrier 102 can be made of the same material as that of the workpiece 104. In semiconductor temporary wafer bonding and debonding process, the carrier 102 can be made of silicon, glass, etc. During the debonding step using such as solvent spraying as will be described below, the carrier 102 can be applied with a certain degree of pulling force to facilitate separation of the carrier from the workpiece.
Suitable adhesives 106 that can be used in the temporary bonding process include thermoplastic polymers. Polymers of slight crosslinking and still solvable in a solvent may still be used. In some embodiments, thermoplastic polymeric adhesives are preferred because they can be recycled and reused after post debonding reclaim treatment, and therefore the total cost of the whole bonding and debonding process can be greatly reduced. Any suitable polymers can be used so long they meet the specifications as required by the processing conditions such as low outgassing, film uniformity, solubility in solvents, temperature tolerance, etc. The polymers can be polyimides, rubbers, cyclic olefins, polyacrylates, poly methyl methacrylate, polyurethanes, polycarbonates, polyethylene terephthalate, cellulose, polyesters, polystyrenes, epoxies, silicones, polyamides, polysulfones, etc. or combination thereof. Photoresists such as those manufactured by JSR Corporation of Japan and AZ series photoresists manufactured by AZ Electronic Materials (Merck) of Germany can also be used. In some embodiments, the polymers can be used in formulations which contain polymers as binders and other fillers and additives such as antioxidants, plasticizers. In some embodiments, single polymers are preferred for ease of recycling and reuse of the polymers.
The polymeric adhesives 106 can be applied to the carrier 102 using spin coating, spray coating, slot coating, knife coating, and other available coating techniques from solutions. The polymeric adhesives 106 can also be applied in dry film lamination. The adhesives 106 should form as uniform films as possible. Bonding of a workpiece such as a device wafer to a carrier wafer coated with adhesives can be accomplished with bonders commercially available from e.g. EVG of Austria, Suss MicroTec of Germany, Tokyo Electron Ltd. of Japan, and other companies, or inhouse made bonders. In some embodiments, the thickness of the polymer adhesive coated on the carrier may range from 1 to 500 microns.
The adhesive bonded carrier-workpiece pair 110 such as a device wafer-carrier wafer pair can be safely subjected to thinning such as back-grinding and chemical-mechanical polishing (CMP). By way of example, a device wafer 104 may be thinned to have a thickness of less than 100 microns. In some applications, a device wafer 104 may be thinned to have a thickness of less than 60 microns or even 30 microns. After thinning, other backside processing can be carried out too, such as through silicon via (TSV) formation, etching such as deep reactive-ion etching (DRIE), metal and dielectric deposition, patterning such as photolithography, via etching, plasma ashing, bonding pads, passivating, annealing, and any combinations thereof. After these processes, the device wafer 104 is ready to be debonded or separated from the carrier wafer 102 and cleaned of the adhesive.
The debonding step 156 can be critical. It is desirable that the debonding step is high throughput, defect less, damage less, and cost effective. The present disclosure provides a debonding method using high-pressure solvent streams or sprays, which can enhance process efficiency, simplify procedures, provide high wafer throughput, and reduce or eliminate defects such as device wafer breakage and internal device damage. The debonding method provided by the present disclosure also greatly increases the range of selection of polymeric adhesives for use in temporary bonding and debonding as a result of solvent use. The use of recyclable thermoplastics is of particular benefit as it can greatly lower the overall cost. The disclosed debonding method allows separation of the workpiece from the carrier and cleaning to be combined into one integrated step to provide high throughput and lower costs.
In accordance with embodiments of the disclosure, a temporarily adhesive-bonded carrier-workpiece pair is debonded or separated using high-pressure solvent streams or sprays. The carrier-workpiece pair temporarily bonded with an adhesive can be held in place using any suitable means. A stream of a liquid solvent is applied to the adhesive at a high pressure ranging from 60 to 10000 pounds per square inch (psi) to debond the carrier-workpiece pair. The liquid solvent is capable of dissolving the adhesive.
The solvent or solvents used in the debonding method of the disclosure can be a single solvent or a combination of several solvents. The selection of solvents may be dictated by the use of polymer adhesives. The selection of a solvent to a particular polymer generally can be based on the “like dissolves like” principal. Solubility parameter is a factor to consider for selection of a solvent or combination of solvent mixtures. The solvent can also be in the form of a formulation. Many of stripping solutions used in the microelectronics industry can be used. Suitable solvents include n-methylpyrrolidone (NMP), dimethyl sulfoxide (DMSO), ethyl lactate ethyl acetate, butyl acetate, methyl ethyl ketone (MEK), propylene glycol methyl ethylene acetate (PGMEA), acetone, cyclopentenone, tetrahydrofuran (THF), dimethyl acetamide, hydrocarbons, cyclic hydrocarbons, or strippers made of these solvents as main components. Examples of photoresist removers and strippers include AZ100, Technistrip P1316, P1331, NI555, etc. For example, NMP can be used if polyimide type polymer “durimide” made by Fujifilm Holdings Corporation is used as the temporary bonding adhesive. Water-containing solvents (water content between 0 to 100 percent) can also be used for environmental considerations so long they can carry the adhesive away during chemical and mechanical debonding.
Still referring to
The high-pressure stream of liquid solvent 508 can be applied in the form of a needle, blade, fan, or any combination thereof through the use of a suitable nozzle. The stream of the liquid solvent 508 can be targeted to the adhesive 506 in a certain angle e.g. ranging from 0 to 80 degrees with respect to the layer of the adhesive. Alternatively or additionally, the carrier wafer 502 can be perforated so that the high-pressure solvent stream or spray can be applied at the backside of the carrier wafer.
In some embodiments, the nozzle 512 of the pump system can move so that the high-pressure solvent stream 508 can be applied to the adhesive 506 in a particular fashion such as in a scanning fashion. The nozzle can move in a vibrational mode or in a three-dimensional (X-Y-Z) mode to allow the solvent stream move accordingly. The nozzle can move at a linear speed or nonlinear speed. Moving the nozzle and thus the solvent stream can maximize or increase debonding speed. In some embodiment, the solvent can also be heated to a temperature below its flash point for fast removal of the adhesive.
Embodiments of debonding temporarily bonded carrier-workpiece pairs have been described. Those skilled in the art will appreciate that various other modifications may be made. All these or other variations and modifications are contemplated by the inventors and within the scope of the invention.