Patent Application
20200350174
The present invention relates to integrated semiconductor devices, and more particularly to a vertical transistor and method for manufacturing the same.
As the critical dimension of metal oxide semiconductor field effect transistor (MOSFET) devices continues to shrink, the short channel effect becomes more problematic. Fin field effect transistor (FinFET) devices have better control capability of gates than planar MOSFET devices to effectively suppress the short channel effect. Gate-all-around (GAA) devices have even better control ability than FinFET devices to more effectively suppress the short channel effect.
A nanowire vertical transistor is an example of a GAA device.
In some conventional methods of manufacturing nanowire vertical transistors, after nanowires 102 are formed on a substrate 101, a contact material 103 is then formed on substrate 101 and on upper surfaces of nanowires 102 by an anisotropic deposition, as shown in
In some other conventional methods of manufacturing a nanowire vertical transistor, after nanowires 102 are formed on a substrate 101, a gate dielectric layer 104 is formed on sidewalls of nanowires 102. A contact material 103 is formed on substrate 101 and on upper surfaces of nanowires by an anisotropic deposition, as shown in
Therefore, there is a need for improved methods for manufacturing a fin-type semiconductor device to overcome these drawbacks.
The present inventors discovered the above-described problems and provide a novel technical solution for solving at least one of the above-described problems.
In one aspect of the present invention, a method for manufacturing a semiconductor device is provided. The method may include providing a substrate structure including a substrate and a semiconductor column vertically protruding from the substrate, sequentially forming a first protective layer and a second protective layer on the substrate, etching a portion of the second protective layer to expose a portion of the first protective layer on the substrate and a portion of the first protective layer on an upper surface of the semiconductor column, removing the exposed portion of the first protective layer on the substrate to expose a lower portion of the semiconductor column, removing a remaining portion of the second protective layer, and forming a first contact material layer on the substrate and in contact with the lower portion of the semiconductor column.
In one embodiment, the substrate structure further includes an insulating layer on a region of the substrate not covered by the semiconductor column. And removing the exposed portion of the first protective layer on the substrate includes removing the insulating layer.
In one embodiment, the semiconductor column includes a semiconductor layer and a hardmask layer on the semiconductor layer, the method further includes, prior to forming the first contact material layer, removing the hardmask layer.
In one embodiment, the semiconductor column further includes a buffer layer between the semiconductor layer and the hardmask layer.
In one embodiment, the first protective layer includes silicon oxide, and the second protective layer includes silicon nitride.
In one embodiment, the method further includes removing a remaining portion of the first protective layer.
In one embodiment, the method further includes forming a first insulating material layer on the first contact material layer, forming a gate dielectric material layer on the semiconductor column and on the first insulating material layer, forming a gate material layer on the gate dielectric material layer, forming a second insulating material layer on the gate material layer, the second insulating material layer having an upper surface lower than an upper surface of the semiconductor column, removing a portion of the gate dielectric material layer on the semiconductor column above the upper surface of the second insulating material layer to expose an upper portion of the semiconductor column, and forming a second contact material layer on the upper portion of the semiconductor column.
In one embodiment, the first protective layer includes a dielectric material layer, the method further includes forming a first insulating material layer on the first contact material layer, forming a gate material layer on the first insulating material layer, forming a second insulating material layer on the gate material layer, the second insulating material layer having an upper surface lower than an upper surface of the semiconductor column, removing a portion of the first protective layer on sidewalls of the semiconductor column above the upper surface of the second insulating material layer to expose an upper portion of the semiconductor column, and forming a second contact material layer on the upper portion of the semiconductor column.
In one embodiment, the method may further include forming a first contact extending to the first contact material layer, a second contact extending to the gate material layer, and a third contact in contact with the second contact material layer.
In one embodiment, the second contact material layer comprises tungsten, nickel, cobalt, titanium, or platinum.
In one embodiment, the semiconductor column is a nanowire. In one embodiment, the semiconductor column includes an array of semiconductor pillars. In one embodiment, the semiconductor column includes silicon.
In one embodiment, the first contact material layer includes tungsten, nickel, cobalt, titanium, or platinum.
In one aspect of the present invention, a semiconductor device includes a substrate, a semiconductor column vertically protruding from the substrate, and a first contact material layer on the substrate and in contact with a lower portion of the semiconductor column, the first contact material layer includes a recess adjacent to the semiconductor column.
In one embodiment, the semiconductor device also includes a first insulating material layer on the first contact material layer, a gate dielectric material layer on a middle portion of the semiconductor column and on the first insulating material layer exposing an upper portion of the semiconductor column, a gate material layer on the gate dielectric material layer, a second insulating material layer on the gate material layer, the second insulating material layer having an upper surface lower than an upper surface of the semiconductor column, and a second contact material layer on the upper portion of the semiconductor column.
In one embodiment, the semiconductor device further includes a first contact extending to the first contact material layer, a second contact extending to the gate material layer, and a third contact in contact with the second contact material layer.
In one embodiment, wherein the semiconductor column is a nanowire. In one embodiment, the semiconductor column includes an array of semiconductor pillars. In one embodiment, the semiconductor column includes silicon.
In one embodiment, the first contact material layer includes tungsten, nickel, cobalt, titanium, or platinum. In one embodiment, the second contact material layer includes tungsten, nickel, cobalt, titanium, or platinum.
In yet another aspect of the present invention, a semiconductor device may include a substrate, a semiconductor column vertically protruding from the substrate, a gate dielectric material layer on a middle portion of the semiconductor column exposing an upper portion and a lower portion of the semiconductor column, a first contact material layer on the substrate and in contact with the lower portion of the semiconductor column, a first insulating material layer on the first contact material layer, a gate material layer on the first insulating material layer, a second insulating material layer on the gate material layer and having an upper surface flush with an upper surface of the gate dielectric material layer, and a second contact material layer on the upper portion of the semiconductor column.
In one embodiment, the first contact material layer covers a portion of the gate dielectric material layer.
In one embodiment, the semiconductor may further include a first contact extending to the first contact material layer, a second contact extending to the gate material layer, and a third contact in contact with the second contact material layer.
The following detailed description together with the accompanying drawings will provide a better understanding of the nature and advantages of the present invention.
The accompanying drawings, referred to herein and constituting a part hereof, illustrate embodiments of the disclosure. The drawings together with the description serve to explain the principles of the invention.
Embodiments of the present invention now will be described more fully hereinafter with reference to the accompanying drawings. The invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. The features may not be drawn to scale, some details may be exaggerated relative to other elements for clarity. Like numbers refer to like elements throughout.
It will be understood that when an element such as a layer, region or substrate is referred to as being “on” or extending “onto” another element, it can be directly on or extend directly onto the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or extending “directly onto” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.
Relative terms such as “below” or “above” or “upper” or “lower” or “horizontal” or “lateral” or “vertical” may be used herein to describe a relationship of one element, layer or region to another element, layer or region as illustrated in the figures. It will be understood that these terms are intended to encompass different orientations of the device in addition to the orientation depicted in the figures.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an”, and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises”, “comprising”, “includes”, and/or “including” when used herein, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
Embodiments of the invention are described herein with reference to cross-sectional illustrations that are schematic illustrations of idealized embodiments and intermediate structures) of the invention. The thickness of layers and regions in the drawings may be enlarged relative to other layers and regions for clarity. Additionally, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, embodiments of the invention should not be construed as limited to the particular shapes of regions illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, an implanted region illustrated as a rectangle will, typically, have rounded or curved features and/or a gradient of implant concentration at its edges rather than a discrete change from implanted to non-implanted region. Likewise, a buried region formed by implantation may result in some implantation in the region between the buried region and the surface through which the implantation takes place. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the actual shape of a region of a device and are not intended to limit the scope of the invention.
References in the specification to “one embodiment”, “an embodiment”, “an example embodiment”, “some embodiments”, etc., indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.
Embodiments of the present invention now will be described more fully hereinafter with reference to the accompanying drawings, in which embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.
Step 202: providing a substrate structure including a substrate and a semiconductor column disposed substantially vertical in relation to the surface of the substrate;
Step 204: sequentially forming a first protection layer and a second protection layer on the substrate;
Step 206: etching the second protection layer to expose a portion of the first protective layer on the substrate and a portion of the first protective layer on the upper surface of the semiconductor column.
Step 208: removing the exposed portion of the first protective layer on the substrate to expose a surface of the substrate and a lower portion of the semiconductor column.
Step 210: removing a remaining second protective layer.
Step 212: forming a first contact material layer on the substrate and in contact with the lower portion of the semiconductor column.
In the embodiment, a first protective layer and a second protective layer are provided so that a first contact material layer is not formed on sidewalls of the semiconductor column. On the other hand, the first contact material layer formed on the surface of the substrate is in contact with the lower portion of the semiconductor column to prevent an increase in the series resistance of a source (e.g., formed at the lower portion of the semiconductor column).
The method of manufacturing a semiconductor device according to one embodiment of the present invention will be described in detail with reference to
Referring to
Substrate 301 may be a silicon substrate, a silicon-on-insulator (SOI) substrate, and the like. Of course, the present invention is not limited thereto. Semiconductor column 302 may include, but is not limited to, silicon, III-V compound semiconductor material, or the like.
In one embodiment, semiconductor column 302 may include an array of semiconductor pillars. The array of semiconductor pillars may include one or more semiconductor pillars. In one embodiment, semiconductor column 302 may be a nanowire. As used herein, the term “nanowire” is referred to a semiconductor wire having an undoped material or a controlled doping and composite in the longitudinal or radial directions, or in both longitudinal and radial directions. The nanowire may include different materials when viewed longitudinally. The nanowire may have various cross-sectional shapes in a transverse direction perpendicular to the longitudinal direction. The various cross-sectional shapes may be circular, oval, square, rectangular, and hexagonal.
In one embodiment, referring to
In one embodiment, the substrate structure may further include an insulating layer 303 (e.g., silicon oxide) on a region where substrate 301 is not covered by semiconductor column 302. Insulating layer 303 will be removed in a subsequent process step to expose a lower portion of semiconductor column 302. In one embodiment, insulating layer 303 may be formed by first depositing an insulating material layer on the substrate structure including substrate 301 and semiconductor column 302; the insulating material layer is then planarized, e.g., using a chemical mechanical polishing process. Thereafter, the planarized insulating material layer is etched back to form insulating layer 303.
It is to be understood that the term “vertically protruding semiconductor column” or “vertical semiconductor column” refers to the longitudinal orientation of the semiconductor column in the vertical direction in relation to the flat surface of the substrate. As used herein, the term “substantially vertical” refers to a vertical orientation within the process variations.
Next, referring to
In one embodiment, first protective layer 304 may include silicon oxide, and second protective layer 305 may include silicon nitride. In one exemplary embodiment, first protective layer 304 includes SiO2, and second protective layer 305 includes carbon-containing silicon nitride, e.g., SiCN. Of course, the present invention is not limited thereto, first protective layer 304 and second protective layer 305 may include other materials as long as first protective layer 304 and second protective layer 305 have different etching selection ratios.
Next, referring to
Next, referring to
It will be appreciated that, in the case where the substrate structure includes insulating layer 303, removing the exposed portions of first protective layer 304 also includes removing insulating layer 303. In practical applications, the horizontal portion of first protective layer 304 may be relatively thin, the presence of insulating layer 303 and its removal ensure that the lower portion of semiconductor columns 302 is exposed. Note that the height of the exposed lower portion of semiconductor column 302 depends on the thickness of first protective layer 304. Alternatively, in the case where substrate structure includes insulating layer 303, the height of the exposed lower portion of semiconductor column 302 depends on the thickness of insulating layer 303 and the thickness of first protective layer 304. Further, referring to
Next, referring to
In the case where semiconductor column 302 includes hardmask layer 332, hardmask layer 332 is first removed prior to forming a first contact material layer. In one exemplary embodiment, hardmask layer 332 may be removed at the same time while the remaining portion of second protective layer 305 is being removed.
Thereafter, referring to
In one exemplary embodiment, a first contact material layer may be deposited on the structure shown in
In one embodiment, first contact material layer 306 may include tungsten, nickel, cobalt, titanium, or platinum. In one embodiment, in the case where first contact material layer 306 includes tungsten, a barrier layer, such as a stack of Ti, Ti/TiN, may be formed between first contact material layer 306 and substrate 301 and between first contact material layer 306 and the lower portion of semiconductor column 302.
A method of manufacturing a semiconductor device according to an embodiment of the present invention has been described in the above sections. Thereafter, a back-end of line process may be performed according to actual requirements. The following is a description of subsequent processes after obtaining the semiconductor structure in
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to
In one exemplary embodiment, a first contact hole may be formed extending through first insulating material layer 401 and second insulating material layer 404 to first contact material layer 306, a second contact hole may be formed through second insulating material layer 404 to gate material layer 403; and a metal material is then deposited filling the contact holes. Thereafter, the metal material may be patterned to form first contact 406 (also referred to as a source contact), second contact 407 (also referred to as a gate contact), and third contact 408 (also referred to as a drain contact).
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to
In one exemplary embodiment, contact holes may first be formed in first insulating material layer 501 and second insulating material layer 503; and a metal material is then deposited filling the contact holes. Thereafter, the metal material may be patterned to form first contact 505 (also referred to as a source contact), second contact 506 (also referred to as a gate contact), and third contact 507 (also referred to as a drain contact).
It should be noted that the terms “upper, lower, and middle portions” of the semiconductor column are used in a relational sense and are intended to describe those portions of the semiconductor column that are in the vicinity of the top, the middle and the bottom of the semiconductor column, respectively. As used herein, the upper portion is in the vicinity of the top, the lower portion is in the vicinity of the bottom of the semiconductor column, and the middle portion is between the upper and lower portions.
Embodiments of the present invention also provide a semiconductor device. Referring to
In one embodiment, referring to
The semiconductor device also includes a gate material layer 403 on gate dielectric material layer 402, and a second insulating material layer 404 on gate material layer 403. Second insulating material layer 404 has an upper surface substantially flush with an upper surface of gate dielectric material layer 402 on the sidewalls of semiconductor column 302.
The semiconductor device also includes a second contact material layer 405 on the upper portion of semiconductor column 302. Second contact material layer 405 may include a metal, e.g., tungsten, nickel, cobalt, titanium, or platinum.
In one embodiment, referring to
Embodiments of the present invention also provide a second semiconductor device. Referring to
The second semiconductor device also includes a first insulating layer 501 on first contact material layer 306, a gate material layer 502 on first insulating layer 501, a second insulating material layer 503 on gate material layer 502. Second insulating material layer 503 has an upper surface that is substantially flush with the upper surface of gate dielectric material layer 304.
The second semiconductor device also includes a second contact material layer 504 on the upper portion of semiconductor column 302.
In one embodiment, referring to still
In one embodiment, referring to
In one embodiment, semiconductor column 302 in each of the above-described semiconductor devices may be a nanowire. In one embodiment, semiconductor column 302 in each of the above-described semiconductor devices may include an array of semiconductor pillars. In one embodiment, semiconductor column 302 in each of the above-described semiconductor devices may include silicon.
It is to be understood that the above described embodiments are intended to be illustrative and not restrictive. Many embodiments will be apparent to those of skill in the art upon reviewing the above description. The scope of the invention should, therefore, be determined not with reference to the above description, but instead should be determined with reference to the appended claims along with their full scope of equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201710222205.8 | Apr 2017 | CN | national |
This application is a divisional of U.S. patent application Ser. No. 15/918,741, filed on Mar. 12, 2018, which claims priority to Chinese patent application No. 201710222205.8, filed with the State Intellectual Property Office of People's Republic of China on Apr. 7, 2017, the content of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15918741 | Mar 2018 | US |
| Child | 16933761 | US |