METHOD OF FORMING DIELECTRIC FILMS, NEW PRECURSORS AND THEIR USE IN SEMICONDUCTOR MANUFACTURING

Abstract
The application relates to a method of deposition on a substrate, of a metal containing dielectric film comprising a compound of the formula (M11-aM2a)ObNc, wherein 0≦a<1, 0
Description
BACKGROUND

The invention relates to a method of forming high-k dielectric films such as hafnium or zirconium oxides or oxynitrides and their use for manufacturing semi-conductors.


With the shrink of the critical dimensions of the future generation of semi-conductor devices, the introduction of new materials, especially having high dielectric constant, is required. In CMOS architectures, high-k dielectrics are required to replace SiO2 which reaches its physical limits, having typically a SiO2 equivalent thickness of about 1 nm.


Similarly, high-k dielectrics are required in Metal-Insulator-Metal architectures for RAM applications. Various metal compositions have been considered to fulfill both the materials requirements (dielectric constant, leakage current, crystallization temperature, charge trapping) and the integration requirements (thermal stability at the interface, dry etching feasibility . . . ).


The Group IV based materials, such as HfO2, HfSiO4, ZrO2, ZrSiO4, HfZrO4, HfLnOx (Ln being selected from the group comprising scandium, yttrium and rare-earth elements) and more generally HfMOx and ZrMOx, M being an element selected from Group II, Group IIIa and Group IIIb, or a transition metal, are among most promising materials. Furthermore, Group IV metals composition can also be considered for electrode and/or Cu diffusion barrier applications, such as TiN for mid-gap metal gate and HfN, ZrN, HfSi, ZrSi, HfSiN, ZrSiN, TiSiN for MIM electrodes.


The main industrial options to enable the deposition of such thin films with a reasonable throughput and an acceptable purity are vapor phase deposition techniques, such as MOCVD (Metal-organic Chemical Vapor Deposition) or ALD (Atomic Layer Deposition). Such deposition processes require metal precursors that must fulfill drastic requirements for a proper industrial use. Metal-organic or metal-halide precursors are required for those processes. Various hafnium and zirconium metal-organic compounds have been considered as precursors to enable such a deposition.


Halides such as HfCl4, ZrCl4 are the most common Hf/Zr precursors and have been widely described. Kim et al. disclosed the use of HfCl4 for the deposition of HfO2 by ALD (Kim et al., Electrochem Soc Proceedings 2005-05, 397, 2005). However, some by-products generated during the deposition process, such as HCl or Cl2, can cause surface/interface roughness that can be detrimental to the final properties. Other possible byproducts, depending on the oxygen source used, may be hazardous. For instance, OCl2, through the OCl fragment by QMS, has been detected as a byproduct of the reaction between HfCl4 and O3. Moreover, in the case of high-k oxide, Cl or F impurities are highly detrimental to the final electrical properties.


Triyoso et al. and Chang et al. studied the use of Hf(OtBu)4 for HfO2 MOCVD and ALD, respectively [Triyoso et al.; J. Electrochem. Soc., 152(3), G203-G209 (2005); Chang et al.; Electrochem. Solid. State Let., 7(6), F42-F44 (2004)]. Williams et al. have evaluated Hf(mmp)4 and Hf(OtBu)2(mmp)2 for MOCVD of HfO2. In WO2003035926, Jones et al. disclose solid Ti, Hf, Zr and La precursors improved with donor functionalized alkoxy ligand (1-methoxy-2-methyl-2-propanolate [OCMe2CH2OMe, mmp]) which helps inhibiting oligomerization of Zr and Hf alkoxide compounds and increasing their stability towards moisture. However, all those alkoxide precursors have the drawback not to enable self-limited deposition in ALD process as suggested by Potter et al. (R. J. Potter, P. R. Chalker, T. D. Manning, H. C. Aspinall, Y. F. Loo, A. C. Jones, L. M. Smith, G. W. Critchlow, M. Schumacher, Chem. Vap. Deposition, 2005, 11, No 3, 159-167).


Alkylamides precursors such as Hf(NEtMe)4, Hf(NMe2)4, Hf(NEt2)4 have been widely disclosed in the literature [Senzaki et al, J. Vac. Sci. Technol. A 22(4) July/August 2004; Haussmann et al, Chem. Mater. 2002, 14, 4350-4353; Kawahara et al., J. Appl. Phys., Vol 43, No 7A, 2004, pp 4129-4134; Hideaki et al., JP 2002-093804; Metzner et al. U.S. Pat. No. 6,858,547; Dip et al. US 2005/0056219 A1]. Group IV alkylamides are both suitable for ALD and MOCVD processes. Furthermore, some are liquid at room temperature (Hf(NEt2)4 and Hf(NEtMe)4) and of sufficient volatility, and they allow self-limited ALD at low temperature for a limited thermal budget process. However, Group IV alkylamides, alkylamides in particular Zr compounds, have several drawbacks, among which they may decompose during the distribution to some extent leading to a possible clogging of the feeding line or the vaporizer, they may generate particles during deposition, they may entail non-uniform compositions during deep trenches deposition processes, and they only allow a narrow self-limited ALD temperature window, hence reducing the process window. In particular, Zr(NEtMe)4 may decompose in the distribution lines and generate particles above 170° C. which is a common distribution temperature. Hf(NEtMe)4 is more thermally stable yet do not afford self-limited atomic layer deposition above 300° C. due to thermal decomposition.


In WO 2007/055088, Thenappan et al. disclose hafnium and zirconium guanidinates complexes and their application for vapor phase deposition. Hf(NEt2)2[(NiPr—CNEt2]2 is given as example. Hafnium and zirconium guanidinates are however generally solids with a very limited volatility. As exemplified in thermal gravimetric analysis, one may not obtain Hf(NEt2)2[(NiPr—CNEt2]2 in vapour phase, without a risk of thermal decomposition and a subsequent particle generation.


Lehn et al. (Chem. Vap. Deposition, 2006, 12, 280-284) disclose tetrakis(trimethylhydrazido) zirconium [Zr(NMeNMe2)4,] and hafnium and their use for low temperature CVD. The exemplified compounds have an acceptable volatility (sublimation at 0.06 Torr, 90° C. reported) but they are solid at room temperature.


Carta et al. disclose the use of bis(cyclopentadienyl)bisdimethyl hafnium, [HfCp2Me2] (Carta et al. discloses in Electrochem Soc Proceedings, 260, 2005-09, 2005) and several authors (Codato et al., Chem Vapor Deposition, 159, 5, 1995; Putkonen et al., J Mater Chem, 3141, 11, 2001; Niinisto et al., Langmuir, 7321, 21, 2005) proposed a new family of Zr and Hf compounds as alternatives to hafnium and zirconium alkylamides: Bis(cyclopentadienyl) bisdimethyl hafnium, bis(cyclopentadienyl) bisdimethyl zirconium, which allow an efficient ALD deposition process with an ALD window up to 400° C. and an achievement of films with less than 0.2% C in optimized conditions with H2O as co-reactant. However, HfCp2Me2 and ZrCp2Me2 both have the drawback of being solid products at room temperature (HfCp2Me2 melting point is 57.5° C.). This prevents IC makers to use those precursors in an industrial manner, that is using delocalized containers filling, and entail both facilitation and process issues.


In U.S. Pat. No. 6,743,473, Parkhe et al. disclose the use of (Cp(R)n)x(MHy-x, to make a metal and/or a metal nitride layer, where M is selected from tantalum, vanadium, niobium and hafnium, Cp is cyclopentadienyl, R is an organic group. Only examples of tantalum and niobium cyclopentadienyl compounds are disclosed. However, no liquid precursor or a precursor having a melting point lower than 50° C. is disclosed.


Liquid bis(cyclopentadienyl) derivatives have recently been proposed by Heys et al. in WO 2006/131751 A1. However, they still present the disadvantage of limited volatility and also present large steric hindrance that may limit the achieved growth rate.


Today, there is a need for providing liquid or low melting point (<50° C.) group IV precursor compounds, and in particular Hf and Zr compounds, that would allow simultaneously a proper distribution (physical state, thermal stability at distribution temperatures), a wide self-limited ALD window, and a deposition of pure films either by ALD or MOCVD.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a Thermal Gravimetric Analysis (TGA) graph showing the percent residual mass versus temperature for (ethylcyclopentadienyl)tris(dimethylamino)zirconium [Zr(EtCp)(NMe2)3]; and



FIG. 2 is a TGA graph showing the percent residual mass versus temperature in open cup and closed cup configuration for Zr(EtCp)(NMe2)3 and tetrakis(ethylmethylamino)zirconium [Zr(NEtMe)4].





DESCRIPTION OF PREFERRED EMBODIMENTS

According to the invention, certain cyclopentadienyl or pentadienyl based group IV metal-organic precursors have been found suitable for the deposition of Group IV metal containing thin films by either ALD or MOCVD processes and to have the following advantages:

    • They are liquid at room temperature or having a melting point lower than 50° C.,
    • They are thermally stable to enable proper distribution (gas phase or direct liquid injection) without particles generation,
    • They are thermally stable to allow wide self-limited ALD window, 4) allowing deposition of a variety of Group IV metals containing films, including ternary or quaternary materials, by using one or a combination of co-reactants (selected from the group comprising of H2, NH3, O2, H2O, O3, SiH4, Si2H6, Si3H8, TriDMAS, BDMAS, BDEAS, TDEAS, TDMAS, TEMAS, (SiH3)3N, (SiH3)2O, TMA or an aluminum-containing precursor, TBTDET, TAT-DMAE, PET, TBTDEN, PEN, lanthanide-containing precursors such as Ln(tmhd)3 . . . ).


According to a first embodiment, the invention relates to a method of deposition on a substrate, of at least one metal containing dielectric film comprising a compound of the formula (I):





(M11-aM2a)ObNc,  (I)


wherein:


0≦a<1,


0<b≦3, preferably 1.5≦b≦2.5;


0≦c≦1,


M1 represents a metal selected from hafnium (Hf), zirconium (Zr) and titanium (Ti); and


M2 represents a metal atom selected from magnesium (Mg), calcium (Ca), zinc (Zn), bore (B), aluminum (A), indium (In), silicon (Si), germanium (Ge), tin (Sn), hafnium (Hf), zirconium (Zr), titanium (Ti), vanadium (V), niobium (Nb), tantalum (Ta); and the Lanthanides atoms, more particularly scandium (Sc), yttrium (Y) and lanthanum (La) and rare-earth metal atoms, which comprises the following steps:

    • A step a) of providing a substrate into a reaction chamber;
    • A step (b) of vaporizing at least one M1 metal containing precursor of the formula (II):





(R1yOp)x(R2tCp)zM1R′4-x-z  (II)


wherein:


M1 is as hereinabove defined;


0≦x≦3, preferably x=0 or 1;


0≦z≦3, preferably z=1 or 2;


1≦(x+z)≦4;


0≦y≦7, preferably y=2 0≦t≦5, preferably t=1;


(R1yOp) represents a pentadienyl (Op) ligand, which is either unsubstituted or substituted by one or more R1 groups, y representing the number of substituting R1 groups on said pentadienyl ligand;


(R2, Cp) represents a cyclopentadienyl (Cp) ligand, which is either unsubstituted or substituted by one or more R2 groups, t representing the number of substituting R1 groups on said cyclopentadienyl ligand;


R1 and R2, are identical or different and are independently selected from the group consisting of the chloro group, the linear or branched, alkyl groups having from one to four carbon atoms, the N-alkyl amino groups, wherein the alkyl group is linear or branched and has from one to four carbon atoms, the N,N-dialkyl amino groups, wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms, the linear or branched alkoxy groups, having from one to four carbon atoms, the alkylsilylamides groups, the amidinates groups and the carbonyl group;


R′ represents a ligand independently selected from the group consisting of the hydrogen, fluoro, chloro, bromo or iodo atoms, the linear or branched, alkyl groups having from one to four carbon atoms, the N-alkyl amino groups, wherein the alkyl group is linear or branched and has from one to four carbon atoms, the N,N-dialkyl amino groups, wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms, the linear or branched alkoxy groups, having from one to four carbon atoms, the alkylsilyl amino groups wherein the alkyl group is linear or branched and has from one to four carbon atoms, the dialkylsilyl amino groups wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms, the trialkylsilyl amino groups wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms, the amidinates groups and the carbonyl, being understood that, if said formula (II) comprises more than one R′ groups, each R′ may be identical or different one from another,


to form a first gas phase metal source;

    • Optionally a step b′) of vaporizing at least one M2 metal containing precursor, M2 being as hereinabove defined; to form an optional second gas phase metal source;
    • A step c) of introducing said first gas phase metal source and said optional second gas phase metal source, in the reaction chamber, in order to provoke their contact with said substrate, to generate the deposition of a metal containing dielectric film comprising a compound of the formula (I) as hereinbefore defined, on said substrate;


      provided that, if the at least one metal containing dielectric film to be formed comprises the compound of the formula (I′):





M11O2  (I′),


corresponding to the formula (I), as hereinbefore defined wherein, a=0, b=2, and c=0, and if the M1 metal containing precursor, which is involved in step b), is a compound of the formula (II′):





(R2tCp)2M1R′2  (II′)


corresponding to the formula (II) as hereinabove defined wherein x=0, and z=2, in said formula (II′), t>0 in at least one of the two (R2tCp) ligands.


In the method as hereinabove defined, the at least one metal containing precursor of the formula (II) and if necessary, the least one M2 metal containing precursor, have a melting point generally below 50° C., preferably below 35° C. and they are preferably liquid at room temperature.


According to a particular embodiment of the method as hereinbefore defined, the vaporization step b) and if necessary, the vaporization step b′) are achieved by introducing a carrier gas into a heated container containing the at least one M1 metal containing precursor of the formula (II):





(R1yOp)x(R2tCp)zM1R′4-x-z  (II)


and if necessary, both the at least one M2 metal containing precursor. The container is preferably heated at a temperature allowing to get the said metal sources in liquid phase and at a sufficient vapor pressure. If necessary, one or both metal precursors may be mixed to a solvent or to a mixture of solvents and/or to a stabilizer. The said solvent is for example selected from octane, hexane, pentane or tetramethylsilane. The concentration of the metal precursors in the solvant or in the mixture of solvents is usually between 0.01 M and 0.5M and is more particularly around 0.05M. The carrier gas is selected, without limitation, from Ar, He, H2, N2 or mixtures of thereof.


If necessary, the container may be heated at temperatures in the range of 80-110° C. Those skilled in the art will consider that the temperature of the container can be adjusted to control the amount of precursor to be vaporized.


The carrier gas flow is usually comprised between 10 sccm (standard cubic centimeter) and 500 sccm. Preferably, the carrier gas flow is comprised between 50 sccm and 200 sccm.


According to another particular embodiment of the method as hereinbefore defined, the vaporization step b) and if necessary, the vaporization step b′) are achieved by introducing in a liquid form, the M1 metal containing precursor of the formula (II):





(R1yOp)x(R2tCp)zM1R′4-x-z  (II)


and if necessary both the M2 metal containing precursor to a vaporizer where it is vaporized. If necessary, one or both metal precursors may be mixed to a solvent or to a mixture of solvents and/or to a stabilizer. The said solvent is for example selected from octane, hexane, pentane or tetramethylsilane. The concentration of the metal precursors in the solvent or in the mixture of solvents is usually between 0.01 M and 0.5M and is more particularly around 0.05M.


According to a more particular embodiment, the vaporization step b) and the vaporization step b′) are combined in one vaporization step b″) of both sources.


During the step c) of the method as hereinbefore defined, the vaporized metal containing precursor is introduced into a reaction chamber where it is contacted to a substrate.


In the context of the present invention, substrate means any substrate used in the semiconductors manufacturing, which, because of their technical function, requires to be coated by metal containing films. Such substrates are for example not only selected from silicon substrates (Si), silica substrates (SiO2), silicon nitride substrates (SiN) or silicon oxy nitride substrates (SiON), but also from tungsten substrates (W) or noble metal substrates such as for example, Platinum substrates (Pt), Palladium substrates (Pd), Rhodium substrates (Rh) or gold substrates (Au).


The substrate is heated until the required temperature to obtain the desired film with a sufficient growth rate and with the desired physical state and composition.


The temperature during step c), usually ranges from 150° C. to 600° C. Preferably the temperature is lower or equal to 450° C.


The pressure in the reaction chamber is controlled to obtain the desired metal containing film with a sufficient growth rate. The pressure during step c) usually ranges from around 1 mTorr (0.1333224 Pa) to around 100 Torr (13332.24 Pa).


In the context of the present invention, the M2 metal containing precursor, is selected from the group consisting of:


Silicon derivatives or their Germanium homologues, such as:


disiloxane, trisilylamine, disilane, trisilane, alkoxysilane of the formula: (III1)





SiHx(OR3)4-x,  (III1)


wherein: 0≦x≦3 and R3 represents a linear or branched hydrocarbon group having 1 to 6 carbon atoms;


silanol derivative of the formula (III2):





Si(OH)x(OR4)4-x  (III2)


wherein: 1≦x≦3 and R4 represents a linear or branched alkyl group, having 1 to 6 carbon atoms, preferably Si(OH)(OR4)3 and more preferably Si(OH)(OtBu)3;


aminosilane derivative of the formula (III3):





SiHx(NR5R6)4-x  (III3)


wherein: 0≦x≦3 and R5 and R6 are identical or different and independently represents an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms, preferably SiH(NMe2)3 (TriDMAS); SiH2(NHtBu)2 (BTBAS); SiH2(NEt2)2 (BDEAS)) and mixtures thereof;


Aluminum derivatives, such as trimethylaluminum [Al(CH3)3], dimethyl aluminum hydride [AlH(CH3)2], alkoxyalane of the formula (IV1):





AlR8x(OR7)3-x  (IV1)


wherein: 0≦x≦3 and R7 represents a linear or branched alkyl having 1 to 6 carbon atom, and R8, identical to or different from R7, represents an hydrogen atom, or preferably AlR9R10(OR7), with R9 and R10 identical or different, which independently represent an linear or branched alkyl having 1 to 6 carbon atoms, most preferably AlMe2(OiPr);


amidoalane of the formula (IV2):





AlR11x(NR12R13)3-x  (IV2)


wherein: 0≦x≦3 and R12 and R13 identical or different, represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms, and R11, identical to or different from R7 and, represents an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms;


Tantalum derivatives, such as: Ta(OMe)5, Ta(OEt)5, Ta(NMe2)5, Ta(NEt2)5, Ta(NEt2)5, a tantalum derivative of the formula (V1):





Ta(OR14)4[O—C(R15)(R16)—CH2—OR17]  (V1)


wherein R14, R15, R16 and R17, identical or different, independently represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms, preferably Ta(OEt)4(OCMe2CH2-OMe) (TAT-DMAE), a tantalum derivative of the formula (V2):





Ta(OR18)4[O—C(R19)(R20)—CH2—N(R21)(R22)]  (V2)


wherein R18, R19, R21 and R22, identical or different, independently represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms, a tatalum derivative of the formula (V3):





Ta(═NR24)(NR25R26)3  (V3)


wherein R24, R25 and R26, identical or different, independently represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms;—


Niobium derivatives, such as Nb(OMe)5, Nb(OEt)5, Nb(NMe2)5, Nb(NEt2)4, Nb(NEt2)5, a niobium derivative of the formula (VI1):





Nb(OR27)4(O—C(R28)(R29)—CH2—OR30)  (VI1)


wherein R27, R28, R29 and R30, identical or different, independently represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms, preferably Nb(OEt)4(OCMe2CH2—OMe) (NBT-DMAE), a niobium derivative of the formula (VI2):





Nb(OR31)4[O—C(R32)(R33)—CH2—N(R34)(R35)]  (VI2)


wherein R31, R32, R33, R34 and R35, identical or different, independently represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms, a niobium derivative of the formula (VI3):





Nb(═NR36)(NR37R38)3  (VI3)


wherein R36, R37 and R38, identical or different, independently represent an hydrogen atom or a linear or branched alkyl having 1 to 6 carbon atoms;


lanthanide derivatives, such as scandium derivatives, yttrium derivatives, cerium derivatives, praseodinum derivatives, gadolinium derivatives, dysprosium derivatives, erbium derivatives, lanthanum derivatives, a derivative with at least one □-diketonate ligand or at least a cyclopentadienyl ligand optionally substituted with one or several linear or branched alkyl groups having 1 to 6 carbon atoms;


divalent metal derivatives, such as strontium (Sr), barium (Ba), magnesium (Mg), calcium (Ca) or zinc (Zn) derivatives, with at least one β-diketonate ligand or at least a cyclopentadienyl ligand optionally substituted with one or several linear or branched alkyl groups having 1 to 6 carbon atoms;


other metal derivatives such as tungsten (W), molybdenum (Mo), hafnium (Hf) or zirconium (Zr) derivatives, for example the alkoxy derivatives, the amino derivatives or adducts containing these species, being understood that said derivatives are not compounds of the formula (II) as hereinbefore defined.


According to another particular embodiment, the method as hereinbefore defined, comprise:

    • A step d), wherein the at least one M1 metal containing precursor of the formula (II), and if necessary, the at least one M2 metal containing precursor, is mixed to at least one reactant specie prior to step c).


In the context of the invention, the at least one reactant specie is chosen in relation to the targeted metal based film, which is expected


According to another embodiment, the reactant specie is an oxygen source and more particularly oxygen (O2), oxygen containing radicals O* or OH*, for instance generated by a remote plasma, ozone (O3), moisture (H2O) and H2O2 and mixture thereof.


According to another embodiment, the reactant specie is a nitrogen source and more particularly nitrogen (N2), nitrogen-containing radicals such as N*, NH*, NH2*, ammonia (NH3), hydrazine (NH2NH2) and its alkyl or aryl derivatives, and mixtures thereof.


According to another embodiment, the reactant specie is both a nitrogen and an oxygen source and more particularly, NO, NO2, N2O, N2O5, N2O4 and mixtures thereof.


Depending on the ratio N/O, which is required, the reactant specie which is, if necessary, used in the method as hereinbefore defined, may be either an oxygen source, either a mixture of an oxygen source and of a nitrogen source either both an oxygen and a nitrogen source or a mixture thereof.


According to another embodiment of the invention, if the targeted metal based film contains carbon, such as for example without limitation metal carbide or metal carbonitride, at least one reactant specie is a carbon source more particularly, methane, ethane, propane, butane, ethylene, propylene, t-butylene.


According to another embodiment of the invention if the targeted metal based film contains silicon, such as for example without limitation metal silicide, silico-nitride, silicate or silico-carbo-nitride, at least on reactant specie is a silicon source such as:


disiloxane, trisilylamine, disilane (Si2H6), trisilane (Si3H3), alkoxysilane of the formulas (III1), (III2) or (III3), as hereinbefore defined, for example SiH(NMe2)3 (TriDMAS); SiH2(NHtBu)2 (BTBAS); SiH2(NEt2)2 (BDEAS)) and mixtures thereof.


According to another particular embodiment, the method as hereinbefore defined, comprise:

    • a step d′) wherein the at least one M1 metal containing precursor of the formula (II) and if necessary, the at least one M2 metal containing precursor, is mixed to at least one reactant specie in the reaction chamber.


The mode of introduction of the at least one M1 metal containing precursor of the formula (II) and if necessary, the at least one M2 metal containing precursor, and the at least one reactant specie in the reaction chamber generally depends on the mode of deposition of the film on the substrate. The metal containing precursors and the reactant species are generally introduced simultaneously in a chemical vapor deposition process, or sequentially in an atomic layer deposition process or according to several combinations, as for example in a pulsed modified atomic layer deposition process wherein the at least one M1 metal containing precursor of the formula (II) and if necessary, the at least one M2 metal containing precursor, are introduced together in one pulse and the at least one reactant specie is introduced in a separate pulse; or in a pulsed chemical vapor deposition process wherein the at least one M1 metal containing precursor of the formula (II) and if necessary, the at least one M2 metal containing precursor, are introduced by pulse and the at least one reactant specie is introduced continuously.


According to another of the invention, the at least one reactant specie is passed through a plasma system localized remotely from the reaction chamber, and decomposed to radicals.


According to another embodiment, the step (b) of the method as hereinabove defined, consists of a step (b1) of mixing at least one first metal containing precursor of the formula (II) together with at least a second of the following precursors: M1(NMe2)4, M1(NEt2)4, M1(NMeEt)4, M1(mmp)4, M1(OtBu)4, M1(OtBu)2(mmp)2 and mixtures thereof and a step (b2) of vaporizing said mixture. According to a more particular embodiment, the invention concerns a method as hereinbefore defined, of deposition of a metal containing dielectric film comprising a compound of the formula (I), wherein the M1 metal containing precursor is of the formula (II1):





(R2tCp)M1[N(R39)(R40)]3  (II1)


corresponding to the formula (II), wherein x=0, z=1 and R′ represents the group N(R39)(R40), wherein R39 and R40, identical or different, independently represent an hydrogen atom, a linear or branched alkyl group having from one to four carbon atoms, an alkylsilyl group, wherein the alkyl group is linear or branched and has from one to four carbon atoms, a dialkylsilyl group, wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms or a trialkylsilyl group wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms


According to a more particular embodiment, the invention concerns a method as hereinbefore defined, of deposition of a metal containing dielectric film comprising a compound of the formula (I1):





M1O2  (I1)


corresponding to the formula (I), wherein a=0, b=2 and c=0, wherein the metal containing precursor of the formula (II) is selected from the group consisting of: HfCp2Cl2, Hf(MeCp)2Me2, HfCp(MeCp)Cl2, Hf(MeCp)2Cl2, HfCp(MeCp)Me2, Hf(EtCp)(MeCp)Me2, Hf(EtCp)2Me2, Hf(MeCp)2(CO)2, ZrCp2Cl2, Zr(MeCp)2Me2, ZrCp(MeCp)Cl2, Zr(MeCp)2Cl2, ZrCp(MeCp)Me2, Zr(EtCp)(MeCp)Me2, Zr(EtCp)2Me2, Zr(MeCp)2(CO)2, Zr(MeCp)(NMe2)3, Zr(EtCp)(NMe2)3, ZrCp(NMe2)3, Zr(MeCp)(NEtMe)3, Zr(EtCp)(NEtMe)3, ZrCp(NEtMe)3, Zr(MeCp)(NEt2)3, Zr(EtCp)(NEt2)3, ZrCp(NEt2)3, Zr(iPr2Cp)(NMe2)3, Zr(tBu2Cp)(NMe2)3, Hf(MeCp)(NMe2)3, Hf(EtCp)(NMe2)3, HfCp(NMe2)3, Hf(MeCp)(NEtMe)3, Hf(EtCp)(NEtMe)3, HfCp(NEtMe)3, Hf(MeCp)(NEt2)3, Hf(EtCp)(NEt2)3, HfCp(NEt2)3, Hf(iPr2Cp)(NMe2)3, Hf(tBu2Cp)(NMe2)3 and mixtures thereof.


According to a more particular embodiment, the invention concerns a method as hereinbefore defined, of deposition of a metal containing dielectric film comprising a compound of the formula (I2):





M1ObNc,  (I2)


corresponding to the formula (I), wherein a=0, 1.5≦b≦2.5 and 0<c≦0.5, wherein the metal containing precursor of the formula (II) is selected from the group consisting of: HfCp2Cl2, Hf(MeCp)2Me2, HfCp(MeCp)Cl2, Hf(MeCp)2Cl2, HfCp(MeCp)Me2, Hf(EtCp)(MeCp)Me2, Hf(EtCp)2Me2, Hf(MeCp)2(CO)2, ZrCp2Cl2, Zr(MeCp)2Me2, Zr(MeCp)2Cl2, ZrCp(MeCp)Me2, Zr(EtCp)(MeCp)Me2, Zr(EtCp)2Me2, Zr(MeCp)2(CO)2, Zr(MeCp)(NMe2)3, Zr(EtCp)(NMe2)3, ZrCp(NMe2)3, Zr(MeCp)(NEtMe)3, Zr(EtCp)(NEtMe)3, ZrCp(NEtMe)3, Zr(MeCp)(NEt2)3, Zr(EtCp)(NEt2)3, ZrCp(NEt2)3, Zr(iPr2Cp)(NMe2)3, Zr(tBu2Cp)(NMe2)3, Hf(MeCp)(NMe2)3, Hf(EtCp)(NMe2)3, HfCp(NMe2)3, Hf(MeCp)(NEtMe)3, Hf(EtCp)(NEtMe)3, HfCp(NEtMe)3, Hf(MeCp)(NEt2)3, Hf(EtCp)(NEt2)3, HfCp(NEt2)3, Hf(iPr2Cp)(NMe2)3, Hf(tBu2Cp)(NMe2)3 and mixture thereof.


According to a more particular embodiment, the invention concerns a method as hereinbefore defined, of deposition of a metal containing dielectric film comprising a compound of the formula (I3):





M11-aM2a)Ob  (I3)


corresponding to the formula (I), wherein 0≦a<1 and c=0, wherein the metal containing precursor of the formula (II) is selected from the group consisting of: HfCp2Cl2, Hf(MeCp)2Me2, HfCp(MeCp)Cl2, Hf(MeCp)2Cl2, HfCp(MeCp)Me2, Hf(EtCp)(MeCp)Me2, Hf(EtCp)2Me2, Hf(MeCp)2(CO)2, ZrCp2Cl2, Zr(MeCp)2Me2, ZrCp(MeCp)Cl2, Zr(MeCp)2Cl2, ZrCp(MeCp)Me2, Zr(EtCp)(MeCp)Me2, Zr(EtCp)2Me2, Zr(MeCp)2(CO)2, Zr(MeCp)(NMe2)3, Zr(EtCp)(NMe2)3, ZrCp(NMe2)3, Zr(MeCp)(NEtMe)3, Zr(EtCp)(NEtMe)3, ZrCp(NEtMe)3, Zr(MeCp)(NEt2)3, Zr(EtCp)(NEt2)3, ZrCp(NEt2)3, Zr(iPr2Cp)(NMe2)3, Zr(tBu2Cp)(NMe2)3, Hf(MeCp)(NMe2)3, Hf(EtCp)(NMe2)3, HfCp(NMe2)3, Hf(MeCp)(NEtMe)3, Hf(EtCp)(NEtMe)3, HfCp(NEtMe)3, Hf(MeCp)(NEt2)3, Hf(EtCp)(NEt2)3, HfCp(NEt2)3, Hf(iPr2Cp)(NMe2)3, Hf(tBu2Cp)(NMe2)3 and the M2 metal containing precursor is preferably selected from the silicon derivatives or their germanium homologues, the tantalum derivatives, lanthanide derivatives, and the magnesium derivatives as hereinabove defined.


According to a more particular embodiment, the invention concerns a method as hereinbefore defined, of deposition of a metal containing dielectric film comprising a compound of the formula (I4):





(M11-aM2a)ObNc  (I4)


corresponding to the formula (I), wherein 0≦a<1 and 0<c≦0.5, wherein the metal containing precursor of the formula (II) is selected from the group consisting of HfCp2Cl2, Hf(MeCp)2Me2, HfCp(MeCp)Cl2, Hf(MeCp)2Cl2, HfCp(MeCp)Me2, Hf(EtCp)(MeCp)Me2, Hf(EtCp)2Me2, Hf(MeCp)2(CO)2, ZrCp2Cl2, Zr(MeCp)2Me2, ZrCp(MeCp)Cl2, Zr(MeCp)2Cl2, ZrCp(MeCp)Me2, Zr(EtCp)(MeCp)Me2, Zr(EtCp)2Me2, Zr(MeCp)2(CO)2, Zr(MeCp)(NMe2)3, Zr(EtCp)(NMe2)3, ZrCp(NMe2)3, Zr(MeCp)(NEtMe)3, Zr(EtCp)(NEtMe)3, ZrCp(NEtMe)3, Zr(MeCp)(NEt2)3, Zr(EtCp)(NEt2)3, ZrCp(NEt2)3, Zr(iPr2Cp)(NMe2)3, Zr(tBu2Cp)(NMe2)3, Hf(MeCp)(NMe2)3, Hf(EtCp)(NMe2)3, HfCp(NMe2)3, Hf(MeCp)(NEtMe)3, Hf(EtCp)(NEtMe)3, HfCp(NEtMe)3, Hf(MeCp)(NEt2)3, Hf(EtCp)(NEt2)3, HfCp(NEt2)3, Hf(iPr2Cp)(NMe2)3, Hf(tBu2Cp)(NMe2)3, the M2 metal containing precursor is preferably selected from the silicon derivatives or their germanium homologues, the tantalum derivatives, lanthanide derivatives, and the magnesium derivatives as hereabove defined, and at least one oxygen containing precursor and at least one nitrogen containing precursor is introduced into the reactor.


According to another embodiment the invention concerns the use of the compounds of the formula (II) as hereinbefore defined, to make dielectric films more particularly for integrated circuits or in the preparation of Metal Insulator Metal (MIM) architectures for Random Access Memories.


According to another embodiment, the invention concerns a compound the formula (II1):





(R2tCp)M1[N(R39)(R40)]3  (II1)


corresponding to the formula (II), wherein x=0, z=1 and R′ represents the group)N(R39)(R40), wherein R39 and R40, identical or different, independently represent an hydrogen atom, a linear or branched alkyl group having from one to four carbon atoms, an alkylsilyl group, wherein the alkyl group is linear or branched and has from one to four carbon atoms, a dialkylsilyl group, wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms or a trialkylsilyl group wherein each alkyl group, identical or different from the other, is linear or branched and has from one to four carbon atoms.


According to a particular embodiment, the invention relates to a compound of the formula (II1) as hereinbefore defined, wherein R2, R39 and R40, identical or different, independently represent a radical selected from the methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl and tert-butyl groups, and more specifically the following compounds:


Zr(MeCp)(NMe2)3, Zr(EtCp)(NMe2)3, ZrCp(NMe2)3, Zr(MeCp)(NEtMe)3, Zr(EtCp)(NEtMe)3, ZrCp(NEtMe)3, Zr(MeCp)(NEt2)3, Zr(EtCp)(NEt2)3, ZrCp(NEt2)3, Zr(iPr2Cp)(NMe2)3, Zr(tBu2Cp)(NMe2)3, Hf(MeCp)(NMe2)3, Hf(EtCp)(NMe2)3, HfCp(NMe2)3, Hf(MeCp)(NEtMe)3, Hf(EtCp)(NEtMe)3, HfCp(NEtMe)3, Hf(MeCp)(NEt2)3, Hf(EtCp)(NEt2)3, HfCp(NEt2)3, Hf(iPr2Cp)(NMe2)3, Hf(tBu2Cp)(NMe2)3.


According to a more specific embodiment, the invention relates to the following compounds:


Zr(EtCp)(NMe2)3, Zr(MeCp)(NMe2)3, ZrCp(NMe2)3, Hf(EtCp)(NMe2)3, Hf(MeCp)(NMe2)3 and HfCp(NMe2)3.

Those skilled in the art will recognize that the hereinabove metal-organic compounds could be used for any other applications than vapour phase deposition processes, such as catalysts or any other industrial process or application requiring the use of metal-organic compounds . . . .


According to another embodiment, the invention concerns a process for the preparation of a compound of the formula (II1) as hereinabove defined, which comprises:

    • a step 1, consisting of the preparation of the compound of the formula (VII1):





(R2tCp)M1Cl3  (VII1)


wherein M1, R2 and t are as hereinabove defined for the formula (II), by the reaction of M1Cl4 with (R2tCp)Na;

    • a step 2, consisting of the reaction of the compound of the formula (VII1) prepared in step 1, with NH(R39)(R40), to produce the compound of the formula (II1).


According to a last embodiment, the invention concerns the following compounds of the formula (II) as hereinabove defined: Hf(EtCp)2Me2, Zr(MeCp)2Me2 or Zr(EtCp)2Me2.


The following examples are an illustration of the various embodiments of the present invention, without being a limitation.


Example I
Deposition of Metal Oxide Film M1O2 with M1 Being Preferably Hafnium and Zirconium

The film to be deposited comprises a compound of the formula (I) wherein a=0, b=2 and c=0.


To make the deposition of such film on the surface of a wafer or in a deep trench to manufacture MIM structures for DRAM, one need to vaporize the M1 metal source as defined in step (b) and to introduce it into the reactor (preferably Hafnium or Zirconium), to inject an oxygen source, preferably moisture, oxygen or ozone into said reactor, react the products at appropriate temperature (preferably between 150° C. and 350° C.) and pressure (preferably between 25 Pa and 1000 Pa) for the duration necessary to achieve either a thin film deposition on the substrate or to fill out deep trenches by ALD or pulse CVD process (sequential pulse injection of metal sources are necessary in order to allow regular deposition of the oxide in the trench to progressively fill out this trench and provide no voids in the dielectric film and therefore no defect in the capacitor dielectric film).


The dielectric film shall have the desired final composition (here essentially variations of the b value around 2 modifying the ratio of precursor to oxygen source).


Three examples of types of compounds of the formula (II) were chosen according to the three following options a, b or c:

    • a) The compound of the formula (II) is chosen from Zr(MeCp)2Me2, Zr(EtCp)2Me2, Hf(MeCp)2Me2 and Hf(MeCp)2Me2.
      • Delivery of molecules in liquid form is usually carried out by bubbling an inert gas (N2, He, Ar, . . . ) into the liquid and providing the inert gas plus liquid gas mixture to the reactor.
    • b) The compound of the formula (II) is chosen from Zr(2,4-Me2Op)2Me2 and Hf(2,4-Me2Op)2Me2.
    • c) The compound of the formula (II) is chosen from Zr(MeCp)(2,4-Me2Op)Me2 and Hf(MeCp)(2,4-Me2Op)Me2. The oxygen source shall be preferably, without limitations, oxygen (O2), oxygen radicals (for instance O or OH), such as radicals generated by a remote plasma system, ozone, NO, N2O, NO2, moisture (H2O) and H2O2.


Regarding the deposition process by itself, the reactants can be introduced into the reactor simultaneously (chemical vapor deposition), sequentially (atomic layer deposition) or different combinations (one example is to introduce metal source and the other metal source together in one pulse and oxygen in a separate pulse [modified atomic layer deposition]; another option is to introduce oxygen continuously and/or to introduce the metal source by pulse (pulsed-chemical vapor deposition).


Example II
Deposition of Metal Oxynitride Films M1ON with M1 Being Preferably Hafnium and Zirconium

The film to be deposited comprises a compound of the formula (I) wherein a=0 and b and c are different from zero.


All the information given in Example I, is applicable in this Example II, except that nitrogen needs to be introduced into the reactor.


The nitrogen shall be selected from a nitrogen source selected from the group comprising nitrogen (N2), ammonia, hydrazine and alkyl derivatives, N-containing radicals (for instance N*, NH*, NH2*), NO, N2O, NO2 or the like.


Example III
Deposition of M1M2 Metal Oxide Films with M1 Being Preferably Hf or Zr and M2 Being Preferably Si or Al

The film to be deposited comprises a compound of the formula (I) wherein a≠0, b≠0 and c=0.


All the information given in Example is applicable in this Example III, except that a M2 metal source is additionally needed.


The M2 containing precursor is also introduced into the reactor to crate the M2 source of metal. This M2 containing precursor source shall be preferably:

    • a) a silicon (or germanium) source, for example Si(OH)(OtBu)3, SiH(NMe2)3 (TriDMAS); SiH2(NHtBu)2 (BTBAS) and SiH2(NEt2)2 (BDEAS)
    • b) an aluminum source, for example AlMe2(OiPr); or
    • c) a tantalum (or niobium) source, for example Ta(OMe)5, Ta(OEt)5 and Ta(OEt)(OCMe2CH2—OMe) (TATDMAE);


The invention is directed to the deposition of dielectric films of the formula I, onto a support such as a wafer, in a reactor using ALD, CVD, MOCVD, pulse CVD processes.


Example IV
Deposition of M1M2 Metal Oxynitride Films with M1 Being Preferably Hf or Zr and M2 Being Preferably Si or Al

The film to be deposited comprises a compound of the formula (I) wherein a∫0, b∫0 and c∫0.


All the information given in Example III, is applicable in this case, except that nitrogen needs to be introduced into the reactor.


The nitrogen source shall be selected from the group comprising nitrogen (N2), ammonia, hydrazine and alkyl derivatives, N-containing radicals (for instance N′, NH′, NH2′), NO, N2O, NO2.


Example V
Synthesis of (Ethylcyclopentadienyl)tris(dimethylamino)zirconium, Zr(EtCp)(NMe2)3

Zr(EtCp)(NMe2)3 is prepared in 3 steps.


The first step is the preparation of Zr(EtCp)Cl3 by the reaction of (EtCp)Na over ZrCl4;


The second step is the reaction LiNMe2 with Zr(EtCp)Cl3 to produce Zr(EtCp)(NMe2)3. The resulting compound is purified by distillation. Overall yield was 35%.


(Ethylcyclopentadienyl)tris(dimethylamino)zirconium has been found to be a stable liquid pale yellow compound.


TGA analysis of Zr(EtCp)(NMe2)3


The thermal gravimetric apparatus was stored in an argon glove box with moisture and oxygen content maintained below 1 ppmv. Thermal gravimetric analysis was performed by placing a 35 mg sample in an aluminum crucible. The sample was then heated at a 10° C./min temperature ramp from 35° C. to 400° C. The mass loss was monitored as a function of the crucible temperature. The residue level was 2.6% with full evaporation temperatures of 260° C. The resulting graph is on FIG. 1.


Example VI
Atomic Layer Deposition of ZrO2 Thin Films Using Zr(EtCp)(NMe2)3

Zr(EtCp)(NMe2)3 is stored into a container. The container is heated at 90° C. and N2 is used as carrier gas at a flow of 50 sccm. The pressure the container is controlled at 50 Torr. O3 is used as oxygen source. The substrate is heated at 350° C. During a first step, Zr(EtCp)(NMe2)3 is introduced into the reaction chamber during 2 s. A N2 purge of 5 s is performed afterwards as second step. As third step, a pulse of O3 is then introduced into the reaction chamber during 2 s, followed by a 2 s N2 purge as fourth step. All four steps are repeated 100 times to obtain a ZrO2 film. Self-limited atomic layer deposition is obtained.


Similar experiments can be performed with Hf analogs. Similar experiments can be conducted with H2O as oxygen source.


Example VII
Metal-Organic Chemical Vapor Deposition of ZrO2 Using Zr(EtCp)(NMe2)3

Zr(EtCp)(NMe2)3 is stored into a container. The container is heated at 90° C. and N2 is used as carrier gas at a flow of 50 sccm. The pressure in the container is controlled at 50 Torr. Zr(EtCp)(NMe2)3 is mixed to an O2/N2 gas mixture into the reaction chamber. The substrate is heated at 500° C. The pressure inside the reaction chamber is set at 10 Torr. A film of zirconium oxide is obtained.


Similar experiments can be performed with Hf analogs.


Example VIII
Comparison of Zr(EtCp)(NMe2)3 and Zr(NEtMe)4 Thermal Behavior

Thermal gravimetric analysis is performed on Zr(EtCp)(NMe2)3 and Zr(NEtMe)4 in similar conditions. Thermal gravimetric apparatus was stored in an argon glove box with moisture and oxygen content maintained below 1 ppmv. Thermal gravimetric analysis was performed by placing a 35 mg sample in an aluminum crucible. The sample was then heated at a 10° C./min temperature ramp from 35° C. to 400° C. The mass loss was monitored as a function of the crucible temperature. In closed cup configuration, a pierced pan (0.8 mm) is placed over the crucible containing the metal-organic compound to slow down the evaporation. This indicates the thermal stability at higher temperature. The results indicates that Zr(EtCp)(NMe2)3 is much more thermally stable than Zr(NEtMe)4, making it further attractive for use as vapor phase precursor. The results are shown on FIG. 2.


It will be understood that many additional changes in the details, materials, steps and arrangement of parts, which have been herein described in order to explain the nature of the invention, may be made by those skilled in the art within the principle and scope of the invention as expressed in the appended claims. Thus, the present invention is not intended to be limited to the specific embodiments in the examples given above.

Claims
  • 1. A method of deposition on a substrate, of at least one metal containing dielectric film comprising a compound of the formula (I): (M11-aM2a)ObNc,  (I)
  • 2. The method of claim 1, wherein the vaporization step b) and the vaporization step b′) are combined in one vaporization step b″) of both sources.
  • 3. The method of claim 1, wherein the M2 metal containing precursor, is selected from the group consisting of: Silicon derivatives or their Germanium homologues, such as:disiloxane, trisilylamine, disilane, trisilane, alkoxysilane of the formula: (III1) SiHx(OR3)4-x,  (III1)
  • 4. The method of claim 3, wherein the M2 metal containing precursor is an hafnium (Hf) derivative.
  • 5. The method of claim 1, which further comprises: A step d), wherein the at least one M1 metal containing precursor, and if necessary, the at least one M2 metal containing precursor, is mixed to at least one reactant specie prior to step c).
  • 6. The method of claim 1, which further comprises: a step d′) wherein the at least one M1 metal containing precursor and if necessary, the at least one M2 metal containing precursor, is mixed to at least one reactant specie in the reaction chamber.
  • 7. The method of claim 1, of deposition of a metal containing dielectric film comprising a compound of the formula (I1): M1O2  (I1)
  • 8. The method of claim 1, of deposition of a metal containing dielectric film comprising a compound of the formula (I2): M1ObNc,  (I2)
  • 9. The method of claim 1, of deposition of a metal containing dielectric film comprising a compound of the formula (I3): (M11-aM2a)Ob  (I3)
  • 10. The method of claim 1, of deposition of a metal containing dielectric film comprising a compound of the formula (I4): (M11-a M2a)ObNc  (I4)
  • 11. The method of claim 1, wherein said M1 metal containing precursor is ZrCp(NMe2)3.
Priority Claims (1)
Number Date Country Kind
PCT/EP2006/062893 Jun 2006 EP regional
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of pending U.S. application Ser. No. 12/303,169 filed Dec. 2, 2008, which is a national stage entry under 21 USC §371 of PCT/EP07/052507 filed Mar. 16, 2007, which claims priority to PCT/EP06/062893 filed Jun. 2, 2006, the entire contents of which are incorporated herein by reference.

Continuation in Parts (1)
Number Date Country
Parent 12303169 Apr 2009 US
Child 13009958 US