The present disclosure relates to a radio frequency (RF) device and a process for making the same, and more particularly to an RF device with enhanced thermal and electrical performance, and a wafer-level fabricating and packaging process to provide the RF device with enhanced performance.
The wide utilization of cellular and wireless devices drives the rapid development of radio frequency (RF) technologies. The substrates on which RF devices are fabricated play an important role in achieving high-level performance in the RF technologies. Fabrications of the RF devices on conventional silicon substrates may benefit from the low cost of silicon materials, a large-scale capacity of wafer production, well-established semiconductor design tools, and well-established semiconductor manufacturing techniques. Despite the benefits of using conventional silicon substrates for the RF device fabrications, it is well known in the industry that the conventional silicon substrates may have two undesirable properties for the RF devices: harmonic distortion and low resistivity values. The harmonic distortion is a critical impediment to achieve high-level linearity in the RF devices built over silicon substrates.
In addition, high-speed and high-performance transistors are more densely integrated in RF devices. Consequently, the amount of heat generated by the RF devices increases significantly due to the large number of transistors integrated in the RF devices, the large amount of power passing through the transistors, and/or the high operation speed of the transistors. Accordingly, it is desirable to package the RF devices in a configuration for better heat dissipation.
Wafer-level fan-out (WLFO) technology and embedded wafer-level ball grid array (eWLB) technology currently attract substantial attention in portable RF applications. WLFO and eWLB technologies are designed to provide high-density input/output ports without increasing the size of a package. This capability allows for densely packaging the RF devices within a single wafer.
To enhance the operation speed and performance of the RF devices, to accommodate the increased heat generation of the RF devices, to reduce deleterious harmonic distortion of the RF devices, and to utilize advantages of WLFO/eWLB technologies, it is therefore an object of the present disclosure to provide an improved wafer-level fabricating and packaging process for the RF devices with enhanced performance. Further, there is also a need to enhance the performance of the RF devices without increasing the device size.
The present disclosure relates to a radio frequency (RF) device with enhanced performance and a process for making the same. According to an exemplary process, a precursor wafer, which includes a number of device regions, a number of individual interfacial layers, and a silicon handle substrate, is first provided. Each device region includes a back-end-of-line (BEOL) portion and a front-end-of-line (FEOL) portion over the BEOL portion. The FEOL portion has isolation sections and an active layer, which is surrounded by the isolation sections and does not extend vertically beyond the isolation sections. Herein, each individual interfacial layer is over one active layer of a corresponding device region, and the silicon handle substrate is over each individual interfacial layer. Each individual interfacial layer is formed of silicon germanium (SiGe). Next, a first bonding layer is formed underneath the precursor wafer. After a support carrier with a second bonding layer is provided, the precursor wafer is attached to the support carrier by bonding the first bonding layer directly to the second bonding layer. Herein, the first bonding layer and the second bonding layer merge to form a bonding structure between the support carrier and the precursor wafer. The silicon handle substrate is then removed from the precursor wafer to provide an etched wafer after attaching the precursor wafer to the support carrier. A first mold compound is applied to the etched wafer to provide a mold device wafer. The first mold compound is applied at least over the active layer of each device region from where the silicon handle substrate is removed.
According to another embodiment, the exemplary process further includes forming a barrier layer covering an entire bottom surface of the precursor wafer before forming the first bonding layer underneath the precursor wafer. Herein, the barrier layer covers a bottom surface of the BEOL portion of each device region, and the barrier layer separates the bonding structure from the device regions.
In one embodiment of the exemplary process, the support carrier is formed of silicon, the bonding structure is formed of silicon oxide, and the barrier layer is formed of a nitride material.
According to another embodiment, the exemplary process further includes removing the support carrier from the mold device wafer after applying the first mold compound, removing the bonding structure after removing the support carrier, and removing the barrier layer after removing the bonding structure. After the removal of the support carrier, the bonding structure, and the barrier layer, the bottom surface of the BEOL portion of each device region is exposed.
In one embodiment of the exemplary process, the support carrier, the bonding structure, and the barrier layer have different reactions to a same etching technique.
In one embodiment of the exemplary process, the support carrier, the bonding structure, and the barrier layer have different etching speeds with a same etchant.
In one embodiment of the exemplary process, the support carrier, the bonding structure, and the barrier layer are removed by different etching processes.
In one embodiment of the exemplary process, the support carrier is removed by a mechanical grinding process followed by an etching process. Herein, the etching process is provided by a wet etching system with an etchant chemistry, which is at least one of tetramethylammonium hydroxide (TMAH), potassium hydroxide (KOH), sodium hydroxide (NaOH), acetylcholine (ACH), and xenon difluoride (XeF2).
In one embodiment of the exemplary process, the support carrier is removed by a mechanical grinding process followed by an etching process. Herein, the etching process is provided by a reactive ion etching system with a chlorine-based gas chemistry or a fluorine-based gas chemistry.
In one embodiment of the exemplary process, the bonding structure is removed by a etch system capable of identifying the presence of the nitride material in the barrier layer.
In one embodiment of the exemplary process, the barrier layer is removed by a etch system capable of identifying the presence of the BEOL portion of each of the plurality of device regions.
According to another embodiment, the exemplary process further includes forming a multilayer redistribution structure underneath the mold device wafer after removing the support carrier, the bonding structure, and the barrier layer. Herein, the multilayer redistribution structure comprises a number of bump structures on a bottom surface of the multilayer redistribution structure and redistribution interconnections within the multilayer redistribution structure. Each bump structure is electrically coupled to one active layer of a corresponding device region via the redistribution interconnections and connecting layers within the BEOL portion of the corresponding device region.
In one embodiment of the exemplary process, the first bonding layer and the second bonding layer are formed of a same material. Herein, the hardness of the bonding structure does not change in a temperature range from a room temperature to 350° C.
According to another embodiment, the exemplary process further includes removing each individual interfacial layer from the etched wafer after removing the silicon handle substrate and before applying the first mold compound.
According to another embodiment, the exemplary process further includes applying a passivation layer over an entire backside of the etched wafer after removing each individual interfacial layer and before applying the first mold compound. Herein, the passivation layer is formed of silicon dioxide. The passivation layer covers at least the top surface of each active layer and the top surface of each isolation section, and the first mold compound is over the passivation layer.
According to another embodiment, the exemplary process further includes applying a thermally conductive film over the passivation layer before applying the first mold compound. Herein, the thermally conductive film has a thermal conductivity greater than 10 w/m·k and an electrical resistivity greater than 1E5 Ohm-cm. The thermally conductive film is formed between the passivation layer and the first mold compound.
In one embodiment of the exemplary process, the thermally conductive film is formed of one of silicon nitride, aluminum nitride, alumina, boron-nitride, and a diamond-based material. The thermally conductive film has a thickness between 100 Å and 50 μm.
In one embodiment of the exemplary process, the thermally conductive film is formed from carbon nanotube-rich layers.
In one embodiment of the exemplary process, silicon crystal, which has no germanium, nitrogen, or oxygen content, does not exist between the active layer of each device region and the first mold compound. The mold device wafer includes a number of mold device dies, each of which includes a corresponding device region, a portion of the passivation layer over the corresponding device region, a portion of the thermally conductive film over the portion of the passivation layer, and a portion of the first mold compound over the portion of the thermally conductive film.
According to another embodiment, the exemplary process further includes singulating the mold device wafer into a plurality of individual mold device dies, and applying a second mold compound around and over each individual mold device die to provide a double mold device wafer. The second mold compound encapsulates a top surface and side surfaces of each individual mold device die, while a bottom surface of each individual mold device die is exposed. A bottom surface of the double mold device wafer is a combination of the bottom surface of each individual mold device die and a bottom surface of the second mold compound. Also the exemplary process includes forming a multilayer redistribution structure underneath the double mold device wafer. Herein, the multilayer redistribution structure includes a number of bump structures on a bottom surface of the multilayer redistribution structure and redistribution interconnections within the multilayer redistribution structure. Each bump structure is electrically coupled to one active layer of a corresponding individual mold device die via the redistribution interconnections within the multilayer redistribution structure and connecting layers within the BEOL portion of the corresponding individual mold device die.
In one embodiment of the exemplary process, the first mold compound and the second mold compound are formed of different materials.
In one embodiment of the exemplary process, providing the precursor wafer starts with providing a starting wafer that includes a common silicon epitaxial layer, a common interfacial layer over the common silicon epitaxial layer, and the silicon handle substrate over the common interfacial layer. The common interfacial layer is formed of SiGe. Next, a complementary metal-oxide-semiconductor (CMOS) process is performed to the starting wafer to provide the precursor wafer. Herein, the isolation sections extend through the common silicon epitaxial layer, the common interfacial layer, and extend into the silicon handle substrate, such that the common interfacial layer is separated into a number of individual interfacial layers, and the common silicon epitaxial layer is separated into a number of individual silicon epitaxial layers. Each active layer of the device regions is formed from a corresponding individual silicon epitaxial layer. Each individual interfacial layer resides over a top surface of a corresponding active layer, and the silicon handle substrate resides over each individual interfacial layer.
In another aspect, any of the foregoing aspects individually or together, and/or various separate aspects and features as described herein, may be combined for additional advantage. Any of the various features and elements as disclosed herein may be combined with one or more other disclosed features and elements unless indicated to the contrary herein.
Those skilled in the art will appreciate the scope of the present disclosure and realize additional aspects thereof after reading the following detailed description of the preferred embodiments in association with the accompanying drawing figures.
The accompanying drawing figures incorporated in and forming a part of this specification illustrate several aspects of the disclosure and, together with the description, serve to explain the principles of the disclosure.
It will be understood that for clear illustrations,
The embodiments set forth below represent the necessary information to enable those skilled in the art to practice the embodiments and illustrate the best mode of practicing the embodiments. Upon reading the following description in light of the accompanying drawing figures, those skilled in the art will understand the concepts of the disclosure and will recognize applications of these concepts not particularly addressed herein. It should be understood that these concepts and applications fall within the scope of the disclosure and the accompanying claims.
It will be understood that, although the terms first, second, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another. For example, a first element could be termed a second element, and, similarly, a second element could be termed a first element, without departing from the scope of the present disclosure. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.
It will be understood that when an element such as a layer, region, or substrate is referred to as being “on” or extending “onto” another element, it can be directly on or extend directly onto the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or extending “directly onto” another element, there are no intervening elements present. Likewise, it will be understood that when an element such as a layer, region, or substrate is referred to as being “over” or extending “over” another element, it can be directly over or extend directly over the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly over” or extending “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.
Relative terms such as “below” or “above” or “upper” or “lower” or “horizontal” or “vertical” may be used herein to describe a relationship of one element, layer, or region to another element, layer, or region as illustrated in the Figures. It will be understood that these terms and those discussed above are intended to encompass different orientations of the device in addition to the orientation depicted in the Figures.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes,” and/or “including” when used herein specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms used herein should be interpreted as having a meaning that is consistent with their meaning in the context of this specification and the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.
Embodiments are described herein with reference to schematic illustrations of embodiments of the disclosure. As such, the actual dimensions of the layers and elements can be different, and variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are expected. For example, a region illustrated or described as square or rectangular can have rounded or curved features, and regions shown as straight lines may have some irregularity. Thus, the regions illustrated in the figures are schematic and their shapes are not intended to illustrate the precise shape of a region of a device and are not intended to limit the scope of the disclosure. Additionally, sizes of structures or regions may be exaggerated relative to other structures or regions for illustrative purposes and, thus, are provided to illustrate the general structures of the present subject matter and may or may not be drawn to scale. Common elements between figures may be shown herein with common element numbers and may not be subsequently re-described.
With the looming shortage of conventional radio frequency silicon-on-insulator (RFSOI) wafers expected in the coming years, alternative technologies are being devised to get around the need for high resistivity using silicon wafers, the trap-rich layer formation, and Smart-Cut SOI wafer process. One alternative technology is based on the use of a silicon germanium (SiGe) interfacial layer instead of a buried oxide layer between a silicon substrate and a silicon epitaxial layer. However, this technology still suffers from the deleterious distortion effects due to the silicon substrate, similar to what is observed in an RFSOI technology. The present disclosure, which relates to a radio frequency (RF) device with enhanced performance, and a wafer-level fabricating and packaging process for making the same, utilizes the SiGe interfacial layer without deleterious distortion effects from the silicon substrate.
In detail, the device region 14 includes a front-end-of-line (FEOL) portion 20 and a back-end-of-line (BEOL) portion 22 underneath the FEOL portion 20. In one embodiment, the FEOL portion 20 may be configured to provide a switch field-effect transistor (FET) and includes an active layer 24 and a contact layer 26. The active layer 24 has a source 28, a drain 30, and a channel 32 between the source 28 and the drain 30. The source 28, the drain 30, and the channel 32 are formed from a same silicon epitaxial layer. The contact layer 26 is formed underneath the active layer 24 and includes a gate structure 34, a source contact 36, a drain contact 38, and a gate contact 40. The gate structure 34 may be formed of silicon oxide and extends horizontally underneath the channel 32 (i.e., from underneath the source 28 to underneath the drain 30). The source contact 36 is connected to and under the source 28, the drain contact 38 is connected to and under the drain 30, and the gate contact 40 is connected to and under the gate structure 34. An insulating material 42 may be formed around the source contact 36, the drain contact 38, the gate structure 34, and the gate contact 40 to electrically separate the source 28, the drain 30, and the gate structure 34. In different applications, the FEOL portion 20 may have different FET configurations or provide different device components, such as a diode, a capacitor, a resistor, and/or an inductor.
In addition, the FEOL portion 20 also includes isolation sections 44, which reside over the insulating material 42 of the contact layer 26 and surround the active layer 24. The isolation sections 44 are configured to electrically separate the RF device 10, especially the active layer 24, from other devices formed in a common wafer (not shown). Herein, the isolation sections 44 may extend from a top surface of the contact layer 26 and vertically beyond a top surface of the active layer 24 to define an opening 46 that is within the isolation sections 44 and over the active layer 24. The isolation sections 44 may be formed of silicon dioxide, which may be resistant to etching chemistries such as tetramethylammonium hydroxide (TMAH), xenon difluoride (XeF2), potassium hydroxide (KOH), sodium hydroxide (NaOH), or acetylcholine (ACH) and may be resistant to a dry etching system, such as a reactive ion etching (RIE) system with a chlorine-based gas chemistry.
In some applications, the active layer 24 may be passivated to achieve proper low levels of current leakage in the device. The passivation may be accomplished with deposition of a passivation layer 48. The passivation layer 48 extends over an entire backside of the device region 14, such that the passivation layer 48 continuously covers exposed surfaces within the opening 46 and top surfaces of the isolation sections 44. In one embodiment, the passivation layer 48 may only be deposited over the top surface of the active layer 24 and within the opening 46 and the isolation sections 44 not covered by the thermally conductive film 15 (not shown). The passivation layer 48 may be formed of silicon dioxide with a thickness between 10 Å and 5000 Å.
In some applications, the RF device 10 may further include an interfacial layer, which is formed of SiGe, over the top surface of the active layer 24 and within the opening 46 (described in the following paragraphs and not shown herein). If the passivation layer 48 and the interfacial layer exist, the interfacial layer is vertically between the active layer 24 and the passivation layer 48.
The thermally conductive film 15 extends over an entire backside of the device region 14, such that the thermally conductive film 15 continuously covers exposed surfaces within the opening 46 and top surfaces of the isolation sections 44. If the passivation layer 48 exists, the thermally conductive film 15 resides over the passivation layer 48. If the passivation layer 48 is omitted, the thermally conductive film 15 may be in contact with the active layer 24 of the FEOL portion 20 (not shown). Note that the thermally conductive film 15 is always adjacent to the active layer 24.
The thermally conductive film 15 has a high thermal conductivity between 10 W/m·K and 3000 W/m·K, and a high electrical resistivity between 1E5 Ohm-cm and 1E12 Ohm-cm. The thermally conductive film 15 may include nitrides and or ceramics, such as silicon nitride, aluminum nitride, alumina, boron nitride, diamond-based materials, and the like. In addition, the thermally conductive film 15 may be formed from carbon nanotube-rich layers. Heat generated in the device region 14 may travel upward to an area above the active layer 24, pass laterally in the area above the active layer 24, and then pass downward through the device region 14 and toward the multilayer redistribution structure 18, which dissipates the heat. It is therefore highly desirable to have a high thermal conductivity region adjacent to the active layer 24 to conduct most of the heat generated by the device region 14. Consequently, the higher the thermal conductivity in the adjacent region above the active layer 24, the better the heat dissipation performance of the device region 14. Depending on different deposition stresses and different deposited materials, the thermally conductive film 15 may have different thicknesses varying from 100 Å to 50 μm. For a diamond-based material, such as chemical vapor deposition diamond, which may have an extremely high thermal conductivity between 1000 W/m·K and 3000 W/m·K, a very thin thickness of the thermally conductive film 15, such as between 100 Å and 1000 Å, is extremely effective for the heat dissipation management of the device region 14. In the case of aluminum nitride, the thermal conductivity is the order of 180 W/m·K and the thermally conductive film 15 may need to be relatively thick for thermal behavior enhancement, such as between 1 μm and 20 μm. In the case of silicon nitride, the thermal conductivity is between 10 W/m·K and 40 W/m·K, and the thermally conductive film 15 may have a thickness between 30 μm and 40 μm.
In addition, the thermally conductive film 15 may also be engineered so as to provide additional tensile strain to the active layer 24. Such strain may be beneficial in providing additional improvement of electron mobility in n-channel devices. In some applications, the thermally conductive film 15 formed of silicon nitride may further passivate the active layer 24. In such case, there may be no need for the passivation layer 48 described above.
The first mold compound 16 is directly over the thermally conductive film 15 and fills the opening 46. Although the first mold compound 16 is not immediately above the active layer 24, the first mold compound 16 is still close to the active layer 24. Consequently, it is also desirable for the first mold compound 16 to have a relatively high thermal conductivity and a relatively high electrical resistivity. In this embodiment, the first mold compound 16 may have a lower thermal conductivity than the thermally conductive film 15. The first mold compound 16 has a thermal conductivity between 1 W/m·K and 100 W/m·K, or between 7 W/m·K and 20 W/m·K. In addition, the first mold compound 16 may have a low dielectric constant less than 8, or between 3 and 5, to yield low RF coupling.
The first mold compound 16 may be formed of thermoplastics or thermoset polymer materials, such as polyphenylene sulfide (PPS), overmold epoxies doped with boron nitride, alumina, carbon nanotubes, or diamond-like thermal additives, or the like. A thickness of the first mold compound 16 is based on the required thermal performance of the RF device 10, the device layout, the distance from the multilayer redistribution structure 18, as well as the specifics of the package and assembly. The first mold compound 16 may have a thickness between 200 μm and 500 μm. Notice that, regardless of the presence of the thermally conductive film 15, the passivation layer 48, and/or the interfacial layer, silicon crystal, which has no germanium, nitrogen, or oxygen content, may not exist between the first mold compound 16 and the top surface of the active layer 24. Each of the thermally conductive film 15, the passivation layer 48, and the interfacial layer is formed of silicon composite.
Further, in some applications, the top surface of each isolation section 44 and the top surface of the active layer 24 may be coplanar (not shown), and the opening 46 is omitted. The thermally conductive film 15 resides over both the active layer 24 and the isolation sections 44 of the FEOL portion 20, and the first mold compound 16 resides over the thermally conductive film 15. Note that the active layer 24 never extends vertically beyond the isolation sections 44; otherwise the isolation sections 44 may not fully separate the active layer 24 from other devices formed from the same wafer.
The BEOL portion 22 is underneath the FEOL portion 20 and includes multiple connecting layers 50 formed within dielectric layers 52. Some of the connecting layers 50 (for internal connection) are encapsulated by the dielectric layers 52 (not shown), while some of the connecting layers 50 have a bottom portion not covered by the dielectric layers 52. Certain connecting layers 50 are electrically connected to the FEOL portion 20. For the purpose of this illustration, one of the connecting layers 50 is connected to the source contact 36, and another connecting layer 50 is connected to the drain contact 38.
The multilayer redistribution structure 18, which is formed underneath the BEOL portion 22 of the mold device die 12, includes a number of redistribution interconnections 54, a dielectric pattern 56, and a number of bump structures 58. Herein, each redistribution interconnection 54 is connected to a corresponding connecting layer 50 within the BEOL portion 22 and extends over a bottom surface of the BEOL portion 22. The connections between the redistribution interconnections 54 and the connecting layers 50 are solder-free. The dielectric pattern 56 is formed around and underneath each redistribution interconnection 54. Some of the redistribution interconnections 54, which connect the mold device die 12 to other device components formed from the same wafer, may be encapsulated by the dielectric pattern 56 (not shown), while some of the redistribution interconnections 54 have a bottom portion exposed through the dielectric pattern 56. Each bump structure 58 is formed at a bottom surface of the multilayer redistribution structure 18 and electrically coupled to a corresponding redistribution interconnection 54 through the dielectric pattern 56. As such, the redistribution interconnections 54 are configured to connect the bump structures 58 to certain ones of the connecting layers 50 in the BEOL portion 22, which are electrically connected to the FEOL portion 20. Consequently, the bump structures 58 are electrically connected to the FEOL portion 20 via corresponding redistribution interconnections 54 and corresponding connecting layers 50. In addition, the bump structures 58 are separate from each other and protrude from the dielectric pattern 56.
In some applications, there may be extra redistribution interconnections (not shown) electrically coupled to the redistribution interconnections 54 through the dielectric pattern 56, and extra dielectric patterns (not shown) formed underneath the dielectric pattern 56, such that a bottom portion of some extra redistribution interconnections may be exposed. Consequently, each bump structure 58 is coupled to a corresponding extra redistribution interconnection through the extra dielectric pattern (not shown). Regardless of the level numbers of the redistribution interconnections and/or the dielectric pattern, the multilayer redistribution structure 18 may be free of glass fiber or glass-free. Herein, the glass fiber refers to individual glass strands twisted to become a larger grouping. These glass strands may then be woven into a fabric. The redistribution interconnections 54 may be formed of copper or other suitable metals. The dielectric pattern 56 may be formed of benzocyclobutene (BCB), polyimide, or other dielectric materials. The bump structures 58 may be solder balls or copper pillars. The multilayer redistribution structure 18 has a thickness between 2 μm and 300 μm.
Initially, a starting wafer 62 with a Si—SiGe—Si structure is provided as illustrated in
Next, a complementary metal-oxide-semiconductor (CMOS) process is performed on the starting wafer 62 to provide a precursor wafer 70 with a number of device regions 14, as illustrated in
In this embodiment, the isolation sections 44 of each device region 14 extend through the common silicon epitaxial layer 64 and the common interfacial layer 66, and extend into the silicon handle substrate 68. As such, the common interfacial layer 66 separates into a number of individual interfacial layers 66I, and the common silicon epitaxial layer 64 separates into a number of individual silicon epitaxial layers 64I. Each individual silicon epitaxial layer 64I is used to form a corresponding active layer 24 in one device region 14. The isolation sections 44 may be formed by shallow trench isolation.
The top surface of the active layer 24 is in contact with a corresponding interfacial layer 66I. The silicon handle substrate 68 resides over each individual interfacial layer 66I, and portions of the silicon handle substrate 68 may reside over the isolation sections 44. The BEOL portion 22 of the device region 14, which includes at least the multiple connecting layers 50 and the dielectric layers 52, is formed under the contact layer 26 of the FEOL portion 20. Bottom portions of certain connecting layers 50 are exposed through the dielectric layers 52 at the bottom surface of the BEOL portion 22.
In another embodiment, the isolation sections 44 do not extend into the silicon handle substrate 68. Instead, the isolation sections 44 only extend through the common silicon epitaxial layer 64 and extend into the common interfacial layer 66 (not shown). Herein, the common interfacial layer 66 remains continuous, and the individual interfacial layers 66I are connected with each other. The common interfacial layer 66 directly resides over the top surface of each active layer 24, and directly resides over a top surface of each isolation section 44. The silicon handle substrate 68 remains over the common interfacial layer 66. Further, the isolation sections 44 may extend through the common silicon epitaxial layer 64 but do not extend into the common interfacial layer 66 (not shown). The top surface of each isolation section 44 and the top surface of each active layer 24 may be coplanar (not shown). The common interfacial layer 66 and the silicon handle substrate 68 remain intact. The common interfacial layer 66 is over each isolation section 44 and each active layer 24, and the silicon handle substrate 68 is over the common interfacial layer 66.
After the precursor wafer 70 is completed, a thin barrier layer 71 is formed to cover an entire bottom surface of the precursor wafer 70, so as to cover the bottom surface of the BEOL portion 22 of each device region 14, as illustrated in
A first bonding layer 72A is then formed at the bottom of the precursor wafer 70 and underneath the barrier layer 71, as illustrated in
A bonding step is then applied to attach the precursor wafer 70 to the support carrier 74 by bonding the first bonding layer 72A directly to the second bonding layer 72B, as illustrated in
Next, the silicon handle substrate 68 is selectively removed to provide an etched wafer 76, as illustrated in
Typically, the higher the germanium concentration, the better the etching selectivity between the silicon handle substrate 68 and the individual interfacial layers 66I. The etching process may be provided by a wet etching system with an etchant chemistry, which is at least one of TMAH, KOH, NaOH, ACH, and XeF2, or a dry etching system, such as a reactive ion etching system with a chlorine-based gas chemistry or a fluorine-based gas chemistry.
During the removal process, the isolation sections 44 are not removed and protect sides of each active layer 24. If the isolation sections 44 extend vertically beyond the individual interfacial layers 66I, the removal of the silicon handle substrate 68 provides the opening 46 over each individual interfacial layer 66I (over each active layer 24) and within the isolation sections 44. Herein, the top surface of each isolation section 44 and a top surface of each individual interfacial layer 66I are exposed after the removal step of the silicon handle substrate 68. If the isolation sections 44 only extend into the common interfacial layer 66 but not through the common interfacial layer 66 (as shown in
Due to the narrow gap nature of the SiGe material, it is possible that the individual interfacial layers 66I (or the common interfacial layer 66) may be conducting. The individual interfacial layers 66I may cause appreciable leakage between the source 28 and the drain 30 of the active layer 24. Therefore, in some applications, such as FET applications, it is desired to also remove the individual interfacial layers 66I (or the common interfacial layer 66), as illustrated in
In some applications, after the removal of the silicon handle substrate 68 and the individual interfacial layers 66I, the active layer 24 may be passivated to achieve proper low levels of current leakage in the device. The passivation layer 48 may be formed directly over the FEOL portion 20 of each device region 14, as illustrated in
The thermally conductive film 15 is then applied over the passivation layer 48, as illustrated in
Herein, the thermally conductive film 15 has a high thermal conductivity between 10 W/m·K and 3000 W/m·K and a high electrical resistivity between 1E5 Ohm-cm and 1E12 Ohm-cm. The thermally conductive film 15 may include nitrides and or ceramics, such as silicon nitride, aluminum nitride, alumina, boron nitride, diamond-based materials, and the like. In addition, the thermally conductive film 15 may be formed from carbon nanotube-rich layers.
Heat generated in the device regions 14 may travel upward to an area above each active layer 24, pass laterally in the area above each active layer 24, and then pass downward through the device regions 14 (toward the multilayer redistribution structure 18 formed later). It is therefore highly desirable to have a high thermal conductivity region adjacent to each active layer 24 to conduct most of the heat generated by the device regions 14. Consequently, the higher the thermal conductivity in the adjacent region above each active layer 24, the better the heat dissipation performance of the device regions 14. Depending on different deposition stresses and different deposited materials, the thermally conductive film 15 may have different thicknesses varying from 100 Å to 50 μm. For a diamond-based material, which has an extremely high thermal conductivity between 1000 W/m·K and 3000 W/m·K, a very thin thickness of the thermally conductive film 15, such as between 100 Å and 1000 Å, is extremely effective for the heat dissipation management of the device regions 14. In the case of aluminum nitride, the thermal conductivity is on the order of 180 W/m·K and the thermally conductive film 15 may need to be relatively thick for thermal behavior enhancement, such as between 1 μm and 20 μm. In the case of silicon nitride, the thermal conductivity is between 10 W/m·K and 40 W/m·K, and the thermally conductive film 15 may have a thickness between 30 μm and 40 μm. The thermally conductive film 15 may be formed by a chemical vapor deposition process, such as plasma enhanced chemical vapor deposition (PECVD) or atomic layer deposition (ALD), such as a PEALD system.
Next, the first mold compound 16 is applied over thermally conductive film 15 to provide a mold device wafer 78, as illustrated in
The first mold compound 16 may be applied by various procedures, such as compression molding, sheet molding, overmolding, transfer molding, dam fill encapsulation, and screen print encapsulation. Although the first mold compound 16 is not immediately above the active layer 24, the first mold compound 16 is still close to the active layer 24. Consequently, it is also desirable for the first mold compound 16 to have a relatively high thermal conductivity and a relatively high electrical resistivity. In one embodiment, the first mold compound 16 may have a lower thermal conductivity than the thermally conductive film 15. The first mold compound 16 has a thermal conductivity between 1 W/m·K and 100 W/m·K, or between 7 W/m·K and 20 W/m·K. In addition, the first mold compound 16 may have a low dielectric constant less than 8, or between 3 and 5, to yield low RF coupling.
During the molding process of the first mold compound 16, the bonding structure 72 and the support carrier 74 provide mechanical strength and rigidity to the etched wafer 76. Unlike the polymer adhesive used for carrier attaching, the bonding structure 72 does not soften with temperature variation (between the room temperature and 350° C.), such that the bonding structure 72 and the support carrier 74 provide mechanical strength and rigidity to the etched wafer 76. A curing process (not shown) is followed to harden the first mold compound 16. The curing temperature is between 100° C. and 320° C. depending on which material is used as the first mold compound 16. After the curing process, the first mold compound 16 may be thinned and/or planarized (not shown).
After the mold device wafer 78 is formed, the support carrier 74, the bonding structure 72, and the barrier layer 71 are removed in sequence, as illustrated in
The bonding structure 72 is then selectively removed, as illustrated in
Next, the barrier layer 71 is selectively removed, as illustrated in
With reference to
A number of the redistribution interconnections 54 are first formed underneath each BEOL portion 22, as illustrated in
Next, a number of the bump structures 58 are formed to complete the multilayer redistribution structure 18 and provide a wafer-level fan-out (WLFO) package 80, as illustrated in
The multilayer redistribution structure 18 may be free of glass fiber or glass-free. Herein, the glass fiber refers to individual glass strands twisted to become a larger grouping. These glass strands may then be woven into a fabric. The redistribution interconnections 54 may be formed of copper or other suitable metals, the dielectric pattern 56 may be formed of BCB, polyimide, or other dielectric materials, and the bump structures 58 may be solder balls or copper pillars. The multilayer redistribution structure 18 has a thickness between 2 μm and 300 μm.
In another embodiment,
After the removal of the support carrier 74, the bonding structure 72, and the thin barrier layer 71 to provide the clean mold device wafer 78 as shown in
Next, the second mold compound 60 is applied around and over the mold device dies 12 to provide a double mold device wafer 82, as illustrated in
With reference to
A number of the redistribution interconnections 54 are first formed underneath the double mold device wafer 82, as illustrated in
Next, a number of the bump structures 58 are formed to complete the multilayer redistribution structure 18 and provide an alternative WLFO package 80A, as illustrated in
It is contemplated that any of the foregoing aspects, and/or various separate aspects and features as described herein, may be combined for additional advantage. Any of the various embodiments as disclosed herein may be combined with one or more other disclosed embodiments unless indicated to the contrary herein.
Those skilled in the art will recognize improvements and modifications to the preferred embodiments of the present disclosure. All such improvements and modifications are considered within the scope of the concepts disclosed herein and the claims that follow.
This application claims the benefit of provisional patent application Ser. No. 62/947,444, filed Dec. 12, 2019, the disclosure of which is hereby incorporated herein by reference in its entirety.
Number | Name | Date | Kind |
---|---|---|---|
4093562 | Kishimoto | Jun 1978 | A |
4366202 | Borovsky | Dec 1982 | A |
5013681 | Godbey et al. | May 1991 | A |
5061663 | Bolt et al. | Oct 1991 | A |
5069626 | Patterson et al. | Dec 1991 | A |
5164687 | Kurian et al. | Nov 1992 | A |
5294295 | Gabriel | Mar 1994 | A |
5362972 | Yazawa et al. | Nov 1994 | A |
5391257 | Sullivan et al. | Feb 1995 | A |
5459368 | Onishi et al. | Oct 1995 | A |
5646432 | Iwaki et al. | Jul 1997 | A |
5648013 | Uchida et al. | Jul 1997 | A |
5699027 | Tsuji et al. | Dec 1997 | A |
5709960 | Mays et al. | Jan 1998 | A |
5729075 | Strain | Mar 1998 | A |
5831369 | Fürbacher et al. | Nov 1998 | A |
5920142 | Onishi et al. | Jul 1999 | A |
6072557 | Kishimoto | Jun 2000 | A |
6084284 | Adamic, Jr. | Jul 2000 | A |
6137125 | Costas et al. | Oct 2000 | A |
6154366 | Ma et al. | Nov 2000 | A |
6154372 | Kalivas et al. | Nov 2000 | A |
6235554 | Akram et al. | May 2001 | B1 |
6236061 | Walpita | May 2001 | B1 |
6268654 | Glenn et al. | Jul 2001 | B1 |
6271469 | Ma et al. | Aug 2001 | B1 |
6377112 | Rozsypal | Apr 2002 | B1 |
6423570 | Ma et al. | Jul 2002 | B1 |
6426559 | Bryan et al. | Jul 2002 | B1 |
6441498 | Song | Aug 2002 | B1 |
6446316 | Fürbacher et al. | Sep 2002 | B1 |
6578458 | Akram et al. | Jun 2003 | B1 |
6649012 | Masayuki et al. | Nov 2003 | B2 |
6703688 | Fitzergald | Mar 2004 | B1 |
6713859 | Ma | Mar 2004 | B1 |
6841413 | Liu et al. | Jan 2005 | B2 |
6864156 | Conn | Mar 2005 | B1 |
6864540 | Divakaruni et al. | Mar 2005 | B1 |
6902950 | Ma et al. | Jun 2005 | B2 |
6943429 | Glenn et al. | Sep 2005 | B1 |
6964889 | Ma et al. | Nov 2005 | B2 |
6992400 | Tikka et al. | Jan 2006 | B2 |
7042072 | Kim et al. | May 2006 | B1 |
7049692 | Nishimura et al. | May 2006 | B2 |
7064391 | Conn | Jun 2006 | B1 |
7109635 | McClure et al. | Sep 2006 | B1 |
7183172 | Lee et al. | Feb 2007 | B2 |
7190064 | Wakabayashi et al. | Mar 2007 | B2 |
7238560 | Sheppard et al. | Jul 2007 | B2 |
7279750 | Jobetto | Oct 2007 | B2 |
7288435 | Aigner et al. | Oct 2007 | B2 |
7307003 | Reif et al. | Dec 2007 | B2 |
7393770 | Wood et al. | Jul 2008 | B2 |
7402901 | Hatano et al. | Jul 2008 | B2 |
7427824 | Iwamoto et al. | Sep 2008 | B2 |
7489032 | Jobetto | Feb 2009 | B2 |
7596849 | Carpenter et al. | Oct 2009 | B1 |
7619347 | Bhattacharjee | Nov 2009 | B1 |
7635636 | McClure et al. | Dec 2009 | B2 |
7714535 | Yamazaki et al. | May 2010 | B2 |
7723838 | Takeuchi et al. | May 2010 | B2 |
7749882 | Kweon et al. | Jul 2010 | B2 |
7790543 | Abadeer et al. | Sep 2010 | B2 |
7816231 | Dyer et al. | Oct 2010 | B2 |
7843072 | Park et al. | Nov 2010 | B1 |
7855101 | Furman et al. | Dec 2010 | B2 |
7868419 | Kerr et al. | Jan 2011 | B1 |
7910405 | Okada et al. | Mar 2011 | B2 |
7955955 | Lane et al. | Jun 2011 | B2 |
7960218 | Ma et al. | Jun 2011 | B2 |
8004089 | Jobetto | Aug 2011 | B2 |
8183151 | Lake | May 2012 | B2 |
8299633 | Su | Oct 2012 | B2 |
8420447 | Tay et al. | Apr 2013 | B2 |
8503186 | Lin et al. | Aug 2013 | B2 |
8563403 | Farooq et al. | Oct 2013 | B1 |
8568547 | Yamazaki | Oct 2013 | B2 |
8643148 | Lin et al. | Feb 2014 | B2 |
8658475 | Kerr | Feb 2014 | B1 |
8664044 | Jin et al. | Mar 2014 | B2 |
8772853 | Hong et al. | Jul 2014 | B2 |
8791532 | Graf et al. | Jul 2014 | B2 |
8802495 | Kim et al. | Aug 2014 | B2 |
8803242 | Marino et al. | Aug 2014 | B2 |
8816407 | Kim et al. | Aug 2014 | B2 |
8835978 | Mauder et al. | Sep 2014 | B2 |
8906755 | Hekmatshoartabari et al. | Dec 2014 | B1 |
8921990 | Park et al. | Dec 2014 | B2 |
8927968 | Cohen et al. | Jan 2015 | B2 |
8941248 | Lin et al. | Jan 2015 | B2 |
8963321 | Lenniger et al. | Feb 2015 | B2 |
8983399 | Kawamura et al. | Mar 2015 | B2 |
9064883 | Meyer et al. | Jun 2015 | B2 |
9165793 | Wang et al. | Oct 2015 | B1 |
9214337 | Carroll et al. | Dec 2015 | B2 |
9349700 | Hsieh et al. | May 2016 | B2 |
9368429 | Ma et al. | Jun 2016 | B2 |
9406637 | Wakisaka | Aug 2016 | B2 |
9461001 | Tsai et al. | Oct 2016 | B1 |
9520428 | Fujimori | Dec 2016 | B2 |
9530709 | Leipold et al. | Dec 2016 | B2 |
9613831 | Morris et al. | Apr 2017 | B2 |
9646856 | Meyer et al. | May 2017 | B2 |
9653428 | Hiner et al. | May 2017 | B1 |
9698081 | Yu et al. | Jul 2017 | B2 |
9786586 | Shih | Oct 2017 | B1 |
9812350 | Costa | Nov 2017 | B2 |
9824951 | Leipold et al. | Nov 2017 | B2 |
9824974 | Gao et al. | Nov 2017 | B2 |
9859254 | Yu et al. | Jan 2018 | B1 |
9875971 | Bhushan et al. | Jan 2018 | B2 |
9941245 | Skeete et al. | Apr 2018 | B2 |
10134837 | Fanelli et al. | Nov 2018 | B1 |
10492301 | Costa | Nov 2019 | B2 |
10727212 | Moon et al. | Jul 2020 | B2 |
10784348 | Fanelli et al. | Sep 2020 | B2 |
10882740 | Costa et al. | Jan 2021 | B2 |
11646289 | Costa | May 2023 | B2 |
20010004131 | Masayuki et al. | Jun 2001 | A1 |
20020070443 | Mu et al. | Jun 2002 | A1 |
20020074641 | Towle et al. | Jun 2002 | A1 |
20020127769 | Ma et al. | Sep 2002 | A1 |
20020127780 | Ma et al. | Sep 2002 | A1 |
20020137263 | Towle et al. | Sep 2002 | A1 |
20020185675 | Furukawa | Dec 2002 | A1 |
20030207515 | Tan et al. | Nov 2003 | A1 |
20040021152 | Nguyen et al. | Feb 2004 | A1 |
20040093901 | Kim | May 2004 | A1 |
20040164367 | Park | Aug 2004 | A1 |
20040166642 | Chen et al. | Aug 2004 | A1 |
20040173790 | Yeo et al. | Sep 2004 | A1 |
20040219765 | Reif et al. | Nov 2004 | A1 |
20040266159 | Gardecki et al. | Dec 2004 | A1 |
20050037595 | Nakahata | Feb 2005 | A1 |
20050077511 | Fitzergald | Apr 2005 | A1 |
20050079686 | Aigner et al. | Apr 2005 | A1 |
20050212419 | Vazan et al. | Sep 2005 | A1 |
20050258447 | Oi et al. | Nov 2005 | A1 |
20050260842 | Kaltalioglu et al. | Nov 2005 | A1 |
20060009041 | Iyer et al. | Jan 2006 | A1 |
20060057782 | Gardes et al. | Mar 2006 | A1 |
20060099781 | Beaumont et al. | May 2006 | A1 |
20060105496 | Chen et al. | May 2006 | A1 |
20060108585 | Gan et al. | May 2006 | A1 |
20060110887 | Huang | May 2006 | A1 |
20060124961 | Sakaguchi et al. | Jun 2006 | A1 |
20060228074 | Lipson et al. | Oct 2006 | A1 |
20060261446 | Wood et al. | Nov 2006 | A1 |
20070020807 | Geefay et al. | Jan 2007 | A1 |
20070034910 | Shie | Feb 2007 | A1 |
20070045738 | Jones et al. | Mar 2007 | A1 |
20070069393 | Asahi et al. | Mar 2007 | A1 |
20070075317 | Kato et al. | Apr 2007 | A1 |
20070121326 | Nall et al. | May 2007 | A1 |
20070122943 | Foong et al. | May 2007 | A1 |
20070158746 | Ohguro | Jul 2007 | A1 |
20070181992 | Lake | Aug 2007 | A1 |
20070190747 | Humpston et al. | Aug 2007 | A1 |
20070194342 | Kinzer | Aug 2007 | A1 |
20070252481 | Iwamoto et al. | Nov 2007 | A1 |
20070276092 | Kanae et al. | Nov 2007 | A1 |
20080020513 | Jobetto | Jan 2008 | A1 |
20080050852 | Hwang et al. | Feb 2008 | A1 |
20080050901 | Kweon et al. | Feb 2008 | A1 |
20080087959 | Monfray et al. | Apr 2008 | A1 |
20080157303 | Yang | Jul 2008 | A1 |
20080164528 | Cohen et al. | Jul 2008 | A1 |
20080251927 | Zhao et al. | Oct 2008 | A1 |
20080265978 | Englekirk | Oct 2008 | A1 |
20080272497 | Lake | Nov 2008 | A1 |
20080277800 | Hwang et al. | Nov 2008 | A1 |
20080315372 | Kuan et al. | Dec 2008 | A1 |
20090008714 | Chae | Jan 2009 | A1 |
20090010056 | Kuo et al. | Jan 2009 | A1 |
20090014856 | Knickerbocker | Jan 2009 | A1 |
20090090979 | Zhu et al. | Apr 2009 | A1 |
20090179266 | Abadeer et al. | Jul 2009 | A1 |
20090230542 | Lin et al. | Sep 2009 | A1 |
20090243097 | Koroku et al. | Oct 2009 | A1 |
20090261460 | Kuan et al. | Oct 2009 | A1 |
20090302484 | Lee et al. | Dec 2009 | A1 |
20100003803 | Oka et al. | Jan 2010 | A1 |
20100012354 | Hedin et al. | Jan 2010 | A1 |
20100029045 | Ramanathan et al. | Feb 2010 | A1 |
20100045145 | Tsuda | Feb 2010 | A1 |
20100081232 | Furman et al. | Apr 2010 | A1 |
20100081237 | Wong et al. | Apr 2010 | A1 |
20100105209 | Winniczek et al. | Apr 2010 | A1 |
20100109122 | Ding et al. | May 2010 | A1 |
20100120204 | Kunimoto | May 2010 | A1 |
20100127340 | Sugizaki | May 2010 | A1 |
20100173436 | Ouellet et al. | Jul 2010 | A1 |
20100200919 | Kikuchi | Aug 2010 | A1 |
20100314637 | Kim et al. | Dec 2010 | A1 |
20110003433 | Harayama et al. | Jan 2011 | A1 |
20110018126 | Kling et al. | Jan 2011 | A1 |
20110026232 | Lin et al. | Feb 2011 | A1 |
20110036400 | Murphy et al. | Feb 2011 | A1 |
20110062549 | Lin | Mar 2011 | A1 |
20110068433 | Kim et al. | Mar 2011 | A1 |
20110102002 | Riehl et al. | May 2011 | A1 |
20110171792 | Chang et al. | Jul 2011 | A1 |
20110227158 | Zhu | Sep 2011 | A1 |
20110272800 | Chino | Nov 2011 | A1 |
20110272824 | Pagaila | Nov 2011 | A1 |
20110294244 | Hattori et al. | Dec 2011 | A1 |
20120003813 | Chuang et al. | Jan 2012 | A1 |
20120045871 | Lee et al. | Feb 2012 | A1 |
20120068276 | Lin et al. | Mar 2012 | A1 |
20120094418 | Grama et al. | Apr 2012 | A1 |
20120098074 | Lin et al. | Apr 2012 | A1 |
20120104495 | Zhu et al. | May 2012 | A1 |
20120119346 | Im et al. | May 2012 | A1 |
20120153393 | Liang et al. | Jun 2012 | A1 |
20120168863 | Zhu et al. | Jul 2012 | A1 |
20120256260 | Cheng et al. | Oct 2012 | A1 |
20120292700 | Khakifirooz et al. | Nov 2012 | A1 |
20120299105 | Cai et al. | Nov 2012 | A1 |
20120313243 | Chang et al. | Dec 2012 | A1 |
20130001665 | Zhu et al. | Jan 2013 | A1 |
20130015429 | Hong et al. | Jan 2013 | A1 |
20130037929 | Essig et al. | Feb 2013 | A1 |
20130049205 | Meyer et al. | Feb 2013 | A1 |
20130082399 | Kim et al. | Apr 2013 | A1 |
20130099315 | Zhu et al. | Apr 2013 | A1 |
20130105966 | Kelkar et al. | May 2013 | A1 |
20130147009 | Kim | Jun 2013 | A1 |
20130155681 | Nall et al. | Jun 2013 | A1 |
20130196483 | Dennard et al. | Aug 2013 | A1 |
20130200456 | Zhu et al. | Aug 2013 | A1 |
20130221493 | Kim et al. | Aug 2013 | A1 |
20130241040 | Tojo et al. | Sep 2013 | A1 |
20130280826 | Scanlan et al. | Oct 2013 | A1 |
20130299871 | Mauder et al. | Nov 2013 | A1 |
20130334698 | Mohammed et al. | Dec 2013 | A1 |
20140015131 | Meyer et al. | Jan 2014 | A1 |
20140021583 | Lo et al. | Jan 2014 | A1 |
20140035129 | Stuber | Feb 2014 | A1 |
20140134803 | Kelly et al. | May 2014 | A1 |
20140168014 | Chih et al. | Jun 2014 | A1 |
20140197530 | Meyer et al. | Jul 2014 | A1 |
20140210314 | Bhattacharjee et al. | Jul 2014 | A1 |
20140219604 | Hackler, Sr. et al. | Aug 2014 | A1 |
20140252566 | Kerr et al. | Sep 2014 | A1 |
20140252567 | Carroll et al. | Sep 2014 | A1 |
20140264813 | Lin et al. | Sep 2014 | A1 |
20140264818 | Lowe, Jr. et al. | Sep 2014 | A1 |
20140306324 | Costa et al. | Oct 2014 | A1 |
20140323064 | McCarthy | Oct 2014 | A1 |
20140327003 | Fuergut et al. | Nov 2014 | A1 |
20140327150 | Jung et al. | Nov 2014 | A1 |
20140346573 | Adam et al. | Nov 2014 | A1 |
20140356602 | Oh et al. | Dec 2014 | A1 |
20150015321 | Dribinsky et al. | Jan 2015 | A1 |
20150021754 | Lin et al. | Jan 2015 | A1 |
20150060956 | Chen | Mar 2015 | A1 |
20150076713 | Tsai et al. | Mar 2015 | A1 |
20150097302 | Wakisaka et al. | Apr 2015 | A1 |
20150108666 | Engelhardt et al. | Apr 2015 | A1 |
20150115416 | Costa et al. | Apr 2015 | A1 |
20150130045 | Tseng et al. | May 2015 | A1 |
20150136858 | Finn et al. | May 2015 | A1 |
20150162307 | Chen et al. | Jun 2015 | A1 |
20150171006 | Hung et al. | Jun 2015 | A1 |
20150197419 | Cheng et al. | Jul 2015 | A1 |
20150235990 | Cheng et al. | Aug 2015 | A1 |
20150235993 | Cheng et al. | Aug 2015 | A1 |
20150243881 | Sankman et al. | Aug 2015 | A1 |
20150255368 | Costa | Sep 2015 | A1 |
20150262844 | Meyer et al. | Sep 2015 | A1 |
20150279789 | Mahajan et al. | Oct 2015 | A1 |
20150311132 | Kuo et al. | Oct 2015 | A1 |
20150364344 | Yu et al. | Dec 2015 | A1 |
20150380394 | Jang et al. | Dec 2015 | A1 |
20150380523 | Hekmatshoartabari et al. | Dec 2015 | A1 |
20160002510 | Champagne et al. | Jan 2016 | A1 |
20160056544 | Garcia et al. | Feb 2016 | A1 |
20160079137 | Leipold et al. | Mar 2016 | A1 |
20160079233 | Deboy et al. | Mar 2016 | A1 |
20160093580 | Scanlan et al. | Mar 2016 | A1 |
20160100489 | Costa et al. | Apr 2016 | A1 |
20160126111 | Leipold et al. | May 2016 | A1 |
20160126196 | Leipold et al. | May 2016 | A1 |
20160133591 | Hong et al. | May 2016 | A1 |
20160141249 | Kang | May 2016 | A1 |
20160141263 | Lin | May 2016 | A1 |
20160155706 | Yoneyama et al. | Jun 2016 | A1 |
20160260745 | Huang et al. | Sep 2016 | A1 |
20160284568 | Morris et al. | Sep 2016 | A1 |
20160284570 | Morris et al. | Sep 2016 | A1 |
20160300771 | Lin | Oct 2016 | A1 |
20160343592 | Costa et al. | Nov 2016 | A1 |
20160343604 | Costa et al. | Nov 2016 | A1 |
20160347609 | Yu | Dec 2016 | A1 |
20160362292 | Chang et al. | Dec 2016 | A1 |
20170005000 | Beyne | Jan 2017 | A1 |
20170024503 | Connelly | Jan 2017 | A1 |
20170032957 | Costa et al. | Feb 2017 | A1 |
20170033026 | Ho | Feb 2017 | A1 |
20170053938 | Whitefield | Feb 2017 | A1 |
20170062284 | Mason et al. | Mar 2017 | A1 |
20170062366 | Enquist | Mar 2017 | A1 |
20170077028 | Maxim et al. | Mar 2017 | A1 |
20170098587 | Leipold et al. | Apr 2017 | A1 |
20170190572 | Pan et al. | Jul 2017 | A1 |
20170200648 | Lee et al. | Jul 2017 | A1 |
20170207350 | Leipold et al. | Jul 2017 | A1 |
20170263539 | Gowda et al. | Sep 2017 | A1 |
20170271200 | Costa | Sep 2017 | A1 |
20170323804 | Costa et al. | Nov 2017 | A1 |
20170323860 | Costa et al. | Nov 2017 | A1 |
20170334710 | Costa et al. | Nov 2017 | A1 |
20170358511 | Costa et al. | Dec 2017 | A1 |
20180019184 | Costa et al. | Jan 2018 | A1 |
20180019185 | Costa et al. | Jan 2018 | A1 |
20180042110 | Cok | Feb 2018 | A1 |
20180044169 | Hatcher, Jr. et al. | Feb 2018 | A1 |
20180044177 | Vandemeer et al. | Feb 2018 | A1 |
20180047653 | Costa et al. | Feb 2018 | A1 |
20180076174 | Costa et al. | Mar 2018 | A1 |
20180138082 | Costa et al. | May 2018 | A1 |
20180138227 | Shimotsusa et al. | May 2018 | A1 |
20180145678 | Maxim et al. | May 2018 | A1 |
20180151461 | Cho | May 2018 | A1 |
20180166358 | Costa et al. | Jun 2018 | A1 |
20180240797 | Yokoyama et al. | Aug 2018 | A1 |
20180261470 | Costa et al. | Sep 2018 | A1 |
20180269188 | Yu et al. | Sep 2018 | A1 |
20180277632 | Fanelli et al. | Sep 2018 | A1 |
20180331041 | Liao et al. | Nov 2018 | A1 |
20180342439 | Costa et al. | Nov 2018 | A1 |
20190013254 | Costa et al. | Jan 2019 | A1 |
20190013255 | Costa et al. | Jan 2019 | A1 |
20190043812 | Leobandung | Feb 2019 | A1 |
20190057922 | Costa et al. | Feb 2019 | A1 |
20190074263 | Costa et al. | Mar 2019 | A1 |
20190074271 | Costa et al. | Mar 2019 | A1 |
20190172826 | Or-Bach et al. | Jun 2019 | A1 |
20190172842 | Whitefield | Jun 2019 | A1 |
20190189599 | Baloglu et al. | Jun 2019 | A1 |
20190229101 | Lee | Jul 2019 | A1 |
20190237421 | Tsuchiya | Aug 2019 | A1 |
20190287953 | Moon et al. | Sep 2019 | A1 |
20190288006 | Paul et al. | Sep 2019 | A1 |
20190304910 | Fillion | Oct 2019 | A1 |
20190304977 | Costa et al. | Oct 2019 | A1 |
20190312110 | Costa | Oct 2019 | A1 |
20190326159 | Costa et al. | Oct 2019 | A1 |
20190378819 | Costa et al. | Dec 2019 | A1 |
20190378821 | Costa et al. | Dec 2019 | A1 |
20200006193 | Costa et al. | Jan 2020 | A1 |
20200027814 | Ichiryu et al. | Jan 2020 | A1 |
20200058541 | Konishi et al. | Feb 2020 | A1 |
20200115220 | Hammond et al. | Apr 2020 | A1 |
20200118838 | Hammond et al. | Apr 2020 | A1 |
20200176347 | Costa et al. | Jun 2020 | A1 |
20200234978 | Costa et al. | Jul 2020 | A1 |
20200235024 | Costa | Jul 2020 | A1 |
20200235040 | Costa et al. | Jul 2020 | A1 |
20200235054 | Costa et al. | Jul 2020 | A1 |
20200235059 | Cok et al. | Jul 2020 | A1 |
20200235066 | Costa et al. | Jul 2020 | A1 |
20200235074 | Costa et al. | Jul 2020 | A1 |
20210134699 | Costa et al. | May 2021 | A1 |
20210167031 | Costa et al. | Jun 2021 | A1 |
20210348078 | Haramoto et al. | Nov 2021 | A1 |
Number | Date | Country |
---|---|---|
1256300 | Jun 2000 | CN |
1696231 | Nov 2005 | CN |
101785098 | Jul 2010 | CN |
101901953 | Dec 2010 | CN |
102956468 | Mar 2013 | CN |
103000537 | Mar 2013 | CN |
103730429 | Apr 2014 | CN |
103811474 | May 2014 | CN |
103872012 | Jun 2014 | CN |
104134607 | Nov 2014 | CN |
106057747 | Oct 2016 | CN |
106098609 | Nov 2016 | CN |
106158786 | Nov 2016 | CN |
107481998 | Dec 2017 | CN |
102014117594 | Jun 2016 | DE |
1098386 | May 2001 | EP |
2862204 | Apr 2015 | EP |
2996143 | Mar 2016 | EP |
S505733 | Feb 1975 | JP |
S5338954 | Apr 1978 | JP |
H11-220077 | Aug 1999 | JP |
200293957 | Mar 2002 | JP |
2002100767 | Apr 2002 | JP |
2002252376 | Sep 2002 | JP |
2004273604 | Sep 2004 | JP |
2004327557 | Nov 2004 | JP |
2006005025 | Jan 2006 | JP |
2007227439 | Sep 2007 | JP |
2008235490 | Oct 2008 | JP |
2008279567 | Nov 2008 | JP |
2009026880 | Feb 2009 | JP |
2009530823 | Aug 2009 | JP |
2009200274 | Sep 2009 | JP |
2009302526 | Dec 2009 | JP |
2011216780 | Oct 2011 | JP |
2011243596 | Dec 2011 | JP |
2012129419 | Jul 2012 | JP |
2012156251 | Aug 2012 | JP |
2013162096 | Aug 2013 | JP |
2013222745 | Oct 2013 | JP |
2013254918 | Dec 2013 | JP |
2014509448 | Apr 2014 | JP |
201409612 | Mar 2014 | TW |
201448172 | Dec 2014 | TW |
201503315 | Jan 2015 | TW |
201705382 | Feb 2017 | TW |
201719827 | Jun 2017 | TW |
201724310 | Jul 2017 | TW |
201733056 | Sep 2017 | TW |
201826332 | Jul 2018 | TW |
201839870 | Nov 2018 | TW |
2007074651 | Jul 2007 | WO |
2010080068 | Jul 2010 | WO |
2015074439 | May 2015 | WO |
2018083961 | May 2018 | WO |
2018125242 | Jul 2018 | WO |
2018168391 | Sep 2018 | WO |
Entry |
---|
US 10,896,908 B2, 01/2021, Costa et al. (withdrawn) |
Corrected Notice of Allowability for U.S. Appl. No. 16/426,527, dated Aug. 18, 2021, 4 pages. |
Advisory Action and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,551, dated Sep. 13, 2021, 3 pages. |
Notice of Allowance and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,551, dated Oct. 21, 2021, 8 pages. |
Advisory Action and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,573, dated Sep. 10, 2021, 3 pages. |
Notice of Allowance and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,573, dated Oct. 21, 2021, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,586, dated Aug. 12, 2021, 16 pages. |
Notice of Allowance and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,602, dated Aug. 12, 2021, 11 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Aug. 26, 2021, 4 pages. |
Decision to Grant for Japanese Patent Application No. 2020119130, dated Sep. 7, 2021, 4 pages. |
Second Office Action for Chinese Patent Application No. 201680058198.6, dated Sep. 8, 2021, 8 pages. |
Raskin, Jean-Pierre et al., “Substrate Crosstalk Reduction Using SOI Technology,” IEEE Transactions on Electron Devices, vol. 44, No. 12, Dec. 1997, pp. 2252-2261. |
Rong, B., et al., “Surface-Passivated High-Resistivity Silicon Substrates for RFICs,” IEEE Electron Device Letters, vol. 25, No. 4, Apr. 2004, pp. 176-178. |
Sherman, Lilli M., “Plastics that Conduct Heat,” Plastics Technology Online, Jun. 2001, Retrieved May 17, 2016, http://www.ptonline.com/articles/plastics-that-conduct-heat, Gardner Business Media, Inc., 5 pages. |
Tombak, A., et al., “High-Efficiency Cellular Power Amplifiers Based on a Modified LDMOS Process on Bulk Silicon and Silicon-On-Insulator Substrates with Integrated Power Management Circuitry,” IEEE Transactions on Microwave Theory and Techniques, vol. 60, No. 6, Jun. 2012, pp. 1862-1869. |
Yamanaka, A., et al., “Thermal Conductivity of High-Strength Polyetheylene Fiber and Applications for Cryogenic Use,” International Scholarly Research Network, ISRN Materials Science, vol. 2011, Article ID 718761, May 25, 2011, 10 pages. |
Non-Final Office Action for U.S. Appl. No. 13/852,648, dated Jul. 18, 2013, 20 pages. |
Final Office Action for U.S. Appl. No. 13/852,648, dated Nov. 26, 2013, 21 pages. |
Applicant-Initiated Interview Summary for U.S. Appl. No. 13/852,648, dated Jan. 27, 2014, 4 pages. |
Advisory Action for U.S. Appl. No. 13/852,648, dated Mar. 7, 2014, 4 pages. |
Notice of Allowance for U.S. Appl. No. 13/852,648, dated Jun. 16, 2014, 9 pages. |
Notice of Allowance for U.S. Appl. No. 13/852,648, dated Sep. 26, 2014, 8 pages. |
Notice of Allowance for U.S. Appl. No. 13/852,648, dated Jan. 22, 2015, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 13/852,648, dated Jun. 24, 2015, 20 pages. |
Final Office Action for U.S. Appl. No. 13/852,648, dated Oct. 22, 2015, 20 pages. |
Non-Final Office Action for U.S. Appl. No. 13/852,648, dated Feb. 19, 2016, 12 pages. |
Final Office Action for U.S. Appl. No. 13/852,648, dated Jul. 20, 2016, 14 pages. |
Non-Final Office Action for U.S. Appl. No. 14/315,765, dated Jan. 2, 2015, 6 pages. |
Final Office Action for U.S. Appl. No. 14/315,765, dated May 11, 2015, 17 pages. |
Advisory Action for U.S. Appl. No. 14/315,765, dated Jul. 22, 2015, 3 pages. |
Non-Final Office Action for U.S. Appl. No. 14/260,909, dated Mar. 20, 2015, 20 pages. |
Final Office Action for U.S. Appl. No. 14/260,909, dated Aug. 12, 2015, 18 pages. |
Non-Final Office Action for U.S. Appl. No. 14/261,029, dated Dec. 5, 2014, 15 pages. |
Notice of Allowance for U.S. Appl. No. 14/261,029, dated Apr. 27, 2015, 10 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 14/261,029, dated Nov. 17, 2015, 5 pages. |
Non-Final Office Action for U.S. Appl. No. 14/529,870, dated Feb. 12, 2016, 14 pages. |
Notice of Allowance for U.S. Appl. No. 14/529,870, dated Jul. 15, 2016, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 15/293,947, dated Apr. 7, 2017, 12 pages. |
Notice of Allowance for U.S. Appl. No. U.S. Appl. No. 15/293,947, dated Aug. 14, 2017, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 14/715,830, dated Apr. 13, 2016, 16 pages. |
Final Office Action for U.S. Appl. No. 14/715,830, dated Sep. 6, 2016, 13 pages. |
Advisory Action for U.S. Appl. No. 14/715,830, dated Oct. 31, 2016, 6 pages. |
Notice of Allowance for U.S. Appl. No. 14/715,830, dated Feb. 10, 2017, 8 pages. |
Notice of Allowance for U.S. Appl. No. 14/715,830, dated Mar. 2, 2017, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 14/851,652, dated Oct. 7, 2016, 10 pages. |
Notice of Allowance for U.S. Appl. No. 14/851,652, dated Apr. 11, 2017, 9 pages. |
Corrected Notice of Allowance for U.S. Appl. No. 14/851,652, dated Jul. 24, 2017, 6 pages. |
Corrected Notice of Allowance for U.S. Appl. No. 14/851,652, dated Sep. 6, 2017, 5 pages. |
Notice of Allowance for U.S. Appl. No. 14/959, 129, dated Oct. 11, 2016, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 15/173,037, dated Jan. 10, 2017, 8 pages. |
Final Office Action for U.S. Appl. No. 15/173,037, dated May 2, 2017, 13 pages. |
Advisory Action for U.S. Appl. No. 15/173,037, dated Jul. 20, 2017, 3 pages. |
Notice of Allowance for U.S. Appl. No. 15/173,037, dated Aug. 9, 2017, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 15/085,185, dated Feb. 15, 2017, 10 pages. |
Non-Final Office Action for U.S. Appl. No. 15/085, 185, dated Jun. 6, 2017, 5 pages. |
Non-Final Office Action for U.S. Appl. No. 15/229,780, dated Jun. 30, 2017, 12 pages. |
Non-Final Office Action for U.S. Appl. No. 15/262,457, dated Aug. 7, 2017, 10 pages. |
Notice of Allowance for U.S. Appl. No. 15/408,560, dated Sep. 25, 2017, 8 pages. |
Notice of Allowance for U.S. Appl. No. 15/287,202, dated Aug. 25, 2017, 11 pages. |
Non-Final Office Action for U.S. Appl. No. 15/353,346, dated May 23, 2017, 15 pages. |
Notice of Allowance for U.S. Appl. No. 15/353,346, dated Sep. 25, 2017, 9 pages. |
Notice of Allowance for U.S. Appl. No. 16/426,527, dated May 14, 2021, 9 pages. |
Final Office Action for U.S. Appl. No. 16/427,019, dated May 21, 2021, 16 pages. |
Advisory Action for U.S. Appl. No. 16/427,019, dated Aug. 2, 2021, 3 pages. |
Final Office Action and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,551, dated Jun. 28, 2021, 9 pages. |
Final Office Action and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,573, dated Jun. 28, 2021, 10 pages. |
Notice of Allowance for U.S. Appl. No. 16/678,619, dated Jul. 8, 2021, 10 pages. |
Final Office Action for U.S. Appl. No. 16/678,602, dated Jun. 1, 2021, 9 pages. |
Notice of Reasons for Refusal for Japanese Patent Application No. 2020119130, dated Jun. 29, 2021, 4 pages. |
Notice of Reasons for Rejection for Japanese Patent Application No. 2019507765, dated Jun. 28, 2021, 4 pages. |
Search Report for Japanese Patent Application No. 2019507768, dated Jul. 15, 2021, 42 pages. |
Notice of Reasons for Refusal for Japanese Patent Application No. 2019507768, dated Jul. 26, 2021, 4 pages. |
Reasons for Rejection for Japanese Patent Application No. 2019507767, dated Jun. 25, 2021, 5 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2019/063460, dated Jun. 10, 2021, 9 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2019/034699, dated Aug. 5, 2021, 9 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2020/014662, dated Aug. 5, 2021, 11 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2020/014665, dated Aug. 5, 2021, 10 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2020/014666, dated Aug. 5, 2021, 11 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2020/014667, dated Aug. 5, 2021, 8 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2020/014669, dated Aug. 5, 2021, 9 pages. |
Notice of Allowance for U.S. Appl. No. 16/454,809, dated Nov. 25, 2020, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 16/427,019, dated Nov. 19, 2020, 19 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,573, dated Feb. 19, 2021, 11 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,602, dated Feb. 19, 2021, 10 pages. |
First Office Action for Chinese Patent Application No. 201680058198.6, dated Dec. 29, 2020, 14 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2019/025591, dated Oct. 15, 2020, 6 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2019/034645, dated Jan. 14, 2021, 9 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/109,935, dated Jan. 10, 2023, 4 pages. |
First Office Action for Chinese Patent Application No. 201780063121.2, dated Nov. 23, 2022, 12 pages. |
Preliminary Examination Report for Taiwanese Patent Application No. 108140788, dated Dec. 9, 2022, 13 pages. |
Non-Final Office Action for U.S. Appl. No. 16/426,527, dated Feb. 9, 2023, 9 pages. |
Non-Final Office Action for U.S. Appl. No. 16/527,702, dated Jan. 10, 2020, 10 pages. |
Office Action for Japanese Patent Application No. 2018-526613, dated Nov. 5, 2019, 8 pages. |
Intention to Grant for European Patent Application No. 17757646.9, dated Feb. 27, 2020, 55 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2019/034645, dated Sep. 19, 2019, 14 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2019/063460, dated Feb. 25, 2020, 14 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2019/055317, dated Feb. 6, 2020, 17 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2019/055321, dated Jan. 27, 2020, 23 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2019/034699, dated Oct. 29, 2019, 13 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 15/695,579, dated Apr. 1, 2020, 4 pages. |
Final Office Action for U.S. Appl. No. 16/204,214, dated Mar. 6, 2020, 14 pages. |
Notice of Allowance for U.S. Appl. No. 15/816,637, dated Apr. 2, 2020, 8 pages. |
Notice of Allowance for U.S. Appl. No. 16/527,702, dated Apr. 9, 2020, 8 pages. |
Decision of Rejection for Japanese Patent Application No. 2015-180657, dated Mar. 17, 2020, 4 pages. |
Dhar, S. et al., “Electron Mobility Model for Strained-Si Devices,” IEEE Transactions on Electron Devices, vol. 52, No. 4, Apr. 2005, IEEE, pp. 527-533. |
Notice of Allowance for U.S. Appl. No. 16/038,879, dated Apr. 15, 2020, 9 pages. |
Notice of Allowance for U.S. Appl. No. 16/004,961, dated Apr. 30, 2020, 8 pages. |
Advisory Action for U.S. Appl. No. 16/204,214, dated Apr. 15, 2020, 3 pages. |
Examination Report for European Patent Application No. 16751791.1, dated Apr. 30, 2020, 15 pages. |
Notification of Reasons for Refusal for Japanese Patent Application No. 2018-526613, dated May 11, 2020, 5 pages. |
Notice of Allowance for U.S. Appl. No. 15/873,152, dated May 11, 2020, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 16/454,687, dated May 15, 2020, 14 pages. |
Welser, J. et al., “Electron Mobility Enhancement in Strained-Si N-Type Metal-Oxide-Semiconductor Field-Effect Transistors,” IEEE Electron Device Letters, vol. 15, No. 3, Mar. 1994, IEEE, pp. 100-102. |
Zeng, X. et al., “A Combination of Boron Nitride Nanotubes and Cellulose Nanofibers for the Preparation of a Nanocomposite with High Thermal Conductivity,” ACS Nano, vol. 11, No. 5, 2017, American Chemical Society, pp. 5167-5178. |
Quayle Action for U.S. Appl. No. 16/703,251, dated Jun. 26, 2020, 5 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 15/695,579, dated May 20, 2020, 4 pages. |
Notice of Allowability for U.S. Appl. No. 15/695,579, dated Jun. 25, 2020, 4 pages. |
Notice of Allowance for U.S. Appl. No. 16/368,210, dated Jun. 17, 2020, 10 pages. |
Non-Final Office Action for U.S. Appl. No. 16/374,125, dated Jun. 26, 2020, 12 pages. |
Non-Final Office Action for U.S. Appl. No. 16/390,496, dated Jul. 10, 2020, 17 pages. |
Non-Final Office Action for U.S. Appl. No. 16/204,214, dated May 19, 2020, 15 pages. |
Non-Final Office Action for U.S. Appl. No. 16/454,809, dated May 15, 2020, 12 pages. |
Examination Report for Singapore Patent Application No. 11201901193U, dated May 26, 2020, 6 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2020/014662, dated May 7, 2020, 18 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2020/014665, dated May 13, 2020, 17 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2020/014666, dated Jun. 4, 2020, 18 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2020/014667, dated May 18, 2020, 14 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2020/014669, dated Jun. 4, 2020, 15 pages. |
Notice of Allowance for U.S. Appl. No. 16/454,687, dated Aug. 14, 2020, 7 pages. |
Decision to Grant for Japanese Patent Application No. 2018-526613, dated Aug. 17, 2020, 5 pages. |
Final Office Action for U.S. Appl. No. 16/454,809, dated Aug. 21, 2020, 12 pages. |
Von Trapp, F., “Hybrid Bonding: From Concept to Commercialization,” Apr. 2, 2018, 3D InCities, https://www.3dincites.com/2018/04/hybrid-bonding-from-concept-to-commercialization/, 10 pages. |
Notice of Allowance for U.S. Appl. No. 16/703,251, dated Aug. 27, 2020, 8 pages. |
Notice of Allowance for U.S. Appl. No. 16/527,702, dated Nov. 13, 2020, 8 pages. |
Notice of Allowance for U.S. Appl. No. 16/374,125, dated Dec. 16, 2020, 9 pages. |
Final Office Action for U.S. Appl. No. 16/390,496, dated Dec. 24, 2020, 21 pages. |
Non-Final Office Action for U.S. Appl. No. 16/426,527, dated Nov. 20, 2020, 7 pages. |
Final Office Action for U.S. Appl. No. 16/204,214, dated Nov. 30, 2020, 15 pages. |
Notice of Allowance for U.S. Appl. No. 16/204,214, dated Feb. 17, 2021, 11 pages. |
Advisory Action for U.S. Appl. No. 16/454,809, dated Oct. 23, 2020, 3 pages. |
Advisory Action for U.S. Appl. No. 16/390,496, dated Mar. 1, 2021, 3 pages. |
Notice of Allowance for U.S. Appl. No. 16/390,496, dated Apr. 5, 2021, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,551, dated Apr. 7, 2021, 9 pages. |
Applicant-Initiated Interview Summary for U.S. Appl. No. 16/678,573, dated May 7, 2021, 2 pages. |
Supplementary Examination Report for Singapore Patent Application No. 112019011945, dated Mar. 10, 2021, 3 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2019/055317, dated Apr. 22, 2021, 11 pages. |
International Preliminary Report on Patentability for International Patent Application No. PCT/US2019/055321, dated Apr. 22, 2021, 14 pages. |
Office Action for Taiwanese Patent Application No. 108140788, dated Mar. 25, 2021, 18 pages. |
Non-Final Office Action for U.S. Appl. No. 17/330,787, dated Oct. 17, 2022, 10 pages. |
Notice of Allowance and Examiner-Initiated Interview Summary for U.S. Appl. No. 16/678,586, dated Sep. 13, 2022, 11 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Oct. 5, 2022, 4 pages. |
Non-Final Office Action for U.S. Appl. No. 16/844,406, dated Oct. 6, 2022, 17 pages. |
Corrected Notice of Allowability U.S. Appl. No. 17/109,935, dated Sep. 14, 2022, 4 pages. |
Notice of Preliminary Rejection for Korean Patent Application No. 10-2018-7006660, dated Sep. 3, 2022, 6 pages. |
Advisory Action for U.S. Appl. No. 17/102,957, dated Oct. 27, 2022, 7 pages. |
Notice of Allowance for U.S. Appl. No. 16/390,496, dated Oct. 27, 2022, 21 pages. |
Notice of Allowance for U.S. Appl. No. 16/204,214, dated Oct. 28, 2022, 11 pages. |
Final Office Action for U.S. Appl. No. 16/427,019, dated Dec. 12, 2022, 19 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Oct. 4, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Nov. 2, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Dec. 7, 2022, 3 pages. |
Non-Final Office Action for U.S. Appl. No. 17/573,112, dated Dec. 9, 2022, 6 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Nov. 14, 2022, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Dec. 9, 2022, 4 pages. |
Non-Final Office Action for U.S. Appl. No. 17/554,477, dated Nov. 25, 2022, 6 pages. |
Notice of Allowance for U.S. Appl. No. 17/109,935, dated Oct. 28, 2022, 7 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/109,935, dated Nov. 10, 2022, 4 pages. |
First Office Action for Chinese Patent Application No. 201780062516.0, dated Nov. 2, 2022, 10 pages. |
Notice of Reasons for Rejection for Japanese Patent Application No. 2022032477, dated Oct. 3, 2022, 4 pages. |
First Office Action for Chinese Patent Application No. 201780058052.6, dated Nov. 2, 2022, 22 pages. |
Notice of Allowance for U.S. Appl. No. 17/330,787, dated Dec. 15, 2022, 7 pages. |
Notice of Allowance for U.S. Appl. No. 15/287,273, dated Jun. 30, 2017, 8 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 15/287,273, dated Jul. 21, 2017, 5 pages. |
Supplemental Notice of Allowability for U.S. Appl. No. 15/287,273, dated Sep. 7, 2017, 5 pages. |
Extended European Search Report for European Patent Application No. 15184861.1, dated Jan. 25, 2016, 6 pages. |
Office Action of the Intellectual Property Office for Taiwanese Patent Application No. 104130224, dated Jun. 15, 2016, 9 pages. |
Non-Final Office Action for U.S. Appl. No. 14/885,202, dated Apr. 14, 2016, 5 pages. |
Final Office Action for U.S. Appl. No. 14/885,202, dated Sep. 27, 2016, 7 pages. |
Advisory Action for U.S. Appl. No. 14/885,202, dated Nov. 29, 2016, 3 pages. |
Notice of Allowance for U.S. Appl. No. 14/885,202, dated Jan. 27, 2017, 7 pages. |
Notice of Allowance for U.S. Appl. No. 14/885,202, dated Jul. 24, 2017, 8 pages. |
Notice of Allowance for U.S. Appl. No. 14/885,243, dated Aug. 31, 2016, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 12/906,689, dated May 27, 2011, 13 pages. |
Non-Final Office Action for U.S. Appl. No. 12/906,689, dated Nov. 4, 2011, 20 pages. |
Search Report for Japanese Patent Application No. 2011-229152, dated Feb. 22, 2013, 58 pages. |
Office Action for Japanese Patent Application No. 2011-229152, dated May 10, 2013, 7 pages. |
Final Rejection for Japanese Patent Application No. 2011-229152, dated Oct. 25, 2013, 2 pages. |
International Search Report and Written Opinion for PCT/US2016/045809, dated Oct. 7, 2016, 11 pages. |
Non-Final Office Action for U.S. Appl. No. 15/652,867, dated Oct. 10, 2017, 5 pages. |
Bernheim et al., “Chapter 9: Lamination,” Tools and Manufacturing Engineers Handbook (book), Apr. 1, 1996, Society of Manufacturing Engineers, p. 9-1. |
Fillion R. et al., “Development of a Plastic Encapsulated Multichip Technology for High Volume, Low Cost Commercial Electronics,” Electronic Components and Technology Conference, vol. 1, May 1994, IEEE, 5 pages. |
Henawy, Mahmoud Al et al., “New Thermoplastic Polymer Substrate for Microstrip Antennas at 60 GHZ,” German Microwave Conference, Mar. 15-17, 2010, Berlin, Germany, IEEE, pp. 5-8. |
International Search Report and Written Opinion for PCT/US2017/046744, dated Nov. 27, 2017, 17 pages. |
International Search Report and Written Opinion for PCT/US2017/046758, dated Nov. 16, 2017, 19 pages. |
International Search Report and Written Opinion for PCT/US2017/046779, dated Nov. 29, 2017, 17 pages. |
Non-Final Office Action for U.S. Appl. No. 15/616,109, dated Oct. 23, 2017, 16 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 14/851,652, dated Oct. 20, 2017, 5 pages. |
Final Office Action for U.S. Appl. No. 15/262,457, dated Dec. 19, 2017, 12 pages. |
Supplemental Notice of Allowability and Applicant-Initiated Interview Summary for U.S. Appl. No. 15/287,273, dated Oct. 18, 2017, 6 pages. |
Supplemental Notice of Allowability for U.S. Appl. No. 15/287,273, dated Nov. 2, 2017, 5 pages. |
Non-Final Office Action for U.S. Appl. No. 15/491,064, dated Jan. 2, 2018, 9 pages. |
Notice of Allowance for U.S. Appl. No. 14/872,910, dated Nov. 17, 2017, 11 pages. |
Notice of Allowance for U.S. Appl. No. 15/648,082, dated Nov. 29, 2017, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 15/652,826, dated Nov. 3, 2017, 5 pages. |
Notice of Allowance for U.S. Appl. No. 15/229,780, dated Oct. 3, 2017, 7 pages. |
Supplemental Notice of Allowability for U.S. Appl. No. 15/287,273, dated Jan. 17, 2018, 5 pages. |
Notice of Allowance for U.S. Appl. No. 15/498,040, dated Feb. 20, 2018, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 15/387,855, dated Jan. 16, 2018, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 15/795,915, dated Feb. 23, 2018, 6 pages. |
International Preliminary Report on Patentability for PCT/US2016/045809, dated Feb. 22, 2018, 8 pages. |
Advisory Action and Applicant-Initiated Interview Summary for U.S. Appl. No. 15/262,457, dated Feb. 28, 2018, 5 pages. |
Supplemental Notice of Allowability for U.S. Appl. No. 15/287,273, dated Feb. 23, 2018, 5 pages. |
Non-Final Office Action for U.S. Appl. No. 15/676,415, dated Mar. 27, 2018, 14 page. |
Non-Final Office Action for U.S. Appl. No. 15/676,621, dated Mar. 26, 2018, 16 pages. |
Notice of Allowance for U.S. Appl. No. 15/795,915, dated Jun. 15, 2018, 7 pages. |
Final Office Action for U.S. Appl. No. 15/387,855, dated May 24, 2018, 9 pages. |
Non-Final Office Action for U.S. Appl. No. 15/262,457, dated Apr. 19, 2018, 10 pages. |
Notice of Allowance for U.S. Appl. No. 15/491,064, dated Apr. 30, 2018, 9 pages. |
Non-Final Office Action for U.S. Appl. No. 15/601,858, dated Jun. 26, 2018, 12 pages. |
Notice of Allowance for U.S. Appl. No. 15/616,109, dated Jul. 2, 2018, 7 pages. |
Notice of Allowance for U.S. Appl. No. 15/676,621, dated Jun. 5, 2018, 8 pages. |
Quayle Action for U.S. Appl. No. 16/426,527, dated May 26, 2022, 5 pages. |
Final Office Action for U.S. Appl. No. 16/427,019, dated Apr. 12, 2022, 15 pages. |
Advisory Action for U.S. Appl. No. 16/427,019, dated Jun. 2, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated May 13, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Jun. 15, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,573, dated May 6, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,573, dated Jun. 10, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Apr. 8, 2022, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated May 13, 2022, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Jun. 10, 2022, 4 pages. |
Notice of Allowance for U.S. Appl. No. 17/109,935, dated Apr. 20, 2022, 15 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2021/063093, dated May 4, 2022, 15 pages. |
Invitation to Pay Additional Fees and Partial International Search for International Patent Application No. PCT/ JS2021/063094, dated Apr. 19, 2022, 15 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2021/062509, dated Mar. 29, 2022, 20 pages. |
Notice of Allowance for U.S. Appl. No. 16/426,527, dated Aug. 17, 2022, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 16/427,019, dated Aug. 15, 2022, 17 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Jul. 14, 2022, 3 pages. |
Final Office Action for U.S. Appl. No. 16/678,586, dated Sep. 1, 2022, 7 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Jul. 14, 2022, 4 pages. |
Advisory Action for U.S. Appl. No. 16/844,406, dated Jul. 26, 2022, 3 pages. |
Corrected Notice of Allowability U.S. Appl. No. 17/109,935, dated Jul. 1, 2022, 4 pages. |
Corrected Notice of Allowability U.S. Appl. No. 17/109,935, dated Jul. 27, 2022, 4 pages. |
Final Office Action for U.S. Appl. No. 17/102,957, dated Aug. 18, 2022, 12 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2021/063094, dated Aug. 9, 2022, 24 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Sep. 2, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Sep. 2, 2022, 4 pages. |
Borel, S. et al., “Control of Selectivity between SiGe and Si in Isotropic Etching Processes,” Japanese Journal of Applied Physics, vol. 43, No. 6B, 2004, pp. 3964-3966. |
Non-Final Office Action for U.S. Appl. No. 16/427,019, dated Dec. 2, 2021, 17 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Nov. 24, 2021, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Jan. 27, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,573, dated Nov. 24, 2021, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,573, dated Jan. 27, 2022, 3 pages. |
Final Office Action for U.S. Appl. No. 16/678,586, dated Nov. 22, 2021, 15 pages. |
Advisory Action for U.S. Appl. No. 16/678,586, dated Jan. 26, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Nov. 24, 2021, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Dec. 30, 2021, 4 pages. |
Decision of Rejection for Chinese Patent Application No. 201680058198.6, dated Nov. 12, 2021, 6 pages. |
Examination Report for European Patent Application No. 17755402.9, dated Dec. 20, 2021, 12 pages. |
Examination Report for European Patent Application No. 17755403.7, dated Dec. 20, 2021, 13 pages. |
Notice of Allowance for Japanese Patent Application No. 2019507767, dated Jan. 19, 2021, 6 pages. |
International Search Report and Written Opinion for International Patent Application No. PCT/US2021/043968, dated Nov. 19, 2021, 15 pages. |
Non-Final Office Action for U.S. Appl. No. 15/676,693, dated May 3, 2018, 14 pages. |
Notice of Allowance for U.S. Appl. No. 15/789, 107, dated May 18, 2018, 8 pages. |
Final Office Action for U.S. Appl. No. 15/616,109, dated Apr. 19, 2018, 18 pages. |
Notice of Allowance for U.S. Appl. No. 15/676,693, dated Jul. 20, 2018, 8 pages. |
Notice of Allowance for U.S. Appl. No. 15/695,629, dated Jul. 11, 2018, 12 pages. |
Notice of Allowance for U.S. Appl. No. 15/387,855, dated Aug. 10, 2018, 7 pages. |
Notice of Allowance for U.S. Appl. No. 15/914,538, dated Aug. 1, 2018, 9 pages. |
Notice of Allowance and Applicant-Initiated Interview Summary for U.S. Appl. No. 15/262,457, dated Sep. 28, 2018, 16 pages. |
Corrected Notice of Allowance for U.S. Appl. No. 15/676,693, dated Aug. 29, 2018, 5 pages. |
Final Office Action for U.S. Appl. No. 15/601,858, dated Nov. 26, 2018, 16 pages. |
Non-Final Office Action for U.S. Appl. No. 15/945,418, dated Nov. 1, 2018, 13 pages. |
First Office Action for Chinese Patent Application No. 201510746323.X, dated Nov. 2, 2018, 12 pages. |
Advisory Action for U.S. Appl. No. 15/601,858, dated Jan. 22, 2019, 3 pages. |
Notice of Allowance for U.S. Appl. No. 16/038,879, dated Jan. 9, 2019, 8 pages. |
Notice of Allowance for U.S. Appl. No. 16/004,961, dated Jan. 11, 2019, 8 pages. |
International Preliminary Report on Patentability for PCT/US2017/046744, dated Feb. 21, 2019, 11 pages. |
International Preliminary Report on Patentability for PCT/US2017/046758, dated Feb. 21, 2019, 11 pages. |
International Preliminary Report on Patentability for PCT/US2017/046779, dated Feb. 21, 2019, 11 pages. |
Non-Final Office Action for U.S. Appl. No. 15/992,613, dated Feb. 27, 2019, 15 pages. |
Non-Final Office Action for U.S. Appl. No. 15/695,579, dated Jan. 28, 2019, 8 pages. |
Notice of Allowance for U.S. Appl. No. 15/992,639, dated May 9, 2019, 7 pages. |
Notice of Allowance for U.S. Appl. No. 15/695,579, dated Mar. 20, 2019, 8 pages. |
Notice of Allowance for U.S. Appl. No. 16/004,961, dated May 13, 2019, 8 pages. |
Non-Final Office Action for U.S. Appl. No. 15/601,858, dated Apr. 17, 2019, 9 pages. |
Tsai, Chun-Lin, et al., “Smart GaN platform; Performance & Challenges,” IEEE International Electron Devices Meeting, 2017, 4 pages. |
Tsai, Szu-Ping., et al., “Performance Enhancement of Flip-Chip Packaged AlGAaN/GaN HEMTs by Strain Engineering Design,” IEEE Transcations on Electron Devices, vol. 63, Issue 10, Oct. 2016, pp. 3876-3881. |
Final Office Action for U.S. Appl. No. 15/992,613, dated May 24, 2019, 11 pages. |
Non-Final Office Action for U.S. Appl. No. 15/873, 152, dated May 24, 2019, 11 pages. |
Notice of Allowance for U.S. Appl. No. 16/168,327, dated Jun. 28, 2019, 7 pages. |
Lin, Yueh, Chin, et al., “Enhancement-Mode GaN MIS-HEMTs With LaHfOx Gate Insulator for Power Application,” EEE Electronic Device Letters, vol. 38, Issue 8, 2017, 4 pages. |
Shukla, Shishir, et al., “GaN-on-Si Switched Mode RF Power Amplifiers for Non-Constant Envelope Signals,” IEEE Topical Conference on RF/Microwave Power Amplifiers for Radio and Wireless Applications, 2017, pp. 88-91. |
International Search Report and Written Opinion for International Patent Application No. PCT/US19/25591, dated Jun. 21, 2019, 7 pages. |
Notice of Reasons for Refusal for Japanese Patent Application No. 2015-180657, dated Jul. 9, 2019, 4 pages. |
Notice of Allowance for U.S. Appl. No. 15/601,858, dated Aug. 16, 2019, 8 pages. |
Advisory Action for U.S. Appl. No. 15/992,613, dated Jul. 29, 2019, 3 pages. |
Final Office Action for U.S. Appl. No. 15/873, 152, dated Aug. 8, 2019, 13 pages. |
Notice of Allowance for U.S. Appl. No. 15/975,230, dated Jul. 22, 2019, 7 pages. |
Notice of Allowance for U.S. Appl. No. 16/004,961, dated Aug. 28, 2019, 8 pages. |
Fiorenza, et al., “Detailed Simulation Study of a Reverse Embedded-SiGE Strained-Silicon MOSFET,” IEEE Transactions on Electron Devices, vol. 55, Issue 2, Feb. 2008, pp. 640-648. |
Fiorenza, et al., “Systematic study of thick strained silicon NMOSFETs for digital applications,” International SiGE Technology and Device Meeting, May 2006, IEEE, 2 pages. |
Huang, et al., “Carrier Mobility Enhancement in Strained Si-On-Insulator Fabricated by Wafer Bonding,” Symposium on VLSI Technology, Digest of Technical Papers, 2001, pp. 57-58. |
Nan, et al., “Effect of Germanium content on mobility enhancement for strained silicon FET,” Student Conference on Research and Development, Dec. 2017, IEEE, pp. 154-157. |
Sugii, Nobuyuki, et al., “Performance Enhancement of Strained-Si MOSFETs Fabricated on a Chemical-Mechanical-Polished SiGE Substrate,” IEEE Transactions on Electron Devices, vol. 49, Issue 12, Dec. 2002, pp. 2237-2243. |
Yin, Haizhou, et al., “Fully-depleted Strained-Si on Insulator NMOSFETs without Relaxed SiGe Buffers,” International Electron Devices Meeting, Dec. 2003, San Francisco, California, IEEE, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 15/695,579, dated Feb. 5, 2020, 5 pages. |
Notice of Allowance for U.S. Appl. No. 15/992,613, dated Sep. 23, 2019, 7 pages. |
Non-Final Office Action for U.S. Appl. No. 16/204,214, dated Oct. 9, 2019, 15 pages. |
Non-Final Office Action for U.S. Appl. No. 15/816,637, dated Oct. 31, 2019, 10 pages. |
Advisory Action for U.S. Appl. No. 15/873, 152, dated Oct. 11, 2019, 3 pages. |
Notice of Allowance for U.S. Appl. No. 15/873,152, dated Dec. 10, 2019, 9 pages. |
Ali, K. Ben et al., “RF SOI CMOS Technology on Commercial Trap-Rich High Resistivity SOI Wafer,” 2012 IEEE International SOI Conference (SOI), Oct. 1-4, 2012, Napa, California, IEEE, 2 pages. |
Anderson, D.R., “Thermal Conductivity of Polymers,” Sandia Corporation, Mar. 8, 1966, pp. 677-690. |
Author Unknown, “96% Alumina, thick-film, as fired,” MatWeb, Date Unknown, date accessed Apr. 6, 2016, 2 pages, http://www.matweb.com/search/DataSheet.aspx?MatGUID=3996a734395a4870a9739076918c4297&ckck=1. |
Author Unknown, “CoolPoly D5108 Thermally Conductive Polyphenylene Sulfide (PPS),” Cool Polymers, Inc., Aug. 8, 2007, 2 pages. |
Author Unknown, “CoolPoly D5506 Thermally Conductive Liquid Crystalline Polymer (LCP),” Cool Polymers, Inc., Dec. 12, 2013, 2 pages. |
Author Unknown, “CoolPoly D-Series—Thermally Conductive Dielectric Plastics,” Cool Polymers, Retrieved Jun. 24, 2013, http:/coolpolymers.com/dseries.asp, 1 page. |
Author Unknown, “CoolPoly E2 Thermally Conductive Liquid Crystalline Polymer (LCP),” Cool Polymers, Inc., Aug. 8, 2007, http://www.coolpolymers.com/Files/DS/Datasheet_e2.pdf, 1 page. |
Author Unknown, “CoolPoly E3605 Thermally Conductive Polyamide 4,6 (PA 4,6),” Cool Polymers, Inc., Aug. 4, 2007, 1 page, http://www.coolpolymers.com/Files/DS/Datasheet_e3605.pdf. |
Author Unknown, “CoolPoly E5101 Thermally Conductive Polyphenylene Sulfide (PPS),” Cool Polymers, Inc., Aug. 27, 2007, 1 page, http://www.coolpolymers.com/Files/DS/Datasheet_e5101.pdf. |
Author Unknown, “CoolPoly E5107 Thermally Conductive Polyphenylene Sulfide (PPS),” Cool Polymers, Inc., Aug. 8, 2007, 1 page, http://coolpolymers.com/Files/DS/Datasheet_e5107.pdf. |
Author Unknown, “CoolPoly Selection Tool,” Cool Polymers, Inc., 2006, 1 page, http://www.coolpolymers.com/select.asp?Application=Substrates+%26+Electcronic_Packaging. |
Author Unknown, “CoolPoly Thermally Conductive Plastics for Dielectric Heat Plates,” Cool Polymers, Inc., 2006, 2 pages, http://www.coolpolymers.com/heatplate.asp. |
Author Unknown, “CoolPoly Thermally Conductive Plastics for Substrates and Electronic Packaging,” Cool Polymers, Inc., 2005, 1 page. |
Author Unknown, “Electrical Properties of Plastic Materials,” Professional Plastics, Oct. 28, 2011, http://www.professionalplastics.com/professionalplastics/ElectricalPropertiesofPlastics.pdf, accessed Dec. 18, 2014, 4 pages. |
Author Unknown, “Fully Sintered Ferrite Powders,” Powder Processing and Technology, LLC, Date Unknown, 1 page. |
Author Unknown, “Heat Transfer,” Cool Polymers, Inc., 2006, http://www.coolpolymers.com/heattrans.html, 2 pages. |
Author Unknown, “Hysol UF3808,” Henkel Corporation, Technical Data Sheet, May 2013, 2 pages. |
Author Unknown, “PolyOne Therma-Tech™ LC-5000C Tc Lcp,” MatWeb, Date Unknown, date accessed Apr. 6, 2016, 2 pages, http://www.matweb.com/search/datasheettext.aspx? matguid=89754e8bb26148d083c5ebb05a0cbff1. |
Author Unknown, “Sapphire Substrate,” from CRC Handbook of Chemistry and Physics, Date Unknown, 1 page. |
Author Unknown, “Thermal Properties of Plastic Materials,” Professional Plastics, Aug. 21, 2010, http://www.professionalplastics.com/professionalplastics/ThermalPropertiesofPlasticMaterials.pdf, accessed Dec. 18, 2014, 4 pages. |
Author Unknown, “Thermal Properties of Solids,” PowerPoint Presentation, No. Date, 28 slides, http://www.phys.huji.ac.il/Phys_Hug/Lectures/77602/PHONONS_2_thermal.pdf. |
Author Unknown, “Thermal Resistance & Thermal Conductance,” C-Therm Technologies Ltd., accessed Sep. 19, 2013, 4 pages, http://www.ctherm.com/products/tci_thermal_conductivity/helpful_links_tools/thermal_resistance_thermal_conductance/. |
Author Unknown, “The Technology: AKHAN's Approach and Solution: The Miraj Diamond™ Platform,” 2015, accessed Oct. 9, 2016, http://www.akhansemi.com/technology.html#/the-miraj-diamond-platform, 5 pages. |
Beck, D., et al., “CMOS on FZ-High Resistivity Substrate for Monolithic Integration of SiGe-RF-Circuitry and Readout Electronics,” IEEE Transactions on Electron Devices, vol. 44, No. 7, Jul. 1997, pp. 1091-1101. |
Botula, A., et al., “A Thin-Film SOI 180nm CMOS RF Switch Technology,” IEEE Topical Meeting on Silicon Monolithic Integrated Circuits in RF Systems, (SiRF '09), Jan. 2009, pp. 1-4. |
Carroll, M., et al., “High-Resistivity SOI CMOS Cellular Antenna Switches,” Annual IEEE Compound Semiconductor Integrated Circuit Symposium, (CISC 2009), Oct. 2009, pp. 1-4. |
Colinge, J.P., et al., “A Low-Voltage, Low-Power Microwave SOI MOSFET,” Proceedings of 1996 IEEE International SOI Conference, Oct. 1996, pp. 128-129. |
Costa, J. et al., “Integrated MEMS Switch Technology On SOI-CMOS,” Proceedings of Hilton Head Workshop: A Solid-State Sensors, Actuators and Microsystems Workshop, Jun. 1-5, 2008, Hilton Head Island, SC, IEEE, pp. 900-903. |
Costa, J. et al., “Silicon RFCMOS SOI Technology with Above-IC MEMS Integration for Front End Wireless Applications,” Bipolar/BiCMOS Circuits and Technology Meeting, 2008, BCTM 2008, IEEE, pp. 204-207. |
Costa, J., “RFCMOS SOI Technology for 4G Reconfigurable RF Solutions,” Session WEC1-2, Proceedings of the 2013 IEEE International Microwave Symposium, 4 pages. |
Esfeh, Babak Kazemi et al., “RF Non-Linearities from Si-Based Substrates,” 2014 International Workshop on Integrated Nonlinear Microwave and Millimetre-wave Circuits (INMMiC), Apr. 2-4, 2014, IEEE, 3 pages. |
Finne, R. M. et al., “A Water-Amine-Complexing Agent System for Etching Silicon,” Journal of The Electrochemical Society, vol. 114, No. 9, Sep. 1967, pp. 965-970. |
Gamble, H. S. et al., “Low-Loss CPW Lines on Surface Stabilized High-Resistivity Silicon,” IEEE Microwave and Guided Wave Letters, vol. 9, No. 10, Oct. 1999, pp. 395-397. |
Huang, Xingyi, et al., “A Review of Dielectric Polymer Composites with High Thermal Conductivity,” IEEE Electrical Insulation Magazine, vol. 27, No. 4, Jul./Aug. 2011, pp. 8-16. |
Joshi, V. et al., “MEMS Solutions in RF Applications,” 2013 IEEE SOI-3D-Subthreshold Microelectronics Technology Unified Conference (S3S), Oct. 2013, IEEE, 2 pages. |
Jung, Boo Yang, et al., “Study of FCMBGA with Low CTE Core Substrate,” 2009 Electronic Components and Technology Conference, May 2009, pp. 301-304. |
Kerr, D.C., et al., “Identification of RF Harmonic Distortion on Si Substrates and Its Reduction Using a Trap-Rich Layer,” IEEE Topical Meeting on Silicon Monolithic Integrated Circuits in RF Systems, (SiRF 2008), Jan. 2008, pp. 151-154. |
Lederer, D., et al., “New Substrate Passivation Method Dedicated to HR SOI Wafer Fabrication with Increased Substrate Resistivity,” IEEE Electron Device Letters, vol. 26, No. 11, Nov. 2005, pp. 805-807. |
Lederer, Dimitri et al., “Substrate loss mechanisms for microstrip and CPW transmission lines on lossy silicon wafers,” Solid-State Electronics, vol. 47, No. 11, Nov. 2003, pp. 1927-1936. |
Lee, Kwang Hong et al., “Integration of III-V materials and Si-CMOS through double layer transfer process,” Japanese Journal of Applied Physics, vol. 54, Jan. 2015, pp. 030209-1 to 030209-5. |
Lee, Tzung-Yin, et al., “Modeling of SOI FET for RF Switch Applications,” IEEE Radio Frequency Integrated Circuits Symposium, May 23-25, 2010, Anaheim, CA, IEEE, pp. 479-482. |
Lu, J.Q., et al., “Evaluation Procedures for Wafer Bonding and Thinning of Interconnect Test Structures for 3D ICs,” Proceedings of the IEEE 2003 International Interconnect Technology Conference, Jun. 2-4, 2003, pp. 74-76. |
Mamunya, Ye.P., et al., “Electrical and Thermal Conductivity of Polymers Filled with Metal Powders,” European Polymer Journal, vol. 38, 2002, pp. 1887-1897. |
Mansour, Raafat R., “RF MEMS-CMOS Device Integration,” IEEE Microwave Magazine, vol. 14, No. 1, Jan. 2013, pp. 39-56. |
Mazuré, C. et al., “Advanced SOI Substrate Manufacturing,” 2004 IEEE International Conference on Integrated Circuit Design and Technology, 2004, IEEE, pp. 105-111. |
Micak, R. et al., “Photo-Assisted Electrochemical Machining of Micromechanical Structures,” Proceedings of Micro Electro Mechanical Systems, Feb. 7-10, 1993, Fort Lauderdale, FL, IEEE, pp. 225-229. |
Morris, Art, “Monolithic Integration of RF-MEMS within CMOS,” 2015 International Symposium on VLSI Technology, Systems and Application (VLSI-TSA), Apr. 27-29, 2015, IEEE, 2 pages. |
Niklaus, F., et al., “Adhesive Wafer Bonding,” Journal of Applied Physics, vol. 99, No. 3, 031101 (2006), 28 pages. |
Parthasarathy, S., et al., “RF SOI Switch FET Design and Modeling Tradeoffs for GSM Applications,” 2010 23rd International Conference on VLSI Design, (VLSID '10), Jan. 2010, pp. 194-199. |
Raskin, J.P., et al., “Coupling Effects in High-Resistivity SIMOX Substrates for VHF and Microwave Applications,” Proceedings of 1995 IEEE International SOI Conference, Oct. 1995, pp. 62-63. |
Non-Final Office Action for U.S. Appl. No. 16/426,527, dated Feb. 16, 2022, 9 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Mar. 9, 2022, 3 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,573, dated Mar. 31, 2022, 3 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,586, dated Mar. 3, 2022, 14 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Feb. 2, 2022, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,602, dated Mar. 9, 2022, 4 pages. |
Non-Final Office Action for U.S. Appl. No. 16/844,406, dated Mar. 14, 2022, 16 pages. |
Non-Final Office Action for U.S. Appl. No. 17/102,957, dated Feb. 17, 2022, 9 pages. |
Summons to Attend for European Patent Application No. 16751791.1, dated Feb. 28, 2022, 10 pages. |
Decision to Grant for Japanese Patent Application No. 2019507765, dated Feb. 10, 2022, 6 pages. |
Decision to Grant for Japanese Patent Application No. 2019507768, dated Feb. 10, 2022, 6 pages. |
Office Letter for Taiwanese Patent Application No. 108140788, dated Jan. 5, 2022, 16 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 16/678,551, dated Apr. 11, 2022, 3 pages. |
Final Office Action for U.S. Appl. No. 16/844,406, dated Jun. 24, 2022, 17 pages. |
Notice of Allowance for U.S. Appl. No. 16/427,019, dated Mar. 10, 2023, 10 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,551, dated Mar. 28, 2023, 14 pages. |
Notice of Allowance for U.S. Appl. No. 17/573,112, dated Mar. 8, 2023, 8 pages. |
Notice of Allowance for U.S. Appl. No. 17/554,477, dated Mar. 7, 2023, 8 pages. |
Final Office Action for U.S. Appl. No. 16/844,406, dated Mar. 6, 2023, 13 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/109,935, dated Mar. 1, 2023, 4 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/109,935, dated Apr. 12, 2023, 4 pages. |
Non-Final Office Action for U.S. Appl. No. 17/102,957, dated Apr. 13, 2023, 24 pages. |
Non-Final Office Action for U.S. Appl. No. 17/389,977, dated Mar. 28, 2023, 10 pages. |
Written Decision on Registration for Korean Patent Application No. 10-2018-7006660, dated Feb. 24, 2023, 8 pages. |
Decision to Grant for Japanese Patent Application No. 2022032477, dated Mar. 14, 2023, 5 pages. |
Decision of Rejection for Chinese Patent Application No. 201780058052.6, dated Mar. 30, 2023, 16 pages. |
Office Action for Taiwanese Patent Application No. 109102892, dated Apr. 14, 2023, 18 pages. |
Advisory Action for U.S. Appl. No. 16/844,406, dated May 12, 2023, 3 pages. |
First Office Action for Chinese Patent Application No. 201980079375.2, dated May 5, 2023, 17 pages. |
Preliminary Examination Report for Taiwanese Patent Application No. 109102895, dated May 30, 2023, 18 pages. |
Preliminary Examination Report for Taiwanese Patent Application No. 109102896, dated Jul. 4, 2023, 19 pages. |
Final Office Action for U.S. Appl. No. 16/426,527, dated May 25, 2023, 9 pages. |
Notice of Allowance for U.S. Appl. No. 16/426,527, dated Jun. 22, 2023, 8 pages. |
Final Office Action for U.S. Appl. No. 16/678,551, dated May 26, 2023, 16 pages. |
Non-Final Office Action for U.S. Appl. No. 16/844,406, dated Jun. 23, 2023, 18 pages. |
Preliminary Examination Report for Taiwanese Patent Application No. 109102894, dated Apr. 7, 2023, 20 pages. |
Notice of Allowance for U.S. Appl. No. 17/306, 194, dated Aug. 24, 2023, 10 pages. |
Notice of Allowance for U.S. Appl. No. 16/390,496, dated Aug. 24, 2023, 24 pages. |
Notice of Allowance for U.S. Appl. No. 17/970,078, dated Aug. 25, 2023, 10 pages. |
Advisory Action for U.S. Appl. No. 16/678,551, dated Jul. 28, 2023, 3 pages. |
Applicant-Initiated Interview Summary for U.S. Appl. No. 16/678,551, dated Aug. 22, 2023, 7 pages. |
Applicant-Initiated Interview Summary for U.S. Appl. No. 16/844,406, dated Sep. 13, 2023, 2 pages. |
Final Office Action for U.S. Appl. No. 16/844,406, dated Sep. 28, 2023, 7 pages. |
Notice of Allowance for U.S. Appl. No. 17/389,977, dated Aug. 16, 2023, 8 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/389,977, dated Sep. 20, 2023, 5 pages. |
Office Action for Taiwanese Patent Application No. 108119536, dated Jul. 13, 2023, 6 pages. |
First Office Action for Chinese Patent Application No. 201980077328.4, dated Aug. 28, 2023, 15 pages. |
Notice of Preliminary Rejection for Korean Patent Application No. 1020217026777, dated Jul. 28, 2023, 12 pages. |
Quayle Action for U.S. Appl. No. 16/678,551, dated Oct. 4, 2023, 6 pages. |
Non-Final Office Action for U.S. Appl. No. 16/678,602, dated Oct. 6, 2023, 18 pages. |
Notice of Allowance for for U.S. Appl. No. 16/844,406, dated Nov. 16, 2023, 11 pages. |
Final Office Action for U.S. Appl. No. 17/102,957, dated Oct. 26, 2023, 27 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/389,977, dated Oct. 25, 2023, 5 pages. |
Board Opinion for Chinese Patent Application No. 201780058052.6, dated Oct. 8, 2023, 15 pages. |
First Office Action for Chinese Patent Application No. 201980050433.9, dated Sep. 4, 2023, 20 pages. |
First Office Action for Chinese Patent Application No. 201980090320.1, dated Sep. 5, 2023, 11 pages. |
Office Action for Taiwanese Patent Application No. 109102892, dated Sep. 13, 2023, 18 pages. |
Preliminary Examination Report for Taiwanese Patent Application No. 109102893, dated Sep. 7, 2023, 10 pages. |
Notice of Allowance for U.S. Appl. No. 16/678,551, dated Dec. 7, 2023, 9 pages. |
Corrected Notice of Allowability for U.S. Appl. No. 17/389,977, dated Nov. 24, 2023, 5 pages. |
Office Action for Taiwanese Patent Application No. 108119536, dated Nov. 24, 2023, 22 pages. |
Preliminary Examination Report for Taiwanese Patent Application No. 108143149, dated Oct. 18, 2023, 30 pages. |
Second Office Action for Chinese Patent Application No. 201980079375.2, dated Nov. 21, 2023, 17 pages. |
Office Action for Taiwanese Patent Application No. 109102895, dated Nov. 30, 2023, 16 pages. |
Notice of Allowance for U.S. Appl. No. 16/426,527, dated Jan. 22, 2024, 10 pages. |
Non-Final Office Action for U.S. Appl. No. 18/306,599, dated Jan. 22, 2024, 11 pages. |
Notice of Allowance for U.S. Appl. No. 17/389,977, dated Jan. 18, 2024, 17 pages. |
Board Opinion for Chinese Patent Application No. 201780058052.6, dated Jan. 15, 2024, 28 pages. |
Reasons for Rejection for Taiwanese Patent Application No. 109102896, dated Dec. 13, 2023. |
Number | Date | Country | |
---|---|---|---|
20210183693 A1 | Jun 2021 | US |
Number | Date | Country | |
---|---|---|---|
62947444 | Dec 2019 | US |