Claims
- 1. A method of making a circuit board from a substrate said circuit board having at least one conductive path on at least one side thereof and having at least one conductive passage therethrough in electrical conduction with at least one of said path, said method comprising the steps of:
- forming a tapered passage through the substrate and at least one groove on at least one side of the substrate with at least one groove connected to said tapered passage;
- filling the passage and the groove on at least one side with an electrically conductive metal powder;
- applying pressure with a die having a tapered portion to compact the metal powder against the wall of the tapered passage without blocking the passage and compact the metal powder in the groove; and
- heating the compacted powder to about its isothermal annealing temperature.
- 2. The method as described in claim 1 wherein the step of applying pressure to compact the powder comprises:
- applying the maximum pressure possible to the powder and substrate which can be applied without affecting the substrate in a manner such that it would not be acceptable for use as a circuit board.
- 3. The method as described in claim 1 wherein the pressure applied is about 20,000 to 55,000 psi at room temperature.
- 4. The method as described in claim 2 wherein the pressure applied is about 20,000 to 55,000 psi at room temperature.
- 5. The method as described in claim 1 wherein the electrically conductive powder is a copper electrolytic dust and the temperature to which the compacted powder is heated is of about 200 degrees centigrade for a period of 20 to 60 minutes.
- 6. The method as described in claim 2 wherein the electrically conductive powder is a copper electrolytic dust and the temperature to which the compacted powder is heated is of about 200 degrees centigrade for a period of 20 to 60 minutes.
- 7. The method as described in claim 1 wherein the conductive powder is tin.
- 8. The method as described in claim 7 wherein the pressure applied is above 10,000 psi at room temperature.
- 9. The method as described in claim 3 wherein the electrically conductive powder is a copper electrolytic dust and wherein the compacted powder is heated to a temperature of about 200 degrees centigrade for a period of 20 to 60 minutes.
- 10. The method as described in claim 4 wherein the electrically conductive powder is a copper electrolytic dust and wherein the compacted powder is heated to a temperature of about 200 degrees centigrade for a period of 20 to 60 minutes.
Parent Case Info
This application is a continuation of application Ser. No. 534,428, filed Sept. 21, 1983, abandoned.
US Referenced Citations (11)
Foreign Referenced Citations (3)
Number |
Date |
Country |
0109084 |
May 1984 |
EPX |
1404697 |
Sep 1975 |
GBX |
8301886 |
May 1983 |
WOX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
534428 |
Sep 1983 |
|