Claims
- 1. The process of forming a substrate for an electronic application, comprising the steps of:
- providing first material particles having a coefficient of thermal expansion in the range of about -20.times.10.sup.-7 to about 50.times.10.sup.-7 in/in.degree.C.;
- providing second material particles having a coefficient of thermal expansion in the range of about 100.times.10.sup.-7 to about 239.times.10.sup.-7 in/in/.degree.C.;
- mixing said first material particles with said second material particles; and
- bonding the mixture of said first and second material particles together with a bonding agent to form a coherent composite being a strong, resistant to thermal shock substrate having a coefficient of thermal expansion substantially less than about 100.times.10.sup.-7 in/in/.degree.C., said bonding agent adhering to said first and second material particles while maintaining the individual characteristics of the first and second material particles.
- 2. The process of claim 1 including the step of selecting said first and second materials so that said composite has a thermal conductivity in the range of about 65 to about 230 BTU/ft/ft.sup.2 /hr/.degree.F.
- 3. The process of claim 2 including the step of selecting said first material of particles from the group consisting of silica, ceramics, glass, metals and metal alloys.
- 4. The process of claim 3 further including said first material being particles of silica.
- 5. The process of claim 3 further including said first material being particles of glass.
- 6. The process of claim 3 further including said first material being particles of metal.
- 7. The process of claim 3 further including said first material being particles of metal alloys.
- 8. The process of claim 3 further including said first material being particles of ceramics.
- 9. The process of claim 3 including the step of selecting said second material from the group consisting of metal and metal alloys.
- 10. The process of claim 9 including the step of forming said composite into a strip.
- 11. The process of claim 10 further including the step of bonding a metallic foil to at least one surface of the composite strip.
- 12. The process of claim 10 including the step of coating a continuous layer of low melting temperature glass onto at least one surface of the composite strip.
- 13. The process of claim 12 further including the step of partially removing said second material from at least one surface of said composite strip to enhance the adherence of the glass coating to the first material particles.
- 14. The process of claim 1 including the steps of:
- compacting the first and second material particles and the bonding agent into a mixture of a desired shape; and
- consolidating the mixture with heat.
- 15. The process of claim 14 further including the step of heating said mixture in a reducing atmosphere to substantially eliminate metal oxides.
- 16. The process of claim 15 further including the step of coating the first material particles with the bonding agent prior to mixing the first and second material particles together.
- 17. The process of claim 15 including the step of coating the first material particles with the second material particles prior to mixing the first and second material particles together.
- 18. The process of claim 2 including the step of filling the interstices between the first and second material particles with a bonding agent.
- 19. The process of claim 9 including the step of selecting said bonding agent from the group consisting of glasses, organic adhesives, ceramics and metals.
- 20. The process of claim 19 further including said bonding agent being glass.
- 21. The process of claim 19 further including said bonding agent being an organic adhesive.
- 22. The process of claim 19 further including said bonding agent being a ceramic.
- 23. The process of claim 19 further including said bonding agent being a metal.
Parent Case Info
This application is a division, of application Ser. No. 539,449, filed Oct. 6, 1983 now U.S. Pat. No. 4,569,692.
US Referenced Citations (3)
Divisions (1)
|
Number |
Date |
Country |
Parent |
539449 |
Oct 1983 |
|