Patent Grant
7355208
1. Field of the Invention
The present invention relates to a nitride-based semiconductor element and a method of forming a nitride-based semiconductor, and more specifically, it relates to a nitride-based semiconductor element including a nitride-based semiconductor layer formed by epitaxial lateral overgrowth and a method of forming a nitride-based semiconductor.
2. Description of the Prior Art
In recent years, a nitride-based semiconductor element utilizing a group III nitride-based semiconductor is actively developed as a semiconductor element employed for a semiconductor light-emitting device such as a light-emitting diode device or a semiconductor laser device or an electronic device such as a transistor. In order to fabricate such a nitride-based semiconductor element, a nitride-based semiconductor layer is epitaxially grown on a substrate consisting of sapphire or the like.
In this case, the substrate of sapphire or the like and the nitride-based semiconductor layer have different lattice constants and hence the nitride-based semiconductor layer grown on the substrate of sapphire or the like has dislocations (lattice defects) vertically extending from the substrate to the surface of the semiconductor layer. Such dislocations in the nitride-based semiconductor layer result in deterioration of the element characteristics of the semiconductor element and reduction of the reliability thereof.
As a method of reducing the density of the aforementioned dislocations in the nitride-based semiconductor layer, epitaxial lateral growth is generally proposed. This epitaxial lateral growth is disclosed in International Workshop on Nitride Semiconductors—IWN2000—, Nagoya, Japan, 2000, p. 79, for example.
First, a GaN layer 102 for serving as an underlayer is formed on a substrate 101 consisting of sapphire or SiC, as shown in
Then, portions of the GaN layer 102 located under regions formed with no mask layers 103 are removed by etching while etching the substrate 101 by a thickness in the range not reaching the bottom surface thereof through the mask layers 103 serving for etching in this process. Thus, the substrate 101 is brought into a ridged shape, while stripe-patterned GaN layers 102 to be in contact substantially with the overall upper surfaces of projection potions of the substrate 101, as shown in
Then, undoped GaN layers 104 are re-grown from exposed side surfaces, serving as seed crystals, of the GaN layers 102, as shown in
In the conventional method of forming a nitride-based semiconductor, as hereinabove described, the undoped GaN layer 102 is formed by epitaxial lateral overgrowth from the exposed side surfaces of the GaN layers 102 serving as seed crystals, whereby lattice defects are scarcely propagated from the GaN layers 102 to a portion around the surface of the undoped GaN layer 104. Thus, the undoped GaN layer 104 reduced in dislocation density is obtained. When a nitride-based semiconductor element layer (not shown) having an element region is formed on such an undoped GaN layer 104 reduced in dislocation density, a nitride-based semiconductor element having excellent crystallinity can be formed.
In the aforementioned conventional method of forming a nitride-based semiconductor employing epitaxial lateral overgrowth, however, the substrate 101 is brought into the ridged shape by removing the portions of the GaN layers 102 located under the regions formed with no mask layers 103 by etching and thereafter further etching the substrate 101. In general, therefore, the layers GaN 102, which are hardly etched nitride-based semiconductor layers, must be etched along the overall thicknesses thereof while the surface of the substrate 101 must also be etched. Thus, the etching time for bringing the substrate 101 into the ridged shape is disadvantageously increased. Consequently, the nitride-based semiconductor is disadvantageously reduced in mass productivity.
In the aforementioned conventional method of forming a nitride-based semiconductor employing epitaxial lateral overgrowth, further, the undoped GaN layer 104 is formed by growing the GaN layers 102 serving as underlayers on the substrate 101 and thereafter epitaxially laterally overgrowing the GaN layers 102. Therefore, this method requires two crystal growth steps for the GaN layers 102 and the undoped GaN layer 104. In general, therefore, the nitride-based semiconductor is reduced in mass productivity also in this point.
An object of the present invention is to provide a nitride-based semiconductor element having superior mass productivity and excellent element characteristics.
Another object of the present invention is to provide a method of forming a nitride-based semiconductor capable of obtaining a nitride-based semiconductor layer having excellent mass productivity and low dislocation density.
A nitride-based semiconductor element according to a first aspect of the present invention comprises a substrate comprising a surface having projection portions, a mask layer formed to be in contact with only the projection portions of the surface of the substrate, a first nitride-based semiconductor layer formed on recess portions of the substrate and the mask layer, and a nitride-based semiconductor element layer, formed on the first nitride-based semiconductor layer, having an element region.
The nitride-based semiconductor element according to the first aspect is provided with the substrate comprising a surface having projection portions and the mask layer formed to be in contact with only the projection portions of the surface of the substrate as hereinabove described, whereby the first nitride-based semiconductor layer having low dislocation density can be readily formed on the recess potions of the substrate and the mask layer through the mask layer serving for selective growth. When the nitride-based semiconductor element layer having the element region is grown on the first nitride-based semiconductor layer having low dislocation density, a nitride-based semiconductor element having excellent element characteristics can be readily obtained. Further, only the surface of the substrate may be etched for forming the projection portions. Thus, the etching time for forming the projection portions can be reduced. According to the first aspect, further, the first nitride-based semiconductor layer can be formed through single growth on the substrate. Consequently, a nitride-based semiconductor element having excellent mass productivity can be obtained.
In the aforementioned nitride-based semiconductor element according to the first aspect, the substrate preferably includes a substrate selected from a group consisting of a sapphire substrate, a spinel substrate, an Si substrate, an SiC substrate, a GaN substrate, a GaAs substrate, a GaP substrate, an InP substrate, a ZrB2 substrate and a quartz substrate. In this case, the substrate preferably includes a sapphire substrate, while the mask layer and the projection portions of the surface of the substrate are preferably formed in the shape of stripes being parallel to the [1-100] direction of the sapphire substrate. The substrate preferably includes an Si substrate, and the mask layer and the projection portions of the surface of the substrate are preferably formed in the shape of stripes being parallel to the [1-10] direction of the Si substrate.
The aforementioned nitride-based semiconductor element according to the first aspect preferably further comprises a buffer layer formed on the interface between the recess portions of the substrate and the first nitride-based semiconductor layer. According to this structure, the first nitride-based semiconductor layer having lower dislocation density can be formed on the buffer layer.
A nitride-based semiconductor element according to a second aspect of the present invention comprises an underlayer, formed on a substrate, consisting of a nitride-based semiconductor and comprising a surface having projection portions, a mask layer formed to be in contact with only the projection portions of the surface of the underlayer, a first nitride-based semiconductor layer formed on recess portions of the underlayer and the mask layer, and a nitride-based semiconductor element layer, formed on the first nitride-based semiconductor layer, having an element region.
The nitride-based semiconductor element according to the second aspect is provided with the underlayer comprising the surface having the projection portions and the mask layer formed to be in contact with only the projection portions of the surface of the underlayer as described above, whereby the first nitride-based semiconductor layer having low dislocation density can be readily formed on the recess portions of the underlayer and the mask layer through the mask layer serving for selective growth. When the nitride-based semiconductor element layer having the element region is grown on the first nitride-based semiconductor layer having low dislocation density, a nitride-based semiconductor element having excellent element characteristics can be readily obtained. Only the surface of the underlayer consisting of a nitride-based semiconductor may be etched for forming the projection portions on the surface. Thus, the etching time for forming the projection portions on the surface can be reduced, and a nitride-based semiconductor element having excellent mass productivity can be obtained as a result.
The aforementioned nitride-based semiconductor element according to the second aspect preferably further comprises a buffer layer formed between the substrate and the underlayer. According to this structure, the underlayer consisting of a nitride-based semiconductor having low dislocation density can be readily formed on the buffer layer.
In the aforementioned nitride-based semiconductor element according to the second embodiment, the substrate preferably includes a substrate selected from a group consisting of a sapphire substrate, a spinel substrate, an Si substrate, an SiC substrate, a GaAs substrate, a GaP substrate, an InP substrate, a ZrB2 substrate and a quartz substrate.
In the aforementioned nitride-based semiconductor element according to the second aspect, the underlayer preferably includes a GaN layer, and the mask layer and the projection portions of the surface of the underlayer are preferably formed in the shape of stripes being parallel to the [11-20] direction or the [1-100] direction of the GaN layer.
A method of forming a nitride-based semiconductor according to a third aspect of the present invention comprises steps of forming projection portions on a surface on a substrate, forming a mask layer to be in contact with only the projection portions of the surface of the substrate and growing a first nitride-based semiconductor layer on recess portions of the substrate and the mask layer through the mask layer serving for selective growth.
In the method of forming a nitride-based semiconductor according to the third embodiment, the surface having the projection portions is formed on the substrate while the mask layer is formed to be in contact with only the projection portions of the surface of the substrate, whereby the first nitride-based semiconductor layer having low dislocation density can be readily formed on the recess portions of the substrate and the mask layer when grown through the mask layer serving for selective growth. Further, only the surface of the substrate may be etched for forming the projection portions on the surface. Thus, the etching time for forming the projection portions on the surface can be reduced. According to the third aspect, further, the first nitride-based semiconductor layer can be formed through single growth on the substrate. Consequently, a method of forming a nitride-based semiconductor excellent in mass productivity can be obtained.
The aforementioned method of forming a nitride-based semiconductor according to the third aspect preferably further comprises a step of forming a buffer layer on the recess portions of the substrate in advance of the step of growing the first nitride-based semiconductor layer. According to this structure, the first nitride-based semiconductor layer having lower dislocation density can be formed on the buffer layer.
In the aforementioned method of forming a nitride-based semiconductor according to the third aspect, the steps of forming the projection portions on the surface on the substrate and forming the mask layer preferably include a step of forming the mask layer on the surface of the substrate and thereafter etching the surface of the substrate through the mask layer serving for etching in this step thereby simultaneously forming the projection portions on the surface of the substrate and the mask layer coming into contact with only the projection portions of the surface. According to this method, the mask layer serving for etching simultaneously serves for selective growth, whereby the fabrication process can be simplified.
The aforementioned method of forming a nitride-based semiconductor according to the third aspect preferably further comprises a step of growing a nitride-based semiconductor element layer having an element region on the first nitride-based semiconductor layer. According to this structure, the nitride-based semiconductor element layer having the element region can be grown on the first nitride-based semiconductor layer having low dislocation density, whereby a nitride-based semiconductor element having excellent element characteristics can be readily formed.
In the aforementioned method of forming a nitride-based semiconductor according to the third aspect, the substrate preferably includes a substrate selected from a group consisting of a sapphire substrate, a spinel substrate, an Si substrate, an SiC substrate, a GaN substrate, a GaAs substrate, a GaP substrate, an InP substrate, a ZrB2 substrate and a quartz substrate. In this case, the substrate preferably includes a sapphire substrate, and the mask layer and the projection portions of the surface of the substrate are preferably formed in the shape of stripes being parallel to the [1-100] direction of the sapphire substrate. Alternatively, the substrate preferably includes an Si substrate, and the mask layer and the projection portions of the surface of the substrate are preferably formed in the shape of stripes being parallel to the [1-10] direction of the Si substrate.
A method of forming a nitride-based semiconductor according to a fourth aspect of the present invention comprises steps of forming an underlayer consisting of a nitride-based semiconductor on a substrate, forming projection portions on a surface on the underlayer, forming a mask layer to be in contact with only the projection portions of the surface of the underlayer and growing a first nitride-based semiconductor layer on recess portions of the underlayer and the mask layer through the mask layer serving for selective growth.
In the method of forming a nitride-based semiconductor according to the fourth aspect, the surface having the projection portions is formed on the underlayer consisting of a nitride-based semiconductor layer provided on the substrate while the mask layer is formed to be in contact with only the projection portions of the surface of the underlayer, whereby the first nitride-based semiconductor layer having low dislocation density can be readily formed on the recess portions of the underlayer and the mask layer when grown through the mask layer serving for selective growth. Further, only the surface of the underlayer consisting of a nitride-based semiconductor may be etched for forming the projection portions on the surface. Thus, the etching time for forming the projection portions on the surface can be reduced, and a method of forming a nitride-based semiconductor having excellent mass productivity can be provided as a result.
The aforementioned method of forming a nitride-based semiconductor according to the fourth aspect preferably further comprises a step of forming a buffer layer on the substrate in advance of the step of forming the underlayer consisting of a nitride-based semiconductor. According to this structure, the underlayer consisting of a nitride-based semiconductor having low dislocation density can be readily formed on the buffer layer.
In the aforementioned method of forming a nitride-based semiconductor according to the fourth aspect, the steps of forming the projection portions on the surface on the underlayer and forming the mask layer preferably include a step of forming the mask layer on the surface of the underlayer and thereafter etching the surface of the underlayer through the mask layer serving for etching in this step thereby simultaneously forming the projection portions on the surface of the underlayer and the mask layer coming into contact with only the projection portions of the surface. According to this method, the mask layer serving for etching simultaneously serves for selective growth, whereby the fabrication process can be simplified.
The aforementioned method of forming a nitride-based semiconductor according to the fourth aspect preferably further comprises a step of growing a nitride-based semiconductor element layer having an element region on the first nitride-based semiconductor layer. According to this structure, the nitride-based semiconductor element layer having the element region can be grown on the first nitride-based semiconductor layer having low dislocation density, whereby a nitride-based semiconductor element having excellent element characteristics can be readily formed.
In the aforementioned method of forming a nitride-based semiconductor according to the fourth aspect, the substrate preferably includes a substrate selected from a group consisting of a sapphire substrate, a spinel substrate, an Si substrate, an SiC substrate, a GaAs substrate, a GaP substrate, an InP substrate, a ZrB2 substrate and a quartz substrate.
In the aforementioned method of forming a nitride-based semiconductor according to the fourth aspect, the underlayer preferably includes a GaN layer, and the mask layer and the projection portions of the surface of the underlayer are preferably formed in the shape of stripes being parallel to the [11-20] direction or the [1-100] direction of the GaN layer.
The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
Embodiments of the present invention are now described with reference to the drawings.
A method of forming a nitride-based semiconductor according to a first embodiment of the present invention is described with reference to
First, striped mask layers 2 of SiO2 having a thickness of about 0.5 μm are formed on a sapphire (0001) plane substrate 1 (hereinafter referred to as “sapphire substrate 1”), as shown in
The mask layers 2 are employed as masks for etching the surface of the sapphire substrate 1 by a thickness of about 1 μm through RIE (reactive ion etching) or the like. Thus, the surface of the sapphire substrate 1 is brought into an uneven shape, as shown in
Then, low-temperature buffer layers 3 of GaN having a thickness of about 15 nm are grown by a crystal growth method such as MOVPE (metal organic vapor phase epitaxy) to be in contact substantially with the overall bottom surfaces of the recess portions of the sapphire substrate 1, as shown in
Then, undoped GaN layers 4 are grown on the low-temperature buffer layers 3 consisting of GaN. In this case, the low-temperature buffer layers 3 and the undoped GaN layers 4 are successively grown without taking the sapphire substrate 1 out of the growth apparatus. In an initial stage, the undoped GaN layers 4 are vertically (upwardly) grown on the low-temperature buffer layers 3. If the low-temperature buffer layers 3 are formed on the side surfaces of the recess portions, the undoped GaN layers 4 are grown laterally from the low-temperature buffer layers 3 formed on the side surfaces. When this growth is further continued, undoped GaN layers 4 having facets on side surfaces thereof are formed on the recess portions, as shown in
From the state shown in
In the method of forming a nitride-based semiconductor according to the first embodiment, the undoped GaN layers 4 are grown from the recess portions of the sapphire substrate 1 as hereinabove described, whereby dislocations of the undoped GaN layers 4 are bent in the in-plane direction of the (0001) plane of the undoped GaN layers 4 when the undoped GaN layers 4 are laterally grown from the low-temperature buffer layers 3 formed on the side surfaces of the recess portions or on the mask layers 2. Thus, the dislocation density can be reduced around the surfaces of the undoped GaN layers 4.
In the method of forming a nitride-based semiconductor according to the first embodiment, the surface of the sapphire substrate 1 is brought into an uneven shape as hereinabove described, whereby only the surface of the sapphire substrate 1 may be etched through the mask layers 2 serving for etching. Thus, the etching time for forming the projection portions on the surface on the sapphire substrate 1 can be reduced as compared with the conventional process of forming the projection portions on the surface shown in
In the method of forming a nitride-based semiconductor according to the first embodiment, growth of the low-temperature buffer layers 3 of GaN formed on the recess portions of the sapphire substrate 1 and selective growth of the undoped GaN layer 4 are successively performed without taking the sapphire substrate 1 out of the growth apparatus, as hereinabove described. Thus, the undoped GaN layer 4 having low dislocation density can be formed through a single growth step. A method of forming a nitride-based semiconductor having excellent mass productivity can be obtained also in this point.
In the method of forming a nitride-based semiconductor according to the first embodiment, further, the undoped GaN layer 4 is grown on the low-temperature buffer layers 3 provided on the sapphire substrate 1, whereby the undoped GaN layer 4 can be grown in lower dislocation density as compared with that directly grown on the sapphire substrate 1.
In the structure of the semiconductor laser device according to the first embodiment, an n-type contact layer 5 of n-type GaN having a thickness of about 4 μm is formed on the undoped GaN layer 4 according to the first embodiment shown in
A p-type first cladding layer 10 of p-type GaN having a thickness of about 40 nm (about 0.04 μm) is formed on the MQW emission layer 9. A mesa (trapezoidal) p-type second cladding layer 11 of p-type AlGaN having a height of about 0.45 μm is formed on the p-type first cladding layer 10. Current blocking layers 12 of n-type GaN having a thickness of about 0.2 μm are formed to cover regions on the p-type first cladding layer 10 other than that formed with the p-type second cladding layer 11 and the side surfaces of the mesa p-type second cladding layer 11 while exposing the upper surface of the p-type second cladding layer 11. A p-type contact layer 13 of p-type GaN having a thickness of about 3 μm to about 5 μm is formed on the current blocking layers 12 to be in contact with the exposed upper surface of the p-type second cladding layer 11.
The layers from the p-type contact layer 13 to the n-type contact layer 5 are partially removed. Protective films 14 of an insulator such as SiO2 or SiN are formed to cover parts of the exposed surface of the n-type contact layer 5 and the exposed side surfaces of the anti-cracking layer 6, the n-type second cladding layer 7, the n-type first cladding layer 8, the MQW emission layer 9, the p-type first cladding layer 10, the current blocking layers 12 and the p-type contact layer 13.
A p-side electrode 15 is formed on the upper surface of the p-type contact layer 13 while an n-side electrode 16 is formed on the partially removed and exposed surface of the n-type contact layer 5.
The n-type contact layer 5, the anti-cracking layer 6, the n-type second cladding layer 7, the n-type first cladding layer 8, the MQW emission layer 9, the p-type first cladding layer 10, the p-type second cladding layer 11, the current blocking layers 12 and the n-type contact layer 13 are examples of the “nitride-based semiconductor element layer having an element region” according to the present invention.
In the semiconductor laser device according to the first embodiment, the undoped GaN layer 4 having excellent mass productivity and low dislocation density formed by the method of forming a nitride-based semiconductor according to the first embodiment shown in
Referring to
According to the second embodiment, striped mask layers 22 of SiO2 having a thickness of about 0.5 μm are formed on the n-type Si substrate 21, as shown in
The mask layers 22 are employed as masks for etching the surface of the Si substrate 21 by a thickness of about 1 μm through wet etching or the like. Thus, the surface of the Si substrate 21 is brought into an uneven shape, as shown in
Then, buffer layers 23 of Si-doped AlGaN having a thickness of about 15 nm are grown by a crystal growth method such as MOVPE to be in contact substantially with the overall bottom surfaces of the recess portions of the Si substrate 21, as shown in
Then, Si-doped GaN layers 24 are grown on the buffer layers 23 consisting of Si-doped AlGaN. In this case, the buffer layers 23 and the Si-doped GaN layers 24 are successively grown without taking the Si substrate 21 out of the growth apparatus. In an initial stage, the Si-doped GaN layers 24 are vertically (upwardly) grown on the buffer layers 23. If the buffer layers 23 are formed on the side surfaces of the recess portions, the Si-doped GaN layers 24 are grown laterally from the buffer layers 23 formed on the side surfaces. When this growth is further continued, Si-doped GaN layers 24 having facets on side surfaces thereof are formed on the recess portions, as shown in
From the state shown in
In the method of forming a nitride-based semiconductor according to the second embodiment, the Si-doped GaN layers 24 are grown from the recess portions of the Si substrate 21, whereby dislocations of the Si-doped GaN layers 24 are bent in the in-plane direction of the (0001) plane of the Si-doped GaN layers 24 when the Si-doped GaN layers 24 are laterally grown from the buffer layers 23 formed on the side surfaces of the recess portions or on the mask layers 22. Thus, the dislocation density can be reduced around the surfaces of the Si-doped GaN layers 24.
In the method of forming a nitride-based semiconductor according to the second embodiment, the surface of the Si substrate 21 is brought into an uneven shape similarly to the first embodiment, whereby only the surface of the Si substrate 21 may be etched through the mask layers 22 serving for etching. Thus, the etching time for forming the projection portions on the surface on the Si substrate 21 can be reduced as compared with the conventional process of forming the projection portions on the surface shown in
In the method of forming a nitride-based semiconductor according to the second embodiment, growth of the buffer layers 23 of Si-doped AlGaN formed on the Si substrate 21 and selective growth of the Si-doped GaN layer 24 are successively performed without taking the Si substrate 21 out of the growth apparatus, similarly to the first embodiment. Thus, the Si-doped GaN layer 24 having low dislocation density can be formed through a single growth step. A method of forming a nitride-based semiconductor having excellent mass productivity can be obtained also in this point.
In the method of forming a nitride-based semiconductor according to the second embodiment, further, the Si-doped GaN layer 24 is grown on the buffer layers 23 provided on the Si substrate 21, whereby the Si-doped GaN layer 24 can be grown in lower dislocation density as compared with that directly grown on the Si substrate 21.
In the structure of the semiconductor laser device according to the second embodiment, an anti-cracking layer 25 of n-type AlGaInN having a thickness of about 0.1 μm, an n-type second cladding layer 26 of n-type AlGaN having a thickness of about 0.45 μm, an n-type first cladding layer 27 of n-type GaN having a thickness of about 50 nm (about 0.05 μm) and a multiple quantum well (MQW) emission layer 28 of GaInN are successively formed on the Si-doped GaN layer 24 according to the second embodiment shown in
A p-type first cladding layer 29 of p-type GaN having a thickness of about 40 nm (about 0.04 μm) is formed on the MQW emission layer 28. A mesa (trapezoidal) p-type second cladding layer 30 of p-type AlGaN having a height of about 0.45 μm is formed on the p-type first cladding layer 29. Current blocking layers 31 of n-type GaN having a thickness of about 0.2 μm are formed to cover regions on the p-type first cladding layer 29 other than that formed with the p-type second cladding layer 30 and the side surfaces of the mesa p-type second cladding layer 30 while exposing the upper surface of the p-type second cladding layer 30. A p-type contact layer 32 of p-type GaN having a thickness of about 3 μm to about 5 μm is formed on the current blocking layers 31 to be in contact with the exposed upper surface of the p-type second cladding layer 30.
A p-side electrode 33 is formed on a projection portion of the p-type contact layer 32 reflecting the mesa shape of the p-type second cladding layer 30. According to the second embodiment, the Si substrate 21 has conductivity dissimilarly to the sapphire substrate 1 according to the first embodiment, and hence an n-side electrode 34 is formed on the back surface of the Si substrate 21.
The anti-cracking layer 25, the n-type second cladding layer 26, the n-type first cladding layer 27, the MQW emission layer 28, the p-type first cladding layer 29, the p-type second cladding layer 30, the current blocking layers 31 and the n-type contact layer 32 are examples of the “nitride-based semiconductor element layer having an element region” according to the present invention.
In the semiconductor laser device according to the second embodiment, the Si-doped GaN layer 24 having excellent mass productivity and low dislocation density formed by the method of forming a nitride-based semiconductor according to the second embodiment shown in
While the sapphire substrate 1 and the Si substrate 21 are employed in the aforementioned first and second embodiments respectively, for example, the present invention is not restricted to this but a spinel substrate, an SiC substrate, a GaAs substrate, a GaP substrate, an InP substrate, a ZrB2 substrate or a quartz substrate may alternatively be employed.
Further alternatively, a GaN substrate may be employed in each of the aforementioned first and second embodiments. In this case, the low-temperature buffer layers 3 or the buffer layers 23 may not necessarily be formed.
Referring to
First, low-temperature buffer layers 42 of AlGaN having a thickness of about 15 nm and the underlayer 43 of undoped GaN having a thickness of about 2 μm are formed on the sapphire substrate 41 by a crystal growth method such as MOVPE, as shown in
Striped mask layers 44 of SiO2 having a thickness of about 0.5 μm are formed on the underlayer 43. The stripe patterns of the mask layers 44 are formed in a cycle of about 6 μm so that the width of the mask layers 44 is about 5 μm and the interval between each adjacent pair of mask layers 44 (the width of mask openings) is about 1 μm. The striped mask layers 44 are formed in parallel to the [11-20] direction of the underlayer 43 consisting of GaN.
The mask layers 44 are employed as masks for etching the surface of the underlayer 43 by a thickness of about 1 μm through RIE or the like. Thus, the surface of the underlayer 43 is brought into an uneven shape, as shown in
Then, undoped GaN layers 45 are re-grown from the bottom and side surfaces, serving as seed crystals, of the exposed recess portions of the underlayer 43 consisting of undoped GaN, as shown in
From the state shown in
In the method of forming a nitride-based semiconductor according to the third embodiment, the undoped GaN layers 45 are grown from the bottom and side surfaces, serving as seed crystals, of the recess portions of the underlayer 43 consisting of undoped GaN as hereinabove described, whereby dislocations of the undoped GaN layers 45 are bent in the in-plane direction of the (0001) plane of the undoped GaN layers 45 when the undoped GaN layers 45 are laterally grown from the side surfaces of the recess portions of the underlayer 43 or on the mask layers 44. Thus, the dislocation density can be reduced around the surfaces of the undoped GaN layers 45.
In the method of forming a nitride-based semiconductor according to the third embodiment, the surface of the underlayer 43 is brought into an uneven shape as hereinabove described, whereby only the surface of the underlayer 43 may be etched. Thus, the etching time for forming the projection portions on the surface on the underlayer 43 can be reduced as compared with the conventional process of forming the projection portions on the surface shown in
In the method of forming a nitride-based semiconductor according to the third embodiment, the underlayer 43 consisting of undoped GaN is grown after forming the low-temperature buffer layers 42 on the sapphire substrate 41, whereby the underlayer 43 having low dislocation density can be readily formed.
In the structure of the semiconductor laser device according to the third embodiment, an n-type contact layer 5, an anti-cracking layer 6, an n-type second cladding layer 7, an n-type first cladding layer 8, an MQW emission layer 9, a p-type first cladding layer 10, a p-type second cladding layer 11, current blocking layers 12, a p-type contact layer 13 and protective films 14 are formed on the undoped layer GaN layer 45 shown in
A p-side electrode 15 is formed on the upper surface of the p-type contact layer 13 while an n-side electrode 16 is formed on a partially removed and exposed surface of the n-type contact layer 5.
In the semiconductor laser device according to the third embodiment, the undoped GaN layer 45 having excellent mass productivity and low dislocation density formed by the method of forming a nitride-based semiconductor according to the third embodiment shown in
Referring to
First, buffer layers 52 of Si-doped AlGaN having a thickness of about 15 nm and an underlayer 53 of Si-doped GaN having a thickness of about 2 μm are formed on the n-type SiC substrate 51 by a crystal growth method such as MOVPE, as shown in
Striped mask layers 54 of SiO2 having a thickness of about 0.5 μm are formed on the underlayer 53. The stripe patterns of the mask layers 54 are formed in a cycle of about 6 μm so that the width of the mask layers 54 is about 5 μm and the interval between each adjacent pair of mask layers 54 (the width of mask openings) is about 1 μm. The striped mask layers 54 are formed in parallel to the [11-20] direction of the underlayer 53 consisting of Si-doped GaN.
The mask layers 54 are employed as masks for etching the surface of the underlayer 53 by a thickness of about 1 μm through RIE or the like. Thus, the surface of the underlayer 53 is brought into an uneven shape, as shown in
Then, Si-doped GaN layers 55 are re-grown from the bottom and side surfaces, serving as seed crystals, of the exposed recess portions of the underlayer 53 consisting of Si-doped GaN, as shown in
From the state shown in
In the method of forming a nitride-based semiconductor according to the fourth embodiment, the Si-doped GaN layers 55 are grown from the bottom and side surfaces, serving as seed crystals, of the recess portions of the underlayer 43 consisting of Si-doped GaN as hereinabove described, whereby dislocations of the Si-doped GaN layers 55 are bent in the in-plane direction of the (0001) plane of the Si-doped GaN layers 55 when the Si-doped GaN layers 55 are laterally grown from the side surfaces of the recess portions of the underlayer 53 or on the mask layers 54. Thus, the dislocation density can be reduced around the surfaces of the Si-doped GaN layers 55.
In the method of forming a nitride-based semiconductor according to the fourth embodiment, the surface of the underlayer 53 is brought into an uneven shape as hereinabove described, whereby only the surface of the underlayer 53 may be etched. Thus, the etching time for forming the projection portions on the surface on the underlayer 53 can be reduced as compared with the conventional process of forming the projection portions on the surface shown in
In the method of forming a nitride-based semiconductor according to the fourth embodiment, the underlayer 53 consisting of Si-doped GaN is grown after forming the buffer layers 52 on the SiC substrate 51, whereby the underlayer 53 having low dislocation density can be readily formed.
In the structure of the semiconductor laser device according to the fourth embodiment, an anti-cracking layer 25, an n-type second cladding layer 26, an n-type first cladding layer 27, an MQW emission layer 28, a p-type first cladding layer 29, a p-type second cladding layer 30, current blocking layers 31 and a p-type contact layer 32 are formed on the Si-doped layer GaN layer 55 shown in
A p-side electrode 33 is formed on a projection portion of the p-type contact layer 32 reflecting the mesa shape of the p-type second cladding layer 30. The SiC substrate 51 has conductivity, and hence an n-side electrode 34 is formed on the back surface of the SiC substrate 51.
In the semiconductor laser device according to the fourth embodiment, the Si-doped GaN layer 55 having excellent mass productivity and low dislocation density formed by the method of forming a nitride-based semiconductor according to the fourth embodiment shown in
While the sapphire substrate 41 and the SiC substrate 51 are employed in the aforementioned third and fourth embodiments respectively, for example, the present invention is not restricted to this but a spinel substrate, a GaN substrate, a GaAs substrate, a GaP substrate, an InP substrate, a ZrB2 substrate or a quartz substrate may alternatively be employed.
Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.
While the recess portions of the surfaces of the sapphire substrate 1, the Si substrate 21 and the underlayers 43 and 53 are formed in the height of about 1 μm in the aforementioned first to fourth embodiments, the present invention is not restricted to this but the height of the recess portions is preferably set in the range of several nm to several μm not reaching the bottom surfaces of the sapphire substrate 1, the Si substrate 21 and the underlayers 43 and 53.
While the striped mask layers 2, 22, 44 and 54 are formed in parallel with the [1-100] direction of the sapphire substrate 1, the [1-10] direction of the Si substrate 21 and the [11-20] directions of the GaN underlayers 43 and 53 in the aforementioned first to fourth embodiments respectively, the present invention is not restricted to this but the striped mask layers may alternatively be formed in a direction different from the aforementioned ones. For example, the mask layers 44 and 45 according to the third and fourth embodiments may be formed in parallel with the [1-100] directions of the GaN underlayers 43 and 53.
While the projection portions of the surfaces of the sapphire substrate 1, the Si substrate 21 and the underlayers 43 and 53 are formed in parallel with the [1-100] direction of the sapphire substrate 1, the [1-10] direction of the Si substrate 21 and the [11-20] directions of the GaN underlayers 43 and 53 in the first to fourth embodiments respectively, the present invention is not restricted to this but the projection portions of the surface may be formed in a direction different from the above. For example, the projection portions of the surfaces of the underlayers 43 and 53 according to the third and fourth embodiments may alternatively be formed in parallel with the [1-100] directions of the GaN underlayers 43 and 53.
While the mask layers 2, 22, 44 and 54 and the openings thereof are formed in a striped shape in the aforementioned first to fourth embodiments, the present invention is not restricted to this but the mask layers may alternatively be formed in a circular, hexagonal or triangular shape, and the openings thereof may also be formed in a circular, hexagonal or triangular shape. When the mask layers and the openings thereof are formed in a hexagonal or triangular shape, the sides of the hexagons or triangles may match with any crystal orientation.
While the recess and projection portions of the surfaces of the sapphire substrate 1, the Si substrate 21 and the underlayers 43 and 53 are formed in a striped shape in the aforementioned first to fourth embodiments, the present invention is not restricted to this but the recess portions or the projection portions of the surfaces of the sapphire substrate 1, the Si substrate 21 and the underlayers 43 and 53 may alternatively be formed in a circular, hexagonal or triangular shape. When the recess or projection potions are formed in a hexagonal or triangular shape, the sides of the hexagons or triangles may match with any crystal orientation.
While the nitride-based semiconductors are employed for preparing semiconductor laser devices in the aforementioned first to fourth embodiments, the present invention is not restricted to this but also applicable to another device such as a light emitting diode device or a transistor employing a nitride-based semiconductor.
In each of the aforementioned first to fourth embodiments, the nitride-based semiconductor may have a wurtzite crystal structure or a zinc blende crystal structure.
While crystal growth of each nitride-based semiconductor layer is performed by MOVPE in the aforementioned first to fourth embodiments, the present invention is not restricted to this but crystal growth may alternatively be performed by HVPE or gas source MBE employing TMA1, TMGa, TMIn, NH3, SiH or Cp2Mg as source gas.
In each of the first to fourth embodiments, the bottom surfaces of the recess portions of the surface of the sapphire substrate 1, the Si substrate 21 or the underlayer 43 or 53 are preferably formed in a width within the range of several 100 nm to several 10 μm.
While the n-type first cladding layers 8 or 27 and the p-type first cladding layers 10 or 29 consist of GaN in the aforementioned first to fourth embodiments, the present invention is not restricted to this but the first cladding layers may consist of other materials having a wider bandgap than the MQW emission layer. For example, AlGaN such as Al0.01Ga0.99N, InGaN such as In0.01Ga0.99N, or AlGaInN such as Al0.01Ga0.98In0.01N may be employed as the materials constituting the first cladding layers.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2001-51348 | Feb 2001 | JP | national |
This application is a divisional of U.S. application Ser. No. 10/081,180 filed on Feb. 25, 2002 which is U.S. Pat. No. 6,994,751.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5777350 | Nakamura et al. | Jul 1998 | A |
| 6015979 | Sugiura et al. | Jan 2000 | A |
| 6153010 | Kiyoku et al. | Nov 2000 | A |
| 6201823 | Kimura et al. | Mar 2001 | B1 |
| 6316785 | Nunoue et al. | Nov 2001 | B1 |
| 6348096 | Sunakawa et al. | Feb 2002 | B1 |
| 6673149 | Solomon et al. | Jan 2004 | B1 |
| 6864160 | Linthicum et al. | Mar 2005 | B2 |
| 6994751 | Hata et al. | Feb 2006 | B2 |
| 20010026950 | Sunakawa et al. | Oct 2001 | A1 |
| 20010040246 | Ishii | Nov 2001 | A1 |
| 20010041427 | Gehrke et al. | Nov 2001 | A1 |
| Number | Date | Country |
|---|---|---|
| 10-312971 | Nov 1998 | JP |
| 11-191657 | Jul 1999 | JP |
| 2000-124500 | Apr 2000 | JP |
| 2000-277437 | Oct 2000 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20050263778 A1 | Dec 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10081180 | Feb 2002 | US |
| Child | 11195637 | US |