Claims
- 1. A process for producing a multilayer printed circuit board, which comprises the steps of:
- (a) printing or coating a filling material for hollow portions and having fluidity at B-stage on hollow portions of a circuit substrate,
- (b) drying the filling material, followed by curing to B-stage,
- (c) piling a copper foil having a layer of insulating adhesive which is capable of forming via holes by chemical etching on one side so as to contact the insulating adhesive with the filling material coated surface, followed by lamination to form an integrated structure,
- (d) removing portions necessary for connection with the copper foil by etching, and removing the insulating adhesive exposed to holes by chemical etching,
- (e) connecting the copper foil with circuits exposed to the holes and forming a surface circuit by processing an outer layer of the copper foil, and
- (f) repeating the steps (a) to (e) depending on the number of circuit layers necessitated,
- said insulating adhesive comprising
- (a) an epoxy resin having a number average molecular weight of 1200 or less in an amount of 30 to 100 parts by weight,
- (b) a carboxylic acid-containing acrylic rubber or a carboxylic acid-containing acrylonitrile-butadiene rubber in an amount of 30 to 70 parts by weight,
- (c) a curing agent for the epoxy resin, and
- (d) a curing accelerator.
- 2. A process according to claim 1, wherein at least one of the filling material and the insulating adhesive contains an inorganic filler having a high thermal conductivity.
- 3. A process for producing a multilayer printed circuit board, which comprises the steps of:
- (a) forming via holes in a copper foil having a layer of insulating adhesive which is capable of forming holes by chemical etching,
- (b) piling the copper foil having a layer of insulating adhesive with via holes on one side of a inner circuit board so as to contact the insulating adhesive with circuit conductors on the inner layer circuit board, followed by lamination to form an integrated structure with heating under pressure,
- (c) removing the insulating adhesive oozed into the holes by chemical etching,
- (d) curing with heating the insulating adhesive to form via holes or a cavity,
- (e) forming conductive paths in via holes or a cavity using an electroconductive paint or metallic deposition by plating, and
- (f) repeating the steps (a) to (e) depending on the number of circuit layers necessitated,
- said insulating adhesive comprising
- (a) an epoxy resin having a number average molecular weight of 1200 or less in an amount of 30 to 100 parts by weight,
- (b) a carboxylic acid-containing acrylic rubber or a carboxylic acid-containing acrylonitrile-butadiene rubber in an amount or 30 to 70 parts by weight,
- (c) a curing agent for the epoxy resin, and
- (d) a curing accelerator.
- 4. A process for producing a multilayer printed circuit board, which comprises the steps of;
- (a) forming a via holes in a sheet of insulating adhesive which is capable of forming holes by chemical etching,
- (b) piling the sheet with holes on one side of an inner circuit board so as to contact the insulating adhesive with circuit conductors on the inner layer circuit board, and piling a copper foil on the insulating adhesive with holes, followed by lamination to form an integrated structure with heating under pressure,
- (c) removing copper from portions in which via holes made in the insulation adhesive, and removing the insulating adhesive oozed into the holes by chemical etching,
- (d) curing with heating the insulating adhesive to form via holes or a cavity,
- (e) forming conductive paths in via holes or a cavity using an electroconductive paint or metallic deposition by plating, and
- (f) repeating the steps (a) to (e) depending on the number of circuit layers necessitated,
- said insulating adhesive comprising
- (a) an epoxy resin having a number average molecular weight of 1200 or less in an amount of 30 to 100 parts by weight,
- (b) a carboxylic acid-containing acrylic rubber or a carboxylic acid-containing acrylonitrile-butadiene rubber in an amount of 30 to 70 parts by weight,
- (c) a curing agent for the epoxy resin, and
- (d) a curing accelerator.
Priority Claims (1)
Number |
Date |
Country |
Kind |
7-111719 |
May 1995 |
JPX |
|
CROSS-REFERENCE TO RELATED APPLICATION
This application is a Divisional of application Ser. No. 08/514,739, filed on Aug. 14, 1995 (now allowed).
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3471631 |
Quintana |
Oct 1969 |
|
5591353 |
Davignon et al. |
Jan 1997 |
|
Divisions (1)
|
Number |
Date |
Country |
Parent |
514739 |
Aug 1995 |
|