The disclosure of Japanese Patent Application No. 2011-265852 filed on Dec. 5, 2011 including the specification, drawings and abstract is incorporated herein by reference in its entirety.
The present invention relates to a semiconductor device and a manufacturing method thereof. More particularly, it relates to a technology effectively applicable to a semiconductor device having MISFETs, and manufacturing thereof.
Over a semiconductor substrate, a gate insulation film is formed. Over the gate insulation film, a gate electrode is formed. Thus, by ion implantation or the like, source/drain regions are formed. As a result, a MISFET (Metal Insulator Semiconductor Field Effect Transistor) can be formed. For such a MISFET, there is known the following technology: to the interface between the gate insulation film and the gate electrode, namely, to the top of the gate insulation film, a trace amount of metal such as hafnium (Hf) is added, thereby to reduce the impurity concentration of the channel region; as a result, the threshold voltage (Vth) is adjusted.
Japanese Unexamined Patent Publication No. 2006-093670 (Patent Document 1) describes the following technology: a metal such as hafnium (Hf) is caused to be present at the interface between the gate electrode and the gate insulation film; as a result, the threshold voltage (Vth) is adjusted.
Japanese Unexamined Patent Publication No. 2006-332179 (Patent Document 2) describes the following technology: a metal such as hafnium (Hf) is introduced into the vicinity of the interface between the gate electrode and the gate insulation film; as a result, the impurity concentration of the channel necessary for achieving the same threshold voltage (Vth) is adjusted so as to be reduced.
WO08/035598 (Patent Document 3) describes the following technology: the gate insulation film is set to be a HfSiON film, and the work function of the gate electrode is adjusted; as a result, the threshold voltage (Vth) is adjusted.
Whereas, there is known the following technology: the type of the metal to be added is varied between an n channel type MISFET and a p channel type MISFET forming a complementary type MISFET; as a result, the transistor characteristics such as threshold voltage (Vth) are adjusted.
WO08/015940 (Patent Document 4) describes the following technology: the type of impurities contained in the Ni silicide region between the gate insulation film and the gate electrode is varied between an n channel type MISFET and a p channel type MISFET; as a result, the threshold voltage (Vth) is adjusted.
Japanese Unexamined Patent Publication No. 2010-103386 (Patent Document 5) describes the following technology: a diffusion preventive film containing Al or the like is formed in the gate insulation film in only the p channel type MISFET; as a result, the flat band voltage is adjusted.
Japanese Unexamined Patent Publication No. 2007-288096 (Patent Document 6) describes the following technology: as a first gate insulation film of an n channel type MISFET, and a second gate insulation film of a p channel type MISFET, a high-k film containing hafnium (Hf) is used; and in order to make even the gate leakage currents of both the MISFETs, the film thickness of the first gate insulation film is set larger than the thickness of the second gate insulation film.
Japanese Unexamined Patent Publication No. 2008-288465 (Patent Document 7) describes the following technology: as the gate insulation film of an n channel type MISFET, a high-k film containing hafnium (Hf) is used, and as the gate insulation film of a p channel type MISFET, a silicon oxide film is used.
Japanese Unexamined Patent Publication No. 2011-009321 (Patent Document 8) describes the following technology: over a region in which a p channel type MISFET is formed, for example, a HfO film with a thickness of 1.0 nm is formed, and over a region in which an n channel type MISFET is formed, for example, a HfO film with a thickness of 1.5 nm is formed.
On the other hand, when a metal such as hafnium (Hf) is added to the gate insulation film, a metal is crystallized by heat load, which may result in the reduction of the reliability of the gate insulation film. However, by allowing the gate insulation film to include a silicon oxynitride film (SiON film) functioning as a barrier layer, it is possible to improve the reliability of the gate insulation film even when a metal is added thereto. Namely, it is an effective method for improving the reliability of the gate insulation film to use a silicon oxynitride film (SiON film) functioning as a barrier layer in the gate insulation film containing a metal such as hafnium (Hf).
Japanese Unexamined Patent Publication No. 2003-008011 (Patent Document 9) describes the following technology: there is used a gate insulation film having a high-k film formed of a hafnium oxide film (HfO2 film) containing silicon (Si), and a lower barrier film formed of a silicon oxynitride film (SiON film) containing hafnium (Hf) formed on the bottom side of the high-k film.
Japanese Unexamined Patent Publication No. 2010-161299 (Patent Document 10) describes the following technology: the surface density of hafnium (Hf) in the n channel type MISFET is set smaller than the surface density of hafnium (Hf) in the p channel type MISFET, and the nitrogen concentration of a silicon oxynitride film (SiON film) in the n channel type MISFET is set smaller than the nitrogen concentration of a silicon oxynitride film (SiON film) in the p channel type MISFET.
[Patent Document 1]
A study by the present inventors revealed the following.
As described above, it is an effective method for improving the reliability of the gate insulation film to use a silicon oxynitride (SiON) film functioning as a barrier film in the gate insulation film containing a metal such as hafnium (Hf). However, in the p channel type MISFET, when a silicon oxynitride (SiON) film is used as a barrier layer, nitrogen (N) is mixed into the gate insulation film, resulting in an increase in positive fixed charges in the gate insulation film. As a result, the threshold voltage (Vth) increases. For this reason, it is difficult to perform adjustment so as to reduce the threshold voltage (Vth).
As a method for manufacturing a p channel type MISFET having a small threshold voltage (Vth), there can also be considered reduction of the impurity concentration in the channel region. However, in a MISFET with a short channel length, the reduction of the impurity concentration in the channel region results in the deterioration of the transistor characteristics, or the like. As a result, the performances of the semiconductor device are reduced.
It is an object of the present invention to provide a technology capable of improving the performances of a semiconductor device.
The foregoing and other objects and novel features of the present invention will be apparent from the description of this specification and the accompanying drawings.
Summaries of the representative ones of the inventions disclosed in the present application will be described in brief as follows.
A semiconductor device in accordance with a representative embodiment includes two types of MISFETs in each of which hafnium has been added to the gate electrode side of a gate insulation film formed of silicon oxynitride. Then, the hafnium concentration in the gate insulation film of one MISFET is set smaller than the hafnium concentration in the gate insulation film of the other MISFET. In addition, the nitrogen concentration in the gate insulation film of one MISFET is set smaller than the nitrogen concentration in the gate insulation film of the other MISFET. As a result, the threshold voltage of one MISFET is adjusted so as to be smaller than the threshold voltage of the other MISFET.
Further, with a method for manufacturing a semiconductor device in accordance with another representative embodiment, with a part of an insulation film formed over a semiconductor substrate, and formed of silicon oxide being covered with a mask film, a first nitriding treatment and a hafnium addition step are performed, and the mask film is removed. Then, a second nitriding treatment and a hafnium addition step are performed. Then, the threshold voltage of a MISFET formed in a region which was covered with the mask film is adjusted so as to be smaller than the threshold voltage of a MISFET formed in a region which was not covered with the mask film.
The effects obtainable by representative ones of the inventions disclosed in the present application will be described in brief as follows.
In accordance with representative embodiments, it is possible to improve the performances of a semiconductor device.
In the description of the following embodiment, the embodiment may be described in a plurality of divided sections or embodiments for convenience, if required. However, unless otherwise specified, these are not independent of each other, but are in a relation such that one is a modification example of a part or the whole of the other, or details, complementary explanation, or the like of the other. Further, in the following embodiments, when a reference is made to the number of elements, and the like (including number, numerical value, quantity, range, or the like), the number of elements is not limited to the specific number, but maybe greater than or less than the specific number, unless otherwise specified, or except the case where the number is apparently limited to the specific number in principle. Further in the following embodiments, it is naturally understood that the constitutional elements (including element steps, or the like) are not always essential, unless otherwise specified, or except the case where they are apparently considered essential in principle, or except for other cases. Similarly, in the following embodiments, when a reference is made to the shapes, positional relationships, or the like of the constitutional elements, or the like, it is understood that they include ones substantially analogous or similar to the shapes or the like, unless otherwise specified, or unless otherwise considered apparently in principle, or except for other cases. This also applies to the foregoing numerical values and ranges.
Below, embodiments of the present invention will be described in details by reference to the accompanying drawings. Incidentally, in all the drawings for describing the following embodiments, members having the same function are given the same reference signs and numerals, and a repeated description thereon is omitted. Further, in the following embodiment, the description of the same or similar parts will not be repeated in principle unless particularly necessary.
Further, in the accompanying drawings for use in the embodiments, hatching may be omitted even in cross section for ease of understanding of the drawing. Whereas, hatching may be given even in plan view for ease of understanding of the drawing.
<Semiconductor Device>
A semiconductor device which is one embodiment of the present invention will be described by reference to the accompanying drawings. The semiconductor device of the present embodiment is a semiconductor device having a MISFET as a semiconductor element.
As shown in
Incidentally, in the present specification, when the magnitudes of the threshold voltages (Vth) are compared, it is assumed that the magnitudes of the absolute values of the threshold voltages (Vth) are compared. Whereas, in
In the n type MISFET formation region AN1, a p type well region PW is formed in the semiconductor substrate 1. In each of the p type MISFET formation regions AP1 and AP2, an n type well region NW is formed in the semiconductor substrate 1.
First, a description will be given to a specific configuration of the n channel type MISFET QN1 formed in the n type MISFET formation region AN1.
The n channel type MISFET QN1 has a gate electrode GE formed over the semiconductor substrate 1. The gate electrode GE is formed over the p type well region PW formed in the semiconductor substrate 1 in the n type MISFET formation region AN1. Whereas, the n channel type MISFET QN1 has a gate insulation film GI1 formed between the gate electrode GE and the semiconductor substrate 1. Namely, the n channel type MISFET QN1 has the gate insulation film GI1 formed over the semiconductor substrate 1 and the gate electrode GE formed over the gate insulation film GI1.
As the gate electrode GE, there is used a conductor film formed of, for example, polycrystal silicon (doped polysilicon) including impurities introduced therein, and made low in resistivity. Alternatively, as the gate electrode GE, there is used a conductor film formed of one of, for example, titanium nitride (TiN), tantalum nitride (TaN), tungsten nitride (WN), titanium carbide (TiC), tantalum carbide (TaC), tungsten carbide (WC), or tantalum carbide nitride (TaCN). Still alternatively, there may be adopted a MIPS (Metal Inserted Poly-silicon Stack) structure which is a lamination structure of a conductor film formed of one of those described above except for polycrystal silicon, and a conductor film formed of polycrystal silicon.
The gate insulation film GI1 includes a metal, silicon, oxygen, and nitrogen.
Examples of the metal to be contained in the gate insulation film GI1 may include hafnium (Hf), aluminum (Al), and titanium (Ti). By adjusting the content of the metal in the gate insulation film GI1, it is possible to adjust the threshold voltage (Vth) of the MISFET QN1 without adjusting the impurity concentration of the channel region. Further, when the metal contained in the gate insulation film GI1 is, for example, titanium (Ti), as the gate insulation film GI1, the one containing, for example, titanium nitride (TiN) can also be used. Whereas, hafnium (Hf) is preferable among the metals described above in that it produces a still larger effect of enabling adjustment of the threshold voltage (Vth) without adjusting the impurity concentration of the channel region by the adjustment of the content of the metal in the gate insulation film GI1.
The silicon, oxygen, and nitrogen included in the gate insulation film GI1 are present as, for example, silicon oxynitride (SiON) in the gate insulation film GI1. Out of these, nitrogen can suppress the deterioration of the reliability of the gate insulation film GI1 due to crystallization of the contained metal when the gate insulation film GI1 contains the metal described above.
Incidentally, a detailed structure of the gate insulation film GI1 will be described later.
Over the sidewall of the gate electrode GE, a sidewall spacer SW is formed as a sidewall insulation film. Then, in portions which are in the n type MISFET formation region AN1, and are on the opposite sides across the gate electrode GE including the sidewall spacer SW formed thereover, there are formed source/drain regions SD. In the n type MISFET formation region AN1, the source/drain regions SD are n type semiconductor regions including n type impurities such as phosphorus (P) or arsenic (As) diffused therein.
Whereas, in the n type MISFET formation region AN1, in the semiconductor substrate 1, there are formed extension regions EX, and the source/drain regions SD with a higher impurity concentration than that thereof; as a result, there are formed source/drain regions of a LDD (Lightly doped Drain) structure.
Incidentally, over the source/drain regions SD and over the gate electrode GE, using a Salicide: Self Aligned Silicide technology, there can be formed a metal silicide layer such as a cobalt silicide layer or a nickel silicide layer.
Then, a description will be given to the specific configuration of the p channel type MISFET QP1 with a large threshold voltage (Vth) formed in the p type MISFET formation region AP1.
The p channel type MISFET QP1 has a gate electrode GE formed over the semiconductor substrate 1. The gate electrode GE is formed over the n type well region NW formed in the semiconductor substrate 1 in the p type MISFET formation region AP1. Whereas, the p channel type MISFET QP1 has a gate insulation film GI1 formed between the gate electrode GE and the semiconductor substrate 1. Namely, the p channel type MISFET QP1 has the gate insulation film GI1 formed over the semiconductor substrate 1, and the gate electrode GE formed over the gate insulation film GI1.
As the gate electrode GE, there can be used the same material as that for the gate electrode GE of the n channel type MISFET QN1.
The gate insulation film GI1 includes a metal, silicon, oxygen, and nitrogen as with the gate insulation film GI1 of the n channel type MISFET QN1.
As the metals to be contained in the gate insulation film GI1, as with the metals to be contained in the gate insulation film GI1 of the MISFET QN1, mention may be made of, for example, hafnium (Hf), aluminum (Al), and titanium (Ti). By adjusting the content of the metal in the gate insulation film GI1, it is possible to adjust the threshold voltage (Vth) of the MISFET QP1 without adjusting the impurity concentration of the channel region. Further, when the metal contained in the gate insulation film GI1 is, for example, titanium (Ti), as the gate insulation film GI1, the one containing, for example, titanium nitride (TiN) can also be used. Whereas, hafnium (Hf) is preferable among the metals described above in that it produces a still larger effect of enabling adjustment of the threshold voltage (Vth) without adjusting the impurity concentration of the channel region by the adjustment of the content of the metal in the gate insulation film GI1.
The silicon, oxygen, and nitrogen included in the gate insulation film GI1 are present as, for example, silicon oxynitride (SIGN) in the gate insulation film GI1 as with the silicon, oxygen, and nitrogen included in the gate insulation film GI1 of the MISFET QN1. Out of these, nitrogen can suppress the deterioration of the reliability of the gate insulation film GI1 due to crystallization of the contained metals when the gate insulation film GI1 includes the metals described above.
Incidentally, the detailed structure of the gate insulation film GI1 will be described later.
Over the sidewall of the gate electrode GE, a sidewall spacer SW is formed as a sidewall insulation film. Then, in portions which are in the p type MISFET formation region AP1, and are on the opposite sides across the gate electrode GE including the sidewall spacer SW formed thereover, there are formed source/drain regions SD. In the p type MISFET formation region AP1, the source/drain regions SD are p type semi, conductor regions including p type impurities such as boron (B) diffused therein.
Whereas, also in the p type MISFET formation region AP1, in the semiconductor substrate 1, the extension regions EX are formed, and the source/drain regions SD of a LDD structure are formed. Further, also in the p type MISFET formation region AP1, over the source/drain regions SD and over the gate electrode GE, using a salicide technology, there can be formed a metal silicide layer.
Then, a description will be given to the specific configuration of a p channel type MISFET QP2 with a small threshold voltage (Vth) formed in the p type MISFET formation region AP2.
The p channel type MISFET QP2 has a gate electrode GE formed over the semiconductor substrate 1. The gate electrode GE is formed over the n type well region NW formed in the semiconductor substrate 1 in the p type MISFET formation region AP2. Whereas, the p channel type MISFET QP2 has a gate insulation film GI2 including silicon, oxygen, nitrogen, and a metal formed between the gate electrode GE and the semiconductor substrate 1. Namely, the p channel type MISFET QP2 has a gate insulation film GI2 formed over the semiconductor substrate 1, and the gate electrode GE formed over the gate insulation film GI2.
As the gate electrode GE, there can be used the same material as that for the gate electrode GE of the p channel type MISFET QP1.
The gate insulation film GI2 includes a metal, silicon, oxygen, and nitrogen as with the gate insulation film GI1 of the p channel type MISFET QP1.
As the metals contained in the gate insulation film GI2, as with the metals contained in the gate insulation film GI1 of the MISFET QP1, mention may be made of, for example, hafnium (Hf), aluminum (Al), and titanium (Ti). By adjusting the content of the metal in the gate insulation film GI2, it is possible to adjust the threshold voltage (Vth) of the MISFET QP2 without adjusting the impurity concentration of the channel region. Further, when the metal contained in the gate insulation film GI2 is, for example, titanium (Ti), as the gate insulation film GI2, the one including, for example, titanium nitride (TiN) can also be used. Whereas, hafnium (Hf) is preferable among the metals described above in that it produces a still larger effect of enabling adjustment of the threshold voltage (Vth) without adjusting the impurity concentration of the channel region by the adjustment of the content of the metal in the gate insulation film GI2.
The silicon, oxygen, and nitrogen included in the gate insulation film GI2 are present as, for example, silicon oxynitride (SiON) in the gate insulation film GI2 as with the silicon, oxygen, and nitrogen included in the gate insulation film GI1 of the MISFET QP1. Out of these, nitrogen can suppress the deterioration of the reliability of the gate insulation film GI2 due to crystallization of the contained metals when the gate insulation film GI2 includes the metals described above.
Incidentally, the detailed structure of the gate insulation film GI2 will be described later.
However, the concentration of the metal in the gate insulation film GI2 is smaller than the concentration of the metal in the gate insulation film GI1. The concentration of nitrogen in the gate insulation film GI2 is smaller than the concentration of nitrogen in the gate insulation film GI1. As a result, the threshold voltage (Vth) of the MISFET QP2 can be adjusted so as to be smaller than both of the threshold voltage (Vth) of the MISFET QP1 and the threshold voltage (Vth) of the MISFET QN1 without adjusting the impurity concentration of the channel region. Further, it is possible to suppress the deterioration of the reliability of the gate insulation film GI2 due to crystallization of the metals contained in the gate insulation film GI2. Thus, in the MISFET QP2, it is possible to suppress the increase in threshold voltage (Vth) due to inclusion of nitrogen in the gate insulation film GI2. Then, the threshold voltage (Vth) can be adjusted so as to be reduced without reducing the impurity concentration. For this reason, even when the channel length is short, it is possible to suppress the deterioration of the transistor characteristics in a MISFET with a small threshold voltage (Vth).
As described previously, as the metal to be contained in the gate insulation films GI1 and GI2, preferably, hafnium (Hf) is used. When hafnium (Hf) is used as the metal to be contained in the gate insulation films GI1 and GI2, the concentration of hafnium (Hf) in the gate insulation film GI2 is smaller than the concentration of hafnium (Hf) in the gate insulation film GI1; and the concentration of nitrogen in the gate insulation film GI2 is smaller than the concentration of nitrogen in the gate insulation film GI1. As a result, the threshold voltage (Vth) of the MISFET QP2 can be adjusted so as to be smaller than both of the threshold voltage (Vth) of the MISFET QP1 and the threshold voltage (Vth) of the MISFET QN1 without adjusting the impurity concentration of the channel region.
Incidentally, the concentration of a metal in the present invention is assumed to mean, for example, the number of atoms of the metal per unit area (atoms/cm2). The concentration of nitrogen in the present invention is assumed to mean, for example, the ratio of number of atoms (atom %) of nitrogen relative to the total sum of respective numbers of atoms of silicon, oxygen, and nitrogen.
Further, the concentration of the metal in the gate insulation film GI1 of the MISFET QN1 is not required to be equal to the concentration of the metal in the gate insulation film GI1 of the MISFET QP1. The concentration of nitrogen in the gate insulation film GI1 of the MISFET QN1 is not required to be equal to the concentration of nitrogen in the gate insulation film GI1 of MISFET QP1.
Over the sidewall of the gate electrode GE, a sidewall spacer SW is formed as a sidewall insulation film. Then, in portions which are in the p type MISFET formation region AP2, and are on the opposite sides across the gate electrode GE including the sidewall spacer SW formed thereover, there are formed source/drain regions SD. In the p type MISFET formation region AP2, the source/drain regions SD are p type semiconductor regions including p type impurities such as boron (B) diffused therein.
Whereas, also in the p type MISFET formation region AP2, in the semiconductor substrate 1, the extension regions EX are formed, and the source/drain regions SD of a LDD structure are formed. Further, also in the p type MISFET formation region AP2, over the source/drain regions SD and over the gate electrode GE, using a salicide technology, there can be formed a metal silicide layer.
Then, a description will be given to the detailed structure of the gate insulation films GI1 and GI2. Incidentally, below, a description will be given to an example in which the gate insulation films GI1 and GI2 contain hafnium as a metal. However, the same also applies to the case where the gate insulation films GI1 and GI2 contain other metal than hafnium among the metals described above.
As shown in
Whereas, the gate insulation film GI2 preferably has a lower layer film LL2 containing silicon, oxygen, and nitrogen formed over the semiconductor substrate 1, and an upper layer film UL2 containing hafnium formed over the lower layer film LL2. As a result, the lower layer film LL2 can be used as a barrier layer for suppressing the deterioration of the reliability of the gate insulation film GI2 due to crystallization of hafnium contained in the upper layer film UL1.
As the lower layer films LL1 and LL2, there is used, for example, a film formed of silicon oxynitride (SiON). As the upper layer films UL1 and UL2, there is used a film formed of one or more of hafnium oxide (HfO), hafnium oxynitride (HfON), and HfSiON.
Further, preferably, the thickness T2 of the upper layer film UL2 is set smaller than the thickness T1 of the upper layer film UL1. As a result, the concentration of hafnium in the gate insulation film GI2 can be made smaller than the concentration of hafnium in the gate insulation film GI1 with ease.
Specifically, the concentration of hafnium in the gate insulation film GI1 is preferably 5×1013 to 2×1014 atoms/cm2. When the concentration of hafnium in the gate insulation film GI1 is less than 5×1013 atoms/cm2, the threshold voltages (Vth) of the MISFETs QP1 and QN1 may be unadjustable so as to be sufficiently large. Whereas, when the concentration of hafnium in the gate insulation film GI1 exceeds 2×1014 atoms/cm2, hafnium becomes more likely to be crystallized. This may reduce the reliability of the gate insulation films GI1 of the MISFETs QP1 and QN1.
Further, the concentration of nitrogen in the gate insulation film GI1 is preferably 5 to 20 atom %. When the concentration of nitrogen in the gate insulation film GI1 is less than 5 atom %, hafnium becomes more likely to be crystallized. This may reduce the reliability of the gate insulation films GI1 of the MISFETs QP1 and QN1. Whereas, when the concentration of nitrogen in the gate insulation film GI1 exceeds 20 atom %, the positive fixed charges in the gate insulation film GI1 increase, which may result in the following: the threshold voltage (Vth) of the MISFET QP1 becomes too large; on the other hand, the threshold voltage (Vth) of the MISFET QN1 cannot be adjusted so as to be sufficiently large.
Whereas, preferably, the concentration of hafnium in the gate insulation film GI2 is 0 to 1×1014 atoms/cm2, and the concentration of hafnium in the gate insulation film GI2 is smaller than the concentration of hafnium in the gate insulation film GI1. When the concentration of hafnium in the gate insulation film GI2 exceeds 1×1014 atoms/cm2, the threshold voltage (Vth) of the MISFET QP2 may be unadjustable so as to be sufficiently small.
Whereas, preferably, the concentration of nitrogen in the gate insulation film GI2 is 2 to 7 atom %, and, the concentration of nitrogen in the gate insulation film GI2 is smaller than the concentration of nitrogen in the gate insulation film GI1. When the concentration of nitrogen in the gate insulation film GI2 is less than 2 atom %, hafnium becomes more likely to be crystallized. This may reduce the reliability of the gate insulation film GI2. Whereas, when the concentration of nitrogen in the gate insulation film GI2 exceeds 7 atom %, the positive fixed charges in the gate insulation film GI2 increase. As a result, the threshold voltage (Vth) of the MISFET QP2 may be unadjustable so as to be sufficiently small.
Incidentally,
In
In the element isolation region 2, in the main surface of the semiconductor substrate 1, there is formed an element isolation trench 2a. In the formed element isolation trench 2a, an insulation film 2b is embedded. The insulation film 2b divides the n channel type MISFET QN1 formed in the n type MISFET formation region AN1, the p channel type MISFET QP1 formed in the p type MISFET formation region AP1, and the p channel type MISFET QP2 formed in the p type MISFET formation region AP2 from one another. The insulation film 2b is preferably formed of a silicon oxide film. The insulation film 2b is formed by, for example, a STI (Shallow Trench Isolation) method as described later.
Over the entire main surface (front surface) of the semiconductor substrate 1, an interlayer insulation film 5 is formed in such a manner as to cover the gate electrodes GE, the sidewall spacers SW, and the source/drain regions SD of the MISFETs QN1, QP1, and QP2. The interlayer insulation film 5 is formed of, for example, a single film of silicon oxide film, or a lamination film of a silicon nitride film and a silicon oxide film thicker than that (with the silicon nitride film on the lower layer side). The top surface of the interlayer insulation film 5 is planarized so that the MISFET formation regions AN1, AP1, and AP2 roughly agree in height with one another.
In the interlayer insulation film 5, there are formed contact holes CNT. In each contact hole CNT, there is formed a conductive plug PG. The contact holes CNT, and the plugs PG filling them, respectively, are formed over the source/drain regions SD and over the gate electrode GE of the MISFET formation regions AN1, AP1, and AP2, and the like. The bottoms of the plugs PG are electrically coupled with the source/drain regions SD and the gate electrodes GE formed in the MISFET formation regions AN1, AP1, and AP2.
Over the interlayer insulation film 5 including the plugs PG embedded therein, there is formed an insulation film 6 formed of, for example, a silicon oxide film. In the wiring trench (opening) formed in the insulation film 6, there is formed a wire M1 as a first-layer wire. The wire M1 is electrically coupled via the plugs PG with the source/drain regions SD and the gate electrodes GE formed in the MISFET formation regions AN1, AP1, and AP2, and the like.
The wire M1 is formed by a damascene technology (herein, a single damascene technology). However, as other modes, the wire M1 can also be formed by a patterned conductive film (e.g., a tungsten wire or an aluminum wire).
<Manufacturing Steps of Semiconductor Device>
The manufacturing steps of the semiconductor device of the present embodiment will be described by reference to the accompanying drawings.
First, as shown in
Then, as shown in
Incidentally, in Step S12, over the entire main surface (front surface) of the semiconductor substrate 1, an insulation film formed of silicon oxide (not shown), and an insulation film formed of silicon nitride (not shown) are successively formed. Then, by dry etching with a photoresist pattern (not shown) as an etching mask, there can be formed the element isolation trenches 2a.
Then, as shown in
Incidentally, the following procedure is also acceptable: before the formation of the insulation film 2b, over the entire main surface (front surface) of the semiconductor substrate 1 including the insides of the element isolation trenches 2a, for example, an insulation film formed of silicon nitride (not shown) is formed thinly; this prevents the oxidation of the sidewalls of the element isolation trenches 2a by the heat treatment.
Further, after polishing by the CMP method, there is performed a procedure for reducing the difference in level between the insulation film 2b embedded in each element isolation trench 2a and the semiconductor substrate 1. FIG. 7 shows the case where the height position of the top surface of the insulation film 2b in each element isolation trench 2a is generally equal to the height position of the top surface of the semiconductor substrate 1, and the difference in level is reduced.
In this manner, as shown in
Then, as shown in
The p type well region PW can be formed by introducing p type impurities into the semiconductor substrate 1 using, for example, an ion implantation method. First, over the entire main surface (front surface) of the semiconductor substrate 1, a photoresist layer is coated. Then, the photoresist layer is exposed to light, and developed. As a result, a photoresist pattern (not shown) is formed in such a manner as to have an opening in the MISFET formation region AN1. Then, using the formed photoresist pattern as a mask, boron (B) is ion-implanted in a concentration of, for example, 5×1012 to 5×1013/cm2. As a result, there is formed a p type well region PW with a concentration of impurities (impurity concentration) of 5×1017 to 5×1018/cm3. Then, the photoresist pattern is removed.
The n type well region NW can be formed by introducing n type impurities into the semiconductor substrate 1 using, for example, an ion implantation method. First, over the entire main surface (front surface) of the semiconductor substrate 1, a photoresist layer is coated. Then, the photoresist layer is exposed to light, and developed. As a result, a photoresist pattern (not shown) is formed in such a manner as to have an opening in the MISFET formation regions AN1 and AN2. Then, using the formed photoresist pattern as a mask, phosphorus (P) or arsenic (As) is ion-implanted in a concentration of, for example, 5×1012 to 5×1013/cm2. As a result, there is formed an n type well region NW with a concentration of impurities (impurity concentration) of 5×1017 to 5×1018/cm3. Then, the photoresist pattern is removed.
Then, as shown in
Then, as shown in
After forming the mask film 9, over the entire main surface (front surface) of the semiconductor substrate 1, a photoresist layer is coated. The photoresist layer is exposed to light and is developed. As a result, a photoresist pattern (not shown) is formed in such a manner as to have an opening in the MISFET formation regions AN1 and AP1. Then, with the photoresist pattern as an etching mask, the mask film 9 is dry etched. Accordingly, in the MISFET formation regions AN1 and AP1, the mask film 9 is removed, and the insulation film 3 is exposed. Thereafter, for example, an ashing treatment and a washing treatment using a treatment solution such as a SPM (Sulfuric acid-Hydrogen Peroxide Mixture) solution are performed, thereby to remove the photoresist pattern. As a result, a hard mask pattern 10 formed of the mask film 3 is formed in such a manner as to have an opening in the MISFET formation regions AN1 and AP1, and to cover the insulation film 3 in the MISFET formation region AP2. Namely, the hard mask pattern 10 formed of the mask film 9 is formed in such a manner as to expose the insulation film 3 in the MISFET formation regions AN1 and AP1, and to cover the insulation film 3 in the MISFET formation region AP2.
Then, as shown in
The nitriding treatment is performed by, for example, plasma nitriding or thermal nitriding. The plasma nitriding is the following method: a plasma excites a nitrogen type gas such as a nitrogen (N2) gas to generate nitrogen ions or nitrogen radicals (active species); the semiconductor substrate 1 is exposed thereto, so that the substrate surface is subjected to a nitriding treatment by nitrogen ions or nitrogen radicals (active species). Whereas, the thermal nitriding is the following method: in an atmosphere such as a nitrogen monoxide (NO) gas, the substrate is held at a high temperature such as about 1000° C., thereby to subject the substrate surface to a nitriding treatment.
Then, as shown in
As the metal-containing film 41, there is formed the one containing a metal such as hafnium (Hf), aluminum (Al), or titanium (Ti). Further, when the metal contained in the metal-containing film 41 is, for example, titanium (Ti), as the metal-containing film 41, there can also be formed the one containing, for example, titanium nitride (TiN). Out of these, hafnium (Hf) is preferable in that it produces a larger effect of enabling adjustment of the threshold voltage (Vth) without adjusting the impurity concentration of the channel region than those of other metals. Whereas, when the metal-containing film 41 contains hafnium, the metal-containing film 41 is formed of one or more of hafnium oxide (HfO), hafnium oxynitride (HfON), and HfSiON. At this step, the concentration of hafnium in the metal-containing film 41 is set to be, for example, about 5×1013 atoms/cm2.
Incidentally, in a subsequent step (Step S19 of
Then, as shown in
Then, as shown in
On the other hand, in Step S20, in the MISFET formation regions AN1 and AP1, the insulation film 31 including the metal-containing film 41 formed on the surface thereof, and formed of silicon oxynitride may be further nitrided. However, in the MISFET formation region AN1, when the insulation film 31 is further nitrided, the positive fixed charges in the resulting gate insulation film GI1(see
The nitriding treatment in Step S20 is also performed in the same manner as the nitriding treatment in Step S17.
Then, as shown in
The insulation film 31 in the MISFET formation regions AN1 and AP1 forms the lower layer film LL1 of the gate insulation film GI1 (see
For the metal-containing film 42, there is used the same material as that for the metal-containing film 41. Further, when the metal-containing film 42 contains hafnium, the concentration of hafnium in the metal-containing film 42 is set to be, for example, about 5×1013 atoms/cm2. Then, when the concentration of hafnium in the metal-containing film 41 is set to be, for example, about 5×1013 atoms/cm2 as described above, the concentration of hafnium in the upper layer film UL2 formed of the metal-containing film 42 is set to be, for example, about 5×1013 atoms/cm2. As a result, the concentration of hafnium in the upper layer film UL1 formed of the metal-containing films 41 and 42 can be set as, for example, about 1×1014 atoms/cm2.
Whereas, in
Then, as shown in
Then, as shown in
Then, there are formed the gate electrodes GE, and the gate insulation films GI1 and GI2 (Step S24 of
As shown in
Incidentally, as described by reference to
Then, as shown in
Then, as shown in
Then, the source/drain regions SD are formed (Step S27 of
In this manner, as shown in
The MISFET QN1 formed in the MISFET formation region AN1 has the gate insulation film GI1 formed of the lower layer film LL1, and the upper layer film UL1 formed over the lower layer film LL1. The MISFET QP1 formed in the MISFET formation region AP1 has the gate insulation film GI1 formed of the lower layer film LL1, and the upper layer film UL1 formed over the lower layer film LL1. The MISFET QP2 formed in the MISFET formation region AP2 has the gate insulation film GI2 formed of the lower layer film LL2, and the upper layer film UL2 formed over the lower layer film LL2. The concentration of hafnium (metal) in the upper layer film UL2 is smaller than the concentration of hafnium (metal) in the upper layer film UL1. The concentration of nitrogen in the lower layer film LL2 is smaller than the concentration of nitrogen in the lower layer film LL1. Therefore, in the n type MISFET formation region AN1, there is formed the n channel type MISFET QN1 having a large threshold voltage (Vth); in the p type MISFET formation region AP1, there is formed the p channel type MISFET QP1 having a large threshold voltage (Vth); and in the p type MISFET formation region AP2, there is formed the p channel type MISFET QP2 having a small threshold voltage (Vth).
Incidentally, after Step S27, and before Step S28 described later, by a salicide technology, a low-resistance metal silicide layer formed of cobalt silicide, nickel silicide, or the like may be formed over the surfaces of the gate electrode GE and the source/drain regions SD.
Then, as shown in
In the Step S28, first, over the entire main surface (front surface) of the semiconductor substrate 1, there is formed the interlayer insulation film 5. Namely, the interlayer insulation film 5 is formed over the entire main surface (front surface) of the semiconductor substrate 1 in such a manner as to cover the gate electrodes GE and the sidewall spacers SW. The interlayer insulation film 5 is formed of, for example, a single film of silicon oxide film, or a lamination film of a silicon nitride film and a silicon oxide film thicker than this. Thereafter, the surface (top surface) of the interlayer insulation film 5 is subjected to polishing by a CMP method, or other treatments. As a result, the top surface of the interlayer insulation film 5 is planarized. Even when the uneven shape is formed at the surface of the interlayer insulation film 5 due to the underlayer step, the surface of the interlayer insulation film 5 is polished by a CMP method, which can provide an interlayer insulation film with the surface planarized.
Then, using the photoresist pattern (not shown) formed over the interlayer insulation film 5 as an etching mask, the interlayer insulation film 5 is dry etched. As a result, in the interlayer insulation film 5, the contact holes CNT are formed. At the bottoms of the contact holes CNT, there are exposed some portions of the main surface of the semiconductor substrate 1 such as a portion of the gate electrode GE, and portions of the source/drain regions SD.
Then, in each contact hole CNT, there is formed a conductive plug PG formed of tungsten (W) or the like. For forming the plugs PG, for example, over the interlayer insulation film 5 including the insides of the contact hole CNT, a barrier conductor film (e.g., a titanium film or a titanium nitride film, or a lamination film thereof) is formed by a plasma CVD method or the like. Then, a main conductor film formed of a tungsten film or the like is formed over the barrier conductor film in such a manner as to fill the contact holes CNT by a CVD method or the like. The unnecessary portions of the main conductor film and the barrier conductor film over the interlayer insulation film 5 are removed by a CMP method, an etching back method, or the like. As a result, the plugs PG can be formed. In
Then, over the interlayer insulation film 5 including the plugs PG embedded therein, the insulation film 6 is formed. The insulation film 6 can also be formed of a lamination film of a plurality of insulation films.
Then, by a single damascene method, there is formed the wire M1 which is a first-layer wire (Step S29 of
Incidentally, as described by reference to
The wire M1 is electrically coupled via the plug PG with the gate electrode GE, the source/drain region SD, or the like. Thereafter, by a dual damascene method, a second-layer wire is formed, but herein, is not shown and not described.
<Regarding Adjustment of Threshold Voltage (Vth) of MISFET>
The semiconductor device of the comparative example also has a p channel type MISFET QP1 having a large threshold voltage (Vth), and a p channel type MISFET QP2 having a small threshold voltage (Vth). However, in the semiconductor device of the comparative example, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is larger than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QP1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is larger than the concentration of nitrogen in the lower layer film LL1 of the MISFET QP1.
Further, the semiconductor device of the comparative example also has the n channel type MISFET QN1, and the p channel type MISFET QP2 having a small threshold voltage (Vth). However, in the semiconductor device of the comparative example, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is larger than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QN1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is larger than the concentration of nitrogen in the lower layer film LL1 of the MISFET QN1.
Still further, the semiconductor device of the comparative example is equal in respective portions to the semiconductor device of the first embodiment, except for the upper layer films UL1 and UL2, and the lower layer films LL1 and LL2.
Then, an analysis by the present inventors indicates the following: for the semiconductor device of the comparative example, a short channel length of a MISFET tends to cause deterioration of the transistor characteristics such as reduction of the threshold voltage (Vth).
In the semiconductor device of the comparative example, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is larger than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QP1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is larger than the concentration of nitrogen in the lower layer film LL1 of the MISFET QP1. In this case, the impurity concentration in the channel region of the MISFET QP2 is adjusted so as to be smaller than the impurity concentration in the channel region of the MISFET QP1. As a result, the threshold voltage (Vth) of the MISFET QP2 is adjusted so as to be smaller than the threshold voltage (Vth) of the MISFET QP1.
However, in the p channel type MISFET, with an increase in concentration of nitrogen in the gate insulation film, the positive fixed charges in the gate insulation film increase, resulting in an increase in threshold voltage (Vth). Namely, the threshold voltage (Vth) of the MISFET QP2 having a large concentration of nitrogen in the lower layer film LL2 is larger than the threshold voltage (Vth) of the MISFET QP1 having a small concentration of nitrogen in the lower layer film LL1. Therefore, the threshold voltage (Vth) of the MISFET QP2 which is originally desired to be reduced in threshold voltage (Vth) becomes larger than the threshold voltage (Vth) of the MISFET QP1 which is originally desired to be increased in threshold voltage (Vth). In order to reduce the threshold voltage (Vth) of the MISFET QP2 as desired in such a state, the impurity concentration in the channel region of the MISFET QP2 is required to be adjusted so as to be further reduced. However, it has been shown as follows: when the channel length of the MISFET QP2 is short, a decrease in the impurity concentration in the channel region makes the transistor characteristics more likely to be deteriorated as described above.
Further, in the semiconductor device of the comparative example, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is larger than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QN1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is larger than the concentration of nitrogen in the lower layer film LL1 of the MISFET QN1. Also in this case, the impurity concentration in the channel region of the MISFET QP2 is adjusted so as to be smaller than the impurity concentration in the channel region of the MISFET QN1. This results in that the threshold voltage (Vth) of the MISFET QP2 is adjusted so as to be smaller than the threshold voltage (Vth) of the MISFET QN1. Incidentally, the term “magnitude relation of the threshold voltages (Vth)” herein used is, as described above, the magnitude relation of the absolute values of the threshold voltages (Vth).
However, in order to reduce the threshold voltage (Vth) of the MISFET QP2 as desired, the impurity concentration in the channel region of the MISFET QP2 is required to be adjusted so as to be reduced. However, it has been shown as follows: when the channel length of the MISFET QP2 is short, a decrease in the impurity concentration in the channel region makes the transistor characteristics more likely to be deteriorated as described above.
<Main Features and Effects of the Present Embodiment>
The semiconductor device of the present embodiment includes the p channel type MISFET QP1 having a large threshold voltage (Vth), and the p channel type MISFET QP2 having a small threshold voltage (Vth). However, in the present embodiment, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is set smaller than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QP1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is set smaller than the concentration of nitrogen in the lower layer film LL1 of the MISFET QP1.
As a result, without adjusting the impurity concentration in the channel region, the threshold voltage (Vth) of the MISFET QP2 can be adjusted so as to be smaller than the threshold voltage (Vth) of the MISFET QP1. Whereas, the lower layer films LL1 and LL2 are each formed of, for example, silicon oxynitride, and include silicon, oxygen, and nitrogen. This can inhibit the deterioration of the reliability of the gate insulation films GI1 and GI2 due to the crystallization of hafnium (metal).
Whereas, in the p channel type MISFET, with an increase in concentration of nitrogen in the gate insulation film, the positive fixed charges in the gate insulation film increase, resulting in an increase in threshold voltage (Vth). In the present embodiment, the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 which is desired to be reduced in threshold voltage (Vth) is smaller than the concentration of nitrogen in the lower layer film LL1 of the MISFET QP1 which is desired to be increased in threshold voltage (Vth). Accordingly, particularly in the MISFET QP2, it is possible to suppress an increase in threshold voltage (Vth) due to the positive fixed charges in the gate insulation film GI2. As a result, when the threshold voltage (Vth) of the MISFET QP2 is adjusted so as to be reduced, the impurity concentration in the channel region is not required to be reduced. For this reason, even when the channel length of the MISFET QP2 is short, it is possible to suppress the deterioration of the transistor characteristics.
Further, the semiconductor device of the present embodiment includes the n channel type MISFET QN1 having a large threshold voltage (Vth), and the p channel type MISFET QP2 having a small threshold voltage (Vth). However, in the present embodiment, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is set smaller than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QN1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is set smaller than the concentration of nitrogen in the lower layer film LL1 of the
As a result, without adjusting the impurity concentration in the channel region, the threshold voltage (Vth) of the MISFET QP2 can be adjusted so as to be smaller than the threshold voltage (Vth) of the MISFET QN1. Whereas, the lower layer films LL1 and LL2 are each formed of, for example, silicon oxynitride, and include silicon, oxygen, and nitrogen. This can inhibit the deterioration of the reliability of the gate insulation films GI1 and GI2 due to the crystallization of hafnium (metal). Incidentally, the term “magnitude relation of the threshold voltages (Vth)” herein used is, as described above, the magnitude relation of the absolute values of the threshold voltages (Vth).
Further, in the p channel type MISFET, with an increase in concentration of nitrogen in the gate insulation film, the positive fixed charges in the gate insulation film increase, resulting in an increase in threshold voltage (Vth). In the present embodiment, the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 which is desired to be reduced in threshold voltage (Vth) is smaller than the concentration of nitrogen in the lower layer film LL1 of the MISFET QN1 which is desired to be increased in threshold voltage (Vth). Accordingly, particularly in the MISFET QP2, it is possible to suppress an increase in threshold voltage (Vth) due to the positive fixed charges in the gate insulation film GI2. As a result, when the threshold voltage (Vth) of the MISFET QP2 is adjusted so as to be reduced, the impurity concentration in the channel region is not required to be reduced. For this reason, even when the channel length of the MISFET QP2 is short, it is possible to suppress the deterioration of the transistor characteristics.
Incidentally, as described above, the same effects can be obtained even when as the metal to be contained in the upper layer films UL1 and UL2, for example, aluminum or titanium is used in place of hafnium. However, use of hafnium is most effective.
Whereas, also for the n channel type MISFET, as with the p channel type MISFET, there may be formed two kinds of MISFETs varying in concentration of hafnium (metal) and concentration of nitrogen in the gate insulation film therebetween. However, for the n channel type MISFET, even when the positive fixed charges in the gate insulation film have increased with an increase in concentration of nitrogen in the gate insulation film, the threshold voltage (Vth) is less likely to increase. Therefore, for the n channel type MISFET, two types of MISFETs varying in concentration of hafnium (metal) and concentration of nitrogen in the gate insulation film therebetween as with the p channel type MISFET are not formed. As described in the present embodiment, preferably, only one type MISFET is formed.
Further, in the present embodiment, a description was given to the example in which there were formed a total of three types of MISFETs of one type of n channel type MISFET and two types of p channel type MISFETs having different threshold voltages (Vth). However, the present invention is also applicable to the case where there are formed a total of two types of MISFETs of an n channel type MISFET, and a p channel type MISFET having a small threshold voltage (Vth). Even when the channel length of the p channel type MISFET having a small threshold voltage (Vth) is short, it is possible to suppress the deterioration of the transistor characteristics. Similarly, the present invention is also applicable to the case where there are formed only two types of p channel type MISFETs having different threshold voltages (Vth). Even when the channel length of the p channel type MISFET having a small threshold voltage (Vth) is short, it is possible to suppress the deterioration of the transistor characteristics.
In the first embodiment, the concentration of hafnium (metal) and the concentration of nitrogen in the gate insulation film are changed, so that there are formed a MISFET having a large threshold voltage (Vth) and a MISFET having a small threshold voltage (Vth). In contrast, in a second embodiment, in addition to the MISFET having a large threshold voltage (Vth) and the MISFET having a small threshold voltage (Vth), there is formed a high breakdown voltage MISFET. Then, the concentration of hafnium (metal) in the gate insulation film of the MISFET having a small threshold voltage (Vth) is smaller than the concentration of hafnium (metal) in the gate insulation film of the high breakdown voltage MISFET. The nitrogen concentration in the gate insulation film of the MISFET having a small threshold voltage (Vth) is smaller than the nitrogen concentration in the gate insulation film of the high breakdown voltage MISFET.
<Semiconductor Device>
In the present embodiment, in addition to the MISFET having a large threshold voltage (Vth) and the MISFET having a small threshold voltage (Vth), there is formed the high breakdown voltage MISFET.
As shown in
Incidentally, in
Further,
Further, in
As shown in
Then, a description will be given to the specific configuration of the high breakdown voltage MISFET QH1 formed in the high breakdown voltage MISFET formation region AH1.
The high breakdown voltage MISFET QH1 has a gate electrode GE formed over the semiconductor substrate 1. The gate electrode GE is formed over the n type well region NW formed in the semiconductor substrate 1 in the high breakdown voltage MISFET formation region AH1. Whereas, the high breakdown voltage MISFET QH1 has a gate insulation film GI3 formed between the gate electrode GE and the semiconductor substrate 1. Namely, the high breakdown voltage MISFET QH1 has the gate insulation film GI3 formed over the semiconductor substrate 1, and the gate electrode GE formed over the gate insulation film GI3.
However, the MISFET QH1 is a high breakdown voltage MISFET. For this reason, the thickness of the gate insulation film GI3 is larger than the thickness of any film of the gate insulation film GI1 of the MISFET QP1 and the gate insulation film GI2 of the MISFET QP2.
For the gate electrode GE, there can be used the same material as that for the gate electrode GE of the p channel type MISFET QP1.
The gate insulation film GI3 includes a metal, silicon, oxygen, and nitrogen.
Examples of the metal to be contained in the gate insulation film GI3 may include hafnium (Hf), aluminum (Al), and titanium (Ti). By adjusting the content of the metal in the gate insulation film GI3, it is possible to adjust the threshold voltage (Vth) of the MISFET QH1 without adjusting the impurity concentration in the channel region. Whereas, when the metal contained in the gate insulation film GI3 is, for example, titanium (Ti), as the gate insulation film GI3, there can be used the one containing, for example, titanium nitride (TiN). Further, hafnium (Hf) is preferable among the metals described above in that it produces a still larger effect of enabling adjustment of the threshold voltage (Vth) without adjusting the impurity concentration of the channel region by the adjustment of the content of the metal in the gate insulation film GI3.
The silicon, oxygen, and nitrogen included in the gate insulation film GI3 are present as, for example, silicon oxynitride (SiON) in the gate insulation film GI3. Out of these, nitrogen can suppress the deterioration of the reliability of the gate insulation film GI3 due to crystallization of the contained metal when the gate insulation film GI3 includes the metal described above.
Incidentally, a detailed structure of the gate insulation film GI3 will be described later.
Over the sidewall of the gate electrode GE, a sidewall spacer SW is formed as a sidewall insulation film. Then, in portions which are in the high breakdown voltage MISFET formation region AH1, and are on the opposite sides across the gate electrode GE including the sidewall spacer SW formed thereover, there are formed source/drain regions SD. In the high breakdown voltage MISFET formation region AH1, the source/drain regions SD are n type semiconductor regions including p type impurities such as boron (B) diffused therein.
Whereas, in the high breakdown voltage MISFET formation region AH1, in the semiconductor substrate 1, the extension regions EX are formed, and the source/drain regions SD of a LDD structure are formed. Further, also in the high breakdown voltage MISFET formation region AH1, over the source/drain regions SD and over the gate electrode GE, a metal silicide layer can be formed using a salicide technology.
Also in the present embodiment, as with the first embodiment, the concentration of the metal in the gate insulation film GI2 is smaller than the concentration of the metal in the gate insulation film GI1. The concentration of nitrogen in the gate insulation film GI2 is smaller than the concentration of nitrogen in the gate insulation film GI1. As a result, without adjusting the impurity concentration in the channel region, the threshold voltage (Vth) of the MISFET QP2 can be adjusted so as to be smaller than the threshold voltage (Vth) of the MISFET QN1. Further, it is possible to suppress the deterioration of the reliability of the gate insulation film GI1 due to the crystallization of the metal contained in the gate insulation film GI1 in the MISFET QP1; and it is possible to suppress the increase in threshold voltage (Vth) due to the inclusion of nitrogen in the gate insulation film GI2 in the MISFET QP2. Then, without reducing the impurity concentration, the threshold voltage (Vth) can be adjusted so as to be reduced. For this reason, even when the channel length is short, it is possible to suppress the deterioration of the transistor characteristics in the MISFET having a small threshold voltage (Vth).
In addition to this, in the present embodiment, the concentration of the metal in the gate insulation film GI2 is smaller than the concentration of the metal in the gate insulation film GI3; and the concentration of nitrogen in the gate insulation film GI2 is smaller than the concentration of nitrogen in the gate insulation film GI3. As a result, without adjusting the impurity concentration in the channel region, the threshold voltage (Vth) of the MISFET QP2 can be adjusted so as to be smaller than the threshold voltage (Vth) of the MISFET QH1. In addition, the breakdown voltage of the MISFET QH1 can be increased, which facilitates the design of a semiconductor device including a high breakdown voltage MISFET merged therein.
Further, the concentration of the metal in the gate insulation film GI3 is preferably equal to the concentration of the metal in the gate insulation film GI1; and the concentration of nitrogen in the gate insulation film GI3 is preferably equal to the concentration of nitrogen in the gate insulation film GI1. As a result, the gate insulation film GI3 and the gate insulation film GI1 can be formed by the same step. This can simplify the manufacturing step of a semiconductor device in which the gate insulation films GI1, GI2, and GI3 are formed individually. In the explanation of the manufacturing step of a semiconductor device described later, a description will be given to an example in which the concentration of the metal in the gate insulation film GI3 is equal to the concentration of the metal in the gate insulation film GI1; and the concentration of nitrogen in the gate insulation film GI3 is equal to the concentration of nitrogen in the gate insulation film GI1.
Then, a description will be given to the detailed structure of the gate insulation film GI3.
As shown in
As the lower layer film LL3, there is used a film formed of, for example, silicon oxynitride (SiON). As the upper layer film UL3, there is used a film formed of one or more of hafnium oxide (HfO), hafnium oxynitride (HfON), and HfSiON.
Further, preferably, the thickness T2 of the upper layer film UL2 is made smaller than the thickness T1 of the upper layer film UL1; and the thickness T2 of the upper layer film UL2 is made smaller than the thickness T3 of the upper layer film UL3. This can make the concentration of hafnium in the gate insulation film GI2 smaller than any of the concentration of hafnium in the gate insulation film GI1 and the concentration of hafnium in the gate insulation film GI3 with ease.
Further, preferably, the thickness of the upper layer film UL3 is made equal to the thickness of the upper layer film UL1. This can make the concentration of hafnium in the gate insulation film GI3 equal to the concentration of hafnium in the gate insulation film GI1 with ease.
Specifically, the concentration of hafnium in the gate insulation film GI3 is preferably 5×1013 to 2×1014 atoms/cm2 and larger than the concentration of hafnium in the gate insulation film GI2 as with the concentration of hafnium in the gate insulation film GI1. When the concentration of hafnium in the gate insulation film GI3 is less than 5×1013 atoms/cm2, the threshold voltage (Vth) of the MISFET QH1 may be unadjustable so as to be sufficiently large. When the concentration of hafnium in the gate insulation film GI3 exceeds 2×1014 atoms/cm2, hafnium becomes more likely to be crystallized, which may result in the reduction of the reliability of the gate insulation film GI3.
Further, preferably, the concentration of nitrogen in the gate insulation film GI3 is 5 to 20 atom %, and larger than the concentration of nitrogen in the gate insulation film GI2. When the concentration of nitrogen in the gate insulation film GI3 is less than 5 atom %, hafnium becomes more likely to be crystallized, which may result in the reduction of the reliability of the gate insulation film GI3. Whereas, the concentration of nitrogen in the gate insulation film GI3 exceeds 20 atom %, the threshold voltage (Vth) of the MISFET QH1 may become too large.
Incidentally,
Besides, respective portions of the element isolation regions 2, the element isolation trenches 2a, the insulation film 2b, the interlayer insulation film 5, the contact holes CNT, the plugs PG, the insulation film 6, and the wire M1 of the semiconductor device of the present embodiment are equal to respective portions of the element isolation regions 2, the element isolation trenches 2a, the insulation film 2b, the interlayer insulation film 5, the contact holes CNT, the plugs PG, the insulation film 6, and the wire M1 of the semiconductor device of the first embodiment, respectively, and hence will not be described.
<Manufacturing Steps of Semiconductor Device>
The manufacturing steps of the semiconductor device of the present embodiment will be described by reference to the accompanying drawings.
First, the same steps (Step S31 and Step S32 of
Then, as shown in
Then, as shown in
Then, as shown in
Then, as shown in
Then, as shown in
Then, as shown in
This results in the following state: as shown in
Then, as shown in
After the formation of the mask film 9, over the entire main surface (front surface) of the semiconductor substrate 1, a photoresist layer is coated. The photoresist layer is exposed to light and developed. As a result, a photoresist pattern (not shown) is formed in such a manner as to have an opening in the MISFET formation regions AH1 and AP1. Then, with the photoresist pattern as an etching mask, the mask film 9 is dry etched. Then, the photoresist pattern is removed. As a result, a hard mask pattern 10 formed of the mask film 3 is formed in such a manner as to have an opening in the MISFET formation regions AN1 and AP1, and to cover the insulation film 3 in the MISFET formation region AP2. Namely, the hard mask pattern 10 formed of the mask film 9 is formed in such a manner as to expose the insulation film 33 in the MISFET formation regions AH1, to expose the insulation film 3 in the MISFET formation region AP1, and to cover the insulation film 3 in the MISFET formation region AP2.
Then, as shown in
Then, as shown in
As the metal-containing film 41, as with the step of Step S18 of
Further, in consideration of the reduction due to etching in the subsequent step (Step S43 of
Then, as shown in
Then, as shown in
The nitriding treatment in Step S44 is also performed in the same manner as the nitriding treatment in Step S41.
Then, as shown in
The insulation film 33a in the MISFET formation region AH1 forms the lower layer film LL3 of the gate insulation film GI3 (see
For the metal-containing film 42, there is used the same material as that for the metal-containing film 41. Whereas, when the metal-containing film 42 contains hafnium, the concentration of hafnium in the metal-containing film 42 is set so as to be, for example, about 5×1013 atoms/cm2. Then, when the concentration of hafnium in the metal-containing film 41 is set at about 5×1013 atoms/cm2 as described above, the concentration of hafnium in the upper layer film UL2 formed of the metal-containing film 42 is set at, for example, about 5×1013 atoms/cm2. As a result, it is possible to set the concentration of hafnium in the upper layer films UL3 and UL1 formed of the metal-containing films 41 and 42 at, for example, about 1×1014 atoms/cm2.
Further, in
Then, the same step as Step S22 of
Then, as with the step of Step S23 of
As shown in
Incidentally, when the metal-containing film 41 and the metal-containing film 42 are not definitely formed, and a metal is added to the insulation film 33a, the insulation film 31, and the insulation film 32 as described by reference to
Thereafter, the same steps (Step S49 to Step S51 of
<Main Features and Effects of the Present Embodiment>
The semiconductor device of the present embodiment also has the p channel type MISFET QP1 having a large threshold voltage (Vth), and the p channel type MISFET QP2 having a small threshold voltage (Vth). Then, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is made smaller than the concentration of hafnium (metal) in the upper layer film UL1 of the MISFET QP1; and the concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is made smaller than the concentration of nitrogen in the lower layer film LL1 of the MISFET QP1. As a result, as with the first embodiment, when the threshold voltage (Vth) of the MISFET QP2 is adjusted so as to be reduced, the impurity concentration in the channel region is not required to be reduced. For this reason, even when the channel length of the MISFET QP2 is short, the deterioration of the transistor characteristics can be suppressed.
Further, the semiconductor device of the present embodiment has the high breakdown voltage MISFET QH1 in addition to the MISFET QP1 having a large threshold voltage (Vth) and the MISFET QP2 having a small threshold voltage (Vth). Then, the concentration of hafnium (metal) in the upper layer film UL2 of the MISFET QP2 is set smaller than the concentration of hafnium (metal) in the upper layer film UL3 of the MISFET QH1. The concentration of nitrogen in the lower layer film LL2 of the MISFET QP2 is set smaller than the concentration of nitrogen in the lower layer film LL3 of the MISFET QH1.
When a circuit including a high breakdown voltage MISFET and a circuit including a (low breakdown voltage) MISFET which does not have a high breakdown voltage are merged in the same semiconductor device, the power supply voltage is high in the circuit including a high breakdown voltage MISFET. Therefore, for the high breakdown voltage MISFET, from the viewpoint of ensuring the high breakdown voltage, and from the viewpoint of so-called hot carrier resistance, it is more advantageous to increase the threshold voltage (Vth) by adjusting the structure of the gate insulation film than to increase the threshold voltage (Vth) by adjusting the impurity concentration in the channel region. Namely, the increase in concentration of the metal such as hafnium in the gate insulation film of the high breakdown voltage MISFET is more advantageous in being capable of increasing the threshold voltage (Vth) of the high breakdown voltage MISFET with ease than the adjustment of the impurity concentration in the channel region.
On the other hand, it can also be considered that the design of the structure of the source/drain regions SD, or the design of the LDD structure including the source/drain regions SD and the extension region EX increases the threshold voltage (Vth) of the high breakdown voltage MISFET. However, as described above, the increase in concentration of the metal such as hafnium in the gate insulation film can increase the threshold voltage (Vth) of the high breakdown voltage MISFET with ease. For this reason, it is possible to improve the performances of the semiconductor device including a high breakdown voltage MISFET merged therein with more ease. As a result, it is possible to design the semiconductor device including a high breakdown voltage MISFET merged therein readily and rationally.
Up to this point, the inventions made by the present inventors were specifically described by way of embodiments thereof. However, it is naturally understood that the present invention is not limited to the embodiments, and may be variously changed within the scope not departing from the gist thereof.
The present invention is effectively applicable to a semiconductor device and a manufacturing method thereof.
Number | Date | Country | Kind |
---|---|---|---|
2011-265852 | Dec 2011 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
6642131 | Harada | Nov 2003 | B2 |
7754570 | Kimizuka et al. | Jul 2010 | B2 |
7915686 | Shimamoto et al. | Mar 2011 | B2 |
8018004 | Sato et al. | Sep 2011 | B2 |
20070284670 | Yamamotot et al. | Dec 2007 | A1 |
20090194823 | Maeda | Aug 2009 | A1 |
20100102395 | Yamamoto et al. | Apr 2010 | A1 |
20100155844 | Takahashi | Jun 2010 | A1 |
20100176455 | Arayashiki | Jul 2010 | A1 |
20100330812 | Akiyama et al. | Dec 2010 | A1 |
20120018814 | Morooka | Jan 2012 | A1 |
20120139055 | Sato et al. | Jun 2012 | A1 |
Number | Date | Country |
---|---|---|
2003-8011 | Jan 2003 | JP |
2006-93670 | Apr 2006 | JP |
2006-332179 | Dec 2006 | JP |
2007-288096 | Nov 2007 | JP |
2008-288465 | Nov 2008 | JP |
2010-103386 | May 2010 | JP |
2010-161299 | Jul 2010 | JP |
2011-9321 | Jan 2011 | JP |
WO 2008015940 | Feb 2008 | WO |
WO 2008035598 | Mar 2008 | WO |
Number | Date | Country | |
---|---|---|---|
20130161753 A1 | Jun 2013 | US |