The present invention relates to a semiconductor device with a wiring structure having interlayer-insulating films each made of an insulating film with a low relative dielectric constant, especially a porous film, and a method of producing this type of semiconductor device.
Two major factors in delay in operation speed for large-scale integrated circuits are delay in operation of transistors themselves and delay (RC delay) in signals propagating through wirings.
Miniaturization and high integration of wirings and devices affects recent advancement in semiconductor fabrication process highlight the effects of RC delay rather than delay in operation of transistors themselves. Protection against RC delay promotes development of wiring materials of a low resistivity and insulating films of a low relative dielectric constant (called low-dielectric-constant insulating films hereinafter).
One recent wiring material is copper (Cu) with resistivity lower than a known wiring material aluminum (Al). Copper requires a relatively high vapor pressure in etching, and hence hard to be processed by reactive ion etching with chloride gas at a low vapor pressure. It is thus processed by damascene in wiring formation.
Developed for low-dielectric-constant insulating films is application of organic material-applied insulating films of a low relative dielectric constant in the range from about 2.5 to 2.8 such as methyl siloxane to multi-layered wiring processes.
Also there are developed porous insulating films having many nanometer-size pores. Porous insulating films can have relative dielectric constant of 2.5 or smaller by lowering the film density with pore-number adjustments. Use of porous insulating films as interlayer-insulating films in semiconductors with a multi-layered wiring structure protects against RC delays.
Organic material-applied insulating films having a low relative dielectric constant are, however, could suffer degradation or increase in hygroscopic property due to O2 gas-ashing in resist-peeling process, when used as interlayer-insulating films in multi-layered wiring process. Insulating films having a low relative dielectric constant could also suffer clucks in etching process.
Moreover, porous insulating films could have a high relative dielectric constant due to permeation of etching gas and chemical solution into pores generated in the porous insulating films, and suffer clucks or peeling-off due to discharging of the etching gas and chemical solution in post-thermal processes.
A wiring-layer structure having interlayer-insulating films may have several types in accordance with a width of each of several wiring layers and a distance between adjacent wiring layers. Such a wiring-layer structure has a tendency to have a small width for each interlayer-insulating film provided laterally as the width of each wiring layer becomes small. This tendency is used for wiring-layer structure miniaturization.
One of the problems for such wiring-layer structure miniaturization is RC delay due to increase in parasitic capacitance between wiring layers.
Several techniques have been proposed for decreasing parasitic capacitance between wiring layers to prevent decrease in signal propagation speed and generation of cross-talks between wiring layers with different relative dielectric constants for interlayer-insulating films having a relatively big inter-wiring distance and those having a relatively small inter-wiring distance.
Japanese Patent No. 2910713 discloses a wiring-layer structure having interlayer-insulating films of high mechanical strength and also high moisture resistance in a wide wiring-interval region and those of low relative dielectric constant in a narrow wiring-interval region.
Japanese Unexamined Patent Publication No. 2000-49228 discloses a dual-damascene wiring-layer structure having a first wide region 240 between metallized portions and a second narrow region between metallized portions, made of a dielectric material having a low dielectric constant.
Neither prior art, however, discloses insulating-film structures at different layer stages of a multi-layered wiring structure.
In detail, the latter prior art does not discuss any multi-layered wiring structure. The former discloses a multi-layered wiring structure in
A method of producing a semiconductor device having a plurality of wiring layers according to the third aspect of the present invention forms first interlayer-insulating film; forms a plurality of grooves for wiring in the first interlayer-insulating film; fills metallic films in the grooves to form wirings; etches the first interlayer-insulating film with the wirings as a mask and removes the interlayer-insulating film between the wirings to provide grooves to be filled; and fills a second interlayer-insulating film made of a material of low dielectric constant in the grooves to be filled.
Further, a method of producing a semiconductor device having a plurality of wiring layers according to the fourth aspect of the present invention forms a first interlayer-insulating film; forms a plurality of grooves for wiring in the first interlayer-insulating film; fills metallic films in the wiring grooves to form wirings; etches the first interlayer-insulating film with the wirings as a mask and removes the interlayer-insulating film between the wirings to provide grooves to be filled; fills a second interlayer-insulating film made of at least one insulating film in the grooves to be filled, the insulating film being made of a material selected from the group consisting of resin having siloxane bonding as a major structure, resin having C—C bonding as a major structure and a resin having C═C bonding as a major structure, and changes the second interlayer-insulating film into a porous insulating film.
Moreover, a method of producing a semiconductor device having a plurality of wiring layers according to the fifth aspect of the present invention forms a first interlayer-insulating film; performs dehydrating polymerization to the first interlayer-insulating film; forms a plurality of grooves for wiring in the dehydrating-polymerized first interlayer-insulating film; fills metallic films in the wiring grooves to form wirings; and applies a solvent to the dehydrating-polymerized first interlayer-insulating film after the wiring formation.
a), 1(b) and 1(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a first embodiment according to the present invention;
d) and 1(e) are sectional views illustrating posterior processes following the process shown in
a), 2(b) and 2(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a second embodiment according to the present invention;
d), 2(e) and 2(f) are sectional views illustrating posterior processes following the process shown in
a), 3(b) and 3(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a third embodiment according to the present invention;
d), 3(e) and 3(f) are sectional views illustrating posterior processes following the process shown in
a), 4(b) and 4(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a fourth embodiment according to the present invention;
d), 4(e) and 4(f) are sectional views illustrating posterior processes following the process shown in
a), 5(b) and 5(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a fifth embodiment according to the present invention;
d), 5(e) and 5(f) are sectional views illustrating posterior processes following the process shown in
a), 6(b) and 6(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a sixth embodiment according to the present invention;
d), 6(e) and 6(f) are sectional views illustrating posterior processes following the process shown in
a), 7(b) and 7(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a seventh embodiment according to the present invention;
d), 7(e) and 7(f) are sectional views illustrating posterior processes following the process shown in
a), 8(b) and 8(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in an eighth embodiment according to the present invention;
d), 8(e) and 8(f) are sectional views illustrating posterior processes following the process shown in
a), 9(b) and 9(c) are sectional views each illustrating an anterior process of a method of producing a semiconductor device having a plurality of wiring layers in a ninth embodiment according to the present invention;
d), 9(e) and 9(f) are sectional views illustrating posterior processes following the process shown in
Several embodiments of semiconductor device having a plurality of wiring layers and method of producing the semiconductor device according to the present invention will be disclosed with reference to the attached drawings.
Disclosed first with reference to
As shown in
The barrier metal film 4 is then formed in each groove with deposition of a TaN film on the groove by sputtering or chemical vapor deposition (abbreviated to CVD hereinafter) for prevention of Cu dispersion and oxidation.
The Cu and TaN layers deposited on the device surface except the grooves are removed by chemical mechanical polishing (abbreviated to CMP hereinafter) until the first interlayer-insulating film 3 is exposed at the device surface, to polish the Cu layer 5 for forming the first wiring layer 6.
Next, as shown in
Next, as shown in
The first embodiment, however, requires dehydrating polymerization at a temperature as low as possible, for example, at about 300° C. before solvent evaporation. A starting temperature for dehydrating polymerization is lowered in the first embodiment by annealing the second interlayer-insulating film 7 in an NH3-gas ambient or annealing the film 7 during, for example, electron-beam (EB) irradiation.
The reason for annealing at a low temperature is to allow cross linking whereas prevent generation of pores, thus cross linking only occurring to a part of the second interlayer-insulating film 7. Pores will be generated at 400° C. or higher as discussed later. A pore-generating process has to be performed after there is no possibility of harmful effects to pores during the process.
A second interlayer-insulating film 7a after dehydrating polymerization only has not been changed yet into a porous film while cross linking has only occurred to a part of the second interlayer-insulating film 7. And, hence permeation of etching gas and chemical solution into pores is out of consideration at this stage. A precursor of a porous insulating film exhibits a low mechanical strength. The dehydrating polymerization, however, generates siloxane bonding among molecules in an insulating film to enhance mechanical strength for the film. The second interlayer-insulating film 7a with a high mechanical strength thus enhanced can be processed with least damages by reactive ion etching (abbreviated to RIE hereinafter).
The second interlayer-insulating film 7a subjected to dehydrating polymerization is processed with lithography and RIE to provide first contact holes and second wiring grooves simultaneously, as shown in
A TaN layer and then a Cu layer are deposited on the second interlayer-insulating film 7a, the first contact holes and the second wiring grooves. Unnecessary Cu and TaN layers are removed by CMP until the second interlayer-insulating film 7a is exposed at the device surface, thus forming a second wiring layer 10 having a second wiring 9a and a first plug 9b.
The second interlayer-insulating film 7a subjected to dehydrating polymerization is further subjected to solvent evaporation at about 400° C. to generate pores therein for the first time through the processes, thus being changed into a porous insulating film 7b, as shown in
As disclosed, the first embodiment performs processing such as RIE to the second interlayer-insulating film 7a before generation of pores, thus having no problem of permeation of etching gas and chemical solution into the pores.
Disclosed next with reference to
The processes for forming the first wiring layer 6 are the same as shown in
As shown in
Or, the second interlayer-insulating film 11 can be formed by applying another specific insulating film on the first interlayer-insulating film 3. The other specific insulating film is an HSQ film, a polymethyl siloxane film and methyl silsesquioxane (abbreviated to MSQ hereinafter), etc.
Next, as shown in
A TaN layer and then a Cu layer are deposited on the second interlayer-insulating film 11, the first contact holes and the second wiring grooves. Unnecessary Cu and TaN layers are removed by CMP until the second interlayer-insulating film 11 is exposed at the device surface, thus forming the second wiring layer 10 having the second wiring 9a and the first plug 9b. The second interlayer-insulating film 11 is a TEOS film.
Next, as shown in
Next, as shown in
Next, as shown in
The porous insulating film 12a changed from the third interlayer-insulating film 12 is polished and removed to flatten the device surface by CMP until the second interlayer-insulating film 10 is exposed at the device surface, as shown in
The process of flattening the third interlayer-insulating film may be performed to the third interlayer-insulating film 12 before the thermal process or to the porous insulating film 12a after the thermal process. In detail, the third interlayer-insulating film 12 may be flattened just after deposited in
This modification to the second embodiment forms the porous insulating film after the second wiring 10 has been formed, thus requiring no processes such as lithography and RIE to the porous insulating film, hence causing no damages and harmful effects to the porous insulating film.
Low-dielectric-constant insulating films such as porous insulating films could suffer cracks, etc., due to their low mechanical strength, against stresses applied in a vertical direction (a direction almost orthogonal to the horizontal plane of the insulating films during packaging process such as bonding.
As disclosed, the second embodiment forms the second insulating film 11 of mechanical strength relatively higher than those of low dielectric constant under the second wiring 9a, to enhance relative mechanical strength for the interlayer-insulating film for avoiding adverse effects such as cracks.
Disclosed next with reference to
As shown in
A TaN film and then a Cu layer are deposited on the grooves for prevention of Cu dispersion and oxidation. Unnecessary Cu layer and TaN film are polished and removed by CMP until the first interlayer-insulating film 3 is exposed at the device surface.
A barrier insulating film 13 as a barrier film is formed on the first interlayer-insulating film 3. The barrier insulating film 13 protects the first Cu wiring against Cu dispersion and oxidation, and also the first interlayer-insulating film against any effects which may otherwise be caused due to formation of upper interlayer-insulating films in later processes.
Next, as shown in
The second interlayer-insulating film 11 and the barrier insulating film 13 are processed with lithography and RIE to provide the first contact holes and the second wiring grooves simultaneously.
A TaN layer and then a Cu layer are deposited on the second interlayer-insulating film 11, the first contact holes and the second wiring grooves. Unnecessary Cu and TaN layers are removed by CMP until the second interlayer-insulating film 11 is exposed at the device surface, thus forming the second wiring layer 10 having the second wiring 9a and the first plug 9b.
Next, as shown in
Next, as shown in
Next, as shown in
The porous insulating film 12a changed from the third interlayer-insulating film 12 is polished and removed to flatten the device surface by CMP until the second interlayer-insulating film 10 is exposed at the device surface, as shown in
The process of flattening the porous insulating film 12a as the third interlayer-insulating film may be performed to the third film before changed into the porous insulating film 12a. In detail, the third interlayer-insulating film 12 may be flattened just after deposited in
Like the second embodiment, the third embodiment forms the porous insulating film after the second wiring 10 has been formed, thus requiring no processes such as lithography and RIE to the porous insulating film, hence causing no damages and harmful effects to the porous insulating film.
Disclosed next with reference to
The processes for forming the first wiring layer 6 are the same as shown in
As shown in
Next, as shown in
A TaN layer and then a Cu layer are deposited on the first contact holes and the second wiring grooves. Unnecessary Cu and TaN layers are removed by CMP, thus forming the second wiring layer 10 having the second wiring 9a and the first plug 9b.
Next, as shown in
Next, as shown in
Next, as shown in
The porous insulating film 17a as the fourth interlayer-insulating film 17 is polished and removed to flatten the device surface by CMP until the second wiring 9a is exposed at the device surface, as shown in
The process of flattening the porous insulating film 17a as the fourth interlayer-insulating film may be performed before the thermal process to form the porous insulating film 17a. In detail, the fourth interlayer-insulating film 17 may be flattened just after deposited in
Like the first and second embodiments, the fourth embodiment forms the porous insulating film after the second wiring 10 has been formed, thus requiring no processes such as lithography and RIE to the porous insulating film, hence causing no damages to the porous insulating film.
Moreover, the fourth embodiment provides the insulating film, of higher mechanical strength than the porous insulating film, between the first wiring 6 and the second wiring 9a, hence achieving an excellent device property against vertically applied stresses.
In the foregoing, a porous insulating film is used for the second interlayer-insulating film in the first embodiment, the third interlayer-insulating film in the second and third embodiments and also the fourth interlayer-insulating film in the fourth embodiment.
Not only that, however, the present invention can use an organic material-applied insulating film such as methyl siloxane for those interlayer-insulating films, instead of a porous insulating film.
Disclosed next with reference to
The production method in the fifth embodiment corresponds to the fourth embodiment providing the barrier film 15 with additional processes of removing the second interlayer-insulating film 11 with the second wiring 9a as a mask by RIE until the barrier insulating film 13 is exposed at the device surface, like the third embodiment.
Like the second and third embodiments, the fifth embodiment protects the second wiring 9a by removing the second interlayer-insulating film 11 after an insulating film of SiN, etc., is formed on the wiring 9a. Therefore, the processes in
The fifth embodiment employs an etchant different from the one used in the fourth embodiment for etching the device surface to reach the upper surfaces of the first interlayer-insulating film 3 and the first wiring 5, the remaining un-etched portion corresponding to the widths of the wiring 9 and the metal 8.
The posterior processes shown in
The methods of producing a semiconductor device having a plurality of wiring layers in the second to fifth embodiments offer no protection against etching on the second wiring 9 and the barrier metal 8.
Not only these embodiments, the present invention employs a cap layer 18 to protect the second wiring 9 and the barrier metal 8 against etching according to sixth to ninth embodiments shown in
The sixth embodiment shown in
The cap layer 18 may be a CVD-SiN film or an SiC film, which is a hard mask functioning to protect the wiring 9 against etching damages. The cap layer 18 remains on the wiring 9 for the posterior processes, which will be buried during integration, thus requiring no peeling-off process, for example.
The seventh embodiment shown in
The eighth embodiment shown in
The ninth embodiment shown in
The first to ninth embodiments for the methods of producing semiconductor device focus on the processes for the second wiring-layer structure. Not only that, however, the first to ninth embodiments can be applied to the first wiring-layer structure and also the third wiring-layer structure or more, for achieving multi-layered wiring structure having low-dielectric-constant insulating films by laminating wiring layers each made according to the present invention.
Shown in
These embodiments show a three-layer wiring structure as a modification of multi-layered wiring structure to the two-layer structure in the first to ninth embodiments. The tenth embodiment corresponds to the first embodiment. The eleventh to eighteenth embodiments correspond to the second to ninth embodiments, respectively.
In detail, there is the basic construction according to the tenth through eighteenth embodiments, as shown in
Moreover, although not shown, the present invention is applied to an n-th-layer wiring structure (n being an integer of four or more) as a further modification to the two-layer structure.
In detail, a semiconductor device having n-th-layer wiring structure may have the following elements: a first insulating film firstly formed in layer; a first wiring layer having a plurality of wirings, formed on the first insulating film; a second wiring layer having a plurality of wirings, formed on or over the first wiring layer; a second insulating film provided on the first insulating film formed as having a plane surface and the first wiring layer, and formed between adjacent wirings of the second wiring layer, located under the second wiring layer but on the first insulating film and the first wiring layer, at least a part of the second insulating film existing between the first and second wiring layers having a relative dielectric constant lower than a relative dielectric constant of the first insulating film; an (n−1)-th wiring layer having a plurality of wirings, formed on or over the second wiring layer; an (n−1)-th insulating film provided on or over the second insulating film formed as having a plane surface and the second wiring layer, and formed between adjacent wirings of the (n−1)-th wiring layer, located under the (n−1)-th wiring layer but over the second insulating film and the second wiring layer, at least a part of the (n−1)-th insulating film existing between the second and (n−1)-th wiring layers having a relative dielectric constant lower than a relative dielectric constant of the second insulating film; an n-th wiring layer having a plurality of wirings, formed on or over the (n−1)-th wiring layer; a low-dielectric-constant insulating film provided on the (n−1)-th insulating film formed as having a plane surface and the (n−1)-th wiring layer, and formed between adjacent wirings of the n-th wiring layer, located under the n-th wiring layer but on the (n−1)-th insulating film and the (n−1)-th wiring layer, at least a part of the low-dielectric-constant insulating film existing between the (n−1)-th and n-th wiring layers having a relative dielectric constant lower than a relative dielectric constant of the (n−1)-th insulating film.
The first to eighteenth embodiments employ Cu as a wiring metal material. In the present invention, however, Al, Au, Ag and W, etc., can be used as a wiring metal material instead of Cu.
It is further understood by those skilled in the art that the foregoing descriptions are embodiments of the disclosed devices and methods for producing the devices and the various changes and modifications may be made in the invention without departing from the sprit and the scope of the invention as hereinafter claimed.
As disclosed in detail, the invention of the semiconductor device and the method of producing the semiconductor device offers several types of multi-layered wiring structures with no processes such as RIE to interlayer-insulating films made of an insulating film of a low dielectric constant, such as an organic material-applied insulating film and a porous insulating film, thus achieving excellent devices properties with low dielectric constant.
Number | Date | Country | Kind |
---|---|---|---|
2001-177005 | Jun 2001 | JP | national |
This application is a divisional application of U.S. patent application Ser. No. 11/565,530, filed on Nov. 30, 2006, which is a divisional and claims the benefit of priority under 35 U.S.C. §120 from U.S. application Ser. No. 10/166,757, filed Jun. 12, 2002, and claims the benefit of priority under 35 U.S.C. § 119 of Japanese Patent Application No. 2001-177005, filed on Jun. 12, 2001. The entire contents of these applications are incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
Parent | 11565530 | Nov 2006 | US |
Child | 12501839 | US | |
Parent | 10166757 | Jun 2002 | US |
Child | 11565530 | US |