Patent Grant
9076786
1. Field of the Invention
The present invention relates to a wiring substrate based on a TSV (through-silicon-via) technology and a manufacturing method therefor. More particularly, it relates to a wiring substrate based on a narrow-pitch TSV technology and a manufacturing method therefor.
2. Description of the Related Art
In order to realize a three-dimensional wiring substrate based on a TSV (through-silicon-via) technology, through electrodes have to be electrically insulated from a silicon substrate. As a means for electrical insulation, Japanese Unexamined Patent Application Publication No. 2008-251964 discloses a technology of providing a ring-shaped isolation groove passing through a silicon substrate and surrounding a through electrode, forming silicon films directly on bottom and side faces of the isolation groove, forming an insulation film on the silicon films so as to fill a space left in the isolation groove, and then thermally oxidizing the surface of the silicon films in contact with inner and outer peripheral side faces of the isolation groove so as to form a thermally oxidized silicon film.
However, since a sufficiently thick insulation film is difficult to form, a metallic component constituting the through electrode, e.g., Cu may be dispersed in the silicon oxide film and the silicon substrate, impairing the electrical insulating properties. Also, cracks may be formed in the insulation film, impairing the insulating properties.
Japanese Patent No. 5225479 discloses a technology effective in solving the above-described problems. The wiring substrate manufacturing method disclosed in Japanese Patent No. 5225479 includes an insulating layer formation process and a columnar conductor formation process. In the insulating layer formation process, a hole or groove is formed in a semiconductor substrate along its thickness direction and an insulating layer is formed in the hole or groove. In the columnar conductor formation process, a hole or groove is formed in a region surrounded by the insulating layer and a vertical columnar conductor containing a metal/alloy component is formed in the hole or groove.
According to the technology disclosed in Japanese Patent No. 5225479, it is possible to produce an insulator having excellent physical and chemical strength, a reliable insulator free from defects such as a gap, a void or a crack, and an insulator having various electrical properties.
However, Japanese Patent No. 5225479 does not disclose a narrow-pitch TSV technology, i.e., technology of forming a lot of vertical columnar conductors at a narrow pitch. When the arrangement pitch of the vertical columnar conductors is equal to or less than 4 μm, for example, even a slight misalignment of grooves or holes, in which the vertical columnar conductors are to be formed, may easily cause a failure such as poor connection. Japanese Patent No. 5225479 fails to disclose a means for preventing the occurrence of such a failure.
When TSVs are formed at a narrow pitch, moreover, the cross sectional area of columns to be used for supporting the vertical columnar conductors or insulators during the manufacturing process becomes too small, which may cause various failures during the manufacturing process, e.g., breakage of columns, misalignment of columns, or contact between columns. Japanese Patent No. 5225479 also fails to disclose a means for preventing the occurrence of such a failure.
It is an object of the present invention to provide a narrow-pitch TSV wiring substrate and a manufacturing method therefor.
It is another object of the present invention to provide a wiring substrate manufacturing method suitable for forming TSVs at a narrow pitch.
It is still another object of the present invention to provide a wiring substrate manufacturing method which can reduce the risk of various failures that may occur when a narrow pitch results in decreasing the cross sectional area of columns to be used for supporting insulators or columnar conductors, e.g., breakage of columns, misalignment of columns, or contact between columns.
In order to attain at least one of the above objects, a wiring substrate according to the present invention comprises a semiconductor substrate, an insulator and a plurality of columnar conductors. The insulator is made of an insulating material filled in a groove or hole provided in the semiconductor substrate. The plurality of columnar conductors are filled in grooves or holes provided in the insulator, the grooves or holes being arranged at a narrow pitch in a plane of the insulator. The insulating material has a Si—O bond obtained by reacting Si particles with an organic Si compound.
In the wiring substrate according to the present invention, as described above, the insulator is made of an insulating material filled in a groove or hole formed in the semiconductor substrate along a thickness direction thereof. Thus, the insulator is integrated with the semiconductor substrate (e.g., Si substrate).
The columnar conductors are filled in minute spaces extending in the thickness direction of the insulator integrated with the semiconductor substrate (e.g., Si substrate), the minute spaces being arranged at a narrow pitch in a plane of the insulator. This means that the individual columnar conductors are electrically insulated not only from each other but also from the semiconductor substrate by a common, single insulator. As compared with the case where a plurality of columnar conductors are arranged in a semiconductor substrate in a separately electrically insulated state (e.g., Japanese Patent No. 5225479), such an electrical insulation structure can greatly reduce the pitch distance between columnar conductors. According to the present invention, therefore, there can be realized a narrow-pitch TSV wiring substrate.
The wiring substrate according to the present invention may include an electronic element. Examples of such electronic elements include a wiring conductor, a wiring substrate and an electronic component, a conductive part of which is at least partially diffusion bonded to at least one of opposite ends of the columnar conductor. With this diffusion bonding, there can be realized a bonding structure having a high bonding strength and high heat resistance. Particularly when the conductive part of the electronic element is thermally diffusion bonded with a nanocomposite brazing alloy or nanocomposite particles, excellent thermal diffusion bond can be formed by a homogeneous disperse system composed of a few kinds of metal/alloy components, oxides, silicides, sulfides, etc. constituting the nanocomposite structure.
A method for manufacturing the foregoing wiring substrate according to the present invention comprises:
leaving a plurality of spaced columns of the semiconductor substrate in the insulator embedded in the semiconductor substrate; and
removing the columns and filling the columnar conductors in resulting vacant spaces.
According to the present invention, as described above, since the spaced columns existing in the insulator embedded in the semiconductor substrate are removed and the columnar conductors are then filled in the resulting vacant spaces, the resulting vacant spaces (minute spaces) to be filled with the columnar conductors are surrounded and defined by the insulator and therefore prevented from varying in width and position. Therefore, TSVs can be certainly formed at a narrow pitch.
Furthermore, since the TSV technology is, as its name says, the art of forming electrically insulated vertical columnar conductors (through electrodes) in a semiconductor substrate such as silicon substrate, the spaced columns inside the insulator are made of the semiconductor substrate such as silicon substrate. Therefore, the columns can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate such as silicon substrate. Thus, the vacant spaces to be filled with columnar conductors and therefore the columnar conductors can be easily, quickly and certainly formed.
Preferably, the wiring substrate manufacturing method according to the present invention includes: forming a plurality of spaced grooves or holes in the semiconductor substrate; and filling a fluid insulating material into the groove or holes and hardening it to form the insulator, wherein at the fluid insulating material-filling step, the columns are supported in contact with the semiconductor substrate or the hardened insulator.
As described above, the formation of TSVs at a narrow pitch, e.g., equal to or less than 4 μm, results in decreasing the cross sectional area of columns to be used for supporting the columnar conductors or insulators, e.g., equal to or less than 2 μm. Therefore, at the fluid insulating material-filling step, the columns affected by the filling pressure may cause various failures, e.g., breakage of columns, misalignment of columns, or contact between columns.
In the above, since the columns are supported in contact with the semiconductor substrate or the hardened insulator at the fluid insulating material-filling step, the mechanical strength of the columns can be increased to reduce the risk of various failures, e.g., breakage of columns, misalignment of columns, or contact between columns.
The fluid insulating material is preferably an insulating paste containing insulating particles, Si particles and an organic Si compound.
According to the present invention, as understood from above, the following advantages can be obtained.
The present invention will be more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus not to be considered as limiting the present invention.
1. Wiring Substrate
The insulator 5 is filled in a minute space 121 formed in one surface 111 of the semiconductor substrate 1. Preferably, the insulator 5 is formed such that an insulating paste containing insulating particles, Si particles and a liquid organic Si compound is filled into a groove or hole (also referred to as minute space) 121 formed in the semiconductor substrate 1 along its thickness direction and then hardened. When the insulating paste filled in the minute space 121 is heat treated, the Si particles and the organic Si compound react with each other to form a Si—O bond, thereby providing an insulation structure in which the insulating particles serve as an aggregate with the Si—O bond filling up the space around the insulating particles. The insulating particles and the Si particles have a particle size of nanometer order (equal to or less than 1 μm). However, the insulating particles and the Si particles are not required to have a uniform particle size but may have various particle sizes within the nanometer range.
The columnar conductors 311 to 326 extend in the direction of the thickness T1 of the semiconductor substrate 1 to have one end appearing on one surface 111 of the semiconductor substrate 1. The columnar conductors 311 to 326 may be a columnar through conductor, the other end of which appears on a bottom surface 112 of the semiconductor substrate 1, or a columnar non-through conductor, the other end of which remains in the semiconductor substrate 1. In this embodiment, the columnar conductors 311 to 326 have a rectangular cross-section, but may have other polygonal shapes or a circular shape. Moreover, although they are arranged in a matrix with 4 rows and 4 columns, the number of rows and columns may arbitrary. The columnar conductors 311 to 326 may be formed by applying a known technology such as a plating process, a molten metal filling process or a conductive paste filling process. For example, the dimensions regarding the columnar conductors 311 to 326 are such that the arrangement pitch d1, d2 is in the range of 4 to 100 μm and the width is in the range of 0.5 to 25 μm. However, the arrangement pitch is not required to be a certain size, and the width is not limited to the above value either.
In the wiring substrate according to the present invention, as described above, the insulator 5 is made of an insulating material filled in the minute space 121 such as groove or hole formed in the semiconductor substrate 1 along the thickness direction. Thus, the insulator 5 is integrated with the semiconductor substrate 1 such as Si substrate.
The columnar conductors 311 to 326 are filled in minute spaces (e.g., grooves or holes) extending in the thickness direction of the insulator 5 integrated with the semiconductor substrate (e.g., Si substrate), the minute spaces being arranged at a narrow pitch d1, d2 in a plane of the insulator 5. This means that the individual columnar conductors 311 to 326 are supported together and electrically insulated not only from each other but also from the semiconductor substrate 1 by the single insulator 5. As compared with the case where a plurality of columnar conductors 311 to 326 are arranged in a semiconductor substrate 1 in a separately electrically insulated state (e.g., Japanese Patent No. 5225479), such an electrical insulation structure can greatly reduce the pitch d1, d2 between columnar conductors, e.g., to 4 μm or less. According to the present invention, therefore, there can be realized a narrow-pitch TSV wiring substrate.
The columnar conductors 311 to 326 contains at least one element selected from the group consisting of Ag, Cu, Au, Pt, Ti, Zn, Al, Fe, B, Si and Ni and at least one element selected from the group consisting of Sn, In, Bi and Ga. The first group consists of high melting point metal materials, while the second group consists of low melting point metal materials.
The number, shape and arrangement of the columnar conductors 311 to 326 may be arbitrarily determined in view of various factors, such as proper signal transmission paths and electrical properties required for signal transmission paths. Specific examples are shown in
On the other hand,
In the above, since the columnar conductors 311 to 318 are filled in the regions surrounded by the hardened insulators (511 to 516) and (521 to 524), TSVs can be certainly formed at a narrow pitch without varying in width and position.
The wiring substrate according to the present invention may be combined with an electronic element. Examples of such electronic elements include a wiring conductor, a wiring substrate and an electronic component, a conductive part of which is at least partially diffusion bonded to at least one of opposite ends of the columnar conductor. Specific examples are shown in
Referring first to
On the other hand,
The electronic component A may be an active element or a passive element. Typically, such an active element may be a system LSI, a memory LSI, an image sensor, a MEMS in the form of a three-dimensional system-in-package (3D-SiP). It may also be an electronic device including an analog or digital circuit, a memory circuit such as DRAM, a logic circuit such as CPU or the like or an electronic equipment that is obtained by preparing different types of circuits such as an analog high frequency circuit and a low frequency, low power consumption circuit in different processes and stacking them.
Moreover, it includes most of electronic equipments or devices having an electronic circuit as a functional element, such as a sensor module, an optoelectronic module, a unipolar transistor, a MOS FET, a CMOS FET, a memory cell, integrated circuits (IC) thereof, or various scales of LSIs. In the present invention, integrated circuits called “LSI” include all types of integrated circuits such as a small-scale integration, a medium-scale integration, a large-scale integration, a very-large-scale integration (VLSI), an ultra-large-scale integration (ULSI), and so on.
The wiring substrate B may be of the type shown in
In the various types of wiring substrates described above, the type of the semiconductor substrate 1 and the shape, arrangement and width of the columnar conductors may be different from those described in this specification. Even then, as long as the structure of the insulator and the relationship of the insulator to the columnar conductors satisfy the requirements, the wiring substrate is included in the scope of the present invention.
2. Method for Manufacturing Wiring Substrate
Hereinbelow, a method for manufacturing the wiring substrate shown in
Then, as shown in
Through the cut-out patterns 711 to 726 of the mask 7, the columns 131 to 146 are deeply etched by a known technology such as a CVD process or a laser drilling process.
Then, as shown in
The columnar conductors 311 to 326 can be formed by applying a known technology such as a plating process, a molten metal filling process or a conductive paste filling process. Among them, the molten metal filling process is preferred from the viewpoint of forming high quality conductors and reducing the production cost. Examples of metal or alloy for use in the molten metal filling process include high melting point metal materials and low melting point metal materials produced with nanocomposite metal/alloy particles.
As described above, since the spaced columns 131 to 146 existing in the insulator 5 embedded in the semiconductor substrate 1 are removed, the resulting vacant spaces (minute spaces 151 to 166) to be filled with the columnar conductors 311 to 326 are surrounded and defined by the insulator 5 and therefore prevented from varying in width and position. Therefore, TSVs can be certainly formed at a narrow pitch.
Furthermore, since the TSV technology is, as its name says, the art of forming electrically insulated columnar conductors (through electrodes) in a semiconductor substrate such as silicon substrate, the spaced columns 131 to 146 inside the insulator 5 are made of the semiconductor substrate 1 such as silicon substrate. Therefore, the columns 131 to 146 can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate 1 such as silicon substrate, for example, a known technology such as a CVD process or a laser drilling process. Thus, the minute spaces 151 to 166 to be filled with the columnar conductors 311 to 326 and therefore the columnar conductors 311 to 326 can be easily, quickly and certainly formed.
Another method for manufacturing the wiring substrate according to the present invention will be described with reference to
Between the minute spaces 121 to 124, there are left long and narrow columns 101 to 103 of the semiconductor substrate 1. These columns 101 to 103 are supported with their opposite ends in the length direction being continuous with the rest of the semiconductor substrate 1.
Then, as shown in
The fluid insulating material is preferably an insulating paste containing insulating particles, Si particles and an organic Si compound. It is also possible to pour a liquid organic Si compound after the insulating particles and the Si particles are put in the minute spaces. In order to harden the fluid insulating material filled in the minute spaces 121 to 124 for formation of the insulators 511 to 514, the organic Si compound is reacted with the Si particles to form the Si—O bond network filling up the space around the insulating particles. Preferably, the reaction between the organic Si compound and the Si particles is allowed to proceed under vacuum while being heated, for example, within a temperature range of 130° C. to 150° C. Thus, the insulators 511 to 514 can be formed. Organic substances resulting from the reaction can be thermally decomposed and discharged as a gas.
The insulators 511 to 514 have a structure in which the space around the insulating particles is completely filled up with the Si—O bond network, more specifically, amorphous silica (SiO2).
More preferably, heating is performed such that the fluid insulating material filled in the minute spaces 121 to 124 is heated under pressure and then cooled under pressure. This process further accelerates the thermal decomposition of the organic substances and also increases the density of the insulators 511 to 514, improving the adhesion to the semiconductor substrate 1.
By performing the above process, the insulators 511 to 514 with excellent physical and chemical strength can be formed in the minute spaces 121 to 124.
Moreover, the Si—O bond filling up the space around the insulating particles, more specifically, the amorphous silica (SiO2) can be formed by reacting the organic Si compound with the Si particles. That is, since the formation of the oxide from the Si particles increases the volume, a reliable insulator can be formed in the minute space, which is free from defects such as a gap, a void or a crack and has a high adhesion strength to the side wall of the minute space. It should be noted that the volume of the SiO2 increases by about 30 to 35% from that of the Si particles. This corresponds to the shrinkage ratio of the Si particles, preventing the formation of a void, a gap or a crack due to the shrinkage.
Furthermore, since the fluid insulating material according to the present invention contains the insulating particles, the insulator can be provided with various electrical properties based on the properties of the insulating particles. Basically, the insulating particles are metal oxide particles (ceramic). For instance, when the insulating particles comprise a ferroelectric material such as barium titanate, the insulator can be provided with a large capacitance; when the insulating particles comprise a low dielectric material such as SiO2 or Al2O3, the insulator can be provided with a small capacitance.
A typical example of the organic Si compound to be used in the present invention is alkylalkoxysilane represented by the formula:
CH3O—[SinOn-1(CH3)n(OCH3)n]—CH3.
In this case, the reaction formula is as follows.
Si+CH3O—[SinOn-1(CH3)n(OCH3)n]—CH3→SiO2+(C,H,O)↑ (1)
When the semiconductor substrate 1 having the minute spaces 121 to 124 is a Si semiconductor substrate, the above reaction also occurs with Si of the Si semiconductor substrate. Alternatively, it is also possible to use organopolysiloxane (alkoxysilane having a functional side chain).
The Si particles may be formed by heat treating a silicon oil put in the minutes spaces 121 to 124. The silicon oil may be dimethylpolysiloxane (C2H6OSi)n.
Then, as shown in
Through the cut-out patterns 711 to 725 of the mask 7, the semiconductor substrate 1 is deeply etched by a known technology such as a CVD process or a laser drilling process.
Then, as shown in
At this point, the columns 131 to 146 are supported with their side faces in contact with the hardened insulators 511 to 514. In the process of filling a fluid insulating material into the minute spaces 151 to 165, therefore, even though a narrow pitch, e.g., equal to or less than 4 μm, results in decreasing the cross sectional area of the columns 131 to 146, it is possible to reduce the risk of various failures, e.g., breakage of the columns 131 to 146, misalignment of the columns 131 to 146, or contact between the columns 131 to 146.
Then, a mask is placed on the surface 111 of the semiconductor substrate 1, and the semiconductor substrate 1 is deeply etched through cut-out patterns of the mask by a known technology such as a CVD process or a laser drilling process (see
Then, as shown in
In the above, since the columnar conductors 311 to 326 are filled in the minute spaces 151 to 166 surrounded by the insulators 511 to 514, 521 to 535, TSVs can be certainly formed at a narrow pitch without varying in width and position.
Furthermore, the spaced columns 131 to 146 left in the insulator 5 are made of the semiconductor substrate 1 such as silicon substrate. Therefore, the columns 131 to 146 can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate 1 such as silicon substrate, for example, a known technology such as a CVD process or a laser drilling process. Thus, the minute spaces 151 to 166 to be filled with the columnar conductors 311 to 326 and therefore the columnar conductors 311 to 326 can be easily, quickly and certainly formed.
Further description will be made with reference to
Then, as shown in
Then, as shown in
In the process of forming the insulators 521 to 525, the columns 131 to 146 are supported with their side faces in contact with the insulators 511 to 514. Therefore, even though a narrow pitch, e.g., equal to or less than 4 μm, results in decreasing the cross sectional area of the columns 131 to 146, it is possible to reduce the risk of various failures, e.g., breakage of the columns 131 to 146, misalignment of the columns 131 to 146, or contact between the columns 131 to 146.
Then, as shown in
Furthermore, the columns 131 to 146 can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate 1 such as silicon substrate, for example, a known technology such as a CVD process or a laser drilling process. Thus, the minute spaces 151 to 166 to be filled with the columnar conductors 311 to 326 and therefore the columnar conductors 311 to 326 can be easily, quickly and certainly formed.
Hereinbelow, another embodiment will be described with reference to
The resist mask 71 has a cut-out pattern that is a combination of a plurality of longitudinal patterns 711 to 713 and a plurality of lateral patterns 714 to 716 and rectangular mask patterns 701 to 704 surrounded by the longitudinal patterns 711 to 713 and the lateral patterns 714 to 716. The number of the longitudinal patterns 711 to 713 and the lateral patterns 714 to 716 may be arbitrary.
As described above, after the minute spaces are formed according to the cut-out patterns 711 to 716 of the resist mask 71, the insulators 511 to 516 are formed by hardening the fluid insulating material filled into the minute spaces. In this case, the insulators 511 to 516 are formed according to the cut-out patterns 711 to 716 of the resist mask 71, while rectangular columns 101 to 104 are formed surrounded by longitudinal patterns 511 to 513 and lateral patterns 514 to 516 constituting the insulators 511 to 516.
Then, as shown in
Since deep etching according to the cut-out patterns 721 to 724 of the resist mask 72 does not scrape off the insulators 511 to 516, the insulators 511 to 516 (filled regions) can be prevented from being damaged by deep etching in the process of forming the minute spaces according to the cut-out patterns 721 to 724.
Then, as shown in
In the process of forming the insulators 521 to 524, the columns 131 to 146 are supported with their side faces in contact with the insulators 511 to 516. Therefore, even though a narrow pitch, e.g., equal to or less than 4 μm, results in decreasing the cross sectional area of the columns 131 to 146, it is possible to reduce the risk of various failures, e.g., breakage of the columns 131 to 146, misalignment of the columns 131 to 146, or contact between the columns 131 to 146.
Then, as shown in
Furthermore, the columns 131 to 146 can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate 1 such as silicon substrate, for example, a known technology such as a CVD process or a laser drilling process. Thus, the minute spaces 151 to 166 to be filled with the columnar conductors 311 to 326 and therefore the columnar conductors 311 to 326 can be easily, quickly and certainly formed.
3. Other Embodiments
The resist mask 71 has a pair of cut-out patterns (711, 717), a common cut-out pattern 712, a pair of cut-out patterns (713, 718), a pair of cut-out patterns (714, 719), a common cut-out pattern 715 and a pair of cut-out patterns (716, 720). They are arranged at intervals in the longitudinal direction (from top to bottom in the drawing).
Then, as shown in
Then, as shown in
In the process of forming the insulators 521 to 524, the columns 131 to 138 are supported with their side faces in contact with the insulators 511 to 520. Therefore, even though a narrow pitch results in decreasing the cross sectional area of the columns 131 to 138, it is possible to reduce the risk of various failures, e.g., breakage of the columns 131 to 138, misalignment of the columns 131 to 138, or contact between the columns 131 to 138.
Then, as shown in
In the above, since the columnar conductors 311 to 318 are filled in the minute spaces 151 to 158 surrounded by the hardened insulator 5, TSVs can be certainly formed at a narrow pitch without varying in width and position.
Furthermore, the columns 131 to 138 can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate 1 such as silicon substrate, for example, a known technology such as a CVD process or a laser drilling process. Thus, the minute spaces 151 to 158 to be filled with the columnar conductors 311 to 138 and therefore the columnar conductors 311 to 138 can be easily, quickly and certainly formed.
On the other hand,
The resist mask 71 has a cut-out pattern that is a combination of a plurality of longitudinal patterns 711 to 713 and a plurality of lateral patterns 714 to 716 and rectangular mask patterns 701 to 704 surrounded by the longitudinal patterns 711 to 713 and the lateral patterns 714 to 716. The number of the longitudinal patterns and the lateral patterns may be arbitrary.
As described above, after the minute spaces are formed according to the cut-out patterns 711 to 716 of the resist mask 71, the insulators 511 to 516 are formed by hardening the fluid insulating material filled into the minute spaces. In this case, the insulators 511 to 516 are formed according to the cut-out patterns 711 to 716 of the resist mask 71, while rectangular columns 101 to 104 are formed surrounded by longitudinal patterns 511 to 513 and lateral patterns 514 to 516.
Then, as shown in
Since deep etching according to the cut-out patterns 721 to 724 of the resist mask 72 does not scrape off the insulators 511 to 516, the insulators 511 to 516 (filled regions) can be prevented from being damaged by deep etching in the process of forming the minute spaces according to the cut-out patterns 721 to 724.
Then, as shown in
In the process of forming the insulators 521 to 524, the two columns (1011, 1012) to (1041, 1042) of the individual rectangular columns 101 to 104 are supported with their side faces in contact with the insulators 511 to 516. Therefore, even though a narrow pitch results in decreasing the cross sectional area of the columns, it is possible to reduce the risk of various failures, e.g., breakage of the columns (1011, 1012) to (1041, 1042), misalignment of the columns (1011, 1012) to (1041, 1042), or contact between the columns (1011, 1012) to (1041, 1042).
Then, as shown in
In the above, since the columnar conductors 311 to 318 are filled in the minute spaces 151 to 158 surrounded by the hardened insulator 5, TSVs can be certainly formed at a narrow pitch without varying in width and position.
Furthermore, the columns (1011, 1012) to (1041, 1042) can be easily, quickly and certainly removed by an etching technology that has been used on the semiconductor substrate 1 such as silicon substrate, for example, a known technology such as a CVD process or a laser drilling process. Thus, the minute spaces 151 to 158 to be filled with the columnar conductors 311 to 138 and therefore the columnar conductors 311 to 138 can be easily, quickly and certainly formed.
Although not described herein, wiring substrates combined with an electronic element as shown in
The present invention is applicable to various types of electronic equipments or devices so as to form TSVs in a semiconductor substrate at a narrow pitch. Typically, such an electronic device can take the form of a three-dimensional system-in-package (3D-SiP). Specifically, it may be a system LSI, a memory LSI, an image sensor, a MEMS or the like. It may also be an electronic device including an analog or digital circuit, a memory circuit such as DRAM, a logic circuit such as CPU or the like or an electronic equipment that is obtained by preparing different types of circuits such as an analog high frequency circuit and a low frequency, low power consumption circuit in different processes and stacking them.
More specifically, it includes most of electronic equipments or devices having an electronic circuit as a functional element, such as a sensor module, an optoelectronic module, a unipolar transistor, a MOS FET, a CMOS FET, a memory cell, integrated circuits (IC) thereof, or various scales of LSIs. In the present invention, integrated circuits called “LSI” include all types of integrated circuits such as a small-scale integration, a medium-scale integration, a large-scale integration, a very-large-scale integration (VLSI), an ultra-large-scale integration (ULSI), and so on.
In the various types of electronic equipments or devices described above, the type of the semiconductor substrate 1 and the shape, arrangement and width of the vertical columnar conductors passing through the semiconductor substrate may be different from those described in this specification. Even then, as long as the structure of the insulator and the relationship of the insulator to the vertical columnar conductors satisfy the requirements, the electronic equipment or device is included in the scope of the present invention.
While the present invention has been particularly shown and described with respect to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit, scope and teaching of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-165314 | Aug 2013 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20060118965 | Matsui | Jun 2006 | A1 |
| 20080237781 | Uchiyama | Oct 2008 | A1 |
| 20090212438 | Kreupl et al. | Aug 2009 | A1 |
| 20100301485 | Sekine et al. | Dec 2010 | A1 |
| 20110140281 | Sekine et al. | Jun 2011 | A1 |
| 20120091481 | Sekine et al. | Apr 2012 | A1 |
| 20120133710 | Joyner et al. | May 2012 | A1 |
| 20130075930 | Sekine et al. | Mar 2013 | A1 |
| 20130207241 | Lee et al. | Aug 2013 | A1 |
| 20130207242 | Lee et al. | Aug 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 743 937 | Jun 2014 | EP |
| 2006-165025 | Jun 2006 | JP |
| 2008-251964 | Oct 2008 | JP |
| 2009-111063 | May 2009 | JP |
| 2011-23497 | Feb 2011 | JP |
| 5225479 | Jul 2013 | JP |
| Entry |
|---|
| Extended European Search Report dated Dec. 9, 2014, issued in European Patent Application No. 14179882.7 (7 pages). |
| Number | Date | Country | |
|---|---|---|---|
| 20150041990 A1 | Feb 2015 | US |