The present invention relates to the manufacture of substrates. More particularly, the invention provides a technique including a method and device for cleaving a substrate in the fabrication of a silicon-on-insulator substrate for semiconductor integrated circuits, for example. But it will be recognized that the invention has a wider range of applicability; it can also be applied to other substrates for multi-layered integrated circuit devices, three-dimensional packaging of integrated semiconductor devices, photonic devices, piezoelectronic devices, microelectromechanical systems (“MEMS”), sensors, actuators, solar cells, flat panel displays (e.g., LCD, AMLCD), biological and biomedical devices, and the like.
Craftsmen or more properly crafts-people have been building useful articles, tools, or devices using less useful materials for numerous years. In some cases, articles are assembled by way of smaller elements or building blocks. Alternatively, less useful articles are separated into smaller pieces to improve their utility. A common example of these articles to be separated include substrate structures, such as a glass plate, a diamond, a semiconductor substrate, and others.
These substrate structures are often cleaved or separated using a variety of techniques. In some cases, the substrates can be separated using a saw operation. The saw operation generally relies upon a rotating blade or tool, which cuts through the substrate material to separate the substrate material into two pieces. This technique, however, is often extremely “rough” and cannot generally be used for providing precision separations in the substrate for the manufacture of fine tools and assemblies. Additionally, the saw operation often has difficulty separating or cutting extremely hard and/or brittle materials, such as diamond or glass.
Accordingly, techniques have been developed to separate these hard and/or brittle materials using cleaving approaches. In diamond cutting, for example, an intense directional thermal/mechanical impulse is directed preferentially along a crystallographic plane of a diamond material. This thermal/mechanical impulse generally causes a cleave front to propagate along major crystallographic planes, where cleaving occurs when an energy level from the thermal/mechanical impulse exceeds the fracture energy level along the chosen crystallographic plane.
In glass cutting, a scribe line using a tool is often impressed in a preferred direction on the glass material, which is generally amorphous in character. The scribe line causes a higher stress area surrounding the amorphous glass material. Mechanical force is placed on each side of the scribe line, which increases stress along the scribe line until the glass material fractures, preferably along the scribe line. This fracture completes the cleaving process of the glass, which can be used in a variety of applications, including households.
Although the techniques described above are satisfactory, for the most part, as applied to cutting diamonds or household glass, they have severe limitations in the fabrication of small complex structures or precision workpieces. For instance, the above techniques are often “rough” and cannot be used with great precision in fabrication of small and delicate machine tools, electronic devices, or the like. Additionally, the above techniques may be useful for separating one large plane of glass from another, but are often ineffective for splitting off, shaving, or stripping a thin film of material from a larger substrate. Furthermore, the above techniques may often cause more than one cleave front, which join along slightly different planes, which is highly undesirable for precision cutting applications.
From the above, it is seen that a technique for separating a thin film of material from a substrate which is cost effective and efficient is desirable.
According to the present invention, an improved technique for removing a thin film of material from a substrate using a controlled cleaving action is provided. This technique allows an initiation of a cleaving process on a substrate using a single or multiple cleave region(s) through the use of controlled energy (e.g., spatial distribution) and selected conditions to allow an initiation of a cleave front(s) and to allow it to propagate through the substrate to remove a thin film of material from the substrate.
In a specific embodiment, the present invention provides a process for forming a film of material from a donor substrate using a controlled cleaving process. The process includes a step of introducing energetic particles (e.g., charged or neutral molecules, atoms, or electrons having sufficient kinetic energy) through a surface of a donor substrate to a selected depth underneath the surface, where the particles are at a relatively high concentration to define a thickness of donor substrate material (e.g., thin film of detachable material) above the selected depth. To cleave the donor substrate material, the method provides energy to a selected region of the donor substrate to initiate a controlled cleaving action in the donor substrate, whereupon the cleaving action is made using a propagating cleave front(s) to free the donor material from a remaining portion of the donor substrate.
In most of the embodiments, a cleave is initiated by subjecting the material with sufficient energy to fracture the material in one region, causing a cleave front, without uncontrolled shattering or cracking. The cleave front formation energy (E) must often be made lower than the bulk material fracture energy (Etna) at each region to avoid shattering or cracking the material. The directional energy impulse vector in diamond cutting or the scribe line in glass cutting are, for example, the means in which the cleave energy is reduced to allow the controlled creation and propagation of a cleave front. The cleave front is in itself a higher stress region and once created, its propagation requires a lower energy to further cleave the material from this initial region of fracture. The energy required to propagate the cleave front is called the cleave front propagation energy (4). The relationship can be expressed as:
Ec=Ep+[cleave front stress energy]
A controlled cleaving process is realized by reducing Ep along a favored direction(s) above all others and limiting the available energy to below the Ep of other undesired directions. In any cleave process, a better cleave surface finish occurs when the cleave process occurs through only one expanding cleave front, although multiple cleave fronts do work.
Numerous benefits are achieved over pre-existing techniques using the present invention. In particular, the present invention uses controlled energy and selected conditions to preferentially cleave a thin film of material from a donor substrate which includes multi-material sandwiched films. This cleaving process selectively removes the thin film of material from the substrate while preventing a possibility of damage to the film or a remaining portion of the substrate. Accordingly, the remaining substrate portion can be re-used repeatedly for other applications.
Additionally, the present invention uses a relatively low temperature during the controlled cleaving process of the thin film to reduce temperature excursions of the separated film, donor substrate, or multi-material films according to other embodiments. This lower temperature approach allows for more material and process latitude such as, for example, cleaving and bonding of materials having substantially different thermal expansion coefficients. In other embodiments, the present invention limits energy or stress in the substrate to a value below a cleave initiation energy, which generally removes a possibility of creating random cleave initiation sites or fronts. This reduces cleave damage (e.g., pits, crystalline defects, breakage, cracks, steps, voids, excessive roughness) often caused in pre-existing techniques. Moreover, the present invention reduces damage caused by higher than necessary stress or pressure effects and nucleation sites caused by the energetic particles as compared to pre-existing techniques.
The present invention achieves these benefits and others in the context of known process technology. However, a further understanding of the nature and advantages of the present invention may be realized by reference to the latter portions of the specification and attached drawings.
The present invention provides a technique for removing a thin film of material from a substrate while preventing a possibility of damage to the thin material film and/or a remaining portion of the substrate. The thin film of material is attached to or can be attached to a target substrate to form, for example, a silicon-on-insulator wafer. The thin film of material can also be used for a variety of other applications. The invention will be better understood by reference to the Figs. and the descriptions below.
1. Controlled Cleaving Techniques
Selected energetic particles implant 22 through the top surface 14 of the silicon wafer to a selected depth 24, which defines the thickness 20 of the material region 12, termed the “thin film” of material. A variety of techniques can be used to implant the energetic particles into the silicon wafer. These techniques include ion implantation using, for example, beam line ion implantation equipment manufactured from companies such as Applied Materials, Eaton Corporation, Varian, and others. Alternatively, implantation occurs using a plasma immersion ion implantation (“PIII”) technique. Examples of plasma immersion ion implantation techniques are described in “Recent Applications of Plasma Immersion Ion Implantation,” Paul K. Chu, Chung Chan, and Nathan W. Cheung, SEMICONDUCTOR INTERNATIONAL, pp. 165-172, June 1996, and “Plasma Immersion Ion Implantation—A Fledgling Technique for Semiconductor Processing,” P. K. Chu, S. Qin, C. Chan, N. W. Cheung, and L. A. Larson, MATERIALS SCIENCE AND ENGINEERING REPORTS: A REVIEW JOURNAL, pp. 207-280, Vol. R17, Nos. 6-7, (Nov. 30, 1996), which are both hereby incorporated by reference for all purposes. Of course, techniques used depend upon the application.
Depending upon the application, smaller mass particles are generally selected to reduce a possibility of damage to the material region 12. That is, smaller mass particles easily travel through the substrate material to the selected depth without substantially damaging the material region that the particles traverse through. For example, the smaller mass particles (or energetic particles) can be almost any charged (e.g., positive or negative) and/or neutral atoms or molecules, or electrons, or the like. In a specific embodiment, the particles can be neutral and/or charged particles including ions such as ions of hydrogen and its isotopes, rare gas ions such as helium and its isotopes, and neon. The particles can also be derived from compounds such as gases, e.g., hydrogen gas, water vapor, methane, and hydrogen compounds, and other light atomic mass particles. Alternatively, the particles can be any combination of the above particles, and/or ions and/or molecular species and/or atomic species. The particles generally have sufficient kinetic energy to penetrate through the surface to the selected depth underneath the surface.
Using hydrogen as the implanted species into the silicon wafer as an example, the implantation process is performed using a specific set of conditions. Implantation dose ranges from about 1015 to about 1018 atoms/cm2, and preferably the dose is greater than about 1016 atoms/cm2. Implantation energy ranges from about 1 KeV to about 1 MeV, and is generally about 50 KeV. Implantation temperature ranges from about −200 to about 600° C., and is preferably less than about 400° C. to prevent a possibility of a substantial quantity of hydrogen ions from diffusing out of the implanted silicon wafer and annealing the implanted damage and stress. The hydrogen ions can be selectively introduced into the silicon wafer to the selected depth at an accuracy of about +/−0.03 to +/−0.05 microns. Of course, the type of ion used and process conditions depend upon the application.
Effectively, the implanted particles add stress or reduce fracture energy along a plane parallel to the top surface of the substrate at the selected depth. The energies depend, in part, upon the implantation species and conditions. These particles reduce a fracture energy level of the substrate at the selected depth. This allows for a controlled cleave along the implanted plane at the selected depth. Implantation can occur under conditions such that the energy state of the substrate at all internal locations is insufficient to initiate a non-reversible fracture (i.e., separation or cleaving) in the substrate material. It should be noted, however, that implantation does generally cause a certain amount of defects (e.g., micro-detects) in the substrate that can typically at least partially be repaired by subsequent heat treatment, e.g., thermal annealing or rapid thermal annealing.
Substrates, however, are not generally free from defects or “weak” regions across the possible cleave front or selected depth zo after the implantation process. In these cases, the cleave generally cannot be controlled, since they are subject to random variations such as bulk material non-uniformities, built-in stresses, defects, and the like.
An example of a cleave process for the substrate illustrated by the above
In a specific embodiment, the present invention provides a controlled-propagating cleave. The controlled-propagating cleave uses multiple successive impulses to initiate and perhaps propagate a cleaving process 700, as illustrated by
Optionally, a built-in energy state of the substrate or stress can be globally raised toward the energy level necessary to initiate the cleaving action, but not enough to initiate the cleaving action before directing the multiple successive impulses to the substrate according to the present invention. The global energy state of the substrate can be raised or lowered using a variety of sources such as chemical, mechanical, thermal (sink or source), or electrical, alone or in combination. The chemical source can include a variety such as particles, fluids, gases, or liquids. These sources can also include chemical reaction to increase stress in the material region. The chemical source is introduced as flood, time-varying, spatially varying, or continuous. In other embodiments, a mechanical source is derived from rotational, translational, compressional, expansional, or ultrasonic energies. The mechanical source can be introduced as flood, time-varying, spatially varying, or continuous. In further embodiments, the electrical source is selected from an applied voltage or an applied electro-magnetic field, which is introduced as flood, time-varying, spatially varying, or continuous. In still further embodiments, the thermal source or sink is selected from radiation, convection, or conduction. This thermal source can be selected from, among others, a photon beam, a fluid jet, a liquid jet, a gas jet, an electro/magnetic field, an electron beam, a thermo-electric heating, and a furnace. The thermal sink can be selected from a fluid jet, a liquid jet, a gas jet, a cryogenic fluid, a super-cooled liquid, a thermo-electric cooling means, an electro/magnetic field, and others. Similar to the previous embodiments, the thermal source is applied as flood, time-varying, spatially varying, or continuous. Still further, any of the above embodiments can be combined or even separated, depending upon the application. Of course, the type of source used also depends upon the application. As noted, the global source increases a level of energy or stress in the material region without initiating a cleaving action in the material region before providing energy to initiate the controlled cleaving action.
In a specific embodiment, an energy source elevates an energy level of the substrate cleave plane above its cleave front propagation energy but is insufficient to cause self-initiation of a cleave front. In particular, a thermal energy source or sink in the form of heat or lack of heat (e.g., cooling source) can be applied globally to the substrate to increase the energy state or stress level of the substrate without initiating a cleave front. Alternatively, the energy source can be electrical, chemical, or mechanical. A directed energy source provides an application of energy to a selected region of the substrate material to initiate a cleave front which self-propagates through the implanted region of the substrate until the thin film of material is removed. A variety of techniques can be used to initiate the cleave action. These techniques are described by way of the Figs. below.
An alternative aspect of the invention is illustrated by
The removed material region provides a thin film of silicon material for processing. The silicon material possesses limited surface roughness and desired planarity characteristics for use in a silicon-on-insulator substrate. In certain embodiments, the surface roughness of the detached film has features that are less than about 60 nm, or less than about 40 nm, or less than about 20 nm. Accordingly, the present invention provides thin silicon films which can be smoother and more uniform than pre-existing techniques.
In a specific embodiment, the energy source can be a fluid jet that is pressurized (e.g., compressional) according to an embodiment of the present invention.
In a preferred embodiment, the energy source can be a compressional source such as, for example, compressed fluid that is static.
In a preferred embodiment, the present invention is practiced at temperatures that are lower than those used by pre-existing techniques. In particular, the present invention does not require increasing the entire substrate temperature to initiate and sustain the cleaving action as pre-existing techniques. In some embodiments for silicon wafers and hydrogen implants, substrate temperature does not exceed about 400° C. during the cleaving process. Alternatively, substrate temperature does not exceed about 350° C. during the cleaving process. Alternatively, substrate temperature is kept substantially below implanting temperatures via a thermal sink, e.g., cooling fluid, cryogenic fluid. Accordingly, the present invention reduces a possibility of unnecessary damage from an excessive release of energy from random cleave fronts, which generally improves surface quality of a detached film(s) and/or the substrate(s). Accordingly, the present invention provides resulting films on substrates at higher overall yields and quality.
The above embodiments are described in terms of cleaving a thin film of material from a substrate. The substrate, however, can be disposed on a workpiece such as a stiffener or the like before the controlled cleaving process. The workpiece joins to a top surface or implanted surface of the substrate to provide structural support to the thin film of material during controlled cleaving processes. The workpiece can be joined to the substrate using a variety of bonding or joining techniques, e.g., electro-statics, adhesives, interatomic. Some of these bonding techniques are described herein. The workpiece can be made of a dielectric material (e.g., quartz, glass, sapphire, silicon nitride, silicon dioxide), a conductive material (silicon, silicon carbide, polysilicon, group III/V materials, metal), and plastics (e.g., polyimide-based materials). Of course, the type of workpiece used will depend upon the application.
Alternatively, the substrate having the film to be detached can be temporarily disposed on a transfer substrate such as a stiffener or the like before the controlled cleaving process. The transfer substrate joins to a top surface or implanted surface of the substrate having the film to provide structural support to the thin film of material during controlled cleaving processes. The transfer substrate can be temporarily joined to the substrate having the film using a variety of bonding or joining techniques, e.g., electro-statics, adhesives, interatomic. Some of these bonding techniques are described herein. The transfer substrate can be made of a dielectric material (e.g., quartz, glass, sapphire, silicon nitride, silicon dioxide), a conductive material (silicon, silicon carbide, polysilicon, group III/V materials, metal), and plastics (e.g., polyimide-based materials). Of course, the type of transfer substrate used will depend upon the application. Additionally, the transfer substrate can be used to remove the thin film of material from the cleaved substrate after the controlled cleaving process.
2. Silicon-On-Insulator Process
A process for fabricating a silicon-on-insulator substrate according to the present invention may be briefly outlined as follows:
(1) Provide a donor silicon wafer (which may be coated with a dielectric material);
(2) Introduce particles into the silicon wafer to a selected depth to define a thickness of silicon film;
(3) Provide a target substrate material (which may be coated with a dielectric material);
(4) Bond the donor silicon wafer to the target substrate material by joining the implanted face to the target substrate material;
(5) Increase global stress (or energy) of implanted region at selected depth without initiating a cleaving action (optional);
(6) Provide stress (or energy) to a selected region of the bonded substrates to initiate a controlled cleaving action at the selected depth;
(7) Provide additional energy to the bonded substrates to sustain the controlled cleaving action to free the thickness of silicon film from the silicon wafer (optional);
(8) Complete bonding of donor silicon wafer to the target substrate; and
(9) Polish a surface of the thickness of silicon film.
The above sequence of steps provides a step of initiating a controlled cleaving action using an energy applied to a selected region(s) of a multi-layered substrate structure to form a cleave front(s) according to the present invention. This initiation step begins a cleaving process in a controlled manner by limiting the amount of energy applied to the substrate. Further propagation of the cleaving action can occur by providing additional energy to selected regions of the substrate to sustain the cleaving action, or using the energy from the initiation step to provide for further propagation of the cleaving action. This sequence of steps is merely an example and should not limit the scope of the claims defined herein. Further details with regard to the above sequence of step§ re described in below in references to the
Selected energetic particles 2109 implant through the top surface of the silicon wafer to a selected depth, which defines the thickness of the material region, termed the thin film of material. As shown, the particles have a desired concentration 2111 at the selected depth (z0). A variety of techniques can be used to implant the energetic particles into the silicon wafer. These techniques include ion implantation using, for example, beam line ion implantation equipment manufactured from companies such as Applied Materials, Eaton Corporation, Varian, and others. Alternatively, implantation occurs using a plasma immersion ion implantation (“PIII”) technique. Of course, techniques used depend upon the application.
Depending upon the application, smaller mass particles are generally selected to reduce a possibility of damage to the material region. That is, smaller mass particles easily travel through the substrate material to the selected depth without substantially damaging the material region that the particles traversed through. For example, the smaller mass particles (or energetic particles) can be almost any charged (e.g., positive or negative) and/or neutral atoms or molecules, or electrons, or the like. In a specific embodiment, the particles can be neutral and/or charged particles including ions of hydrogen and its isotopes, rare gas ions such as helium and its isotopes, and neon. The particles can also be derived from compounds such as gases, e.g., hydrogen gas, water vapor, methane, and other hydrogen compounds, and other light atomic mass particles. Alternatively, the particles can be any combination of the above particles, and/or ions and/or molecular species and/or atomic species.
The process uses a step of joining the implanted silicon wafer 2100 to a workpiece 2201 or target wafer, as illustrated in
In a specific embodiment, the silicon wafers are joined or fused together using a low temperature thermal step. The low temperature thermal process generally ensures that the implanted particles do not place excessive stress on the material region, which can produce an uncontrolled cleave action. In one aspect, the low temperature bonding process occurs by a self-bonding process. In particular, one wafer is stripped to remove oxidation therefrom (or one wafer is not oxidized). A cleaning solution treats the surface of the wafer to form O—H bonds on the wafer surface. An example of a solution used to clean the wafer is a mixture of H2O2—H2SO4. A dryer dries the wafer surfaces to remove any residual liquids or particles from the wafer surfaces. Self-bonding occurs by placing a face of the cleaned wafer against the face of an oxidized wafer.
Alternatively, a self-bonding process occurs by activating one of the wafer surfaces to be bonded by plasma cleaning. In particular, plasma cleaning activates the wafer surface using a plasma derived from gases such as argon, ammonia, neon, water vapor, and oxygen. The activated wafer surface 2203 is placed against a face of the other wafer, which has a coat of oxidation 2205 thereon. The wafers are in a sandwiched structure having exposed wafer faces. A selected amount of pressure is placed on each exposed face of the wafers to self-bond one wafer to the other.
Alternatively, an adhesive disposed on the wafer surfaces is used to bond one wafer onto the other. The adhesive includes an epoxy, polyimide-type materials, and the like. Spin-on-glass layers can be used to bond one wafer surface onto the face of another. These spin-on-glass (“SOG”) materials include, among others, siloxanes or silicates, which are often mixed with alcohol-based solvents or the like. SOG can be a desirable material because of the low temperatures (e.g., 150 to 250° C.) often needed to cure the SOG after it is applied to surfaces of the wafers.
Alternatively, a variety of other low temperature techniques can be used to join the donor wafer to the target wafer. For instance, an electro-static bonding technique can be used to join the two wafers together. In particular, one or both wafer surface(s) is charged to attract to the other wafer surface. Additionally, the donor wafer can be fused to the target wafer using a variety of commonly known techniques. Of course, the technique used depends upon the application.
After bonding the wafers into a sandwiched structure 2300, as shown in
The controlled cleaving action is initiated by way of any of the previously noted techniques and others and is illustrated by way of
Optionally, an energy or stress of the substrate material is increased toward an energy level necessary to initiate the cleaving action, but not enough to initiate the cleaving action before directing an impulse or multiple successive impulses to the substrate according to the present invention. The global energy state of the substrate can be raised or lowered using a variety of sources such as chemical, mechanical, thermal (sink or source), or electrical, alone or in combination. The chemical source can include particles, fluids, gases, or liquids. These sources can also include chemical reaction to increase stress in the material region. The chemical source is introduced as flood, time-varying, spatially varying, or continuous. In other embodiments, a mechanical source is derived from rotational, translational, compressional, expansional, or ultrasonic energies. The mechanical source can be introduced as flood, time-varying, spatially varying, or continuous. In further embodiments, the electrical source is selected from an applied voltage or an applied electro-magnetic field, which is introduced as flood, time-varying, spatially varying, or continuous. In still further embodiments, the thermal source or sink is selected from radiation, convection, or conduction. This thermal source can be selected from, among others, a photon beam, a fluid jet, a liquid jet, a gas jet, an electro/magnetic field, an electron beam, a thermo-electric heating, and a furnace. The thermal sink can be selected from a fluid jet, a liquid jet, a gas jet, a cryogenic fluid, a super-cooled liquid, a thermo-electric cooling means, an electro/magnetic field, and others. Similar to the previous embodiments, the thermal source is applied as flood, time varying, spatially varying, or continuous. Still further, any of the above embodiments can be combined or even separated, depending upon the application. Of course, the type of source used depends upon the application. As noted, the global source increases a level of energy or stress in the material region without initiating a cleaving action in the material region before providing energy to initiate the controlled cleaving action.
In a preferred embodiment, the method maintains a temperature which is below a temperature of introducing the particles into the substrate. In some embodiments, the substrate temperature is maintained between −200 and 450° C. during the step of introducing energy to initiate propagation of the cleaving action. Substrate temperature can also be maintained at a temperature below 400° C. or below 350° C. In preferred embodiments, the method uses a thermal sink to initiate and maintain the cleaving action, which occurs at conditions significantly below room temperature.
A final bonding step occurs between the target wafer 2201 and thin film of material region 2101 according to some embodiments, as illustrated by
In some embodiments, the oxidized silicon surface from either the target wafer or the thin film of material region (from the donor wafer) are further pressed together and are subjected to an oxidizing ambient 2401. The oxidizing ambient can be in a diffusion furnace for steam oxidation, hydrogen oxidation, or the like. A combination of the pressure and the oxidizing ambient fuses the thin film of silicon material 2101 to the target silicon wafer 2201 together at the oxide surface or interface 2305. These embodiments often require high temperatures (e.g., 700° C.).
Alternatively, the two silicon surfaces are further pressed together and subjected to an applied voltage between the two wafers. The applied voltage raises temperature of the wafers to induce a bonding between the wafers. This technique limits the amount of crystal defects introduced into the silicon wafers during the bonding process, since substantially no significant mechanical force is needed to initiate the bonding action between the wafers. Of course, the technique used depends upon the application.
After bonding the wafers, silicon-on-insulator has a target substrate 2201 with an overlying film of silicon material 2101 and a sandwiched oxide layer 2205 between the target substrate 2201 and the silicon wafer 2100, as also illustrated in
Alternatively, chemical mechanical polishing or planarization (“CMP”) techniques finish the detached surface of the film, as illustrated by
This acid solution generally interacts with the silicon material from the wafer during the polishing process. The polishing process preferably uses a poly-urethane polishing pad. An example of this polishing pad is one made by Rodel and sold under the trade name of IC-1000. The polishing pad is rotated at a selected speed. A carrier head which picks up the target wafer having the film applies a selected amount of pressure on the backside of the target wafer such that a selected force is applied to the film. The polishing process removes about a selected amount of film material, which provides a relatively smooth film surface 2601 for subsequent processing, as illustrated by
In certain embodiments, a thin film of oxide 2406 overlies the film of material overlying the target wafer, as illustrated in
Although the above description is in terms of a silicon wafer, other substrates may also be used. For example, the substrate can be almost any monocrystalline, polycrystalline, or even amorphous type substrate. Additionally, the substrate can be made of III/V materials such as gallium arsenide, gallium nitride (GaN), and others. The multi-layered substrate can also be used according to the present invention. The multi-layered substrate includes a silicon-on-insulator substrate, a variety of sandwiched layers on a semiconductor substrate, and numerous other types of substrates. Additionally, the embodiments above were generally in terms of providing a pulse of energy to initiate a controlled cleaving action. The pulse can be replaced by energy that is scanned across a selected region of the substrate to initiate the controlled cleaving action. Energy can also be scanned across selected regions of the substrate to sustain or maintain the controlled cleaving action. One of ordinary skill in the art would easily recognize a variety of alternatives, modifications, and variations, which can be used according to the present invention.
While the above is a full description of the specific embodiments, various modifications, alternative constructions and equivalents may be used. Therefore, the above description and illustrations should not be taken as limiting the scope of the present invention which is defined by the appended claims.
This application is a continuation of U.S. application Ser. No. 12/218,149 filed on Jul. 10, 2008 now U.S. Pat. No. 7,846,818, which is a continuation of U.S. application Ser. No. 11/627,920 filed on Jan. 26, 2007 now U.S. Pat. No. 7,410,887, which is a continuation of U.S. application Ser. No. 11/281,042 filed on Nov. 16, 2005 now U.S. Pat. No. 7,371,660, which is a continuation of U.S. application Ser. No. 10/644,644 filed on Aug. 19, 2003 now U.S. Pat. No. 7,160,790, which is a continuation of U.S. application Ser. No. 09/483,393 filed Jan. 13, 2000 now U.S. Pat. No. 6,632,724, which is a continuation of U.S. application Ser. No. 09/026,034 filed Feb. 19, 1998 now U.S. Pat. No. 6,013,563, which claims priority from U.S. provisional patent application entitled A CONTROLLED CLEAVAGE PROCESS AND RESULTING DEVICE, filed May 12, 1997 and assigned Application No. 60/046,276. The disclosure of all of the above applications is hereby incorporated by reference in its entirety for all purposes.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5341608 | Mains, Jr. | Aug 1994 | A |
| 6130379 | Shiotsuka et al. | Oct 2000 | A |
| 6294478 | Sakaguchi et al. | Sep 2001 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20100282323 A1 | Nov 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60046276 | May 1997 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12218149 | Jul 2008 | US |
| Child | 12789361 | US | |
| Parent | 11627920 | Jan 2007 | US |
| Child | 12218149 | US | |
| Parent | 11281042 | Nov 2005 | US |
| Child | 11627920 | US | |
| Parent | 10644644 | Aug 2003 | US |
| Child | 11281042 | US | |
| Parent | 09483393 | Jan 2000 | US |
| Child | 10644644 | US | |
| Parent | 09026034 | Feb 1998 | US |
| Child | 09483393 | US |