Patent Application
20180291517
The present disclosure relates generally to method and apparatus for electroplating a metal layer on a semiconductor wafer. More particularly, the method and apparatus described herein are useful for controlling plating uniformity.
The transition from aluminum to copper in integrated circuit (IC) fabrication required a change in process “architecture” (to damascene and dual-damascene) as well as a whole new set of process technologies. One process step used in producing copper damascene circuits is the formation of a “seed-” or “strike-” layer, which is then used as a base layer onto which copper is electroplated (“electrofill”). The seed layer carries the electrical plating current from the edge region of the wafer (where electrical contact is made) to all trenches and via structures located across the wafer surface. The seed film is typically a thin conductive copper layer. It is separated from the insulating silicon dioxide or other dielectric by a barrier layer. The seed layer deposition process should yield a layer which has good overall adhesion, excellent step coverage (more particularly, conformal/continuous amounts of metal deposited onto the side-walls of an embedded structure), and minimal closure or “necking” of the top of the embedded feature.
Market trends of increasingly smaller features and alternative seeding processes drive the need for a capability to plate with a high degree of uniformity on increasingly thin seeded wafers. In the future, it is anticipated that the seed film may simply be composed of a plateable barrier film, such as ruthenium, or a bilayer of a very thin barrier and copper (deposited, for example, by an atomic layer deposition (ALD) or similar process). Such films present the engineer with an extreme terminal effect situation. For example, when driving a 3 amp total current uniformly into a 30 ohm per square ruthenium seed layer (a likely value for a 30-50 Å film) the resultant center to edge (radial) voltage drop in the metal will be over 2 volts. To effectively plate a large surface area, the plating tooling makes electrical contact to the conductive seed only in the edge region of the wafer substrate. There is no direct contact made to the central region of the substrate. Hence, for highly resistive seed layers, the potential at the edge of the layer is significantly greater than at the central region of the layer. Without appropriate means of resistance and voltage compensation, this large edge-to-center voltage drop could lead to an extremely non-uniform plating rate and non-uniform plating thickness distribution, primarily characterized by thicker plating at the wafer edge. This plating non-uniformity is radial non-uniformity, that is, uniformity variation along a radius of the circular wafer.
Another type of non-uniformity, which needs to be mitigated, is azimuthal non-uniformity. For clarity, we define azimuthal non-uniformity, using polar coordinates, as thickness variations exhibited at different angular positions on the workpiece at a fixed radial position from the wafer center, that is, a non-uniformity along a given circle or portion of a circle within the perimeter of the wafer. This type of non-uniformity can be present in electroplating applications, independently of radial non-uniformity, and in some applications may be the predominant type of non-uniformity that needs to be controlled. It often arises in through resist plating, where a major portion of the wafer is masked with a photoresist coating or similar plating-preventing layer, and the masked pattern of features or feature densities are not azmuthally uniform near the wafer edge. For example, in some cases there may be a technically required chord-region of missing pattern features near the notch of the wafer to allow for wafer numbering or handling. The radially and azimuthally variable plating rates inside missing region may cause chip die to be non-functional, therefore methods and apparatus for avoiding this situation are needed.
Electrochemical deposition is now poised to fill a commercial need for sophisticated packaging and multichip interconnection technologies known generally as wafer level packaging (WLP) and through silicon via (TSV) electrical connection technology. These technologies present their own very significant challenges.
These technologies require electroplating on a significantly larger size scale than damascene applications. Depending on the type and application of the packaging features (e.g. through chip connecting TSV, interconnection redistribution wiring, or chip to board or chip bonding, such as flip-chip pillars), plated features are usually, in current technology, greater than about 2 micrometers in diameter and typically are 5-100 micrometers in diameter (for example, pillars may be about 50 micrometers). For some on-chip structures such as power busses, the feature to be plated may be larger than 100 micrometers. The aspect ratios of the WLP features are typically about 2:1 (height to width) or lower, more typically 1:1 or lower, while TSV structures can have very high aspect ratios (e.g., in the neighborhood of about 10:1 or 20:1).
Given the relatively large amount of material to be deposited, not only feature size, but also plating speed differentiates WLP and TSV applications from damascene applications. For many WLP applications, plating must fill features at a rate of at least about 2 micrometers/minute, and typically at least about 4 micrometers/minute, and for some applications at least about 7 micrometers/minute. The actual rates will vary depending on the particular metal being deposited. But at these higher plating rate regimes, efficient mass transfer of metal ions in the electrolyte to the plating surface is very important. Higher plating rates present challenges with respect to uniformity of the electrodeposited layer.
Described are method and apparatus for controlling plating uniformity, particularly, azimuthal non-uniformity, radial non-uniformity, or both. Apparatus and methods described herein can be used for electroplating on a variety of substrates, including semiconductor wafer substrates having TSV or WLP recessed features.
In some embodiments, a method for electroplating an asymmetrical plating workpiece (including a geometrically symmetrical workpiece substrate whose exposed area to be plated is asymmetrical, such as a wafer with an azimuthally non-uniformly patterning), is provided. The asymmetry refers not only to purely geometric asymmetry of the substrate (such as presence of a notch, or a flat region cut along a chord), but also to asymmetry within the features on the substrate, which may result in unwanted ionic current crowding during plating, and lead to increased plating at certain azimuthal regions of the wafer. For example, in some embodiments electroplating is performed on a substrate having a missing die. Electroplating on such substrate leads to current crowding in the areas that are adjacent to the azimuthal variable patterning discontinuities at the periphery, such as a region with missing features and missing die, and, consequently, to plating non-uniformity in this region.
Provided methods and apparatus, in some embodiments, employ azimuthally asymmetric shields—shields that provide shielding from the plating (ionic) current to a greater degree at some azimuthal (angular) positions than at other azimuthal (angular) positions, at least at one of radial positions.
Provided methods and apparatus, in some embodiments, employ azimuthally asymmetric auxiliary electrodes—electrodes configured to divert plating current (auxiliary cathodes or thieves), to donate plating current (auxiliary anodes), or to both donate and divert current at different time points (referred to as anode/cathodes), where the electrodes are shaped or confined such as to predominantly modify current to a greater degree at some azimuthal (angular) positions in preference to other positions.
An example of an azimuthally asymmetric electrode is a C-shaped electrode (a cathode, anode, or an anode/cathode). The C-shaped electrode, is located, in some embodiments, relatively close to the wafer substrate (e.g., within a distance of not greater than 0.2 of the radius of the wafer), and is electrically connected to a power supply and a controller, which, in some embodiments, provide for it being energized in correlation with rotation of the wafer. In some embodiments the body of the C-shaped electrode, preferably, has an arc length of less than about 120 degrees, such as less than about 90 degrees.
In one aspect, provided methods and apparatus employ azimuthally asymmetric shields and/or azimuthally asymmetric auxiliary electrodes and/or multi-segmented auxiliary electrodes, where rotation of the wafer is adjusted such that different angular (azimuthal) positions of the wafer have different dwell times in the shielded area or in the area proximate the auxiliary electrode or its segment.
Thus, for example, a missing die area may spend more time, on average, in a relatively more shielded area than an equivalent portion of the wafer at a different angular (azimuthal) position but having the same average arc length and same average radial position.
In another aspect, provided methods and apparatus employ azimuthally asymmetric auxiliary electrodes and/or multi-segmented auxiliary electrodes, where the electrodes are energized in correlation with the rotation of the wafer such that different angular (azimuthal) positions of the wafer are exposed to different amounts of plating current being donated and/or diverted by an auxiliary electrode (or electrode segment).
For example, a C-shaped auxiliary electrode may be energized in correlation with the rotating wafer, e.g., such as when the missing die region of the wafer passes through proximity of the C-shaped electrode, the electrode may be energized at a first level (e.g., to divert current at a first level), while it is energized at a different level, or not energized, or energized to have an opposite polarity, when other azimuthal (angular) positions of the wafer pass through its proximity during the course of wafer rotation. The terms angular and azimuthal positions are synonymous and can be used interchangeably.
It should be understood that the all secondary or auxiliary electrode functionality described herein can be operated as either anodes, cathodes, or both. The anode may be an inert anode or dimensionally stable anode, for example generating oxygen gas, or it can be a metallic anode, creating metal ions. The cathode may have metal plating thereupon, or may undergo another cathodic reaction, such as hydrogen evolution (e.g. if plateable metal ions are excluded from the electrode's surface). The electrode may, in some embodiments, combine two or more of the above processes, changing in time during a wafer plating cycle (an anode/cathode). Therefore, while some embodiments described herein, are exemplified, by thief cathodes, it is understood that all of these embodiments can be used not only with thief cathodes, but with other types of auxiliary electrodes, including anodes (positively biased electrodes configured for donating plating current) and anode/cathodes (electrodes, which can be biased both negatively and positively, at different time points as desired). The auxiliary electrodes may be energized either continuously or for some portion of the rotation of the wafer.
Further, while it may not be mentioned with each of the methods described, preferably each method includes an operation prior to electroplating in which the desired azimuthal position of the substrate is registered (e.g., by an optical device), such that this position is known, and such that the apparatus could be programmed, such as to provide appropriate plating current correction for this specific position (or for a different position residing at a certain angle from the known position) during the course of electroplating. The registration of the selected angular position (e.g., a notch) can be performed in the electroplating apparatus, or in a different apparatus, as long as the recorded position remains known, up to the point of electroplating.
In one aspect, a method of electroplating a metal on a cathodically biased substrate while controlling azimuthal uniformity, includes providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the apparatus comprises an anode and a stationary auxiliary azimuthally asymmetric electrode; and electroplating the metal on the substrate while rotating the substrate, and while providing power to the auxiliary azimuthally asymmetric electrode in correlation with the rotation of the substrate, such that the auxiliary azimuthally asymmetric electrode diverts and/or donates plating current to a first portion of the substrate at a selected azimuthal position of the substrate differently than to a second portion of the substrate having the same average arc length and the same average radial position and residing at a different azimuthal angular position.
It is understood that providing desired power to the auxiliary electrode can be achieved by controlling current, voltage or combination thereof from a power supply electrically connected to the auxiliary electrode. The auxiliary electrode can be energized such that a different current is applied to it when the selected azimuthal position passes in its proximity, while the auxiliary electrode may be energized by a different level of current, not energized at all, or energized at a different polarity, when other angular positions of the wafer pass through its proximity. Typically, during one full rotation of the wafer the auxiliary electrode passes through at least two distinct states (e.g., energized by different levels of current, energized at different polarities, or energized/non-energized states).
In some embodiments the azimuthally asymmetric electrode is C-shaped. In some embodiments the electrode may reside in an azimuthal current flow confinement structure. If the confinement structure provides an exposure of plating current (e.g., through a slot or a series of openings) that approximates a C-shape, the auxiliary electrode itself may have a variety of shapes, because the modification of plating current by the auxiliary electrode will be governed by the exposure created by the confinement structure. In some embodiments, the auxiliary azimuthally asymmetric electrode is housed in a separate chamber and the exposure of plating current from the auxiliary electrode is through at least one channel that delivers current into a region of the cell near the periphery of the substrate over an arc angle of less than about 120 degrees.
In some embodiments, the auxiliary azimuthally asymmetric electrode is cathodically biased and is configured to divert different amounts of plating current from different azimuthal positions of the substrate during electroplating. For example, during one full rotation of the wafer, the electrode may accept a first level of cathodic current (when the selected angular position of the rotating wafer passes in its proximity) and then a different (lower or higher) level of current (when a different angular position passes through its proximity). In another example, during one full rotation of the wafer, the electrode may accept a first level of cathodic current (when the selected angular position of the rotating wafer passes in its proximity) and then may remain non-energized (when a different angular position passes through its proximity).
In other embodiments, the auxiliary azimuthally asymmetric electrode is anodically biased and is configured to donate different amounts of plating current to different azimuthal positions of the substrate during electroplating. For example, during one full rotation of the wafer, the electrode may accept a first level of anodic current (when the selected angular position of the rotating wafer passes in its proximity) and then a different (lower or higher) level of current (when a different angular position passes through its proximity). In another example, during one full rotation of the wafer, the electrode may accept a first level of anodic current (when the selected angular position of the rotating wafer passes in its proximity) and then may remain non-energized (when a different angular position passes through its proximity).
In other embodiments, the auxiliary azimuthally asymmetric electrode is both anodically and cathodically biased during electroplating, and is configured to divert plating current from a first azimuthal position on the substrate and to donate plating current to a second azimuthal position on the substrate. For example, during one full rotation of the wafer, the electrode may accept a level of anodic current (when the selected angular position of the rotating wafer passes in its proximity) and then a level of cathodic current (when a different angular position of the rotating wafer passes through its proximity). Such anode/cathode is typically electrically connected to a bipolar power supply, which is configured to change polarity of the auxiliary electrode, as necessary.
In some embodiments, the electroplating apparatus includes a shield, shielding the periphery of the substrate at all azimuthal positions, and the auxiliary azimuthally asymmetric electrode is anodically biased at least during a portion of a time of a full rotation of the substrate, and is configured to donate current to the selected azimuthal position on the substrate. By using the azimuthally symmetrical shield, the entire periphery of the wafer may be lacking in plating current, which can be corrected by donating plating current at different levels to different angular positions, by an auxiliary anode.
In another aspect, a method of electroplating a metal on a cathodically biased substrate includes providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the apparatus comprises an auxiliary azimuthally asymmetric or multi-segmented anode in the proximity of the substrate; and electroplating the metal on the substrate while rotating the substrate, and while providing power to the auxiliary azimuthally asymmetric anode at a substantially constant level to donate current to the substrate.
In another aspect an electroplating apparatus for electroplating a metal on a substrate is provided, where the apparatus includes a plating chamber configured to contain an electrolyte, an anode, and an azimuthally asymmetric auxiliary electrode; a substrate holder configured to hold the substrate; and a controller comprising program instructions for electroplating the metal on the substrate while rotating the substrate, and while providing power to the auxiliary azimuthally asymmetric electrode in correlation with the rotation of the substrate, such that the auxiliary azimuthally asymmetric electrode diverts and/or donates plating current to a first portion of the substrate at a selected azimuthal position of the substrate differently than to a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position. In some embodiments this apparatus is integrated into a system configured for photolithographic processing which further includes a stepper.
In another aspect a non-transitory computer machine-readable medium comprising program instructions for control of an electroplating apparatus is provided, wherein the program instructions include code for electroplating the metal on the substrate while rotating the substrate, and while providing power to the auxiliary azimuthally asymmetric electrode in correlation with the rotation of the substrate, such that the auxiliary azimuthally asymmetric electrode diverts and/or donates plating current to a first portion of the substrate at a selected azimuthal position of the substrate differently than to a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
In some embodiments the methods provided herein are integrated into the general processing schemes that include photolithographic processing, and further include the steps of. applying photoresist to the substrate; exposing the photoresist to light; patterning the resist and transferring the pattern to the workpiece; and selectively removing the photoresist from the work piece. In some embodiments, the photoresist is applied and patterned prior to electroplating and is removed after electroplating.
In another aspect, an electroplating apparatus for electroplating a metal on a substrate, is provided, wherein the apparatus includes: a plating chamber configured to contain an electrolyte; a substrate holder configured to hold and rotate the substrate during electroplating; an anode; and an azimuthally asymmetric auxiliary electrode configured to be biased both anodically and cathodically during electroplating.
In another aspect an electroplating apparatus for electroplating a metal on a substrate is provided, wherein the apparatus includes: a plating chamber configured to contain an electrolyte; a substrate holder configured to hold and rotate the substrate during electroplating; an anode; a shield configured to shield current at the periphery of the substrate; and an azimuthally asymmetric auxiliary anode configured to donate current to the shielded periphery of the substrate at a selected azimuthal position on the substrate.
In another aspect an electroplating apparatus for electroplating a metal on a substrate is provided, where the apparatus includes: a plating chamber configured to contain an electrolyte; a substrate holder configured to hold and rotate the substrate during electroplating; an anode; and a multi-segmented auxiliary electrode configured to be biased both anodically and cathodically during electroplating, or a multi-segmented auxiliary anode.
In another aspect, a method of electroplating a metal on a cathodically biased substrate while controlling azimuthal uniformity includes: (a) providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the apparatus comprises a first anode and a multi-segmented auxiliary anode or a multi-segmented auxiliary electrode configured to serve both as an auxiliary anode and an auxiliary cathode; and (b) electroplating the metal on the substrate while rotating the substrate, and while providing power to the segments of the multi-segmented auxiliary anode or the multi-segmented auxiliary electrode in correlation with the rotation of the substrate, such that said anode donates plating current to a first portion of the substrate at a selected azimuthal position of the substrate to a different level than to a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position, or such that said auxiliary electrode donates current to the first portion and diverts the current from the second portion.
In another aspect a method of electroplating a metal on a substrate while controlling azimuthal uniformity includes: (a) providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating; and (b) electroplating the metal on the substrate while rotating the substrate relative to a shield such that a selected portion of the substrate at a selected azimuthal position dwells in a shielded area for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
For example, the substrate may be rotated at a first speed when the selected portion of the substrate is less shielded, and at a second speed when the selected portion of the substrate is more shielded, wherein one full rotation of the substrate comprises a first period of rotation at the first speed and a second period of rotation at the second speed. In some embodiments, the second speed is lower than the first speed, that is, the substrate slows down when the selected angular position of the wafer (usually the one affected by current crowding) passes through the more shielded area. In a more specific example, the first speed is at least about 20 rpm, the second speed is less than about 10 rpm, and the substrate makes at least about 5 variable-speed full rotations during the course of electroplating.
In some embodiments, different dwell times in the shielded area are achieved by rotating the substrate bidirectionally at a constant speed. The bidirectional rotation is configured such that the selected angular position of the wafer spends more (or less) time in the shielded area in comparison with other angular positions.
Preferably, the distance between the shield and the platable surface of the substrate is no more than about 0.1 of the radius of the substrate. In some embodiments, the distance between the shield and the platable surface of the substrate is no more than about 4 mm.
In some embodiments the electroplating apparatus further comprises an ionically resistive ionically permeable element having a flat surface that is substantially parallel to and separated from the plating face of the substrate by a distance of about 10 millimeters or less during electroplating, wherein the element has a plurality of non-communicating holes. In some embodiments, the shield is an azimuthally asymmetric shield eclipsing some of the holes of the ionically resistive ionically permeable element or the shield itself is the ionically resistive ionically permeable element having an azimuthally asymmetric distribution of hoes.
In one aspect an electroplating apparatus for electroplating a metal on a substrate is provided, where the apparatus includes: a plating chamber configured to contain an electrolyte and a shield; a substrate holder configured to hold the substrate; and a controller comprising program instructions for electroplating the metal on the substrate while rotating the substrate relative to the shield such that a selected portion of the substrate at a selected azimuthal position dwells in a shielded area for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position. In another aspect, a system comprising such apparatus and a stepper is provided.
In another aspect, a non-transitory computer machine-readable medium comprising program instructions for control of an electroplating apparatus, is provided, where the program instructions include code for electroplating metal on a substrate while rotating the substrate relative to a shield such that a selected portion of the substrate at a selected azimuthal position dwells in a shielded area for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
In another aspect a method of electroplating a metal on a substrate while controlling azimuthal uniformity is provided, where the method includes: providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the electroplating apparatus comprises a multi-segmented auxiliary electrode configured to divert and/or donate current during electroplating; and (b) electroplating the metal on the substrate while rotating the substrate relative to the stationary multi-segmented auxiliary electrode such that a selected portion of the substrate at a selected azimuthal position dwells in an area proximate to a segment of the auxiliary electrode for a different amount of time than a second portion of the substrate having the same average arc length and the same radial position and residing at a different angular azimuthal position, and wherein at least one segment of the auxiliary electrode diverts and/or donates plating current differently than another segment. For example, one of the segments may be accept a current at a different level than other segments (anodic or cathodic), or one of the segments may have the opposite polarity from the other segments.
In another aspect, a method of electroplating a metal on a substrate while controlling azimuthal uniformity includes: providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the electroplating apparatus comprises an azimuthally asymmetric auxiliary electrode configured to divert and/or donate current during electroplating; and electroplating the metal on the substrate while rotating the substrate relative to the azimuthally asymmetric auxiliary electrode such that a selected portion of the substrate at a selected azimuthal position dwells in an area proximate to the azimuthally asymmetric auxiliary electrode for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
In another embodiment a method of electroplating a metal on a substrate while controlling azimuthal uniformity includes: (a) providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the electroplating apparatus comprises a rotatable multi-segmented thief cathode configured to divert current during electroplating; and (b) electroplating the metal on the substrate while rotating the substrate and the thief cathode at the same speed such that a selected portion of the substrate at a selected azimuthal position dwells in an area proximate to a segment of the thief cathode for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
In another embodiment, a method of electroplating a metal on a substrate while controlling azimuthal uniformity includes (a) providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the electroplating apparatus comprises a rotatable azimuthally asymmetric thief cathode configured to divert current during electroplating; and (b) electroplating the metal on the substrate while rotating the substrate and the thief cathode at the same speed such that a selected portion of the substrate at a selected azimuthal position dwells in an area proximate to the thief cathode for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
In another embodiment, a method of electroplating a metal on a substrate while controlling azimuthal uniformity includes providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the electroplating apparatus comprises a rotatable multi-segmented auxiliary anode configured to divert current during electroplating or a rotatable multi-segmented auxiliary electrode configured to function both as an anode and a cathode; and electroplating the metal on the substrate while rotating the substrate and the multi-segmented auxiliary anode or the multi-segmented auxiliary electrode at the same speed such that a selected portion of the substrate at a selected azimuthal position dwells in an area proximate to a segment of the anode or the electrode for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal positions.
In another embodiment a method of electroplating a metal on a substrate while controlling azimuthal uniformity includes: (a) providing the substrate into an electroplating apparatus configured for rotating the substrate during electroplating, wherein the electroplating apparatus comprises a rotatable azimuthally asymmetric anode configured to divert current during electroplating or a rotatable azimuthally asymmetric anode/cathode configured to both divert and donate current during electroplating; and (b) electroplating the metal on the substrate while rotating the substrate and the anode or anode/cathode at the same speed such that a selected portion of the substrate at a selected azimuthal position dwells in an area proximate to the anode or the anode/cathode for a different amount of time than a second portion of the substrate having the same average arc length and the same average radial position and residing at a different angular azimuthal position.
In some embodiments, all methods presented herein may further include rotating a shield having a generally annular body with a removed segment, which resides in close proximity of the wafer, during the course of electroplating. This can optimize the flow of electrolyte in the proximity of the wafer as the electrolyte will tend to move laterally at the wafer surface in the direction of the opening of that shield. In some embodiments this flow diverter is rotated at a speed that is different from the wafer rotation speed, thereby maximizing randomization of the flow patterns.
For all methods disclosed herein, the selected portion of the substrate may include an area adjacent to a wafer notch, a wafer flat or a set of azimuthally missing features, which is registered (e.g., by an optical aligner) prior to electroplating. Electroplating, in some embodiments includes filling recessed features during TSV or WLP processing.
These and other features and advantages of the present invention will be described in more detail below with reference to the associated drawings.
Methods and apparatus for electroplating a metal on a substrate while controlling uniformity of the electroplated layer, such as azimuthal uniformity, radial uniformity, or both, are provided.
Embodiments are described generally where the substrate is a semiconductor wafer; however the invention is not so limited. Provided apparatus and methods are useful for electroplating metals in TSV and WLP applications, but can also be used in a variety of other electroplating processes, including deposition of copper in damascene features. Examples of metals that can be electroplated using provided methods include, without limitation, copper, tin, a tin-lead composition, a tin-silver composition, nickel, cobalt, nickel and/or cobalt alloys with each other and with tungsten, a tin-copper composition, a tin-silver-copper composition, gold, palladium, and various alloys which include these metals and compositions.
In a typical electroplating process, the semiconductor wafer substrate, which may have one or more recessed features on its surface is placed into the wafer holder, and its platable surface is immersed into an electrolyte contained in the electroplating bath. The wafer substrate is biased negatively, such that it serves as a cathode during electroplating. The ions of the platable metal (such as ions of metals listed above) which are contained in the electrolyte are being reduced at the surface of the negatively biased substrate during electroplating, thereby forming a layer of plated metal. The wafer, which is typically rotated during electroplating, experiences an electric field (ionic current field of the electrolyte) that may be non-uniform for a variety of reasons, including azimuthal asymmetry existing in the wafer substrate. This may lead to non-uniform deposition of metal.
The electroplating apparatus provided herein typically includes a substrate holder configured for holding and rotating the substrate during electroplating; a plating bath configured for holding an electrolyte and an anode; and a power supply having a negative terminal electrically connected to the wafer substrate, and a positive terminal electrically connected to the anode. The apparatus further includes one or more elements, such as shields, and auxiliary electrodes (cathodes, anodes or anode/cathodes), that are configured for tailoring uniformity profile during plating. The apparatus, in some embodiments, further includes a controller having program instructions for performing methods disclosed herein, such as for varying rotational speed and/or rotational direction of the substrate in a manner that allows controlling plating uniformity. The controller, in some embodiments, further includes program instructions for energizing auxiliary electrodes in correlation with the wafer rotation.
The present disclosure relates to method and apparatus for controlling plating uniformity particularly, not only radial non-uniformity but also azimuthal non-uniformity. Azimuthal non-uniformity can arise in a number of ways. In one example, semiconductor wafers are sometimes cut along a chord (e.g. JEDA wafers) and have a notch, e.g. for registration purposes during process manipulations. These chords or notches constitute azimuthal non-uniformities in the wafer. As the wafer is rotated and exposed to a plating field, the edges of the wafer along the chord or notch are exposed to different field strength than other corresponding areas of the wafer along the same annulus (i.e., same radial position). During plating, there will be azimuthal non-uniformity from the edge of the chord or notch going inward toward the center areas of the wafer. As another example, a seed layer is typically deposited on a wafer that has been patterned with device features, or device features are patterned in a layer of photoresist overlying the seed layer on a wafer that is substantially round (with the exception of a notch for angular registry). These device features are typically repeated as a series of, for example, rectangular dies. Since the wafer itself is round, inevitably there are areas at the edge of the wafer where there is insufficient room for a complete die with all the die device features or patterns (or where the topography is significantly different than that of the features as a whole). Because of this, there are inevitably boundaries between the areas where there are no features (for example unexposed unpatterned resist) and the areas with features. Therefore along a given annulus within the perimeter of the wafer, typically but not necessarily toward the perimeter of the wafer, there are feature pattern variations, such as regions containing featured and other non-featured surfaces. Because there are boundaries between featured and non-featured (or topographically different) areas, there are necessarily azimuthal plating variations due to the fact that the line of current flow and the electric field is tailored to plate, for example, on a particular topography a certain way and/or because, at these boundaries, there is a different topography and an excess exposure to the plating cell's field and lines of current, so plating current crowded or built up at these transition locations. One way to overcome the topography change would be to print partial (non-functional) features and dies to fill the areas where dies would not normally fit, extending the pattern to the wafer edge, for example, all the way around the periphery of the wafer. However, since dies are commonly lithographed individually on the wafer, there is an associated prohibitive cost to forming these “dummy” features. These substrates will be referred to as azimuthally asymmetric substrates. Notably, such substrates may be geometrically asymmetric (e.g., have a notch or a cut-out portion and the substrate itself is not substantially round), or the asymmetry may be lie in the distribution of the features defined on the substrate (e.g., a missing set of features or die), or both. In an azimuthally asymmetric substrate, there is azimuthal variation of substrate geometry or substrate topography at least at one radial position.
Azimuthal plating non-uniformity on substrates, particularly on azimuthally asymmetric substrates is addressed, in some embodiments, by using azimuthally asymmetric shields and azimuthally asymmetric auxiliary electrodes and/or by using rotational techniques that align selected azimuthal positions of the substrates with shielded areas or areas in the proximity of thief cathodes.
Azimuthally asymmetric shields are shields that shield the substrate from plating current at some azimuthal positions, and not to the same extent or not at all in other azimuthal positions, along at least one radial position. These include wedge-shaped shields, batwing-shaped shields, etc. A purely annular shield (without protrusions to the center of the annulus) is not azimuthally asymmetric with respect to a round workpiece such as a wafer. Shields are typically made of an ionically resistive material relative to the main plating solution media, and are placed in the proximity of the wafer substrate to prevent unwanted excessive current crowding at selected positions of the substrate. In some cases the ionic resistance of the shield is not absolute, but is only significantly greater than the plating media itself In other cases the shield has not only an azimuthally variable shape, but also has an azimuthally and/or radially variable ionic resistance, for example, created by having a variable pattern of holes in a resistive plate such as a piece of plastic or ceramic. Generally the shields are electrically non-conductive (they do not conduct electrical current by transport of electronics), and are therefore made of dielectric material such as plastics, glasses, and ceramics, and not made of metals. The shields are most effective at tailoring azimuthal plating uniformity if the distance between the platable surface of the wafer and the closest surface of the shield is no more than about 0.1 times the radius of the substrate, such as no more than about 0.2 of the radius of the substrate. As a specific example, the azimuthal edge correcting shield according to this invention for a 300 mm diameter wafer would be closer than about 30 mm, more typically spaced less than 15 mm from the wafer substrate, for example, about 7 mm from the wafer surface. In many embodiments, the shields are disposed in the plating bath, immersed in the electrolyte, very close to the substrate, such as within 4 mm of the platable surface of the substrate.
Azimuthally asymmetric thief cathodes are azimuthally asymmetric negatively biased members (e.g., strips of metal), which are disposed in ionic communication with the plating electrolyte (e.g., either directly in the plating bath, or in an adjacent chamber in ionic communication with the wafer and wafer edge), where the thieves are configured for diverting a portion of ionic plating current emanating from the main anode placed generally below and aligned with the wafer away from the substrate to the thief cathode. Alternatively, the electrode may operate as an auxiliary anode, configured and operating for delivering additional ionic plating current, in excess of what would be supplied from the main anode. In some embodiments the electrode can cycle its operation between both of these two modes, acting as an auxiliary anode, and later as an auxiliary cathode, both synchronized with the rotation of the wafer, such that the electrode is energized at a first level and/or polarity when selected angular position of the rotating substrate passes through its proximity, and is energized at a different level and/or with different polarity when a different angular position of the rotating wafer passes through its proximity. Thus, during one full rotation of the wafer the azimuthally asymmetric electrode has at least two states (energized by applying two levels of current, energized/non-energized, or energized at different polarities). Anodes/cathodes can be energized by a bipolar power supply which allows for switching from cathode to anode mode without change in hardware. Auxiliary electrodes are typically biased and controlled separately from the substrate, e.g., using a separate power supply or resistive controlling circuity, or a separate channel on the same power supply that provides current to the substrate. Azimuthally asymmetric electrodes such as thief cathodes, auxiliary anodes, and anode/cathodes modify plating current at some azimuthal positions of the wafer to a different extent than at other azimuthal positions around at least one radial position. An example of an azimuthally asymmetric thief, anode, or an anode/cathode is a C-shaped auxiliary electrode that surrounds the wafer periphery out beyond the radius of the wafer over only a portion of the wafer circumference (e.g., an annular thief having a segment removed). In some embodiments, the body of the C-shaped electrode has an arc length of less than about 120 degrees such as less than about 90 degrees. An annular electrode, in contrast, is azimuthally symmetric and surrounds the wafer entirely over the entire portion of the circumference. In some embodiments the azimuthally asymmetric electrodes reside in close proximity to the wafer, e.g., preferably within a distance not greater than 0.2 times the radius of the wafer. In some embodiments, the azimuthally asymmetric electrodes reside in a confinement structure that provides a current exposure (e.g., through a slot or series of openings in the confinement structure) approximating a C-shaped electrode. In this case the electrode itself may have a variety of shapes, as its function will be determined by the shape of the confinement structure, which essentially forms a virtual electrode. The position of the auxiliary electrode, in some embodiments, may include any position about the periphery of the wafer, such as those disclosed in the U.S. Patent Application Pub. No. 2010/0116672, titled “Method and Apparatus for Electroplating” by Mayer et al. published May 13, 2010, which is herein incorporated by reference in its entirety. The containment structure for the auxiliary electrode, when used, may include a plurality of through-holes allowing for communication of the electrode with the plating cell, such as those described in the Provisional U.S. Application No. 61/499,653, titled “Purging Micro-Containments During Electroplating” filed Jul. 1, 2011 by Feng et al.
Methods and apparatus for aligning and varying the amount of current and the sign of the current in time and space between the azimuthally asymmetric electrodes and the selected azimuthal positions on the wafer substrate, and for adjusting dwell times of selected azimuthal positions of the wafer in the proximity of thief cathodes, are provided.
In the embodiments presented herein, it is important that the position of the selected azimuthal region on the substrate (i.e., that region targeted for special treatment) be known prior to electroplating. Therefore, in the embodiments presented herein a selected azimuthal position is registered prior to electroplating, e.g., with an optical aligner. For example, a position of the notch on the wafer (selected azimuthal position) can be measured by a notch aligner. Some position and notch aligners use an optical measuring device, comprising a photodiode array, which is capable of acquiring a shadow image of the substrate and store it in a memory file, e.g., in a digital linear file. The registration of the notch position is determined, and with this knowledge, by computation relative to the notch, of the selected azimuthal region for special treatment, allows controlling the orientation of this azimuthal position throughout the plating process, and synchronization of shields and/or auxiliary electrodes (position and/or power applied) with a specific azimuthal region on the wafer, as desired. In a typical electroplating process provided herein, the position of a selected azimuthal portion of the substrate is known with respect to the indexing notch position prior to electroplating and during electroplating, allowing for orchestration of azimuthal current correction throughout the plating process. As a specific example, the wafers may be notch aligned inside the Front Opening Unified Pod (FOUP) prior to being placed onto the plating tool. In another example, the wafers pass through a notch aligning device just prior to undergoing plating. In a third example, the notch alignment is done on a plating tool as a initial step in the sequence of subsequent plating and/or non-plating operations (e.g. rinsing and chemical pretreatment, vacuum pretreating, surface pretreating, copper plating, nickel plating, lead-free solder plating, gold plating) wherein the change in the orientation of the wafer can be tracked as long as the operation in each chamber does not lead to a loss of registry (such as slipping in a wafer holding chuck).
In some embodiments, the methods and apparatus provided herein address corrections for both radial and azimuthal non-uniformity.
In some embodiments, radial plating uniformity control can be achieved through use of an ionically resistive ionically permeable element, positioned between the working electrode (the wafer substrate) and the counter electrode (the anode) during plating, in order to shape the electric field and control electrolyte flow characteristics. For example, an ionically resistive element having electrolyte-permeable 1-D (i.e., non-communicating) through-holes, where the element resides in close proximity of the wafer substrate has been found to be highly effective in this regard. One example of such an ionically resistive element is described in U.S. non-provisional application Ser. No. 12/291,356, entitled, “Method and Apparatus for Electroplating,” by Jonathan Reid et al., filed on Nov. 7, 2008, which is incorporated by reference herein for all purposes. The ionically resistive ionically permeable element described therein substantially improves radial plating uniformity on thin resistive seed layers. It is particularly useful when employed in combination with a second (thief) cathode or anode configured to divert or supply a portion of current from near-edge region of the wafer. It is also compatible with potential-controlled wafer entry, which is, in some embodiments, a preferred wafer entry process. The ionically resistive ionically permeable element serves for achieving a nearly constant and uniform current source in the proximity of the wafer (cathode) and has been referred to as a virtual anode. In contrast, an anode in the same close-proximity to the substrate would be significantly less apt to supply a nearly constant current to the wafer, but rather, would support a constant potential at the anode metal surface, thereby allowing the current to be greatest where the net resistance from the anode plane to the terminus (e.g. to peripheral contact points on the wafer) is smaller. So while the ionically resistive ionically permeable element has been referred to as a high-resistance virtual anode (HRVA), this does not imply that electrochemically the two are interchangeable. While the HRVA is certainly viewable as a “virtual current source”, i.e. it is a plane from which the current is emanating, and therefore can be considered a “virtual anode” because it is a source of anodic current flow, it is the relatively high-ionic-resistance of the element (with respect to the electrolyte) that leads to further advantageous, generally superior wafer uniformity when compared to having a metallic anode located at the same physical location. And of particular relevance to this disclosure is a preferred embodiment construct wherein a variable spacing, size and density of the 1-D HRVA holes in either the radial and/or the azimuthal array of holes creates a highly controllable, non-uniform source of current at the periphery. This, combined with the registration of the wafer angular position (notch) and the dwell/rotation rate with angular position, operates to correct for azimuthal non-uniformities in an analogous manner to having a shield blocking the source of current from an anode below the wafer.
Two features of the HRVA are of particular importance: the placement of HRVA in close proximity with respect to the wafer, and the fact that through-holes in the HRVA are spatially and ionically isolated from each other and do not form interconnecting channels within the body of HRVA. Such through-holes will be referred to as 1-D through-holes because they extend in one dimension, often, but not necessarily, normal to the plated surface of the wafer (in some embodiment the 1-D holes are at an angle with respect to the wafer which is generally parallel to the HRVA front surface). These through-holes are distinct from 3-D porous networks, where the channels extend in three dimensions and form interconnecting pore structures. An example of a HRVA is a disc made of an ionically resistive material, such as polyethylene, polypropylene, polyvinylidene difluoride (PVDF), polytetrafluoroethylene, polysulphone, polyvinyl chloride (PVC), polycarbonate, and the like, having between about 6,000-12,000 1-D through-holes. The disc, in many embodiments, is substantially coextensive with the wafer (e.g., has a diameter of about 300 mm when used with a 300 mm wafer) and resides in close proximity of the wafer, e.g., just below the wafer in a wafer-facing-down electroplating apparatus. Preferably, the plated surface of the wafer resides within about 10 mm, more preferably within about 5 mm of the closest HRVA surface.
The presence of a resistive but ionically permeable element close to the wafer substantially reduces the terminal effect and improves radial plating uniformity. It also simultaneously provides the ability to have a substantially spatially-uniform impinging flow of electrolyte directed upwards at the wafer surface by acting as a flow diffusing manifold plate. Importantly, if the same element is placed farther from the wafer, the uniformity of ionic current and flow improvements become significantly less pronounced or non-existent. Further, because 1-D through-holes do not allow for lateral movement of ionic current or fluid motion within the HRVA, the center-to-edge current and flow movements are blocked within the HRVA, leading to further improvement in radial plating uniformity.
Another important feature of the HRVA structure is the diameter or principal dimension of the through-holes and its relation to the distance between the HRVA and the substrate. Preferably the diameter of each through-hole (or of majority of through-holes), should be no more than the distance from the plated wafer surface to the closest surface of the HRVA. Thus, the diameter or principal dimension of the through holes should not exceed 5 mm, when HRVA is placed within about 5 mm of the plated wafer surface.
Thus use of a HRVA as described above can address radial non-uniformity. In order to address azimuthal non-uniformity additional features and methods are needed. Embodiments described herein include one or more components of the plating apparatus that compensate for the azimuthal asymmetry on the wafer surface during plating. More specifically, the one or more components of the plating apparatus shape the electric field in such a way so as to compensate for the azimuthal asymmetry on the wafer surface and thus provide highly uniform azimuthal plating in addition to highly uniform radial plating. “Azimuthal asymmetry” may refer to azimuthal non-uniformity in topography, the resultant plating current non-uniformity that results, the resultant field variations created by such local topography, or combinations thereof.
It is noted that in some embodiments, the HRVA plate can be used primarily or exclusively as an electrolyte flow shaping element, regardless of whether it tailors radial deposition uniformity or not. Thus, for example, in TSV and WLP electroplating, where metal is being deposited at very high rates, uniform distribution of electrolyte flow is very important, while radial non-uniformity control may be less necessary. Therefore the HRVA plate can be referred to as both ionically resistive ionically permeable element, and as a flow shaping element, and can serve from a deposition-rate corrective prospective in either altering the flow of ionic current, in altering the convective flow of material, or both.
Embodiments described herein address azimuthal non-uniformity using components of the plating apparatus that shape the field in such a way as to compensate for azimuthal topographical variation on the wafer during plating. More specifically, the wafer and these field shaping components are moved, in some embodiments, relative to one another in such a way that the localized field or fields produced by the components are proximate to the azimuthally asymmetric topographical features for which they are intended to compensate and thus uniform azimuthal plating is achieved. In embodiments described herein, control of the wafer rotation and/or shield rotation and/or the HRVA rotation and/or auxiliary electrode rotation can be accurately synchronized using one or more rotational digital encoders. Additionally, the localized shaped fields produced by components described herein need not always be proximate the areas of the wafer with azimuthally asymmetric topography, that is, the localized fields may only spend a disproportionate amount of time (referred to as “dwell”) proximate these areas relative to other portions of the wafer so that azimuthally uniform plating is achieved. This may be termed “azimuthal averaging.”
Since the methods described herein in some embodiments, involve one or more of the wafer and/or shields rotating relative to one another, the methods are sometimes referred to as “rotationally variable shielding” (RVS), and the apparatus as containing rotationally variable shields (RVS's). The azimuthally asymmetric shields used herein may include any of the azimuthally asymmetric shields described in the U.S. Pat. No. 6,919,010 issued on Jul. 19, 2005 to Mayer et al., and titled “Uniform electroplating of thin metal seeded wafers using rotationally asymmetric variable anode correction”, in the U.S. Pat. No. 7,682,498 issued on Mar. 23, 2010 to Mayer et al., titled “Rotationally asymmetric variable electrode correction” and in U.S. Pat. No. 6,027,631 issued on Feb. 22, 2000 to Broadbent et al., and titled “Electroplating system with shields for varying thickness profile of deposited layer”, which are all herein incorporated by reference.
Below is a short description of some operative characteristics of RVSs. Generally, as in the description herein, the RVS shield is a dielectric element that is located close to the wafer that serves to block lines of current from reaching the wafer from an anode position “below” (in the case where the anode is below the wafer) for a period of time when a particular portion of the wafer lies “above” the RVS shield. To be most highly effective, the RVS element should be positioned relatively close to the wafer so that current cannot circumvent the shield, flowing around the RVS element edges and into the bulk of the shielded area. The imprint or influence of the RVS is therefore limited by the “proximity focusing” of the element. To avoid significant smearing of the elements effects, the element's arc length (about an azimuth) at a particular distance from the center of rotation therefore should be several times (e.g. >3 times) the distance between the RVS shield and the wafer surface. For example, if the distance between the wafer and the RVS shield is 4 mm, the RVS shield would need to be about 12 mm in arc length to be highly effective. In designing a shield, in particular, for designing uniformity corrections at near the wafer center, these characteristic ratios may no longer need be used, and so modifications in the shape of the RVS as would be predicted by a “blocking model” may be required to compensate for the ability of current to travel around the RVS and significantly into the area behind the shield.
In some embodiments, the RVS shield is incorporated into the design of a HRVA plate. A “HRVA,” as used herein, is for convenience, because when used in this particular set of operations, the porous plate does not necessarily have to exhibit a relatively high resistance to the total cell electrolytic solution resistance to be functional as a rotationally variable shielding element. As mentioned above, it can also be referred as a flow shaping element. The HRVA plate can serve many purposes, for example, including but not limited to modifying the current distribution on the wafer, creating shearing flow between the rotation wafer and the plate, creating a high impinging flow up at the wafer surface, and flow turbulence. In some embodiments the HRVA plate is created by drilling a large number of holes (e.g. 6000 holes 0.5 mm in diameter over an approximately 300 mm diameter area) into a solid piece of dielectric material (e.g. a 0.5 inches thick piece of plastic such as polypropylene). With regards to the embodiments described herein, the RVS shield is then created by not drilling holes in the plate in a spatially regular pattern, but rather only into select areas and not into other area, in order to create the various current blocking patterns described herein as required by the RVS (as well as other techniques for selectively blocking predrilled holes are described below). In some embodiments, a select HRVA constructed with a particular holes pattern is used to create the shield pattern. In other embodiments only the RVS pattern is created in this manner, and peripheral extra holes in the HRVA can be blocked by placing shields of various sizes, angles, etc., allowing for modification of the shield performance as may be needed from time to time or from wafer-pattern to wafer-pattern. The HRVA having azimuthally asymmetric hole-free regions assumes a function of an azimuthally asymmetric shield.
For the purposes of simplicity, the following description assumes that there is a single feature or region of the wafer that has azimuthal asymmetry, for example, a sector of a wafer has die and non-die areas, or for example, a wafer where a chord or notch is cut from the wafer. Embodiments described herein also include methods and apparatus to achieve high azimuthal plating uniformity where there is azimuthal topographical variation, for example, in more than one area on the wafer, for example, where multiple dies are lithographed over most of the wafer's surface, and where there are non-die outlying areas near and around the entire perimeter of the wafer surface. In such instances, components are configured and/or methods performed, to compensate for such azimuthal asymmetry, as will be apparent to one of ordinary skill in the art in light of this description.
Unidirectional Wafer Rotation
In one embodiment, the wafer is rotated in a single direction, for example clockwise about an axis perpendicular to the surface of the wafer, and the components configured to produce a localized field proximate to the azimuthally asymmetric topographical features are varied in synchronization with respect to the rotating wafer in order to compensate for the azimuthal asymmetry and provide uniform azimuthal plating. Examples of this embodiment are described below. It is noted that these described embodiments are illustrated as used in conjunction with a unidirectionally rotated wafer, but, more generally, can be also used where the wafer rotates bidirectionally (both clockwise and counterclockwise) during electroplating and where the wafer rotates at constant or variable speed (including both unidirectionally and bidirectionally).
Segmented Auxiliary Electrode
In some embodiments, a second electrode, a (thief) cathode or source (anode) or an anode/cathode, includes several segments, where each of the segments can be separately powered by a separate power supply or using one power supply having multiple switches or channels adapted to independently power segments of the second cathode. Specifically, in one example, segments of a second cathode are used for providing plating current corrections at different azimuthal positions of the wafer as the wafer rotates. The current applied to any individual secondary electrode segment at any point in time may be positive, negative, or zero, with the sign and amount of current varying in time correlated and synchronized with the wafer angular position at that time. As it has been previously mentioned, any of the current, voltage, or a combination of these may be controlled, in order to correlate power provided to electrode (or a segment) with the rotation of the wafer.
In this multi-segmented electrode embodiment, the wafer substrate is first registered such that a position of a selected azimuthal portion on the wafer is known, is secured in the substrate holder in the electroplating apparatus such that its platable surface is immersed into electrolyte, and is rotated in the electroplating apparatus having a stationary multi-segmented thief cathode or anode source or an anode/cathode, which is configured to divert or supply additional current from or to the wafer edge in the limited area of the wafer periphery associated with the location and azimuthal extent of the particular electrode. The individual segments of the thief cathode or secondary anode source are disposed about different azimuthal positions, and can be powered separately, such that different levels of current can be applied to different segments of the thief cathode. The power applied to the segments is synchronized with the rotation of the substrate in such a manner that a selected portion of the substrate at a selected azimuthal position will experience a different amount of plating current diverted by a thief (or donated by an auxiliary anode), than an analogous portion (i.e. a portion of the average same arc length and same average radial position) of the substrate at a different azimuthal position. For example, a higher (or lower) level of thieving current may be applied to those segments of the thief cathode, which are located proximate the selected azimuthal position.
This concept is illustrated in
Because current density at the missing die region will be different than the current density at other regions of the wafer, a different amount of current needs to be diverted from the missing die part as compared with the other parts. Accordingly, in one embodiment, the thief cathode segments are powered in concert with wafer rotation, such that a first level of current is supplied to the segments aligned with the missing die region, while a second level of current is supplied to the thief segments aligned with the other portions of the wafer.
For example, in a position shown in
As it has been mentioned, this embodiment is not limited to the use of a multi-segmented thief cathode, but may also be used with a multi-segmented anode, or a multi-segmented anode/cathode. In a particularly preferred embodiment, the current of each element may be of an optimally determined waveform having a sequence of alternating current levels or signs during the period of wafer rotation. For example, by having a plating cell designed with an edge shield and/or HRVA that would create a generally thin deposit in regions of the wafer which are not missing die or features, and designed to give a generally thick set of features in the missing die/feature region, current adding and removing “pulses” to the wafer can be applied to the wafer as it rotates. Then the sign of each of the segments of the multi-segmented-electrode will change from anodic (supplying peripheral anodic current) when the thin majority edge is proximate, and cathodic (removing peripheral anodic current) when the minority thick region (missing die/feature region) is aligned and proximate.
It is understood that the presentation shown in
While the multi-segmented thief cathode is particularly useful with a HRVA disposed in close proximity of the wafer, this is a separate embodiment which can be used both independently and in combination with various plating apparatus features disclosed herein. In other embodiments, which will later be illustrated with reference to
Rotating HRVA having Non-uniform Distribution of 1D Through-holes
In another embodiment, the plating uniformity on azimuthally asymmetrical wafers can be adjusted by using a rotating asymmetrical HRVA. The asymmetrical HRVA can have a portion that has a different hole distribution pattern from the main portion, or a portion that is cut off, or a portion without holes altogether. The rotating HRVA is aligned with the rotating wafer such that a distinct portion of the wafer is aligned with a distinct portion of the HRVA. For example, a wafer having a wafer flat region or missing die can be rotated at the same speed as the rotating HRVA such that a region of HRVA having a non-uniform hole distribution (e.g., lower density of holes) is aligned with the wafer flat region during rotation.
This embodiment can be used separately or in combination with the auxiliary electrode and other features disclosed herein. In some embodiments using rotating asymmetrical HRVA, the HRVA does not need to be positioned in close proximity of the wafer.
Stationary HRVA with a Rotating Shield
In another embodiment, the plating uniformity control for an azimuthally asymmetrical wafer is achieved by using a rotating shield positioned above or below the HRVA. In some embodiments, the rotating shield is positioned in close proximity of the substrate (e.g., with a distance to the platable surface of the substrate within about 0.1 of the substrate's radius, such as within about 0.2 of the substrate's radius, and, preferably, within about 4 mm). The shield is configured to eclipse the HRVA holes and is shaped such as to compensate for non-uniformity of current density distribution at the regions of the wafer having azimuthally asymmetric topographical features. The shield is aligned with the wafer flat and rotates at the same speed as the wafer, providing a continuous adjustment to current density experienced by the region where azimuthal surface variation exists. The shield can have a variety of shapes, such as a wedge shape, a gingko leaf shape, a bat-wing shape, etc. The synchronization of the shield and wafer rotating speeds can be done using a controller having program instructions for synchronization. More generally, the HRVA is not necessary in some embodiments, and the rotating azimuthally asymmetric shield is aligned with a selected portion of the substrate at a selected azimuthal position and is rotated with the substrate at the same speed, such that the selected portion of the substrate at a selected azimuthal position dwells in the shielded area for a different amount of time than an analogous portion at a different azimuthal position.
The embodiments described above are within the scope of this invention, but may be regarded as having more moving parts than are necessary to achieve azimuthal plating uniformity. By rotating the wafer bidirectionally or at variable speed, many of the implementation difficulties associated with moving parts can be avoided.
Bidirectional Wafer Rotation.
In another embodiment, the components, configured to produce a localized field proximate to the azimuthally asymmetric topographical features, are fixed and the wafer is rotated bidirectionally, for example clockwise and counterclockwise about an axis perpendicular to the surface of the wafer, such that the synchronization between the wafer and the field shaping components is achieved and thus the azimuthal asymmetry on the wafer is compensated for and uniform azimuthal plating is achieved. The components include stationary azimuthally asymmetric shields (including a stationary HRVA with an azimuthally asymmetric distribution of holes), azimuthally asymmetric auxiliary electrodes (thief cathodes, anodes, and anode/cathodes) and multi-segmented auxiliary electrodes, having segments distributed at various azimuthal positions. Bidirectional rotation can be used such as to adjust a dwell time of a selected portion of the substrate at a selected azimuthal position in a shielded area, or in an area proximate to an auxiliary electrode (or an electrode segment) such that this dwell time is different from a dwell time of an analogous portion of a substrate at a different azimuthal position (having the same average arc length and same average radial position). For example, if the wafer is rotated clockwise and counterclockwise to a different degree, it will spend more time at certain azimuthal positions, relative to others. These positions may be selected such as to correspond to azimuthal positions that are shielded or that are proximate to an azimuthally asymmetric thief or a thief segment. For example, if the wafer is rotated clockwise by 360 degrees and counterclockwise by 90 degrees, it will spend more time in the sector between 270-360 degrees. Furthermore, bidirectional rotation can tends to reduce or eliminate any particular directional wafer flow field bias.
Segmented Auxiliary Electrode (Thief Cathode/Source Anode or Anode/Cathode) or an Azimuthally Asymmetric Auxiliary Electrode with Bidirectional Wafer Movement.
As described above, when a segmented thief cathode or an azimuthally asymmetric thief cathode, which is adapted for diverting a portion of current from the edge of the wafer, is used to compensate for azimuthal non-uniformities on a wafer, and when the wafer is rotated unidirectionally, one way to achieve azimuthal plating uniformity is to move the thief cathode synchronously with the wafer so that the appropriate localized field configured to compensate for the azimuthal non-uniformity remains registered with the selected area of the wafer for which it was designed to compensate. Such thief cathodes may be segmented so that more than one area has azimuthal plating correction, for example, where the segments are arranged appropriately on a support which rotates in sync with the wafer during plating.
If the wafer is moved bidirectionally in a manner described above, then the secondary thief cathode can remain stationary, as the selected azimuthal position of the wafer, e.g., a missing die region will have a different dwell time in the proximity of the auxiliary electrode or its segment than a different azimuthal position of the wafer. This obviates a number of mechanical complexities. One embodiment is a plating apparatus configured for bidirectional movement of a wafer, a segmented secondary thief cathode configured to divert the plating current, wherein the apparatus is configured to adjust the field to compensate for azimuthal non-uniformities on the wafer. In this embodiment in the bidirectional rotation, the wafer rotates clockwise and counterclockwise to a different degree (or rotates to the same degree without making a full rotation, e.g., over selected arc length), such that the selected portion of the wafer at a selected azimuthal position dwells in proximity of a thief cathode segment for a different time (e.g., longer) than an analogous portion of the substrate at a different azimuthal position. In some embodiments, the selected segment of the cathode is powered differently from other segments (e.g., has a different level of current applied or different polarity from other segments. Another embodiment is a method of plating including rotating the wafer bidirectionally, relative to a secondary segmented thief cathode, so as to compensate for azimuthal non-uniformities on the wafer during plating. Although this embodiment was illustrated with a thief cathode diverting current, it can also be used with an auxiliary multi-segmented anode or anode/cathode. In these embodiments the HRVA may or may not be present and may or may not be rotated during plating. Typically, but not necessarily, the HRVA is a symmetrical HRVA as opposed to an unsymmetrical HRVA as described above. The secondary auxiliary electrodes operate to manipulate the field as described herein, but are not moved during plating.
Azimuthally Asymmetric Shields
In some embodiments, the apparatus is configured for rotating the wafer bidirectionally and the apparatus includes one or more stationary azimuthally asymmetric shields, configured for restricting plating current in the proximity of the substrate. The shields may be used independent of the HRVA, and may be placed above or below the HRVA plate blocking the HRVA holes, or the shield may itself be the HRVA having azimuthally asymmetric distribution of through-holes. In some embodiments the bidirectional rotation is adjusted such that a selected portion of the substrate at a selected azimuthal position (e.g., proximate to a notch or a missing die) dwells in the shielded area for a different time than an analogous portion of the substrate at a different azimuthal position. This may be accomplished, for example, if clockwise and counterclockwise rotations are performed to different degrees, such as to create a longer dwell time of a selected azimuthal portion of the wafer in a certain shielded position. Below are non-limiting examples of various implementations of azimuthally asymmetric shielding.
Stationary HRVA with a Segmented or Irregular Annular Shield:
In one embodiment, the plating uniformity control for an azimuthally asymmetrical wafer is achieved by using a stationary HRVA with an attached azimuthally asymmetric shield, where the azimuthally asymmetric shield is an annular shield which has one or more segments removed and/or one or more areas disposed azimuthally about the annulus that impart azimuthal asymmetry to the annular shield. The wafer is rotated bidirectionally, for example one or more rotations clockwise and then one or more rotations counter clockwise, such that the wafer areas in need of azimuthal plating compensation are azimuthally averaged, that is, positioned over the appropriate segments and/or aforementioned areas appropriately to provide field shaping for the azimuthally uniform plating to occur. The adjustment of the dwell time of a specific azimuthal position over the shield via adjustment of wafer rotating speeds and/or directions can be done using a controller having program instructions for synchronization.
In one embodiment, symmetrical HRVA is used in combination with an annular shield that attaches to the HRVA. In one embodiment, the annular shield (or spacer) is affixed to the HRVA, and the annular shield has a sector removed, a feature or area that imparts asymmetry to the annulus. Typically, when bidirectional wafer rotation is employed, the HRVA and attached shield are not moved. In one embodiment, the annular shield has a sector removed, as depicted in
Referring to
Annular shield 300 can be attached to or proximate the circumference of the flow shaping plate and extending toward the rotating work piece. In some embodiments depicted here, the top surface of the edge element of the shield provides a very small gap (e.g., about 0.1 to 0.5 mm) between the bottom of the wafer holder and flow diverter over the majority of the region between a substrate holder periphery and the top of the edge element. Outside this region (between about 30 to 120 degrees arc), there is a gap in the edge element that provides a relatively low resistance path for electrolyte to flow out of the nearly closed chamber. In other embodiments, where there is no segment removed from the annular shield, i.e., there is an area that imparts azimuthal asymmetry, the shield may or may not be as close to the wafer depending upon, for example, the amount of desired electrolyte flow.
During plating, since the shield shapes the field differently in the sector defined by the cut out segment, the wafer is rotated back and forth, under the appropriate timing and synchronization with the shield, in order to achieve uniform azimuthal plating in the areas on the wafer with azimuthal non-uniformity.
In some embodiments the shield having an annular shape with a removed sector is not affixed to the HRVA but is rotated during electroplating, preferably at a speed that is different than the speed of the wafer, which helps optimize the flow of electrolyte in the proximity of the wafer.
As discussed, the annular shield need not be segmented. For example, it may include a portion that imparts azimuthal asymmetry (in one embodiment, the shield includes both at least one segmented portion and at least one portion that imparts azimuthal asymmetry).
It is important to note that although shield 300 is depicted as having uniform thickness (dimension B as depicted in
The shape of the portion of the annular shield (or independent shield described herein) may be tailored to accommodate not only azimuthal plating non-uniformity but also radial non-uniformity. Referring to
As described, these non-uniformities in the field created by the various combinations of shielding and thieving described herein are exploited by combining plating time and synchronization with or without the asymmetric portion of the field to compensate for azimuthal non-uniformities on the wafer surface and achieve uniform azimuthal plating. In the embodiments described in this section, bidirectional wafer rotation is used in combination with the shields described. The timing and synchronization will depend on, among other factors, the azimuthal non-uniformities on the wafer, the shield configuration, the amount of plating desired, the rate of plating, and the like. The synchronization of the shield features with certain areas of the wafer, wafer rotation speeds and rotation direction can be done using a controller having program instructions for synchronization. Since the areas of the wafer with azimuthal non-uniformities wafer will spend a certain period of time over (or synchronized with) certain features of the shield, the described methods for obtaining azimuthal plating uniformity are sometimes referred to as “dwell shielding” methods. To obtain a particular “dwell” over a shield, the wafer may be rotated at a certain rotation rate or speed (vs a rate over a non-shielded area), the shield may be wider, the wafer rotated a certain arc to ensure dwell time, and combinations of these.
Stationary HRVA with a Segmented or Irregular Annular Shield and One or More Additional Fixed Shields
In another embodiment, the plating uniformity control for an azimuthally asymmetrical wafer is achieved by using an annular shield as described in the previous section, for example a segmented shield attached to a symmetrical HRVA, in addition to one or more fixed shields in between the annular shield and the wafer. The one or more fixed shields are configured to eclipse the HRVA holes and are shaped such as to compensate, along with bidirectional rotation of the wafer and the segmented annular shield, for non-uniformity of current density distribution at the regions of the wafer having azimuthally asymmetric topographical features (and to compensate for radial non-uniformity).
In one embodiment, the number of fixed shields, N, used in conjunction with shield 300 is defined by a formula, N=360°/Ω. For example, when Ω is 90° as in
There are advantages to both having separate shields as depicted in
It is also important to note that the shields described thus far in relation to a HRVA are described in terms of additional components, that is, separate from the HRVA. This need not be so. For example,
During plating, the wafer is rotated, for example bidirectionally, over the HRVA and shields in order to obtain uniform plating both radially and azimuthally. For example, referring to the shield arrangements in any of
Plating with Variable Rotation Wafer Speed
It is important to note that although the embodiments described above are in terms of unidirectional or bidirectional wafer rotation where the rotation is a portion of a full 360 degrees rotation, azimuthal corrections can also be performed by using variable speed wafer rotation. That is, if a wafer is rotated at a certain angular speed, R1, over a given area, for example a holed area of the HRVA, and then rotated at a different angular speed, R2, over another area, for example a shielded area, the similar results can be obtained. That is, varying the rotation speed during any individual full rotation is one way to adjust and obtain azimuthal variable amounts of time-averaged shielding to which the wafer is exposed. One embodiment is any of the above described embodiments, where the wafer speed is varied during each rotation, or alternatively, the speed may be varied during a single rotation or in some rotations and not others. Also, the wafer speed may be varied only while spinning in one direction of rotation (e.g. clockwise) and not the other direction (e.g. counterclockwise), or it may be varied in both rotational directions. One embodiment is any embodiment described in relation to bidirectional wafer rotation, but using either unidirectional rotation where the rotation speed is varied during one or more single rotations or a bidirectional rotation where the rotation speed is varied.
These processes are illustrated by the process flow diagrams shown in
It is understood that in some embodiments, where multiple shields and/or multiple thief segments are contained in the apparatus, and/or where the wafer contains multiple selected areas where azimuthal uniformity needs to be corrected, one full rotation of the wafer may include multiple periods of alternating slower and faster rotation, such as to register the required shields and/or thieves with all the necessary selected azimuthal portions.
It is also noted that both bidirectional rotation and variable speed rotation uniformity correction methods can be characterized by the capacity to provide different dwell times for a selected portion of a substrate at a selected azimuthal position relative to dwell times of an analogous portion of the substrate at a different azimuthal positions, wherein the dwell times refer to dwell of the selected portion in a shielded area on in a proximity of a thief cathode (or its segment). As it has been previously mentioned, these embodiments may be also used with other types of auxiliary electrodes, such as auxiliary azimuthally asymmetric anodes, and anode/cathodes, as well as multi-segmented anodes and anode/cathodes.
A schematic simplified cross-sectional view of an electroplating apparatus, in accordance with one exemplary embodiment presented herein, is shown in
Preferably, in order to optimally control the uniformity, both the flow shaping element and the shield are positioned in close proximity to the substrate. In some embodiments the distance from a bottom surface of the substrate holder during electroplating and the top surface of the flow shaping element is between about 1 and 5 mm. The shield 917 preferably resides within about 4 mm of the bottom surface of the substrate holder.
In some embodiments the flow shaping element is between about 5 mm and about 10 mm thick and the substrate-facing surface of the flow shaping element is separated from the plating face of the substrate by a distance of about 10 millimeters or less, more preferably by a distance of about 5 millimeters or less during electroplating. In some embodiments, the flow shaping element is a disk having between about 6,000-12,000 channels.
The wafer 911 typically has a plurality of electrical contacts made to a periphery of the wafer, and is electrically connected to a negative terminus of a power supply (not shown), such that the wafer, having a conductive layer thereon, serves as a cathode during electroplating. The positive terminus of the power supply is electrically connected to the anode 905. When potential difference is applied, an ionic current, which moves ions of platable metal and protons to the wafer surface, results. The ions of metal are reduced at the wafer surface, forming a layer of electroplated metal on the surface of the substrate. The uniformity of plated layers depends on distribution of the plating field in the proximity of the substrate, which in turn, can be adjusted by shielding with the azimuthally asymmetric shield 917, and current diversion with the azimuthally asymmetric thief 915, using methods provided herein.
A controller 919, electrically connected to the components of the electroplating apparatus 901 includes program instructions, specifying necessary parameters for electroplating, such as levels of current applied to the wafer and the thief, parameters related to delivery of electrolyte to the plating bath, and speeds of rotation of the substrate and direction of rotation. The controller 919 includes program instructions for performing all methods described herein, such as registering the selected azimuthal position of the wafer such that it dwells differently in the shielded area or in the proximity of the thief in comparison with an analogous region of the wafer at a different azimuthal position. The controller will typically include one or more memory devices and one or more processors. The processor may include a CPU or computer, analog and/or digital input/output connections, stepper motor controller boards, etc.
In certain embodiments, the controller controls all of the activities of the deposition apparatus. The system controller executes system control software including sets of program instructions for controlling wafer rotation speeds, registration of azimuthal position, etc.
Typically there will be a user interface associated with controller. The user interface may include a display screen, graphical software displays of the apparatus and/or process conditions, and user input devices such as pointing devices, keyboards, touch screens, microphones, etc.
The computer program code for controlling the deposition processes can be written in any conventional computer readable programming language: for example, assembly language, C, C++, or others. Compiled object code or script is executed by the processor to perform the tasks identified in the program.
It is understood that the depiction shown in
The apparatus and methods described herein may be used in conjunction with lithographic patterning tools or processes, for example, for the fabrication or manufacture of semiconductor devices, displays, LEDs, photovoltaic panels and the like. Typically, though not necessarily, such tools/processes will be used or conducted together in a common fabrication facility. Lithographic patterning of a film typically comprises some or all of the following steps, each step enabled with a number of possible tools: (1) application of photoresist on a workpiece, i.e., substrate, using a spin-on or spray-on tool; (2) curing of photoresist using a hot plate or furnace or UV curing tool; (3) exposing the photoresist to visible or UV or x-ray light with a tool such as a wafer stepper; (4) developing the resist so as to selectively remove resist and thereby pattern it using a tool such as a wet bench; (5) transferring the resist pattern into an underlying film or workpiece by using a dry or plasma-assisted etching tool; and (6) removing the resist using a tool such as an RF or microwave plasma resist stripper. One embodiment is a method as described herein further including: applying photoresist to the wafer after electroplating for both radial and azimuthal uniformity; exposing the photoresist to an energy source; patterning the resist and transferring the pattern to the wafer; and selectively removing the photoresist from the wafer. One embodiment is system including an apparatus as described herein further comprising a stepper. In some embodiments, used in TSV and WLP processing, the photoresist is applied and patterned to provide a surface having one or more recessed features prior to electroplating; the features are filled with metal during electroplating, and the photoresist is removed after electroplating.
In the preceding sections the auxiliary electrodes, such as azimuthally asymmetric and multi-segmented electrodes were primarily exemplified by thief cathodes,—negatively biased electrodes which are configured to divert ionic (plating) current. It is herein provided that in other embodiments—auxiliary azimuthally asymmetric and auxiliary multi-segmented anodes,—positively biased electrodes which are configured to donate plating current, are used to make azimuthal corrections, instead of thieves. Yet in other embodiments, azimuthally asymmetric and multi-segmented electrodes configured to function both as an anode and a cathode (also referred to as anode/cathodes) are used instead of thieves. The anode/cathode is configured to be biased positively (anodically) for a portion of a time, such that it is able to donate current, and negatively (cathodically) for another portion of time during electroplating, when it is configured to divert current and functions as a current thief. Embodiments provided herein include any of the embodiments described above, where instead of a thief cathode, an auxiliary anode, or an auxiliary anode/cathode is used.
In general, thief cathodes, auxiliary anodes, and auxiliary anode/cathodes are referred herein to as auxiliary electrodes. These include azimuthally asymmetric electrodes (such as C-shaped electrodes) and multi-segmented auxiliary electrodes.
The auxiliary anode may be an inert anode or dimensionally stable anode, for example generating oxygen gas, or it can be a metallic anode, creating metal ions of the plated metal. The auxiliary cathode may undergo metal plating thereupon during use, or may undergo another cathodic reaction, such as hydrogen evolution. Hydrogen evolution rather than metal plating can be enabled if plateable metal ions are excluded from the electrode's surface, for example, by having the auxiliary electrode exposed to a metal free solution, such as a solution containing only acids or non-plateable salts, and having the auxiliary electrode to be physically separated from the main chamber so as to avoid mixing of materials containing plating metal, but such that it is still in ionic communication with the main plating chamber (housing the wafer) via an ionically conducting media that is resistant to fluid transport (e.g. a cationic membrane).
The use of an auxiliary anode or an anode/cathode is sometimes preferable, because metal is deposited on thief cathodes during electroplating in many embodiments, which may lead to formation of stray particles, flaking of the metal, and contamination of the plating bath. In contrast, auxiliary anodes are positively biased, and deposition of metal on their surface is avoided. Further, in some embodiments, an anode/cathode, which spends more time being positively biased than negatively biased, is preferred for the same reason, i.e. there is a net anodic current and therefore no net buildup of metal on the electrode over the processing complete cycle. Such anode/cathode with a “net” anode function , would not accumulate deposits of metal on its surface, because any metal deposited on it during its cathodic phase would be redissolved during its anodic phase.
The auxiliary anodes and anode/cathodes are most preferably used in conjunction with shielding, because a shield, such as a symmetrical annular shield placed below the wafer to uniformly shield the wafer periphery, can render the surface of the wafer (e.g., at its periphery) generally deficient in plating current (a “cold” area that would result in thinner than desired plating). The primary parameter influencing the magnitude of the symmetrical annular shields' effectiveness and range of area of influence causing the edge-region-deficient plating relative to more centrally located regions of the wafer is shields' size (the shields inner-most diameter of current blocking). The asymmetry of the wafer will introduce one or more regions at one or more azimuthal positions that are more or less deficient in current than the rest of the wafer. By using an appropriately selected shield size, azimuthal regions of wafer near missing die or features can be tuned to exhibit somewhat thicker-than-average features, while simultaneously; azimuthal regions of the wafer without missing die/feature will then tend to be deficient in current and thickness. Using a shield that blocks more of the edge (smaller inner diameter) might create a situation where both the missing die regions and the general edge regions are both deficient, but the missing die region is somewhat less deficient than the general edge. Or, a shield having an inner diameter larger than both of the preceding two examples might be selected, in which case both the general edge and the missing die edge are thicker than the wafer center, but the missing die region features are the thickest on the wafer. The auxiliary “C” shaped electrode can then correct for any other these cases, i.e. both cases of excess and for deficiencies, by donating or scavenging edge plating current to a different extent and/or different sign (anodic vs. cathodic) at different azimuthal locations. The auxiliary anode/cathodes can correct this problem by donating current to a selected azimuthal positions of the wafer (during the time the anode/cathode is positively biased) and by diverting current from a different azimuthal position of the wafer (during the time the anode/cathode is negatively biased).
In some embodiments, for example with heavy shielding of wafer periphery, the wafer periphery may be very “cold”, while the missing die refion is less “cold”, such that all azimuthal positions require current donation by an auxiliary anode, but to a different extent. This is illustrated in
In some embodiments, for example when the shielding is light the cathodic current level provided to the anode/cathode may be substantially greater than an anodic current level. This is illustrated, for example, in
Yet in another embodiment, e.g., with little or no general symmetric shielding, the auxiliary C-shaped electrode can function as a cathode only. That is, a first level of cathodic current is supplied to the electrode when it is in the proximity of the selected azimuthal position, and a different level of cathodic current is supplied when the selected position is rotated away from the C-shaped auxiliary cathode. Thus, during one full rotation of the wafer, the electrode spends a portion of time biased as a cathode at a first power level (or current level) and a portion of time biased as a cathode at a different power level (or current level), where the power levels are correlated with the rotation of the wafer in such a way as to provide a specific correction to a selected azimuthal position of the wafer.
Note that even in the absence of a missing die or feature region, the application of current (anodic or cathodic) can be used to tune the general edge thickness distribution, and therefore, the use of the apparatus is not limited to operations with wafers having azimuthally non-uniform patterns. Rather, this design is useful for both cases of edge corrections, those having and those not having azimuthal non-uniform patterns.
The embodiment illustrated in
In an alternative embodiment, azimuthally asymmetric electrodes (e.g., C-shaped anodes, cathodes or anode/cathodes) or multi-segmented electrodes are found useful even when a constant power level is applied to them for general correction of plating current.
The position of the electrode relative to the wafer edge, and/or confinement of the auxiliary electrodes line of current, can be of significant importance. In some embodiments, it is preferable that the auxiliary electrode (such as a C-shaped anode, cathode or anode/cathode) resides in close proximity of the wafer substrate. Preferably, the distance between the substrate and the electrode should be no more than 0.2 of the radius of a circular substrate. At this distance, the electrode is particularly effective at correcting ionic current environment at the substrate surface. At larger distances, the auxiliary electrode effect will be much less pronounced because ionic current diversion/donation will be less preferentially-favored right in front of the electrode face, and diffused over a larger area of the wafer comprising many azimuthal positions, potentially making the control of the process somewhat more difficult. However, in close proximity the diversion and/or donation of current by the electrode can be focused on the specific azimuthal region that needs to be corrected. The auxiliary anodes provided herein are distinct from the azimuthally asymmetric anodes located at larger distances from the wafer.
Alternatively, or in addition to proximity focusing described above, the auxiliary electrode may be housed in a confinement structure, which prevents the donated/diverted current from being substantially distributed in the x-y direction. A top view of the apparatus having a C-shaped auxiliary electrode 1103 in an azimuthal current flow confinement structure 1101 is shown in
It is noted that with the use of confinement or virtual chambers, the shape of the physical electrode itself becomes less important, as the shape of the diverted and/or donated current will be defined by the shape of the confinement structure housing the electrode or its opening, where the confinement structure essentially serves as a virtual auxiliary electrode.
It is understood that some aspects of the invention pertaining to the azimuthal correction described herein can be applied to many other film deposition and removal applications beyond electrodeposition, with the appropriate application and consideration of the known-in-the art differences in the physical mechanism and modus-operandi of other deposition and removal technologies. For example, a C-shaped or horse-shoe auxiliary target would be suitable to enable azimuthal variable rates of deposition on a rotating substrate, or an asymmetric physical mask placed similar to that described here, in front of a rotating wafer inside a plasma etching apparatus, would lead to an angularly controllable rate of etching at the edge and at a particular angular location on the wafer edge.
Electroplating apparatus as described herein includes hardware for accomplishing the process operations and a system controller having instructions for controlling process operations in accordance with the present invention. For example, a rotational digital encoder, wafer holder that rotates the wafer, any moving shield elements, HRVA, power levels applied to the auxiliary asymmetric or multi-segmented electrodes, etc. are controlled and synchronized by a system controller. The system controller will typically include one or more memory devices and one or more processors configured to execute the instructions so that the apparatus will perform a method in accordance with the present invention. Machine-readable media containing instructions for controlling process operations in accordance with the present invention may be coupled to the system controller.
This application is a continuation claiming priority to U.S. patent application Ser. No. 14/987,170, titled “Electroplating Apparatus for Tailored Uniformity Profile” naming Mayer et al. as inventors, filed Jan. 4, 2016, which is a continuation claiming priority to U.S. patent application Ser. No. 14/483,942, titled “Electroplating Apparatus for Tailored Uniformity Profile” naming Mayer et al. as inventors, filed Sep. 11, 2014 (issued as U.S. Pat. No. 9,260,793 on Feb. 16, 2016), which is a continuation claiming priority to U.S. patent application Ser. No. 13/438,443, titled “Electroplating Apparatus for Tailored Uniformity Profile” naming Mayer et al. as inventors, filed Apr. 3, 2012 (issued as U.S. Pat. No. 8,858,774 on Oct. 14, 2014), which claims benefit under 35 U.S.C. § 119(e) to U.S. Provisional Patent Application No. 61/471,624, titled “Electroplating Apparatus for Tailored Uniformity Profile”, naming Mayer et al. as inventors, filed Apr. 4, 2011 and to U.S. Provisional Patent Application No. 61/598,054, titled “Electroplating Apparatus for Uniform Electrolyte Flow Distribution” naming Buckalew et al. as inventors, filed Feb. 13, 2012, which are herein incorporated by reference. U.S. patent application Ser. No. 13/438,443 is also a continuation-in-part claiming priority to U.S. patent application Ser. No. 12/291,356, titled “Method and Apparatus for Electroplating” naming Reid et al. as inventors, filed Nov. 7, 2008, now U.S. Pat. No. 8,308,931, issued Nov. 13, 2012, which is herein incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 61598054 | Feb 2012 | US | |
| 61471624 | Apr 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14987170 | Jan 2016 | US |
| Child | 16007800 | US | |
| Parent | 14483942 | Sep 2014 | US |
| Child | 14987170 | US | |
| Parent | 13438443 | Apr 2012 | US |
| Child | 14483942 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12291356 | Nov 2008 | US |
| Child | 13438443 | US |