Patent Grant
7119033
This invention relates generally to the field of integrated circuit design and fabrication. Specifically, the invention relates to ion-assisted oxidation methods and the structures formed thereby.
Silicon oxide is used in integrated circuit (IC) and semiconductor fabrication, especially metal-oxide-semiconductor (MOS) fabrication, due to its excellent dielectric properties for insulation and field enhancement. See, for example, U.S. Pat. Nos. 4,776,925 and 5,521,126, the disclosures of which are incorporated herein by reference. Silicon oxide, both doped and undoped, is especially useful for fabrication of transistors. A transistor is typically fabricated by growing a gate structure containing a gate dielectric and a gate conductor on the surface of a silicon substrate, followed by forming source and drain regions in portions of the substrate flanking the gate structure. Unfortunately, the gate dielectric will be etched partially during the dry etch of the gate conductor. A thinner gate dielectric along the gate conductor edge will degrade the gate dielectric intensity and increase the gate-induced drain leakage. In order to eliminate these problems, the gate dielectric needs to be re-grown.
A high-temperature (greater than about 700° C.) oxidation is often used in the IC industry to re-grow the gate dielectric. High-temperature oxidation, however, can cause problems such as changes in impurity profiles, non-uniform oxide thicknesses along the side wall of the gate conductor, and defect formation in the underlying substrate. When certain metals, such as tungsten, are used as the gate conductor, a high-temperature oxidation process can form materials, such as tungsten oxide, that are volatile and can cause product yield loss.
Different oxidation techniques, such as plasma oxidation and anodization, have been proposed to reduce the temperature necessary to re-grow gate dielectrics. Most of these low-temperature techniques, however, fail to produce the high-quality gate dielectric necessary to maintain good gate dielectric integrity and low leakage.
The present invention provides methods of oxidization using vertical ion bombardment in an oxidant-containing atmosphere. Specifically, the present invention forms an oxide layer on source and drain regions of a substrate by re-oxidizing an oxide layer previously formed thereon. The re-oxidation is performed by vertically bombarding the previously formed oxide layer with inert ions in an atmosphere containing at least one oxidant.
The present invention includes an oxidation method which provides an oxide layer on a substrate and then re-oxidizes the oxide layer by vertical ion bombardment in an atmosphere containing at least one oxidant. The oxide layer may be provided over diffusion regions, such as source and drain regions, in a substrate. The oxide layer may also flank a gate structure provided on the substrate. The at least one oxidant may be oxygen, water, ozone, hydrogen peroxide, or a mixture thereof. The atmosphere may also contain hydrogen. The ion bombardment may use krypton (Kr), helium (He), or argon (Ar) ions, at a temperature ranging from about 25° C. to about 700° C., at an energy ranging from about 100 to about 300 eV, and for a time ranging from about 5 minutes to about 500 minutes.
The present invention permits a high-quality thin oxide layer to be formed at relatively low temperatures when compared with conventional techniques. Low-temperature oxidation leads to fewer thermal stresses, fewer crystal defects, less wafer warpage, and reduction of oxidation-enhanced diffusion. The present invention also allows less oxidation of the sidewalls of conductive layers in transistor gate structures to occur during oxidation. The present invention also facilitates fabrication of a transistor exhibiting lower amounts of current leakage to source and drain regions during operation.
The figures presented in conjunction with this description are not actual views of any particular portion of an actual semiconductor device or component, but are merely representations employed to clearly and fully depict the present invention.
The present invention provides ion-assisted oxidation methods and the structures formed thereby. The ion-assisted oxidation methods are employed to form a high-quality oxide layer over source and drain regions of a substrate. The ion-assisted oxidation methods form this high-quality oxide layer when inert ions, such as argon, vertically bombard a pre-existing oxide layer on the substrate or structures thereof in an atmosphere containing at least one oxidant, thereby increasing the quality and thickness of the pre-existing oxide layer. The energy for forming the high-quality oxide layer comes from the energy of the inert ions, rather than a high temperature.
The following description provides specific details such as material thicknesses and types in order to provide a thorough understanding of the present invention. The skilled artisan, however, would understand that the present invention may be practiced without employing these specific details. Indeed, the present invention can be practiced in conjunction with fabrication techniques conventionally used in the industry.
The process steps and structures described below do not form a complete process flow for manufacturing IC devices, the remainder of which is known to those of ordinary skill in the art. Accordingly, only the process steps and structures necessary to understand the present invention are described.
A preferred method of practicing the present invention is illustrated in
Dielectric layer 4 is then formed over semiconductor substrate 2. Dielectric layer 4 isolates the overlying gate electrode, as described below, from the upper surface of semiconductor substrate 2. Accordingly, any suitable dielectric material can be employed as dielectric layer 4, such as undoped or doped silicon oxide, boron- and/or phosphorous-doped silicate glass, silicon oxynitride, silicon nitride, or a composite layer containing these materials. Preferably, dielectric layer 4 is a silicon oxide layer formed by a suitable thermal oxidation process, such as oxidizing the preferred silicon substrate 2 in an atmosphere containing oxygen for about 60 to about 200 minutes at about 750 to about 950° C.
Next, conductive layer 6 is deposited. Since conductive layer 6 will form the gate electrode, any suitable gate electrode material may be employed. Preferably, conductive layer 6 is a doped polysilicon layer. Preferred polysilicon layer 6 may be formed by any suitable deposition method known in the art, such as physical or chemical vapor deposition. Preferably, preferred polysilicon layer 6 is deposited by low-pressure chemical vapor deposition (LPCVD) to a thickness ranging from about 1000 to about 5000 angstroms. Preferred polysilicon layer 6 can be in-situ doped during deposition by including a gas containing the desired dopant in the deposition atmosphere. Second conductive layer 8 comprising a material with a lower resistance and lower melting point than the material of conductive layer 6 may optionally be deposited over conductive layer 6. When conductive layer 6 is doped polysilicon, second conductive layer 8 may be tungsten silicide, titanium silicide, a titanium nitride and tungsten mixture, a tungsten nitride and tungsten mixture, a titanium nitride and molybdenum mixture, or the like.
Second dielectric layer 10 may optionally be formed over conductive layer 6 or second conductive layer 8. Second dielectric layer 10 comprises any suitable dielectric material used in the art, such as undoped or doped silicon oxide, boron- and/or phosphorous-doped silicate glass, silicon oxynitride, silicon nitride, or a composite layer containing these materials. Preferably, second dielectric layer 10 comprises silicon oxide or silicon nitride. Second dielectric layer 10 may be formed by any suitable deposition process, such as LPCVD.
As depicted in
Diffusion regions 12, such as source/drain regions, are then formed in semiconductor substrate 2. Diffusion regions 12 can be formed by any suitable process known in the art, such as by doping or ion implanting a suitable dopant, such as B, As, or P, through oxide layer 3 at an energy and dose sufficient to form the desired dopant concentration and profile.
Next, as illustrated in
In a preferred vertical ion-assisted bombardment (VIAB) method, oxide layer 14 is formed by re-oxidizing oxide layer 3. During the etching process used to fabricate gate structure 16 and the doping or implanting process used to form diffusion regions 12, oxide layer 3 is damaged. Thus, damaged oxide layer 3 is re-oxidized to form oxide layer 14 to repair this damage. The re-oxidation is preferably performed by “vertical” ion-bombardment, meaning that ions vertically bombard oxide layer 3 in the process of forming oxide layer 14, with little to no ion-bombardment of sidewalls 18 of gate structure 16. Thus, the only oxidation occurring is the re-oxidation of oxide layer 3, with little to no oxidation of sidewalls 18. This re-oxidation is “ion-assisted” bombardment, meaning that ions bombard the oxygen in oxide layer 3 and give the oxygen the necessary energy to re-oxidize and form oxide layer 14. In contrast, in high-temperature oxidation methods, the energy for oxide growth is derived from the higher temperatures.
This VIAB method is performed in an atmosphere containing at least one oxidant and hydrogen. The oxidant may be any gas containing oxygen, such as oxygen (O2), water (H2O), ozone (O3), or hydrogen peroxide (H2O2), or a mixture thereof. Preferably, water is employed as the oxidant in the present invention. Any concentration of the oxidant can be used, provided it sufficiently re-oxidizes oxide layer 3 with the desired selectivity (e.g., forms oxide layer 14 to the desired thickness without oxidizing sidewalls 18). For example, the flow of water in the atmosphere can range from about 1 to about 500 sccm, and preferably is about 50 sccm.
The atmosphere also contains hydrogen as well as at least one oxidant. Hydrogen is included in the ambient because hydrogen helps reduce oxide growth on sidewalls 18 during the VIAB process. Any concentration of hydrogen can be used in the ambient, provided it sufficiently prevents oxide growth on sidewalls 18. For example, the flow of hydrogen in the ambient can range from about 1 to about 200 sccm, and is preferably about 10 sccm.
The ambient also contains a source for the inert ions which are used in the bombardment process. Any suitable source for the inert ions can be used, such as KR, He, or Ar gas. Preferably, argon gas is used as the source of the inert ions.
The VIAB method is performed at a temperature sufficient to provide the desired selectivity. The temperature should be kept as low as possible to avoid imparting more energy than necessary to the oxygen used to form oxide layer 14. More energy imparted to the oxygen via a higher temperature results in more oxide growth on sidewalls 18. The temperature in the preferred VIAB method can range from about 25° C. to about 700° C., and preferably is about 400° C.
The VIAB method of the present invention is performed for a time sufficient to grow the desired thickness of oxide layer 14 without growing an oxide layer on sidewalls 18. For example, to obtain an oxide layer 14 thickness of about 50 Å to about 100 Å, the length of the preferred VIAB process can range from about 5 minutes to about 500 minutes. Preferably, for such a thickness of oxide layer 14, the length of the preferred VIAB process is about 100 minutes.
The VIAB process is performed at an energy sufficient to excite the inert ions and impart the necessary energy to the oxygen and grow oxide layer 14 to the desired thickness. Preferably, the energy may range from 1 to about 300 eV, and more preferably is about 100 eV.
Since the VIAB process proceeds via vertical ion bombardment, it is desired that little to no lateral oxide growth occur on the sidewalls 18 of conductive layer 6 or second conductive layer 8. Accordingly, the parameters (e.g., time, temperature, energy, etc.) described above should be selected to minimize this lateral growth when possible. Preferably, this lateral growth during the VIAB process may be up to about 100 angstroms. More preferably, this lateral growth during the VIAB process is about 10 angstroms.
Subsequent processing steps can then be undertaken to form the desired IC device. For example, dielectric sidewall spacers 20 for gate structure 16 can be formed, contact holes can be formed in oxide layer 14, and a patterned metal layer 22 can be formed to achieve desired metal contacts.
While the preferred embodiments of the present invention have been described above, the invention defined by the appended claims is not to be limited by particular details set forth in the above description, as many apparent variations thereof are possible without departing from the spirit or scope thereof.
This application is a continuation of application Ser. No. 09/934,916, filed Aug. 22, 2001, now U.S. Pat. No. 6,770,538, issued Aug. 3, 2004, which is a continuation of application Ser. No. 09/146,710, filed Sep. 3, 1998, now U.S. Pat. No. 6,355,580, issued Mar. 12, 2002.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3849276 | Greiner | Nov 1974 | A |
| 3943542 | Ho et al. | Mar 1976 | A |
| 4351712 | Cuomo et al. | Sep 1982 | A |
| 4652463 | Peters | Mar 1987 | A |
| 4776925 | Fossum et al. | Oct 1988 | A |
| 4784975 | Hofmann et al. | Nov 1988 | A |
| 4864375 | Teng et al. | Sep 1989 | A |
| 4902647 | Chutjian et al. | Feb 1990 | A |
| 4945867 | Hosaka | Sep 1990 | A |
| 4997746 | Greco et al. | Mar 1991 | A |
| 5146291 | Watabe et al. | Sep 1992 | A |
| 5183775 | Levy | Feb 1993 | A |
| 5210056 | Pong et al. | May 1993 | A |
| 5219773 | Dunn | Jun 1993 | A |
| 5279978 | See et al. | Jan 1994 | A |
| 5344793 | Zeininger et al. | Sep 1994 | A |
| 5349467 | Sulzbach et al. | Sep 1994 | A |
| 5382820 | Yang et al. | Jan 1995 | A |
| 5387546 | Maeda et al. | Feb 1995 | A |
| 5427962 | Sasaki et al. | Jun 1995 | A |
| 5436481 | Egawa et al. | Jul 1995 | A |
| 5508368 | Knapp et al. | Apr 1996 | A |
| 5521126 | Okamura et al. | May 1996 | A |
| 5527718 | Seita et al. | Jun 1996 | A |
| 5536679 | Park | Jul 1996 | A |
| 5702849 | Sakata et al. | Dec 1997 | A |
| 5723896 | Yee et al. | Mar 1998 | A |
| 5759900 | Suh | Jun 1998 | A |
| 5811326 | Yamamoto | Sep 1998 | A |
| 5836772 | Chang et al. | Nov 1998 | A |
| 5847427 | Hagiwara | Dec 1998 | A |
| 5885877 | Gardner et al. | Mar 1999 | A |
| 5915190 | Pirkle | Jun 1999 | A |
| 5930617 | Wu | Jul 1999 | A |
| 5965926 | Schwalke | Oct 1999 | A |
| 6010936 | Son | Jan 2000 | A |
| 6022794 | Hsu | Feb 2000 | A |
| 6037639 | Ahmad | Mar 2000 | A |
| 6097062 | Gardner et al. | Aug 2000 | A |
| 6097069 | Brown et al. | Aug 2000 | A |
| 6110278 | Saxena | Aug 2000 | A |
| 6110794 | Liu | Aug 2000 | A |
| 6124216 | Ko | Sep 2000 | A |
| 6127248 | Kim | Oct 2000 | A |
| 6198142 | Chau et al. | Mar 2001 | B1 |
| 6221743 | Fujikawa et al. | Apr 2001 | B1 |
| 6306712 | Rodder et al. | Oct 2001 | B1 |
| 6355580 | Li et al. | Mar 2002 | B1 |
| 6429496 | Li et al. | Aug 2002 | B1 |
| 6559027 | Ishitsuka et al. | May 2003 | B1 |
| 6566703 | Liang et al. | May 2003 | B1 |
| 6770538 | Li et al. | Aug 2004 | B1 |
| 20020048888 | Li et al. | Apr 2002 | A1 |
| 20020158285 | Clementi et al. | Oct 2002 | A1 |
| 20020175382 | Li et al. | Nov 2002 | A1 |
| 20040266213 | Li et al. | Dec 2004 | A1 |
| 20050277259 | Takami | Dec 2005 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20040266213 A1 | Dec 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09934916 | Aug 2001 | US |
| Child | 10880886 | US | |
| Parent | 09146710 | Sep 1998 | US |
| Child | 09934916 | US |