Patent Application
20130105932
The present invention relates to a molecular adhesion bonding carried out at low pressure (also referred to as LPB for “Low Pressure Bonding”) between two “wafers”.
In order to obtain a high bonding energy and limit the weakly bonded or non-bonded zones at the periphery of the wafers, it is known to carry out molecular adhesion bonding between two wafers under a reduced pressure or partial vacuum, as described particularly in document EP 2 200 077 A1. During molecular adhesion bonding at low pressure, the force necessary for initiating the propagation of a bonding wave between two wafers is less than that required at ambient pressure. Furthermore, the lower the pressure, the more rapidly the bonding wave propagates between the wafers.
The quality of a structure obtained by low pressure bonding between two wafers, however, is variable. In fact, the Applicant has observed that bonding carried out between two wafers by molecular adhesion at low pressure, typically at a pressure less than or equal to 1 millibar, is equally likely to give very satisfactory results and poor results in terms of deformations of the wafers, even for wafers coming from the same batch. This lack of a reproducible nature of the results after bonding is due to the fact that the propagation of the bonding wave may be initiated during the operations of alignment and progressive contacting of the wafers before carrying out the bonding per se, owing to the low pressure environment in which the wafers are placed and which promotes such initiation.
When the propagation of a bonding wave is initiated during these prior steps of handling the wafers, inhomogeneous deformations can occur on one or both wafers.
These deformations are problematic because they are not controllable and they are irreversible.
A particular case in which the occurrence of these inhomogeneous deformations is problematic is that of multilayer semiconductor structures (also referred to as “multilayer semiconductor wafers”) produced according to the technology of three-dimensional integration (3D integration) which involves the transfer onto a first wafer, referred to as the final substrate, of at least one layer formed from a second wafer, which is bonded by molecular adhesion onto the first wafer and is generally thinned after bonding, this layer corresponding to the portion of the second wafer in which elements have been formed, for example a plurality of microcomponents. Other corresponding elements may optionally also be formed in the first wafer.
In the case of a first wafer intended to carry microcomponents, in particular because of the very small size or large number of the microcomponents present on a given layer, each transferred layer, that is to say each wafer comprising the layer, must be positioned on the final substrate (the first wafer on its own or already comprising other transferred layers) with a correct precision in order to comply with alignment with the underlying layer, of the order of 0.3 microns. It may furthermore be necessary to carry out treatments on the layer after its transfer, for example in order to form other microcomponents, in order to uncover microcomponents on the surface, in order to produce interconnects, etc., these treatment operations also having to be carried out with very great precision in relation to the components present in the layer.
Although molecular adhesion bonding at low pressure makes it possible to obtain a high bonding energy without having to carry out an anneal for reinforcing the bonding interface at high temperature, which could damage the microcomponents, the inhomogeneous deformations generated in the wafers as explained above may make it very difficult or even impossible to form additional microcomponents in alignment with the microcomponents formed before the transfer. This type of problem of inhomogeneous deformations of the bonded wafers exists even outside the scope of 3D integration, that is to say in the case in which the first wafer does not comprise microcomponents or is not intended to carry them later.
In the particular case of 3D integration, the inhomogeneous deformations resulting from the low pressure molecular bonding subsequently lead to a phenomenon of misalignment of the microcomponents of the various layers. This misalignment phenomenon also referred to as “overlay”, described with reference to
Even when using positioning tools, however, offsets occur between certain of the microcomponents 411 to 419 on the one hand, and 421 to 429 on the other hand, such as the offsets Δ11, Δ22, Δ33, Δ44 indicated in
These offsets do not result from elementary transformations (translation, rotation or combinations thereof) which could have resulted from imprecise assembly of the substrates. These offsets result from inhomogeneous deformations which occur in the layer coming from the initial substrate during its bonding to the final substrate. Specifically, these deformations lead to nonuniform local displacements level with certain microcomponents 411 to 419. Also, certain of the microcomponents 421 to 429 formed on the exposed surface of the substrate after transfer exhibit position variations with respect to these microcomponents 411 to 419, which may be of the order of several hundreds of nanometers, or even one micron.
This phenomenon of misalignment (also referred to as “overlay”) between the two layers of microcomponents may give rise to short circuits, distortions in the stack or connection defects between the microcomponents of the two layers. Thus, in the case in which the transferred microcomponents are imagers formed by pixels and the post-transfer treatment steps are intended to form color filters on each of these pixels, a loss of the coloration function is observed for some of these pixels.
This misalignment phenomenon also leads to a reduction of the quality and the value of the multilayer semiconductor wafers being fabricated. The impact of this phenomenon is becoming more and more critical because of the incessantly increasing requirements in respect of the miniaturization of the microcomponents and their integration density per layer.
The present invention relates to a method for bonding at least a first wafer and a second wafer by molecular adhesion. This method comprises providing a first wafer, providing a second wafer, wherein the first wafer may be a silicon-on-insulator (SOI) type structure or substrate, placing the first wafer and the second wafer in an environment having a first pressure (P1) greater than a predetermined threshold pressure, aligning the first wafer and the second wafer, bringing the first wafer and the second wafer into contact, reducing the pressure within the environment to a second pressure (P2) below the threshold pressure, and initiating the propagation of a bonding wave between the first and second wafer, wherein propagation of the bonding wave is initiated by applying a mechanical pressure point to one of the two wafers, wherein the pressure applied by the mechanical pressure point onto one of the two wafers lies between 1 MPa and 33.3 MPa. The initiation may be carried out using a tool equipped with a stylet, and the mechanical pressure exerted by the stylet onto the wafer may be controlled in order to limit the deformations at the level of the contact point. The bonding wave may be initiated by applying a mechanical pressure Pm onto the substrate in proximity to its edge. The first pressure (P1) is greater than a predetermined threshold pressure, wherein the predetermined threshold value is between 20 millibar and 5 millibar. The first pressure (P1) may be at or above a pressure of about 400 millibar.
The pressure in the environment is reduce to a second pressure (P2) of less than 1 mbar, so as to spontaneously initiate the bonding wave.
The method further comprises arranging the first wafer and the second wafer such that the surfaces to be brought into contact are facing one another, while interposing spacer elements to maintain a space between the two wafers, and wherein the wafers are aligned by applying a lateral force to the wafers. There are at least three spacer elements interposed between the two wafers to maintain the space between the wafers, and the lateral force is applied to the wafers by a pusher that can move from a retracted position to an alignment position, wherein a head of the pusher abuts the edges of the wafers.
The method further comprises retracting one of the spacer elements, such that the second wafer descends onto the first wafer, applying a first lateral force by a pusher onto the wafers so as to align the two wafers with respect to one another, wherein the wafers are retained by at least one holding finger, retracting the second and third spacer elements, retracting the pusher to thereby allow the lower face of the second wafer to rest on the upper face of the first wafer, applying a second lateral force by the pusher to the two wafers, and retracting the pusher before initiating the propagation of the bonding wave.
The first wafer and the second wafer have alignment marks that interact with a holding finger, and further wherein the force exerted by the pusher places the wafers in abutment against at least the holding finger interacting with the alignment marks.
According to an aspect of the invention, during the initiation of a propagation bonding wave, the wafers are placed in an environment at a second pressure of less than 1 mbar, so as to spontaneously initiate the bonding wave.
According to another aspect of the invention, the initiation of a propagation bonding wave comprises the application of a mechanical pressure point on one of the two wafers.
The present invention also relates to a method for producing a three-dimensional composite structure comprising providing a first wafer, wherein there is a first layer of microcomponents on one face of the first wafer, providing a second wafer, placing the first wafer with microcomponents thereon and the second wafer in an environment having a first pressure (P1) greater than a predetermined threshold pressure, aligning the first wafer and the second wafer, bringing the face of the first wafer comprising the layer of microcomponents into contact with the face of the second wafer, reducing the pressure within the environment to a second pressure (P2) below the threshold pressure, and initiating the propagation of a bonding wave between the first and second wafer.
In another embodiment, the method may further comprise forming an oxide layer on the face of the first wafer covering the first layer of microcomponents prior to bonding the first and second wafers. The method may also comprise thinning the first wafer, and/or producing a second layer of microcomponents on the face of the first wafer opposite the face having the first layer of microcomponents, wherein at least the first layer of microcomponents on the first wafer may be image sensors.
The present method makes it possible to limit the inhomogeneous deformations which occur in a wafer or a substrate during its bonding by molecular adhesion onto another wafer or substrate, while preserving the advantages of low pressure bonding.
The present invention further still relates to a three-dimensional composite structure comprising a wafer and a layer of semiconductor crystalline material bonded on the wafer by molecular adhesion. The layer has a first face located in the vicinity of the bonding interface between the layer and the wafer and a second face opposite to the first face. The layer of semiconductor crystalline material includes a first series of microcomponents on its first face and a second series of microcomponents on its second face in alignment with the first series of microcomponents.
Advantageously, the residual alignment offsets between the first series of microcomponents and the second series of microcomponents are less than 100 nm homogeneously over the entire surface of the structure. With such a limited residual alignment, the occurrence of manufacturing defects such as short circuits, distortions or connection defects between the microcomponents of the two series of microcomponents is considerably reduced. In the case in which the first series of microcomponents comprises imagers formed by pixels while the second series of microcomponents comprises color filters intended to be aligned with each pixel, the coloration function can be ensured for all pixels.
According to another aspect of the invention, the residual alignment offsets between the first series of microcomponents and the second series of microcomponents are less than 50 nm over at least 50% of the surface of the structure.
These advantages are preferably provided in a composite structure that has a diameter of 300 mm or more, and at least some of the microcomponents are image sensor.
Other characteristics and advantages of the invention will become apparent from the following description of particular embodiments of the invention, given by way of nonlimiting examples, with reference to the appended drawings in which:
The present invention relates to a method for molecular adhesion bonding between at least a first wafer and a second wafer comprising at least a step of mechanical alignment, a step of bringing the two wafers in contact and a step of initiating the propagation of a bonding wave between the two wafers, in which method, during the said steps of mechanical alignment and bringing the two wafers in contact, the wafers are placed in an environment at a first pressure greater than or equal to a predetermined pressure threshold value, and during the step of initiating the propagation of a bonding wave, the wafers are placed in an environment at a second pressure less than the predetermined pressure threshold value.
The present invention applies in general to the production of composite structures comprising at least the molecular adhesion bonding of a first substrate or wafer onto a second substrate or wafer.
Molecular adhesion bonding is a technique well known in the art. The principle of molecular adhesion bonding is based on bringing two surfaces in direct contact, (i.e.: without using a specific material such as adhesive, wax, braze, etc.). Such an operation requires that the surfaces to be bonded are sufficiently smooth, and free of particles or contamination, and that they are brought sufficiently close together in order to make it possible to initiate contact, typically at a distance of less than a few nanometers. In this case, the attractive forces between the two surfaces are high enough to cause the propagation of a bonding wave which leads to molecular adhesion (bonding induced by all the attractive forces (Van Der Waals forces) of electronic interaction between atoms or molecules of the two surfaces to be bonded).
The molecular adhesion is achieved by initiating at least one contact point on one wafer in intimate contact with another wafer in order to trigger the propagation of a bonding wave from this contact point. Here, a “bonding wave” refers to the front of connection or molecular adhesion which propagates from the initiation point and which corresponds to the spreading of the attractive forces (Van Der Waals forces) from the contact point over the entire surface of intimate contact between the two wafers (bonding interface). The contact point is typically initiated by applying a mechanical pressure onto the exposed surface of one of the two wafers. This contact point may nevertheless be generated spontaneously by subjecting the two wafers in contact to a very low pressure, typically less than 5 millibar (mbar) and/or by the action of the force of gravity of one wafer on the other.
Although molecular adhesion bonding at low pressure makes it possible to improve the quality of the bonding, the Applicant has observed that if the bonding, and more precisely the propagation of a bonding wave, is initiated during the phase of mechanical alignment and bringing the wafers in contact, inhomogeneous deformations can be produced in the wafers.
To this end, the invention proposes to carry out the operations of mechanical alignment and bringing the wafers in contact by placing them in an environment having a pressure greater than a predetermined pressure threshold value below which there are risks of initiating the propagation of a bonding wave between the two wafers during their handling.
The term “ambient pressure” is intended to mean the pressure naturally prevailing in the bonding chamber, which is to say without using a pumping means, this pressure corresponding to the atmospheric pressure of the environment in which the bonding machine is located. The pressure threshold value is less than atmospheric pressure.
Once these operations have been carried out, the pressure of the chamber can be reduced below the defined pressure threshold value in order to allow the initiation of the propagation of a bonding wave between the two wafers.
An example of molecular adhesion bonding between two wafers according to an embodiment of the method of the invention will now be described with reference to
In
Once the wafer 20 is held on the support plate, three spacer elements 41 to 43 intended to temporarily prevent contact between the two wafers are put in position. The bonding machine furthermore comprises a pusher 44 which comprises a head 441. The pusher 44 is displaced between a retracted position in which the head 441 is at a distance from the edges of the wafers 20 and 30 and does not exert a force on the wafers (as illustrated in
The wafer 30 is then deposited on the spacer elements 41 to 43 so as to arrange the lower surface or face 32 of the wafer 30 facing the upper surface 22 of the wafer 20 (
In a well-known fashion, the surfaces 22 and 32 respectively of the wafers 20 and 30 intended to be bonded have been prepared (polishing, cleaning, hydrophobic/hydrophilic treatment, etc.) in order to allow molecular adhesion.
During the subsequent operation, the spacer element 41 is retracted then the pusher 44 is placed in its retracted position (
The pusher 44 is again placed in its alignment position in order to keep the wafers aligned (
The pusher 44 is once more placed in its mechanical alignment position in order to ensure that the wafers 20 and 30 are properly aligned before initiation of the propagation of a bonding wave (
According to the invention, the steps S1 to S8, are carried out while placing the wafers in an environment at a first pressure P1. To this end, as illustrated in
More precisely, and as explained above, the first pressure P1 is greater than a predetermined pressure threshold value, for example lying between 20 mbar and 5 mbar, in order to prevent the initiation of the bonding propagation during the steps of mechanical alignment and bringing the wafers in contact. Specifically, from Step S3 onwards, a portion of the bonding face 31 of the wafer 30 lies in contact with the bonding face 21 of the wafer 20. Consequently, from this moment on and if the wafers were to be placed in an environment whose pressure is less than the pressure threshold value, any contacts or shocks applied to the wafers during their handling, in particular during the contact between the pusher and the wafers or when it is retracted so as to make the wafer 30 descend onto the wafer 20, would be liable to cause the initiation of the propagation of a bonding wave.
By resorting to a pressure P1 above the threshold value, at this stage of the method it is possible to avoid triggering the propagation of a bonding wave which could give rise to inhomogeneous deformations in the wafers and subsequent phenomena of misalignment (“overlay”). The pressure P1 of the environment in which the wafers are placed during the steps S1 to S8 may or may not be constant (i.e. potentially it is variable during the steps of alignment and contacting). The initiation of the propagation of the bonding wave may be initiated spontaneously between the wafers 20 and 30 by lowering the pressure P2 in the chamber to a very low value, typically less than 5 mbar.
After the steps of mechanical alignment and bringing the wafers in contact, the molecular adhesion bonding is carried out (Step S9). To this end, the pressure of the chamber 110 is lowered to a second pressure P2 less than the pressure threshold value, namely a pressure typically less than 20 mbar, preferably less than 5 mbar.
The pressure P2 of the environment in which the wafers are placed during Step S9 may or may not be constant (i.e. potentially it is variable during the initiation step). As illustrated in
The bearing element, and more particularly its end intended to come in contact with the wafer, may be made of or covered with a material such as TEFLON®, silicone or a polymer. In general, the end of the bearing element is made or covered with a sufficiently rigid material in order to be able to apply a pressure in a controlled way. Specifically, too flexible a material could deform and lead to an imprecise contact surface and, consequently, to a lack of precision of the applied pressure. Furthermore, too rigid a material could lead to the formation of defects (imprint) on the surface of the wafer.
It is furthermore possible to raise the pressure again in a transient phase between the steps of mechanical alignment and bringing the wafers in contact and the step of initiating the propagation of a bonding wave.
The method of the invention is applicable to the assembling of any type of material compatible with molecular bonding, and in particular semiconductor materials such as silicon or germanium, glass, quartz, sapphire etc. The wafers to be assembled may in particular have a diameter of 100 mm, 150 mm, 200 mm, 300 mm, or 450 mm. The wafers may furthermore comprise microcomponents on the majority of their surface or only on a limited region.
One particular but not exclusive field of the bonding method of the present invention is that of the production of three-dimensional structures.
A method for producing a three-dimensional structure by transferring a layer of microcomponents formed on an initial substrate onto a final substrate, according to another embodiment of the invention, will now be described with reference to
The production of the three-dimensional structure starts with the formation of a first series of microcomponents 110, which is preferably made of a semiconductor crystalline material, on the surface of an initial wafer or substrate 100 (
The face 101 of the initial substrate 100 comprising the microcomponents 110 is then positioned facing and in contact with a face 201 of a final wafer or substrate 200 (Steps S20,
An oxide layer, for example of SiO2, may furthermore be formed on the face 101 of the initial substrate 100 comprising the microcomponents 110 and located at the vicinity of the bonding interface between the initial substrate 100 and the final substrate 200 and/or on the face 201 of the final substrate 200 intended to be bonded to the face 101.
According to the invention, the pressure in the chamber or enclosure (not represented in
Indeed, in most instances, it has been observed that lowering the pressure in chamber to a value of less than 5 mbar, an preferably less than 3 mbar, initiation of a contact point and propagation of the bonding wave occur spontaneously, that is to say without applying additional mechanical pressure on the wafers. Decreasing the pressure into the chamber or enclosure below 5 mbar was sufficient to spontaneously trigger this initiation. It is currently believed that under these low pressure conditions, the weight of the substrate on the underlying substrate is sufficient to spontaneously initiate the molecular bonding.
In case where the pressure in the chamber is not lowered to less than 5 mbar or to ensure the initiation of a contact point in any case, a contact point may be also initiated between the two substrates by applying a mechanical pressure Pm onto the substrate 200, preferably in proximity to its edge. As indicated above, the pressure Pm may lie between 1 MPa and 33.3 MPa and be applied onto a bearing surface less than or equal to 1 mm2.
The initiation of the contact point leads to the propagation of a bonding wave over the interface between the initial substrate 100 and the final substrate 200. The two substrates are then bonded together by molecular adhesion over their entire surface in contact (bonding interface). A buried layer of microcomponents 110 is thus obtained at the bonding interface between the substrates 100 and 200.
After bonding, and as represented in
As represented in
In a variant, the three-dimensional structure is formed by a stack of layers, each layer having been added by the assembly method of the present invention and each layer being in alignment with the directly adjacent layers. In yet another variant, the final substrate 200 itself also comprises microcomponents.
By virtue of the molecular adhesion bonding method of the invention, it has been possible to bond the initial substrate 100 onto the final substrate without deformation or at the very least with a reduction of the deformations such that significant residual alignment offsets of the microcomponents 110 are no longer observed before and after transfer of the initial substrate 100 onto the final substrate 200. It is thus possible to limit the residual offsets to values of less than 100 nm, homogeneously over the entire surface of the wafer. In the particular example of
The microcomponents 140, even if they are of very small sizes (for example <1 μm), can then be formed easily in alignment with the microcomponents 110, even after transfer of the initial substrate. This makes it possible, for example, to interconnect with one another the microcomponents existing in two layers, or on two separate faces of the same layer, by means of metallic connections while minimizing the risks of bad interconnection.
The bonding method of the present invention consequently makes it possible to limit the phenomena of inhomogeneous deformations of the wafers during their molecular bonding at low pressure. In the particular case in which the wafers comprise microcomponents, the method in the end makes it possible to eliminate the phenomenon of misalignment (“overlay”) during the transfer of one circuit layer onto another layer or onto a support substrate, and to produce multilayer semiconductor wafers of very high quality.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1056566 | Aug 2010 | FR | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13192312 | Jul 2011 | US |
| Child | 13718624 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12910081 | Oct 2010 | US |
| Child | 13192312 | US |