Patent Grant
6992020
The present invention relates to a semiconductor device and a method of fabricating the same and, more particularly, to a semiconductor device and a method of fabricating the same preferable when a dielectric interlayer is formed on a gate electrode or when an insulating film is buried in a trench in STI (Shallow Trench Isolation).
After a gate electrode is formed, a silicon oxide (SiO2) film is formed as a dielectric interlayer, or a silicon oxide film is buried in a trench in STI formation.
When a silicon oxide film is formed at a film formation temperature of 500° C. or less in an O3/TEOS ambient atmosphere, a film having flowability, i.e., self-flatness is obtained without any reflow step, so excellent filling characteristics can be obtained.
Unfortunately, a film formation reaction in this case is sometimes very sensitive to and dependent on the surface of an underlayer. Especially when a silicon oxide film is formed on the surface of a silicon nitride (SiN) film, abnormal growth often occurs to form a porous film. This phenomenon is generally called underlayer dependence.
An electrode material is deposited on the surface of a semiconductor substrate 10 and patterned to form a gate electrode 11. A silicon nitride film 12 is so formed as to cover the gate electrode 11 and the semiconductor substrate 10. After that, a silicon oxide film 13 as a dielectric interlayer is so formed as to cover the silicon nitride film 12, at a film formation temperature of 500° C. or less in an O3/TEOS ambient atmosphere. Since this silicon oxide film 13 has underlayer dependence, the flowability unique to the O3/TEOS process is lost, and the filling characteristics extremely deteriorate. Consequently, voids 14 are formed in the silicon oxide film 13.
When film formation is performed in an ambient atmosphere at a low O3 concentration, no underlayer dependence is produced. Conventionally, therefore, a method which forms films in two stages is often used. In this method, film formation is performed using low-concentration O3 gas in the initial stage, and then film formation is performed using high-concentration O3 gas.
When films are formed by this method, however, a silicon oxide film as the first layer must have a film thickness of 100 nm or more in order to reduce the underlayer dependence.
Additionally, this silicon oxide film as the first layer formed at a low O3 concentration has poor filling characteristics. In recent microfabricated patterns, trenches are filled with the silicon oxide film as the first layer. This makes the two-stage film formation method difficult to use.
The underlayer dependence can also be eliminated by improving the surface of a silicon nitride film by plasma irradiation. In this case, however, the cost increases because an apparatus for plasma irradiation is additionally required. In addition, the transistor characteristics may deteriorate by plasma damage. Therefore, this method is also difficult to use.
As described above, when a silicon oxide film is formed to fill a portion between gate electrodes or to fill STI in conventional devices, the filling characteristics deteriorate by the underlayer dependence.
According to an aspect of the present invention, there is provided a semiconductor device comprising a silicon nitride film formed on a semiconductor substrate and having a density of 2.2 g/cm3 or less, and a silicon oxide film formed on the silicon nitride film in an ambient atmosphere containing TEOS and O3.
According to another aspect of the present invention, there is provided a semiconductor device comprising a gate electrode formed on a semiconductor substrate, a silicon nitride film so formed as to cover the gate electrode and having a density of 2.2 g/cm3 or less, and a silicon oxide film formed on the silicon nitride film in an ambient atmosphere containing TEOS and O3.
According to another aspect of the present invention, there is provided a semiconductor device comprising a silicon nitride film so formed as to cover the inner surfaces of a trench formed in the surface of a semiconductor substrate, and having a density of 2.2 g/cm3 or less, and a silicon oxide film formed in an ambient atmosphere containing TEOS and O3 so as to fill the trench covered with the silicon nitride film.
According to another aspect of the present invention, there is provided a semiconductor device fabrication method comprising the steps of forming a silicon nitride film having a density of 2.2 g/cm3 or less on a semiconductor substrate, and forming a silicon oxide film on the silicon nitride film at a film formation temperature of 500° C. or less and a film formation pressure of 200 to 760 Torr in an ambient atmosphere which contains TEOS and O3 and in which the concentration of O3 is 5 wt % or more.
According to an aspect of the present invention, there is provided a semiconductor device fabrication method comprising forming a gate electrode on a semiconductor substrate, forming a silicon nitride film having a density of 2.2 g/cm3 or less so as to cover the gate electrode, and forming a silicon oxide film on the silicon nitride film at a film formation temperature of 500° C. or less and a film formation pressure of 200 to 760 Torr in an ambient atmosphere which contains TEOS and O3 and in which the concentration of O3 is 5 wt % or more.
According to another aspect of the present invention, there is provided a semiconductor device fabrication method comprising forming a trench in the surface of a semiconductor substrate, forming a silicon nitride film having a density of 2.2 g/cm3 or less so as to cover the inner surfaces of the trench, and forming a silicon oxide film on the silicon nitride film at a film formation temperature of 500° C. or less and a film formation pressure of 200 to 760 Torr in an ambient atmosphere which contains TEOS and O3 and in which the concentration of O3 is 5 wt % or more.
As described above, the underlayer dependence when a silicon oxide film is formed is a problem in conventional devices. The present inventor has found that this dependence is reduced when the film density of an underlying silicon nitride film is low. As explained in the following embodiments, a silicon oxide film is formed on a silicon nitride film having low film density at a film formation temperature of 500° C. in an O3/TEOS ambient, as film formation conditions under which flowability is obtained. In this manner, a silicon oxide film having low underlayer dependence and superior filling performance can be formed.
Embodiments of the present invention made on the basis of the above consideration will be described below with reference to the accompanying drawings.
(1) First Embodiment
The first embodiment of the present invention will be described below with reference to FIG. 1. This embodiment relates to a device in which a silicon oxide film is formed as a dielectric interlayer on a gate electrode.
An electrode material is deposited on the surface of a semiconductor substrate 20 and patterned to form gate electrodes 21. A silicon nitride film is so deposited as to cover the gate electrodes 21 and substrate 20 and left behind only on the side surfaces of the electrodes 21 by etch back, thereby forming spacers 22.
In addition, a silicon nitride film 23 is so formed as to cover the gate electrodes 21, spacers 22, and semiconductor substrate 20. The formation of this silicon nitride film 23 is done by low-pressure CVD at a film formation temperature of 350 to 600° C. and, preferably, 450° C., by using HCD gas, i.e., SinCl(2n+2−x)Hx (n is an integer of 2 or more, and x is an integer of 0 to 2n+1) and ammonia (NH3) as materials. When film formation is performed at this low temperature, the density of the silicon nitride film can be decreased to 2.2 g/cm3 or less.
The nitrogen/silicon ratio of this silicon nitride film 23 is 1.2 or less. When HCD gas is used, the concentration of chlorine contained in the silicon nitride film 23 is 1.0E21 to 1.0E22 atoms/cm3 because of chlorine contained in the gas. Also, this silicon nitride film 23 has a low film density, so its surface is readily oxidized. Hence, the oxygen concentration is 1.0E21 atoms/cm3 or more from the film surface to a depth of 1 to 3 nm.
To cover the obtained low-density silicon nitride film 23, a silicon oxide film 24 is deposited as a dielectric interlayer as shown in
Since the silicon nitride film 23 is formed as a low-density film, the underlayer dependence of the silicon oxide film 24 disappears. Accordingly, the formation of voids in the silicon oxide film 24 is prevented without losing the flowability unique to the O3/TEOS process or deteriorating the filling performance.
In this embodiment as explained above, on a silicon nitride film having a low film density, a silicon oxide film is formed in an O3/TEOS ambient atmosphere at a temperature of 500° C. or less. Consequently, the underlayer dependence disappears, and good filling characteristics can be obtained.
(2) Second Embodiment
The second embodiment of the present invention will be described below with reference to
As shown in
As shown in
As shown in
As shown in
On the surface of this silicon nitride film 36, a silicon oxide film 37 is deposited as an STI filling material under the same film formation conditions as in the first embodiment. After that, as shown in
If a silicon oxide film is formed by O3/TEOS directly on a silicon oxide film formed by thermal oxidation, a large underlayer dependence appears. In this embodiment, the silicon oxide film 37 is not directly formed in an O3/TEOS ambient atmosphere on the silicon oxide film 35 formed by thermal oxidation. That is, the silicon nitride film 36 having a low film density is formed as a buffer layer. Consequently, the underlayer dependence of the silicon oxide film 37 disappears in the O3/TEOS ambient atmosphere. Accordingly, the flowability unique to the O3/TEOS process appears and the filling characteristics improve, so the trench 34 can be filled without forming any voids.
Although the silicon nitride film 36 remains inside the trench 34, the device characteristics are not adversely affected because the film is an insulating film.
In discussion of the underlayer dependence, the deposition rate ratio (=the growth rate of a silicon oxide film on a silicon nitride film/the growth rate of a silicon oxide film on a silicon substrate) is often used as an index. When the underlayer dependence exists, the film growth rate of a silicon oxide film on a silicon nitride film decreases, so the deposition rate ratio decreases.
As is apparent from this graph, when the film density of the silicon nitride film exceeds 2.2 g/cm3, the underlayer dependence appears and abnormally grows the silicon oxide film, and the surface roughness of the silicon oxide film increases. Similar to the deposition rate ratio described above, this change in the surface roughness of the silicon oxide film also improves from a region in which the film density of the silicon nitride film is 2.2 g/cm3 or less.
A silicon nitride film having a film density of 2.2 g/cm3 or less is a low-quality porous film. Since this makes the film surface readily oxidizable, oxygen is contained at a concentration of about 1.0E21 from the film surface to a depth of 1 to 3 nm. The underlayer dependence is reduced probably because many adsorption sites of intermediate products exist in this porous silicon nitride film having a low film density.
As described above, this silicon nitride film is formed at a low temperature. A large amount of chlorine is entrapped into the film during the film formation, so the concentration of chlorine in the film is 1.0E21 to 1.0E22 atoms/cm3.
By using this porous silicon nitride film as an underlayer, a silicon oxide film can be formed by O3/TEOS having superior filling properties.
The above embodiments are merely examples and hence do not restrict the present invention. For example, in the above embodiments, HCD gas is used to allow the formation of a silicon nitride film at a low temperature. However, another gas such as BTBAS gas can also be used so that film formation at a low temperature is possible.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-200266 | Jul 2002 | JP | national |
This is a division of application Ser. No. 10/235,917, filed Sep. 6, 2002, now U.S. Pat. No. 6,841,850 which is incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5523616 | Den | Jun 1996 | A |
| 6037018 | Jang et al. | Mar 2000 | A |
| 6133160 | Komiyama et al. | Oct 2000 | A |
| 6228780 | Kuo et al. | May 2001 | B1 |
| 6235650 | Yao | May 2001 | B1 |
| 6251795 | Shan et al. | Jun 2001 | B1 |
| 6277706 | Ishikawa | Aug 2001 | B1 |
| 6319849 | Oda et al. | Nov 2001 | B1 |
| 6333547 | Tanaka et al. | Dec 2001 | B1 |
| 6407007 | Tsan et al. | Jun 2002 | B1 |
| 6489254 | Kelkar et al. | Dec 2002 | B1 |
| 6579764 | Kuwazawa | Jun 2003 | B2 |
| 20020001917 | Park | Jan 2002 | A1 |
| 20020076916 | Yamashita et al. | Jun 2002 | A1 |
| 20020197823 | Yoo et al. | Dec 2002 | A1 |
| Number | Date | Country |
|---|---|---|
| 2994616 | Oct 1999 | JP |
| 2000-349082 | Dec 2000 | JP |
| 2002-0002578 | Jan 2002 | KR |
| Number | Date | Country | |
|---|---|---|---|
| 20050012171 A1 | Jan 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10235917 | Sep 2002 | US |
| Child | 10902414 | US |