Patent Grant
7112531
The present invention relates to the field of semiconductor manufacturing. More particularly, the present invention provides methods of simultaneously depositing and etching silicon oxide on a substrate.
Silicon oxide is a useful isolation material used in many semiconductor processes. In one use, silicon oxide can be used as a spacer to provide sloped sidewalls on semiconductor structures with generally vertical sidewalls, such as transistors, trace lines, etc. Because the silicon oxide material has a low dielectric constant, it can also be used to electrically isolate the structures.
Known processes of providing silicon oxide spacers involve a first step of depositing doped or undoped silicon oxide on the semiconductor structures. The silicon oxide can be deposited by a variety of methods including chemical vapor deposition (CVD) and plasma-enhanced chemical vapor deposition (PECVD). Source gases for the silicon oxide layers include silane and tetraethyl orthosilicate (TEOS). Silicon oxide deposited employing PECVD with a TEOS source gas is particularly useful in some instances because the processing temperatures needed for deposition are lower than standard chemical vapor deposition temperatures, i.e., typically about 375° C. Another advantage of PECVD with a TEOS source gas is that it can be used to deposit silicon oxide in between adjacent sidewalls having larger aspect ratios than PECVD or CVD methods using silane as a source gas.
After the layer of silicon oxide is deposited, sloped sidewalls are provided by etching the silicon oxide and/or by reflowing the silicon oxide layer at high temperatures (where those temperatures will not adversely affect any other layers or structures already on the semiconductor wafer). These additional steps of etching and/or reflowing the silicon oxide are performed separately from the step of depositing the silicon oxide, i.e., after the silicon oxide layer has been deposited. As a result, additional time is required for processing—thereby increasing the cost of manufacturing the semiconductor devices on the wafer. In addition, in many instances, the temperatures needed for reflow are not safe to use with the semiconductor wafer.
One particular application in which silicon oxide is used is in the manufacture of stacked capacitor DRAM cells.
Typically, a number of layers of silicon oxide 10 are deposited and etched until the desired facets 18 are obtained. As a result, the wafer may be subjected to a number of discrete, sequential deposition and etching process steps to obtain the desired faceted or sloped sidewalls needed to ensure complete coverage of the bottom surfaces 14 between sidewalls 12 by both the silicon oxide and later-deposited layers. Those multiple deposition and etching steps add to the cost of the wafers and reduce throughput of the process.
The present invention provides methods of providing silicon oxide on a substrate in a single process step as opposed to multiple sequential deposition-etch-deposition methods. In addition, if the etch gas contains fluorine, the resulting silicon oxide will also contain fluorine, thereby reducing its dielectric constant which further enhances the insulating properties of the silicon oxide.
The method involves simultaneously introducing both a source gas and an etch gas into a CVD chamber. As a result, the method will typically involve simultaneous deposition and etching of the silicon oxide.
In one aspect according to the present invention, the method includes the steps of depositing silicon oxide on a substrate by contacting the substrate with a plasma enhanced source gas, and contacting the silicon oxide with a plasma enhanced etching gas at the same time as the silicon oxide is deposited.
In another aspect according to the present invention, the method includes forming a silicon oxide spacer on a substrate by depositing silicon oxide on the substrate by contacting the substrate with a plasma enhanced source gas, and contacting the silicon oxide with a plasma enhanced etching gas at the same time as the silicon oxide is deposited.
In another aspect according to the present invention, the method includes forming a silicon oxide spacer on a substrate by providing a substrate in a chamber; providing a plasma enhanced source gas in the chamber, wherein silicon oxide is formed on the substrate; and providing a plasma enhanced etching gas in the chamber at the same time as the source gas is provided in the chamber; wherein a silicon oxide spacer is formed on the substrate.
In another aspect according to the present invention, the method includes depositing a silicon oxide spacer on a DRAM cell by contacting the cell with a plasma enhanced source gas, wherein silicon oxide is formed on the cell, and contacting the silicon oxide with a plasma enhanced etching gas at the same time as the silicon oxide is deposited.
In another aspect according to the present invention, the method includes forming a silicon oxide spacer on a DRAM cell by depositing silicon oxide on the cell by contacting the cell with a plasma enhanced source gas, and contacting the silicon oxide with a plasma enhanced etching gas at the same time as the silicon oxide is deposited.
In another aspect according to the present invention, the method includes forming a silicon oxide spacer on a DRAM cell by providing a DRAM cell in a chamber; providing a plasma enhanced source gas in the chamber, wherein silicon oxide is formed on the DRAM cell; and providing a plasma enhanced etching gas in the chamber at the same time as the source gas is provided in the chamber; wherein a silicon oxide spacer is formed on the DRAM cell.
These and other features and advantages of methods according to the present invention will become more apparent upon reviewing the detailed description of the invention below.
The present invention provides a method of depositing silicon oxide by plasma-enhanced chemical vapor deposition on a substrate (typically a semiconductor wafer) which includes providing a plasma enhanced source gas and a plasma enhanced etch gas in the CVD chamber at the same time. The result is that, across the substrate, silicon oxide is being deposited and etched simultaneously in a single process step. Because the deposition and etching occur simultaneously, it is referred to herein as a “co-deposition/etching” process. By describing that the deposition and etching processes occur simultaneously, it should be understood that after some of the silicon oxide is deposited in a given area, a portion of it is removed in the etching process, and then, in the same process step, some additional silicon oxide may be deposited in the same area. The desired result of the co-deposition/etching process according to the present invention is that a contiguous, unbroken layer of silicon oxide is deposited on a substrate. Where the substrate includes generally vertical sidewalls, a sloped or faceted profile can be obtained in the silicon oxide remaining on the semiconductor wafer after processing is complete.
A significant advantage is provided by the methods according to the present invention is that the sloped or faceted sidewall provided by the silicon oxide layer can be produced in a single process step as compared to the multiple, sequential deposition and etching steps typically required to form sloped or faceted sidewalls from silicon oxide deposited by chemical vapor deposition.
Furthermore, the methods of the present invention are particularly well-suited for providing silicon oxide spacers on the surface of a substrate or substrate assembly, referred to herein generally as “substrate,” used in forming integrated circuits, such as a silicon wafer, with or without layers or structures formed thereon. It is to be understood that the methods of the present invention are not limited to deposition on silicon wafers; rather, other types of wafers (e.g., gallium arsenide, etc.) can be used as well. Also, the methods of the present invention can be used in connection with silicon-on-insulator technology. In addition, substrates other than semiconductor substrates or substrate assemblies can be used in connection with the present invention. These include, for example, fibers, wires, etc. If the substrate is a semiconductor substrate or substrate assembly, the silicon oxide can be formed directly on the lowest semiconductor surface of the substrate, or they can be formed on any variety of other layers or structures formed on the substrate.
One structure 30 on a semiconductor wafer substrate with which the present invention is particularly useful is a stacked capacitor DRAM cell which includes a transistor having a pair of sidewalls 22 as shown in
Although a stacked capacitor DRAM cell is one preferred structure for use in the method of the present invention, it will be understood that the method is useful for depositing silicon oxide having a sloped or faceted surface on any structure located on a substrate and having at least one generally vertical sidewall. As used in connection with the present invention, a generally vertical sidewall will be understood as a wall or surface that forms an angle of about 70° to about 110° with the general plane of the substrate.
One method used to obtain the layer of silicon oxide in a single process step is schematically illustrated in
Flow rates of the source and etch gases are related in that a higher flow rate of source gas will typically be paired with a higher flow rate of the corresponding etch gas. This relationship is typically limited at either end by the deposition rate limits under the given process conditions. Typically, however, when TEOS is used as the source gas, its flow rate (when the substrate temperature is about 400° C. and the chamber pressure is between about 1 Torr to about 10 Torr) is preferably between about 1×105 standard cubic centimeters per minute (sccm) to about 1.5×105 sccm, more preferably between about 1×105 sccm to about 0.8×105 sccm. Under those conditions, the flow rate of a preferred etch gas (C2F6) is about 5 sccm to about 100 sccm to accomplish the desired co-deposition/etching process according to the present invention.
As a result, the silicon oxide is etched during the deposition process, resulting in faceted or sloped surfaces 42 near to, i.e., proximate, the intersection between the sidewalls 22 and top surfaces 26. One desirable feature of the faceted or sloped surfaces 42 is that their slope is pro-grade as opposed to retro-grade. In other words, the thickness (measured parallel to the general plane of the bottom surface 24) of the silicon oxide layer 40 increases from the top of the sidewall 22 to the bottom of the sidewall 22 near the bottom surface 24. That faceted surface 42 can improve step coverage for later-deposited layers by providing a smoother transition over the features on which the silicon oxide is deposited.
In addition to a faceted or sloped surface 42 in the silicon oxide, the area between the sidewalls 22, i.e., the area above bottom surface 24, is filled with silicon oxide 40 to a higher level than typically seen when sequential deposition and etching steps are used. This phenomenon may also improve step coverage and smooth the surface of the substrate for later-deposited layers.
The source gas preferably includes tetraethyl orthosilicate which is used to form the desired silicon oxide layer. The source gas can include other constituents, e.g., boron, where a doped silicon oxide layer is preferred. Other potential source gases include any suitable gas or combination of gases that can form reactive species in plasma necessary to form silicon oxide layers. Examples include silane, disilane, 1,3,5,7-tetramethylcyclo-tetrasiloxane (TMCTS), etc. In those gas mixtures which do not include an oxygen source (such as silane or disilane) it may be necessary to include pure oxygen or another oxygen-bearing gas as a portion of the source gas to form the silicon oxide layer.
Any etch gas used in connection with the present invention should be selected for its ability to form reactive species in plasma that can react with the silicon oxide being deposited. Another consideration is that the products of the reactions between the reactive species and the silicon oxide are preferably volatile to provide for their removal from the deposition/etching chamber. Preferred etch gases include fluorine-containing gases that are useful in etching silicon oxide, for example, CF4, C2F6, C3F8, CHF3, and combinations of one or more of the gases.
An advantage in using a fluorine-containing etch gas is that the silicon oxide layer ultimately deposited on the wafer incorporates fluorine, which has been shown to lead to a reduction in the refractive index of the silicon oxide layer from about 4.1 for pure silicon oxide to about 3.4 for the fluorine-enhanced silicon oxide layer. The reduction in refractive index will generally correlate to a reduction in the dielectric constant of the fluorine-enhanced silicon oxide layer (as compared to the dielectric constant of pure silicon oxide). A lower dielectric constant for the fluorine-enhanced silicon oxide increases the isolating properties of the silicon oxide material.
Features and advantages of the methods according to the present invention are further illustrated in the following example. It is recognized, however, that while the example serves this purpose, the particular process conditions, source and etch gases, and structures on which the silicon oxide is deposited, are not to be construed in a manner that would unduly limit the scope of this invention.
A silicon wafer substrate having word lines formed thereon was placed in CVD chamber. The pressure in the chamber was held at about 5×10−6 Torr and the temperature of the substrate was about 400° C. TEOS was introduced into the chamber at a rate of about 500 Standard Liters per Minute (slm) using a liquid injection system. The etch gas used was C2F6 and it was introduced into the chamber at the same time as the TEOS, but at a flow rate of 150 sccm. Both the source gas and the etch gas were excited by a plasma generator operating at 450 Watts. The source and etch gases were provided for a period of about 20 seconds.
After the process was complete, a scanning electron microscope was used to examine the resulting oxide spacers which had profiles similar to those depicted in
Although specific methods and examples have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that any arrangement that is calculated to achieve the same purpose may be substituted for the specific methods and examples described. This application is intended to cover any adaptations or variations of the present invention. Therefore, it is manifestly intended that this invention be limited only by the claims and the equivalents thereof.
This is a continuation of application Ser. No. 09/138,917, filed Aug. 24, 1998 now U.S. Pat. No. 6,534,409 which is a division of application Ser. No. 08/760,289, filed Dec. 4, 1996 (abandoned), which are all incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3916034 | Tsuchimoto | Oct 1975 | A |
| 4432132 | Kinsbron et al. | Feb 1984 | A |
| 4690729 | Douglas | Sep 1987 | A |
| 4702795 | Douglas | Oct 1987 | A |
| 4732761 | Machida et al. | Mar 1988 | A |
| 5089422 | Brubaker | Feb 1992 | A |
| 5089442 | Olmer | Feb 1992 | A |
| 5110408 | Fujii et al. | May 1992 | A |
| 5150276 | Gonzalez et al. | Sep 1992 | A |
| 5162248 | Dennison et al. | Nov 1992 | A |
| 5223448 | Su | Jun 1993 | A |
| 5236858 | Lee et al. | Aug 1993 | A |
| 5264396 | Thakur et al. | Nov 1993 | A |
| 5275977 | Otsubo et al. | Jan 1994 | A |
| 5278091 | Fazan et al. | Jan 1994 | A |
| 5283204 | Rhodes et al. | Feb 1994 | A |
| 5302233 | Kim et al. | Apr 1994 | A |
| 5346585 | Doan et al. | Sep 1994 | A |
| 5364809 | Kwon et al. | Nov 1994 | A |
| 5403630 | Matsui et al. | Apr 1995 | A |
| 5407837 | Eklund | Apr 1995 | A |
| 5429995 | Nishiyama et al. | Jul 1995 | A |
| 5432116 | Keum et al. | Jul 1995 | A |
| 5433794 | Fazan et al. | Jul 1995 | A |
| 5472825 | Sayka | Dec 1995 | A |
| 5500256 | Watabe | Mar 1996 | A |
| 5518959 | Jang et al. | May 1996 | A |
| 5571571 | Musaka et al. | Nov 1996 | A |
| 5571576 | Qian et al. | Nov 1996 | A |
| 5595929 | Tseng | Jan 1997 | A |
| 5599740 | Jang et al. | Feb 1997 | A |
| 5858876 | Chew | Jan 1999 | A |
| 5882975 | Ishikawa | Mar 1999 | A |
| 5915190 | Pirkle | Jun 1999 | A |
| 5935649 | Koizumi et al. | Aug 1999 | A |
| 6225228 | Srinivasan | May 2001 | B1 |
| 6274897 | Blalock et al. | Aug 2001 | B1 |
| 6534409 | Srinivasan | Mar 2003 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20030162346 A1 | Aug 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 08760289 | Dec 1996 | US |
| Child | 09138917 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09138917 | Aug 1998 | US |
| Child | 10378429 | US |