Method for fabricating a III nitride film, an underlayer for fabricating a III nitride film and a method for fabricating the same underlayer

Abstract

On a given substrate is formed an underfilm including a surface of concave-convex structure in which 50% or over is occupied by the flat region and made of a III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the III nitride. Then, a desired III nitride film is formed on the underfilm by a normal MOCVD method.

Description

BACKGROUND OF THE INVENTION

[0001] (1). Field of the Invention

[0002] This invention relates to a method for fabricating a III nitride film, an underlayer for fabricating a III nitride film and a method for fabricating the same underlayer, particularly usable for semiconductor films constituting a light-emitting diode or a high velocity IC chip.

[0003] (2). Related Art Statement

[0004] III nitride films are employed as semiconductor films constituting a light-emitting diode, and recently, win a lot of attention as semiconductor films 10 constituting high velocity IC chips to be used in cellular phones.

[0005] Such III nitride films are usually fabricated by MOCVD methods.

[0006] Concretely, a substrate on which III nitride films are formed is set onto a susceptor installed in a given reactor, and then, heated to 1000° C. or over with a heater provided in or out of the susceptor. Thereafter, raw material gases are introduced with a carrier gas into the reactor and supplied onto the substrate.

[0007] On the substrate, the raw material gases are dissolved through thermochemical reaction into constituent elements, which are reacted to deposit and fabricate a desired III nitride film on the substrate.

[0008] There are few suitable substrates, which have nearly equal lattice constants and thermal expansion coefficients to those of III nitride films. In this case, the difference in the lattice constants between the III nitride film and the substrate may induce more misfit dislocations at the boundary between the III nitride film and the substrate. In order to reduce such misfit dislocations, generally, a lower crystallinity buffer layer, which is fabricated at a lower temperature, is provided between the substrate and the III nitride film. In this case, the difference in lattice constant is compensated, and thus, much misfit dislocations are not created.

[0009] However, the misfit dislocations are not reduced sufficiently even though the buffer layer is provided, so that much dislocation of about 109-1010/cm2 may be created in the III nitride film originated from the propagation of the misfit dislocations. As a result, the crystal quality of the III nitride film is degraded, and thus, the electrical and optical properties of the III nitride film are degraded.

[0010] In order to iron out the above problem, such an attempt is made as to form a patterned mask made of SiO2 on the substrate and epitaxially grow the III nitride film laterally on the substrate. In this case, misfit dislocations are propagated laterally on the mask, and not propagated vertically. Therefore, the dislocation density of the III nitride film can be lowered in the region above the patterned mask.

[0011] However, since a photolithography process including an etching step is required in forming the patterned mask, the total steps of the fabricating process for the III nitride film are increased and complicated.

SUMMARY OF THE INVENTION

[0012] It is an object of the present invention to provide a method able to easily fabricate a III nitride film of lower dislocation density.

[0013] In order to achieve the above object, this invention relates to A method for fabricating a III nitride film, including steps of preparing a given substrate, forming an underfilm having its surface of concave-convex structure in which 50% or below is occupied by the flat region and made of a first III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the first III nitride, and forming a III nitride film on the underfilm.

[0014] The inventors had intensely studied to obtain a III nitride film of lower dislocation density through an easy fabricating process without a patterned mask made of SiO2. As a result, they found out that such an underfilm as mentioned above is formed on a substrate, thus, a given III nitride film is formed on the underfilm by a MOCVD method, to reduce the dislocation density of the III nitride film.

[0015] Such an underfilm can be made as follows. First of all, a V raw material gas and a III raw material gas are supplied onto a substrate at a flow ratio (V raw material gas/III raw material gas) of 600 or below, to form, on the substrate, a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period. Then, the raw material gas and the III material gas are supplied onto the substrate at flow ratio (V raw material gas/III raw material gas) of more than 600, to form, on the first film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period.

[0016] Moreover, a V raw material gas and a III raw material gas are supplied onto the substrate under a pressure of 20 Torr or below, to form, on the substrate, a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the III element through the epitaxial growth for a given period. Then, the raw material gas and the III material gas are supplied onto the substrate under a pressure of more than 20 Torr, to form, on the first film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period.

[0017] Furthermore, a V raw material gas and a III raw material gas are supplied onto the substrate heated at 1100° C. or over, to form, on the substrate, a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period. Then, the raw material gas and the III material gas are supplied onto the substrate heated at less than 1100° C., to form, on the first film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period.

[0018] That is, the above-mentioned underfilm is stepwisely formed by using respective two fabricating conditions of MOCVD. In this case, the crystallinity of the underfilm is developed and a concave-convex structure is formed on the underfilm. If Al element of 50 atomic percentages or over for all of the III elements incorporated into the underfilm, the concave-convex structure can be easily formed. Therefore, without using a complicated photolithography process, the underfilm can be easily formed in the same apparatus as that of the III nitride film.

[0019] Therefore, the III nitride film of lower dislocation density and good crystallinity can be fabricated without complicating the fabricating process.

[0020] Herein, the first through the third fabricating method may be employed in isolation or combination of two or over. Moreover, another fabricating method may be employed. For example, if the flow ratio of (V raw material gas/III raw material gas) is set to 1000 or over, the underfilm can be formed at one step by using one fabricating condition of MOCVD.

BRIEF DESCRIPTION OF THE DRAWINGS

[0021] For better understanding of the present invention, reference is made to the attached drawings, wherein

[0022] FIG. 1 is a SEM photograph showing the surface figuration of an AlN underfilm fabricated according to the present invention,

[0023] FIG. 2 is a SEM photograph showing the surface figuration of another AlN underfilm fabricated according to the present invention,

[0024] FIG. 3 is a SEM photograph showing the surface figuration of still another AlN underfilm fabricated according to the present invention,

[0025] FIG. 4 is a SEM photograph showing the surface figuration of a further AlN underfilm, and

[0026] FIG. 5 is a SEM photograph showing the surface figuration of a still further AlN underfilm.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] This invention will be described in detail, hereinafter.

[0028] In the fabricating method of a III nitride film according to the present invention, it is required that a first III nitride to constitute an underfilm includes 50 atomic percentages or over, preferably 70 atomic percentages or over of Al element for all of the III elements of the first III nitride. Particularly, the first III nitride is preferably made of AlN. In this case, the dislocation density of the III nitride film to be formed on the underfilm can be reduced effectively, and thus, the crystal quality of the III nitride film can be enhanced.

[0029] The first III nitride may include an additive element such as Ge, Si, Mg, Zn, Be, P or B as occasion demands. Moreover, the first III nitride may include a minute impurity contained in the raw material gases and the reactor or contained dependent on the forming condition.

[0030] Moreover, it is required that the flat region in the surface of the underfilm is set to 50% or below, preferably 10% or below. Herein, the wording “flat region” means an average roughness Ra of 10 Å or below. Particularly, it is desired that no flat region is formed in the surface of the underfilm, and thus, a concave-convex structure is formed over the surface of the underfilm entirely. In this case, the dislocation density of the III nitride film to be formed on the underfilm can be reduced effectively.

[0031] From the same reason as mentioned above, it is desired that the concave-convex structure except the flat region includes {101} facets.

[0032] As a result, the dislocation density of the III nitride film is reduced and thus improved to about 106-107, which is order of 1/102-1/103 as compared with the one of a conventional III nitride film.

[0033] The underfilm may be fabricated by two fabricating steps as follows.

[0034] First of all, a V raw material gas and a III raw material gas containing the constituent elements of the first III nitride of the underfilm are introduced into a reactor so that the flow ratio of (V raw material gas/III raw material gas) is set to 600 or below, preferably 450 or below and the pressure inside the reactor is set to 20 Torr or below, preferably 15 Torr or below, and then, supplied onto a substrate heated at 1100° C. or over, preferably 1150° C. or over, to form a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the II elements through the epitaxial growth for a given period.

[0035] Herein, it is not necessary that all of the flow rate condition, the pressure condition and the substrate temperature condition are satisfied, but it is necessary that at least one of these conditions is satisfied.

[0036] Thereafter, on the condition that the above-mentioned pressure condition and the above-mentioned substrate temperature condition are satisfied, the flow ratio of (V raw material gas/III raw material gas) is set to 600 or over, preferably 1000 or over, to form, on the first III nitride film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements. In this way, a concave-convex structure is formed in the surface of the thus obtained underfilm made of the first and the second nitride films.

[0037] In forming the second III nitride film, the pressure condition instead of the flow ratio condition may be varied, to form the underfilm having a concave-convex structure. Concretely, on the condition that the above-mentioned flow ratio condition and the above-mentioned substrate temperature condition are satisfied, the interior pressure of the reactor is set to 20 Torr or over, preferably 40 Torr or over.

[0038] Moreover, in forming the second III nitride film, the substrate temperature condition instead of the flow rate condition and the pressure condition may be varied, to form the underfilm having a concave-convex structure. Concretely, on the condition that the above-mentioned flow rate condition and the pressure condition are satisfied, the substrate temperature is set to 1100° C. or over, preferably 900° C. or below, more preferably within a range of 950-1050° C. Herein, the substrate temperature means a “setting temperature for the substrate”.

[0039] The upper limit value and lower limit value not specified may be determined appropriately dependent on the composition of the underfilm and the film-forming rate.

[0040] The substrate may be made of oxide single crystal such as sapphire single crystal, ZnO single crystal, LiAlO2 single crystal, LiGaO2 single crystal, MgAl2O4 single crystal, or MgO single crystal, IV single crystal or IV-IV single crystal such as Si single crystal or SiC single crystal, III-V single crystal such as GaAs single crystal, AlN single crystal, GaN single crystal or AlGaN single crystal, and boride single crystal such as ZrB2.

[0041] Particularly, in the case of making the substrate of the sapphire single crystal, it is desired that surface-nitriding treatment is performed on the main surface of the substrate for the underlayer to be formed. The surface-nitriding treatment is performed as follows. First of all, the sapphire single crystal substrate is set in a nitrogen-including atmosphere such as an ammonia atmosphere, and then, heated for a given period. The thickness of the resulting surface nitride layer can be adjusted by controlling the nitrogen concentration, the nitriding temperature and the nitriding period appropriately.

[0042] If the sapphire single crystal substrate having the surface nitriding layer thereon is employed, the crystal quality of the underlayer formed directly on the main surface can be more developed. As a result, the crystal quality of the III nitride film to be formed on the underlayer can be developed, and thus, the dislocation density of the III nitride film can be more reduced.

[0043] It is desired that the surface-nitriding layer is formed thicker, for example, so that the nitrogen content of the sapphire single crystal substrate at the depth of 1 nm from the main surface is set to five atomic percentages or over, in ESCA analysis.

[0044] In view of enhancing the crystal quality of the underfilm, it is desired that the underfilm is formed at a higher temperature of 1100° C. or over and preferably 1250° C. or below.

[0045] Moreover, an epitaxial substrate composed of a given base material and a high crystallinity surface layer made of a second III nitride having a full width at half maximum (FWHM) of 90 seconds or below in X-ray rocking curve may be used.

[0046] Using such a substrate as mentioned above and such a fabricating method as according to the present invention, the underfilm to satisfy the conditions required according to the present invention as mentioned above can be fabricated easily and precisely. As a result, the III nitride film of lower dislocation density can be fabricated easily at good yield ratio.

[0047] In the present invention, the III nitride film to be formed on the underfilm has preferably the composition of AlxGayInzN (x+y+z=1), and, may include an additive element such as Ge, Si, Mg, Zn, Be, P or B as occasion demands. Moreover, the III nitride film may include a minute impurity contained in the raw material gases and the reactor or contained dependent on the forming condition.

EXAMPLES:

[0048] This invention will be concretely described, hereinafter.

Example 1

[0049] A C-faced sapphire single crystal substrate was employed, and then, set on a susceptor installed in a reactor of a MOCVD apparatus, and heated to 1200° C. with a heater built in the susceptor.

[0050] First of all, an ammonia gas (NH3) was flown with a hydrogen (H2) carrier gas for five minutes, to nitride the main surface of the substrate. In ESCA analysis, it was turned out that a surface-nitriding layer was formed on the main surface by the surface-nitriding treatment, and the nitrogen content at the depth of 1 nm from the main surface was seven atomic percentages.

[0051] Then, a trimethyl aluminum (TMA), a trimethyl gallium (TMG) and a trimethyl indium (TMI) were employed as Al raw material, Ga raw material and In raw material, respectively. Moreover, an ammonia gas was employed as nitrogen raw material. These raw material gases were introduced with a H2 carrier gas into the reactor at a flow ratio of NH3/TMA=450 under a pressure of 15 Torr, and supplied onto the substrate, to form an AlN film as a first III nitride film through epitaxial growth for 60 minutes. Thereafter, changing the flow ratio to 1000 from 450, another AlN film was formed as a second III nitride film, to form an AlN underfilm having a thickness of 1.5 μm.

[0052] FIG. 1 is a SEM photograph showing the surface figuration of the AlN underfilm. In FIG. 1, the flat region in the surface of the AlN underfilm is designated by the white region, and the concave-convex structure is designated by the black region. As is apparent from FIG. 1, about 50% of the surface of the AlN film is occupied by the flat region. When the surface roughness of the flat region was observed with a AFM, it was turned out that the average roughness Ra of the flat region was 5 Å.

[0053] When the FWHM in X-ray rocking curve of the (002) plane of the AlN underfilm was examined, it was 80 seconds.

[0054] Then, the substrate was heated at 1050° C. with the heater built in the susceptor, and then, a TMG as Ga raw material and an ammonia gas as nitrogen raw material were introduced with a H2 and N2 carrier gas into the reactor at a flow ratio of NH3/TMG=5000, and supplied onto the substrate, to form a GaN film having a thickness of 3 μm.

[0055] When the dislocation density of the GaN film was observed with a transmission electron microscope (TEM), it was about 1×107/cm2.

[0056] In forming the second AlN film, if the substrate temperature may be changed to 1080° C. from 1200° C. or the raw material pressure inside the reactor may be changed to 30 Torr from 15 Torr, instead of changing the flow ratio, such an underfilm as having almost 50% flat region ratio can be fabricated and thus, such a GaN film as having a lower dislocation density of about 1×107/cm2 can be obtained.

Example 2

[0057] Except that the TMA and the NH3 were supplied onto the substrate heated at 1200° C., made of C-faced sapphire crystal, at a flow ratio of NH3/TMA=1000 under a pressure of 15 Torr, to form an AlN underfilm having a thickness of 0.7 μm through the epitaxial growth for 60 minutes at one step, a GaN film was formed in a thickness of 3 μm on the AlN underfilm in the same manner as Example 1.

[0058] It was confirmed that a concave-convex structure was formed in the surface of the AlN underfilm, as shown in FIG. 1, and the surface roughness (average roughness Ra) of the flat region in the surface of the AlN underfilm was about 5 Å. Also, about 50% of the surface of the AlN film was occupied by the flat region. When the FWHM in X-ray rocking curve of the (002) plane of the AlN underfilm was examined, it was 80 seconds. The dislocation density of the GaN film was about 1×107/cm2.

Example 3

[0059] Except that, in forming the second AlN film, the flow ratio NH3/TMA was changed to 1500 from 1000, an AlN underfilm was formed in the same manner as Example 1.

[0060] FIG. 2 is a SEM photograph showing the surface figuration of the AlN underfilm. As is apparent from FIG. 2, about 20% of the surface of the AlN underfilm was occupied by the flat region. The FWHM in X-ray rocking curve of the (002) plane of the AlN underfilm was 80 seconds.

[0061] Then, a GaN film was formed in a thickness of 3 μm on the AlN underfilm in the same manner as Example 1. The dislocation density of the GaN film was turned out to be about 5×106/cm2 through the TEM observation.

Example 4

[0062] Except that, in forming the second AlN film, the flow ratio NH3/TMA was changed to 2000 from 1000, an AlN underfilm was formed in the same manner as Example 1.

[0063] FIG. 3 is a SEM photograph showing the surface figuration of the AlN underfilm. As is apparent from FIG. 3, none of the surface of the AlN underfilm was almost occupied by the flat region, and thus, a concave-convex structure was formed over the AlN underfilm entirely.

[0064] Then, a GaN film was formed in a thickness of 3 μm on the AlN underfilm in the same manner as Example 1. The dislocation density of the Ga film was turned out to be about 1×106/cm2 through the TEM observation.

[0065] In forming the second AlN film, if the substrate temperature may be changed to 1040° C. from 1200° C. or the raw material pressure inside the reactor may be changed to 45 Torr from 15 Torr, instead of changing the flow ratio, such an underfilm as having the almost 0% flat region ratio can be fabricated and thus, such a GaN film as having a lower dislocation density of about 1×106/cm2 can be obtained.

Comparative Example 1

[0066] The TMA and NH3 were supplied onto a C-faced sapphire substrate heated at 1200° C. at a flow ratio of NH3/TMA=450 under a pressure of 15 Torr, to form an AlN underfilm having a thickness of 1 μm at one step.

[0067] FIG. 4 is a SEM photograph showing the surface figuration of the AlN underfilm. As is apparent from FIG. 4, all of the surface of the AlN underfilm was occupied by the flat region.

[0068] Then, a GaN film was formed on the AlN underfilm in the same manner as Examples. The dislocation density of the AlN underfilm was about 1×108/cm2.

Comparative Example 2

[0069] The TMA and NH3 were supplied onto a C-faced sapphire substrate heated at 1200° C. at a flow ratio of NH3/TMA=700 under a pressure of 15 Torr, to form an AlN underfilm having a thickness of 1 μm at one step.

[0070] FIG. 5 is a SEM photograph showing the surface figuration of the AlN underfilm. As is apparent from FIG. 5, most of the surface, that is, about 70% of the surface of the AlN underfilm was occupied by the flat region.

[0071] Then, a GaN film was formed on the AlN underfilm in the same manner as Examples. The dislocation density of the GaN film was turned out to be about 8×107/cm2.

[0072] As is apparent from Examples and Comparative Examples, if an AlN underfilm is formed according to the present invention and a GaN film as a III nitride film is formed on the AlN underfilm, the dislocation density of the GaN film can be reduced to an order of 107/cm2.

[0073] Although the present invention was described in detail with reference to the above examples, this invention is not limited to the above disclosure and every kind of variation and modification may be made without departing from the scope of the present invention.

[0074] For example, in forming the second AlN film in Examples, only if the flow ratio NH3/TMA is set within the range required according to the present invention, it may be changed during the formation of the second AlN film constituting the AlN underfilm. Instead of the GaN film, an AlGaInN film or an AlN film may be formed on the AlN underfilm. Moreover, although the AlN underfilm and the GaN film are formed in the same MOCVD apparatus, they may be done in their respective appropriate MOCVD apparatuses.

[0075] For developing the crystal qualities of an underfilm made of e.g., AlN and a III nitride film made of e.g., GaN, a buffer layer or a multi-layered stacking films constituting, e.g., a distorted superlattice structure may be provided between a substrate and the underfilm or between the underfilm and the III nitride film.

[0076] As explained above, if an underfilm is formed on a given substrate by a simple MOCVD method according to the present invention, and then, a desired III nitride film is formed on the underfilm, the dislocation density of the III nitride film can be reduced remarkably.

Claims

1. A method for fabricating a III nitride film, comprising the steps of: preparing a given substrate, forming an underfilm having its surface of concave-convex structure in which 50% or below is occupied by the flat region and made of a first III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the first III nitride, and forming a III nitride film on the underfilm.

2. A fabricating method as defined in claim 1, wherein the first III nitride constituting the underfilm includes 70 atomic percentages or over of Al element for all of the III elements constituting the first III nitride.

3. A fabricating method as defined in claim 2, wherein the first III nitride constituting the underfilm is AlN.

4. A fabricating method as defined in claim 1, wherein 10% of the surface of the underfilm is occupied by the flat region.

5. A fabricating method as defined in claim 1, wherein the concave-convex structure except the flat region of the surface of the underfilm includes {101} facets.

6. A fabricating method as defined in claim 1, wherein the substrate is made of sapphire single crystal or SiC single crystal.

7. A fabricating method as defined in claim 6, wherein a surface nitriding treatment is performed onto the main surface of the sapphire single crystal substrate to form a nitrided surface layer at the main surface, and the underfilm is formed on the sapphire single crystal substrate via the nitrided surface layer.

8. A fabricating method as defined in claim 1, further comprising the step of forming, on the substrate, a surface layer having an average roughness Ra of 10 Å or below, and made of a second III nitride having a full width at half maximum in X-ray rocking curve of 90 seconds or below and including 50 atomic percentages or over of Al element for all of the III elements constituting the second III nitride.

9. An underfilm for fabricating a III nitride film, including a surface of concave-convex structure in which 50% or over is occupied by the flat region and made of a first III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the first III nitride.

10. An underfilm as defined in claim 9, wherein the first III nitride constituting the underfilm includes 70 atomic percentages or over of Al element for all of the III elements constituting the first III nitride.

11. An underfilm as defined in claim 10, wherein the first III nitride constituting the underfilm is AlN.

12. An underfilm as defined in claim 9, wherein 10% of the surface of the underfilm is occupied by the flat region.

13. An underfilm as defined in claim 9, wherein the concave-convex structure except the flat region of the surface of the underfilm includes {101} facets.

14. A method for fabricating an underfilm including a surface of concave-convex structure in which 50% or over is occupied by the flat region and made of a first III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the first III nitride, usable for fabricating a III nitride film, comprising the steps of: preparing a substrate, supplying a V raw material gas and a III raw material gas onto the substrate at a flow ratio (V raw material gas/III raw material gas) of 600 or below, to form, on the substrate, a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period, and supplying the raw material gas and the III material gas onto the substrate at flow ratio (V raw material gas/III raw material gas) of more than 600, to form, on the first film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period.

15. A method for fabricating an underfilm including a surface of concave-convex structure in which 50% or over is occupied by the flat region and made of a first III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the first III nitride, usable for fabricating a III nitride film, comprising the steps of: preparing a substrate, supplying a V raw material gas and a III raw material gas onto the substrate under a pressure of 20 Torr or below, to form, on the substrate, a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the III element through the epitaxial growth for a given period, and supplying the raw material gas and the III material gas onto the substrate under a pressure of more than 20 Torr, to form, on the first film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period.

16. A method for fabricating an underfilm including a surface of concave-convex structure in which 50% or over is occupied by the flat region and made of a first III nitride including 50 atomic percentages or over of Al element for all of the III elements constituting the first III nitride, usable for fabricating a III nitride film, comprising the steps of: preparing a substrate, supplying a V raw material gas and a III raw material gas onto the substrate heated at 1100° C. or over, to form, on the substrate, a first film made of a III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period, and supplying the raw material gas and the III material gas onto the substrate heated at less than 1100° C., to form, on the first film, a second film made of another III nitride including 50 atomic percentages or over of Al element for all of the III elements through the epitaxial growth for a given period.