1. Field of the Invention
This invention relates generally to semiconductor device manufacturing. More particularly, the present invention is directed to methods and apparatus for handling solder balls in forming ball grid arrays (BGAs).
2. State of the Art
Integrated circuit semiconductor devices (ICs) are small electronic circuits formed on the surface of a wafer of semiconductor material such as silicon. The ICs are fabricated in plurality in wafer form and tested by a probe to determine electronic characteristics applicable to the intended use of the ICs. The wafer is then subdivided into discrete IC chips or semiconductor dice, and then further tested and assembled for customer use through various well-known individual IC die testing and packaging techniques, including lead frame packaging, Chip-On-Board (COB) packaging, and flip-chip packaging (FCP). Depending upon the semiconductor die and wafer sizes, each wafer is divided into a few dice or as many as several hundred or more than one thousand discrete die.
Interconnection of discrete semiconductor packages onto a substrate such as a printed circuit board (PCB) is often accomplished with solder preforms having generally a spherical or other shape. In a process using a ball-grid-array (BGA), spherical solder balls are attached to prefluxed metallized locations on a workpiece such as a circuit board or a semiconductor device. The workpiece is then heated to reflow the solder balls, and the solder balls become attached to the metallized locations during subsequent cooling. A semiconductor package or circuit board having a corresponding but reversed pattern of connection sites may then be aligned with the BGA and bonded to it by controlled heating in a reflow furnace.
The use of flip-chip technology with solder bumps has numerous advantages for interconnection, it being widely used in the electronics industry. Flip-chip design provides improved electrical performance for high frequency processor applications, such as mainframes, computer workstations, and personal computers having powerful processors. Ball-grid-array interconnections are of small size. In addition, easier thermal management and reduced susceptibility to EMI and RFI emissions are inherent in the use of BGA technology.
In addition, surface mount technology (SMT) using solder “bump” or ball interconnects eliminates the outer package leads level of interconnection, significantly reducing the cost.
Solder bumps may be formed on a workpiece by processes of evaporation, electroplating, stencil printing, and serial methods. Each of these processes has particular limitations. U.S. Pat. No. 5,672,542 of Schwiebert et al. is an example of a modified stencil printing process.
In U.S. Pat. No. 3,716,907 of Anderson, the use of germanium hemispheres as conductive contacts is disclosed. The germanium hemispheres are connected to the substrates with solder.
Relative to other types of interconnections, the use of solder preforms, in particular spherical or near-spherical balls, has proven to have significant advantages. One advantage is that while the solder balls are formed with ball-to-ball size differences, they may be easily classified by size prior to application to a workpiece. Thus, a uniform size of solder balls may be used within a ball-grid-array.
Various methods have been used for aligning, placing, retaining and fixing solder balls on an array of sites on a workpiece.
In U.S. Pat. No. 5,620,927 of Lee, a template with an array of through-holes is placed on the workpiece and solder balls are introduced into the holes by rolling the solder balls across the workpiece surface. The apparatus may be installed on a tilt table to encourage filling of all holes. In U.S. Pat. No. 4,871,110 of Fukasawa et al., a template having an array of holes is placed on a ball holder with a like array of smaller holes to which vacuum is applied and over which solder balls are rolled. After the array is filled with solder balls, the template and ball holder with balls are removed and the exposed ends of the balls attached to a substrate by e.g. reflow. The template and ball holder are then pulled from the substrate, leaving a ball-grid-array ready for attachment to another substrate or workpiece. A vacuum system is required, and there is no easy way to replace a solder ball onto a bond pad to which a ball did not become attached (i.e., missing ball).
As shown in U.S. Pat. No. 3,719,981, an array of solder balls is arranged on the tacky surface of a pressure sensitive (PS) tape for alignment through a template to solder bumps on a wafer. After thermal reflow, the template and tape are removed.
The use of a template for forming solder bumps or “balls” on a workpiece from flux and solder pieces is disclosed in U.S. Pat. No. 5,492,266 of Hoebener et al.
U.S. Pat. No. 5,431,332 of Kirby et al., a template is placed over the bond pads of a substrate, solder balls are poured over the template, and an air knife “sweeps” the surface free of excess solder balls.
The use of a ball pick-up tool with an array of vacuum suction ball retainers to pull up balls from an underlying reservoir and place them on a substrate is disclosed in U.S. Pat. No. 5,088,639 of Gondotra et al., U.S. Pat. No. 5,284,287 of Wilson et al., U.S. Pat. No. 5,445,313 of Boyd et al., U.S. Pat. No. 5,467,913 of Nemekawa et al., U.S. Pat. No. 5,615,823 of Noda et al., U.S. Pat. No. 5,680,984 of Sakemi, U.S. Pat. No. 5,685,477 of Mallik et al., U.S. Pat. No. 5,687,901 of Hoshiba et al., and U.S. Pat. No. 5,695,667 of Eguchi et al. It is known in the art that shutting off the vacuum to release each ball onto the substrate is not always successful, and sometimes balls remain attached to the pick-up tool. Again, there is no easy way to replace a missing ball except with a single ball pickup tool.
U.S. Pat. No. 5,506,385 of Murakami et al. discloses the use of a single manipulable suction head for picking up a solder ball, moving it to a position above a fluxed contact pad on a substrate, and depositing it on the contact pad. Because of the high number of repetitive actions in separate placement of each ball, ball placement is time consuming.
U.S. Pat. No. 5,695,667 shows a single ball suction head which is used to place a solder ball on a contact pad which is missing a solder ball of a ball-grid-array.
The application of flux to solder balls held in a vacuum apparatus by dipping the balls into a flux reservoir is taught in U.S. Pat. No. 5,088,639 of Gondotra et al. and in U.S. Pat. No. 5,284,287 of Wilson et al.
The use of ultrasonic vibration to cause solder ball movement in the ball reservoir, and to remove excess solder balls from a vacuum pickup tool, is taught in U.S. Pat. No. 5,687,901 of Hoshiba et al.
The invention comprises apparatus and methods for rapidly, accurately, and reliably placing an array of conductive spheres such as solder balls on conductive sites, e.g. bond pads, on a substrate. The substrate may be a circuit board of any composition, e.g. BT resin, or may be a silicon wafer or even a single semiconductor die such as an “IC chip”. The conductive sites on the substrate may comprise bond pads which include those which project from the substrate and those which are recessed into the substrate surface. Projecting bond pads require a pre-application of flux or other sticky substance by which the spheres cling to the bond pads. Use of flux or sticky substance may not necessarily be required with recessed bond pads.
The apparatus includes a stencil plate or screen overlying the substrate, wherein the stencil plate is parallel to and slightly spaced from the substrate. The stencil plate has an array of through-holes corresponding to a desired placement pattern of conductive spheres on the substrate. The invention also includes ball supply apparatus for providing conductive spheres to the stencil plate, wherein all through-holes in the stencil plate are filled with one, and only one, sphere. Spheres placed into the through-holes of the stencil plate drop by gravity to the substrate for retention by pre-applied flux or by depressed bond pads. Each through-hole is slightly larger than a sphere and constrains a sphere on the substrate until the substrate and stencil plate are further separated e.g. for solder reflow. The stencil plate thickness and proximity to the substrate prevent more than one ball from entering each through-hole of the stencil plate.
A first embodiment of a ball supplying apparatus is a sphere-retaining hopper with a lower opening through which spheres may drop into through-holes of the stencil plate and thence onto the substrate surface. The hopper is closely spaced from the stencil plate to maintain control over all the spheres therein. Sphere placement is accomplished by horizontal movement of the hopper across the through-hole pattern of the stencil plate, filling each through-hole with one, and only one, sphere. As the hopper moves, only the spheres dropping into the through-holes, one to a through-hole, can escape from the hopper. The numbers of spheres passing over each through-hole ensure that each hole is filled, but a higher degree of assurance can be obtained by making several passes.
In a second embodiment, a sphere supply apparatus includes a shuttle plate with the same through-hole pattern as the stencil plate. The shuttle plate closely overlies the stencil plate and is reversibly movable between a first position wherein its through-hole pattern is aligned with the pattern of the stencil plate and a second position wherein the through-hole patterns are non-aligned. In the first position, spheres may drop from the shuttle plate through-holes into the stencil plate through-holes. In the latter position, spheres are prevented from entering the through-holes of the stencil plate. The through-holes of the shuttle plate may be fed from an overlying open bottom reservoir, which may be fixed to the shuttle plate or fixed in position. The linear movement of the shuttle plate is less than the inter-sphere distance, i.e. pitch, and is generally equal to about one-half of the pitch.
The following drawings illustrate various embodiments of the invention, not necessarily drawn to scale, wherein:
The invention comprises an improved method and apparatus for placing a plurality of conductive spheres 12, such as preformed solder balls or germanium balls, on conductive sites 14 on a surface 16 of a substrate 20. The term “substrate” is used in a broad generic sense herein to include any semiconductor device including a wafer or a packaged or unpackaged bare die, as well as traditional substrates including circuitized boards such as printed circuit boards (PCBs). The method of the invention may be applied to the placement of conductive spheres 12 on any conductive site 14, whether the site, e.g. a bond pad, projects from the substrate 20 or is recessed therein. The terms “conductive site” and “bond pad” are used interchangeably herein to denote any site 14 at which a conductive sphere 12 is to be placed.
One embodiment of the sphere placement apparatus 10 and the placement method used therewith are illustrated in drawing
As depicted in drawing
A stencil plate 30 of the sphere placement apparatus 10 is a planar plate with upper surface 38 and lower surface 42. An array of through-holes 34 is arranged in a through-hole pattern 32 which corresponds to bond pad pattern 22 of the substrate 20. Through-holes 34 have a diameter 36 which is slightly larger than the mean diameter 28 of the conductive spheres 12, so that the spheres may easily pass through, yet be closely constrained in lateral movement.
The stencil plate 30 has a thickness 40 which is configured and positioned for holding conductive spheres 12 on bond pads 14, such that a sphere supply apparatus 50 moving across the stencil plate does not intercept the placed spheres, while preventing more than one sphere from entering each through-hole 34.
The stencil plate 30 is configured to have its through-hole pattern 32 aligned with the bond pad pattern 22. Thus, through-holes 34A, 34B, 34C and 34D are shown vertically aligned by centerlines 26A, 26B, 26C and 26D with bond pads 14A, 14B, 14C and 14D, respectively.
Each stencil plate 30 is configured to operate with a substrate 20 having a particular bond pad pattern 22, a particular sphere diameter 28, and a given range of bond pad projection height 58 (
Referring to drawing
The sphere placement apparatus 10 includes a sphere supply apparatus 50 which in this embodiment is a hopper 50A having a lower opening 44 (
The lower opening 44 has a width 48 equivalent to about two (2) to about ten (10) sphere diameters 28. Thus, for conductive spheres 12 having a diameter 28 of 1.0 mm, the lower opening may have a width 48 of about 0.2 cm. to about 1.0 cm.
As shown in drawing
The substrate 20, stencil plate 30, and hopper 50A are each manipulated in robotic action to maintain the desired clearances and alignments, and to move the hopper 50A between positions 64 and 66.
In the drawings of
The hopper 50A may have inside wall surfaces 46 which are sloping, as in
Another embodiment of the sphere placement apparatus 10 is shown in drawing
In another embodiment of the shuttle plate 80 and sphere reservoir 90, they are not connected. The reservoir 90 may be kept in one position while the shuttle plate 80 moves past it for filling the through-holes 84.
Turning now to the method of using apparatus 10 for placing conductive spheres 12 on a substrate 20, we examine drawing
As shown in drawing
After a layer 52 is formed on the bond pads 14, the lower surface 42 of a stencil plate 30 and the upper surface 16 of a substrate 20 are aligned to provide a desired plate-to-pad gap 56 (see
The hopper 50A, having conductive spheres 12 therein, is moved in direction 68 across the through-hole pattern 32 of the stencil plate 30, whereby spheres are dropped into each through-hole 34 to become adhered to the bond pads 14 (as shown in
At this point in the process, the stencil plate 30 may be tested, either visually or by other methods known in the art, to ensure that all through-holes 34 are filled. If any through-holes 34 are unfilled, the hopper movement may be repeated.
Upon filling of all through-holes 34 with conductive spheres 12, the substrate 20 and/or the stencil plate 30 with hopper 50A are moved in direction 70, separating the substrate as shown in drawing
The placement method for the embodiment of drawing
The methods described herein present many advantages to the BGA formation process, including higher reliability, lower cost, reduced ball wastage, etc. The apparatus and methods are relatively simple, yet provide a great deal of flexibility in substrate type, sphere size, sphere composition, etc. Non-filling of a through-hole of the stencil plate is easily cured by moving the sphere supply apparatus through another cycle. There is no need for using a single-head ball picker to place a single ball as noted in the prior art.
This invention may be embodied in several forms without departing from the spirit of essential characteristics of the invention. The embodiments as described herein are therefore intended to be only illustrative and not restrictive, and the scope of the invention is defined by the appended claims rather than the preceding description, and all variations that fall within the metes and bounds of the subject matter claimed, or are equivalent thereto, are therefore intended to be embraced by the following claims:
This application is a divisional of application Ser. No. 09/576,727, filed May 23, 2000, pending, which is a divisional of application Ser. No. 09/168,621, filed Oct. 8, 1998, now U.S. Pat. No. 6,268,275, issued Jul. 31, 2001.
Number | Date | Country | |
---|---|---|---|
Parent | 09576727 | May 2000 | US |
Child | 10977301 | Oct 2004 | US |
Parent | 09168621 | Oct 1998 | US |
Child | 09576727 | May 2000 | US |