This invention relates to hard, wear resistant coatings vapour deposited over a metallic or non-metallic surface, in particular, the invention relates to a coating to be deposited on rotary tools having cutting edges utilized in industrial, medical and dental cutting, and form scraping, and is more particularly directed to improvements in blades and rotary cutting instruments.
Hard wearing surfaces are in common use in various industries, and such hard wearing surfaces are frequently obtained by coating the surface of a tool made of steel or similar metal, or other hard, enduring material, with a layer of hard wearing ceramic substance, such as carbides, nitrides and carbonitrides, or providing a hard microcrystalline diamond coating. There are known methods for obtaining hard wearing coatings, such as for example, having a coating of diamond particles in combination with a carbide or nitride layer and then filling the gaps between the abrasive particles with a softer intermetallic compound. Another known method is vapour deposition of hard-wearing ceramic materials from plasma or by utilizing molten ceramic substances. Hard wearing surfaces for use on medical, surgical and dental tools have additional requirements, as such surgical and dental tools need to be frequently sterilized, hence medical tools have to be corrosion resistant.
A device for yielding hard ceramic surfaces by cathodic arc plasma deposition is described in U.S. Pat. No. 4,851,095, issued to M. A. Scobey et al. on Jul. 25, 1989. The apparatus of Scobey et al. utilizes a high intensity ion flux. Vapour deposition of a hard ceramic material, such as titanium or zirconium nitride, on a stainless steel or titanium surface by utilizing a molten evaporant and a hollow cathode, is described in U.S. Pat. No. 5,152,774, issued to W. A. Schroeder on Oct. 6, 1992. The vapour deposition of Schroeder is conducted at relatively low temperature, thus the substrate will have lost little of its initial high strength properties, however, the requirement of low surface roughness of the deposited layer is not addressed by U.S. Pat. No. 5,152,774. In U.S. Pat. No. 4,981,756, issued to H. S. Rhandhawa on Jan. 1, 1991, a method is taught to coat surgical tools and instruments by cathodic arc plasma deposition. The ceramic coating obtained by this technology is a nitride, carbide or carbonitride of zirconium or hafnium, in a single layer of 3-10 μm thickness. U.S. Pat. No. 4,981,756 also refers to various publications describing known equipment for obtaining hard-wearing surfaces by cathodic arc plasma deposition. U.S. Pat. Nos. 5,940,975 and 5,992,268 issued to T. G. Decker et al. on Aug. 24, 1999 and Nov. 30, 1999, respectively, teach hard, amorphous diamond coatings obtained in a single layer on thin metallic blades or similar metallic strips utilizing filtered cathodic arc plasma generated by vaporizing graphite. It is noted that no interlayer is formed between the blade surface and the deposited amorphous diamond coating.
The grain size of deposits obtained in conventional cathodic plasma arc methods may range between 0.5 to 10 μm. Any post-deposition heat treatment which may be required to maintain maximum hardness of the substrate's core metal, may lead to internal stresses in the coating due to differences in the grain size, and can eventually lead to abrasion, spalling, crack formation, grain separation, surface fractures, uneven edges and rough surfaces, and the like, which can drastically reduce the wear resistance and durability of surgical instruments and dental tools. None of the above discussed methods are concerned with even grain size and surface structure, and low micro-roughness of the vapour deposited hard, ceramic coatings, which have particular importance for dental and surgical tools, and in other applications where straight, sharp, even and nick-free edges are essential requirements.
Users desire cutting blades with sharp edges possessing long life and corrosion resistance. Typically, blades are initially sharpened to form a wedge shaped cutting edge and re-sharpened as needed, except in the case of razor blades which cannot be re-sharpened. Sharpness of a cutting blade is measured in terms of “ultimate tip radius”, which is different depending on the application. For kitchen knives, rotary cutters, and similar cutting instruments, ultimate tip radius may be several thousand Angstroms. In agricultural implements incorporating rotary blades that cut through the soil, axes, and in chisels, the cutting edge radius may be expressed in microns or even in millimeters rather than Angstroms. Shaving razor blades ordinarily have ultimate tip radii of about 1,500 Angstroms or less. This radius usually includes a layer of hard material coating applied to the wedge shaped base material of the razor blade. A self-sharpening blade having a cutting edge with different hardness and wear resistance on opposite sides of the blades, provided by applying different coating layers on opposite sides of the blade is described in U.S. Pat. No. 6,105,261, issued to Ecer on Aug. 22, 2000. This invention provides a solution to the problem of the cutting edge dulling by providing self-sharpening cutting edges with different hardness and wear resistance on opposite sides of the edge while both sides have micro-hardness and wear resistance significantly greater than the substrate metal. Cutting areas are kept sharp longer with this method especially in such adverse environments as in dental/surgical applications, use as saw blades and scrapers and in the construction industry. The disadvantage of this approach is that more intensive wear on one side of the edge leaves the hard layer unsupported which eventually results in a failure of the more brittle hard layer by fracturing. The soft side of the cutting edge has a higher wear rate which affects the support of the brittle thin film coating on the opposite side.
Coatings such a TiN, Ti(CN), or (TiAl)N deposited onto the blade edge region of a steel knife blade blank by a cathodic arc process with simultaneous heating and rotation of the blade blank relative to the deposition sources are described in U.S. Pat. No. 5,724,868, issued to Knudsen et al. The blade edge region may be sharpened or unsharpened prior to deposition of the coating material. If the blade edge region is unsharpened prior to deposition, it is thereafter sharpened, preferably on one side only. An improvement of this method was proposed in U.S. Pat. No. 6,656,186, issued to Meckel et al. and includes depositing different coatings with different hardness on both sides of the blades adjacent to cutting edge. However, in operation the material on the softer side of the blade suffers greater wear and is not be able to support the harder coating on the opposite side of the blade. Further, this method as well as the methods described previously, does not address issues of friction and galling properties of the coated surface on the cutting tool.
It is known to coat dental tools and surgical instruments with titanium nitride and titanium, wherein the coating is obtained by conventional cathodic arc deposition applied to corrosion resistant stainless steel substrates. The cutting surfaces of such medical tools need to be smooth, as well as hard-wearing to prevent trapping and retaining materials which can be harmful to the patient. Hence, another requirement is that the cutting edges be very straight, sharp and nick-free to avoid damage to the surrounding flesh and skin during dental or surgical treatment. There are known methods described, wherein the cutting tips of surgical instruments made of steel have been sand-blasted and then coated with a hard-wearing ceramic composition, however this method can, and is likely to, increase surface roughness and unevenness, rather than eliminate it. The main disadvantage of these methods is that the hard or even superhard coating with micro-hardness in excess of 20 GPa is deposited on relatively soft substrate surface made of steel or other alloy having micro-hardness less than 8 GPa. That creates a so-named egg-shell effect when the failure of the hard and brittle thin film coating is due to mechanical deformation of underlying soft substrate material.
The duplex technology utilizing ionitriding followed by thin film coating was developed to improve the wear resistance to bridge the mechanical properties between the soft substrate metal and hard coating. This technology however is limited to selective types of steels and metal alloys due to poor adhesion of the hard coatings to most ionitrided metallic materials.
In U.S. Pat. No. 6,617,057 issued to Gorokhovsky a multilayer cermet coating is described which employs alternating metal and ceramic layers. This coating architecture provides high hardness and at the same time secures necessary elasticity and ductility so the brittle hard ceramic layer will not fail due to bending and deformation of the substrates while the tool is in operation. Using the cathodic arc technology to create the multilayer coating eliminates the problems of surface roughness and increased radius of cutting edge. The coatings produced have a moderate hardness and wear resistance but exhibit relatively high friction and high galling properties. These cermet coatings have relatively higher friction in comparison with carbon diamond like (DLC) and related coatings.
There is a need for a method which can provide a fine grained, hard wearing ceramic surface that has low micro-roughness, sharp even edges, and has a low friction coefficient and presents anti-galling properties. In preferred cases, the coating should also withstand post-deposition heat treatment without degradation of the coating.
All patents, patent applications, provisional patent applications and publications referred to or cited herein, are incorporated by reference in their entirety to the extent they are not inconsistent with the teachings of the specification.
An object of invention is to obtain a stable cutting edge consisting of multilayer coating with different architectures on both sides of the blade of a rotary tool. These coatings primarily focus on reduction of stickiness and friction of the rotary instruments to reduce torsion fatigue when they come in contact with their counterpart. Other properties of the surface engineered instruments are dedicated for improvement of coating toughness, abrasion wear resistance and corrosion resistance.
The coating of the subject invention generally comprises a top wear-resistant low friction anti-galling segment overlaying a bottom multilayer bondcoating cermet segment which accommodates the internal stresses in the top segment and secures the highest toughness of the entire coating system. A hard case can be optionally created on the surface of the bulk metal substrate under the bondcoating segment by ionitriding or carburizing, which reduces the gradient of mechanical properties between the hard ceramic coating and the relatively soft metallic substrate. In addition the ionitrided or carburized layer serves as a hard foundation to support the thin low friction top segment coating against mechanical deformation of the soft base metal material. The top coating segment comprises of a near amorphous matrix composed of carbon, metal doped carbon, hydrogenated carbon having a mixture of diamond like and graphite like interatomic bonding. The amorphous matrix can be optionally filled with nanocrystalline refractory ceramic phases such as carbides, nitrides, silicides, borides, oxides, carbo-borides and a like compounds with size of the crystals ranging from 0.5 to 100 nm. The coefficient of friction of the top segment coating is less than 0.3. The bottom multilayer cermet coating segment has a fine columnar structure which contributes to the extremely high adhesion and flexural rigidity while the top layer reduces friction and galling forces and contributes to the high wear resistance of the coating. This coating architecture is especially beneficial for rotary instruments for protection against abrasive wear, reducing torsional friction, and improving fatigue life. This not only improves the durability of the instrument, but also reduces the negative effect of cutting on counterparts, which is especially important in the case of dental and medical instruments. A cutting tool with the coating of this invention leaves a smooth surface after cutting without holes and disruptions created by chunks of materials being removed due to scuffing induced by stickiness of the cutting material to the surface of the cutting tool.
According to one embodiment of the present invention a wear resistant, composite vapour deposited metal ceramic coating is provided on a substrate capable of electrical conduction. The coating comprises a bottom bond segment composed of a metal-ceramic multilayer architecture and a top low friction anti-galling nanostructured segment. The bottom bond segment includes at least one metallic layer selected from the group consisting of titanium, chromium, vanadium, aluminum, molybdenum, niobium, tungsten, hafnium, zirconium and alloys thereof and having a metallic layer thickness. The bottom bond segment further includes at least one ceramic layer selected from the group consisting of nitrides, carbides, carbonitrides, oxynitrides, borides, carboborides, borocarbonitrides, silicides, borosilicides and combinations thereof. The bottom bond segment coating has a thickness greater than 0.01 μm, a micro-roughness of less than the total thickness of the uppermost ceramic layer, and a micro-hardness in excess of 20 GPa. The top low friction anti-galling coating segment includes amorphous diamond like matrix composed of the group of elements consisting of carbon, boron, silicon, nitrogen, hydrogen, oxygen and transition metals optionally filled with nanocrystalline refractory ceramic phase embedded in the amorphous matrix. The amorphous matrix can further include diamond-like interatomic bonding. The nanocrystalline refractory ceramic phase comprises carbides, borides, silicates, nitrides and oxides. The thickness of the top segment coating is greater than 0.01 μm. The size of refractory ceramic nanocrystals ranging from 0.5 to 100 nm. The coefficient of friction of the top coating segment is less than 0.3.
The substrate can be of steel or titanium alloys. The steel substrate is preferably made from high chromium steel such as, for example, 440 series and 17-4 series. The substrates made of titanium alloys include Nickel-Titanium based alloys. The steel can have an ion nitrided, ion implanted, oxi-nitrided or carburized surface layer between it and the bottom bond coating segment.
A process is provided for producing a wear resistant, low friction, composite vapour deposited metal-ceramic coating on the surface of the substrate capable of electrical conduction. The surface of a substrate is first cleaned then placed into the vacuum chamber of a vapor depositing device capable of providing controlled electric and magnetic fields where the substrate is coated with at least one metallic layer and at least one ceramic layer then coated with a top coat. Optionally, the surface of the substrate is treated in a ionitriding, oxynitriding, ion implantation or carburizing process step. The process comprises the following steps:
i) providing a substrate capable of electrical conduction, having a surface and cleaning said surface with at least one cleaning method selected from the group consisting of chemical cleaning, electrolytic cleaning, grinding, polishing, tumbling and ion bombardment to produce a cleaned substrate;
Alternatively, a blank (unsharpened) substrate can be coated with a cermet bondcoating segment, then sharpened. The sharpened surface is then cleaned and coated with a low-friction, anti-galling top coat. The method comprises the steps of:
The following optional step can be introduced between step ii) and step iii); if required or preferred, heat treating the obtained vapour deposited first segment coating deposited on said substrate surface.
The following additional optional step can be introduced between step iv) and step v); if required or preferred, ionitriding or ion implantation prior to deposition of top segment low friction anti-galling coating layer.
The distinguishing feature of the coating deposition steps, when applied to the substrates made of thermally sensitive alloys, is that it exposes the substrate to the plasma deposition in a periodic pulsing manner with depositing time, when the substrate is exposed to the vapour plasma deposition process followed by pause time, when plasma environment is removed from contact with the substrate and the substrate is cooled by means of radiation cooling and conduction cooling. The thermal sensitive substrates are defined by their sensitivity to being heated to the temperatures above a certain value critical for this particular alloy causing them to lose some of the important functional properties, which may or may not be further restored by subsequent heat treatment.
A detailed description of the preferred embodiments of the invention will follow, illustrated by working examples.
For the sake of clarity, definition of what is understood by some of the terminology used in the discussion of the preferred embodiments of the present invention is provided below.
“Substrate” is understood to mean a three dimensional body providing the surface on which the vapour species is deposited. Only a portion of the surface, usually the surface in the proximity of one end of the substrate body, is utilized as the depositing surface, and the other end of the body of the substrate is attached to or is supported by, a substrate mount or holder. It is preferred that the portion of the surface on which the deposit is to be obtained, has close to uniform temperature, while the rest of the substrate may be in a temperature gradient.
“Plasma” is considered to mean an atmosphere of low pressure and high temperature, containing a mixture of ionized gases and metal vapor. Not all the gases in the plasma are ionized, but it is usual that the species to be deposited is ionized. The components of plasma often include argon or similar inert gases, both in the atomic state and in an ionized state.
“Even surface” in the context of a deposited layer surface is understood to mean that the average distance between the peaks of the deposited surface and the valleys of the deposited surface, is small. In other words, the micro-roughness of an evenly deposited surface is considered to be low.
In one embodiment of the present invention multiple layers of a controlled thickness of a metal and of a hard-wearing ceramic compound of the same metal, are deposited in successive steps on a conductive substrate surface, usually stainless steel, titanium alloy, or other appropriate metal. It is preferred that at least two pairs of the metal layer and the hard-wearing ceramic layer are deposited on the steel substrate. The number of layer pairs constituting the coating may range from 2 to as high as 100s, depending on the desired coating thickness, and on economic considerations. The bottom bondcoating segment can have at least one pair of a metal layer and a ceramic layer having a common metal ion component. The bottom bondcoating segment can comprise a multiplicity of pairs of metal and ceramic layers having a common metal ion component. The composite vapor deposited metal-ceramic coating can be heat treated subsequent to deposition. The thickness of the bottom bond coating segment can range between 0.01 μm and 30 μm. The vapor deposited metal-ceramic coating can comprise a portion of a surface of a dental tool, a surgical tool or a cutting tool. The bottom bond coating segment can comprise one side of the blade, or both sides, while the top low friction segment can overlay both sides of the blade. The top coat, low friction layer can be deposited over the multilayer bondcoat. The thickness of the top low friction anti-galling coating segment can range between 0.01 μm and 30 μm. The total coating thickness can range between 0.02 μm and 40 μm.
Several different coating deposition processes either associated with physical vapor deposition (PVD) or chemical vapor deposition (CVD) or hybrid PVD+CVD technology can be used for deposition of the coating of the subject invention. The protective or functional thin coatings on dental and medical instruments are aimed to improve cutting efficiency, durability and bio-compatibility. Conventional CVD technology requires high temperature for decomposition of metal-organic, halide or hydrocarbon based precursors, which makes its applications restricted to high temperature substrates. Using low pressure plasma assisted CVD processes (PACVD) allows for reduced substrate temperatures during the coating deposition stage, but is still restricted to a limited number of elemental compositions and coating architectures. PVD processes such as magnetron sputtering and electron beam evaporation are widely used for coating deposition on cutting tools. Electron beam PVD technology (EBPVD) can provide a theoretically unlimited evaporation rate of a wide variety of different materials: metals, ceramics, cermets, both conductive and dielectric materials, but the ionization rate of the EBPVD metal vapor flow is extremely low (<0.1%) which require ion beam assistance to achieve dense coatings with acceptable adhesion and fine microstructure.
Sputtered multilayer coating stacks using multiple sources within the same system, are used routinely for industrial manufacturing on any substrate that can handle vacuum and plasma exposure. To reduce cross contamination from one source to another either zoned vessels or other means to isolate a source from adjacent neighbors are common. Sputtering in conjunction with a reactive gas can yield a myriad of coatings with a wide variety of elemental compositions and architectures. Matrix sputter source structures using 2 or more part targets are possible that yield various composition combinations simultaneously. The magnetron sputtering process is capable of generating an atomized vapor flow from targets having low electrical conductivity. Using a split target of graphite or boron carbide with a metal segment made of molybdenum, titanium or other transition metals allows for deposition of Me doped diamond-like and boron carbide based coatings. Co-sputtering (2 sources with different targets on each) yield variability of composition over the course of a given process. By having various targets adjacent or oriented at roughly 45° to 90° in respect to the substrate surface and varying the power to each source separately it is possible to yield not only different thickness but also different compositions within a thin film. The primary issues with sputtering are low productivity (rate of deposition) and necessity of using large concentrations of argon as a sputtering gas. Low ionization rates on the order of 1-3% in magnetron sputtering flows reduce the intensity of ion bombardment assistance during coating deposition processes resulting in coarse coating morphology and fair adhesion. To improve coating structure, adhesion toughness, and functional properties, a number of different processes were introduced. Unbalanced magnetron methods are successful in attaining higher ionization (up to 10-15%) in comparison to conventional magnetron sources but it is still too low for substantial improvement of coating density and adhesion. Using recently introduced pulse magnetron sputtering technology allows further increases in the ionization rate, but the drawback of this approach is the reduction in the coating deposition rate (productivity). Large pulses can also generate an increased amount of macroparticles increasing the density of surface defects. PACVD, magnetron sputtering and EBPVD processes produce vapor plasma flow with low, near thermal kinetic energy, which can be detrimental for deposition of coating on substrates composed of materials with low electrical conductivity.
The cathodic arc deposition (CAD) technology can evaporate electrically conductive (metal like) targets and produce a nearly 100% ionized vapor plasma with kinetic energy of ions ranging from 40 to 200 eV and it does not require sputtering gas, but it suffers from large amount of macroparticles generated along with vapor plasma from cathodic arc spots located at the cathode target surface. This setback of the conventional CAD technology is overcome by filtered cathodic arc processes, which effectively eliminate the macroparticles and yield up to 100% ionized and atomized metal vapor flow. This filtration can occur by means of mechanical shutters in the direct path of the plasma to the substrate materials. The filtration can also be accomplished by bending the plasma flow in one or more bends using magnetic steering coils. In the following a brief and simplified description of this technology will be provided, however, it should be understood that this is given merely to allow clarification of the process parameters and is not intended as an accurate scientific description of the mechanisms involved in filtered cathodic arc technology. In cathodic arc technology metal droplets and metal vapour are generated by applying an arc of high current to a negatively charged target metal in a vacuum chamber. At the same time, high concentrations of electrons are also released from the target metal cathode at high speed. The vacuum chamber, by definition, contains a gas at a low pressure, and it is usual that the gas is fed to the chamber as plasma containing a gas or a gas mixture at high temperature in a partially ionized state. The high speed electrons collide with the gas molecules, thereby further ionizing the gas molecules, which in turn collide with and ionize the metal droplets and metal vapour. The ionized gas and the ionized metal vapor and metal droplets proceed towards the negatively charged substrate also located in the vacuum chamber. The metal deposits in a layer over the surface of the substrate. When the gas is an inert gas no reaction takes place between the ionized gas and metal vapour. On the other hand, in the instance of the plasma also containing reactive gases, the ionized gases will react with the metal vapour, forming a deposited ceramic compound layer. In conventional cathodic arc plasma deposition the vaporized metal droplets in the plasma can vary in size, thus the metal or the ceramic compound deposited on the substrate is likely to exhibit widely varying grain sizes and surface unevenness.
In a recent modification of plasma technology deposits are obtained by filtering a cathodic arc source by means of appropriately adjusted magnetic fields. An example of such a cathodic arc plasma coating apparatus is described in U.S. Pat. No. 5,435,900 issued to V.I. Gorokhovsky, which is incorporated herein by reference. The operating pressure of the filtered arc deposition process ranges from 10−6 torr to 10−2 torr, which overlaps with most of the conventional plasma assisted PVD and low pressure CVD processes. This makes it possible to use the filtered arc plasma environment as ionization and activation means for hybrid processes utilizing a combination of different conventional PVD and low pressure CVD processes operating in a filtered arc plasma immersion environment as it is better described in US Pat. Application Publication No. 2004/0168637 A1 of V. I. Gorokhovsky, which is incorporated herein by reference. The hybrid surface engineering system, based on this approach, which includes conventional unbalanced magnetron sputtering plasma sources, EBPVD evaporation sources, thermal evaporation source, low pressure PACVD plasma source and large area dual filtered arc depositing (LAFAD) plasma sources, which can be used in practicing the present invention is shown schematically in
The application of magnetic filtering of the cathodic arc stream eliminates macroparticles, as well as neutral non-ionized species, and thereby substantially only ionized metal vapor and nano-sized metal droplets carrying a charge, will reach the substrate. This results in deposit layers of even grain size, and surfaces having very low micro-roughness. Such surfaces can be referred to as evenly deposited surfaces.
The substrate selected for deposition in the present process is a conductive material, such as a metal or a hard-wearing substance having relatively high electrical conductivity. It can be chosen from different grades of stainless steels or titanium alloys. In one of the preferred embodiments the substrate is stainless steel of the AISI 300, 400 (such as high chromium 440A, 440B, 440C and 440XH (Carpenter) stainless steel) or 1700 series, such as the 17-4 series. One skilled in the recognizes the compositions of several of these preferred steels, for example; TRIM RITE-C 0.15/0.30, Mn 1.00, P 0.04, S 0.03, Si 1.00, Cr 13.50/15.00, Ni 0.25/1.00, Mo 0.04/1.00, balance Fe; 440F—Se—C 0.95/1.20, Mn 1.25, P 0.040, S or Se 0.15 (min.), Si 1.00, Cr 16.00/18.00, Mo 0.60, balance Fe; TRINAMET-type analysis C (max.) 0.30%, Mn (max.) 1.00%, P (max.) 0.040%, S (max.) 0.03%, Si (max.) 1.00%, Cr12.00 to 14.00%, Mo 1.00 to 3.00%, Cu 2.00 to 3.00%, Fe, balance; IRK91 (see U.S. Patent Application Publication No. 2004/0197581) (Sandvik Bioline)-C+N≤0.05, Cr 12.0, Ni 9.0, Mo 4.0, Ti 0.9, Al 0.30, Si 0.15, Cu 2.0; 7C27Mo2-C 0.38, Si 0.4, Mn 0.6, P (max.) 0.025, S (max.) 0.01, Cr 13.5, Mo 1.0; 20AP-C 1.0, Si 0.2, Mn 0.4, P (max.) 0.03, S 0.05, Cr (max.) 0.10, Ni (max.) 0.10, Mo (max.) 0.03, other Pb 0.2. In another embodiments it is a shape memory alloy such as NITINOL, ENDONOL, or NiTi alloy composed of various compositions of nickel and titanium or equiatomic (50/50 at. %) composition of Nickel and Titanium. It is possible that NiTi steels be doped with other elements as well, such as, for example, copper.
The coatings and methods of the subject invention are exemplified for use primarily on endofiles and implant drills. The subject coatings and methods can be applied to scalers, ultrasonic scalers, and dental burs as well. In preferred embodiments, scalers are made of the following steels: 440A, 440C, 440Xh, 440F—Se, 1RK91, 13C26, 4C27Mo2, and 20AP. Both Piezo and magnetostrictive ultrasonic scalers are preferably made of: the 17-4 family of steels, 13-8, TRIMRITE, TTRINAMET, 420, 1RK91, 13C26, 4C27Mo2, 20 AP. Preferred compositions for implant drills include: 17-4 steel and 300 series steel, 1RK91, 13C26, 4C27Mo2, and 20AP. Dental burs are preferably carbide-stainless steel with high hardness. It is preferred that endofiles are made of 17-4, 13-8, NiTi, TRIMRITE, TRINAMET 420, 1RK91, 13C26, 4C27Mo2, and 20 AP steels.
The substrate surface to be coated is first cleaned, by a usual cleaning processes which can include degreasing, tumbling, grinding, polishing, chemical cleaning, degreasing, electrolytic cleaning, ion bombardment or similar conventional cleaning steps which can render the surface receptive of the deposited substance.
The cleaned substrate can optionally be ion nitrided, oxi-nitrided or carburised or subjected to ion implantation to increase the hardness and corrosion resistance of the substrate surface and possibly further improve adherence of the deposited coating. The ion nitriding or ion implantation step may be conducted in a separate apparatus, or the universal surface engineering system shown on
The substrate having a cleaned, and optionally nitrided depositing surface, is then placed in the vacuum chamber of a suitable cathode arc plasma depositing device having at least one of plasma vapor deposition means, such as described above. The arc cathode targets, magnetron targets, EBPVD evaporating material, resistive evaporating material and PACVD reactive gaseous precursors are selected for the plasma vapour generation, are selected as they are capable of forming low friction, anti-galling, hard, wear and corrosion resistant compounds by vapour deposition. The metallic and non-metallic elements which are preferred in such compound formation are titanium, chromium, vanadium, molybdenum, aluminum, hafnium, zirconium, niobium, tungsten, their alloys, carbon, boron, silicon, and elements of similar nature. The preferred reaction gaseous precursors are nitrogen, hydrogen, oxygen, hydro-carbon gases, borazin, boron trichloride, trimethylsilane (3MS) and gases of similar nature.
The gas atmosphere in the cathodic arc depositing device is controlled such that it can yield either a vapour deposited metal layer or a vapour deposited ceramic compound layer. The ceramic compounds that have desired wear resistance, corrosion resistance and hardness are the carbides, nitrides, carbonitrides, oxycarbides and oxynitrides of the above listed metals. The plasma for depositing the desired ceramic layers contains one or more of the following gases: nitrogen, methane or other hydro-carbon gas, borazin, 3MS and oxygen. In the vapour deposition of layers of the above listed metals only argon, or similar inert gas containing plasma is used. Argon may also be utilized to dilute or carry the gases reacting with the metal vapour or metal deposit, to form the desired ceramic [metal] compounds. The metal and ceramic compound combinations suitable for forming hard, wear resistant coatings by vapour deposition in the present invention, are listed in Table 1 below.
The first metal layer to form a metal-ceramic compound layer pair, is obtained by having one of the metals listed above as cathodic target metal. The metal layer is deposited in an inert gas, usually argon, in a thickness ranging between 0.01 μm and 0.2 μm. The preferred range is 0.01 to 0.1 μm. Usually, the same cathodic target metal is used in obtaining the second, ceramic compound layer of the pair, however, the cathodic plasma arc composition is adjusted to contain the gaseous component required to form the appropriate ceramic [metal] compound. The thickness of the vapour deposited ceramic compound layer is usually selected to be between 0.01 and 2 μm, depending on the design, shape and ultimate purpose of the deposited coating on the substrate. The metal/ceramic multilayer coating has to have a high cohesion toughness, which is often determined by resistance to plastic deformation parameter H3/E*2, where H is hardness and E is elastic modulus of the coating. It is required that multilayer coating of this invention has the H3/E*2>0.05.
The multilayer cermet coatings using a ceramic sublayers composed of nitride, carbonitride, carbide, boride, carbo-boride, carbo-boron-nitrides and combinations thereof can be used as a coating protecting against abrasion wear and corrosion as described in U.S. Pat. No. 6,617,057 issued to V.I. Gorokhovsky, which is incorporated herein by reference.
While the multilayer metal-ceramic coating architecture addresses the abrasion wear resistance and corrosion resistance, there are important issues which must be addressed in the case of rotary dental instruments such as implant drills and root canal endofiles. In this case the friction and stickiness between the instrument surface and counterpart (body tissue) creates a large torsional momentum which contributes to the development of cracks through the surface of the tool and leads to separation of the instrument. As shown in the U.S. Pat. No. 6,074,209 issued to W. B. Johnson, which is incorporated herein by reference, torsional fatigue is the main reason for the failure of rotary endodontic instruments such as endofiles. When debris sticks to the surface of the rotary instrument flute it prevents the flute from removing the debris from the hole, accumulates a large amount of debris along the flute and dramatically increases the torsional momentum imposed on the tool. In addition to reduction of friction and stickiness the top coating of the subject invention imposes a substantial compressive stress on the surface layer of the instrument, which prevents cracks from developing and slows the propagation of the cracks effectively improving the torsional fatigue life of the instrument. The top coating of this invention typically provides the compressive stress ranging from 0.1 to 8 GPa. The bottom multilayer metal-ceramic coating segment protects against both pitting and stress induced corrosion. The integrity of this segment is quite important. If the metal surface finish is near perfect the pitting and stress corrosion is concentrated through the coating defects, imperfections, voids, porosity. The LAFAD technology substantially reduces the surface defects by effectively eliminating the macroparticles and increasing ionization of the depositing metal-gaseous plasma. Using intense ion bombardment during vapor plasma deposition process allows not only reduction of the coating roughness, but also fills and mitigates the initial surface defects via the increase of adatom mobility and surface diffusivity.
In one of the preferred embodiments, a steel substrate has a bottom bondcoating segment of several vapour deposited layer pairs and is subsequently removed from the vacuum chamber of the filtered cathodic arc plasma depositing device and annealed or heat treated in vacuum or in a low pressure inert gas at a temperature between 900° C. and 1100° C. by usual methods, followed by quenching in nitrogen or nitrogen/argon atmosphere and tempering at 150° C. to 400° C. The coated and heat treated substrate then can be sharpened or ground to prepare a necessary cutting shape blade or flute. After this step, the substrate is cleaned by applying at least one finishing method selected from the group consisting of sandblasting, chemical cleaning, electrolytic cleaning, grinding, polishing, vibratory tumbling and ion etching to produce a cleaned substrate. The cleaned substrate the subjected to a subsequent coating deposition process to apply the overlay low friction, anti-galling coating, which reduces the stickiness between the rotary tool surface and the counterpart. The low friction coating is selected from the group containing carbides, carbo-nitrides, borides, and carbo-borides with an excessive amount of amorphous carbon forming a DLC type matrix. It can also be a doped or un-doped DLC layer. The hydrogenated DLC can be used for further reduction of the friction and stickiness between the instrument and the counterpart.
Table 2 lists the preferred metals and alloys used to obtain the appropriate top segment nanostructured coating having low friction and anti-galling properties in conjunction with the bottom bondcoating segment.
The top layer can be also composed of cermet based material doped with lubricious metals such as silver, gold or a like. In this case the cermet provides a wear resistant tough anti-galling matrix with embedded lubricious metallic inclusions. One example of such coating is TiCN+Ag. Other examples include multiphase nanocrystalline carbides, carbo-nitrides, and borides with addition of silver and/or gold metallic inclusions. Alternatively, the lubricous metal coatings such as silver can be applied over the bondcoating layer as a replacement for DLC type top low friction segment, forming Me/MeN+Ag coating architecture. Another alternative solution for the low friction coating segment can be solid lubricant materials such as MoS2 and WS2. These solid lubricant compounds can be embedded into a hard coating matrix either in the bottom bondcoating or top coating segment. One example of such a nanocomposite self-lubricating coating is Ti/TiCN multilayer matrix with embedded WS2 inclusions. This coating can be prepared by hybrid LAFAD-UBM process. In this process the LAFAD will be equipped with two targets made of transition metals such as Ti, Cr, V or a like or their alloys. The magnetron targets will be WS2 or MoS2. The reaction gas atmosphere will be formed by nitrogen or mixture of nitrogen with methane or other HC gas, while argon will be supplied in the vicinity of magnetron targets as a sputtering gas. The resulting coating will consist of hard cermet matrix with embedded MoS2 or WS2 solid lubricant phases.
The preferred substrate surface temperature during the cathodic arc plasma deposition steps is between 100 and 500° C. In some cases the temperature of the substrates to be coated cannot exceed a certain value; otherwise it can have a detrimental effect on the bulk metal properties. For example, temperature must be controlled in coating of rotary instruments made of cold work hardening steel such as AISI 300 series or NiTi nickel-titanium alloy. In case of instruments made of AISI 300 series stainless steel the bulk metal properties cannot be restored by appropriate post-deposition heat treatment. In the case of dental instruments such as endofiles made of NiTi shape memory alloy the temperature must not exceed 100°-300° C. during the coating process, otherwise post-deposition thermal-mechanical treatments are necessary to restore the shape memory properties of the instrument. In some cases the properties of the NiTi may not be able to be restored at all if, for example, the instrument is exposed to too high of a temperature for too long a period of time. For NiTi type substrates with thin part diameters exposure to temperatures as high as 350° C. or five minutes can degrade the shape memory effect of the material. At 300° C. this loss can occur in 20 minutes, one hour at 250° C., or 2 hours at 200° C. Both the coating of the substrate material, and post deposition heat treatment are meant to maintain the stiffness or increase the stiffness properties of the substrate when used in many applications. It is also important to notice that some of the coating layers, specifically the free carbon contained top low friction segment coatings are extremely sensitive to high temperature treatment in both oxidizing and reducing environments. Therefore heat treatment of these coatings is as problematic as the bulk metal substrates. In all these cases precise thermal management of the substrate in the vacuum plasma coating deposition process is required.
In a deep vacuum, the only cooling mechanisms are radiation and conduction cooling. Using the pulsing mode of the LAFAD plasma source the precise thermal management of the tiny instruments such as endofiles can be achieved by periodically interrupting the exposure of the instrument substrate to the vapor plasma environment. This can be accomplished by using a magnetic shutter which effectively closes the path of the vapor metal plasma flow toward the substrates to be coated. When the magnetic shutter is closed (the deflection magnetic system OFF) only the near neutral metal vapor flow generated by the EBPVD source or magnetrons will be deposited on the metal instrument substrate, bringing a negligible amount of heat, while the substrate is losing the thermal energy by radiation cooling. This allows the temperature of the substrate to be controlled during the deposition of the cermet coating at a desirable level and not to exceed the temperature which damages the bulk metal properties.
The duration time and duty cycle of the filtered arc source operation effectively determine the substrate temperature in the vacuum plasma deposition process of the cermet coating, while the total coating time determines the coating thickness. The periodic interruption of substrate exposure to metal vapor plasma flow can also be achieved by periodic turning on and off the plasma sources. Since substrate temperature is a very important parameter in determining film properties, special attention is paid to in-situ monitoring of substrate temperature using a high-precision pyrometers and built-in thermocouples.
In addition, the substrate rotary tools such as endofiles are installed into blocks having a high thermal capacity for heat transfer, these blocks may be made of copper, aluminum, or similar alloy, then a heat sink paste is used to provide appropriate heat transfer during the coating deposition process as shown in
tp=(Ct×(Tm−T0))/q, (1)
where T0 is initial temperature of the instrument, which can be estimated as room temperature, Tm is maximum temperature to which the instrument can be heated during vapor plasma deposition treatment. More thorough calculations must be provided to take in to account the radiation and conduction cooling of the instruments during pause time in the cycled deposition process. In this case the expression (1) still gives a first rough estimate of the maximum plasma exposure time. The total coating deposition process time is limited by the heat capacity of the substrate holder blocks made of copper, aluminum or other metal with suitable high thermal conductivity and heat capacity. When the temperature of substrate holder block Tb>(2/3)Tm the coating deposition process must be interrupted until the temperature of the substrate holder block drops below this level.
Another way of trimming the substrate temperature below the value detrimental to bulk metal properties, is placing a substrate in a metallic or wire cage, which can effectively reduce the heat of the substrate due to intense ion bombardment as illustrated in
The technology described in this invention can be applied to wide variety of applications in forming and cutting tools, machine parts, medical and dental instruments and many others. In dental instruments applications it can be applied to both handle instruments such as regular and ultrasonic scalers, scalpels, needleholders and to rotating instruments such as root canal endofiles, dental drills and burs. The substrate dental instruments can be made of different type of steel and metal alloys. The preferable type of steel or metal alloy for different kind of dental instruments is shown in Table 3.
A set of endofiles made of 17-4 stainless steel were installed into the substrate holders positioned on the satellites of the rotating table of surface engineering system shown in
A set of endofiles made of NiTi nickel-titanium alloy were placed in the copper blocks and installed in the substrate holders, positioned on the satellites of the rotating table of surface engineering system shown in
The following process parameters were used for the deposition of DLC low friction carbon coating using two LAFAD plasma sources, one (for bondcoating layer) equipped with two Ti targets and another one equipped with two graphite targets. The ion cleaning step was performed in argon ionized in auxiliary arc discharge, created between primary cathodes of one LAFAD plasma source as an emitter of electrons and auxiliary anodes installed around the substrate table in a main vacuum chamber. The auxiliary anode current was 100 amperes, the argon pressure was 0.5 mtorr and bias voltage, created autopolarization of substrates under 13.56 MHz voltage provided by a RF generator, was 200 volts. The ion cleaning step lasts 2 min, which protects the substrates against overheating. After the ion cleaning step the deflecting magnetic field of LAFAD source with Ti targets was turned ON for deposition of the bond coating Ti/TiN/TiC layer. It was started from depositing of the 10 nm Ti layer followed by deposition of 30 to 50 nm of TiN layer in nitrogen and topped with 100 nm of TiC layer deposited in a methane reactive gas atmosphere. The gas pressure during deposition of the bondcoating is 0.5 mTorr, the auto-bias voltage is 50 volts.
After deposition of the bondcoating layer the LAFAD source with Ti targets was turned OFF and substrates were subjected to cooling step in helium or hydrogen at the pressure ranging from 1 to 10 mTorr. The duration of cooling step ranging from 10 min to 1 hr or more, depending upon thermal capacity of the substrates to be coated and substrate holder blocks. After the cooling step, the chamber was pumped down to 0.01 mTorr and other LAFAD source with graphite targets is turned ON. The 13.56 MHz RF bias power supply was connected to the substrate table instead of DC pulse bias power supply, used during deposition of cermet bond coating bottom segment. The substrate auto-bias during this stage was set at −50 volts. In addition the high voltage pulses having 2.5 kV amplitude, 25 μs width and 600 Hz repetition frequency were applied subsequent to the low auto-polarization bias voltage. During the DLC deposition step the LAFAD deflecting field was periodically turned off for 10 s and turned on for 5 s which results in the plasma deposition and heating of substrates with subsequent cooling. This approach is capable of precise thermal management of substrates in vapor plasma deposition processes. After 1 hr of DLC coating deposition step the LAFAD filter is turned off and substrates are discharged from the vacuum chamber. It is found that with approximately 1 μm of DLC coating the NiTi endofiles fully restored their shape memory, while torsional fatigue life was improved up to 200% due to reduction of friction and stickiness to the counterbody (bovine). Deposition of the top DLC layer having amorphous structure also results in substantial improvement of corrosion resistance by effectively filling the holes, voids and other imperfections and defects both on the substrate surface and in the bottom cermet layer, preventive it against pitting corrosion attacks.
A set of blank endofiles made of 17-4 stainless steel is cleaned by vibratory tumbling followed by ultrasonic cleaning dried and then loaded in the surface engineering system shown in
In this process the blank endofiles without flutes made of NITINOL or 50/50 at % NiTi alloy are subjected to deposition of a relatively thick TiCr/TiCrN/TiCrCN/TiCrC multilayer gradient cermet coating 2 μm thick at the first stage of the surface engineering process. During deposition of the bottom bond coating segment the temperature of the endofile substrates can reach up to 500° C., which effectively erases the shape memory properties. After this stage the coated blanks are removed from the LAFAD surface engineering chamber and subjected to annealing heat treatment stage. During this stage the coated blank files are subjected to 30 min heating at 1100° C. in nitrogen (99.995 purity) followed by rapid cooling by immersing the boat with files into ice. After annealing the coated blank files are subjected to thermal-mechanical treatment stage consisting of grinding by fine diamond wheels in a multi-step grinding-tempering process. Alternatively, after annealing and rapid quench the files can be subjected to tempering at temperatures ranging from 400 to 650° C. for time duration ranging from 15 min to 2 hrs. During this process the files are subjected in turn to grinding and tempering in a tempering furnace which allows restoring its shape memory properties. After this stage the files, which now have a flute are cleaned by mild vibratory tumbling and loaded second time in the LAFAD coating chamber for the subsequent deposition of hydrogen free DLC coating. This process is provided by LAFAD plasma source shown in
A novel coating is described that protects the coated surface against wear and corrosion while providing a low friction, anti-galling surface. In the exemplified embodiment, this novel coating architecture of a multilayer metal/ceramic bondcoat topped with a non-friction, anti-galling top coat is applied to rotary tools for dental and medical applications. It is important to note however that the subject coating can be effectively applied to other dental and surgical instruments including, but not limited to, saw blades, scalers, curettes, scissors, razorblades, scalpels, orthodontic components, burs, and implants. Additionally, the subject coating and the method of temperature control described for applying the coating are intended to be used for coating ultrasonic cutting, debriement, surgical, and periodontal therapy tools or instruments both of Piezo and Magneto Restrictive types for dental and medical applications. Finally the coatings and methods of the subject invention can be applied to other industries, such as the aerospace industry, the automotive industry (for use on, for example, gears, bearings, combustion engine components such as pistons and piston rings, valves etc.) and other cutting and forming tools industries (for example, for use on dies and molds).
It is understood that the foregoing examples are merely illustrative of the present invention. Certain modifications of the articles and/or methods may be made and still achieve the objectives of the invention. Such modifications are contemplated as within the scope of the claimed invention.
This application is a continuation of U.S. application Ser. No. 13/103,871, filed May 9, 2011 which is a divisional of U.S. application Ser. No. 11/804,433, filed May 17, 2007, now U.S. Pat. No. 7,939,172 B2, issued May 10, 2011, which claims the benefits of U.S. Provisional Application No. 60/801,142, filed May 17, 2006, the disclosures of which are hereby incorporated by reference in their entirety including all figures, tables and drawings.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4851095 | Scobey et al. | Jul 1989 | A |
| 4981756 | Rhandhawa | Jan 1991 | A |
| 5152774 | Schroeder | Oct 1992 | A |
| 5435900 | Gorokhovsky | Jul 1995 | A |
| 5707748 | Bergmann | Jan 1998 | A |
| 5724868 | Knudsen et al. | Mar 1998 | A |
| 5843244 | Pelton | Dec 1998 | A |
| 5940975 | Decker et al. | Aug 1999 | A |
| 5992268 | Decker et al. | Nov 1999 | A |
| 6074209 | Johnson | Jun 2000 | A |
| 6105261 | Ecer | Aug 2000 | A |
| 6547562 | Kumar | Apr 2003 | B2 |
| 6617057 | Gorokhovsky et al. | Sep 2003 | B2 |
| 6656186 | Meckel | Dec 2003 | B2 |
| 20020102400 | Gorokhovsky | Aug 2002 | A1 |
| 20040076857 | Sjolen | Apr 2004 | A1 |
| 20040168637 | Gorokhovsky | Sep 2004 | A1 |
| 20040197581 | Berglund | Oct 2004 | A1 |
| 20040219294 | Massler et al. | Nov 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 03078679 | Sep 2003 | WO |
| Entry |
|---|
| Thompson (International Endodontic Journal, 33 (2000) 297-310). |
| Weinert (Materials Science and Engineering A 378 (2004) 180-184). |
| Zabinski, J S et al., Recent developments in the design, deposition, and processing of hard coatings, Journal of Vacuum Science and Films, American Institute 1998, p. 1890-1900, vol. 16, No. 3. |
| Database WPI Week199841, Forming thin film diamond carbon implant ion surface base material irradiate form layer dissocate 1998, abstract, Derwent Publication Ltd, London, GB. |
| Kobayashi S et al., Diamond-like carbon coating on orthodontic archwires, Diamond and Related Material, 2005, pp. 1094-1097, vol. 14, No. 307 Elsevier Science Publishers. |
| Number | Date | Country | |
|---|---|---|---|
| 20160040280 A1 | Feb 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60801142 | May 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11804433 | May 2007 | US |
| Child | 13103871 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13103871 | May 2011 | US |
| Child | 14839698 | US |