3D INTEGRATION USING Al-Ge EUTECTIC BOND INTERCONNECT

Abstract

A method includes aligning a germanium feature on a first CMOS wafer with an aluminum feature on a second CMOS wafer. The aluminum feature and the germanium feature are pressed together. A eutectic bond is formed connecting the aluminum feature to the germanium feature. The eutectic bond has a melting point which is lower than the melting point of aluminum and the melting point of germanium.

Description

BACKGROUND

CMOS (“complementary metal-oxide semiconductor”) compatible wafer-wafer bonding is desirable for wafer-level-packaging. Its use has been demonstrated in a variety of different technologies, however solutions are limited by large bond size and high parasitic capacitance. For example, larger bonds such as microbumps occupy a large amount of space. As a result, the number of connections between wafers may be limited for direct wafer-wafer stacking. Therefore, a need remains for a robust wafer level integration that can allow for simultaneous wafer-level-packaging and high density electrical interconnects which optimize power, performance, and size of stacked solutions.

SUMMARY

Provided herein is method including aligning a germanium feature on a first CMOS wafer with an aluminum feature on a second CMOS wafer. The aluminum feature and the germanium feature are pressed together. A eutectic bond is formed connecting the aluminum feature to the germanium feature. The eutectic bond has a melting point which is lower than the melting point of aluminum and the melting point of germanium.

These and other features and aspects of the concepts described herein may be better understood with reference to the following drawings, description, and appended claims.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 shows two CMOS wafers aligned for bonding according to one aspect of the present embodiments.

FIG. 2 shows two CMOS wafers with contact between the germanium layer and the aluminum well according to one aspect of the present embodiments.

FIG. 3 shows two CMOS wafers with an Al-Ge eutectic bond according to one aspect of the present embodiments.

FIG. 4 shows two CMOS wafers with a number of interconnects according to one aspect of the present embodiments.

FIG. 5 shows two CMOS wafers bonded together with a shortened standoff according to one aspect of the present embodiments.

FIG. 6 shows two CMOS wafers bonded together with a standoff and surface pad according to one aspect of the present embodiments.

FIG. 7 shows two CMOS wafers bonded together with two opposing standoffs according to one aspect of the present embodiments.

FIG. 8 shows an exemplary flow diagram for forming a eutectic bond between two CMOS wafers according to one aspect of the present embodiments.

DESCRIPTION

Before various embodiments are described in greater detail, it should be understood by persons having ordinary skill in the art that the embodiments are not limiting, as elements in such embodiments may vary. It should likewise be understood that a particular embodiment described and/or illustrated herein has elements which may be readily separated from the particular embodiment and optionally combined with any of several other embodiments or substituted for elements in any of several other embodiments described herein.

It should also be understood by persons having ordinary skill in the art that the terminology used herein is for the purpose of describing the certain concepts, and the terminology is not intended to be limiting. Unless indicated otherwise, ordinal numbers (e.g., first, second, third, etc.) are used to distinguish or identify different elements or steps in a group of elements or steps, and do not supply a serial or numerical limitation on the elements or steps of the embodiments thereof. For example, “first,” “second,” and “third” elements or steps need not necessarily appear in that order, and the embodiments thereof need not necessarily be limited to three elements or steps. It should also be understood that, unless indicated otherwise, any labels such as “left,” “right,” “front,” “back,” “top,” “middle,” “bottom,” “forward,” “reverse,” “clockwise,” “counter clockwise,” “up,” “down,” or other similar terms such as “upper,” “lower,” “above,” “below,” “vertical,” “horizontal,” “proximal,” “distal,” and the like are used for convenience and are not intended to imply, for example, any particular fixed location, orientation, or direction. Instead, such labels are used to reflect, for example, relative location, orientation, or directions. It should also be understood that the singular forms of “a,” “an,” and “the” include plural references unless the context clearly dictates otherwise.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by persons of ordinary skill in the art to which the embodiments pertain.

CMOS wafers may be vertically stacked (e.g. 3D integration), a first wafer on top of a second wafer. The CMOS wafers may be electrically connected to each other using TSV (“Through Silicon Via”) or microbump connections. However, TSV and microbump connections are limited due to large size and high parasitic elements (e.g. resistance, capacitance, etc.). Therefore, provided herein are embodiments for 3D integration of CMOS wafer-wafer bonding using aluminum-germanium (“Al-Ge”) eutectic bond interconnects. The small size of the eutectic bonds, relative to TSV and microbump, enables a high density of interconnects between stacked CMOS with low parasitic capacitance. As a result, the Al-Ge eutectic bond interconnects enable optimization of power, performance, and size of the stacked CMOS.

Referring now to FIG. 1, two CMOS wafers aligned for bonding are shown according to one aspect of the present embodiments. A first CMOS wafer 102 includes a substrate 104 top layer, an inter layer dielectric (“ILD”) middle layer 106, and a passivation bottom layer 108. The first CMOS wafer 102 also includes an aluminum standoff 110, below the passivation bottom layer 108. The aluminum standoff 110 includes a germanium layer 112.

The functionality of the first CMOS wafer 102 is not limited. For example, various non-limiting embodiments may include advanced CMOS SOC (“system on chip”), analog (e.g. SERDES (“serializer/deserializer”)) chip, memory chip, FPGA (“field programmable gate array”), FPGA configuration memory, LUTs (“look up table”), etc.

The ILD middle layer 106 may contain one or more structures including, for example, metal connectors 114. In various embodiments, tungsten vias 116 connect the metal connectors 114 to each other and/or the aluminum standoff 110. It is understood that in various embodiments, the tungsten vias 116 may be any metal, alloy, or electrically conductive material. It is further understood that in various embodiments, the interconnects are not limited to aluminum and may include other metals (e.g. copper). Furthermore, embodiments of the present invention are not limited to including vias (e.g. tungsten vias 116).

The passivation bottom layer 108 may include one or more layers. For example, the passivation bottom layer 108 may include an SiO₂ layer and an SiN layer. In various embodiments, the SiO₂ layer is disposed between the ILD middle layer 106 and the SiN layer. It is understood that the SiO₂ layer and the SiN layer are merely exemplary, and the passivation bottom layer 108 may include other compounds, combinations, or number of layers.

A second CMOS wafer 120, includes a substrate bottom layer 122, an ILD middle layer 124, and a passivation top layer 126. The second CMOS wafer 120 also includes an aluminum well 128, within the passivation top layer 126. In the present embodiment, the aluminum well 128 is a depression within the passivation top layer 126, wherein the depression includes an aluminum portion (e.g. an aluminum surface) for electrically connecting to elements of the second CMOS wafer 120. In various embodiments the aluminum well 128 is created by opening the passivation top layer 126. The aluminum layer 128 includes an aluminum portion for electrically conducting to elements of the second CMOS wafer 120. As will be discussed later, the aluminum portion may also be replaced with germanium or coated with germanium.

The functionality of the second CMOS wafer 120 is not limited. For example, various non-limiting embodiments may include advanced CMOS SOC, analog (e.g. SERDES) chip, memory chip, FPGA, FPGA configuration memory, LUTs, etc.

The ILD middle layer 124 may contain one or more structures including, for example, metal connectors 128. In various embodiments, one or more tungsten vias 130 connect the metal connectors 128 to each other (not shown) and/or the aluminum well 128 (e.g. exposed aluminum surface). It is understood that in various embodiments, the tungsten vias 130 may be any metal, alloy, or electrically conductive material.

The passivation top layer 126 may include one or more layers. For example, the passivation top layer 126 may include an SiO₂ layer and an SiN layer. In various embodiments, the SiO₂ layer is disposed between the ILD middle layer 124 and the SiN layer.

Referring now to FIG. 2, the two CMOS wafers with contact between the germanium layer 112 and the aluminum well 128 (e.g. exposed aluminum surface) are shown according to one aspect of the present embodiments. The first CMOS wafer 102 has been aligned with the second CMOS wafer 120, such that the aluminum standoff 110 with the germanium layer 112 contacts the aluminum well 128. As a result, aluminum and germanium are now in contact and prepared for eutectic bonding.

In the present embodiment, the aluminum standoff 110 with the germanium layer 112 is a first feature including a height, and the aluminum well 128 is a second feature including a depth. As a result, in order for the first CMOS wafer 102 to be bonded with the second CMOS wafer 120, the present embodiment includes the first feature with a height (e.g. less than 500 Å) that is greater than or equal to the depth of the second feature. Further embodiments may include different features with different combinations of heights and depths. For example, both wafers may include aligned standoffs, as described below.

Although the first CMOS wafer 102 includes the aluminum standoff 110 with the germanium layer 112, and the second CMOS wafer 120 includes the aluminum well 128, various embodiments may include other combinations. For example, one embodiment may include a germanium standoff and an aluminum well. Another embodiment may include an aluminum standoff and an aluminum well with a germanium layer. A still further embodiment may include a germanium standoff, a germanium well, and an aluminum layer on either the germanium standoff or the germanium well.

Further embodiments may include a standoff instead of a well. For example, the first CMOS wafer may include an aluminum standoff with a germanium layer. The second CMOS wafer may include an aluminum standoff (instead of an aluminum well). In a further example, the first CMOS wafer may include a germanium standoff and the second CMOS wafer may include an aluminum standoff. In a still further example, the first CMOS wafer may include a germanium standoff, the second CMOS wafer may include a germanium standoff, and an aluminum layer may be disposed on either of the germanium standoffs.

Therefore, it is understood that the alignment and contact between the first CMOS wafer 102 and the second CMOS wafer 120 bring aluminum and germanium features of either structure into contact. Thus, the first CMOS wafer 102 and the second CMOS wafer 120 are prepared for eutectic bonding to each other. As will be described below with reference to later figures, the height of the aluminum standoff may be adjusted to control a standoff distance 132 between the first CMOS wafer 102 and the second CMOS wafer 120. For example, the standoff distance 132 may range from 0 to 2000 Å. However, it is understood that in various embodiments the standoff distance 132 is not limited, and my greatly exceed 2000 Å.

Referring now to FIG. 3, the two CMOS wafers with an Al-Ge eutectic bond 340 are shown according to one aspect of the present embodiments. During the bonding process, heat is applied in order to bring the temperature up to at least the eutectic melting point and form the Al-Ge eutectic bond. It is understood that the eutectic melting point is lower than the melting point of aluminum and lower than the melting point of germanium. In addition, pressure is applied to the first CMOS wafer 102 and the second CMOS wafer 120 in order to press aluminum and germanium features together. In the present embodiment, the aluminum standoff 110 with the germanium layer 112 is pressed to the aluminum well 128.

Sufficient pressure is applied to aid in the eutectic bonding process, however too much pressure may cause melted Al-Ge to spill out of the well 128 and onto the passivation top layer 126. Therefore, the pressure is controlled to maintain the Al-Ge eutectic bond 340 substantially to the contact points between the first CMOS wafer 102 and the second CMOS wafer 120. For example, in the present embodiment the Al-Ge eutectic bond 340 is confined to the aluminum well 128. In a further example, the width of the eutectic bond 340 is narrower than the width of a first feature (e.g. the aluminum standoff 110) and narrower than the width of a second feature (e.g. the aluminum well 128).

Various embodiments may use different methods for reaching the Al-Ge eutectic melting point. For example in some embodiments, the temperature may be raised in step fashion to below the eutectic melting point, the surfaces brought into contact, and then the temperature raised again. It is understood that above examples are merely for illustration and should not be limiting.

After melting, the Al-Ge eutectic bond 340 is formed between a first feature on the first CMOS wafer 102 and a second feature on the second CMOS wafer 120. As previously discussed, some non-limiting examples of first and second features may include: an aluminum standoff, a germanium standoff, an aluminum standoff with a germanium layer, a germanium standoff with an aluminum layer, an aluminum well, a germanium well, an aluminum well with a germanium layer, a germanium well with an aluminum layer, etc. As a result, the Al-Ge eutectic bond 340 may include any combination of aluminum and germanium features.

Further embodiments may also use elements other than aluminum and germanium. Any elements that form a eutectic bond may be used. For example, CMOS wafers may form eutectic bonds with gold features and silicon features. In a further examples, CMOS wafers may form eutectic bonds with copper features and tin features. In various examples, CMOS wafers may include a number of different eutectic combinations for forming different eutectic interconnects between two CMOS wafers. In some embodiments the eutectic bonding temperature is lower than the maximum temperature a CMOS circuit can withstand without being damaged during processing (e.g. <430C).

Referring now to FIG. 4, two CMOS wafers with a number of interconnects 441 are shown according to one aspect of the present embodiments. In the present embodiment, the interconnects 441 include standoffs 410, Al-Ge eutectic bonds 440, and wells 428. Various embodiments may include interconnects of various structures and forms that electrically interconnect to each other through Al-Ge eutectic bonds.

A first CMOS wafer 402 and a second CMOS wafer 420 have been bonded together with a number of the Al-Ge eutectic bonds 440. In addition a TSV 442 and a solderbump 444 are electrically connected through the second CMOS wafer 420 to the Al-Ge eutectic bonds 440.

It is understood that in various embodiments CMOS wafers may include mechanical imperfections. For example, CMOS wafers may not be flat and may include warpage, non-uniformity, and native oxides that need to be broken through. Therefore in various embodiments, enough force to overcome the mechanical imperfections of one or more CMOS wafers is applied.

For example, in the case of warpage, one or more standoffs 410 and wells 428 may contact one another before other standoffs 410 and wells 428, thereby preventing the other standoffs 410 and wells 428 from contacting. Therefore, additional pressure (e.g. force) is applied to the first CMOS wafer 402 and the second CMOS wafer 420 in order to bring all of the standoffs 410 and wells 428 into contact. However, the pressure is also controlled to mitigate overly spreading the Al-Ge eutectic bonds 440 (as previously discussed).

The TSV 442, the solder bump 444, and the interconnects 441 are figuratively illustrated. However, it is understood that the interconnects 441 are much smaller than the TSV 442 and the solderbump 444. As a result, the density of the interconnects 441 may be much greater than the possible density of TSVs or solderbump. As illustrated, a number of interconnects 441 may fit within the area of a single TSV or microbump. For example in one non-limiting embodiment, a TSV or microbump could range in the tens of microns (e.g. from 10 to 50 microns or more) while a eutectic interconnect could range from 1 to 2 microns or even sub-micron. Various embodiments may also include combinations of different interconnects. For example, CMOS wafers may include any combination interconnects (e.g. eutectic bonds, TSVs, microbumps, wire bonding, etc.).

The small size of the interconnects 441 and high density have many advantages. For example, parasitic capacitance of the interconnects 441 is greatly reduced from the TSVs or microbumps. In addition, the small size of the interconnects 441 enable new integration methods of stacking die (e.g. partitioning of interconnect and IP blocks between multiple die to optimize power, performance, and size of the stacked solution). In various embodiments, heterogeneous integration enables partitioning of interconnect and IP (“intellectual property”) blocks using cost optimized technologies. For example, a 14 nm microprocessor SOC may be bonded to 65 nm memory, 40 nm SERDES, or 28 nm SERDES. In further example, FPGA configuration memory blocks may be segregated from LUTs.

Referring now to FIG. 5, two CMOS wafers bonded together with a shortened standoff are shown according to one aspect of the present embodiments. In the present embodiment the height of a standoff 510 has been selected to reduce to zero a standoff height 532 between a first CMOS wafer 502 and a second CMOS wafer 520 after eutectic bonding. Therefore, after forming a eutectic bond 540, facing layers of the first CMOS wafer 502 and the second CMOS wafer 520 are in contact with each other. In the present embodiment a passivation bottom layer 508 of the first CMOS wafer 502 is in contact with a passivation top layer 526 of the second CMOS wafer 520. However, it is understood that other embodiments may include different layers of two CMOS wafers in contact with each other.

The height of the standoff 510 may be selected to achieve a predetermined standoff height 532 between the first CMOS wafer 502 and the second CMOS wafer 520. In one embodiment the height of the standoff 510 may be substantially increased (not shown) to create a much larger standoff height 532 between the first CMOS wafer 502 and the second CMOS wafer 520. In another embodiment, the height of the standoff 510 may be only slightly increased (not shown) to create a very small standoff height 532 between the first CMOS wafer 502 and the second CMOS wafer 520. Therefore, the height of the standoff 510 may be adjusted to achieve a desired standoff height 532.

Furthermore, the depth of the well 528 may be selected to achieve a predetermined standoff height 532 between the first CMOS wafer 502 and the second CMOS wafer 520. In one embodiment the depth of the well 528 may be substantially decreased (not shown) to create a much larger standoff height 532 between the first CMOS wafer 502 and the second CMOS wafer 520. In another embodiment, the depth of the well 528 may be only slightly decreased (not shown) to create a very small standoff height 532 between the first CMOS wafer 502 and the second CMOS wafer 520. Therefore, the depth of the well 528 may be adjusted to achieve a desired standoff height 532.

Referring now to FIG. 6, two CMOS wafers bonded together with a standoff and surface pad are shown according to one aspect of the present embodiments. A first CMOS wafer 602 includes a standoff 610. A second CMOS wafer 620 includes a pad 628 or a surface that is continuous (e.g. flat) with a surface of the second CMOS wafer 620. A eutectic bond 640 interconnects the first CMOS wafer 602 to the second CMOS wafer 620 through the standoff 610 and the pad 628. In the present embodiment, a standoff height 632 is determined by the length of the standoff 610, as previously discussed above with respect to variations in the height of the standoff.

Referring now to FIG. 7, two CMOS wafers bonded together with two opposing standoffs are shown according to one aspect of the present embodiments. A first CMOS wafer 702 includes a first standoff 710. A second CMOS wafer 720 includes a second standoff 728. A eutectic bond 740 interconnects the first CMOS wafer 702 to the second CMOS wafer 720 through the first standoff 710 and the second standoff 728. In the present embodiment, a standoff height 732 is determined by the length of the first standoff 710 and the length of the second standoff 728, as previously discussed above with respect to variations in the height of the standoff.

FIG. 8 shows an exemplary flow diagram for forming a eutectic bond between two CMOS wafers according to one aspect of the present embodiments. At block 802, a germanium feature on a first CMOS wafer is aligned with an aluminum feature on a second CMOS wafer. For example, in FIG. 1 the standoff of first CMOS wafer is aligned with the well of the second CMOS wafer. The standoff is aluminum with a germanium layer that faces an aluminum well within the passivation layer.

At block 804, the aluminum feature and the germanium feature are pressed together. For example, in FIG. 2 the first CMOS wafer has been pressed together with the second CMOS wafer, such that the aluminum standoff with the germanium layer contacts the aluminum well.

In some embodiments, the germanium feature is a germanium layer on an aluminum standoff. For example, in FIG. 1 the first CMOS wafer also includes an aluminum standoff, below the passivation bottom layer, and the aluminum standoff includes a germanium layer. In other embodiments, the germanium feature is a germanium standoff. For example, in FIG. 2, although the first CMOS wafer includes the aluminum standoff with the germanium layer, and the second CMOS wafer includes the aluminum well, various embodiments may include other combinations. Thus, one embodiment may include a germanium standoff and an aluminum well. Another embodiment may include an aluminum standoff and an aluminum well with a germanium layer. A still further embodiment may include a germanium standoff, a germanium well, and an aluminum layer on either the germanium standoff or the germanium well.

In some embodiments, the aluminum feature is a well within a passivation layer. For example, in FIG. 1 the second CMOS wafer also includes an aluminum well, within the passivation top layer. In some embodiments, the eutectic bond, while melted, is confined to the well. For example, in FIG. 3 sufficient pressure is applied to aid in the eutectic bonding process, however too much pressure may cause melted Al-Ge to spill out of the well and onto the passivation layer. Therefore, the pressure is controlled to maintain the Al-Ge eutectic bond substantially to the contact points between the first CMOS wafer and the second CMOS wafer, thereby confining the eutectic bond to the aluminum well.

At block 806, a eutectic bond is formed connecting the aluminum feature to the germanium feature, wherein the eutectic bond has a melting point which is lower than the melting point of aluminum and the melting point of germanium. For example, in FIG. 3 heat and pressure are applied in order to bring the temperature up to at least the eutectic melting point and form the Al-Ge bond.

In some embodiments, the aluminum feature and the germanium feature are heated to a point below the melting point of the eutectic bond, and after the pressing the aluminum feature and the germanium feature are heated to at least the melting point of the eutectic bond. For example, in FIG. 3 the temperature may be raised in step fashion to below the eutectic melting point, the surfaces brought into contact, and then the temperature raised again.

In some embodiments, a number of additional germanium features on the first CMOS wafer are aligned with a number of additional aluminum features on the second CMOS wafer, wherein, before the pressing, distances are inconsistent between a number of the additional aluminum features and a number of the additional germanium features, and wherein further, after the pressing, the number of additional aluminum features contact the number of additional germanium features. For example, in FIG. 4 the CMOS wafers are not always perfectly flat. As a result, one or more standoffs and wells may contact one another before other standoffs and wells, thereby preventing the other standoffs and wells from contacting. Therefore, additional pressure is applied to the first CMOS wafer and the second CMOS wafer in order to bring all of the standoffs and wells into contact and form the Al-Ge eutectic bonds.

While the embodiments have been described and/or illustrated by means of particular examples, and while these embodiments and/or examples have been described in considerable detail, it is not the intention of the Applicants to restrict or in any way limit the scope of the embodiments to such detail. Additional adaptations and/or modifications of the embodiments may readily appear to persons having ordinary skill in the art to which the embodiments pertain, and, in its broader aspects, the embodiments may encompass these adaptations and/or modifications. Accordingly, departures may be made from the foregoing embodiments and/or examples without departing from the scope of the concepts described herein. The implementations described above and other implementations are within the scope of the following claims.

Claims

1. A method comprising: aligning a germanium feature on a first CMOS wafer with an aluminum feature on a second CMOS wafer;pressing together the aluminum feature and the germanium feature;forming a eutectic bond connecting the aluminum feature to the germanium feature, wherein the eutectic bond has a melting point which is lower than the melting point of aluminum and the melting point of germanium.

2. The method of claim 1, further comprising: heating the aluminum feature and the germanium feature to a point below the melting point of the eutectic bond; andafter the pressing, heating the aluminum feature and the germanium feature to at least the melting point of the eutectic bond.

3. The method of claim 1, further comprising: aligning a plurality of additional germanium features on the first CMOS wafer with a plurality of additional aluminum features on the second CMOS wafer, wherein before the pressing, distances are inconsistent between a number of the plurality of additional aluminum features and a number of the plurality of additional germanium features, andafter the pressing, the plurality of additional aluminum features contact the plurality of additional germanium features.

4. The method of claim 1, wherein the germanium feature is a germanium standoff.

5. The method of claim 1, wherein the aluminum feature is a well within a passivation layer.

6. The method of claim 5, further comprising confining the eutectic bond, while melted, to the well.

7. A method comprising: aligning a germanium feature on a first CMOS wafer with an aluminum feature on a second CMOS wafer, wherein the second CMOS wafer includes a depression within a surface of the second CMOS wafer, andthe depression includes the aluminum feature;pressing together the aluminum feature and the germanium feature;forming a eutectic bond connecting the aluminum feature to the germanium feature, wherein the eutectic bond has a melting point which is lower than the melting point of aluminum and the melting point of germanium.

8. The method of claim 7, further comprising: heating the aluminum feature and the germanium feature to a point below the melting point of the eutectic bond; andafter the pressing, heating the aluminum feature and the germanium feature to at least the melting point of the eutectic bond.

9. The method of claim 7, further comprising: aligning a plurality of additional germanium features on the first CMOS wafer with a plurality of additional aluminum features on the second CMOS wafer, wherein before the pressing, distances are inconsistent between a number of the plurality of additional aluminum features and a number of the plurality of additional germanium features, andafter the pressing, the plurality of additional aluminum features contact the plurality of additional germanium features.

10. The method of claim 7, wherein the germanium feature is a germanium standoff.

11. The method of claim 7, wherein the aluminum feature is a well within a passivation layer.

12. The method of claim 11, further comprising confining the eutectic bond, while melted, to the well.

13. A method comprising: aligning a first feature on a first CMOS wafer with a second feature on a second CMOS wafer, wherein the first feature is a standoff with a height,the second feature is a depression with a depth, andthe height is greater than the depth;pressing together the first feature and the second feature;forming a eutectic bond connecting the first feature to the second feature, wherein the eutectic bond has a melting point which is lower than the melting point of the first feature and the melting point of the second feature.

14. The method of claim 13, further comprising: heating the first feature and the second feature to a point below the melting point of the eutectic bond; andafter the pressing, heating the first feature and the second feature to at least the melting point of the eutectic bond.

15. The method of claim 13, wherein the first feature is a germanium feature and the second feature is an aluminum feature.

16. The method of claim 15, further comprising: aligning a plurality of additional germanium features on the first CMOS wafer with a plurality of additional aluminum features on the second CMOS wafer, wherein before the pressing, distances are inconsistent between a number of the plurality of additional aluminum features and a number of the plurality of additional germanium features, andafter the pressing, the plurality of additional aluminum features contact the plurality of additional germanium features.

17. The method of claim 13, wherein the first feature is a germanium standoff.

18. The method of claim 13, wherein the second feature is a well within a passivation layer.

19. The method of claim 18, further comprising confining the eutectic bond, while melted, to the well.

20. The method of claim 13, wherein a width of the eutectic bond is narrower than a width of the first feature.