Patent Application
20180247811
This invention relates to an icosahedral boron-rich composition of matter and, more particularly, to a self-assembled picocrystalline oxysilaborane composition of matter. It further pertains to a method of making such composition.
As discussed by Becker et al., in a paper “Boron, The New Graphene?” in Vacuum Technology & Coating, April 2015, pp. 38-44, boron supports a unique and mysterious chemistry that has greatly perplexed scientists for many years in the pursuit of useful commercial applications that continue to defy a full chemical understanding. As further discussed in this article, there is an increasing belief by many scientists that new boron compounds could possibly exist in allotropes or polymorphs similar to, and superior to, the recently discovered carbon allotropes comprising fullerenes, carbon nanotubes, and graphene.
Boron is a light electron-deficient element with a small interatomic space between natural boron atoms supporting one shared molecular bonding orbital and two shared molecular antibonding orbitals amongst three boron atoms. As the result of this property, boron atoms tend to form three-center chemical bonds such that two valence electrons bond three boron atoms, with the peak electron density being in the center of the triangle comprised by three boron atoms. This type of chemical bond is very different from a two-center chemical bond in which the peak electron density exists along the rectilinear axis joining two valence electrons. Although boron is a Group-III element, it does not chemically act like other Group-III elements. Boron acts like a nonmetal and forms an extended series of hydrides.
Due to three-center bonds, boron tends to form polyhedral molecules comprising triangular faces. The highest-order symmetrical regular polyhedron formed by triangular faces is an icosahedron with twenty equilateral triangular faces that are interconnected by thirty edges so as to result in twelve vertices. Each vertex of a boron icosahedron is occupied by a boron atom with three valence electrons, such that conventional two-center chemical bonds cannot exist along the 30 icosahedral edges. In a boron icosahedron, the coordination number exceeds the number of boron valence electrons so as to result an electron deficiency. Similar to buckminsterfullerene C60, boron icosahedra can potentially form a cage-like molecule, but, boron icosahedra, because they are formed by only triangular faces, can display a higher symmetry than the truncated icosahedral buckminsterfullerene molecule formed by 20 hexagonal faces and 12 pentagonal faces.
In a key landmark paper, “The Electronic Structure of an Icosahedron of Boron,” Proceedings of the Royal Society, A230, 1955, p. 110, Longuet-Higgins and Roberts developed the molecular bonding conditions of a closed-shell boron icosahedron exhibiting an icosahedral symmetry A with a boron nucleus at each vertex. Longuet-Higgins and Roberts obtained the 48 molecular orbitals of a boron icosahedron by the linear combination of 48 nonorthogonal atomic orbitals that are related to 48 symmetry orbitals in terms of the irreducible representations of the regular icosahedral group Ih comprising the nondegenerate (Ag) irreducible representation along with threefold (T1u, T1g, T2u, T2g), fourfold (Gu, Gg), and fivefold (Hu, Hg) degenerate irreducible representations of a regular icosahedron.
As originally established by Jahn and Teller in “Stability of Polyatomic Molecules in Degenerate Electronic States. I. Orbital Degeneracy,” Proceedings of the Royal Society A, Vol. 161, 1937, pp. 220-235: Nonlinear nuclear configurations are not suitable for a stable orbitally-degenerate electronic state. It is quite significant that the orbital degeneracy considered by Jahn and Teller explicitly excluded a degeneracy due to spin. The bonding and antibonding orbitals of icosahedral boron manifestly involve nonlinear orbitally-degenerate electronic states. The Jahn-Teller effect results in a symmetry-breaking which lifts electronic orbital degeneracies by normal displacements of the 12 nuclei, known as Jahn-Teller-active modes, that distort polyatomic ions and molecules. The vibrational Jahn-Teller-active modes can be described in terms of the same irreducible representations as the electronic state, such that the vibrational state can be specified in terms of the irreducible representations of a regular icosahedron.
In the known boron-rich solids, the icosahedral symmetry is broken and the boron icosahedra are distorted by the Jahn-Teller effect. Most boron-rich solids in the prior art act as inverted molecular solids in which intericosahedral bonds are stronger than the intraicosahedral bonds. Icosahedral boron-rich solids are often referred to as inverted molecules. What is needed in the art is a genus of icosahedral boron-rich solids in which icosahedral symmetry is preserved. Such materials potentially offer electronic properties that are at least as important as those found in graphene, with the further capability of being compatible with monocrystalline silicon using standard manufacturing techniques. An excellent survey of boron-rich solids is given by Emin in “Unusual properties of icosahedral boron-rich solids,” Journal of Solid-State Chemistry, Vol. 179, 2006, pp. 2791-2798.
There potentially exists a novel form of boron capable of overcoming limitations of the recently discovered allotropes of carbon comprising the fullerenes, carbon nanotubes, and graphene. Although the study of graphene has advanced the general understanding of quantum electrodynamics in condensed matter physics, inherent limitations in its structure and, indeed, the structure of the allotropes of carbon, hinder practical applications. Chief among such limitations is an inability to combine these materials with monocrystalline silicon, on which the electronics industry has been built. Boron, which sits adjacent to carbon on the periodic chart, provides an alternative bridge between quantum electrodynamics and condensed matter physics, with an added benefit that, by carefully controlling its form, it can be integrated with silicon in a highly novel picocrystalline polymorph.
A novel class of boron-rich compositions that self-assemble from boron, silicon, hydrogen and, optionally, oxygen is disclosed. Self-assembly will occur with or without oxygen and the oxygen content can be varied as required. An impurity that alters electrical properties, hereinafter referred to as a “significant impurity” such as gold, for example, can optionally be included in minor amounts. The compositions can be formed by vapor deposition on a substrate. Monocrystalline silicon can be employed as the substrate. This novel class of self-assembled boron compounds exhibit unique electrical properties.
As used herein “self-assembly”, “self-assemble, or “self-assembled” is defined as the spontaneous and irreversible organization of molecular units into ordered structures by non-covalent interactions. One important property of the self-assembled boron compounds of the present invention is that under the specified reaction conditions the reactants spontaneously form into molecular nanostructures that build themselves. Further, the self-assembly of these novel boron compounds is not dependent on a specific substrate or deposition surface.
Thus, this invention pertains to a method for forming self-assembled hydrogen-containing compositions from boron, silicon and, optionally, oxygen. The preferred method of self-assembly is by vapor deposition at relatively low temperatures of reactant gases. The stability of the compositions can be enhanced by ensuring nearly anhydrous conditions during the process. Depending upon the desired characteristics of the compositions, trace amounts of a coinage metal such as gold can be included in the reactant gas mixture.
In accordance with the present invention, the compositions have the formula: (B12H4)xSiyOz, where the boron content is greater than about 50% by relative atomic concentration. These novel solid compositions of matter are hereinafter referred to as “oxysilaborane”. Some species of the compositions do not contain oxygen (z=0) and such species may sometimes be referred to as “silaborane.” The broadest compositional range of the novel materials disclosed here is represented by “(B12)xSiyOzHw”, with w, x, y, and z being numbers within the respective ranges of: 0≤w≤5, 2≤x≤4, 2≤y≤5 and 0≤z≤3. The preferred stoichiometric range for the compositions is (B12Hw)xSiyOz with 3≤w≤5, 2≤x≤3, 2≤y≤5 and 0≤z≤3. Boron is preferably present in from about 63% to about 89% by relative atomic concentration. Particularly preferred compositions are where w=4, x=3, y=5, z=0 and w=4, x=2, y=4, z=2. These compositions can also include trace amounts of significant impurities that do not affect the atomic ratios set forth above. A preferred significant impurity would be a coinage metal such as gold. The oxygen content of the compositions can be varied so as to form regions of higher or lower oxygen content in the oxysilaborane by, for example, controlling the rate of delivery of oxygen containing gases to the reaction site. In like fashion, should it be desirable to employ gold or another significant impurity in trace amounts to alter electrical properties, a metal containing compound can be introduced to the reaction site for deposition along with the self-assembled oxysilaborane. Such trace additions of a significant impurity do not affect the basic stoichiometry of the compositions.
These materials are also unique in that they contain picocrystalline quantum dots that form artificial atoms. The picocrystalline quantum dots (in the form of boron icosahedra with a nearly-symmetrical nuclear configuration) can replace corner silicon atoms in a structure that demonstrates both short-range and long-range order as determined by x-ray diffraction of actual samples. The picocrystalline oxysilaboranes tend to form a borane solid with a continuous network similar to that of monocrystalline silicon, albeit a continuous random network in which certain silicon atoms are orderly replaced by picocrystalline artificial atoms comprising boron icosahedra with a nearly-symmetrical nuclear configuration. Thus, by carefully controlling the reactants and reaction conditions as described below, this new class of materials self assembles boron-based artificial atoms so as to attain a short-range order of nearly-spherical quantum dots and further self assembles those structures (with their quantized energy levels) into materials with a long-range bond-orientational order. This long-range bond-orientational order is physically compatible with monocrystalline silicon, thereby allowing an engineered introduction of the boron picocrystalline quantum dots (artificial atoms) into semiconductor structures by using standard techniques. By varying the oxygen content and the presence or absence of a significant impurity such as gold, unique electrical devices can be constructed that improve upon and are compatible with current semiconductor technology.
Preferred embodiments of the invention are illustrated in the accompanying drawings in which:
A new type of solid composition of matter derived from the heating of boron and silicon hydrides in the presence of hydrogen and, optionally, an oxidizing chemical agent is disclosed. The compositional range of preferred materials, hereinafter referred to as “picocrystalline oxysilaboranes” and represented by the formula “(B12H4)xSiyOz”, comprises (B12H4)4Si4 at one extreme and (B122−H4)2Si4O22+ at the opposite extreme, with x, y, and z being numbers in the preferred respective ranges of: 2≤x≤4, 3≤y≤5 and 0≤z≤2. Picocrystalline oxysilaborane (B12H4)xSiyOz is itself contained in a broader compositional range of novel materials, also discussed here for the first time and hereinafter referred to as “oxysilaboranes” and represented by “(B12)xSiyOzHw”, with w, x, y, and z being numbers in the respective ranges: 0≤w≤5, 2≤x≤4, 2≤y≤5 and 0≤z≤3. When no oxygen is present (z=0), the materials are referred to as simply “silaboranes” as they are formed from hydrogen, boron and silicon.
The picocrystalline oxysilaboranes of this invention are nearly transparent solids believed to be constituted by a continuous random network of polymorphic unit cells that satisfy a modification of rules established by Zachariasen, “The Atomic Arrangement in Glass,” Journal of the American Chemical Society, Vol. 54, 1932, pp. 3841-3851. Zachariasen focused upon oxide glasses and, more specifically, on amorphous SiO2 and amorphous B2O3. Zachariasen established that amorphous SiO2 is formed by a continuous random network of SiO4 tetrahedra. Similarly, the picocrystalline oxysilaboranes are believed to be constituted by a continuous random network of polyhedra with a nearly-symmetrical boron icosahedron at each of the polyhedral corners.
In order to illustrate the fact that the novel oxysilaborane compositions are neither amorphous nor monocrystalline, but instead exhibit a novel combination of short-range and long-range order, reference is made to data collected from actual samples of the materials.
To better illustrate the short-range order of the picocrystalline borane solid 402, the HRTEM diffraction intensity of the monocrystalline silicon substrate 401 is graphed in
The broadened circular ring in the FFT image of the picocrystalline borane solid 402 in
There are two broadened diffraction peaks located near 2θ=13.83° and 2θ=34.16° in
The picocrystalline borane solid appears to be an amorphous film in
However, the analysis further establishes that a picocrystalline borane solid is not polycrystalline. A polycrystalline film is comprised of a large number of crystalline grains that are randomly ordered, such that all sets of regular interplanar lattice spacings are brought into a Bragg condition in a GIXRD scan by virtue of the random ordering of the polycrystalline grains. The lack of any sharp peak in
Preferred embodiments of this present invention involve a type of order not known in the prior art. Long-range periodic translational order is defined herein as a regular repetition of a certain invariant arrangement of atoms, known as a unit cell, over space so as to thereby form a translationally-invariant tiling in a regular array of atoms well beyond first- and second-nearest neighbor atoms. Monocrystalline and polycrystalline materials possess a long-range periodic translational order throughout space. The periodic repetition of atomic positions is maintained throughout the entire space of a monocrystalline material. In a polycrystalline material, a periodic repetition of atomic positions is maintained over the limited, finite space in grains, which can themselves be arbitrarily oriented over the entire space of a polycrystalline material. As used herein, a nanocrystalline material is a special polycrystalline material wherein the grain sizes range between 300 nm and 300 pm.
Short-range periodic translational order is defined herein as a repetition of atomic positions over a space substantially confined to only first- and second-nearest neighbor atoms. The radii of isolated neutral atoms range between 30 and 300 pm. As the result, and as used herein, a picocrystalline material is a material exhibiting a short-range periodic translational order limited to repeating atomic positions in finite groups of first- and second-nearest neighbor natural atoms. An amorphous material, as used herein, is a material void of regularly repeating arrangements of atoms, so as to be incapable of supporting a constructive interference of x-rays.
It might seem that these definitions of various types of crystalline materials fully describe the allowable order of repeating atomic positions in space. But, these definitions remain limited in the sense that they are based strictly upon repeating positions of individual atoms over space. They cannot be applied to materials that include tightly packed clusters of atoms arranged in space such that the clusters may themselves be bonded to single atoms that are not so clustered. These definitions must be extended in order to comprehend a quantum dot, which is defined, for purposes herein, as a cluster of atoms in which a discrete quantization of energy levels occurs. The size of a typical quantum dot in the prior art is on the order of 10 nm. The above noted definitions of the various types of solid crystalline materials are also independent of any energy quantization. This leads to the requirement for a new definition that comprehends both the spatial arrangement of atoms and also the presence of a discrete quantization of energy levels. Therefore, as used herein, a “picocrystalline artificial atom” is a cluster, of a size less than 300 pm, of natural atoms that are mutually bonded together so as to support a short-range periodic translational order and an internal discrete quantization of energy levels. As further described below, special types of picocrystalline artificial atoms can also be bonded to other natural atoms in order to form an extended lattice of natural atoms and picocrystalline artificial atoms. As used herein, a natural atom is any isotope of a stable chemical element contained in the periodic chart.
A particular type of picocrystalline artificial atom utilized in embodiments of this invention is a boron icosahedron with a nearly-symmetrical nuclear configuration which escapes Jahn-Teller distortion. The boron icosahedra in most all known boron-rich solids exhibit a broken icosahedral symmetry due to Jahn-Teller distortion, such that the first and second-nearest neighbor boron atoms do not exist in repeating spatial positions that are capable of supporting a short-range periodic translational order. Most boron icosahedra in the prior art are bonded by the molecular orbitals obtained by Longuet-Higgins and Roberts in the paper entitled “The Electronic Structure of an Icosahedron of Boron,” Proceedings of the Royal Society A, Vol. 230, 1955, p. 110.
In their molecular orbital analysis, Longuet-Higgins and Roberts never resolved the atomic orbitals of the three-center boron bond in terms of the icosahedral symmetry operations. In connection with the invention described here, a molecular orbital analysis that describes the three-center boron bonds by a generalization of the methodology of Longuet-Higgins and Roberts was performed. That generalized molecular orbital analysis describes a boron icosahedron comprising 12 boron nuclei 102, with a nearly-symmetrical nuclear configuration, that can be formed by 24 delocalized atomic orbitals so as to result in a nearly-symmetrical spheroid with all displacement ideally restricted to only periodic vibrations along the four k(111) wave vectors shown in
The self-assembly of the picocrystalline oxysilaboranes involves the self-selective replacement of silicon atoms in a monocrystalline silicon lattice by boron icosahedra with a nearly-symmetrical nuclear configuration in the form of picocrystalline artificial borane atoms 101. To further illustrate the order present in picocrystalline oxysilaboranes, the characteristic order of the unit cell of monocrystalline silicon, prior to such self-selective replacement of silicon atoms, will be explained. The monocrystalline silicon unit cell 200 in 111
cubic body diagonal in a tetrahedral arrangement. The monocrystalline silicon unit cell 200 is periodically translated over space so as to form a monocrystalline silicon lattice in which the silicon vertex atoms 201 and the silicon face-center atoms 202 are covalently bonded to, and only to, silicon basis atoms 203 along a
111
crystalline orientation. The resultant monocrystalline silicon lattice has a long-range periodic translational order in terms of cubic unit cells of ˜543 pm along each edge, without any
100
chemical bonds.
Per the normal crystallographic convention, a crystal orientation along, or parallel to, any cubic edge is generally represented by 100
. Any particular
100
orientation, e.g. the [010] orientation along the positive y-axis, will be specifically denoted. A cubic face, or a plane parallel to any cubic face, is generally represented by {100}. A particular {100} plane, e.g. the xz-plane normal to the [010] direction, is represented by (010). A particular
100
orientation, e.g. the [010] orientation, is always normal to the corresponding {100} plane, viz. the (010) plane in this case. By further convention, any orientation along, or parallel to, a cubic body diagonal is represented by
111
. There are two classes of icosahedral faces: 8 icosahedral faces are constituted by {111} planes normal to a
111
cubic body diagonal and 12 icosahedral faces are constituted by planes intersecting in pairs along a
100
orientation. The generalized molecular orbital analysis predicts that the atomic orbitals of three-center boron bonds exist along edges of the {111} planes.
The above-described picocrystalline artificial borane atoms 101 can now be utilized to address an existing limitation in semiconductor fabrication. The invariance of the dimensions of the monocrystalline silicon unit cell 200 is maintained in the presence of extensive valence electron eigenstate changes by a spatial displacement of the silicon basis atoms 203 along a 111
crystal orientation. It is quite significant that the silicon vertex atoms 201 and silicon face-center atoms 202 are ideally motionless while the silicon basis atoms 203 can be displaced along a
111
cubic body diagonal. A change in eigenstate of a valence electron eigenfunction involves a change in spatial extension of the electron eigenfunction. The diamond lattice of monocrystalline silicon supports extensive changes in valence electron eigenstates, without mechanical work, due to an invariant lattice constant of the constituent unit cells. The basis atoms 203 support a long-range
111
bond-orientational order that complements the long-range periodic translational order.
The practical means to exploit the ability of a solid monocrystalline silicon lattice to support extensive changes in eigenstate in the absence of any mechanical work is fundamentally limited by its very structure. First, monocrystalline silicon can only be epitaxially deposited over monocrystalline silicon substrates. Secondly, the termination of a monocrystalline silicon lattice, in order to electrically contact it, results in Tamm-Shockley states which pin the electrochemical potential within the forbidden energy region between the bottom of the conduction band and top of the valence band. This pinning of the electrochemical potential results in a rectifying contact independent of the metal work function of electrodes. See Bardeen, by way of example, “Surface States at a Metal Semi-Conductor Contact,” Phys. Rev. 10, No. 11, 1947, p. 471. Thus, it is desirable for the Tamm-Shockley interface state density to be substantially reduced.
By well-established processing techniques, a substantial reduction in the Tamm-Shockley interface state density can be achieved by terminating crystalline silicon regions with an amorphous silicon dioxide film such that the surface electrochemical potential can be modulated, in device operation, throughout the forbidden energy region. A field-effect transistor exploits the ability to modulate the electrical conductivity of a monocrystalline silicon surface by capacitively-coupled electrodes via an intervening silicon dioxide thin-film. However, the silicon dioxide must be removed from semiconductor contact regions due to the high resistivity of silicon dioxide ˜1016 Ω-cm. In order to reduce the Tamm-Shockley interface states in the semiconductor contact zones, the semiconductor surface is degenerately doped, such that the electrochemical potential can be selectively pinned in either the conduction energy band or the valence energy band.
A metal or a silicide can be alloyed to the degenerate semiconductor surface, such that mobile charges can tunnel through the potential barrier into the isotype homojunction. Under low-level injection, the isotype homojunction behaves as an ohmic contact to any high-resistivity semiconductor region. However, this widely-used type of ohmic contact prevents the employment of a monocrystalline semiconductor in an electrochemical rectifier wherein the electrochemical potential can vary between the external electrodes. So, as only one example of the many useful properties of novel materials described herein, this deficiency is remedied by the incorporation of picocrystalline artificial borane atoms 101, shown in
A diamond-like picocrystalline silaborane unit cell 300 is constructed by replacing each silicon vertex atom 201 within the monocrystalline silicon unit cell 200 with a picocrystalline artificial borane atom 101, as shown in 111
wave vectors of the four
111
threefold axes.
Whereas an oxide glass is constituted by a continuous random network of oxygen tetrahedra or oxygen triangles, the picocrystalline oxysilaboranes constitute a solid formed by a continuous random network of borane hexahedra, which, by definition, form a hexahedron with a picocrystalline artificial borane atom 101 at each hexahedral corner. Whereas the monocrystalline silicon unit cell 200 in
Whereas Zachariasen represented the atomic arrangement of any oxide glass by means of a continuous random network of polymorphic oxygen tetrahedra or polymorphic oxygen triangles, the atomic arrangement of a borane solid will now be established in terms of a continuous random network of irregular polymorphic borane hexahedra 300. The eight corners of the borane hexahedron 300 shown in
Each tetravalent natural atom 303 bonds to one or more face-center atom 302 in the borane hexahedron 300 shown in 111
crystalline orientation.
Unlike an oxide glass, the picocrystalline oxysilaboranes form a borane solid by a continuous random network of borane hexahedra 300 in which the hexahedral edges and faces are shared, in addition to the eight corners. Whereas the borane hexahedron 300 is represented as a cube in
For a regular boron icosahedron with an ideal edge of 1.77 Å, the interplanar lattice spacing of the ten sets of parallel triangular faces in each picocrystalline artificial borane atom 101 is d=2.69 Å. This intraicosahedral plane spacing corresponds to a diffraction angle of 2θ=33.27° for 1.54 Å x-rays (which is x-ray wavelength used in all the XRD scans in the figures herein). This diffraction angle is contained within the broadened, low-intensity diffraction peak near 2θ=34.16° in the ω-2θ XRD scan shown in
There is a geometric distortion due to the mixture of boron isotopes 510B and 511B in boron icosahedra comprising the picocrystalline oxysilaboranes, which causes a broadening of the Bragg peaks associated with the intraicosahedral constructive x-ray diffraction patterns due to the ten sets of nearly-parallel plane faces of the constituent boron icosahedra. However, it is believed that this distortion is similarly preserved in most of the boron icosahedra, such that Bragg peaks are associated with intericosahedral constructive x-ray diffraction patterns between parallel planes of the picocrystalline artificial borane atoms 101 at the corners of the irregular borane hexahedra 300 forming a continuous random polyhedral network. The distance between the body centers of the corner picocrystalline artificial borane atoms 101 varies randomly, such that sharp Bragg peaks exist between corresponding parallel icosahedral faces of different picocrystalline artificial borane atoms 101 for each x-ray angle of incidence over a broad diffraction angle range near 2θ=13.83°.
A nanocrystalline solid, as used herein, is taken to be a polycrystalline solid with small grains, with grain sizes being less than 300 nm. As the grain size is reduced, then the periodic translational order is of a shorter range and the x-ray diffraction peaks are broadened. Whereas a typical nanocrystalline material is void of any long-range order, the picocrystalline oxysilaboranes of this invention possess a short-range periodic translational order along with a long-range bond-orientational order that is believed to be due to the self-alignment of the picocrystalline artificial borane atoms 101. By a definition herein, a picocrystalline borane solid is a solid, comprised of at least boron and hydrogen, that possesses a long-range bond-orientational order due to sharp x-ray diffraction peaks when subjected to grazing-incidence x-ray diffraction (GIXRD).
In order to understand the long-range bond-orientational order which characterizes the picocrystalline oxysilaboranes, it is purposeful to focus on the picocrystalline artificial borane atoms 101. The ten pairs of nearly-parallel faces of a picocrystalline artificial borane atom 101 are ideally separated by d=269 pm, which supports a broad intraicosahedral x-ray diffraction peak at 2θ=33.27°. As discussed, the intraicosahedral x-ray diffraction peaks in a picocrystalline artificial borane atom 101 are broadened by a mixture of the boron isotopes 510B and 511B. It is purposeful to more precisely define as to what is meant by “broad” and “sharp” x-ray diffraction peaks.
Any sharp x-ray diffraction peak is characterized by a peak width at half intensity that is at least five times smaller than the peak height. Conversely, a broad x-ray diffraction peak is characterized by a peak width, at half intensity, which is greater than half the peak height. The very broad x-ray diffraction peak near 2θ=52.07° in
The fivefold symmetry of a regular icosahedron is incompatible with the fourfold symmetry of a regular hexahedron (cube), such that it is impossible to periodically translate any regular hexahedral unit cell, with picocrystalline artificial borane atoms 101 at the vertices, over space in a translationally invariant manner. Symmetry breaking must occur in the irregular borane hexahedra 300 shown in
It is believed that the fivefold rotational symmetry of the picocrystalline artificial borane atoms 101 (
The above-described structure can be more fully understood by considering in more detail the believed structure of one extreme, (B12H4)4Si4, of the picocrystalline oxysilaboranes. In (B12H4)4Si4, each irregular borane hexahedron 300 forming a solid lattice is ideally constituted by: 8 corner picocrystalline artificial borane atoms 101, 6 face-center picocrystalline artificial borane atoms 101, and 4 natural silicon atoms 303. Due to the sharing of 8 hexahedral corners and the sharing of 2 hexahedral faces, a translation of the irregular borane hexahedra 300 over space ideally results in (B12H4)4Si4. In this manner, (B12H4)4Si4 forms a picocrystalline polymorph, very similar to monocrystalline silicon, that is comprised of tetravalent natural silicon atoms 303 and tetravalent picocrystalline artificial borane atoms 101.
As shown in 111
wave vector. In this manner, a picocrystalline artificial borane atom 101 is highly novel since it comprises a boron icosahedron in which all of the 36 of the boron valence electrons occupy intraicosahedral molecular orbitals, such that all intericosahedral chemical bonds are ideally by means of hydrogen valence electrons.
A caged boron icosahedron, with a nearly-symmetrical nuclear configuration and void of any exo-icosahedral bonds due to radial boron orbitals, is not known to exist in the prior art. In a real sense, the artificial nucleus of a picocrystalline artificial borane atom 101 constitutes a caged icosahedral molecule with a higher degree of symmetry than that of the caged truncated icosahedral molecule of buckminsterfullerene. The molecular truncation of buckminsterfullerene eliminates the symmetry operations associated with the fivefold rotation about the 12 icosahedral vertices. The restoration of the fivefold icosahedral rotation in a picocrystalline artificial borane atom 101 results in a greater bond delocalization and, thus also, a greater aromaticity than that of buckminsterfullerene. This is believed to be due to spin-orbit coupling.
As discussed hereinabove, the artificial nucleus of a picocrystalline artificial borane atom 101 constitutes a boron icosahedron with a nearly-symmetrical nuclear configuration which escapes Jahn-Teller distortion. It is believed that polyatomic electronic orbital degeneracies of the boron icosahedron of a picocrystalline artificial borane atom 101 are lifted by spin-orbit coupling, which was not contemplated by Jahn and Teller in their paper “Stability of Polyatomic Molecules in Degenerate Electronic States. I. Orbital Degeneracy,” Proceedings of the Royal Society A, Vol. 161, 1937, pp. 220-235. The lifting of the polyatomic electronic orbital degeneracies by spin-orbit coupling causes a discrete energy quantization in the artificial nucleus of a picocrystalline artificial borane atom 101 that is subject, in whole or in part, to Dirac's relativistic wave equation.
A discrete energy quantization, subject to Dirac's relativistic wave equation, tends to support a charge-conjugation symmetry between electrons and holes characteristic of graphene and other such low-dimensional materials. It is believed that such a charge-conjugation symmetry is supported in picocrystalline (B12H4)4Si4 if the electron-hole pair generation rate is increased by a trace incorporation of a coinage metal, such as natural gold. In the absence of trace impurities, the charge-conjugation symmetry in the artificial nucleus of picocrystalline (B12H4)4Si4 is broken such that it behaves as an electron-deficient B12H4 molecule.
It is believed that B12H4 molecules tend to attain a greater stability by means of a disproportionation in which the molecules are simultaneously ionized into pairs of B122−H4 dianions and B122+H4 dications. In one sense, the disproportionation in picocrystalline (B12H4)4Si4 is similar to the disproportionation of boron carbide B13C2 into anion and cation pairs. In yet another sense, there exists a fundamental difference between the disproportionation of picocrystalline (B12H4)4Si4 and that of carbide B13C2. As is well known in the literature, the icosahedral symmetry in boron carbide is broken by Jahn-Teller distortions. Picocrystalline (B12H4)4Si4 escapes said icosahedral symmetry breaking due to a lifting of the polyatomic electronic orbital degeneracies by spin-orbit coupling. This endows picocrystalline (B12H)4Si4 unique chemical properties.
At issue are spectroscopic principles of chemistry. Spectroscopic principles can be described by reference to the book by Harris and Bertolucci, Symmetry and Spectroscopy, Oxford Univ. Press, 1978. On pages 1-2, Harris and Bertolucci emphasize an important concept: “Light of infrared frequencies can generally promote molecules from one vibrational energy level into another. Hence, we call infrared spectroscopy vibrational spectroscopy. Visible and ultraviolet light are much more energetic and can promote the redistribution of electrons in a molecule such that the electronic potential energy of the molecule is changed. Hence, we call visible and ultraviolet spectroscopy electronic spectroscopy.” This does not account for spin-orbit coupling.
In the presence of a spin-orbit coupling the rotational, vibrational, and electronic degrees of freedom can be intertwined in rovibronic energy levels which support a redistribution of electrons in response to microwave radiation. This phenomenon impacts disproportionation in picocrystalline (B12H4)4Si4 due to the belief that the B122+H4 dianions and B122+H4 dications exist in different energy levels separated by an energy difference on the order of 45 micro-electron-volts. In boron carbide B13C2, disproportionation results in anions and cations at the same energy level due to the absence of a spin-orbit coupling. It is for this reason that the preferred compositions of this invention do not contain significant amounts of carbon. Although picocrystalline (B12H4)4Si4 ideally supports the maximum disproportionation in picocrystalline oxysilaborane (B12H4)xSiyOz over the preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2), the actual composition with the maximum observed disproportionation appears, based on actual data, to be picocrystalline silaborane (B12H4)3Si5.
At the other extreme of the picocrystalline genus (B12—H4)xSiyOz is a picocrystalline species (B122−H4)4Si4O22+ in which there is ideally no disproportionation. In this particular species, natural oxygen atoms are ionized so as to ideally stabilize the artificial nucleus of a picocrystalline artificial borane atom 101 without resort to disproportionation. The chemical nature of the species (B12H4)3Si5 and (B122−H4)4Si4O22+ of the genus (B12H4)xSiyOz, over a preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2), can be described in terms of the concept of electronegativity introduced by Linus Pauling in The Nature of the Chemical Bond, Cornell University Press, Third Edition, 1960, pp. 64-108. Pauling established electronegativity as the measure of the ionicity of any covalent chemical bond. Pauling's concept of electronegativity assumed two-center covalent bonds, which can be carried over to the picocrystalline oxysilaboranes of this invention.
In picocrystalline oxysilaboranes of this invention, picocrystalline artificial borane atoms 101 are covalently bonded to natural atoms or to other picocrystalline artificial borane atoms 101. At one genus extreme, picocrystalline silaborane (B12H4)3Si5 exhibits a tendency to capture a pair of electrons and, thus, is said to possess a high electronegativity. At the other genus extreme, picocrystalline oxysilaborane (B122−H4)4Si4O22+ is said to possess a low electronegativity due to an electronic closed-shell configuration. One utility of picocrystalline oxysilaborane (B12H4)xSiyOz is the ability to vary the electronegativity of various species over the preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2) by chemically varying the electronegativity of picocrystalline artificial borane atoms 101. At one compositional extreme, the relatively high electronegativity of picocrystalline silaborane (B12H4)3Si5 promotes a disproportionation in the absence of an external source of electrons while, at the other compositional extreme, the relatively low electronegativity of picocrystalline oxysilaborane (B122−H4)4Si4O22+ impedes any disproportionation.
The ability to chemically modulate the electronegativity of picocrystalline artificial borane atoms 101 over a compositional range supports a novel and useful thermochemistry that is not known in the prior art. The chemical modulation of the electronegativity in artificial atoms is made possible by a discrete energy quantization in picocrystalline artificial borane atoms 101 due to spin-orbit coupling. It is by means of spin-orbit coupling that an electron redistribution occurs between microwave energy levels. The intraicosahedral three-center bonds of the artificial nuclei of the picocrystalline artificial borane atoms 101 are much stronger than the intericosahedral two-center covalent bonds of picocrystalline artificial borane atoms 101 to natural atoms or to other picocrystalline artificial borane atoms 101. This is made possible by spin-orbit coupling.
The peak electron density of the three-center bonds of the picocrystalline artificial borane atoms 101 ideally resides in the center of the 8 icosahedral faces normal to the k111
wave vectors shown in
The naturally-occurring ratio of boron 511B to boron 510B is approximately 4.03. The isotopic enrichment boron 510B relative to boron 511B further shifts the three-center bonds away from the geometric center of the icosahedral faces of the artificial nucleus of a picocrystalline artificial borane atom 101 and, therefore, increases the entropy of the picocrystalline artificial borane atom 101. Such an increase in entropy results in a decrease in Gibbs free energy. The increase in entropy associated with an isotopic enrichment results in a greater decrease in Gibbs free energy than the corresponding decrease in enthalpy, such that an entropic redistribution of electrons is believed to occur between microwave energy levels when spin-orbit coupling maintains nearly-symmetrical boron icosahedra in the picocrystalline oxysilaboranes (B12H4)xSiyOz of this invention.
By replacing natural atoms with picocrystalline artificial borane atoms 101, atomic engineering can be established in the picocrystalline oxysilaboranes (B12H4)xSiyOz over a preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2). Atomic engineering can be supported by a chemical modification of picocrystalline artificial borane atoms 101 that act as variable atomic elements in novel boron-rich molecules supporting a picotechnology not known in the prior art. Preferred types of picocrystalline oxysilaboranes will be described by actual examples. By means of these examples, the novelty and utility of the picocrystalline oxysilaboranes (B12H4)SiyOz over a preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2) can be better understood.
A method for making the oxysilaborane films of the present invention is a chemical vapor deposition causing the precipitation of a solid film by passing gas vapors containing boron, hydrogen, silicon, and oxygen over a heated substrate in a sealed chamber maintained at a pressure below that of the atmosphere. The preferred vapors are nitrous oxide N2O and the lower-order hydrides of boron and silicon, with diborane B12H6 and monosilane SiH4 being the most preferred. Both hydrides can be diluted in a hydrogen carrier gas. By passing hydrogen-diluted diborane and monosilane, and optionally nitrous oxide, over a sample heated above ˜200° C. at a pressure of ˜1-30 torr, a solid oxysilaborane film self-assembles over the substrate under preferred conditions.
The heating can be realized with equipment generally known to those skilled in the art of semiconductor processing. A molybdenum susceptor, by way of an example, can provide a solid substrate carrier that can be resistively or inductively heated. The substrate can be heated without any susceptor in a resistively-heated quartz tube. In these methods, there can exist heated surfaces (other than the intended deposition substrate) on which an oxysilaborane film is deposited. The substrate can be heated without a susceptor in a cold-wall reactor by radiative heat by halogen lamps in a low-pressure rapid thermal chemical vapor deposition that minimizes reactor outgassing from heated surfaces coated by prior depositions.
Whenever the deposition temperature exceeds ˜350° C. hydrogenation effects are substantially eliminated. Conversely, by reducing the deposition temperature below ˜350° C. a thin picocrystalline solid can become significantly hydrogenated, such that hydrogen can be actively incorporated in chemical bonds. The relative atomic concentration of hydrogen in a picocrystalline oxysilaborane solid deposited below ˜350° C. is usually within the range of 10-25% depending on the degree of oxygen incorporation. When hydrogen is not actively incorporated in the chemical bonds of an oxysilaborane solid, it is more particularly referred to as an oxysilaboride solid. An oxysilaborane solid substantially void of oxygen is specifically referred to as a silaborane solid.
Oxygen can be incorporated into a picocrystalline oxysilaborane solid by either individual oxygen atoms or as part of water molecules. A picocrystalline oxysilaborane solid that contains water molecules is said to be hydrous while a picocrystalline oxysilaborane solid formed by individual hydrogen and oxygen atoms, with a relatively negligible amount of water, is said to be anhydrous. It has been observed that hydrous picocrystalline oxysilaborane solids undergo a change in color and stoichiometry over time due, apparently, to the change in the trapped water. Unless explicitly stated otherwise, picocrystalline oxysilaborane solids in embodiments described hereinbelow are understood to be anhydrous. In order to minimize hydration, a deposition reactor is fitted with a load-lock chamber isolating the reaction chamber from a direct exposure to ambient moisture. However, adsorbed moisture is difficult to fully eliminate during sample loading.
In addition to color changes, hydration can alter the boron-to-silicon ratio. In one preferred embodiment of oxysilaborane, the boron-to-silicon ratio is ideally six. An incorporation of atomic oxygen without hydration in oxysilaborane reduces the boron-to-silicon ratio while the incorporation of water molecules into hydrous oxysilaborane tends to increase the boron-to-silicon ratio. Both such effects can exist concurrently. A preferred introduction of oxygen into anhydrous oxysilaborane is by means of nitrous oxide. The relative atomic concentration of boron atoms in oxysilaborane amongst boron, silicon, and oxygen atoms is ideally ˜83%. In the absence of any hydration effects, the relative atomic concentration of boron amongst boron, silicon, and oxygen atoms does not significantly exceed ˜89%. The susceptibility to hydration depends, in part, on the relative oxygen atomic concentration and the method by which oxygen is introduced.
Self-assembled picocrystalline oxysilaborane has characteristics that are useful in electronic integrated circuits using covalent semiconductors, such as monocrystalline silicon. The electronic properties of an oxysilaborane solid can be altered in a controlled manner by processing conditions during the vapor-phase deposition. Picocrystalline oxysilaborane exhibits a long-range bond-orientational order. X-ray photoelectron spectroscopy (XPS) established the binding energy of the boron Is electron in picocrystalline oxysilaborane as ˜188 eV, which is characteristic of chemical bonds in an icosahedral boron molecule. The oxygen is electron binding energy, ˜532 eV, is quite similar to that of the oxygen Is electron binding energy in a metallic oxide, which is different from that of the oxygen is electron in a glass.
The silicon 2p electron binding energy in the oxysilaborane solids of this invention exhibits a sharp energy peak of 99.6 eV over the full compositional range. This is important for several reasons. First of all, the absence of two energy peaks in oxysilaborane implies that the Si—Si and Si—H bonds possess an identical binding energy. Secondly, the measured binding energy of a silicon 2p electron in oxysilaborane is essentially that of monocrystalline silicon constituted by tetrahedral chemical bonds in the diamond lattice. The silicon 2p electron binding energy in silicon dioxide is 103.2 eV. When oxysilaborane is deposited on amorphous silicon dioxide, there exists a distinct difference in the silicon 2p electron binding energy in the two compositions. The silicon 2p electron binding energy in oxysilaborane is similar to that of monocrystalline silicon, despite being deposited on an amorphous oxide, due to a self-assembly of picocrystalline oxysilaboranes.
By appropriately controlling the chemical vapor deposition processing conditions, picocrystalline oxysilaborane (B12H4)xSiyOz self-assembles over the preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2) that is bounded by picocrystalline silaborane (B12H4)3Si5 at one compositional extreme and by picocrystalline oxysilaborane (B122−H4)4Si4O22+ at the opposite such compositional extreme. In order to more fully understand the preferred processing conditions, the processing of non-preferred species in the broader range (0≤w≤5, 2≤x≤4, 2≤y≤5, 0≤z≤3) of oxysilaborane (B12)xSiyO2Hw will be taught by a number of examples.
Now, various embodiments of oxysilaborane compositions according to the present invention are described by examples, but the scope of the invention is not limited thereto. As will be understood by those skilled in the art, this invention may be embodied in other forms without a departure from the spirit or essential characteristics thereof. The disclosure and descriptions herein below are intended to be illustrative, but not limiting, of the scope of the invention.
Phosphorous was diffused into the 100 mm diameter monocrystalline (001) p-type silicon substrate 404 (
The reactant gas flow rate was stabilized at a pressure of 3.29 torr, whereupon the tungsten-halogen lamps were turned on for 30 seconds and regulated so as to maintain the sample wafer at 605° C. As shown in
The relative hydrogen concentration in the thin silaboride solid 406 was measured by means of hydrogen forward scattering (HFS), in which hydrogen atoms are elastically scattered by incident high-energy helium atoms. Hydrogen forward scattering (HFS) is not as quantitative as the Rutherford backscattering spectroscopy (RBS), due to the oblique angle of incident helium atoms that causes a variation in the charge integration in various samples. Although the hydrogen counts per unit solid angle are constant, the solid angle itself can change between different samples. No hydrogen was detected. A solid comprised of boron and silicon in the absence of hydrogen is referred to as a silaboride composition.
A secondary ion mass spectroscopy (SIMS) analysis determined the 511B/510B ratio of the silaboride solid 406 as the naturally-occurring ratio 4.03. The absence of any hydrogen or isotopic enrichment in the silaboride solid 406 of this example is due to the deposition temperature. A hydrogenation of silaborane can be realized when the deposition temperature is below ˜350° C. or when oxygen is introduced, as will be discussed in examples herein below. The silaboride solid 406 of this example was established by x-ray diffraction to be a picocrystalline boron solid. A GIXRD scan of the picocrystalline silaboride solid 406 of this example is shown in
The procedure described in Example 1 was carried out with the two exceptions that undiluted nitrous oxide N20 was introduced at 704 sccm and the flow rates of the hydride gases were doubled. A 3% mixture by volume of diborane in hydrogen B2H6(3%)/H2(97%) at a flow rate of 728 sccm, a 7% mixture by volume of monosilane in hydrogen SiH4(7%)/H2(93%) at a flow rate of 780 seem, and undiluted nitrous oxide N2O at a flow rate of 704 sccm were introduced. The vapor flow rate was stabilized at 9.54 torr, whereupon the tungsten-halogen lamps were turned on for 30 seconds, and regulated, in order to maintain the sample substrate 404 at 605° C. As shown in
A conventional ω-2θ XRD scan of the thin oxysilaborane solid 407 is shown in
By Rutherford backscattering spectroscopy (RBS) and hydrogen forward scattering (HFS) the relative bulk atomic concentrations of boron, hydrogen, silicon, and oxygen within the oxysilaborane solid 407 of this example were respectively determined as: 72%, 5.6%, 13.4%, and 9.0%. The picocrystalline boron solid 407 of the present example is not a borane solid but, rather, is much better characterized as an oxygen-rich composition (B12)2Si3.5O2.5H in which the hydrogen atoms are, most probably, bonded to the oxygen atoms. Secondary ion mass spectroscopy (SIMS) established the isotopic ratio 511B/510B as being the naturally-occurring ratio of the boron isotopes, to within the experimental error. It is currently believed that the existence of a naturally-occurring isotopic ratio in 511B/510B is indicative of the absence of intertwined rovibronic energy levels that are capable of promoting the redistribution of electrons between microwave energy levels.
The pyrolysis of boron and silicon hydrides was carried out by a low-pressure chemical vapor deposition (LPCVD) within a horizontal resistively-heated reactor comprising a five-inch diameter quartz deposition tube, which was constrained on a table. The resistive heating element was mounted upon a motorized track, such that 75 mm silicon substrates could be loaded onto a quartz holder in the front of the tube at room temperature. Water vapor adsorbed onto the quartz walls during sample loading provided a source of water vapor for the subsequent chemical reaction. A 75 mm diameter monocrystalline (001) n-type silicon substrate 408 of a resistivity of 20 Ω-cm was loaded onto a quartz holder in the quartz tube, which was sealed and mechanically pumped down to a base pressure of 30 mtorr.
As shown in
An x-ray photoelectron spectroscopy (XPS) depth profile of the silaborane solid 409 was performed. The oxygen in the silaborane solid 409 is due to an outgassing of water vapor from the quartz walls. The XPS depth profile in
The Auger electron spectroscopy (AES) depth profile in
The film in Example 3 is referred to as a silaborane solid 409 since the small relative atomic concentration of oxygen is believed to be in the form of water. As a result, this film is better referred to as a hydrous silaborane solid 409. The conventional ω-2θ XRD diffraction pattern in
Referring now to
The substrate temperature was increased to 280° C. by a resistively-heated rotating susceptor. Upon stabilization at the deposition temperature of 280° C., the chemical reaction was allowed to proceed for 5 minutes, whereupon susceptor heating was arrested and the sample was allowed to cool to below 80° C. before removing it from the deposition chamber. A thin solid 411 with a polymeric semitransparent color was deposited upon the substrate 410, as shown in
RBS and HFS analysis established the relative atomic concentrations of boron, hydrogen, and silicon as being: 66%, 22%, and 11%. The silaborane solid 411 of this example is very similar to the silaborane solid 409 in Example 3, except that the silaborane solid 411 of this example did not exhibit noticeable hydration effects. Electrical characteristics of the silaborane solid 411 were measured by an HP-4145 parameter analyzer, with the sweep signals by a mercury probe. Linear and log-log graphs of the current-voltage characteristics of the silaborane solid 411 are shown in
Space-charge-limited current conduction in a solid was first proposed by Mott and Gurney, Electronic Processes in Ionic Crystals, Oxford University Press, second edition, 1948, pp. 168-173. In analogy to Child's law of vacuum-tube devices, Mott and Gurney developed that a space-charge-limited current density between electrodes, intervened by a dielectric, quadratically varies with an impressed electromotive force. The Mott-Gurney law is satisfied when a unipolar excess mobile charge exists due to a nonvanishing divergence of the electric field per Gauss' law. The conduction current in the picocrystalline oxysilaboranes is space-charge-limited.
The procedure described in Example 4 was carried out with the sole exception that nitrous oxide was introduced at a flow rate of 40 seem. As shown in
The electrical impedance of the oxysilaborane solid 412 of the present example was measured by an HP-4145 parameter analyzer, with the sweep signals provided by a mercury probe. Linear and log-log graphs of the impedance characteristics of the oxysilaborane solid 412 of this example are respectively shown in
The procedure described in Example 5 was carried out with a single exception that the flow rate of the nitrous oxide was increased from 40 sccm to 80 sccm. The thickness of the oxysilaborane solid 412 was measured by variable-angle spectroscopic ellipsometry as being 147 nm. The XPS depth profile in
An RBS and HFS analysis established the bulk relative atomic concentrations of boron, hydrogen, silicon, and oxygen as respectively being: 63%, 23%, 11%, and 3%. The relative atomic concentration of oxygen is close to its RBS detection limit and, thus, is not accurate. The impedance of the oxysilaborane solid 412 of this example was measured by an HP-4145 parameter analyzer, with the sweep signals obtained by a mercury probe. Linear and logarithm graphs of the impedance characteristics of the oxysilaborane solid 412 are respectively shown in
The procedure described in Example 6 was carried out with the sole exception that the flow rate of the nitrous oxide was increased from 80 sccm to 100 sccm. The thickness of the oxysilaborane solid 412 was established by variable-angle spectroscopic ellipsometry as 140 nm. The XPS depth profile in
The procedure described in Example 7 was carried out with the sole exception that the flow rate of nitrous oxide was increased from 100 sccm to 300 sccm. The thickness of the thin oxysilaborane solid 412 was measured by variable-angle spectroscopic ellipsometry as being 126 nm. The XPS depth profile in
The procedure in Example 8 was carried out with the sole exception that the nitrous oxide flow rate was increased from 300 to 500 sccm. The thickness of the thin oxysilaborane solid 412 of this example was measured by variable-angle spectroscopic ellipsometry as 107 nm. The XPS depth profile in
The oxysilaborane solid 412 of this example is oxygen-rich, such that it does not exist within the preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2) of self-assembled picocrystalline oxysilaborane (B12H4)xSiyOz but rather is contained in the broader compositional range (0≤w≤5, 2≤x≤4, 2≤y≤5, 0≤z≤3) of oxysilaborane (B12)xSiyOzHw. It is significant that picocrystalline oxysilaborane unpins the surface Fermi level of monocrystalline silicon so as to modulate the surface electrochemical potential of monocrystalline silicon and, at the same time, to conduct electricity. In order to more fully appreciate such a property, it is purposeful to consider examples in which an electrochemical rectifier is formed with monocrystalline silicon.
It is heretofore impossible in the prior art to vary the electrochemical potential of a monocrystalline silicon region throughout the forbidden energy region, while conducting electric charge, due to an undesirable contact potential associated with mobile-charge diffusion between a monocrystalline silicon region and a conjoined solid of a different work function. This deficiency is remedied by self-assembled picocrystalline oxysilaborane by means of actual examples.
Monocrystalline silicon was epitaxially deposited over a (001) boron-doped p-type monocrystalline substrate 421 with a 100 mm diameter and 525 μm thickness. The resistivity of the degenerate monocrystalline silicon substrate 421 was 0.02 Ω-cm, which corresponds to an acceptor concentration of 4×1018 cm−3. A nondegenerate p-type monocrystalline silicon layer 422 was deposited on the silicon substrate 421. The epitaxial silicon layer 422 had a thickness of 15 μm and a resistivity of 2 Ω-cm, which relates to an acceptor impurity concentration of ˜7×1015 cm−3. All oxide was removed by a hydrofluoric acid deglaze. After the acid deglaze, the silicon substrate 421 was inserted onto a resistively-heated susceptor in an EMCORE MOCVD reactor by a load-lock system isolating the deposition chamber from the ambient. The deposition chamber was mechanically pumped below 50 mtorr, whereupon a 3% mixture by volume of diborane in hydrogen B12H6(3%)/H2(97%) at the flow rate of 150 seem and a 7% mixture by volume of silane in hydrogen SiH4(7%)/H2(93%) at the flow rate of 300 sccm were introduced into the deposition chamber. Nitrous oxide N2O was introduced at a flow rate of 100 seem.
The gases were permitted to mix before entering into the deposition chamber. Upon the stabilization of the reactant gases, the chamber pressure was regulated at 1.5 torr while the susceptor was rotated at 1100 rpm. The substrate temperature was the increased to 230° C. for 2 minutes. The susceptor temperature was then further increased to 260° C., whereupon it stabilized and the chemical reaction was permitted to proceed for 12 minutes. The susceptor heating was secured and the sample was permitted to cool below 80° C. in the reactant gases before it was removed from the deposition chamber. An oxysilaborane solid 423 was deposited. The thickness was measured by variable-angle spectroscopic ellipsometry as being 12.8 nm. Due to the thickness, the oxysilaborane solid 423 showed no additional coloration as a result of the solid deposition.
Aluminum was evaporated over the substrate 421 backside in a bell-jar evaporator, after which, a similar layer of aluminum was evaporated on the oxysilaborane solid 423 through a shadow mask in the bell-jar evaporator. The topside aluminum formed the cathode electrode 424 and the backside aluminum formed the anode electrode 425, as shown in
As shown in
The procedure described in Example 10 was carried out with the sole exception that the flow rate of nitrous oxide N2O was increased from 20 sccm to 65 sccm. The thickness of the oxysilaborane solid 423 was measured by variable-angle spectroscopic ellipsometry as 12.4 nm. The electrical characteristics of the p-isotype electrochemical rectifier 420 of this example were measured by an HP-4145 parameter analyzer, with sweep signals obtained from the anode and cathode electrodes 425 and 424 by microprobes. The linear current-voltage characteristics of the p-isotype electrochemical rectifier 420 of this example are shown at different ranges in
The procedure described above in Example 11 was carried out with the exception that the reaction time at 260° C. was decreased from 12 minutes to 6 minutes. The thickness of the oxysilaborane solid 423 of this present example was measured by variable-angle spectroscopic ellipsometry as 7.8 nm. The electrical characteristics of the p-isotype electrochemical rectifier 420 of this example were measured by an HP-4145 parameter analyzer, with sweep signals obtained from the anode and cathode electrodes 425 and 424 by two microprobes. Linear current-voltage characteristics of the p-isotype electrochemical rectifier 420 of the present example are shown at three different current-voltage ranges in
The procedure in Example 12 was carried out with the exception that nitrous oxide N2O was never introduced. The thickness of the silaborane solid 426 represented in
Ignoring interfacial effects, the composition of the oxysilaborane solid 423 described in Examples 11-12 is prototypical picocrystalline oxysilaborane (B122−H4)4Si4O22+ and the silaborane solid 426 of Example 13 is picocrystalline silaborane (B12H4)3Si5. Picocrystalline oxysilaborane (B122−H4)4Si4O22+ and picocrystalline silaborane (B12H4)3Si5 exhibit different, albeit complementary, electrochemical properties. The profound difference between the two compositions is exemplified by the fundamental difference in the rectification of the electrochemical devices 420 in Example 12 and Example 13 due to the critical role of oxygen. The difference in devices 420 of these two examples is the oxygen concentration of the picocrystalline solids 423 and 426.
Referring to
A different situation occurs when the electrochemical rectifier 420 is reverse-biased. Referring now to
Whenever a charge plasma is injected into a semiconductor or dielectric, the current density and voltage vary linearly until a sufficiently high level of charge injection gives rise to a space-charge-limited current density due to a breakdown in charge neutrality. High-level charge injection into a semiconductor tends to result in a quadratic dependence of a space-charge-limited current density on voltage while high-level charge injection in a dielectric tends to result in a cubic dependence of a space-charge-limited current density on voltage. The principal difference between a semiconductor and a dielectric is that the former is typically characterized by a large extrinsic mobile-charge concentration of a negative or positive polarity while the latter is characterized by a negligible mobile-charge concentration.
In principle, the log-log current-voltage characteristic of the electrochemical rectifier 420 in
For example, per the above reference by Lampert and Mark, a silicon p-i-n diode with a length of the intrinsic silicon region being 4 mm exhibits a space-charge-limited current-voltage characteristic with a cubic dependency of the current density upon the impressed voltage beyond a relaxation voltage of 10V. When the length of the intrinsic silicon region of the p-i-n diode was reduced to approximately 1 mm, the current density varied exponentially with an impressed voltage due to a dominance of mobile-charge diffusion. Referring, again, to
This is only possible if the extrinsic charge concentration is sufficiently large that the Debye length of the oxysilaborane solid 423 is less than approximately 4 nm. The extrinsic charge concentration p0 of self-assembled picocrystalline oxysilaborane (B12H4)xSiyOz over the preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2) is essentially constant at p0≈1018 cm−3. The extrinsic carrier concentration relates to the impurity doping concentration in monocrystalline silicon at the onset of bandgap narrowing. Picocrystalline oxysilaborane (B12H4)xSiyOZ is a novel compound since it exhibits a closed-shell electronic configuration and, also, an extrinsic mobile-charge concentration near the onset of bandgap narrowing in silicon.
It is believed that a possible explanation of the atomic engineering of compositions, made in accordance with this invention, may be given with respect to the picocrystalline artificial borane atom 101 shown in
In conventional chemistry, the atomic and molecular energy levels are all assumed to obey Schrödinger's nonrelativistic wave equation. Although electrons are known to possess a spin angular momentum, spin is not comprehended by Schrödinger's nonrelativistic wave equation. As the result, electrons possessing a different spin angular momentum can occupy a common energy level characterized by a common azimuthal quantum number l associated with a whole-integer-quantized orbital angular momentum. Said orbital angular momentum degeneracy is lifted in the presence of spin-orbit coupling, such that energy levels associated with a whole-integer azimuthal quantum number l are split into doublets of energy levels associated with a half-integer-quantized total angular momentum. A splitting of energy levels by spin-orbit coupling is shown in
The energy levels in
In addition to these positive-definite energy levels, Dirac's relativistic wave equation requires an equal number of negative-definite energy levels, which are appropriately designated in
The positive-definite energy levels in
The valence electrons in
It is believed that all bonding energy levels in
The ionization of picocrystalline artificial borane atoms B122−H4 or B122+H4 101 is due to the ionization of the artificial nuclei B122− or B122+ without any change in the four artificial valence electrons H4. The ability to ionize an artificial nucleus, without altering the artificial electrons, is responsible for a novel type of atomic engineering of picocrystalline oxysilaborane (B12H4)xSiyOz over the preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2). The electronic closed-shell of the negatively-ionized picocrystalline artificial borane atom B122−H4 101 in
The trace concentration of positively-ionized picocrystalline artificial borane atoms B122+H4 101 results in the extrinsic carrier concentration p0≈1018 cm−3 of picocrystalline silaborane (B12H4)3Si5. This is experimentally verified in Example 13. In this particular example, the acceptor doping of the silicon substrate 421 results an extrinsic carrier concentration of p0≈4×1018 cm−3. The extrinsic carrier concentration of the nondegenerate p-type monocrystalline silicon layer 422 is p0≈7≤x≤105 cm−3. As a result, mobile holes are injected into the p-type monocrystalline silicon layer 422 from either the silicon substrate 421 or the picocrystalline silaborane (B12H4)3Si5 film 426 in Example 13, dependent upon the bias polarity of the anode and cathode electrodes 425 and 424. When the cathode electrode 424 is biased negative relative to the anode electrode 425, mobile holes are injected from the silicon substrate 421 into the p-type monocrystalline silicon layer 422.
Conversely, when the cathode electrode 424 is biased positive relative to the anode electrode 425, mobile holes are injected from the picocrystalline silaborane (B12H4)3Si5 film 426 into the p-type monocrystalline silicon layer 422. Referring now to the impedance characteristics in
The utility of the atomic engineering of picocrystalline artificial borane atoms 101 in picocrystalline silaborane (B12H4)3Si5 and picocrystalline oxysilaborane (B122−H4)4Si4O22+ can be better understood by considering the believed operation of the thermophotovoltaic diode 500 in
An isolated natural boron atom possesses 3 valence electrons distributed amongst 4 orthonormal atomic orbitals: ψi(s), ψi(px), ψi(py), and ψi(pz). These 4 orthonormal atomic orbitals are linearly independent of each other. When the 12 natural boron atoms are bonded together by three-center bonds, the atomic orbitals become intertwined, such that they are no longer linearly independent of each other. Although linearly-dependent intertwined atomic orbitals are difficult to analyze, they result in a molecular bond delocalization that supports novel electronic properties not sustainable in any other type of molecule. Following Longuet-Higgins and Roberts, a regular icosahedron is inscribed in a cube in the manner shown in
A natural boron nucleus 102 exists at each icosahedral vertex in 100
) shown in
It follows that the 12 tangential atomic orbitals ψi(p100
) exist in the laboratory frame field while the 12 tangential atomic orbitals ψi(p{111}) reside in the molecular frame field. This is quite important since the 120 symmetry operations of a regular icosahedron cause all three of the Cartesian axes in the laboratory frame to rotate, such that the displacement of the boron nuclei 102 in response to the 120 symmetry operations of a regular icosahedron cannot be fully described in the laboratory frame field. Due to the corotating Cartesian axes in the laboratory frame field of the circumscribed cube, there exist 3 other delocalized sets of 12 tangential atomic orbitals ψi(p{111}) that are shown in
The generalization of the molecular orbital analysis by Longuet-Higgins and Roberts, to account for the full impact of the 120 icosahedral symmetry operations on the displacement of the boron nuclei 102, results in the symmetrical nuclear configuration of a boron icosahedron in 111
wave vectors shown in
The 24 nonorthogonal tangential atomic orbitals ψi(p{111}) shown in
In a like way, the nearly-twelvefold-degenerate bonding molecular orbital cluster of electrons ΨY(T1u, Gu, Hg) is believed to be associated with: 1) the threefold-degenerate icosahedral irreducible representation T1u, (2) the fourfold-degenerate icosahedral irreducible representation Gu, and also (3) the fivefold-degenerate icosahedral irreducible representation Hg. Whereas the fourfold-degenerate icosahedral irreducible representation Gu is associated with surface spherical harmonics of an icosahedron, the threefold-degenerate icosahedral irreducible representation T1u and fivefold-degenerate icosahedral irreducible representation Hg are, more generally, associated with the radial and surface spherical harmonics of an icosahedron. It is believed that the nearly-twelvefold-degenerate antibonding molecular orbital cluster of electrons ΨY(T1g,Gg,Hu) is ideally associated with +2s, +2p, +3s, +3p, +3d energy levels in
The above-described clustering of valence electron energy levels in a regular boron icosahedron is portrayed in 100
) are parallel. This is remedied by representing the 24 tangential atomic orbitals ψi(p{111}) by the threefold-degenerate icosahedral irreducible representation T1g associated with rotation and the threefold-degenerate icosahedral irreducible representation T1u associated with translation.
By so doing, it was proven that the 120 symmetry operations of a regular icosahedron result in no icosahedral rotation and confine all icosahedral translation along the rectilinear axes of the k111
wave vectors shown in
111
wave vectors in
The valence electrons in the antibonding intraicosahedral orbitals of a regular boron icosahedron are within the nearly-twelvefold-degenerate molecular orbital cluster ΨY(T1g,Gg,Hu) while the valence electrons in the bonding intraicosahedral orbitals of a regular boron icosahedron are within the nearly-twelvefold-degenerate molecular orbital cluster ΨY(T1u,Gu,Hg). The nearly-twelvefold-degenerate antibonding molecular orbital cluster ΨY(T1g,Gg,Hu) of valence electrons is believed to support a delocalized peak electron density near the geometric center of the 4 {111} icosahedral faces normal to the k111
wave vectors of the picocrystalline artificial borane atom 101 in
In this manner, the positive-definite half-integer-quantized energy levels in
The 18 valence electrons in the half-integer-quantized, positive-definite antibonding energy levels and the 18 valence electrons in the half-integer-quantized, negative-definite bonding energy levels exist near the geometric center of opposite icosahedral faces amongst the delocalized pairs of icosahedral faces normal to the 4 k111
wave vectors of the picocrystalline artificial borane atom 101 in
There are two different elementary types of atomic engineering of the picocrystalline oxysilaboranes of this invention. One elementary type of atomic engineering involves the absence of any significant trace impurity, such that charge-conjugate symmetry is broken between the half-integer-quantized energy levels within the artificial nuclei B12 of neutral picocrystalline artificial borane atoms B2H4 101 per
It is believed that the valence electron configuration in
The impact of the radial spherical harmonics can be understood in conjunction with the disproportionation of neutral picocrystalline artificial borane atoms B12H4 101 into equal pairs of dianions B122−H4 101 and dications B122+H4 101 in the manner represented in
The occupied electronic energy levels of the artificial nuclei of the first- and second-nearest neighbor picocrystalline artificial borane atoms 101 of a pair of conjoined picocrystalline silaborane (B12H4)3Si5 and picocrystalline oxysilaborane (B122−H4)4Si4O22+ regions 501 and 502 are respectively shown in shown in
As discussed above, the trace concentration p0≈1018 cm−3 of neutral picocrystalline artificial borane atoms B12H4 101 in a picocrystalline silaborane (B12H4)3Si5 region 501 undergo a disproportionation into neighboring pairs of ionized picocrystalline artificial borane atoms B122−H4 and B122+H4 101. The occupied electronic energy levels of the artificial nuclei B122− and B122+ of certain neighboring picocrystalline artificial borane atoms B122−H4 and B122−H4 101 within a picocrystalline silaborane (B12H4)3Si5 region 501 are represented in
A pair of mobile holes spontaneously diffuses from the artificial nucleus B122+ in and, in a similar manner, the pair of holes diffusing from the −3p3/2 energy level in
. The latter convention exploits the fact that, when completely occupied by 4 electrons, the −3p3/2 energy level in
. It follows that |−3p3/22
represents a pair of missing electrons, and thus a pair of holes, in the −3p3/2 energy level in
The existence of a pair of mobile electrons |−2s1/22 and a pair of mobile holes |−3p3/22
in two different energy levels, separated by a microwave energy difference, supports a novelty and utility of preferred embodiments of this invention. This can be better comprehended by considering the occupied energy levels in
diffusing from the artificial nucleus B122+ in
shown in
diffusing from the artificial nucleus B12 in
shown in
A disentanglement of the −2sp1/2 energy level by spin-orbit coupling necessitates 45 micro-electron-volts of energy. In the absence of any such disentanglement, this energy is believed to be manifested in a vibrational energy along the k111
wave vectors of the picocrystalline artificial borane atoms 101. The 45 micro-electron-volts thereby corresponds to a vibrational frequency of 10.9 GHz, which is below the maximum frequency (160 GHz) of the cosmic background radiation. Thus, any radiation of a frequency greater than cosmic background radiation is capable of exciting electrons from the entangled −2sp1/2 energy level into the disentangled −3p3/2 energy level, in the manner represented in
The energy levels in and |−3p3/22
in the thermophotovoltaic diode 500 in
from each picocrystalline silaborane (B12H4)3Si5 region 501, in the form of transformed mobile holes |−2s1/20
, into the conjoined picocrystalline oxysilaborane (B122−H4)4Si4O22+ region 502. The diffusion of mobile holes |−2s1/20
into the picocrystalline oxysilaborane (B122−H4)4Si4O22+ region 502 necessarily results in an accumulated space-charge region with a width of approximately two Debye lengths. Since the Debye length of the picocrystalline oxysilaborane (B122−H4)4Si4O22+ region 502 is on the order of approximately 4 nm, then the width of said accumulated space-charge region is 8 nm. The electric current density is determined by the width of the picocrystalline oxysilaborane (B122−H4)4Si4O22+ region 502.
If the width of the picocrystalline oxysilaborane (B122−H4)4Si4O22+ region 502 is greater than approximately 8 nm, the space-charge-limited drift current density will be similar to that in
This novel and useful application of the picocrystalline oxysilaboranes (B12H4)xSiyOz of the present invention is due to an atomic engineering that supports a controlled variation in the electronegativity of the picocrystalline artificial borane atoms 101 over a preferred compositional range (2≤x≤4, 3≤y≤5 and 0≤z≤2). Although the particular conjoined regions 501 and 502 of the thermophotovoltaic diode 500 shown in
Although mobile holes |−3p3/22 and mobile electrons |−2s1/22
in a thermophotovoltaic diode 500 were associated hereinabove with very specific energy levels separated by more than 45 micro-electron-volts, it is to be understood that mobile holes and mobile electrons more generally exist in discrete energy levels separated by a microwave energy. This capability provides for the operation of a thermophotovoltaic diode, constituted by conjoined picocrystalline oxysilaboranes (B12H4)xSiyOz of this invention, to ideally operate at an ambient temperature and, more practically, to operate at the ambient temperature of the infrared terrestrial heat radiation emitted by earth. This is very different from a conventional thermophotovoltaic diode.
A conventional thermophotovoltaic diode in the prior art is comprised of a thermal emitter and a photovoltaic diode, with said thermal emitter being typically heated to a temperature above the photovoltaic diode. In a conventional photovoltaic diode, mobile electron-hole pairs are radiatively generated and separated such that mobile electrons are thereby excited into an extended conduction energy band (constituted by a continuum of antibonding molecular orbitals) and mobile holes are excited into an extended valence energy band (constituted by a continuum of bonding molecular orbitals). As used herein, an extended energy band is a large group of antibonding or bonding molecular orbitals respectively behaving as continuum of energy levels extending over a region of space well beyond the first- and second-nearest neighbor natural or artificial atoms, such that mobile electrons are displaced in space at a common energy amongst antibonding molecular orbitals and mobile holes are displaced in space at a different common energy amongst the bonding molecular orbitals. The forbidden energy region between the bottom of the conduction energy band and the top of the valence energy band limits the minimum temperature of the thermal emitter relative to the photovoltaic diode of a conventional thermophotovoltaic diode.
The discrete quantization of energy within the artificial nuclei (constituted by nearly-symmetrical icosahedra with natural boron nuclei 102 residing at the icosahedral vertices) of the picocrystalline artificial borane atoms 101 of this invention allows for an atomic engineering by which mobile holes can exist in different discrete energy levels, separated by a microwave energy, within bonding molecular suborbitals that are confined in space amongst first- and second-nearest neighbor picocrystalline artificial borane atoms 101. By means of this type of atomic engineering, mobile holes and mobile electrons can be generated and separated into discrete energy levels, with a forbidden energy region on the order of 45 micro-electron-volts, so as to be displaced over space at different energy levels. Since the forbidden energy region between discrete energy levels within the artificial nuclei of the picocrystalline artificial borane atoms 101 is on the order of 45 micro-electron-volts, then a continued generation of mobile electron-hole pairs at different energy levels in the picocrystalline artificial borane atoms 101 of the thermophotovoltaic diode 500 in
One type of atomic engineering of picocrystalline artificial borane atoms 101 that can support a novel thermophotovoltaic diode capable of harvesting terrestrial radiation was described above. This type of atomic engineering utilizes a breakdown in the charge-conjugation symmetry in the artificial nuclei of picocrystalline artificial borane atoms 101. Another useful type of atomic engineering of the picocrystalline artificial borane atoms 101 maintains the charge-conjugation symmetry of the artificial nuclei. This second type of atomic engineering is achieved by means of the incorporation of a significant impurity atom, such as gold, so as to ideally occupy the energy levels of the picocrystalline artificial borane atoms 101 in the manner represented in
As used herein, the suffix “:Au” in (B12H4)3Si5:Au denotes the trace incorporation of natural gold atoms. The trace concentration of gold atoms in (B12H4)3Si5:Au is approximately the same as the extrinsic carrier concentration of p0≈1018 cm−3. By introducing oxygen, picocrystalline oxysilaborane (B122−H4)4Si4O22+:Au becomes a conductive material with an electrical conductivity that is many orders of magnitude greater than the conductivity of picocrystalline oxysilaborane (B122−H4)4Si4O22+. As used herein, the explicit absence of the suffix “:Au” is intended to denote that picocrystalline oxysilaborane (B122−H4)4Si4O22+ is void of any detectable concentration of impurity gold atoms. An example of the incorporation of trace gold atoms is now provided.
Referring to
A secondary ion mass spectroscopy (SIMS) was then performed in order to measure a trace impurity concentration of gold in the oxysilaborane film 605. The SIMS depth profile in
Thus, one skilled in the art will recognize that layers of picocrystalline oxysilaboranes having varying amounts of oxygen and impurities such as gold can be deposited, for example by chemical vapor deposition techniques, so as to create electronic properties on a tailor-made basis by an atomic engineering of picocrystalline artificial borane atoms 101. All devices, variations and adaptations for using the novel compositions of matter disclosed herein are intended to fall within the scope of the appended claims.
This application is a divisional of U.S. application Ser. No. 15/363,230 filed on Nov. 29, 2016 and issued as U.S. patent Ser. No. ______, which is a continuation-in-part of U.S. application Ser. No. 15/167,672 entitled “Composition and Method for Making Picocrystalline Artificial Atoms,” filed on May 27, 2016 and now abandoned, and claims priority to U.S. Provisional Application No. 62/167,418 entitled “Self-Assembled Supramolecular Oxysilaborane and Method for Making Same” filed on May 28, 2015, the disclosures of which are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62167418 | May 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15363230 | Nov 2016 | US |
| Child | 15959463 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15167672 | May 2016 | US |
| Child | 15363230 | US |